KR20140085400A - 유기광전소자용 화합물 및 이를 포함하는 유기광전소자 - Google Patents

유기광전소자용 화합물 및 이를 포함하는 유기광전소자 Download PDF

Info

Publication number
KR20140085400A
KR20140085400A KR1020140064737A KR20140064737A KR20140085400A KR 20140085400 A KR20140085400 A KR 20140085400A KR 1020140064737 A KR1020140064737 A KR 1020140064737A KR 20140064737 A KR20140064737 A KR 20140064737A KR 20140085400 A KR20140085400 A KR 20140085400A
Authority
KR
South Korea
Prior art keywords
group
substituted
unsubstituted
chemical formula
carbon atoms
Prior art date
Application number
KR1020140064737A
Other languages
English (en)
Inventor
김형선
유은선
강의수
김영훈
민수현
이호재
채미영
Original Assignee
제일모직주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 제일모직주식회사 filed Critical 제일모직주식회사
Priority to KR1020140064737A priority Critical patent/KR20140085400A/ko
Publication of KR20140085400A publication Critical patent/KR20140085400A/ko

Abstract

유기광전소자용 화합물 및 이를 포함하는 유기광전소자에 관한 것으로, 상기 유기광전소자용 화합물은 하기 화학식 1로 표시되는 것을 제공한다.
[화학식 1]
Figure pat00127

상기 화학식 1에서 Ar1 내지 Ar4 및 R1 내지 R4의 정의는 명세서에 기재된 바와 같다. 상기 유기광전소자용 화합물을 이용하면, 열적/전기화학적 안정성 및 수명, 효율이 우수한 유기광전소자를 제공할 수 있다.

