KR20130062020A - Two weaving sructure jacquard fabric for outerwear have the excellent quic drying fuller - Google Patents

Abstract

PURPOSE: A double weave jacquard fabric for outerwear with excellent sweat-absorbing quick-drying property is provided to ensure freshness on the skin and light weight using a high functional material and a natural material. CONSTITUTION: A method for fabricating a double weave jacquard fabric for outerwear with excellent sweat-absorbing quick-drying property comprises: a step of placing a sweat-absorbing quick-drying yarn on a first beam in a warp arrangement using a natural fiber yarn, a metallic yarn, or a blended yarn thereof as a weft and the sweat-absorbing quick-drying yarn, a shaped yarn, a blended yarn of high and low shrinkage filaments, or a hollow yarn of non-circular cross-section as a warp; a step of placing the shaped yarn, the blended yarn of high and low shrinkage filaments, or the hollow yarn of non-circular cross-section on a second beam to form the back side layer by the nylon sweat-absorbing quick-drying yarn; a step of supplying the warp to form the frond side layer by the shaped yarn, the blended yarn of high and low shrinkage filaments, or a hollow yarn of non-circular cross-section; a step of supplying the natural fiber yarn or the metallic yarn as a weft and weaving a fabric with a pattern part and a bottom part; a step of performing thermal treatment to form a pitch skin loop on the surface of the pattern part and on the back side of the bottom part.

Description

Two weaving sructure jacquard fabric for outerwear have the excellent quic drying fuller}

The present invention is woven using a double beam apparatus using a functional (artificial fiber) material and a natural material, and has a warp array in which functional (artificial fiber) materials having different functionalities are positioned to form different layers. The present invention relates to a double-woven jacquard outwear fabric having excellent sweat-absorbing quick-drying and voluminous feel by supplying natural materials such as cotton spun yarn, hemp spun yarn, silk and the like and a method of manufacturing the same.

Women's outerwear has been pursuing materials that are excellent in light weight and memory effect and excellent in volume and drape when worn. However, in recent years, the trend includes sweat in summer and absorbs sweat in summer. Consumers are demanding technology development for this, as the uneven effect on the surface of fabrics and fabrics is clearly required.In developed countries, technology development and future trends of outwear products are more maximized than existing functions. Since the pursuit of new functionality, technology development is urgently required.

In addition, in Korea, we develop and sell materials for outerwear suits mainly in blended materials using hemp for summer. In the foreign countries, we develop products by combining double beam device and functional materials using hemp and cotton. Because of the high response rate, the development direction and product performance of the product have been steadily researched.

However, the technical development of the outerwear dobby / jacquard fabric has a significant difference in the physical properties of the material, causing problems due to the upright and defects in the fabric after weaving. In particular, since the shape of the fine dot pattern is repeatedly reproduced on the surface of the fabric, it is recognized as a defect in weaving, and many problems have emerged, and many difficulties, problems, and defects have occurred due to the construction and arrangement of functional materials, and weaving. The plan has yet to establish a clear solution.

On the other hand, as a related technology for the jacquard fabric is disclosed in the Republic of Korea Patent Publication No. 10-0402733 "method of weaving the jacquard fabric", and the Republic of Korea Patent Publication No. 10-0958732 "a jacquard fabric having asymmetric double-sided pattern And a method of manufacturing the same, and Korean Patent Publication No. 10-0919854 discloses a jacquard weaving method and a fabric of which a protruding pattern layer is formed on both sides by double side shaling.

1. Republic of Korea Patent Publication No. 10-0402733 2. Republic of Korea Patent Publication No. 10-0958732

1. Journal of the Korean Society of Fashion & Beauty Vol. 4, No. 2 (2006) pp. 50 ~ 64 2. "A Study on the Pattern Design and Weaving Process of Jacquard Fabrics" (Ph.D. Thesis (2006.2.); Department of Clothing and Textiles, Graduate School of Gyeongsang National University)

In the present invention, the functional yarns having different materials in a slanted arrangement are used for the production of two beams. The quick-absorbing quick-drying yarn is used as the bottom beam (back layer), and the functional (hollow fiber) material yarn having excellent lightness and wearing comfort is a single beam (front surface). Layer) It is placed in two types of beams and arranged inclined, and wefts are prepared with natural material yarns as weft yarns, and then metal metals are used to invent the fabric and color. It is a double-woven jacquard that has excellent sweat-absorbing quick drying and volume feeling by using the beam device, and it is easy to absorb when wearing, and it improves the discomfort when wearing it by fast drying. It is an object of the present invention to provide an outerwear fabric and a method of manufacturing the same.

