KR20130041524A - Lubricating strip for use in wet shaving systems which comprises a bio-degradable polymer - Google Patents

Lubricating strip for use in wet shaving systems which comprises a bio-degradable polymer Download PDF

Info

Publication number
KR20130041524A
KR20130041524A KR1020110105829A KR20110105829A KR20130041524A KR 20130041524 A KR20130041524 A KR 20130041524A KR 1020110105829 A KR1020110105829 A KR 1020110105829A KR 20110105829 A KR20110105829 A KR 20110105829A KR 20130041524 A KR20130041524 A KR 20130041524A
Authority
KR
South Korea
Prior art keywords
weight
water
parts
acid
aliphatic
Prior art date
Application number
KR1020110105829A
Other languages
Korean (ko)
Inventor
서병준
이경식
Original Assignee
주식회사 도루코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 도루코 filed Critical 주식회사 도루코
Priority to KR1020110105829A priority Critical patent/KR20130041524A/en
Priority to PCT/KR2012/008496 priority patent/WO2013058550A2/en
Publication of KR20130041524A publication Critical patent/KR20130041524A/en

Abstract

PURPOSE: A lubrication band for a wet-type shaving razor is provided to maintain a lubrication function by hydrolysis using polyester resin, to reduce environmental loads through biodegrading, and to manufacture a dermotropic lubrication band using resin extracted from a plant. CONSTITUTION: A lubrication band(40) of a wet-type shaving razor is made of a composite including non-aqueous polylactide, aliphatic polyester, water soluble polymer, and viscosity increasing agent.

Description

습식 면도 시스템의 윤활밴드{Lubricating strip for use in wet shaving systems which comprises a bio-degradable polymer}Lubricating strip for wet shaving systems which comprises a bio-degradable polymer

본 발명은 습식 면도 시스템의 면도기 윤활밴드에 관한 것으로서 비 수용성 물질에 피부 친화적이며 생분해 기능을 가진 폴리에스테르 수지를 포함하는 습식 면도 시스템의 면도기 윤활밴드에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to razor lubricating bands of wet shaving systems, and to razor lubricating bands of wet shaving systems comprising a polyester resin that is skin-friendly and biodegradable to non-aqueous materials.

최근 면도기 분야에서 윤활밴드의 피부 기능성을 중요시하고 있다. 그러나 피부에 직접적으로 접속하는 밴드의 매트릭스 구성물을 석유계로부터 유래된 폴리에틸렌, 폴리프로필렌, 폴리스티렌 및 폴리아세틸을 사용하고 있다.Recently, in the field of razors, the skin functionality of the lubrication band is important. However, ethylene-derived polyethylene, polypropylene, polystyrene and polyacetyl are used as the matrix composition of the band that directly connects to the skin.

석유계 수지는 생분해성 수지에 비하여 내열성, 내후성, 제품 균일성에서 우수하지만, 폐기시 분해가 되지 않고 축적되어 환경 부하를 높일 수 있으며, 식물에서 추출하여 만들어진 폴리락트산계 수지 보다 민감성 피부의 경우 자극적일 수 있다.Although petroleum resin is superior in heat resistance, weather resistance and product uniformity compared to biodegradable resin, it can accumulate without disassembly at the time of disposal and can increase environmental load, and it is more irritating to sensitive skin than polylactic acid resin extracted from plants. Can be.

또한 매트릭스의 내구성이 너무 강하면, 지속적이면서도 면도기 수명이 다 될 때까지 수용성 폴리머들의 용출이 용이하지 못해 사용자로 하여금 마찰견인, 절모 필요한 힘, 피부손상의 등의 요인을 야기할 수 있지만 폴리락트산을 사용하면 수분과의 가수분해로 면도기 수명 다 할 때까지 지속적인 용출을 기대할 수 있다.Also, if the durability of the matrix is too strong, it will not be easy to dissolve the water-soluble polymers until the end of the razor's life is continuous, which may cause the user to cause factors such as friction towing, force reduction, and skin damage. This can be expected to continue dissolution until the end of the shaver life by hydrolysis with water.

하지만 폴리락트산 단독으로 사용할 경우 사출공정상 열에 대한 내열성이 너무 낮아 수지의 용융으로 미성형 또는 버어(burr) 발생 문제가 나타나고 열접착력이 너무 강하여 압출공정 또한 용이하지 못한 문제점이 있으며 또한 공정에서 재결정화 시간이 길어 양산성에 문제가 있다. 이러한 문제점들의 해결이 요망되고 있다.However, when polylactic acid alone is used, the heat resistance to heat in the injection process is so low that unmolding or burr occurs due to melting of the resin, and the heat adhesion is so strong that the extrusion process is not easy. There is a problem with mass productivity because of the long time. There is a need for solving these problems.