Description

유기광전소자용 화합물 및 이를 포함하는 유기광전소자{Compound for organic photoelectric device and organic photoelectric device including the same}
수명, 효율, 전기화학적 안정성 및 열적 안정성이 우수한 유기광전소자를 제공할 수 있는 유기광전소자용 화합물 및 이를 포함하는 유기광전소자에 관한 것이다.
유기 광전 소자(organic photoelectric device)라 함은 정공 또는 전자를 이용한 전극과 유기물 사이에서의 전하 교류를 필요로 하는 소자를 의미한다.
유기 광전 소자는 동작 원리에 따라 하기와 같이 크게 두 가지로 나눌 수 있다. 첫째는 외부의 광원으로부터 소자로 유입된 광자에 의하여 유기물층에서 엑시톤(exciton)이 형성되고 이 엑시톤이 전자와 정공으로 분리되고, 이 전자와 정공이 각각 다른 전극으로 전달되어 전류원(전압원)으로 사용되는 형태의 전자소자이다.
둘째는 2 개 이상의 전극에 전압 또는 전류를 가하여 전극과 계면을 이루는 유기물 반도체에 정공 또는 전자를 주입하고, 주입된 전자와 정공에 의하여 동작하는 형태의 전자소자이다.
유기 광전 소자의 예로는 유기광전소자, 유기태양전지, 유기 감광체 드럼(organic photo conductor drum), 유기 트랜지스터 등이 있으며, 이들은 모두 소자의 구동을 위하여 정공의 주입 또는 수송 물질, 전자의 주입 또는 수송 물질, 또는 발광 물질을 필요로 한다.
특히, 유기광전소자(organic light emitting diodes, OLED)는 최근 평판 디스플레이(flat panel display)의 수요가 증가함에 따라 주목받고 있다. 일반적으로 유기 발광 현상이란 유기 물질을 이용하여 전기에너지를 빛에너지로 전환시켜주는 현상을 말한다.
이러한 유기광전소자는 유기발광재료에 전류를 가하여 전기에너지를 빛으로 전환시키는 소자로서 통상 양극(anode)과 음극(cathode) 사이에 기능성 유기물 층이 삽입된 구조로 이루어져 있다. 여기서 유기물층은 유기광전소자의 효율과 안정성을 높이기 위하여 각기 다른 물질로 구성된 다층의 구조로 이루어진 경우가 많으며, 예컨대 정공주입층, 정공수송층, 발광층, 전자수송층, 전자주입층 등으로 이루어질 수 있다.
이러한 유기광전소자의 구조에서 두 전극 사이에 전압을 걸어주게 되면 양극에서는 정공(hole)이, 음극에서는 전자(electron)가 유기물층에 주입되게 되고, 주입된 정공과 전자가 만나 재결합(recombination)에 의해 에너지가 높은 여기자를 형성하게 된다. 이때 형성된 여기자가 다시 바닥상태(ground state)로 이동하면서 특정한 파장을 갖는 빛이 발생하게 된다.
1987년 이스트만 코닥(Eastman Kodak)사에서는 발광층 형성용 재료로서 저분자인 방향족 디아민과 알루미늄 착물을 이용하고 있는 유기 EL 소자를 처음으로 개발하였고(Appl. Phys. Lett. 51, 913, 1987), 유기 전계 발광 소자에 대해서는 1987년에 C. W. Tang 등이 최초로 실용적인 성능을 가진 소자를 보고하였다 (AppliedPhysics Letters, 51(12), 913-915, 1987년).
상기 문헌은 유기층으로서 디아민 유도체의 박막(정공 수송층)과 트리스(8-하이드록시-퀴놀레이트)알루미늄(tris(8-hydroxy-quinolate)aluminum, Alq3)의 박막을 적층한 구조를 기재하고 있다.
최근에는, 형광 발광물질뿐 아니라 인광 발광물질도 유기 광전 소자의 발광물질로 사용될 수 있음이 알려졌으며(D. F.O'Brien 등, Applied Physics Letters, 74(3), 442-444, 1999; M. A. Baldo 등, Applied Physics letters, 75(1), 4-6, 1999), 이러한 인광 발광은 바닥상태(ground state)에서 여기상태(excited state)로 전자가 전이한 후, 계간 전이(intersystem crossing)를 통해 단일항 여기자가 삼중항 여기자로 비발광 전이된 다음, 삼중항 여기자가 바닥상태로 전이하면서 발광하는 메카니즘으로 이루어진다.
상기한 바와 같이 유기광전소자에서 유기물층으로 사용되는 재료는 기능에 따라, 발광 재료와 전하 수송 재료, 예컨대 정공주입 재료, 정공수송 재료, 전자수송 재료, 전자주입 재료 등으로 분류될 수 있다.
또한, 발광 재료는 발광색에 따라 청색, 녹색, 적색 발광재료와 보다 나은 천연색을 구현하기 위해 필요한 노란색 및 주황색 발광 재료로 구분될 수 있다.
한편, 발광 재료로서 하나의 물질만 사용하는 경우 분자간 상호 작용에 의하여 최대 발광 파장이 장파장으로 이동하고 색순도가 떨어지거나 발광 감쇄 효과로 소자의 효율이 감소되는 문제가 발생하므로, 색순도의 증가와 에너지 전이를 통한 발광 효율과 안정성을 증가시키기 위하여 발광 재료로서 호스트/도판트 계를 사용할 수 있다.
유기광전소자가 전술한 우수한 특징들을 충분히 발휘하기 위해서는 소자 내 유기물층을 이루는 물질, 예컨대 정공주입 물질, 정공수송 물질, 발광 물질, 전자수송 물질, 전자주입 물질, 발광 재료 중 호스트 및/또는 도판트 등이 안정하고 효율적인 재료에 의하여 뒷받침되는 것이 선행되어야 하며, 아직까지 안정하고 효율적인 유기광전소자용 유기물층 재료의 개발이 충분히 이루어지지 않은 상태이며, 따라서 새로운 재료의 개발이 계속 요구되고 있다. 이와 같은 재료 개발의 필요성은 전술한 다른 유기 광전 소자에서도 마찬가지이다.
발광, 또는 전자 주입 및 수송역할을 할 수 있고, 적절한 도펀트와 함께 발광 호스트로서의 역할을 할 수 있는 유기광전소자용 화합물을 제공한다.
수명, 효율, 구동전압, 전기화학적 안정성 및 열적 안정성이 우수한 유기광전소자를 제공하고자 한다.
본 발명의 일 측면에서는, 하기 화학식 1로 표시되는 유기광전소자용 화합물을 제공한다.
[화학식 1]
Figure pat00001
상기 화학식 1에서, Ar1 및 Ar2는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, Ar3 및 Ar4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, R1 내지 R4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
상기 유기광전소자용 화합물은 하기 화학식 2로 표시될 수 있다.
[화학식 2]
Figure pat00002
상기 화학식 2에서, Ar1 및 Ar2는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, Ar3 및 Ar4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, R1 내지 R4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
