KR20150144023A

KR20150144023A - Refillable Fragrance Gypsum Fragrance

Info

Publication number: KR20150144023A
Application number: KR1020140072593A
Authority: KR
Inventors: 김혜진
Original assignee: 김혜진
Priority date: 2014-06-16
Filing date: 2014-06-16
Publication date: 2015-12-24

Abstract

The present invention relates to a gypsum air freshener capable of emitting fragrances. The air freshener includes a base forming material, alcohol, oil, and a colorant. The base forming material includes: a predetermined amount of gypsum powder having a predetermined particle size; a rice paper liquid prepared by soaking a predetermined amount of rice paper in a predetermined amount of water; and a predetermined amount of cosmetic cotton. The refillable gypsum air freshener absorbs fragrances, emits the absorbed fragrances to the air for a predetermined period, and is filled with new air freshener refill products having different fragrances repeatedly when the amount of fragrances being emitted decreases in order to emit identical or different fragrances in a semi-permanent basis. The gypsum air freshener has tenacity to reduce the risk of damage while being handled, prevents the generation of bubbles in the body, and shortens the hardening time to extend the period of emitting the fragrances while maintaining the same absorption amount.

Description

{Refillable Fragrance Gypsum Fragrance}

본 발명은 방향제를 흡수시키고 흡수된 방향제로부터 향기가 공기 중으로 발산하도록 하는 방향제 흡수 및 발산용 석고방향제에 관한 것으로, 석고방향제에 흡수된 방향제로부터 발산되는 향기가 감소되면 다량의 반복적으로 방향제를 리필하고, 리필된 방향제의 향기발산 기간을 증가시키면서 석고방향제에 인성을 부가하여 취급시 훼손 위험이 감소되도록 하는 방향제 리필용 석고방향제에 관한 발명이다.The present invention relates to a gypsum fragrance for absorbing and dispersing fragrance which absorbs the fragrance and emits the fragrance from the absorbed fragrance into the air. When the fragrance emitted from the fragrance absorbed by the gypsum fragrance is reduced, a large amount of the fragrance is repeatedly refilled To increase the fragrance emission period of the refilled fragrance, while adding toughness to the gypsum fragrance to reduce the risk of damage during handling.

일반적으로 사용되는 방향제는 일정기간을 경과하여 사용하면 방향제가 소진되어 향기를 발산시키지 못함에 따라 다공성 물질에 방향제를 일정횟수에 걸쳐 반복적으로 흡착시켜 향기가 발산되도록 하는 기술이 알려져 있다.In general, when a perfume is used over a certain period of time, the fragrance is exhausted and the fragrance can not be emitted, so that the perfume is repeatedly adsorbed to the porous material by a predetermined number of times.

상기 다공성 물질 중에는 석고를 기반재로 하되, 석고에 오일과 유화제 및 색소를 혼합하여 다양한 모양으로 성형하고, 성형된 석고에 원하는 향을 흡수시켜 향기가 발산되도록 하며, 향기 발산이 소진되면 방향제를 보충하여 다시 향기가 발산되도록 하는 동시에 시각적 아름다움을 느끼도록 하는 기술이 알려져 있다.The porous material is made of gypsum as a base material. The gypsum is mixed with an oil, an emulsifier and a pigment to form various shapes, and the desired gypsum is absorbed to absorb the desired fragrance. When the gyration is exhausted, So that the fragrance can be diffused again and at the same time the visual beauty can be felt.

그러나 상기 석고 성형품은 단지 석고에 형성되는 다공질 부위에만 방향제가 침투되는 것이어서, 방향제의 미량만을 흡수하기 때문에 향기가 발산되는 기간이 짧아 수시로 방향제를 뿌려서 흡수시켜야 하는 문제가 발생되고 있다.However, since the gypsum molded article is only permeated into the porous portion formed only on the gypsum, only the minute amount of the fragrance is absorbed, so that the fragrance is diverted for a short period of time, so that the fragrance is often sprayed and absorbed.