본 발명의 목적은, 습식면도에서 윤활밴드의 비수용성 구성물을 생분해성 폴리유산이 대표적인 폴리 에스테르계 수지의 사용을 통하여 자체가수분해로 윤활 기능을 지속하고 생분해를 통하여 환경부하를 줄이며, 식물 추출 수지를 사용함으로 피부친화적 윤활밴드를 제조하는 것이다.An object of the present invention is to maintain the lubrication function by self-hydrolysis and reduce the environmental load through biodegradation through the use of a polyester resin, the biodegradable polylactic acid is a water-insoluble component of the lubrication band in wet shaving, plant extraction resin By using to prepare a skin-friendly lubrication band.

본 발명은, 비수용성의 폴리락티드; 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르; 수용성 폴리머; 및 점도 증진제를 포함하는 윤활밴드 조성물로 형성된 것을 특징으로 하는 습식 면도 시스템의 윤활밴드를 제공한다.The present invention is a water-insoluble polylactide; Water-insoluble aliphatic polyesters or aliphatic-aromatic polyesters; Water-soluble polymers; And a lubrication band composition comprising a viscosity enhancer.

본 발명은, 상기 습식 면도 시스템의 윤활밴드를 포함하는 것을 특징으로 하는 면도기를 제공한다.The present invention provides a razor comprising a lubrication band of the wet shaving system.

본 발명은, 비수용성의 폴리락티드; 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르; 수용성 폴리머; 및 점도 증진제를 포함하는 윤활밴드 조성물을 준비하는 단계 및 상기 윤활밴드 조성물을 사출하는 단계를 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법을 제공한다.The present invention is a water-insoluble polylactide; Water-insoluble aliphatic polyesters or aliphatic-aromatic polyesters; Water-soluble polymers; And a step of preparing a lubrication band composition comprising a viscosity enhancer and injecting the lubrication band composition.

습식 면도 시스템에서 수용성 폴리머를 석유계에서 생분해성 폴리유산으로 대체함으로 친환경성 확보(생분해, 저온 공정) 식물 유래 수지 사용을 통한 피부 저자극 가수분해를 통해 지속적인 용출 성능 발휘 등의 효과를 보일 수 있다.Securing environment-friendly (biodegradation, low temperature process) by replacing water-soluble polymer with biodegradable polylactic acid in petroleum in wet shaving system, it can show the effect of continuous dissolution performance through skin hypoallergenic hydrolysis through the use of plant-derived resin. .

윤활밴드 제조 공정 중 폴리 유산을 별도로 개질하여 생분해성은 유지하면서 공정상 열접착력, 내열성 부족 등의 문제점을 해결할 수 있다.By modifying the polylactic acid separately during the lubrication band manufacturing process, it is possible to solve problems such as heat adhesion and lack of heat resistance while maintaining biodegradability.

도 1은 일 실시예로서 습식 면도기의 카트리지 분해 사시도이다.1 is an exploded perspective view of a cartridge of a wet shaver in one embodiment.

이하, 본 발명의 바람직한 실시예를 설명한다.Hereinafter, preferred embodiments of the present invention will be described.

습식 면도기는 다수의 면도날이 결합되어 있는 카트리지와 손잡이로 구성된다.Wet razors consist of a cartridge and a handle to which a plurality of razor blades are coupled.

도 1은 습식 면도기의 일 실시예로서, 카트리지의 분해도를 도시한 것이다.1 illustrates an exploded view of a cartridge as one embodiment of a wet shaver.

도 1을 참조하면 카트리지 몸체(10), 카트리지 몸체(10)에 설치되는 면도날(20), 면도날(20)의 양단을 고정시키는 클립(30)과, 면도날(20)의 후방에 구비되는 윤활밴드(40), 면도날(20)의 전방에 구비되는 가드바(50), 및 카트리지 몸체(10)가 손잡이와 결합하도록 하는 연결부(60)를 포함하여 구성된다.Referring to FIG. 1, the cartridge body 10, the razor blade 20 installed on the cartridge body 10, a clip 30 fixing both ends of the razor blade 20, and a lubrication band provided at the rear of the razor blade 20. 40, the guard bar 50 provided in front of the blade 20, and the cartridge body 10 is configured to include a connection portion 60 to engage with the handle.

한편, 본 발명에 따른 습식 면도기의 윤활밴드는, 비수용성의 폴리락티드; 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르; 수용성 폴리머; 및 점도 증진제를 포함하는 윤활밴드 조성물로 형성된 것을 특징으로 한다.On the other hand, the lubrication band of the wet razor according to the present invention, water-insoluble polylactide; Water-insoluble aliphatic polyesters or aliphatic-aromatic polyesters; Water-soluble polymers; And a lubrication band composition comprising a viscosity enhancer.