상기 유기광전소자용 화합물은 하기 화학식 3로 표시될 수 있다.
[화학식 3]
Figure pat00003
상기 화학식 3에서, Ar1 및 Ar2는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, Ar3 및 Ar4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, R1 내지 R4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
상기 유기광전소자용 화합물은 하기 화학식 4로 표시될 수 있다.
[화학식 4]
Figure pat00004
상기 화학식 4에서, Ar2 및 Ar5는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, Ar3, Ar4 및 Ar6은 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, R1 내지 R6는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
상기 유기광전소자용 화합물은 하기 화학식 5로 표시될 수 있다.
[화학식 5]
Figure pat00005
상기 화학식 5에서, Ar2 및 Ar5는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, Ar3, Ar4 및 Ar6은 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있고, R1 내지 R6는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
상기 Ar5는 탄소수 6 내지 12의 아릴기일 수 있고, 상기 Ar2는 탄소수 10 내지 20의 융합 링 폴리시클릭기일 수 있다.
상기 Ar5는 탄소수 6 내지 12의 아릴기일 수 있고, 상기 Ar2는 탄소수 6 내지 30의 치환 또는 비치환된 아릴아민기, 탄소수 6 내지 30의 치환 또는 비치환된 아미노아릴기, 치환 또는 비치환된 카바졸기, 치환 또는 비치환된 피리딘기, 치환 또는 비치환된 피리미딘기 및 치환 또는 비치환된 트리아진기로 이루어진 군에서 선택될 수 있다.
상기 Ar5는 탄소수 6 내지 12의 아릴기일 수 있고, 상기 Ar2는 탄소수 10 내지 20의 융합 링 폴리시클릭기일 수 있다.
상기 Ar5는 탄소수 6 내지 12의 아릴기일 수 있고, 상기 Ar2는 탄소수 6 내지 30의 치환 또는 비치환된 아릴아민기, 탄소수 6 내지 30의 치환 또는 비치환된 아미노아릴기, 치환 또는 비치환된 카바졸기, 치환 또는 비치환된 피리딘기, 치환 또는 비치환된 피리미딘기 및 치환 또는 비치환된 트리아진기로 이루어진 군에서 선택될 수 있다.
본 발명의 다른 측면에서는, 양극, 음극 및 상기 양극과 음극 사이에 개재되는 적어도 한 층 이상의 유기박막층을 포함하는 유기광전소자에 있어서, 상기 유기박막층 중 적어도 어느 한 층은 전술한 유기광전소자용 화합물을 포함하는 유기광전소자를 제공한다.
상기 유기박막층은 발광층, 정공수송층, 정공주입층, 전자수송층, 전자주입층, 정공차단층 및 이들의 조합을 이루어진 군에서 선택될 수 있다.
상기 유기광전소자용 화합물은 전자수송층 또는 전자주입층 내에 포함될 수 있다.
상기 유기광전소자용 화합물은 발광층 내에 포함될 수 있다.
상기 유기광전소자용 화합물은 발광층 내에 인광 또는 형광 호스트 재료로서 사용될 수 있다.
상기 유기 광전 소자용 화합물은 발광층 내에 형광 청색 도펀트 재료로서 사용될 수 있다.
상기 유기광전소자는 유기 발광 소자, 유기 태양 전지, 유기 트랜지스터, 유기 감광체 드럼 및 유기 메모리 소자로 이루어진 군에서 선택될 수 있다.
본 발명의 또 다른 측면에서는, 전술한 유기광전소자를 포함하는 표시장치를 제공한다.
우수한 전기화학적 및 열적 안정성으로 수명 특성이 우수하고, 낮은 구동전압에서도 높은 발광효율을 가지는 유기광전소자를 제공할 수 있다.
도 1 내지 도 5는 본 발명의 일 구현예에 따른 유기광전소자용 화합물을 이용하여 제조될 수 있는 유기광전소자에 대한 다양한 구현예들을 나타내는 단면도이다.
<도면의 주요 부분에 대한 부호의 설명>
100 : 유기광전소자 110 : 음극
120 : 양극 105 : 유기박막층
130 : 발광층 140 : 정공 수송층
150 : 전자수송층 160 : 전자주입층
170 : 정공주입층 230 : 발광층 + 전자수송층
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구범위의 범주에 의해 정의될 뿐이다.
본 명세서에서 "헤테로"란 별도의 정의가 없는 한, 하나의 고리기내에 N, O, S 및 P로 이루어진 군에서 선택되는 헤테로 원자를 1 내지 3개 함유하고, 나머지는 탄소인 것을 의미한다.
본 명세서에서 "이들의 조합"이란 별도의 정의가 없는 한, 둘 이상의 치환기가 연결기로 결합되어 있거나, 둘 이상의 치환기가 축합하여 결합되어 있는 것을 의미한다.
본 명세서에서 "알킬(alkyl)"이란 별도의 정의가 없는 한, 지방족 탄화수소 그룹을 의미한다. 알킬 부위는 어떠한 알켄이나 알킨 부위를 포함하고 있지 않음을 의미하는 "포화 알킬(saturated alkyl)" 그룹일 수 있다. 알킬 부위는 적어도 하나의 알켄 또는 알킨 부위를 포함하고 있음을 의미하는 "불포화 알킬(unsaturated alkyl)" 부위일 수도 있다. "알켄(alkene)" 부위는 적어도 두 개의 탄소원자가 적어도 하나의 탄소-탄소 이중 결합으로 이루어진 그룹을 의미하며, "알킨(alkyne)" 부위는 적어도 두 개의 탄소원자가 적어도 하나의 탄소-탄소 삼중 결합으로 이루어진 그룹을 의미한다. 포화이든 불포화이든 간에 알킬 부위는 분지형, 직쇄형 또는 환형일 수 있다.
알킬 그룹은 1 내지 20 개의 탄소원자를 가질 수 있다. 알킬 그룹은 1 내지 10 개의 탄소원자들을 가지는 중간 크기의 알킬일 수도 있다. 알킬 그룹은 1 내지 6 개의 탄소원자들을 가지는 저급알킬일 수도 있다.
예를 들어, C1-C4 알킬은 알킬쇄에 1 내지 4 개의 탄소원자, 즉, 알킬쇄는 메틸, 에틸, 프로필, 이소-프로필, n-부틸, 이소-부틸, sec-부틸 및 t-부틸로 이루어진 군에서 선택됨을 나타낸다.
전형적인 알킬 그룹에는 메틸, 에틸, 프로필, 이소프로필, 부틸, 이소부틸, t-부틸, 펜틸, 헥실, 에테닐, 프로페닐, 부테닐, 시클로프로필, 시클로부틸, 시클로펜틸, 시클로헥실 등으로부터 개별적으로 그리고 독립적으로 선택된 하나 또는 그 이상의 그룹들로 치환될 수도 있는 그룹임을 의미한다.
