KR20130045615A - Self lubricant pad - Google Patents

Self lubricant pad Download PDF

Info

Publication number
KR20130045615A
KR20130045615A KR1020110109935A KR20110109935A KR20130045615A KR 20130045615 A KR20130045615 A KR 20130045615A KR 1020110109935 A KR1020110109935 A KR 1020110109935A KR 20110109935 A KR20110109935 A KR 20110109935A KR 20130045615 A KR20130045615 A KR 20130045615A
Authority
KR
South Korea
Prior art keywords
resin
weight
self
lubricating
lubricant
Prior art date
Application number
KR1020110109935A
Other languages
Korean (ko)
Other versions
KR101345654B1 (en
Inventor
유고협
곽승국
Original Assignee
주식회사 와이티씨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 와이티씨 filed Critical 주식회사 와이티씨
Priority to KR1020110109935A priority Critical patent/KR101345654B1/en
Publication of KR20130045615A publication Critical patent/KR20130045615A/en
Application granted granted Critical
Publication of KR101345654B1 publication Critical patent/KR101345654B1/en

Abstract

PURPOSE: An autonomous lubrication pad is provided to effectively reduce a frictional force between components with a lubricant which flows from inside the pad. CONSTITUTION: An autonomous lubrication pad includes a modified lubricating layer and an adhesive. The modified lubricating layer includes 40 to 95 wt% of a polymer resin which is urethane reaction resin or urethane foaming reaction resin which is formed by reaction between polyol and isocyanate and 50 to 60 wt% of silicon resin. The adhesive is spread beneath the modified lubricating layer. The modified lubricating layer further includes a hardening accelerator or a setting retarder. The hardening accelerator or the setting retarder is mixed into the modified lubricating layer in a ratio of under 3 wt% against the weight of a mixture of the polymer resin and the silicon resin. [Reference numerals] (AA) Modified lubricating layer; (BB) Base material(PET film); (CC) Adhesive

Description

자가 윤활패드 {Self lubricant pad}Self lubricant pad

본 발명은 자가 윤활 시스템을 갖춘 자가 윤활패드에 관한 것으로서 구성요소 사이 표면에 적용됨으로써 구성요소 사이의 마찰을 감소시키고 마찰에 의한 열화, 마모 및 소음을 감소시키는 자가 윤활패드에 관한 것이다.
The present invention relates to a self-lubricating pad having a self-lubricating system, and to a self-lubricating pad which is applied to a surface between components to reduce friction between components and reduce frictional degradation, wear and noise.

일반적으로 자동차 부품, 정밀 계측기기, 정밀 화학기기 등의 대다수 기계장치는 수많은 부품이 상호 유기적으로 결합되어 구성되는데, 상기 각 부품이 서로 물리적으로 결합되어 작동하는 과정에서 소음과 진동이 발생하고, 부품 간의 마찰에 의해 마모가 발생되며 그로 인해 정밀 작동 또는 정밀 계측이 불가능하게 되는 경우가 발생하고 있다.
In general, many mechanical devices such as automobile parts, precision measuring instruments, and fine chemical devices are composed of a large number of components organically coupled to each other, and noise and vibration are generated while the components are physically coupled to each other. Abrasion is caused by friction of the liver, which causes precision operation or precision measurement to be impossible.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출한 것으로서, 자동차 부품, 정밀 계측기기, 정밀 화학기기 등의 부품 표면에 간편하게 부착함으로써 부품 사이의 마찰을 감소시켜 마찰부위의 마찰력을 감소시키고 마찰에 의한 열화, 마모 및 소음을 감소시킬 수 있는 자가 윤활패드를 제공하는 것이 본 발명의 목적이다.
The present invention has been made in order to solve the above problems, by simply attaching to the surface of the parts, such as automotive parts, precision measuring instruments, fine chemicals, etc. by reducing the friction between the parts to reduce the frictional force of the friction parts and It is an object of the present invention to provide a self-lubricating pad that can reduce degradation, wear and noise.

상기의 목적을 달성하기 위하여 본 발명의 일 실시예는 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 40~95중량%와, 실리콘 수지 5~60중량%가 혼합되어 구성된 개질윤활층; 상기 개질윤활층의 하부에 도포된 점착제;를 포함하여 자가 윤활패드가 구성된다.In order to achieve the above object, an embodiment of the present invention comprises a mixture of 40 to 95% by weight of a polymer resin, which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting polyol with isocyanate, and 5 to 60% by weight of a silicone resin. Modified lubricating layer; A self-lubricating pad is configured to include a pressure-sensitive adhesive applied to the lower portion of the modified lubrication layer.

이때, 상기 개질윤활층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자 수지와 실리콘 수지 혼합물의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.At this time, the modified lubricating layer is configured to further comprise a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is characterized in that the mixing is not more than 3% by weight relative to the weight of the polymer resin and silicone resin mixture It is done.

또한, 상기 개질윤활층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자 수지와 실리콘 수지 혼합물의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the modified lubricating layer is configured to further comprise a sieving pigment, the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin and silicone resin mixture.

또한, 상기 개질윤활층과 점착제 사이에는 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성된 지지층이 더 포함되어 구성된 것을 특징으로 한다.In addition, between the modified lubrication layer and the pressure-sensitive adhesive is characterized in that it further comprises a support layer formed of a polymer resin of a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and isocyanate.

또한, 상기 지지층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자 수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the support layer is configured to further comprise a curing accelerator or a curing retardant, characterized in that the curing accelerator or curing retardant is mixed in a range that does not exceed 3% by weight relative to the weight of the polymer resin.

또한, 상기 지지층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the support layer is configured to further include a sieving pigment, the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin.

또한, 상기 개질윤활층과 점착제 사이에 PET(Polyethylene terephthalate resin) 수지를 재질로 형성된 기재가 더 포함되어 구성된 것을 특징으로 한다.In addition, the substrate is formed of a polyethylene terephthalate resin (PET) resin between the modified lubrication layer and the adhesive.

또한, 상기 기재는 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 PET 수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the substrate is configured to further comprise a curing accelerator or curing retardant, characterized in that the curing accelerator or curing retardant is mixed in a range that does not exceed 3% by weight relative to the weight of the PET resin.

또한, 상기 기재는 체질안료를 더 포함하여 구성되되, 상기 체질안료는 PET 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the base material is configured to further include a sieving pigment, characterized in that the sieving pigment is mixed in a range not exceeding 20% by weight relative to the weight of the PET resin.

또한, 상기 개질윤활층의 하부에는, 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성된 지지층;을 더 포함하고, 상기 지지층의 하부에는 PET(Polyethylene terephthalate resin) 수지를 재질로 형성된 기재;를 더 포함하여 구성된 것을 특징으로 한다.In addition, the lower portion of the modified lubrication layer, a support layer formed of a polymer resin, which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and isocyanate; further comprising a polyethylene terephthalate resin (PET) under the support layer It characterized in that the configuration further comprises a; a substrate formed of a resin material.

본 발명의 다른 실시예에 의한 자가 윤활패드는 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 35~95중량%와, 실리콘 수지 1~60중량%, 윤활제 0.1~30중량%가 혼합되어 구성된 자가윤활층;, 상기 자가윤활층의 하부에 형성되는 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성된 지지층; 또는 PET(Polyethylene terephthalate resin) 수지를 재질로 형성된 기재;, 상기 지지층 또는 기재의 하부에 도포된 점착제;를 포함하여 구성된다.Self-lubricating pad according to another embodiment of the present invention is 35 to 95% by weight of a polymer resin which is a urethane reaction resin or urethane foaming reaction resin formed by reacting polyol and isocyanate, 1 to 60% by weight of silicone resin, 0.1 to 30% by weight of lubricant A self-lubricating layer comprising a mixture of%, a support layer formed of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate formed under the self-lubricating layer; Or a base material formed of polyethylene terephthalate resin (PET) resin, and an adhesive applied to a lower portion of the support layer or the base material.