상기 수용성 폴리머는, 산화폴리에틸렌, 폴리비닐 피롤리돈, 아크릴로부타디엔스티렌, 폴리아크릴아미드, 및 폴리하이드록시에틸메타크릴레이트 중에서 선택될 수 있다.The water-soluble polymer may be selected from polyethylene oxide, polyvinyl pyrrolidone, acrylobutadiene styrene, polyacrylamide, and polyhydroxyethyl methacrylate.

상기 점도 증진제는, 소듐 폴리아크릴레이트, 메틸셀룰로우즈, 하이드록시프로필메틸셀룰로우즈, 카르복시메틸셀룰로우즈, 및 폴리에틸렌글리콜 중에서 선택될 수 있다.The viscosity enhancer may be selected from sodium polyacrylate, methylcellulose, hydroxypropylmethylcellulose, carboxymethylcellulose, and polyethylene glycol.

상기 윤활밴드 조성물은, 무기물, 결정화제, 및 분산제 중 선택된 1종 이상의 첨가제를 더 포함할 수 있다.The lubricating band composition may further include at least one additive selected from an inorganic substance, a crystallizing agent, and a dispersing agent.

상기 윤활밴드 조성물 총 100중량부를 기준으로, 상기 비수용성의 폴리락티드 20~50 중량부, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 5~15 중량부, 상기 무기물 1~20 중량부, 상기 결정화제 0.1~5중량부, 상기 분산제 0.1~5중량부, 상기 수용성 폴리머 50~80 중량부, 및 상기 점도 증진제 1~20중량부로 포함할 수 있다.Based on 100 parts by weight of the total lubrication band composition, 20 to 50 parts by weight of the water-insoluble polylactide, 5 to 15 parts by weight of the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and 1 to 20 parts by weight of the inorganic material. 0.1 to 5 parts by weight of the crystallization agent, 0.1 to 5 parts by weight of the dispersant, 50 to 80 parts by weight of the water-soluble polymer, and 1 to 20 parts by weight of the viscosity enhancer.

상기 윤활밴드 조성물 총 100중량부를 기준으로, 상기 비수용성의 폴리락티드 20~50 중량부, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 5~15 중량부, 상기 수용성 폴리머 50~80 중량부, 및 상기 점도 증진제 10~20 중량부로 포함할 수 있다.20 to 50 parts by weight of the water-insoluble polylactide, 5 to 15 parts by weight of the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and 50 to 80 parts by weight of the water-soluble polymer, based on 100 parts by weight of the lubricating band composition. And 10 to 20 parts by weight of the viscosity enhancer.

상기 폴리락티드의 중량 평균분자량은 1만~40만일 수 있다.The weight average molecular weight of the polylactide may be 10,000 to 400,000.

상기 지방족 폴리에스테르의 혼합량 또는 공중합량은 혼합체 또는 공중합체의 전량에 대하여 1～40 중량부일 수 있다.The mixed amount or copolymerization amount of the aliphatic polyester may be 1 to 40 parts by weight based on the total amount of the mixture or copolymer.

구체적으로 설명하면, 이 지방족 폴리에스테르의 혼합량 또는 공중합량은 혼합체 또는 공중합체의 전량에 대하여 1～10 중량% 정도, TiO2의 혼합량은 혼합체 전량을 기준으로 1～40 중량% 정도, 바람직하게는 5～30 중량%, 더욱 바람직하게는 10～20 중량% 이고, 이 밖의 첨가제의 혼합량은 혼합체 전량을 기준으로 1～5% 정도가 적합하다.Specifically, the mixed amount or copolymerized amount of the aliphatic polyester is about 1 to 10% by weight based on the total amount of the mixture or copolymer, and the mixed amount of TiO 2 is about 1 to 40% by weight based on the total amount of the mixture, preferably 5 It is 30 to 30 weight%, More preferably, it is 10 to 20 weight%, The amount of mixing of other additives is suitable about 1 to 5% based on the whole mixture amount.