용어 "아릴(aryl)"은 공유 파이 전자계를 가지고 있는 적어도 하나의 링을 가지고 있는 카르보시클릭아릴(예를 들어, 페닐)을 포함하는 아릴 그룹을 의미한다. 이 용어는 모노시클릭 또는 융합 링 폴리시클릭(즉, 탄소원자들의 인접한 쌍들을 나눠 가지는 링들) 그룹들을 포함한다. 또한, 이 용어는 하나의 탄소를 접점으로 가지고 있는 스피로(spiro) 화합물을 포함한다.
용어 "헤테로아릴(heteroaryl)"은 공유 파이 전자계를 가지고 있는 적어도 하나의 링을 가지고 있는 헤테로시클릭 아릴(예를 들어, 피리딘)을 포함하는 아릴 그룹을 의미한다. 이 용어는 모노시클릭 또는 융합 링 폴리시클릭(즉, 탄소원자들의 인접한 쌍들을 나눠 가지는 링들) 그룹들을 포함한다. 또한, 이 용어는 하나의 탄소를 접점으로 가지고 있는 스피로(spiro) 화합물을 포함한다.
본 명세서에서 "치환"이란 별도의 정의가 없는 한, 탄소수 1 내지 30의 알킬기, 탄소수 1 내지 10의 알킬실릴기, 탄소수 3 내지 30의 시클로알킬기, 탄소수 6 내지 30의 아릴기, 탄소수 2 내지 30의 헤테로아릴기, 탄소수 1 내지 10의 알콕시기, 플루오로기, 트리플루오로메틸기 등의 탄소수 1 내지 10의 트리플루오로알킬기, 탄소수 12 내지 30의 카바졸기, 탄소수 6 내지 30의 아릴아민기, 탄소수 6 내지 30의 치환 또는 비치환된 아미노아릴기 또는 시아노기로 치환된 것을 의미한다.
본 발명의 일 구현예에 따른 유기광전소자용 화합물은 두 개의 카바졸기가 결합된 코어 부분에 치환기가 선택적으로 결합된 구조를 가진다.
또한, 상기 유기광전소자용 화합물은 코어 부분과 코어 부분에 치환된 치환기에 다양한 또 다른 치환기를 도입함으로써 다양한 에너지 밴드 갭을 갖는 화합물을 합성할 수 있으므로, 전자 주입층 및 전달층뿐만 아니라 발광층에서 요구되는 조건들을 충족시킬 수 있는 화합물들이 될 수 있다.
상기 화합물의 치환기에 따라 적절한 에너지 준위를 갖는 화합물을 유기광전소자에 사용함으로써, 전자전달 능력이 강화되어 효율 및 구동전압 면에서 우수한 효과를 가지고, 전기화학적 및 열적 안정성이 뛰어나 유기광전소자 구동시 수명 특성을 향상시킬 수 있다.
이러한 본 발명의 일 구현예에 따르면, 하기 화학식 1로 표시되는 유기광전소자용 화합물을 제공한다.
[화학식 1]
Figure pat00006
상기 화학식에서, Ar1 및 Ar2는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
또한, Ar3 및 Ar4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
Ar1 내지 Ar4의 파이공액길이(π-conjugation length)를 조절하여 삼중항 에너지 밴드갭을 크게 함으로서 인광호스트로 유기광전소자의 발광층에 매우 유용하게 적용될 수 있다.
R1 내지 R4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
이러한 치환기가 결합된 구조는 열적 안정성 또는 산화에 대한 저항성이 뛰어나, 유기광전소자의 수명 특성을 향상시킬 수 있다.
이 때, 두 개의 카바졸기는 하기 화학식 2 또는 3과 같이 각각의 카바졸의 3번 또는 4번 위치에 결합될 수 있다.
[화학식 2]
Figure pat00007
[화학식 3]
Figure pat00008
상기 화학식 2와 같이 각 카바졸의 3번 위치에 결합된 구조의 경우, 합성이 용이하며, 카바졸의 3번 위치의 수소를 치환함으로서 산화안정성이 높아지는 장점이 있다.
또한, 화학식 3과 같이 각 카바졸의 4번 위치에 결합된 구조의 경우는 두 개의 카바졸이 같은 평면에 있지 않아 결정화 현상을 크게 억제할 수 있으며, 용해도도 그게 증가한다. 또한 파이공액길이가 매우 짧아져서 삼중항 밴드갭이 높은 장점이 있다.
상기 Ar1 내지 Ar4 및 R1 내지 R4는 전술한 바와 같다.
상기와 같은 코어 부분의 구조에서 Ar1은 또 다른 카바졸일 수 있다. 그 예는 하기 화학식 4 또는 5와 같다.
[화학식 4]
Figure pat00009
[화학식 5]
Figure pat00010
상기 화학식에서, Ar2 및 Ar5는 서로 동일하거나 상이하며, 각각 독립적으로 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있으며, Ar3, Ar4 및 Ar6은 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택될 수 있다.
Ar2 내지 Ar6의 파이공액길이(π-conjugation length)를 조절하여 삼중항 에너지 밴드갭을 크게 함으로서 인광호스트로 유기광전소자의 발광층에 매우 유용하게 적용될 수 있으며, 카바졸의 증가로 인해 정공 주입 및 전달 특성이 증가하는 효과를 가져 올 수 있다.
R1 내지 R6는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택된다.
이러한 치환기가 결합된 구조는 열적 안정성 또는 산화에 대한 저항성이 뛰어나, 유기광전소자의 수명 특성을 향상시킬 수 있다.
상기 화학식에서, Ar5는 탄소수 6 내지 12의 아릴기이고, Ar2는 탄소수 10 내지 20의 융합 링 폴리시클릭기일 수 있다.
상기 화학식이 치환기로 융합 링 폴리시클릭기를 가지는 경우 열안정성이 증가하며, 전자 전달 및 주입 특성이 증가하는 장점이 있다.
또한, 상기 화학식에서 Ar5는 탄소수 6 내지 12의 아릴기이고, Ar2는 탄소수 6 내지 30의 치환 또는 비치환된 아릴아민기, 탄소수 6 내지 30의 치환 또는 비치환된 아미노아릴기, 치환 또는 비치환된 카바졸기, 치환 또는 비치환된 피리딘기, 치환 또는 비치환된 피리미딘기 및 치환 또는 비치환된 트리아진기로 이루어진 군에서 선택될 수 있다.
상기와 같은 치환기들 중 정공 전달 특성을 갖는 아릴아민기, 아미노아릴기 또는 카바졸기의 경우는 본 화합물의 정공 주입 및 전달 특성을 향상시키는 효과를 가져올 수 있고, 전자 전달 특성을 갖는 피리미딘기, 트리아진기의 경우는 화합물의 전자 주입 및 전달 특성을 향상시키는 효과를 가져 오는 장점이 있다.
치환기의 개수에 따라 상기 화합물의 전자수송 능력을 조절할 수 있다. 또한, 치환기의 조절로 화합물의 구조를 벌크하게 제조할 수 있으며, 이로 인해 결정화도를 낮출 수 있다. 화합물의 결정화도가 낮아지게 되면 소자의 수명이 길어질 수 있다.
상기 유기광전소자용 화합물은 하기 화학식 6 내지 화학식 83로 표시되는 것을 사용할 수 있다. 그러나 본 발명이 하기 화합물에 한정되는 것은 아니다.
[화학식 6] [화학식 7]
Figure pat00011
Figure pat00012
[화학식 8] [화학식 9]
Figure pat00013
Figure pat00014
[화학식 10] [화학식 11]
Figure pat00015
Figure pat00016
[화학식 12] [화학식 13]
Figure pat00017
Figure pat00018
[화학식 14] [화학식 15]