The method for producing a double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and volume sense of the present invention that solved the above problems is to use a natural fiber yarn, metal yarn or blended yarn thereof as the weft yarn, sweat-absorbing quick-drying yarn, heteromorphic cross-section yarn Using diaxial mixed fiber or shaped section hollow fiber; Place the absorbent quick-drying yarn in the first beam in an inclined arrangement, and place the release cross-sectional yarn, double shrink blended yarn or release cross-section hollow fiber in the second beam, and place the nylon absorbent quick-dry yarn in the back layer. Fabric that forms a patterned part and a bottom part according to the ratio of inclination and weft by supplying the inclined section yarn, the heteroshrink blended yarn, or the sectioned hollow fiber to form the front layer, and supplying the natural fiber yarn or the metal yarn to the weft yarn. After weaving, the heat treatment is performed to form a pitch skin loop on the surface of the pattern portion, and the bottom portion is characterized in that the pitch skin loop is formed to be formed.

Here, the yarn used as the warp and weft yarn is characterized in that the yarn dyed.

Here, the natural fiber yarn is characterized in that any one selected from the group consisting of cotton spun yarn, hemp spun yarn, silk or a combination of these.

Here, the sweat-absorbing quick-drying yarn is characterized in that any one selected from the group consisting of polyester yarns, release cross-section nylon yarns or microfiber yarns.

Here, the fabric is characterized in that weaving at a density of inclination density 510 ~ 550 bone / inch × weft density 430 ~ 530 bone / inch.

In the present invention, there is provided a double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and volume sensed by the disclosed manufacturing method.

At this time, the fabric is one side layer is a quick-drying sweat-absorbent yarn, the back layer has a heterogeneous cross-sectional yarn, heteroshrink blended yarn or a heterogeneous cross-section hollow yarn is located, the fabric is inclined density 510 ~ 550 / / weft yarn Density It is characterized by having a density of 430 ~ 530 bone / inch.

According to the woven by the manufacturing method of the present invention, by using a high-functional material and a natural material excellent in sweat absorption and quick drying, the comfort with the skin is good, there is a light weight, there is an effect of easy wearing.

In addition, the fabric provided by the present invention has good moisture permeability, good shape stability, less wrinkles, excellent shape resilience to recover wrinkles by simple tissue such as rubbing by hand even if wrinkles occur, shrinkage resistance by washing This has an excellent advantage.

Hereinafter, the present invention will be described in more detail.

In the present invention, in the manufacturing process of the position of the functional yarns with different materials in the inclined array in the two beams, using a sweat-absorbent quick-drying yarn as the bottom beam (back layer), single-beam functional (hollow fiber) material yarn with excellent lightness and wearing comfort (Front layer) Used to place two types of beams inclined array, and wefts prepared natural material yarns as wefts, and then using metal yarns, etc. to invent the quality and color of the fabric, irregularities can be realized on the fabric surface It is a double-beam device that improves the volume, so it has excellent sweat absorption and dryness, and it is easy to absorb when it is worn. To provide a double-woven jacquard outwear fabric and its manufacturing method,

The method for producing a double-woven jacquard outwear fabric having excellent sweat-absorbent quick-drying and voluminous feel provided by the present invention uses natural fiber yarn, metal yarn, or blended yarn thereof as a weft yarn, and absorbs quick-drying yarn, heteromorphic cross-section yarn, and shrink shrink blend Using thread or shaped section hollow fiber; Place the absorbent quick-drying yarn in the first beam in an inclined arrangement, and place the release cross-sectional yarn, double shrink blended yarn or release cross-section hollow fiber in the second beam, and place the nylon absorbent quick-dry yarn in the back layer. Fabric that forms a patterned part and a bottom part according to the ratio of inclination and weft by supplying the inclined section yarn, the heteroshrink blended yarn, or the sectioned hollow fiber to form the front layer, and supplying the natural fiber yarn or the metal yarn to the weft yarn. After weaving, the heat treatment is performed to form a pattern skin on the surface to form a pitch skin loop, and the bottom part is made to form a pitch skin loop on the back surface.

Preferably, the functional yarns and natural fiber yarns used as the warp and weft yarns are preferably used for the pre-dyed yarn.

The natural fiber yarn used in the present invention may be any one selected from the group consisting of cotton spun yarn, hemp spun yarn, silk or twisted yarns thereof, more preferably 550 T of two or more natural fiber yarns selected from the natural fiber yarns. It is recommended to use a double-ply yarn of / M.

The sweat-absorbing quick-drying yarn used in the present invention may be any one selected from the group consisting of polyester yarns, cross-sectional nylon yarns, or microfiber yarns.

The release cross-section nylon yarn or release cross-section yarn used in the present invention is used having a cross section.

According to the invention, the fabric is preferably woven to have a density of warp density of 510 ~ 550 bone / inch × weft density of 430 ~ 530 bone / inch.

In addition, according to the present invention, there is provided a double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and volume sense woven in accordance with the disclosed manufacturing method.

At this time, the fabric is one side layer is a quick-drying sweat-absorbent yarn, the back layer has a sloping arrangement so that the heteromorphic cross-section yarn, heteroshrink blended yarn or hetero sectional hollow fiber is located, the fabric is inclined density 510 ~ 550 bone / inch × weft Density 430 ~ 530 bone / inch will have a density.

According to the present invention, in the weaving of the jacquard outerwear fabric, weaving with a weaving yarn, weaving, weaving according to the design pattern of the jacquard fabric, such as metallic yarn, to express the high-quality fabric and color of the fabric, so that irregularities can be implemented on the surface of the fabric Fabric can be designed.