상기 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르로는, 폴리히드록시카르본산, 히드록시카르본산 또는 지방족 다가알콜과 지방족 다가염기산으로 이루어지는 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 또는 히드록시카르본산이나 지방족 다가알콜에서 선택되는 2종 이상의 모노머 성분 및 지방족 다가염기산에서 선택되는 2종 이상의 모노머 성분으로 이루어지는 랜덤 공중합체 또는 블록 공중합체의 단독 또는 2종 이상을 혼합한 것 또는 랜덤 공중합 또는 블록 공중합 시킨 것일 수 있다.As said aliphatic polyester or aliphatic-aromatic polyester, an aliphatic polyester or aliphatic-aromatic polyester or hydroxycarboxylic acid or aliphatic consisting of polyhydroxycarboxylic acid, hydroxycarboxylic acid or aliphatic polyhydric alcohol and aliphatic polybasic acid. One or more of random copolymers or block copolymers composed of two or more monomer components selected from polyhydric alcohols and two or more monomer components selected from aliphatic polybasic acids or mixed or random copolymerized or block copolymerized Can be.

상기 히드록시카르본산은, 글리콜산, L-젖산, D-젖산, D/L-젖산, 3-히드록시브티르산, 4-히드록시브티르산, 3-히드록시발레르산, 5-히드록시발레르산, 6-히드록시카프론산 중에서 선택된 1종 이상을 포함할 수 있다.The hydroxycarboxylic acid, glycolic acid, L- lactic acid, D- lactic acid, D / L- lactic acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, 3-hydroxy valeric acid, 5- hydrate It may include one or more selected from oxyvaleric acid, 6-hydroxycapronic acid.

상기 지방족 다가알콜은, 에틸렌 글리콜, 디에틸렌 글리콜, 트리에틸렌 글리콜, 폴리에틸렌 글리콜, 프로필렌 글리콜, 디프로필렌 글리콜, 1,3-부탄디올, 1,4-부탄디올, 3-메틸-1,5-펜탄디올, 1,6-헥산디올, 1,9-노난디올, 네오펜틸 글리콜, 폴리테트라메틸렌 글리콜, 1,4-사이클로헥산디메탄올, 1,4-벤젠디메탄올 중에서 선택된 1종 이상을 포함할 수 있다.The aliphatic polyhydric alcohol is ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, 1,3-butanediol, 1,4-butanediol, 3-methyl-1,5-pentanediol, It may include one or more selected from 1,6-hexanediol, 1,9-nonanediol, neopentyl glycol, polytetramethylene glycol, 1,4-cyclohexanedimethanol, 1,4-benzenedimethanol.

상기 지방족 다가염기산은 숙신산, 옥살산, 말론산, 글루타르산, 아디프산, 피메린산(pimelic acid), 스베린산(sberic acid), 아젤라인산(azelaic acid), 세바신산, 운데칸 디카르복시산, 도데칸 디카르복시산, 페닐숙신산, 1,4-페닐렌 디아세트산 중에서 선택된 1종 이상을 포함할 수 있다.The aliphatic polybasic acid is succinic acid, oxalic acid, malonic acid, glutaric acid, adipic acid, pimelic acid (pimelic acid), sberic acid, azelaic acid (azelaic acid), sebacic acid, undecane dicarboxylic acid It may include one or more selected from dodecane dicarboxylic acid, phenyl succinic acid, 1,4-phenylene diacetic acid.

예컨대, 상기 폴리락티드는 60~99중량부로 포함하고, 상기 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르는 1~40중량부로 포함하는 것이 바람직하다.For example, the polylactide is included in 60 to 99 parts by weight, and the aliphatic polyester or aliphatic-aromatic polyester is preferably included in 1 to 40 parts by weight.

여기서, 상기 첨가량 범위 보다 과량으로 첨가되면 분산성이 저하될 수 있고 원가 상승이 초래될 수 있으며, 상기 첨가량 범위 보다 소량으로 첨가되면 유연성이 저하될 수 있다.In this case, when the amount is added in an amount exceeding the range of addition, the dispersibility may be lowered and a cost increase may be caused. When the amount is added in a smaller amount than the range of addition, flexibility may be lowered.

한편, 본 발명에 따른 면도기는, 상기 습식 면도 시스템의 윤활밴드를 포함할 수 있다.On the other hand, the razor according to the present invention may include a lubrication band of the wet shaving system.

한편, 습식 면도 시스템의 윤활밴드의 제조방법은, 비수용성의 폴리락티드; 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르; 수용성 폴리머; 및 점도 증진제를 포함하는 윤활밴드 조성물을 준비하는 단계 및 상기 윤활밴드 조성물을 사출하는 단계를 포함할 수 있다. 앞서 설명한 동일한 구성에 대해서는 설명을 생략하기로 한다.On the other hand, the method for producing a lubrication band of the wet shaving system, water-insoluble polylactide; Water-insoluble aliphatic polyesters or aliphatic-aromatic polyesters; Water-soluble polymers; And preparing a lubrication band composition comprising a viscosity enhancer and injecting the lubrication band composition. Description of the same configuration described above will be omitted.