또한 상기 석고 성형품은 외부와 내부 모두 동일한 석고로 이루어지기 때문에 흡수된 방향제가 쉽게 건조되어 향기가 발산되는 기간이 짧아 수시로 방향제를 뿌려야 하므로 방향제 소비량이 증가하는 문제가 발생되고 있다. In addition, since the gypsum molded article is made of the same gypsum both inside and outside, the absorbed fragrance is easily dried and the fragrance is emitted for a short period of time.

또한 상기 석고 성형품은 성형시 다량의 기포가 발생되기 때문에 표면이 매끄럽지 않고 성형품의 모서리 등이 쉽게 부서지며, 인성이 떨어져 작은 충격에도 성형품이 파손되는 문제가 발생되고 있다.In addition, since a large amount of bubbles are generated in the gypsum molded article, the surface of the gypsum molded article is not smooth, the edges of the molded article are easily broken, and the molded article tends to break even in small impacts.

이러한 문제점을 해소하기 위한 종래기술로서 한국 공개특허공보 특1999-58712호 젤형 방향제 조성물이 공지되어 있는데, 이는 향료를 다공성 무기분체에 흡착시킨 다음, 이를 수용성 고분자 물질, 습윤제, 분산제 및 지연제가 함유된 용액에 분산시키는 것으로, 다공성 무기분체는 실리카, 산화알루미늄, 규조토, 제올라이트, 탈크, 벤토나이트, 셀룰로오스, 카올린, 전분, 석고, 규산칼슘 등을 사용할 수 있고, 무기분체는 젤형 방향제 조성물 총 중량에 대하여 0.525.0중량%의 양으로 함유시키는 기술이다.A gel-type fragrance composition disclosed in Korean Patent Laid-Open Publication No. 1999-58712 is known as a conventional technique for solving such a problem. The fragrance is adsorbed on a porous inorganic powder, and then the fragrance is adsorbed on the porous inorganic powder, The porous inorganic powder may be silica, aluminum oxide, diatomaceous earth, zeolite, talc, bentonite, cellulose, kaolin, starch, gypsum or calcium silicate. The inorganic powder may be used in an amount of 0.525 By weight, based on the total weight of the composition.

이러한 상기 종래기술의 젤형 방향제는 조성물에서 향료가 흡착된 다공성 무기분체를 함유하여도 향료는 온도나 공기의 흐름에 의하여 서서히 방출하게 되므로, 이것을 지연 또는 방지시키기 위하여 수용성 고분자 물질이 함유된 수용액에 향료가 흡착된 다공성 무기분체를 분산시켜서 향료흡착분체가 수용성 고분자 물질로 코팅되도록 한 기술이다.In order to delay or prevent the above-mentioned gel-type fragrance, the fragrance is gradually released by the temperature or air flow even if the composition contains the porous inorganic powder adsorbed with the fragrance. Is adsorbed on the porous inorganic powder to disperse the porous inorganic powder to adsorb the fragrance adsorbent powder onto the porous polymer material.

그러나 상기 종래기술은 다공성 무기분체에 흡착된 향료가 소진되면 재사용이 불가능하고, 또한 조성물이 젤 형태이기 때문에 조성물을 보관하는 용기가 별도로 필요하며, 또한 조성물 자체만으로 특정 형상으로 제조할 수 없는 문제가 있다.However, in the above-mentioned prior art, it is impossible to reuse the fragrance adsorbed on the porous inorganic powder when the fragrance is exhausted. Moreover, since the composition is in the form of a gel, a container for storing the composition is separately required. Furthermore, have.

본 발명은 상기와 같은 문제점을 해소하기 위하여 창출된 것으로, 특정 모양으로 성형이 가능한 석고방향제에 향을 흡수시키고, 흡수된 향이 석고방향제로부터 공기 중으로 일정기간 발산하도록 하되, 향 발산이 감소되면 동일 또는 다른 종류의 향을 가지는 방향제를 반복적으로 리필하여 향 발산 기간을 증가시키는 동시에 석고방향제에 인성을 부가하여 취급시 파손과 훼손 위험을 감소시킴으로써, 석고방향제를 특정 모양으로 성형하고 특정 모양으로 성형된 석고방향제를 통해 향을 발산시켜 시각과 후각을 만족시키는 방향제 리필용 석고방향제를 제공하는 것을 목적으로 한다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a gypsum fragrance capable of being molded into a specific shape and to absorb the fragrance, By repeatedly refilling the fragrance having different kinds of fragrance to increase the fragrance period and adding toughness to the gypsum fragrance to reduce the risk of breakage and damage during handling, the gypsum fragrance is molded into a specific shape, And to provide a gypsum fragrance for a perfume refill which satisfies visual and olfactory angles by radiating fragrance through a fragrance.