이때, 상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합된 것을 특징으로 한다.At this time, the lubricant is characterized in that any one or two or more of the silicone-based, fluorine-based, fatty acid-based, PE-based or PP-based lubricants are mixed.

또한, 상기 불소계 윤활제는 분자량이 500이상인 것을 특징으로 한다.In addition, the fluorine-based lubricant is characterized in that the molecular weight is 500 or more.

또한, 상기 실리콘계 윤활제는 분자량이 700~70,000인 것을 특징으로 한다.In addition, the silicone lubricant is characterized in that the molecular weight of 700 ~ 70,000.

또한, 상기 지방산계 윤활제는 분자구조 중 탄소의 함량이 11개 이상인 것을 특징으로 한다.In addition, the fatty acid-based lubricant is characterized in that the content of more than 11 carbon in the molecular structure.

또한, 상기 자가윤활층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자수지, 실리콘수지 및 윤활제의 혼합물 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the self-lubricating layer is configured to further comprise a curing accelerator or curing retardant, wherein the curing accelerator or curing retardant is mixed in a range not exceeding 3% by weight relative to the weight of the mixture of the polymer resin, silicone resin and lubricant It is characterized by.

또한, 상기 자가윤활층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자수지, 실리콘수지 및 윤활제의 혼합물 중량대비 PET 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the self-lubricating layer is configured to further include a sieving pigment, wherein the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the PET resin to the weight of the mixture of the polymer resin, silicone resin and lubricant. do.

또한, 상기 지지층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자 수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the support layer is configured to further comprise a curing accelerator or a curing retardant, characterized in that the curing accelerator or curing retardant is mixed in a range that does not exceed 3% by weight relative to the weight of the polymer resin.

또한, 상기 지지층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the support layer is configured to further include a sieving pigment, the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin.

본 발명의 또 다른 실시예에 의한 자가 윤활패드는 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 35~95중량%와, 실리콘 수지 1~60중량%, 윤활제 0.1~30중량%가 혼합되어 구성된 자가윤활층;, 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성되어 상기 자가윤활층의 하부에 형성되는 지지층;, PET(Polyethylene terephthalate resin) 수지를 재질로 형성되어 상기 지지층의 하부에 형성되는 기재;, 상기 기재의 하부에 도포된 점착제;를 포함하여 구성된다.Self-lubricating pad according to another embodiment of the present invention is 35 to 95% by weight of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting polyol and isocyanate, 1 to 60% by weight silicone resin, 0.1 to 30 lubricant A self-lubricating layer composed of a mixture of wt%, a support layer formed of a polymer resin, which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate, and formed under the self-lubricating layer; and PET (polyethylene terephthalate) resin) a base material formed of a resin and formed under the support layer; and a pressure-sensitive adhesive applied to the bottom of the base material.

본 발명의 또 다른 실시예에 의한 자가 윤활패드는 폴리올과 이소시아네이트로 반응되어 형성된 수지, 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 70~99.9중량%와, 윤활제 0.1~30중량%가 혼합되어 구성된 윤활층;, 폴리올과 이소시아네이트로 반응되어 형성된 수지, 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성되어 상기 윤활층 하부에 형성되는 지지층; 및 상기 지지층하부에 도포되는 점착제;를 포함하여 구성된다.Self-lubricating pad according to another embodiment of the present invention is composed of 70 to 99.9% by weight of a polymer resin which is a resin formed by reacting a polyol and an isocyanate, a urethane reaction resin or a urethane foaming reaction resin, and 0.1 to 30% by weight of a lubricant A lubrication layer, a support layer formed of a resin formed by reacting a polyol with an isocyanate, a polymer resin which is a urethane reaction resin, or a urethane foaming reaction resin and formed under the lubrication layer; And an adhesive applied under the support layer.

이때, 상기 윤활층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자수지 및 윤활제 혼합물의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In this case, the lubricating layer is configured to further comprise a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is characterized in that it is mixed in a range not exceeding 3% by weight relative to the weight of the polymer resin and the lubricant mixture. .

또한, 상기 윤활층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자수지 및 윤활제 혼합물의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the lubricating layer is configured to further comprise a sieving pigment, the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin and the lubricant mixture.

또한, 상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합된 것을 특징으로 한다.In addition, the lubricant is characterized in that any one or two or more of the silicone-based, fluorine-based, fatty acid-based, PE-based or PP-based lubricants are mixed.

또한, 상기 불소계 윤활제는 분자량이 500이상인 것을 특징으로 한다.In addition, the fluorine-based lubricant is characterized in that the molecular weight is 500 or more.

또한, 상기 실리콘계 윤활제는 분자량이 700~70,000인 것을 특징으로 한다.In addition, the silicone lubricant is characterized in that the molecular weight of 700 ~ 70,000.

또한, 상기 지방산계 윤활제는 분자구조 중 탄소의 함량이 11개 이상인 것을 특징으로 한다.In addition, the fatty acid-based lubricant is characterized in that the content of more than 11 carbon in the molecular structure.

또한, 상기 지지층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.In addition, the support layer is configured to further comprise a curing accelerator or a curing retardant, characterized in that the curing accelerator or curing retardant is mixed in a range not exceeding 3% by weight relative to the weight of the polymer resin.

또한, 상기 지지층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 한다.
In addition, the support layer is configured to further comprise a sieving pigment, characterized in that the sieving pigment is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin.

상기와 같이 구성된 본 발명의 자가 윤활패드는 사용자가 수시로 부품의 표면에 윤활유를 도포하거나 코팅처리 할 필요 없이 고분자의 개질을 통하여 플라스틱제품 및 금속제품 등 부품 사이의 마찰을 방지하여 마찰에 의한 열화, 마모 및 소음을 감소시키고, 유지보수의 필요성을 줄여줄 수 있다.The self-lubricating pad of the present invention configured as described above is deteriorated due to friction by preventing friction between parts such as plastic products and metal products through the modification of the polymer without the user having to apply lubricating oil or coating on the surface of the parts from time to time. It can reduce wear and noise and reduce the need for maintenance.

또한, 윤활패드에 윤활제를 적용한 본 발명의 자가 윤활패드는 내부에서 흘러나오는 윤활제에 의해 부품 간의 마찰력을 더욱 효과적으로 감소시킬 수 있다.In addition, the self-lubricating pad of the present invention to which the lubricant is applied to the lubricating pad can more effectively reduce the friction force between the parts by the lubricant flowing from the inside.

또한, 부품 표면이 복잡하게 구성된 곡면부나 꺽임부에 간편하게 부착하여 사용할 수 있으므로 다양한 형태의 부품에 사용가능한 효과가 있다.
In addition, since the surface of the component can be easily attached to the curved portion or the bent portion is configured to be used can be used for various types of components.

도 1은 본 발명의 일 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.
도 2는 본 발명의 다른 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.
도 3은 본 발명의 또 다른 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.
도 4는 본 발명의 또 다른 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.
도 5는 본 발명의 또 다른 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.
도 6은 본 발명의 또 다른 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.
도 7은 본 발명의 또 다른 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도.1 is a cross-sectional view showing the configuration of a self-lubricating pad according to an embodiment of the present invention.
Figure 2 is a cross-sectional view showing the configuration of a self-lubricating pad according to another embodiment of the present invention.
Figure 3 is a cross-sectional view showing the configuration of a self-lubricating pad according to another embodiment of the present invention.
Figure 4 is a cross-sectional view showing the configuration of a self-lubricating pad according to another embodiment of the present invention.
Figure 5 is a cross-sectional view showing the configuration of a self-lubricating pad according to another embodiment of the present invention.
Figure 6 is a cross-sectional view showing the configuration of a self-lubricating pad according to another embodiment of the present invention.
Figure 7 is a cross-sectional view showing the configuration of a self-lubricating pad according to another embodiment of the present invention.

이하 첨부한 도면에 의하여 본 발명을 상세하게 설명한다.BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 일 실시예에 의한 자가 윤활패드의 구성을 도시한 단면도이다.1 is a cross-sectional view showing the configuration of a self-lubricating pad according to an embodiment of the present invention.