상기 윤활밴드 조성물을 준비하는 단계는, 상기 비수용성의 폴리락티드 및 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르를 포함하는 제 1조성물을 제조하는 단계; 상기 제1조성물에 상기 수용성 폴리머를 첨가하여 제2조성물을 제조하는 단계; 및 상기 제2조성물에 상기 점도 증진제를 첨가하여 상기 윤활밴드 조성물을 제조하는 단계를 포함할 수 있다.The preparing of the lubricating band composition may include preparing a first composition including the water-insoluble polylactide and the water-insoluble aliphatic polyester or aliphatic-aromatic polyester; Preparing a second composition by adding the water-soluble polymer to the first composition; And adding the viscosity enhancer to the second composition to prepare the lubrication band composition.

상기 제1조성물을 제조하는 단계는, 무기물, 결정화제, 및 분산제 중 선택된 1종 이상의 첨가제를 첨가하여 제조할 수 있다.The preparing of the first composition may be performed by adding one or more additives selected from an inorganic material, a crystallization agent, and a dispersant.

상기 제1조성물을 제조하는 단계에서는, 상기 비수용성의 폴리락티드, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르, 및 상기 첨가제를 혼합시켜 상기 비수용성 물질을 개질한 상태로 제조하며, 상기 제2조성물을 제조하는 단계에서는, 상기 제1조성물에 상기 수용성 폴리머를 첨가하여 제조하며, 상기 윤활밴드 조성물을 제조하는 단계에서는, 상기 제2조성물에 상기 점도 증진제를 첨가하여 제조할 수 있다.In the step of preparing the first composition, the water-insoluble polylactide, the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and the additives are mixed to prepare the water-insoluble material in a modified state, In the preparing of the second composition, the water-soluble polymer is added to the first composition, and in the preparing of the lubrication band composition, the viscosity enhancer may be added to the second composition.

이하에서는, 실시예 및 비교예를 통해 본 발명에 대해 더욱 구체적으로 설명하기로 한다. 실시예 및 비교예1,2는 비수용성 폴리락티드 기반의 윤활밴드이고, 비교예3은 기존 폴리스티렌 기반의 윤활밴드이다.Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. Examples and Comparative Examples 1 and 2 are lubricating bands based on water-insoluble polylactide, and Comparative Example 3 is lubricating bands based on existing polystyrene.

실시예Example

윤활밴드 조성물 총 100 중량부를 기준으로, 비수용성 폴리락티드 20중량부(Natureworks 2002D), 지방족 폴리에스테르(Basf ecoflex7011) 5중량부와, 무기물 15중량부, 결정화제 5중량부, 분산제 5중량부를 포함하고, 수용성 산화폴리에틸렌(Meisei ALKOX E-300G/E-30G혼합) 50중량부를 포함하여 제조하였다.Based on 100 parts by weight of the total lubricating band composition, 20 parts by weight of water-insoluble polylactide (Natureworks 2002D), 5 parts by weight of aliphatic polyester (Bas ecoflex7011), 15 parts by weight of inorganic material, 5 parts by weight of crystallization agent, and 5 parts by weight of dispersant. It was prepared, including 50 parts by weight of water-soluble polyethylene oxide (Meisei ALKOX E-300G / E-30G mixture).

상기와 같은 윤활밴드 조성물 총 100 중량부에 점도 증진제 Sodium Polyacrlate (WCS-0702) 5중량부를 포함하여 제조하였다.A total of 100 parts by weight of the lubricating band composition as described above was prepared including 5 parts by weight of a viscosity enhancer Sodium Polyacrlate (WCS-0702).

비교예 1 Comparative Example 1

윤활밴드 조성물 총 100 중량부를 기준으로, 비수용성 폴리락티드 35 중량부(Natureworks 2002D), 지방족-방향족 폴리에스테르(Enpol G4260) 15중량부에, 수용성 산화폴리에틸렌(ALKOX E-300G/E-30G혼합) 50중량부를 포함하여 제조하였다.35 parts by weight of water-insoluble polylactide (Natureworks 2002D), 15 parts by weight of aliphatic-aromatic polyester (Enpol G4260) based on 100 parts by weight of the lubricating band composition, water-soluble polyethylene oxide (ALKOX E-300G / E-30G mixture) ) Was prepared to include 50 parts by weight.

상기와 같은 윤활밴드 조성물 총 100 중량부에 점도 증진제 Sodium Polyacrlate (WCS-0702) 5중량부를 포함하여 제조하였다.A total of 100 parts by weight of the lubricating band composition as described above was prepared including 5 parts by weight of a viscosity enhancer Sodium Polyacrlate (WCS-0702).