As described above, the functional yarns having different functionalities are inclinedly arranged and the wefts of natural fiber yarns are secured in order to secure the superiority of fabrics and the comfort of the fabrics. It is possible to manufacture the best women's outwear jacquard fabric with a comfort function that is easy to absorb sweat when worn and does not give a discomfort when worn with quick drying.

Hereinafter, the present invention will be described in more detail with reference to preferred embodiments. However, the following examples are not intended to limit the present invention, and modifications and changes may be made without departing from the scope of the present invention.

Example 1

Prepare a nylon intake ramp and a cross-section hollow fiber, and place the nylon perspiration yarn in a first beam, arrange the cross-section hollow fiber in a second beam, and then supply the cotton spun yarn to a weft yarn. According to the fabric design, weaving the fabric forming the pattern part and the bottom part at the ratio between the warp and the weft, and then performing heat treatment to form the pitch skin loop on the pattern part and the bottom part to the back Double weave jacquard fabrics were made to form skin loops.

The shrinkage after washing and the fastness to washing were measured for the woven fabric as described above, and the wrinkle resistance was determined by using a general synthetic fiber yarn as a warp yarn and a cotton spun yarn as a weft yarn. As a result, the shrinkage was less than 4%, the wash fastness was more than 4 grades, showed excellent morphological stability, the wrinkle resistance was compared, the fabric woven in the above example compared to the fabric woven in a single inclination was significantly superior Indicated.

In addition, using the fabric of Example 1 and the general synthetic fiber yarn as a warp, weaving a woven fabric using a cotton spun yarn as a weft yarn was performed by a simple operation of rubbing by hand, as a result, the fabric of Example 1 Although silver wrinkles showed excellent wrinkle recovery, almost no wrinkles were observed.

In addition, as a result of the secondary processing of the fabric of Example 1 to the user to examine the feeling of use, it was found that the fabric of Example 1 exhibits excellent breathability of the secondary processed product and does not adhere well to the body, thereby exhibiting excellent fit. Could.

As a result, the jacquard outwear fabric woven by the manufacturing method provided by the present invention is excellent in sweat comfort and dryness by using a high-performance material and a natural material, good comfort with the skin, light weight and excellent fit It has a good moisture-repellency, good shape stability, less wrinkles, excellent shape resilience to recover wrinkles by simple tissue such as rubbing by hand even if wrinkles occur, and has excellent advantages in shrinkage resistance by washing.

Claims (8)

Natural weaving yarn, metal yarn or blended yarn of them are used as the weft yarn, and a quick-absorbing quick-drying yarn, a cross-sectional cross-section yarn, a shrinking blended yarn, or a cross-section hollow fiber is used as a warp yarn.
Place the absorbent quick-drying yarn in the first beam in an inclined arrangement, and place the release cross-sectional yarn, double shrink blended yarn or release cross-section hollow fiber in the second beam, and place the nylon absorbent quick-dry yarn in the back layer. Fabric that forms a patterned part and a bottom part according to the ratio of inclination and weft by supplying the inclined section yarn, the heteroshrink blended yarn, or the sectioned hollow fiber to form the front layer, and supplying the natural fiber yarn or the metal yarn to the weft yarn. After weaving, heat treatment is performed to form a pitch skin loop on the surface of the pattern, and the bottom part is a double-woven jacquard outwear having excellent sweat-absorbing quick drying and volume feeling, which is manufactured to form a pitch skin loop on the back side. Method of making a fabric.
The method of claim 1,
The yarn used as the warp and weft yarn is a yarn dyed yarn, characterized in that the quick-drying quick-drying and excellent volume of the double-woven jacquard outwear fabric manufacturing method.
The method of claim 1,
The natural fiber yarn is cotton spun yarn, hemp spun yarn, silk, or any one selected from the group consisting of a combination yarn of the double sweat jacquard outwear fabric excellent in sweat-absorbent quick-drying, characterized in that the volume.
The method of claim 1,
The sweat-absorbent quick-drying yarn is a polyester yarn, a release cross-section nylon yarn or a microfiber yarn, any one selected from the group consisting of a sweat-absorbent quick-drying and excellent volume of the double-woven jacquard outwear fabric manufacturing method.
The method of claim 1,
The fabric is a method of producing a double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and volume, characterized in that weaving at a density of inclination density 510 ~ 550 book / inch × weft density 430 ~ 530 book / inch.
A double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and a volume feeling woven by the manufacturing method of any one of claims 1 to 5.
The method according to claim 6,
The fabric is a double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and volume sense, characterized in that the one-side layer has a sweat-absorbent quick-drying yarn, the back layer has a sloping arrangement where the hetero-cross section yarns, heteroshrink blended yarn or hetero-section hollow fiber is located. .
The method according to claim 6,
The fabric is a double-woven jacquard outwear fabric excellent in sweat-absorbent quick-drying and volume, characterized by having a density of inclination density 510 ~ 550 book / inch × weft density 430 ~ 530 book / inch