본 발명의 일 실시예는 도 1에 도시한 바와 같이, 기재의 하부에 점착제층이 형성되고 기재의 상부에 개질윤활층이 형성된다.In one embodiment of the present invention, as shown in Figure 1, the pressure-sensitive adhesive layer is formed on the lower portion of the substrate and the modified lubrication layer is formed on the upper portion of the substrate.

상기 기재는 PET(Polyethylene terephthalate resin)를 재질로 7~12㎛ 두께로 성형된 것으로서, 윤활제의 층간 이동하는 것을 방지하고 윤활패드가 치수안정성을 갖도록 하는 역할을 한다.The substrate is formed of polyethylene terephthalate resin (PET) in a thickness of 7 to 12 μm, and serves to prevent lubrication between layers of the lubricant and to provide dimensional stability of the lubrication pad.

점착제층은 본 발명의 윤활패드를 윤활대상물에 부착 고정하기 위한 것으로서 공지의 점착제를 사용한다.The pressure-sensitive adhesive layer is used for attaching and fixing the lubrication pad of the present invention to a lubrication object.

개질윤활층은 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지) 40~95중량%, 실리콘 수지 5~60중량%가 혼합되어 구성된다.The modified lubricating layer is composed of 40 to 95% by weight of a polymer resin (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with a polyol and isocyanate) and 5 to 60% by weight of a silicone resin.

상기 개질윤활층을 구성하는 고분자 수지는 폴리올과 이소시아네이트가 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지로서 유연성으로 인하여 꺽임부위와 각진 부위, 굴곡부위 등 형상에 관계없이 부착될 수 있고 탄성력으로 인하여 적용 부품 사이에서 밀착에 대한 반발탄성을 갖고 있어 부품의 마모를 막아 줄 수 있다.The polymer resin constituting the modified lubrication layer is a urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet form by reacting polyol and isocyanate, and is attached regardless of the shape such as bending part, angled part, and bending part due to flexibility. It has a resilience against adhesion between applied parts due to the elastic force, which can prevent the wear of the parts.

상기 개질윤활층을 구성하는 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)는 40중량% 미만으로 혼합되면 유연성이 약화되어 굴곡 밀착성이 불량해지고 95중량%를 초과하여 혼합되면 개질을 위한 실리콘 수지의 함량이 작아져 윤활성을 갖을 수 없으므로 40~95중량%로 혼합하는 것이 바람직하다.When the polymer resin constituting the modified lubrication layer (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with polyol and isocyanate) is mixed at less than 40% by weight, flexibility is weakened, resulting in poor bending adhesion. If the content is more than 95% by weight, the content of the silicone resin for the modification is small, so it may not have lubricity.

그리고 상기 개질윤활층을 구성하는 실리콘 수지는 고분자 수지를 개질하여 고분자 수지의 표면에 윤활성능을 구현할 수 있다.The silicone resin constituting the modified lubrication layer may implement a lubricating performance on the surface of the polymer resin by modifying the polymer resin.

상기 개질윤활층을 구성하는 실리콘 수지는 5중량% 미만으로 혼합되면 표면의 윤활효과가 불량해지며 60중량%를 초과하여 혼합되면 인열강도 및 마모도와 같은 제품의 기계적 물성 및 유연성과 탄성력을 약화시켜 제품 적용부위에 한정성을 갖게되므로 5~60중량%를 혼합하는 것이 바람직하다.When the silicone resin constituting the modified lubricating layer is mixed at less than 5% by weight, the lubricating effect of the surface is poor, and when mixed at more than 60% by weight, the mechanical properties, flexibility, and elasticity of the product, such as tear strength and wear, are weakened. It is preferable to mix 5 to 60% by weight because it will have a limit to the product application site.

그리고 상기 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)와 실리콘 수지의 혼합물 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합하여 개질윤활층을 구성할 수 있다.And a range of not more than 3% by weight of the curing accelerator or curing retardant based on the mixture weight of the polymer resin (a urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with a polyol and an isocyanate) and a silicone resin. The modified lubricating layer can be formed by mixing in the inside.

상기 경화촉진제 또는 경화지연제를 혼합량을 조절함으로써 원하는 작업속도에 맞추어 경화시킬 수 있다.The curing accelerator or curing retardant may be cured at a desired working speed by adjusting the mixing amount.

또한, 상기 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)와 실리콘 수지의 혼합물 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 개질윤활층을 구성할 수 있다.In addition, the polymeric pigment (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with a polyol and isocyanate) and a silicone resin are mixed within a range not exceeding 20% by weight based on the weight of the mixture. To form a modified lubricating layer.

상기 체질안료는 원하는 도막의 기계적 강도 또는 부피확보를 목적으로 하는 것으로서 체질안료를 20중량%를 초과하여 혼합하면 작업성이 불량해지므로 고분자 수지와 실리콘 수지의 혼합물 중량 대비 20중량%를 초과하지 않는 범위 내에서 혼합하는 것이 바람직하다.The extender pigments are intended for securing the mechanical strength or volume of the desired coating film, and when the extender pigments are mixed in excess of 20% by weight, the workability becomes poor, and thus does not exceed 20% by weight relative to the weight of the mixture of the polymer resin and the silicone resin. It is preferable to mix in the range.

또한, 상기 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)와 실리콘 수지의 혼합물 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 개질윤활층을 구성함으로써 원하는 색상에 맞출 수 있다.
In addition, a color pigment is mixed within a range not exceeding 5% by weight, based on a mixture weight of the polymer resin (a urethane reaction resin or a urethane foaming reaction resin capable of forming a film or sheet by reacting with a polyol and an isocyanate) and a silicone resin. By forming the modified lubricating layer can be matched to the desired color.

본 발명의 다른 실시예는 도 2에 도시한 바와 같이 점착제, 기재, 지지층 및 개질윤활층이 차례로 적층되어 구성된다.Another embodiment of the present invention is composed of a pressure-sensitive adhesive, a substrate, a support layer and a modified lubrication layer are sequentially stacked as shown in FIG.

상기 점착제와 기재층은 도 1에 도시한 본 발명의 일 실시예와 동일한 구성이다.The pressure-sensitive adhesive and the base layer have the same configuration as the embodiment of the present invention shown in FIG. 1.

상기 지지층은 개질윤활층과 기재의 밀착력을 극대화하기 위하여 PET 및 개질윤활층의 수지와 친화력이 큰 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응수지)를 사용하였고 내유성이 우수한 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)를 사용하여 윤활성분의 층간 이동이 불가능하도록 구성한다.The support layer is a polymer resin having a high affinity with a resin of PET and a modified lubricating layer (urethane reaction resin or urethane foaming reaction resin which can be formed into a film or sheet form by reacting with polyol and isocyanate in order to maximize adhesion between the modified lubricating layer and the substrate). ), And it is constructed so that the lubrication component cannot be moved between layers by using a polymer resin having excellent oil resistance (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with polyol and isocyanate).

그리고 상기 고분자 수지의 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합함으로써 원하는 작업속도에 맞추어 경화시킬 수 있다.In addition, the curing accelerator or curing retardant with respect to the weight of the polymer resin may be mixed in a range not exceeding 3% by weight to cure according to the desired working speed.

또한, 상기 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)의 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 지지층을 구성할 수 있다.In addition, the support layer is formed by mixing the extender pigment with respect to the weight of the polymer resin (a urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with a polyol and isocyanate) within a range not exceeding 20% by weight. can do.

상기 체질안료는 원하는 도막의 기계적 강도 또는 부피확보를 목적으로 하는 것으로서 체질안료를 20중량%를 초과하여 혼합하면 작업성이 불량해지므로 고분자 수지와 실리콘 수지의 혼합물 중량 대비 20중량%를 초과하지 않는 범위 내에서 혼합하는 것이 바람직하다.The extender pigments are intended for securing the mechanical strength or volume of the desired coating film, and when the extender pigments are mixed in excess of 20% by weight, the workability becomes poor, and thus does not exceed 20% by weight relative to the weight of the mixture of the polymer resin and the silicone resin. It is preferable to mix in the range.