비교예 2Comparative Example 2

윤활밴드 조성물 총 100 중량부를 기준으로, 비수용성 폴리락티드 50 중량부(Natureworks 2002D), 수용성 산화폴리에틸렌(ALKOX E-300G/E-30G혼합) 50중량부를 포함하여 제조하였다. 상기와 같은 윤활밴드 조성물 총 100 중량부에 점도 증진제 Sodium Polyacrlate (WCS-0702) 5중량부를 포함하여 제조하였다.Based on 100 parts by weight of the total lubricating band composition, 50 parts by weight of water-insoluble polylactide (Natureworks 2002D) and 50 parts by weight of water-soluble polyethylene oxide (ALKOX E-300G / E-30G mixed) were prepared. A total of 100 parts by weight of the lubricating band composition as described above was prepared including 5 parts by weight of a viscosity enhancer Sodium Polyacrlate (WCS-0702).

비교예 3Comparative Example 3

윤활밴드 조성물 총 100 중량부를 기준으로 비수용성 폴리스티렌 50중량부 (KUMHOHI-425TVL), 수용성 산화폴리에틸렌(ALKOX E-300G/E-30G혼합) 50중량부를 포함하여 제조하였다. 상기와 같은 윤활밴드 조성물 총 100 중량부에 Sodium Polyacrlate (WCS-0702) 5중량부를 포함하여 제조하였다.50 parts by weight of water-insoluble polystyrene (KUMHOHI-425TVL) and 50 parts by weight of water-soluble polyethylene oxide (ALKOX E-300G / E-30G mixed) were prepared based on 100 parts by weight of the lubricating band composition. 100 parts by weight of the lubricating band composition as described above was prepared including 5 parts by weight of Sodium Polyacrlate (WCS-0702).

실험예 1(개질유무 결과)Experimental Example 1 (modification presence result)

폴리유산을 가공 상태와 미가공 상태로 수용성 물질과 조합하여 사출 한 경우 미가공 상태는 냉각시간의 차이가 두 배이상으로 벌어지면서 긴 사출시간을 보이며, 내열성 부족으로 급격한 용융지수의 증가로 불량 발생률이 1.5배 이상 발생하여 양산성에 문제를 보였다. 즉, 개질방법을 택한 실시예방식이 비교예 방식보다 사출성면에서 안정적이었으며, 비교예3보다는 비교예2가 안정적이었고 그중 실시예방식이 가장 우수한 특성이 관찰되었다.When polylactic acid is injected in combination with water-soluble materials in the processed and unprocessed state, the unprocessed state shows a long injection time due to the difference in cooling time more than doubled, and the incidence rate is 1.5 due to rapid increase of the melt index due to lack of heat resistance. Occurred more than twice, showing problems with mass production. That is, the embodiment method using the modified method was more stable in terms of injection properties than the comparative example method, Comparative Example 2 was more stable than Comparative Example 3, and the most excellent characteristics of the Example method was observed.

실험예 2(사출테스트 결과)Experimental Example 2 (Injection Test Results)

비수용성 폴리머 구성분에 폴리유산 기반의 조성물이(실시예 방식) 폴리스티렌 기반의 조성물(비교예3방식)보다 낮은 온도에서 사출이 되었다.The polylactic acid based composition (inventive mode) was injected at a lower temperature than the polystyrene based composition (comparative example 3) in the water-insoluble polymer component.

구체적으로는, 폴리스티렌 기반 조성물의 사출기 노즐온도는 약 210℃ 인 것에 비해, 폴리유산 기반의 조성물 사출시에는 약 190℃의 노즐온도로 용이한 공정 특성의 윤활밴드가 얻어졌다. 이처럼 폴리유산 기반의 조성물은 기존대비 약 20도 낮은 온도에서 사출됨을 알 수 있었다.Specifically, an injection machine nozzle temperature of the polystyrene-based composition was about 210 ° C., whereas a lubrication band of easy process characteristics was obtained at a nozzle temperature of about 190 ° C. when the polylactic acid-based composition was injected. As such, the polylactic acid-based composition was found to be injected at a temperature lower than about 20 degrees.

이와 같이, 낮은 온도에서 사출되면 수용성 폴리머인 산화폴리에틸렌의 열적 분해를 최소화하여 용출기능이 우수해진다. 구체적으로는 2분간 25℃의 water dipping 테스트 결과, 20%의 증가된 용출성능이 관찰되었다.As such, when injected at a low temperature, the thermal decomposition of polyethylene oxide, a water-soluble polymer, is minimized, and the elution function is excellent. Specifically, as a result of water dipping test at 25 ° C. for 2 minutes, an increased dissolution performance of 20% was observed.