본 발명은 상술한 과제를 해결하기 위하여, 향 발산용 석고방향제에 있어서, 상기 석고방향제는 기초 조형재와 알콜 및 오일을 포함하고, 여기에 색소를 첨가하여 이루어지는 것을 특징으로 하는 방향제 리필용 석고방향제를 제공하도록 한다.In order to solve the above problems, the present invention provides a gypsum aromatic agent for incense-dissipating, which comprises a base molding material, an alcohol and an oil, and a coloring matter added thereto, .

상기 기초 조형재는 일정크기의 입도를 가지는 일정량의 석고분과 일정량의 화선지를 일정량의 물에 불리는 화선지액 및 일정량의 화장솜을 포함하도록 한다.The basic molding material includes a predetermined amount of gypsum having a predetermined size and a predetermined amount of veneers, and a predetermined amount of water and a certain amount of cosmetic cotton.

상기 알콜은 석고방향제 전체 중량을 기준으로 1.5 내지 2.5중량%을 포함시키고, 상기 오일은 석고방향제 전체 중량을 기준으로 3.5 내지 4.5중량%를 포함시키도록 한다.The alcohol comprises from 1.5 to 2.5% by weight, based on the total weight of the gypsum fragrance, and the oil comprises from 3.5 to 4.5% by weight, based on the total weight of the gypsum fragrance.

상기 석고분은 입자크기 230 ~ 260 메쉬의 조형용 석고가루로 형성하고, 화선지액에 포함되는 화선지는 닥나무로 제조된 연습용 박지로 형성하며, 화장솜은 면 100%의 화장용 솜으로 형성하도록 한다.The gypsum powder is formed by molding gypsum powder having a particle size of 230 to 260 mesh, and the corrugated paper included in the corrugated paper is formed of a training paper made of mulberry tree, and the cosmetic cotton is formed of 100% cotton.

상기 석고분은 석고방향제 전체 중량을 기준으로 60 내지 65중량%를 포함시키고, 상기 화선지액은 석고방향제 전체 중량을 기준으로 25 내지 35중량%를 포함시키며, 상기 화장솜은 석고방향제 전체 중량을 기준으로 0.5 내지 1.0중량%를 포함시키도록 한다.Wherein the gypsum powder comprises from 60 to 65% by weight, based on the total weight of the gypsum fragrance, the gypsum liquid comprises from 25 to 35% by weight, based on the total weight of the gypsum fragrance, To 0.5% by weight to 1.0% by weight.

본 발명은 석고방향제에 향을 흡수시키고, 흡수된 향이 석고방향제로부터 공기 중으로 일정기간 발산하도록 하되, 향 발산이 감소되면 동일 또는 다른 종류의 향을 가지는 방향제를 반복적으로 리필하여 반영구적으로 동일 또는 다른 종류의 향을 발산시킬 수 있는 효과가 발생된다.The present invention absorbs fragrance in a gypsum fragrance and causes the absorbed fragrance to diffuse from the gypsum fragrance to the air for a certain period of time, but when the fragrance emission is reduced, the fragrance having the same or different kinds of fragrance is repeatedly refilled, It is possible to emit an aroma of the present invention.

본 발명은 석고방향제에 인성을 부가하여 취급시 파손과 훼손 위험이 감소되는 효과가 발생되고, 또한 석고방향제의 몸체에 기포가 발생되는 것을 억제하며, 석고방향제가 굳는 시간을 단축하고, 동일한 량의 방향제를 흡수시켜 향이 발산되는 기간을 증가시키는 효과가 발생된다.The present invention relates to a method for producing a gypsum fragrance by adding toughness to a gypsum fragrance agent, thereby reducing the risk of breakage and damage during handling, suppressing the generation of bubbles in the gypsum fragrance body, shortening the time required for solidifying the gypsum fragrance agent, The effect of absorbing the fragrance and increasing the period of the fragrance is generated.