또한, 상기 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)의 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 지지층을 구성함으로써 원하는 색상에 맞출 수 있다.
In addition, the support layer is constituted by mixing the color pigments within a range not exceeding 5% by weight with respect to the weight of the polymer resin (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with polyol and isocyanate). By matching it with the desired color.

본 발명의 또 다른 실시예는 도 3에 도시한 바와 같이 점착제, 기재층 및 자가윤활층이 차례로 적층되어 구성된다.Another embodiment of the present invention is composed of a pressure-sensitive adhesive, a substrate layer and a self-lubricating layer are sequentially stacked as shown in FIG.

상기 점착제와 기재층은 도 1에 도시한 본 발명의 일 실시예와 동일한 구성이다.The pressure-sensitive adhesive and the base layer have the same configuration as the embodiment of the present invention shown in FIG. 1.

상기 자가윤활층은 윤활제 성분이 Migration되면서 표면 마찰력을 더욱 감소시켜 마찰소음을 예방하기 위하여 윤활제를 첨가하여 구성된다.The self-lubricating layer is configured by adding a lubricant to prevent friction noise by further reducing the surface friction force as the lubricant component is migrated.

또한, 자가윤활층이 개질윤활층과 유사한 조성으로 구성된 이유는 개질윤활층 표면 윤활성은 유지하면서 Migration되는 윤활제에 의한 마찰소음 억제를 극대화하기 위함이다.In addition, the reason why the self-lubricating layer is composed of a similar composition to the modified lubricating layer is to maximize the friction noise suppression by the migrated lubricant while maintaining the modified lubricating layer surface lubricity.

상기 자가윤활층은 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상으로 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지) 35~95중량%, 실리콘 수지 1~60중량%, 윤활제 0.1~30중량%가 혼합되어 구성된다.The self-lubricating layer is 35 to 95% by weight of a polymer resin (urethane reaction resin or urethane foaming reaction resin which can be formed into a film or sheet by reacting with polyol and isocyanate), 1 to 60% by weight of silicone resin, and 0.1 to 30% by weight of lubricant. % Is mixed.

상기 자가윤활층을 구성하는 고분자 수지가 35중량% 미만으로 혼합되면 유연성이 저하되어 굴곡 밀착성이 불량해지고 95중량%를 초과하여 혼합되면 개질을 위한 실리콘수지의 혼합량과 윤활제의 혼합량이 작아져 윤활성이 저하되므로 고분자 수지는 35~95중량%가 혼합되는 것이 바람직하다.When the polymer resin constituting the self-lubricating layer is mixed at less than 35% by weight, the flexibility decreases, and the bending adhesion is poor. When the polymer resin is mixed at more than 95% by weight, the mixing amount of the silicone resin for reforming and the mixing amount of the lubricant are reduced, so that the lubricity is reduced. Since it is lowered, it is preferable that 35-95 weight% of polymer resins are mixed.

그리고 상기 자가윤활층을 구성하는 실리콘 수지는 1~60중량%가 혼합되는데 1중량% 미만으로 혼합되면 표면의 윤활효과가 불량해지고 60중량%를 초과하여 혼합되면 제품의 기계적 물성(인열강도, 마모도) 및 유연성과 탄성력을 약화시켜 제품 적용부위에 한정성을 갖게 되므로 실리콘 수지는 1~60중량% 혼합하는 것이 바람직하다.And when the silicone resin constituting the self-lubricating layer is mixed 1 to 60% by weight but less than 1% by weight, the lubricating effect of the surface is poor, and when mixed in excess of 60% by weight of the mechanical properties of the product (tear strength, Abrasion degree) and the flexibility and elasticity of the weakening of the product application area by weakening the silicone resin is preferably mixed 1 to 60% by weight.

상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합된 윤활제이다.The lubricant is a lubricant in which any one or two or more of silicone, fluorine, fatty acid, PE or PP lubricants are mixed.

상기 자가윤활층을 구성하는 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상으로 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)는 35중량% 미만이 혼합되면 유연성이 약화되어 굴곡진 부품 표면에 밀착성이 저하되고 97중량%를 초과하여 혼합되면 개질을 위한 실리콘 수지와 윤활제의 혼합량이 작아져 윤활성이 저하되므로 고분자 수지는 35~95중량%로 혼합하는 것이 바람직하다.The polymer resin constituting the self-lubricating layer (urethane reaction resin or urethane foaming reaction resin which can be formed into a film or sheet by reacting with polyol and isocyanate) is mixed with less than 35% by weight, which decreases its flexibility to the surface of the curved part. When the adhesiveness is lowered and mixed in excess of 97% by weight, the mixing amount of the silicone resin and the lubricant for the modification is reduced and the lubricity is lowered, so that the polymer resin is preferably mixed at 35 to 95% by weight.

상기 자가윤활층을 구성하는 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합되는데 상술한 바와 같이 윤활제는 윤활제가 Migration되면서 윤활 지속성과 마찰소음억제의 특성을 부여한다.The lubricant constituting the self-lubricating layer is any one or two or more of silicone, fluorine, fatty acid, PE, or PP-based lubricants are mixed. As described above, the lubricant has characteristics of lubrication persistence and friction noise suppression as the lubricant is migrated. Grant.

상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제를 선택적으로 혼합하여 구성하면 혼합되는 윤활제에 따라 각 윤활제의 분자 구조와 분자량 차이에 의해 자가윤활층 내부에서 표면으로 윤활제가 이동하는 Migration 속도를 조절할 수 있다.When the lubricant is composed by selectively mixing a silicone-based, fluorine-based, fatty acid-based, PE-based or PP-based lubricant, the migration of the lubricant from the self-lubricating layer to the surface due to the molecular structure and molecular weight difference of each lubricant depending on the lubricant to be mixed You can adjust the speed.

상기 윤활제는 30중량%를 초과하여 혼합되면 윤활제가 도막 표면에 과도하게 Migration되어 피착물을 오염시키므로 윤활제는 0.1~30중량%를 혼합하는 것이 바람직하다.When the lubricant is mixed in excess of 30% by weight, the lubricant is excessively migrated on the surface of the coating to contaminate the adherend, so the lubricant is preferably mixed 0.1 to 30% by weight.

또한, 불소계 윤활제의 분자량이 500 이상인 것을 사용하는 것이 바람직한데 불소계 윤활제의 분자량이 500 미만인 경우 Migration도는 속도가 빨라 제품 표면이 심하게 오염되므로 불소계 윤활제는 분자량이 500 이상인 것을 사용하는 것이 바람직하다.In addition, it is preferable to use a molecular weight of 500 or more of the fluorine-based lubricant, but when the molecular weight of the fluorine-based lubricant is less than 500, the degree of migration is fast and the surface of the product is seriously contaminated. Therefore, it is preferable to use a fluorine-based lubricant having a molecular weight of 500 or more.

또한, 실리콘계 윤활제인 경우 분자량이 700~70,000인 것을 사용하는 것이 바람직한데 실리콘계 윤활제의 분자량이 700 미만인 경우 Migration 되는 속도가 빨라서 제품 표면이 심하게 오염되고 분자량이 70,000을 초과하는 경우 점도가 매우 높아 작업성이 불량해지므로 실리콘계 윤활제는 분자량이 700~70,000인 것을 사용하는 것이 바람직하다.In addition, it is preferable to use a molecular weight of 700 ~ 70,000 in the case of silicone lubricant, but when the molecular weight of the silicone lubricant is less than 700, the migration rate is fast, so that the surface of the product is heavily contaminated and the viscosity is very high when the molecular weight exceeds 70,000 workability Since this defect becomes poor, it is preferable to use a silicone type lubricant whose molecular weight is 700-70,000.