Figure pat00019
Figure pat00020
[화학식 16] [화학식 17]
Figure pat00021
Figure pat00022
[화학식 18] [화학식 19]
Figure pat00023
Figure pat00024
[화학식 20] [화학식 21]
Figure pat00025
Figure pat00026
[화학식 22] [화학식 23]
Figure pat00027
Figure pat00028
[화학식 24] [화학식 25]
Figure pat00029
Figure pat00030
[화학식 26] [화학식 27]
Figure pat00031
Figure pat00032
[화학식 28] [화학식 29]
Figure pat00033
Figure pat00034
[화학식 30] [화학식 31]
Figure pat00035
Figure pat00036
[화학식 32] [화학식 33]
Figure pat00037
Figure pat00038
[화학식 34] [화학식 35]
Figure pat00039
Figure pat00040
[화학식 36] [화학식 37]
Figure pat00041
Figure pat00042
[화학식 38] [화학식 39] [화학식 40] [화학식 41]
Figure pat00043
Figure pat00044
Figure pat00045
Figure pat00046
[화학식 42] [화학식 43] [화학식 44] [화학식 45]
Figure pat00047
Figure pat00048
Figure pat00049
Figure pat00050
[화학식 46] [화학식 47] [화학식 48] [화학식 49]
Figure pat00051
Figure pat00052
Figure pat00053
Figure pat00054
[화학식 50] [화학식 51] [화학식 52] [화학식 53]
Figure pat00055
Figure pat00056
Figure pat00057
Figure pat00058
[화학식 54] [화학식 55] [화학식 56] [화학식 57]
Figure pat00059
Figure pat00060
Figure pat00061
Figure pat00062
[화학식 58] [화학식 59] [화학식 60] [화학식 61]
Figure pat00063
Figure pat00064
Figure pat00065
Figure pat00066
[화학식 62] [화학식 63] [화학식 64] [화학식 65]
Figure pat00067
Figure pat00068
Figure pat00069
Figure pat00070
[화학식 66] [화학식 67] [화학식 68] [화학식 69]
Figure pat00071
Figure pat00072
Figure pat00073
Figure pat00074
[화학식 70] [화학식 71] [화학식 72]
Figure pat00075
Figure pat00076
Figure pat00077
[화학식 73] [화학식 74] [화학식 75]
Figure pat00078
Figure pat00079
Figure pat00080
[화학식 76] [화학식 77] [화학식 78]
Figure pat00081
Figure pat00082
Figure pat00083
[화학식 79] [화학식 80] [화학식 81]
Figure pat00084
Figure pat00085
Figure pat00086
[화학식 82] [화학식 83]
Figure pat00087
Figure pat00088
상기와 같은 화합물을 포함하는 유기광전소자용 화합물은 유리전이온도가 110℃ 이상이며, 열분해온도가 400℃이상으로 열적 안정성이 우수하다. 이로 인해 고효율의 유기광전소자의 구현이 가능하다.
또한, 상기와 같은 화합물은 적절한 호모 에너지 준위를 가지고 있어, 정공의 주입이 원활하며, 정공과 전자를 모두 잘 전달할 수 있다.
상기와 같은 화합물을 포함하는 유기광전소자용 화합물은 발광, 또는 전자 주입 및/또는 수송역할을 할 수 있으며, 적절한 도판트와 함께 발광 호스트로서의 역할도 할 수 있다. 즉, 상기 유기광전소자용 화합물은 인광 또는 형광의 호스트 재료, 청색의 발광도펀트 재료, 또는 전자수송 재료로 사용될 수 있다.
본 발명의 일 구현예에 따른 유기광전소자용 화합물은 유기박막층에 사용되어 유기광전소자의 수명 특성, 효율 특성, 전기화학적 안정성 및 열적 안정성을 향상시키며, 구동전압을 낮출 수 있다.
이에 따라 본 발명의 일 구현예는 상기 유기광전소자용 화합물을 포함하는 유기광전소자를 제공한다. 이 때, 상기 유기광전소자라 함은 유기광전소자, 유기 태양 전지, 유기 트랜지스터, 유기 감광체 드럼, 유기 메모리 소자 등을 의미한다. 특히, 유기 태양 전지의 경우에는 본 발명의 일 구현예에 따른 유기광전소자용 화합물이 전극이나 전극 버퍼층에 포함되어 양자 효율을 증가시키며, 유기 트랜지스터의 경우에는 게이트, 소스-드레인 전극 등에서 전극 물질로 사용될 수 있다.
이하에서는 유기광전소자에 대하여 구체적으로 설명한다.
본 발명의 다른 일 구현예는 양극, 음극 및 상기 양극과 음극 사이에 개재되는 적어도 한 층 이상의 유기박막층을 포함하는 유기광전소자에 있어서, 상기 유기박막층 중 적어도 어느 한 층은 본 발명의 일 구현예에 따른 유기광전소자용 화합물을 포함하는 유기광전소자를 제공한다.
상기 유기광전소자용 화합물을 포함할 수 있는 유기박막층으로는 발광층, 정공수송층, 정공주입층, 전자수송층, 전자주입층, 정공차단층 및 이들의 조합으로 이루어진 군에서 선택되는 층을 포함할 수 있는 바, 이 중에서 적어도 어느 하나의 층은 본 발명에 따른 유기광전소자용 화합물을 포함한다. 특히, 전자수송층 또는 전자주입층에 본 발명의 일 구현예에 따른 유기광전소자용 화합물을 포함할 수 있다. 또한, 상기 유기광전소자용 화합물이 발광층 내에 포함되는 경우 상기 유기광전소자용 화합물은 인광 또는 형광호스트로서 포함될 수 있고, 특히, 형광 청색 도펀트 재료로서 포함될 수 있다.
도 1 내지 도 5는 본 발명의 일 구현예에 따른 유기광전소자용 화합물을 포함하는 유기광전소자의 단면도이다.
도 1 내지 도 5를 참조하면, 본 발명의 일 구현예에 따른 유기광전소자(100, 200, 300, 400 및 500)는 양극(120), 음극(110) 및 이 양극과 음극 사이에 개재된 적어도 1층의 유기박막층(105)을 포함하는 구조를 갖는다.