도 1은 본 발명에 따른 방향제 리필용 석고방향제의 구성요소를 도시한 도면이다.
도 2는 본 발명에 따른 기초 조형제 구성을 도시한 도면이다.
도 3은 본 발명에 따른 방향제 리필용 석고방향제와 몰드의 실시형태를 도시한 도면이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a view showing components of a gypsum aroma agent for a perfume refill according to the present invention. Fig.
2 is a view showing the constitution of the basic molding composition according to the present invention.
3 is a view showing an embodiment of a mold and a gypsum aromatic agent for a perfume refill according to the present invention.

본 발명과 본 발명의 실시에 의해 달성되는 기술적 과제는 다음에서 설명하는 본 발명의 바람직한 실시예들에 의해 명확해질 것이다. 다음의 실시 예들은 단지 본 발명을 설명하기 위하여 예시된 것에 불과하며, 본 발명의 범위를 제한하기 위한 것은 아니다. BRIEF DESCRIPTION OF THE DRAWINGS The above and other objects, features and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. The following examples are merely illustrative of the present invention and are not intended to limit the scope of the present invention.

이하, 본 발명에 따른 바람직한 실시예를 도면을 참고로 상세하게 설명한다.Hereinafter, preferred embodiments according to the present invention will be described in detail with reference to the drawings.

본 발명은 방향제 리필용 석고방향제에 관한 것으로, 도 1에 도시한 바와 같이, 상기 석고방향제는 기초 조형재(1)와 알콜(2) 및 오일(3)을 포함하고, 여기에 색소를 첨가하여 이루어진다.The present invention relates to a gypsum aroma agent for refracting a fragrance. As shown in Fig. 1, the gypsum aroma agent comprises a base molding material 1, an alcohol 2 and an oil 3, and a pigment is added thereto.

상기 기초 조형재(1)는 도 2에 도시한 바와 같이, 일정크기의 입도를 가지는 일정량의 석고분(4)과; 일정량의 화선지를 일정량의 물에 불리는 화선지액(5)과; 일정량의 화장솜(6)을 포함하여 이루어진다.As shown in FIG. 2, the foundation primer 1 comprises a predetermined amount of gypsum powder 4 having a predetermined particle size; (5) which is called a predetermined amount of water, And a certain amount of cosmetic cotton (6).

상기 알콜(2)은 공업용 메틸알콜을 사용하고, 오일(3)은 과일 또는 식물로부터 추출된 천연 에센스 오일을 사용하도록 한다.The alcohol (2) is an industrial methyl alcohol and the oil (3) is a natural essence oil extracted from fruits or plants.

상기 석고분(4)은 입자크기 230 ~ 260 메쉬의 조형용 석고가루를 사용하고, 화선지액(5)을 형성하는 화선지는 닥나무로 제조된 연습용 박지를 사용하며, 화장솜(6)은 면 100%의 통상적인 화장용 솜을 사용한다.The gypsum powder 4 is used for molding gypsum powder having a particle size of 230 to 260 mesh and the foil paper for forming the foil liquor 5 is made of mulberry paper. Of a conventional cosmetic cotton.

또한 상기 기초 조형재(1)에 포함되는 석고분(4)은 석고방향제 전체 중량을 기준으로 60 내지 65중량%를 포함시켜 일정한 모양으로 성형하되, 방향제가 충분히 흡수되고 보존되면서 향이 발산되도록 하며, 화선지액(5)은 석고방향제 전체 중량을 기준으로 25 내지 35중량%를 포함시켜 조형물에 방향제가 흡수되면서 석고재로 이루어지는 석고방향제에 인성을 부가하여 취성을 감소시키도록 하고, 화장솜(6)은 석고방향제 전체 중량을 기준으로 0.5 내지 1.0중량%를 함유시켜 석고방향제에 뿌려져서 흡수되는 방향제의 건조 시간이 지연되도록 한다.The gypsum powder (4) contained in the foundation molding material (1) contains 60 to 65% by weight based on the total weight of the gypsum fragrance and is shaped into a predetermined shape so that the fragrance is sufficiently absorbed and preserved, The liquid 5 contains 25 to 35% by weight based on the total weight of the gypsum aroma so that the fragrance is absorbed into the molding and tritium is added to the gypsum fragrance to reduce brittleness, 0.5% to 1.0% by weight based on the total weight of the gypsum fragrance is sprayed onto the gypsum fragrance to delay the drying time of the absorbed fragrance.