또한, 지방산계 윤활제의 분자구조 중 탄소의 함량이 11개 이상인 것을 사용하는 것이 바람직한데 지방산계 윤활제의 부자구조 중 탄소의 함량이 10개 이하인 경우에는 계면활성력이 낮아서 윤활특성이 저하되므로 탄소의 함량이 11개 이상인 지방산계 윤활제를 사용하는 것이 바람직하다.In addition, it is preferable to use a carbon content of 11 or more in the molecular structure of the fatty acid-based lubricant, but when the carbon content of the fatty acid-based lubricant in the substructure of 10 or less, it has a low interfacial activity and the lubrication properties are deteriorated. Preference is given to using fatty acid-based lubricants having a content of 11 or more.

그리고 상기 고분자 수지, 실리콘 수지 및 윤활제가 혼합된 혼합물의 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합함으로써 원하는 작업속도에 맞추어 경화시킬 수 있다.The curing accelerator or curing retardant may be cured at a desired working speed by mixing the curing accelerator or curing retardant in a range not exceeding 3% by weight based on the weight of the mixture of the polymer resin, the silicone resin, and the lubricant.

또한, 상기 고분자 수지, 실리콘 수지 및 윤활제가 혼합된 혼합물의 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 지지층을 구성할 수 있다.In addition, the support layer may be formed by mixing the extender pigment with respect to the weight of the mixture of the polymer resin, the silicone resin, and the lubricant within a range not exceeding 20% by weight.

상기 체질안료는 원하는 도막의 기계적 강도 또는 부피확보를 목적으로 하는 것으로서 체질안료를 20중량%를 초과하여 혼합하면 작업성이 불량해지므로 상기 고분자 수지, 실리콘 수지 및 윤활제가 혼합된 혼합물의 중량 대비 20중량%를 초과하지 않는 범위 내에서 혼합하는 것이 바람직하다.The extender pigments are intended to secure the mechanical strength or volume of the desired coating film, and when the extender pigments are mixed in excess of 20% by weight, the workability becomes poor, so that the weight of the mixture of the polymer resin, the silicone resin, and the lubricant 20 is mixed. It is preferable to mix in the range which does not exceed weight%.

또한, 상기 고분자 수지, 실리콘 수지 및 윤활제가 혼합된 혼합물의 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 자가윤활층을 구성함으로써 원하는 색상에 맞출 수 있다.
In addition, by mixing the color pigment with respect to the weight of the mixture of the polymer resin, the silicone resin and the lubricant within a range not exceeding 5% by weight to form a self-lubricating layer can be matched to the desired color.

본 발명의 또 다른 실시예는 도 4에 도시한 바와 같이 점착제, 기재, 지지층 및 자가윤활층이 차례로 적층되어 구성되는 것으로서 도 3에 기재된 윤활패드의 자가윤활층과 기재의 사이에 지지층이 더 구성된 것이고, 도 4에 기재된 점착제, 기재 및 자가윤활층은 도 3에 기재된 것과 동일하다.According to another embodiment of the present invention, as shown in FIG. 4, a pressure-sensitive adhesive, a substrate, a support layer, and a self-lubricating layer are sequentially stacked, and a support layer is further provided between the self-lubricating layer of the lubricating pad of FIG. 3 and the substrate. The pressure-sensitive adhesive, base material and self-lubricating layer described in FIG. 4 are the same as those described in FIG. 3.

도 4에 기재된 본 발명의 또 다른 실시예는 도 3에 기재된 윤활패드의 자가윤활층과 기재사이에 지지층을 구성한 것으로서, 상기 지지층은 자가윤활층과 기재의 밀착력을 극대화하기 위하여 PET 및 개질윤활층의 수지와 친화력이 큰 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응수지)를 사용하였고 내유성이 우수한 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)를 사용하여 윤활성분의 층간 이동이 불가능하도록 구성한다.Another embodiment of the present invention described in FIG. 4 constitutes a support layer between the self-lubricating layer and the substrate of the lubricating pad of FIG. 3, wherein the support layer is formed of PET and a modified lubrication layer to maximize adhesion between the self-lubricating layer and the substrate. Polymer resin (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with polyol and isocyanate with polyol and isocyanate) was used. Urethane reaction resin or urethane foaming reaction resin capable of shaping of the shape) is used to prevent laminar movement of lubricating components.

상기 지지층은 도 2에 도시한 지지층과 마찬가지로 고분자 수지의 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합함으로써 원하는 작업속도에 맞추어 경화시킬 수 있고, 상기 고분자 수지의 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 지지층을 구성할 수 도 있다.Like the support layer shown in Figure 2, the support layer can be cured at a desired working speed by mixing the curing accelerator or curing retardant in a range not exceeding 3% by weight with respect to the weight of the polymer resin, the weight of the polymer resin Contrast extender pigments may be mixed within a range not exceeding 20% by weight to form a support layer.

상기 체질안료는 도막의 기계적 강도 또는 부피확보를 목적으로 하는 것으로서 체질안료를 20중량%를 초과하여 혼합하면 작업성이 불량해지므로 고분자 수지의 중량 대비 20중량%를 초과하지 않는 범위 내에서 혼합하는 것이 바람직하다.The extender pigment is intended to secure the mechanical strength or volume of the coating film, and when the extender pigment is mixed in excess of 20% by weight, the workability becomes poor, so that the mixing is performed within a range not exceeding 20% by weight of the polymer resin. It is preferable.

또한, 상기 고분자 수지의 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 원하는 색상에 맞출 수 있다.
In addition, the color pigment to the weight of the polymer resin may be mixed within a range not exceeding 5% by weight to match the desired color.

본 발명의 또 다른 실시예는 도 5에 도시한 바와 같이 점착제 및 개질윤활층을 적층하여 구성된다.Another embodiment of the present invention is configured by stacking the pressure-sensitive adhesive and the modified lubrication layer as shown in FIG.

상기 점착제와 개질윤활층은 도 1에 도시한 점착제와 개질윤활층과 동일하다.The pressure-sensitive adhesive and the modified lubricating layer are the same as the pressure-sensitive adhesive and the modified lubricating layer shown in FIG.

즉, 점착제는 공지의 점착제이고, 개질윤활층은 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지) 40~95중량%, 실리콘 수지 5~60중량%가 혼합되어 구성된다.That is, the pressure-sensitive adhesive is a known pressure-sensitive adhesive, the modified lubricating layer is 40 to 95% by weight of the polymer resin (urethane reaction resin or urethane foaming reaction resin that can be formed into a film or sheet form by reacting with polyol and isocyanate), silicone resin 5 to 60 Wt% is mixed.

이때, 상기 개질윤활층은 도 1에 도시한 개질윤활층과 마찬가지로 고분자 수지와 실리콘 수지의 혼합물 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합하여 작업속도를 조절할 수 있다.At this time, the modified lubrication layer can adjust the working speed by mixing the curing accelerator or curing retardant in a range not exceeding 3% by weight, as in the modified lubrication layer shown in Figure 1 with respect to the mixture weight of the polymer resin and the silicone resin have.

또한, 상기 고분자 수지와 실리콘 수지의 혼합물 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 원하는 도막의 기계적 강도 또는 부피를 조절할 수 있다.In addition, the extender pigment may be mixed within the range not exceeding 20% by weight based on the weight of the mixture of the polymer resin and the silicone resin to adjust the mechanical strength or volume of the desired coating film.

또한, 상기 고분자 수지와 실리콘 수지의 혼합물 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 개질윤활층을 구성함으로써 원하는 색상에 맞출 수 있다.
In addition, by mixing the color pigment with respect to the mixture weight of the polymer resin and the silicone resin within a range not exceeding 5% by weight to form a modified lubrication layer can be matched to the desired color.

본 발명의 또 다른 실시예는 도 6에 도시한 바와 같이 점착제, 지지층 및 개질윤활층이 차례로 적층되어 구성된다.Another embodiment of the present invention is composed of a pressure-sensitive adhesive, a support layer and a modified lubrication layer are sequentially stacked as shown in FIG.

상기 점착제와 개질윤활층은 도 1에 도시한 점착제와 개질윤활층과 동일하고, 지지층은 도 2에 도시한 지지층과 동일하다.The pressure-sensitive adhesive and the modified lubricating layer are the same as the pressure-sensitive adhesive and the modified lubricating layer shown in FIG. 1, and the supporting layer is the same as the supporting layer shown in FIG. 2.