상기 양극(120)은 양극 물질을 포함하며, 이 양극 물질로는 통상 유기박막층으로 정공주입이 원활할 수 있도록 일함수가 큰 물질이 바람직하다. 상기 양극 물질의 구체적인 예로는 니켈, 백금, 바나듐, 크롬, 구리, 아연, 금과 같은 금속 또는 이들의 합금을 들 수 있고, 아연산화물, 인듐산화물, 인듐주석산화물(ITO), 인듐아연산화물(IZO)과 같은 금속 산화물을 들 수 있고, ZnO와 Al 또는 SnO2와 Sb와 같은 금속과 산화물의 조합을 들 수 있고, 폴리(3-메틸티오펜), 폴리[3,4-(에틸렌-1,2-디옥시)티오펜](polyehtylenedioxythiophene: PEDT), 폴리피롤 및 폴리아닐린과 같은 전도성 고분자 등을 들 수 있으나, 이에 한정되는 것은 아니다. 바람직하게는 상기 양극으로 ITO(indium tin oxide)를 포함하는 투명전극을 사용할 수 있다.
상기 음극(110)은 음극 물질을 포함하여, 이 음극 물질로는 통상 유기박막층으로 전자주입이 용이하도록 일 함수가 작은 물질인 것이 바람직하다. 음극 물질의 구체적인 예로는 마그네슘, 칼슘, 나트륨, 칼륨, 타이타늄, 인듐, 이트륨, 리튬, 가돌리늄, 알루미늄, 은, 주석, 납, 세슘, 바륨 등과 같은 금속 또는 이들의 합금을 들 수 있고, LiF/Al, LiO2/Al, LiF/Ca, LiF/Al 및 BaF2/Ca과 같은 다층 구조 물질 등을 들 수 있으나, 이에 한정되는 것은 아니다. 바람직하게는 상기 음극으로 알루미늄 등과 같은 금속전극을 사용할 수 있다.
먼저 도 1을 참조하면, 도 1은 유기박막층(105)으로서 발광층(130)만이 존재하는 유기광전소자(100)를 나타낸 것으로, 상기 유기박막층(105)은 발광층(130)만으로 존재할 수 있다.
도 2를 참조하면, 도 2는 유기박막층(105)으로서 전자수송층을 포함하는 발광층(230)과 정공수송층(140)이 존재하는 2층형 유기광전소자(200)를 나타낸 것으로, 도 2에 나타난 바와 같이, 유기박막층(105)은 발광층(230) 및 정공 수송층(140)을 포함하는 2층형일 수 있다. 이 경우 발광층(130)은 전자 수송층의 기능을 하며, 정공 수송층(140)은 ITO와 같은 투명전극과의 접합성 및 정공수송성을 향상시키는 기능을 한다.
도 3을 참조하면, 도 3은 유기박막층(105)으로서 전자수송층(150), 발광층(130) 및 정공수송층(140)이 존재하는 3층형 유기광전소자(300)로서, 상기 유기박막층(105)에서 발광층(130)은 독립된 형태로 되어 있고, 전자수송성이나 정공수송성이 우수한 막(전자수송층(150) 및 정공수송층(140))을 별도의 층으로 쌓은 형태를 나타내고 있다.
도 4를 참조하면, 도 4는 유기박막층(105)으로서 전자주입층(160), 발광층(130), 정공수송층(140) 및 정공주입층(170)이 존재하는 4층형 유기광전소자(400)로서, 상기 정공주입층(170)은 양극으로 사용되는 ITO와의 접합성을 향상시킬 수 있다.
도 5를 참조하면, 도 5는 유기박막층(105)으로서 전자주입층(160), 전자수송층(150), 발광층(130), 정공수송층(140) 및 정공주입층(170)과 같은 각기 다른 기능을 하는 5개의 층이 존재하는 5층형 유기광전소자(500)를 나타내고 있으며, 상기 유기광전소자(500)는 전자주입층(160)을 별도로 형성하여 저전압화에 효과적이다.
상기 도 1 내지 도 5에서 상기 유기박막층(105)을 이루는 전자 수송층(150), 전자 주입층(160), 발광층(130, 230), 정공 수송층(140), 정공 주입층(170) 및 이들의 조합으로 이루어진 군에서 선택되는 어느 하나는 상기 유기광전소자용 화합물을 포함한다. 이 때 상기 유기광전소자용 화합물은 상기 전자 수송층(150) 또는 전자주입층(160)을 포함하는 전자수송층(150)에 사용될 수 있으며, 그중에서도 전자수송층에 포함될 경우 정공 차단층(도시하지 않음)을 별도로 형성할 필요가 없어 보다 단순화된 구조의 유기광전소자를 제공할 수 있어 바람직하다.
또한, 상기 유기 광전 소자용 화합물이 발광층(130, 230) 내에 포함되는 경우 상기 유기 광전 소자용 화합물은 인광 또는 형광호스트로서 포함될 수 있으며, 또는 형광 청색 도펀트로서 포함될 수 있다.
상기에서 설명한 유기광전소자는, 기판에 양극을 형성한 후, 진공증착법(evaporation), 스퍼터링(sputtering), 플라즈마 도금 및 이온도금과 같은 건식성막법; 또는 스핀코팅(spin coating), 침지법(dipping), 유동코팅법(flow coating)과 같은 습식성막법 등으로 유기박막층을 형성한 후, 그 위에 음극을 형성하여 제조할 수 있다.
본 발명의 또 다른 일 구현예에 따르면, 상기 유기광전소자를 포함하는 표시장치를 제공한다.
이하에서는 본 발명의 구체적인 실시예들을 제시한다. 다만, 하기에 기재된 실시예들은 본 발명을 구체적으로 예시하거나 설명하기 위한 것에 불과하며, 이로서 본 발명이 제한되어서는 아니된다.
(유기광전소자용 화합물의 제조)
실시예 1: 화학식 12로 표시되는 화합물의 합성
본 발명의 유기광전소자용 화합물의 보다 구체적인 예로서 제시된 상기 화학식 12로 표시되는 화합물은 아래의 반응식 1과 같은 방법을 통하여 합성되었다.
[반응식 1]
Figure pat00089
제 1 단계 : 화합물 A의 합성
질소 분위기의 교반기가 부착된 250 mL 둥근바닥 플라스크에서 화합물 3-브로모-6-페닐 카바졸 5 g(15.5 mmol), 3-페닐-6-카바졸 보론산 피나콜레이트 6.3 g(17.1 mmol) 및 테트라하이드로퓨란 100 mL 와 2M-탄산칼륨 수용액을 혼합한 후, 질소기류하에서 12 시간 동안 가열 환류하였다. 반응 종결 후 반응물에 헥산을 부어 생기는 고형물을 필터 한 다음, 고형물을 다시 톨루엔과 테트라하이드로퓨란(50:50 부피비) 혼합용액에 녹여 활성탄 과 무수황산마그네슘을 넣어 교반한다. 용액을 팰터한 다음 디클로로메탄과 헥산을 이용해 재결정 하여 화합물 A 4.5 g(수울 60%)을 얻었다.
제 2 단계 : 화학식 12의 합성
100 mL의 둥근 플라스크에서 화합물 A로 표시되는 중간체 생성물 2 g(4.13 mmol), 3-브로모-N-페닐 카바졸 3.8 g(10.3 mmol), 및 염화구리 0.2 g(2.1 mmol), 탄산칼륨 3.4 g(24.8 mmol), 1,10-페난트롤린 0.37 g(2.1 mmol) 와 다이메틸설폭사이드 80 mL를 넣은 다음 질소 기류하에서 180 ℃로 24 시간 동안 가열한다. 유기용매를 감압증류하에 제거한 다음 칼럼크로마토그래피를 이용해 분리하여 3 g(수율: 77 %)의 화합물 12를 얻었다.
상기 수득된 화학식 12의 화합물을 원소분석으로 분석한 결과는 다음과 같았다.
calcd. C72H46N4: C, 89.41; H, 4.79; N, 5.79; found: C, 89.52; H, 4.99; N, 5.62
실시예 2: 화학식 26으로 표시되는 화합물의 합성
본 발명의 유기광전소자용 화합물의 보다 구체적인 예로서 제시된 상기 화학식 26으로 표시되는 화합물은 아래의 반응식 2와 같은 방법을 통하여 합성되었다.
[반응식 2]
Figure pat00090
제 1 단계 : 화합물 B의 합성