그리고 상기 기초 조형재(1)와 혼합하는 알콜(2)은 석고방향제 전체 중량을 기준으로 1.5 내지 2.5중량%을 포함시켜 기초 조형재를 혼합할 때 부드러우면서 석고방향제 내부에 기포 발생이 방지되도록 하고, 오일(3)은 석고방향제 전체 중량을 기준으로 3.5 내지 4.5중량%를 혼합하여 혼합된 석고방향제 건조시간이 단축되도록 한다. 상기 색소는 색상 구현이 가능한 정도의 미량을 포함한다.The alcohol (2) to be mixed with the basic molding material (1) contains 1.5 to 2.5% by weight based on the total weight of the gypsum aroma agent, so that when the basic molding material is mixed, bubbles are prevented from being generated inside the gypsum aroma agent, The oil (3) is mixed with 3.5 to 4.5% by weight based on the total weight of the gypsum fragrance to shorten the drying time of the mixed gypsum fragrance. The coloring matter contains a trace amount of such a degree that color rendering is possible.

보다 구체적인 실시예로서 기초 조형재에 100g의 석고분(4)을 포함하는 경우, 화선지액(5)은 45g, 화장솜(6)은 1g을 포함시켜 기초 조형재(1)를 형성하고, 여기에 알콜(2)은 3g, 오일(3) 6g과 미량의 색소를 혼합하여 총 155g의 석고방향제가 형성되도록 한다.In a more specific embodiment, when the base molding material contains 100 g of the gypsum powder 4, the base molding material 1 is formed by including 45 g of the phosphorus pentoxide solution 5 and 1 g of the cosmetic cotton 6, 3g of oil (2), 6g of oil (3) and a trace amount of pigment are mixed to form a total of 155g of gypsum aroma agent.

상기 석고분(4)을 석고방향제 전체 중량을 기준으로 60 내지 65중량%를 포함시켜 석고방향제를 형성하고 방향제 3g을 뿌려주면 향 발산기간이 10 ~ 15일 지속된다. When the gypsum powder (4) is contained in an amount of 60 to 65% by weight based on the total weight of the gypsum fragrance, a gypsum fragrance is formed, and 3 g of the fragrance is sprayed.

그러나 석고분(4)을 60중량% 미만인 59중량%를 포함시켜 석고방향제를 형성하고 방향제 3g을 뿌려주면, 방향제가 흡수되는 기본 재료가 부족하여 향을 발산시키는 시간이 8일 내지 9일로 감축되고, 석고분(4)을 65중량%를 초과하여 66중량%를 포함시켜 석고방향제를 형성하고 방향제 3g을 뿌려주면, 방향제가 흡수되는 기본 재료가 지나치게 많아 쉽게 건조되기 때문에 향 발산기간이 5 ~ 7일 정도 지속된다. 특히 석고분(4)을 65중량% 초과하여 포함시키는 경우 향 발산기간 10 ~ 15일 유지시키기 위해서는 방향제를 적어도 6g 이상을 뿌려주어야 한다.However, when the gypsum fragrance (4) is contained in an amount of less than 60% by weight and 59% by weight is formed to form a gypsum fragrance and 3 g of the fragrance is sprayed, the time required for the fragrance to dissipate is shortened to 8 days to 9 days , And the gypsum powder (4) is contained in an amount of more than 65 wt% to 66 wt% to form a gypsum fragrance, and 3 g of the fragrance is sprayed, the fragrance dispersion period is 5 to 7 It lasts for about a day. In particular, when the gypsum powder (4) is contained in an amount exceeding 65% by weight, at least 6 g of a fragrance should be sprayed to maintain the fragrance period of 10 to 15 days.