또한 환경적인 면에서도 낮은 온도의 사출은 이산화탄소 발생량을 줄여주며 무엇보다도 식물에서 시작된 폴리 유산은 스티렌에 비하여 환경부하가 월등히 낮다.In addition, environmentally friendly low-temperature injection reduces carbon dioxide emissions, and above all, polylactic acid originated from plants has significantly lower environmental load than styrene.

또한 윤활밴드의 용출 성능은 지속력에 있어 폴리 유산의 면도환경에서의 가수분해를 통해 우수하게 지켜지고 있었다.In addition, the dissolution performance of the lubrication band was excellently maintained by hydrolysis in the shaving environment of polylactic acid in terms of sustainability.

이와 같이 본 발명은 1단계로 폴리락티드(PLA)와 지방족 폴리에스테르 및 첨가제를 함께 혼합시킨 비수용성 물질 개질한 상태에서 2단계 수용성물질 첨가가 이루어 진다. 즉, PLA와의 혼합개질 유무를 통해 본 발명의 친환경성, 점도 지속성의 장점이 발휘되는 것이다.As such, the present invention is a two-step water-soluble material is added in a modified state of the water-insoluble material mixed with polylactide (PLA) and aliphatic polyester and additives in one step. In other words, through the presence of mixed reforming with PLA is an advantage of the environment-friendly, viscosity persistence of the present invention.

이처럼 본 발명은 수용성 폴리머를 석유계(HIPS)에서 생분해성 폴리유산(PLA)으로 대체 함으로써, 친환경성 확보(생분해성, 저온 공정), 식물유래 수지 사용을 통한 피부 저자극, 가수분해를 통해 지속적인 용출성능 효과를 가진 PLA윤활밴드를 제공할 수 있다.As such, the present invention replaces a water-soluble polymer with a biodegradable polylactic acid (PLA) in petroleum (HIPS), thereby ensuring environmental friendliness (biodegradable, low temperature process), skin irritation through the use of plant-derived resin, and sustained through hydrolysis. It is possible to provide a PLA lubrication band having an elution performance effect.

10 : 카트리지 몸체 20 : 면도날
30 : 클립 40 : 윤활밴드
50 : 가드바 60 : 연결부10: cartridge body 20: razor blade
30: clip 40: lubrication band
50: guard bar 60: connection

Claims (20)