100 mL의 둥근 플라스크에서 화합물 A로 표시되는 중간체 생성물 2 g(4.13 mmol), 3-브로모-N-페닐 카바졸 2.3 g(6.2 mmol), 및 염화구리 0.2 g(2.1 mmol), 탄산칼륨 1.7 g(12.4 mmol), 1,10-페난트롤린 0.37 g(2.1 mmol)과 다이메틸설폭사이드 80 mL를 넣은 다음 질소 기류하에서 180 ℃로 24 시간 동안 가열한다. 유기용매를 감압증류하에 제거한 다음 칼럼크로마토그래피를 이용해 분리하여 2 g(수율: 67 %)의 화합물 B를 얻었다.
제 2 단계 : 화학식 26의 합성
100 mL의 둥근 플라스크에서 화합물 B로 표시되는 중간체 생성물 2 g(2.76 mmol), 1-브로모-3,5-디페닐피리딘 1.3 g(4.1 mmol), 및 염화구리 0.14 g(1.4 mmol), 탄산칼륨 1.14 g(8.3 mmol), 1,10-페난트롤린 0.25 g(1.4 mmol) 와 다이메틸설폭사이드 80 mL를 넣은 다음 질소 기류하에서 180 ℃로 24 시간 동안 가열한다. 유기용매를 감압증류하에 제거한 다음 칼럼크로마토그래피를 이용해 분리하여 2.1 g(수율: 80 %)의 화합물 26을 얻었다.
상기 수득된 화학식 26의 화합물을 원소분석으로 분석한 결과는 다음과 같았다.
calcd. C71H46N4: C, 89.28; H, 4.85; N, 5.87; found: C, 89.74; H, 4.91; N, 5.77
실시예 3: 화학식 10으로 표시되는 화합물의 합성
본 발명의 유기광전소자용 화합물의 보다 구체적인 예로서 제시된 상기 화학식 10으로 표시되는 화합물은 아래의 반응식 3과 같은 방법을 통하여 합성되었다.
[반응식 3]
Figure pat00091
100 mL의 둥근 플라스크에서 화합물 B로 표시되는 중간체 생성물 2 g(2.76 mmol), N-(4-브로모페닐)디페닐아민 1.3 g(4.1 mmol), 및 염화구리 0.14 g(1.4 mmol), 탄산칼륨 1.14 g(8.3 mmol), 1,10-페난트롤린 0.25 g(1.4 mmol) 와 다이메틸설폭사이드 80 mL를 넣은 다음 질소 기류하에서 180 ℃로 24 시간 동안 가열한다. 유기용매를 감압증류하에 제거한 다음 칼럼크로마토그래피를 이용해 분리하여 2 g(수율: 75 %)의 화합물 8을 얻었다.
상기 수득된 화학식 10의 화합물을 원소분석으로 분석한 결과는 다음과 같았다.
calcd. C72H48N4: C, 89.23; H, 4.99; N, 5.78; found: C, 89.65; H, 5.21; N, 5.55
(유기광전소자의 제조)
실시예 4
상기 실시예 1에서 합성된 화합물을 호스트로 사용하고, Ir(PPy)3를 도펀트로 사용하여 유기광전소자를 제작하였다. 양극으로는 ITO를 1000 Å의 두께로 사용하였고, 음극으로는 알루미늄(Al)을 1000 Å의 두께로 사용하였다.
구체적으로, 유기광전소자의 제조방법을 설명하면, 양극은 15 Ω/cm2의 면저항값을 가진 ITO 유리 기판을 50 mm × 50 mm × 0.7 mm의 크기로 잘라서 아세톤과 이소프로필알코올과 순수물 속에서 각 15 분 동안 초음파 세정한 후, 30 분 동안 UV 오존 세정하여 사용하였다.
상기 기판 상부에 진공도 650×10-7 Pa, 증착속도 0.1 내지 0.3 nm/s의 조건으로 N,N'-디(1-나프틸)-N,N'-디페닐벤지딘 (NPB) (70 nm) 및 4,4',4"-트리(N-카바졸일)트리페닐아민 (TCTA) (10 nm)를 증착하여 800 Å의 정공수송층을 형성하였다.
이어서, 동일한 진공 증착조건에서 상기 실시예 1에서 합성된 화합물을 이용하여 막 두께 300 Å의 발광층을 형성하였고, 이 때, 인광 도펀트인 Ir(PPy)3을 동시에 증착하였다. 이 때, 인광 도펀트의 증착속도를 조절하여, 발광층의 전체량을 100 중량%로 하였을 때, 인광 도펀트의 배합량이 7 중량%가 되도록 증착하였다.
상기 발광층 상부에 동일한 진공 증착조건을 이용하여 비스(8-하이드록시-2-메틸퀴놀리나토)-알루미늄비페녹시드(BAlq)를 증착하여 막 두께 50 Å의 정공저지층을 형성하였다.
이어서, 동일한 진공 증착조건에서 Alq3를 증착하여, 막 두께 200 Å의 전자수송층을 형성하였다.
상기 전자수송층 상부에 음극으로서 LiF와 Al을 순차적으로 증착하여 유기광전소자를 제작하였다.
상기 유기광전소자의 구조는 ITO/ NPB (70 nm)/ TCTA (10 nm)/ EML (실시예 1의 화합물(93 중량%) + Ir(PPy)3(7 중량%), 30 nm)/ Balq (5 nm)/ Alq3 (20 nm)/ LiF (1 nm) / Al (100 nm) 의 구조로 제작하였다.
실시예 5
상기 실시예 2에서 합성된 화합물을 발광층의 호스트로 사용한 것을 제외하고는 상기 실시예 4와 동일한 방법으로 유기광전소자를 제작하였다.
실시예 6
상기 실시예 3에서 합성된 화합물을 발광층의 호스트로 사용한 것을 제외하고는 상기 실시예 4와 동일한 방법으로 유기광전소자를 제작하였다.
비교예 1
상기 실시예 1에서 합성된 화합물을 발광층의 호스트로 사용한 것을 대신하여, 4,4-N,N-다이카바졸바이페닐(CBP)를 발광층의 호스트로 사용한 것을 제외하고는 상기 실시예 4와 동일한 방법으로 유기광전소자를 제작하였다.
(유기광전소자의 성능 측정)
실험예
상기 실시예 4 내지 6 및 비교예 1에서 제조된 각각의 유기광전소자에 대하여 전압에 따른 전류밀도 변화, 휘도변화 및 발광효율을 측정하였다. 구체적인 측정방법은 다음과 같고, 그 결과는 하기 표 1에 나타내었다
(1) 전압변화에 따른 전류밀도의 변화 측정
제조된 유기광전소자에 대해, 전압을 0 V 부터 10 V까지 상승시키면서 전류-전압계(Keithley 2400)를 이용하여 단위소자에 흐르는 전류값을 측정하고, 측정된 전류값을 면적으로 나누어 결과를 얻었다.
(2) 전압변화에 따른 휘도변화 측정
제조된 유기광전소자에 대해, 전압을 0 V 부터 10 V까지 상승시키면서 휘도계(Minolta Cs-1000A)를 이용하여 그 때의 휘도를 측정하여 결과를 얻었다.
(3) 발광효율 측정
상기(1) 및 (2)로부터 측정된 휘도와 전류밀도 및 전압을 이용하여 동일 밝기(1000 cd/m2)의 전류 효율(cd/A) 및 전력 효율(lm/W)을 계산하였다. 그 결과를 하기 표 2 및 3에 나타내었다.
(4) 색좌표는 휘도계(Minolta Cs-100A)를 이용하여 측정하였고, 그 결과를 하기 표 1에 나타내었다.
Figure pat00092
상기 표 1을 참조하면, 실시예 4 내지 6의 경우 기준 물질인 CBP 에 비해 구동전압 및 효율에서 더 우수하다는 것을 알 수 있다. 이는 실시에 1 내지 3에서 제조된 화합물이 양호한 유기광전소자용 재료로 사용될 수 있는 가능성을 보여준다.
본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.