상기 화선지액(5)은 석고방향제 전체 중량의 20중량% 내지 35중량%를 포함시켜 방향제 리필용 조형물을 형성하고, 석고방향제에 70kg/cm²의 하중을 가하여 압축강도를 실험하면, 실험대상의 10 ~ 20%가 부서지거나 깨지는 현상이 발생된다. 즉 석고방향제 10개 제조하여 실험하면 그 중 1개 또는 2개가 부서지거나 깨지는 것이다.When the compressive strength was tested by applying a load of 70 kg / cm ^{2 to} the gypsum fragrance agent, 10 g of the target 10 ~ 20% are broken or cracked. That is, when 10 gypsum fragrances are manufactured and tested, one or two of them are broken or broken.

그러나 기초 조형재 전체를 석고분으로 형성하는 경우에는 위 하중 조건에서 실험대상 석고방향제의 90 ~ 95%에 부서짐 또는 깨짐이 발생되고, 상기 화선지액을 20중량% 미만인 19중량% 포함시키는 경우에는 실험대상 석고방향제의 70% 이상에서 부서짐 또는 깨짐이 발생되며, 화선지액을 35중량%를 초과하여 36중량%를 포함시키는 경우에도 실험대상 석고방향제의 70% 이상에서 부서짐 또는 깨짐이 발생된다.However, in the case of forming the whole of the basic molding material by gypsum, crushing or cracking occurs in 90 to 95% of the gypsum fragrance under the above load conditions, and when 19 wt% Breakage or cracking occurs in 70% or more of the gypsum fragrance, and even when the phosphorus liquor is contained in an amount of more than 35% by weight and 36% by weight, breakage or breakage occurs in 70% or more of the gypsum fragrance to be tested.

이처럼 상기 화선지액(5)을 20중량% 미만을 포함시킨 경우 석고분과 혼합 결합이 이루어지는 화선지액의 포함량이 적기 때문에 인성이 떨어져 쉽게 부서지거나 깨지고, 35중량%를 초과하여 포함시킨 경우에는 화선지액 포함량이 지나치게 많아 석고와 혼합시 결집력이 떨어지기 때문에 20중량% 미만을 포함시키는 경우와 동일하게 부서짐 또는 깨짐 발생량이 증가하게 되는 것이다.If less than 20% by weight of the phosphorus liquor (5) is contained, the toughness is easily broken and broken because the amount of the phosphorus liquor mixed with the gypsum powder is small. When the phosphorus liquor is contained in an amount exceeding 35% by weight, The aggregation force is lowered when mixed with gypsum. Therefore, as in the case of containing less than 20% by weight, the amount of cracking or cracking is increased.

따라서 상기 기초 조형재(1)에 화선지액(4)을 20중량% 내지 35중량%를 포함시켜 석고분이 인성을 가지도록 함으로써, 석고방향제에 하중이 가해지거나 높은 곳에서 낙하하더라도 부서지거나 깨지거나 현상이 현저하게 낮아지는 것이다.Therefore, by making the gypsum powder toughness by including 20% by weight to 35% by weight of the phosphoric acid solution (4) in the foundation molding material (1), even if a load is applied to the gypsum fragrance or when it falls from a high place, It is remarkably low.

또한 본 발명은 석고방향제에 흡수시킨 방향제의 건조 시간이 지연되도록 상기 기초 조형재(1)에 화장솜(6)을 0.5 내지 1.0중량%를 포함시키는데, 이를 통해 향 발산기간은 10 ~ 15일 지속된다. 석고방향제에 뿌려서 흡수시키는 향은 3g이다.In addition, the present invention includes 0.5 to 1.0 wt% cosmetic cotton (6) in the basic molding material (1) so that the drying time of the aromatic material absorbed in the gypsum aromatic material is delayed, . The fragrance to be absorbed by the gypsum fragrance is 3g.