즉, 점착제는 공지의 점착제이고, 개질윤활층은 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지) 40~95중량%, 실리콘 수지 5~60중량%가 혼합되어 구성된다.That is, the pressure-sensitive adhesive is a known pressure-sensitive adhesive, the modified lubricating layer is 40 to 95% by weight of the polymer resin (urethane reaction resin or urethane foaming reaction resin that can be formed into a film or sheet form by reacting with polyol and isocyanate), silicone resin 5 to 60 Wt% is mixed.

이때, 상기 개질윤활층은 도 1에 도시한 개질윤활층과 마찬가지로 고분자 수지와 실리콘 수지의 혼합물 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합하여 작업속도를 조절할 수 있다.At this time, the modified lubrication layer can adjust the working speed by mixing the curing accelerator or curing retardant in a range not exceeding 3% by weight, as in the modified lubrication layer shown in Figure 1 with respect to the mixture weight of the polymer resin and the silicone resin have.

또한, 상기 고분자 수지와 실리콘 수지의 혼합물 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 원하는 도막의 기계적 강도 또는 부피를 조절할 수 있다.In addition, the extender pigment may be mixed within the range not exceeding 20% by weight based on the weight of the mixture of the polymer resin and the silicone resin to adjust the mechanical strength or volume of the desired coating film.

또한, 상기 고분자 수지와 실리콘 수지의 혼합물 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 개질윤활층을 구성함으로써 원하는 색상에 맞출 수 있다.In addition, by mixing the color pigment with respect to the mixture weight of the polymer resin and the silicone resin within a range not exceeding 5% by weight to form a modified lubrication layer can be matched to the desired color.

그리고 상기 지지층은 개질윤활층과 점착제의 밀착력을 극대화하기 위하여 PET 및 개질윤활층의 수지와 친화력이 큰 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응수지)를 사용하였고 내유성이 우수한 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트 형상의 성형이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응 수지)를 사용하여 윤활성분의 층간 이동이 불가능하도록 구성한다.In addition, the support layer is a polymer resin having a high affinity with a resin of PET and a modified lubricating layer (polyurethane and isocyanate to be formed into a film or a sheet to form a film or sheet in order to maximize adhesion between the modified lubricating layer and the pressure-sensitive adhesive. Resin) and a polymer resin having excellent oil resistance (urethane reaction resin or urethane foaming reaction resin capable of forming a film or sheet by reacting with polyol and isocyanate) is used to prevent lubrication between layers.

그리고 상기 고분자 수지의 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합함으로써 원하는 작업속도에 맞추어 경화시킬 수 있다.In addition, the curing accelerator or curing retardant with respect to the weight of the polymer resin may be mixed in a range not exceeding 3% by weight to cure according to the desired working speed.

또한, 상기 고분자 수지의 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 지지층을 구성할 수 있다.In addition, the support layer may be configured by mixing the extender pigment with respect to the weight of the polymer resin within a range not exceeding 20% by weight.

상기 체질안료는 원하는 도막의 기계적 강도 또는 부피확보를 목적으로 하는 것으로서 체질안료를 20중량%를 초과하여 혼합하면 작업성이 불량해지므로 고분자 수지와 실리콘 수지의 혼합물 중량 대비 20중량%를 초과하지 않는 범위 내에서 혼합하는 것이 바람직하다.The extender pigments are intended for securing the mechanical strength or volume of the desired coating film, and when the extender pigments are mixed in excess of 20% by weight, the workability becomes poor, and thus does not exceed 20% by weight relative to the weight of the mixture of the polymer resin and the silicone resin. It is preferable to mix in the range.

또한, 상기 고분자 수지의 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 지지층을 구성함으로써 원하는 색상에 맞출 수 있다.
In addition, by mixing the color pigment with respect to the weight of the polymer resin within a range not exceeding 5% by weight to form a support layer can be matched to the desired color.

본 발명의 또 다른 실시예는 도 7에 도시한 바와 같이 점착제, 지지층 및 자가윤활층이 차례로 적층되어 구성된다.Another embodiment of the present invention is composed of a pressure-sensitive adhesive, a support layer and a self-lubricating layer are sequentially stacked as shown in FIG.

상기 점착제, 지지층 및 자가윤활층은 도 4에 도시한 점착제, 지지층 및 자가윤활층과 동일하다.
The pressure-sensitive adhesive, support layer and self-lubricating layer are the same as the pressure-sensitive adhesive, support layer and self-lubricating layer shown in FIG.

본 발명의 또 다른 실시예는 도 8에 도시한 바와 같이 점착제, 지지층, 윤활층이 차례로 적층되어 구성된다.Another embodiment of the present invention is composed of a pressure-sensitive adhesive, a support layer, and a lubrication layer are sequentially stacked as shown in FIG.

상기 점착제와 지지층은 도 2에 도시한 점착제 및 지지층과 동일하다.The pressure-sensitive adhesive and the support layer are the same as the pressure-sensitive adhesive and the support layer shown in FIG.

상기 윤활층은 고분자 수지(폴리올과 이소시아네이트로 반응되어 필름 또는 시트형상이 가능한 우레탄 반응 수지 또는 우레탄 발포 반응수지) 70~99.9중량%와 윤활제 0.1~30중량%가 혼합되어 구성된다.The lubricating layer is composed of 70 to 99.9% by weight of a polymer resin (a urethane reaction resin or a urethane foaming reaction resin capable of reacting with a polyol and isocyanate to form a film or a sheet) and a lubricant to 0.1 to 30% by weight.

그리고 상기 고분자 수지 윤활제가 혼합된 혼합물의 중량 대비 경화촉진제 또는 경화지연제를 3중량%를 초과하지 않는 범위 내에서 혼합함으로써 원하는 작업속도에 맞추어 경화시킬 수 있다.In addition, the curing accelerator or curing retardant is mixed in a range not exceeding 3% by weight with respect to the weight of the mixture of the polymer resin lubricant can be cured to the desired working speed.

또한, 상기 고분자 수지 및 윤활제가 혼합된 혼합물의 중량 대비 체질안료를 20중량%를 초과하지 않는 범위 내에서 혼합하여 윤활층을 구성할 수 있다.In addition, the lubricating layer may be formed by mixing the extender pigment with respect to the weight of the mixture of the polymer resin and the lubricant in a range not exceeding 20% by weight.

상기 체질안료는 원하는 도막의 기계적 강도 또는 부피확보를 목적으로 하는 것으로서 체질안료를 20중량%를 초과하여 혼합하면 작업성이 불량해지므로 상기 고분자 수지 및 윤활제가 혼합된 혼합물의 중량 대비 20중량%를 초과하지 않는 범위 내에서 혼합하는 것이 바람직하다.The sieving pigment is intended to ensure the mechanical strength or volume of the desired coating film, when the sieving pigment is mixed in excess of 20% by weight, the workability is poor, so 20% by weight relative to the weight of the mixture of the polymer resin and lubricant mixture It is preferable to mix in the range which does not exceed.

또한, 상기 고분자 수지 및 윤활제가 혼합된 혼합물의 중량 대비 색상안료를 5중량%를 초과하지 않는 범위 내에서 혼합하여 윤활층을 구성함으로써 원하는 색상에 맞출 수 있다.In addition, by mixing the color pigment with respect to the weight of the mixture of the polymer resin and the lubricant mixed within the range not exceeding 5% by weight to form a lubricating layer can be matched to the desired color.

상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합된 윤활제이다.The lubricant is a lubricant in which any one or two or more of silicone, fluorine, fatty acid, PE or PP lubricants are mixed.

상기 윤활층을 구성하는 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합되는데 상술한 바와 같이 윤활제는 윤활제가 Migration되면서 윤활 지속성과 마찰소음억제의 특성을 부여한다.The lubricant constituting the lubricating layer is any one or two or more of a silicone, fluorine, fatty acid, PE or PP-based lubricant is mixed. As described above, the lubricant imparts characteristics of lubrication persistence and friction noise suppression as the lubricant is migrated. do.