Claims (12)

  1. 하기 화학식 2로 표시되는 것인 유기광전소자용 화합물:
    [화학식 2]
    Figure pat00093

    상기 화학식 2에서,
    Ar1는 치환 또는 비치환된 탄소수 6 내지 30의 아릴기, 치환 또는 비치환된 카바졸기, 및 치환 또는 비치환된 피리딘기로 이루어진 군에서 선택되고,
    Ar2는 치환 또는 비치환된 피리딘기이고,
    Ar3 및 Ar4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택되고,
    R1 내지 R4는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택된다.
  2. 하기 화학식 4로 표시되는 것인 유기광전소자용 화합물:
    [화학식 4]
    Figure pat00094

    상기 화학식 4에서,
    Ar2는 탄소수 6 내지 30의 치환 또는 비치환된 아미노아릴기, 치환 또는 비치환된 피리딘기, 치환 또는 비치환된 피리미딘기, 및 치환 또는 비치환된 트리아진기로 이루어진 군에서 선택되고,
    Ar5는 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택되고,
    Ar3, Ar4 및 Ar6은 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택되고,
    R1 내지 R6는 서로 동일하거나 상이하며, 각각 독립적으로 수소, 치환 또는 비치환된 탄소수 1 내지 30의 알킬기, 치환 또는 비치환된 탄소수 6 내지 30의 아릴기 및 치환 또는 비치환된 탄소수 2 내지 30의 헤테로아릴기로 이루어진 군에서 선택된다.
  3. 제 2 항에 있어서,
    상기 Ar5는 탄소수 6 내지 12의 아릴기이고,
    상기 Ar2는 탄소수 6 내지 30의 치환 또는 비치환된 아미노아릴기, 치환 또는 비치환된 피리딘기, 치환 또는 비치환된 피리미딘기, 및 치환 또는 비치환된 트리아진기로 이루어진 군에서 선택된 것인 유기광전소자용 화합물.
  4. 하기 화학식 6 내지 화학식 37로 이루어진 군에서 선택된 화학식으로 표시되는 것인 유기광전소자용 화합물.
    [화학식 6] [화학식 7]
    Figure pat00095
    Figure pat00096

    [화학식 8] [화학식 9]
    Figure pat00097
    Figure pat00098

    [화학식 10] [화학식 11]
    Figure pat00099
    Figure pat00100

    [화학식 12] [화학식 13]
    Figure pat00101
    Figure pat00102

    [화학식 14] [화학식 15]
    Figure pat00103
    Figure pat00104

    [화학식 16] [화학식 17]
    Figure pat00105
    Figure pat00106

    [화학식 18] [화학식 19]
    Figure pat00107
    Figure pat00108

    [화학식 20] [화학식 21]
    Figure pat00109
    Figure pat00110

    [화학식 22] [화학식 23]
    Figure pat00111
    Figure pat00112

    [화학식 24] [화학식 25]
    Figure pat00113
    Figure pat00114

    [화학식 26] [화학식 27]
    Figure pat00115
    Figure pat00116

    [화학식 28] [화학식 29]
    Figure pat00117
    Figure pat00118

    [화학식 30] [화학식 31]
    Figure pat00119
    Figure pat00120

    [화학식 32] [화학식 33]
    Figure pat00121
    Figure pat00122

    [화학식 34] [화학식 35]
    Figure pat00123
    Figure pat00124

    [화학식 36] [화학식 37]
    Figure pat00125
    Figure pat00126
  5. 양극, 음극 및 상기 양극과 음극 사이에 개재되는 적어도 한 층 이상의 유기박막층을 포함하는 유기광전소자에 있어서,
    상기 유기박막층 중 적어도 어느 한 층은 상기 제 1 항 내지 제 4 항 중 어느 한 항에 따른 유기광전소자용 화합물을 포함하는 것인 유기광전소자.
  6. 제 5 항에 있어서,
    상기 유기박막층은 발광층, 정공수송층, 정공주입층, 전자수송층, 전자주입층, 정공차단층 및 이들의 조합을 이루어진 군에서 선택되는 것인 유기광전소자.
  7. 제 5 항에 있어서,
    상기 유기광전소자용 화합물은 전자수송층 또는 전자주입층 내에 포함되는 것인 유기광전소자.
  8. 제 5 항에 있어서,
    상기 유기광전소자용 화합물은 발광층 내에 포함되는 것인 유기광전소자.
  9. 제 5 항에 있어서,
    상기 유기광전소자용 화합물은 발광층 내에 인광 또는 형광 호스트 재료로서 사용되는 것인 유기광전소자.
  10. 제 5 항에 있어서,
    상기 유기 광전 소자용 화합물은 발광층 내에 형광 청색 도펀트 재료로서 사용되는 것인 유기광전소자.
  11. 제 5 항에 있어서,
    상기 유기광전소자는 유기 발광 소자, 유기 태양 전지, 유기 트랜지스터, 유기 감광체 드럼 및 유기 메모리 소자로 이루어진 군에서 선택되는 것인 유기광전소자.
  12. 제 5 항의 유기광전소자를 포함하는 것인 표시장치.
KR1020140064737A 2014-05-28 2014-05-28 유기광전소자용 화합물 및 이를 포함하는 유기광전소자 KR20140085400A (ko)