그러나 상기 화장솜(6)을 0.5g 미만인 0.4g을 포함시키고 3g의 향을 뿌려서 흡수시키면 기초 조형재에 포함되는 화장솜의 량이 적어 석고방향제가 쉽게 건조하기 때문에 향 발산기간은 7 ~ 9일에 그치게 된다. 또한 화장솜(6)을 1.0g을 초과하여 1.1g을 혼합하면 5 ~ 7일 향이 발산되는데, 이는 석고분에 포함되는 화장솜의 량이 많아져 석고방향제 몸체의 통기성이 증가하여 쉽게 건조하기 때문이다.However, when 0.4 g of the cosmetic cotton (6) is contained in an amount of 0.4 g, and 3 g of fragrance is sprayed and absorbed, the amount of the cosmetic cotton contained in the basic molding material is small and the gypsum fragrance easily dries. do. Also, when 1.1 g of 1.0 g or more of cosmetic cotton 6 is mixed, the fragrance of 5 to 7 days is diverted because the amount of cosmetic cotton contained in the gypsum powder is increased to increase the breathability of the gypsum fragrance body, .

상기 알콜(2)은 기초 조형재(1)에 1.5 내지 2.5중량%을 혼합시키는데, 이는 기초 조형재를 혼합할 때 부드러우면서 조형물 내부에 기포가 발생되지 않도록 하는 것으로, 상기 기초 조형재에 알콜을 전혀 혼합하지 않고 방향제 리필용 석고방향제를 형성할 경우 석고방향제 몸체에는 석고가 굳으면서 석고방향제 체적의 5 ~ 10%에 해당하는 기포가 석고방향제 내부 및 외부에 분포되어 발생된다.The alcohol (2) is mixed with the basic molding material (1) in an amount of 1.5 to 2.5% by weight, which softens when mixing the basic molding material and prevents bubbles from being generated in the molding material. When a gypsum fragrance is formed without a gypsum, the gypsum in the gypsum fragrance body is hardened and bubbles corresponding to 5 ~ 10% of the volume of gypsum fragrance are distributed inside and outside the gypsum fragrance.

본 발명은 기초 조형재에 1.5 내지 2.5중량%의 알콜(2)을 기초 조형재(1)와 혼합하여 석고방향제를 형성하는 것으로서, 이로 인해 석고방향제 체적의 2% 미만의 기포가 발생될 뿐이어서 석고방향제의 전체적인 외면을 매끈하게 형성할 수 있게 된다.In the present invention, 1.5 to 2.5% by weight of alcohol (2) is mixed with a basic molding material (1) to form a gypsum aromatizing agent, whereby bubbles of less than 2% of the gypsum aroma volume are generated, It is possible to smoothly form the entire outer surface of the semiconductor device.

그러나 기초 조형재(1)에 1.5중량% 미만인 1.4중량%의 알콜(2)을 혼합하면 기초 조형재에 함유되는 알콜량이 적기 때문에 기포 발생을 억제하지 못하여 석고방향제 체적의 4 ~ 5%의 기포가 발생되고, 2.5중량%를 초과한 2.6중량%의 알콜을 혼합하면 함유되는 알콜이 지나치게 많아 기초 조형재의 온도가 빠르게 낮아짐에 따라 기포발생은 큰 폭으로 감소되지만 취성이 증가하여 쉽게 파손되는 현상이 발생된다.However, when 1.4% by weight of alcohol (2), which is less than 1.5% by weight, is mixed in the basic molding material (1), the amount of alcohol contained in the basic molding material is small so that bubble generation can not be suppressed and bubbles of 4-5% And 2.6 wt% of alcohol exceeding 2.5 wt% are mixed together, the amount of alcohol contained in the mixture is too much, so that the temperature of the base molding material is rapidly lowered, the bubble generation is greatly reduced but the brittleness is increased.

상기 오일(3)은 3.5 내지 4.5중량%를 기초 조형재와 혼합하도록 한다. 그리고 기초 조형재를 평균 두께 5cm의 석고방향제로 제조하면, 상기 석고방향제가 굳는 시간은 상온에서 일반적인 경우에 비해 20 ~ 30분 단축된다. 오일을 사용하지 않고 석고방향제를 제조하는 경우 굳는 시간은 통상적으로 2 ~ 3 시간이 소요된다.The oil (3) is mixed with 3.5 to 4.5% by weight of the basic molding material. When the basic molding material is made of a gypsum aromatic material having an average thickness of 5 cm, the solidifying time of the gypsum aromatic material is shortened by 20 to 30 minutes at room temperature, as compared with the ordinary case. In the case of producing gypsum fragrance without using oil, the solidification time usually takes 2 to 3 hours.