상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제를 선택적으로 혼합하여 구성하면 혼합되는 윤활제에 따라 각 윤활제의 분자 구조와 분자량 차이에 의해 윤활층 내부에서 표면으로 윤활제가 이동하는 Migration 속도를 조절할 수 있다.When the lubricant is formed by selectively mixing a silicone-based, fluorine-based, fatty acid-based, PE-based or PP-based lubricant, the migration speed at which the lubricant moves from the inside of the lubricating layer to the surface due to the molecular structure and molecular weight difference of each lubricant depending on the mixed lubricant. Can be adjusted.

상기 윤활제는 30중량%를 초과하여 혼합되면 윤활제가 도막 표면에 과도하게 Migration되어 피착물을 오염시키므로 윤활제는 0.1~30중량%를 혼합하는 것이 바람직하다.When the lubricant is mixed in excess of 30% by weight, the lubricant is excessively migrated on the surface of the coating to contaminate the adherend, so the lubricant is preferably mixed 0.1 to 30% by weight.

또한, 불소계 윤활제의 분자량이 500 이상인 것을 사용하는 것이 바람직한데 불소계 윤활제의 분자량이 500 미만인 경우 Migration도는 속도가 빨라 제품 표면이 심하게 오염되므로 불소계 윤활제는 분자량이 500 이상인 것을 사용하는 것이 바람직하다.In addition, it is preferable to use a molecular weight of 500 or more of the fluorine-based lubricant, but when the molecular weight of the fluorine-based lubricant is less than 500, the degree of migration is fast and the surface of the product is seriously contaminated. Therefore, it is preferable to use a fluorine-based lubricant having a molecular weight of 500 or more.

또한, 실리콘계 윤활제인 경우 분자량이 700~70,000인 것을 사용하는 것이 바람직한데 실리콘계 윤활제의 분자량이 700 미만인 경우 Migration 되는 속도가 빨라서 제품 표면이 심하게 오염되고 분자량이 70,000을 초과하는 경우 점도가 매우 높아 작업성이 불량해지므로 실리콘계 윤활제는 분자량이 700~70,000인 것을 사용하는 것이 바람직하다.In addition, it is preferable to use a molecular weight of 700 ~ 70,000 in the case of silicone lubricant, but when the molecular weight of the silicone lubricant is less than 700, the migration rate is fast, so that the surface of the product is heavily contaminated and the viscosity is very high when the molecular weight exceeds 70,000 workability Since this defect becomes poor, it is preferable to use a silicone type lubricant whose molecular weight is 700-70,000.

또한, 지방산계 윤활제의 분자구조 중 탄소의 함량이 11개 이상인 것을 사용하는 것이 바람직한데 지방산계 윤활제의 부자구조 중 탄소의 함량이 10개 이하인 경우에는 계면활성력이 낮아서 윤활특성이 저하되므로 탄소의 함량이 11개 이상인 지방산계 윤활제를 사용하는 것이 바람직하다.
In addition, it is preferable to use a carbon content of 11 or more of the molecular structure of the fatty acid-based lubricant, but when the carbon content of the fatty acid-based lubricant has a carbon content of 10 or less, since the interfacial force is low, the lubrication properties are lowered. Preference is given to using fatty acid-based lubricants having a content of 11 or more.

상기와 같이 구성된 본 발명은 자동차 부품, 정밀 계측기기, 정밀 화학기기 등의 부품 표면에 간편하게 부착함으로써 도막표면의 폴리머 매트릭스 경계에서 슬립을 야기하여 마찰에 의한 마모와 소음을 감소시켰으며 여기에 자가 윤활 시스템을 적용함으로써 내부의 윤활제가 지속적으로 Migration되어 폴리머 매트릭스의 경계에서 윤활레이어를 형성하여 슬립을 극대화함으로써 마찰에 의한 열화와 소음을 방지한다.The present invention configured as described above easily adheres to the surface of components such as automobile parts, precision measuring instruments, and fine chemicals, causing slip at the polymer matrix boundary of the coating film surface, thereby reducing frictional wear and noise, and in addition to the self-lubrication system. By applying, the internal lubricant is continuously migrated to form a lubrication layer at the boundary of the polymer matrix to maximize slip to prevent deterioration and noise caused by friction.

이상 본 발명에 의한 자가 윤활패드에 대하여 설명하였다.The self-lubricating pad according to the present invention has been described above.

상기 본 발명의 기술적 구성은 본 발명이 속하는 기술분야의 당업자가 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다.It will be understood by those skilled in the art that the technical features of the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof.

그러므로, 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해되어야 하고, 본 발명의 범위는 전술한 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 이미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 할 것이다.Therefore, the above-described embodiments are to be understood in all respects as illustrative and not restrictive, the scope of the invention being indicated by the following claims rather than the foregoing detailed description, and already and All changes or modifications derived from the scope and equivalent concepts thereof should be construed as being included in the scope of the present invention.

Claims (29)

폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 40~95중량%와, 실리콘 수지 5~60중량%가 혼합되어 구성된 개질윤활층;
상기 개질윤활층의 하부에 도포된 점착제;를 포함하여 구성된 것을 특징으로 하는 자가 윤활패드.
A modified lubricating layer comprising 40 to 95% by weight of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate, and 5 to 60% by weight of a silicone resin;
Self-adhesive pad, characterized in that configured; including a pressure-sensitive adhesive applied to the lower portion of the modified lubrication layer.
제1항에 있어서,
상기 개질윤활층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자 수지와 실리콘 수지 혼합물의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 1,
The modified lubrication layer is configured to further include a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is characterized in that the mixing is not more than 3% by weight relative to the weight of the polymer resin and silicone resin mixture Self-lubricating pad.
제1항에 있어서,
상기 개질윤활층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자 수지와 실리콘 수지 혼합물의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 1,
The reformed lubricating layer is configured to further comprise a sieving pigment, wherein the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin and silicone resin mixture.
제1항에 있어서,
상기 개질윤활층과 점착제 사이에는 폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성된 지지층이 더 포함되어 구성된 것을 특징으로 하는 자가 윤활패드.
The method of claim 1,
A self-lubricating pad, characterized in that further comprising a support layer formed of a polymer resin, which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate between the modified lubrication layer and the pressure-sensitive adhesive.
제4항에 있어서,
상기 지지층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자 수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
5. The method of claim 4,
The support layer is configured to further comprise a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is self-lubricating pad, characterized in that mixed in a range not exceeding 3% by weight of the polymer resin.
제4항에 있어서,
상기 지지층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
5. The method of claim 4,
The support layer is configured to further comprise a sieving pigment, the sieving pigment is characterized in that the self-lubricating pad is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin.
제1항에 있어서,
상기 개질윤활층과 점착제 사이에 PET(Polyethylene terephthalate resin) 수지를 재질로 형성된 기재가 더 포함되어 구성된 것을 특징으로 하는 자가 윤활패드.
The method of claim 1,
Self-lubricating pad, characterized in that further comprising a substrate formed of a polyethylene terephthalate resin (PET) resin between the modified lubricating layer and the adhesive.
제7항에 있어서,
상기 기재는 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 PET 수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 7, wherein
The substrate further comprises a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is self-lubricating pad, characterized in that mixed in a range not exceeding 3% by weight of the PET resin.
제7항에 있어서,
상기 기재는 체질안료를 더 포함하여 구성되되, 상기 체질안료는 PET 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 7, wherein
The substrate is configured to further comprise a extender pigment, wherein the extender pigment is self-lubricating pad, characterized in that the mixing in the range not to exceed 20% by weight relative to the weight of the PET resin.
제1항에 있어서,
상기 개질윤활층의 하부에는,
폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성된 지지층;을 더 포함하고,
상기 지지층의 하부에는 PET(Polyethylene terephthalate resin) 수지를 재질로 형성된 기재;를 더 포함하여 구성된 것을 특징으로 하는 자가 윤활패드.
The method of claim 1,
Under the modified lubrication layer,
And a support layer formed of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate.
A lower portion of the support layer is a self-lubricating pad, characterized in that it further comprises; a substrate formed of a material of polyethylene terephthalate resin (PET) resin.
폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 35~95중량%와, 실리콘 수지 1~60중량%, 윤활제 0.1~30중량%가 혼합되어 구성된 자가윤활층;,
상기 자가윤활층의 하부에 형성되는 폴리올과 이소시아네이트로 반응되어 형성된 수지, 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성된 지지층; 또는 PET(Polyethylene terephthalate resin) 수지를 재질로 형성된 기재;,
상기 지지층 또는 기재의 하부에 도포된 점착제;를 포함하여 구성된 것을 특징으로 하는 자가 윤활패드.
A self-lubricating layer comprising 35 to 95% by weight of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate, 1 to 60% by weight of a silicone resin, and 0.1 to 30% by weight of a lubricant;
A support layer formed of a polymer resin which is a resin, a urethane reaction resin, or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate formed under the self-lubricating layer; Or a substrate formed of polyethylene terephthalate resin (PET) resin;
Self-adhesive pad, characterized in that comprises ;; an adhesive applied to the lower portion of the support layer or the substrate.
제11항에 있어서,
상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합된 것을 특징으로 하는 자가 윤활패드.
The method of claim 11,
The lubricant is a self-lubricating pad, characterized in that any one or two or more of the silicone-based, fluorine-based, fatty acid-based, PE-based or PP-based lubricants are mixed.
제12항에 있어서,
상기 불소계 윤활제는 분자량이 500이상인 것을 특징으로 하는 자가 윤활패드.
The method of claim 12,
The fluorine-based lubricant is a self-lubricating pad, characterized in that the molecular weight is 500 or more.
제12항에 있어서,
상기 실리콘계 윤활제는 분자량이 700~70,000인 것을 특징으로 하는 자가 윤활패드.
The method of claim 12,
The silicone lubricant is self-lubricating pad, characterized in that the molecular weight is 700 ~ 70,000.
제12항에 있어서,
상기 지방산계 윤활제는 분자구조 중 탄소의 함량이 11개 이상인 것을 특징으로 하는 자가 윤활패드.
The method of claim 12,
The fatty acid-based lubricant is a self-lubricating pad, characterized in that the content of more than 11 carbon in the molecular structure.
제11항에 있어서,
상기 자가윤활층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자수지, 실리콘수지 및 윤활제의 혼합물 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 11,
The self-lubricating layer further comprises a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is mixed in a range not exceeding 3% by weight relative to the weight of the mixture of polymer resin, silicone resin and lubricant. Self-lubricating pad.
제11항에 있어서,
상기 자가윤활층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자수지, 실리콘수지 및 윤활제의 혼합물 중량대비 PET 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 11,
The self-lubricating layer is configured to further comprise a sieving pigment, wherein the sieving pigment is characterized in that it is mixed in a range not exceeding 20% by weight relative to the weight of the PET resin to the weight of the mixture of the polymer resin, silicone resin and lubricant Lubrication pads.
제11항에 있어서,
상기 지지층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자 수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 11,
The support layer is configured to further comprise a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is self-lubricating pad, characterized in that mixed in a range not exceeding 3% by weight of the polymer resin.
제11항에 있어서,
상기 지지층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자 수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 11,
The support layer is configured to further comprise a sieving pigment, the sieving pigment is characterized in that the self-lubricating pad is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin.
폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 35~95중량%와, 실리콘 수지 1~60중량%, 윤활제 0.1~30중량%가 혼합되어 구성된 자가윤활층;,
폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성되어 상기 자가윤활층의 하부에 형성되는 지지층;,
PET(Polyethylene terephthalate resin) 수지를 재질로 형성되어 상기 지지층의 하부에 형성되는 기재;,
상기 기재의 하부에 도포된 점착제;를 포함하여 구성된 것을 특징으로 하는 자가 윤활패드.
A self-lubricating layer comprising 35 to 95% by weight of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate, 1 to 60% by weight of a silicone resin, and 0.1 to 30% by weight of a lubricant;
A support layer formed of a polymer resin that is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate and formed under the self-lubricating layer;
A substrate formed of polyethylene terephthalate resin (PET) resin and formed under the support layer;
Self-adhesive pad, characterized in that comprises; adhesive applied to the lower portion of the base.
폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄발포 반응 수지인 고분자 수지 70~99.9중량%와, 윤활제 0.1~30중량%가 혼합되어 구성된 윤활층;,
폴리올과 이소시아네이트로 반응되어 형성된 우레탄 반응 수지 또는 우레탄 발포 반응 수지인 고분자 수지를 재질로 형성되어 상기 윤활층 하부에 형성되는 지지층; 및
상기 지지층하부에 도포되는 점착제;를 포함하여 구성된 것을 특징으로 하는 자가 윤활패드.
A lubricating layer comprising 70 to 99.9 wt% of a polymer resin which is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate, and 0.1 to 30% by weight of a lubricant;
A support layer formed of a polymer resin that is a urethane reaction resin or a urethane foaming reaction resin formed by reacting with a polyol and an isocyanate and formed under the lubrication layer; And
Self-adhesive pads, characterized in that comprises; an adhesive applied to the lower support layer.
제21항에 있어서,
상기 윤활층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자수지 및 윤활제 혼합물의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 21,
The lubricating layer is configured to further include a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is self-lubricating, characterized in that mixing in a range not exceeding 3% by weight relative to the weight of the polymer resin and lubricant mixture pad.
제21항에 있어서,
상기 윤활층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자수지 및 윤활제 혼합물의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 21,
The lubricating layer is configured to further comprise a sieving pigment, wherein the sieving pigment is characterized in that the self-lubricating pad is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin and the lubricant mixture.
제21항에 있어서,
상기 윤활제는 실리콘계, 불소계, 지방산계, PE계 또는 PP계 윤활제 중 어느 하나 또는 둘 이상이 혼합된 것을 특징으로 하는 자가 윤활패드.
The method of claim 21,
The lubricant is a self-lubricating pad, characterized in that any one or two or more of the silicone-based, fluorine-based, fatty acid-based, PE-based or PP-based lubricants are mixed.
제24항에 있어서,
상기 불소계 윤활제는 분자량이 500이상인 것을 특징으로 하는 자가 윤활패드.
25. The method of claim 24,
The fluorine-based lubricant is a self-lubricating pad, characterized in that the molecular weight is 500 or more.
제24항에 있어서,
상기 실리콘계 윤활제는 분자량이 700~70,000인 것을 특징으로 하는 자가 윤활패드.
25. The method of claim 24,
The silicone lubricant is self-lubricating pad, characterized in that the molecular weight is 700 ~ 70,000.
제24항에 있어서,
상기 지방산계 윤활제는 분자구조 중 탄소의 함량이 11개 이상인 것을 특징으로 하는 자가 윤활패드.
25. The method of claim 24,
The fatty acid-based lubricant is a self-lubricating pad, characterized in that the content of more than 11 carbon in the molecular structure.
제21항에 있어서,
상기 지지층은 경화촉진제 또는 경화지연제를 더 포함하여 구성되되, 상기 경화촉진제 또는 경화지연제는 고분자수지의 중량대비 3중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 21,
The support layer is configured to further comprise a curing accelerator or a curing retardant, wherein the curing accelerator or curing retardant is self-lubricating pad, characterized in that the mixing in the range not to exceed 3% by weight of the polymer resin.
제21항에 있어서,
상기 지지층은 체질안료를 더 포함하여 구성되되, 상기 체질안료는 고분자수지의 중량대비 20중량%를 초과하지 않는 범위로 혼합되는 것을 특징으로 하는 자가 윤활패드.
The method of claim 21,
The support layer is configured to further comprise a sieving pigment, the sieving pigment is characterized in that the self-lubricating pad is mixed in a range not exceeding 20% by weight relative to the weight of the polymer resin.
KR1020110109935A 2011-10-26 2011-10-26 Self lubricant pad KR101345654B1 (en)