상기 오일(3)을 3.5중량% 미만인 3.4중량%를 혼합하는 경우에는 동일한 조건에서 석고방향제의 굳는 시간이 통상적인 경우보다 10분미만 단축되고 4.5중량%를 초과하는 4.6중량%를 혼합하면, 굳는 시간이 오일이 지나치게 많이 포함되어 굳는 시간이 통상적인 경우보다 5분미만 단축된다.When 3.4 wt% of the oil (3) is mixed with less than 3.5 wt%, the hardening time of the gypsum fragrance under the same conditions is shorter than 10 min and the mixing of 4.6 wt% exceeding 4.5 wt% The time is too short for the oil to get harder and harder than 5 minutes.

정리하면, 본 발명은 석고분(4) 60 내지 65중량%와, 화선지액(5) 25 내지 35중량%와, 화장솜(6) 0.5 내지 1.0중량%를 혼합하여 기초 조형재를 형성하며, 상기 기초 조형재를 알콜(2) 1.5 내지 2.5중량%와 오일(3) 3.5 내지 4.5중량%와 미량의 색소를 혼합하여 도 3에 도시한 바와 같이 다양한 모양을 가지는 몰드(7)에 채워넣어 성형한다.In summary, the present invention relates to a method for forming a base molding material by mixing 60 to 65% by weight of gypsum powder (4), 25 to 35% by weight of phosphorus pentad liquid (5) and 0.5 to 1.0% The basic molding material is mixed with 1.5 to 2.5% by weight of the alcohol (2) and 3.5 to 4.5% by weight of the oil (3) and a small amount of pigment is mixed with the mold (7) having various shapes as shown in Fig.

그리고 몰드에서 성형된 석고방향제를 빼내어 굳힌 다음, 여기에 반복적으로 방향제를 뿌려 향을 흡착 저장시킴으로써 반영구적으로 장기간에 걸쳐 향을 발산시킬 수 있는 방향제 리필용 석고방향제를 제공할 수 있게 되는 것이다.It is also possible to provide a gypsum aroma agent for refracting a fragrance which is able to emit a fragrance over a long period of time by adsorbing and storing the fragrance of the gypsum fragrance formed in the mold and spraying the fragrant fragrance repeatedly thereafter.

1 : 기초 조형재 2 : 알콜
3 : 오일 4 : 석고분
5 : 화선지액 6 : 화장솜
7 : 몰드1: Basic molding material 2: Alcohol
3: oil 4: gypsum powder
5: Phosphorus solution 6: Cosmetic cotton
7: Mold

Claims

In the gypsum fragrance for fragrance,
Wherein the gypsum aroma agent comprises a basic molding material, an alcohol and an oil, and a coloring matter added thereto.

The method according to claim 1,
Wherein the basic molding material comprises a predetermined amount of gypsum powder having a predetermined size and a predetermined amount of a predetermined amount of water, and a predetermined amount of water and a certain amount of cosmetic cotton.

The method according to claim 1,
The alcohol comprises from 1.5 to 2.5% by weight, based on the total weight of the gypsum fragrance,
Wherein the oil comprises 3.5 to 4.5 wt% based on the total weight of the gypsum fragrance.

3. The method of claim 2,
The gypsum powder was formed from gypsum powder having a particle size of 230 to 260 mesh,
The orange paper included in the orange paper liquor is formed of a training paper made of mulberry tree,
Wherein the cosmetic cotton is formed from 100% cotton cosmetic cotton.

5. The method of claim 4,
The gypsum powder comprises 60 to 65 wt% based on the total weight of the gypsum fragrance,
The gypsum liquid comprises 25 to 35% by weight, based on the total weight of the gypsum fragrance,
Wherein the cosmetic cotton comprises 0.5 to 1.0 wt.%, Based on the total weight of the gypsum fragrance, of the gypsum fragrance.