비수용성의 폴리락티드; 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르; 수용성 폴리머; 및 점도 증진제를 포함하는 윤활밴드 조성물로 형성된 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.Water-insoluble polylactide; Water-insoluble aliphatic polyesters or aliphatic-aromatic polyesters; Water-soluble polymers; And a lubrication band composition comprising a viscosity enhancer. 청구항 1에 있어서,
상기 수용성 폴리머는, 산화폴리에틸렌, 폴리비닐 피롤리돈, 아크릴로부타디엔스티렌, 폴리아크릴아미드, 및 폴리하이드록시에틸메타크릴레이트 중에서 선택되는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 1,
The water-soluble polymer is a lubrication band of a wet shaving system, characterized in that selected from polyethylene oxide, polyvinyl pyrrolidone, acrylobutadiene styrene, polyacrylamide, and polyhydroxyethyl methacrylate. 청구항 1에 있어서,
상기 점도 증진제는, 소듐 폴리아크릴레이트, 메틸셀룰로우즈, 하이드록시프로필메틸셀룰로우즈, 카르복시메틸셀룰로우즈, 및 폴리에틸렌글리콜 중에서 선택되는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 1,
The viscosity enhancer is a lubrication band of a wet shaving system, characterized in that selected from sodium polyacrylate, methyl cellulose, hydroxypropyl methyl cellulose, carboxymethyl cellulose, and polyethylene glycol. 청구항 1에 있어서,
무기물, 결정화제, 및 분산제 중 선택된 1종 이상의 첨가제를 더 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 1,
A lubrication band of a wet shaving system, characterized in that it further comprises at least one additive selected from inorganics, crystallizers, and dispersants. 청구항 4에 있어서,
상기 윤활밴드 조성물 총 100중량부를 기준으로, 상기 비수용성의 폴리락티드 20~50 중량부, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 5~15 중량부, 상기 무기물 1~20 중량부, 상기 결정화제 0.1~5중량부, 상기 분산제 0.1~5중량부, 상기 수용성 폴리머 50~80 중량부, 및 상기 점도 증진제 1~20중량부로 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method of claim 4,
Based on 100 parts by weight of the total lubrication band composition, 20 to 50 parts by weight of the water-insoluble polylactide, 5 to 15 parts by weight of the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and 1 to 20 parts by weight of the inorganic material. , 0.1 to 5 parts by weight of the crystallizing agent, 0.1 to 5 parts by weight of the dispersant, 50 to 80 parts by weight of the water-soluble polymer, and 1 to 20 parts by weight of the viscosity enhancer. 청구항 1에 있어서,
상기 윤활밴드 조성물 총 100중량부를 기준으로, 상기 비수용성의 폴리락티드 20~50 중량부, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 5~15 중량부, 상기 수용성 폴리머 50~80 중량부, 및 상기 점도 증진제 10~20 중량부로 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 1,
20 to 50 parts by weight of the water-insoluble polylactide, 5 to 15 parts by weight of the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and 50 to 80 parts by weight of the water-soluble polymer, based on 100 parts by weight of the lubricating band composition. And a lubrication band of a wet shaving system, comprising 10 to 20 parts by weight of the viscosity enhancer. 청구항 1에 있어서,
상기 폴리락티드의 중량 평균분자량은 1만~40만인 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 1,
Lubricating band of the wet shaving system, characterized in that the weight average molecular weight of the polylactide is 10,000 to 400,000. 청구항 1에 있어서,
상기 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르로는, 폴리히드록시카르본산, 히드록시카르본산 또는 지방족 다가알콜과 지방족 다가염기산으로 이루어지는 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 또는 히드록시카르본산이나 지방족 다가알콜에서 선택되는 2종 이상의 모노머 성분 및 지방족 다가염기산에서 선택되는 2종 이상의 모노머 성분으로 이루어지는 랜덤 공중합체 또는 블록 공중합체의 단독 또는 2종 이상을 혼합한 것 또는 랜덤 공중합 또는 블록 공중합 시킨 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 1,
As said aliphatic polyester or aliphatic-aromatic polyester, an aliphatic polyester or aliphatic-aromatic polyester or hydroxycarboxylic acid or aliphatic consisting of polyhydroxycarboxylic acid, hydroxycarboxylic acid or aliphatic polyhydric alcohol and aliphatic polybasic acid. One or more of random copolymers or block copolymers composed of two or more monomer components selected from polyhydric alcohols and two or more monomer components selected from aliphatic polybasic acids, or a mixture of random copolymers or block copolymers Lubrication band for wet shaving system. 청구항 8에 있어서,
상기 히드록시카르본산은, 글리콜산, L-젖산, D-젖산, D/L-젖산, 3-히드록시브티르산, 4-히드록시브티르산, 3-히드록시발레르산, 5-히드록시발레르산, 6-히드록시카프론산 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 8,
The hydroxycarboxylic acid, glycolic acid, L- lactic acid, D- lactic acid, D / L- lactic acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, 3-hydroxy valeric acid, 5- hydrate Lubricating band of the wet shaving system, characterized in that it comprises at least one selected from oxyvaleric acid, 6-hydroxycapronic acid. 청구항 8에 있어서,
상기 지방족 다가알콜은, 에틸렌 글리콜, 디에틸렌 글리콜, 트리에틸렌 글리콜, 폴리에틸렌 글리콜, 프로필렌 글리콜, 디프로필렌 글리콜, 1,3-부탄디올, 1,4-부탄디올, 3-메틸-1,5-펜탄디올, 1,6-헥산디올, 1,9-노난디올, 네오펜틸 글리콜, 폴리테트라메틸렌 글리콜, 1,4-사이클로헥산디메탄올, 1,4-벤젠디메탄올 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 8,
The aliphatic polyhydric alcohol is ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, 1,3-butanediol, 1,4-butanediol, 3-methyl-1,5-pentanediol, Characterized in that it comprises one or more selected from 1,6-hexanediol, 1,9-nonanediol, neopentyl glycol, polytetramethylene glycol, 1,4-cyclohexanedimethanol, 1,4-benzenedimethanol Lubrication band for wet shaving system. 청구항 8에 있어서,
상기 지방족 다가염기산은 숙신산, 옥살산, 말론산, 글루타르산, 아디프산, 피메린산(pimelic acid), 스베린산(sberic acid), 아젤라인산(azelaic acid), 세바신산, 운데칸 디카르복시산, 도데칸 디카르복시산, 페닐숙신산, 1,4-페닐렌 디아세트산 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드.The method according to claim 8,
The aliphatic polybasic acid is succinic acid, oxalic acid, malonic acid, glutaric acid, adipic acid, pimeric acid (pimelic acid), sberic acid, azelaic acid (azelaic acid), sebacic acid, undecane dicarboxylic acid Lubricating band of the wet shaving system comprising at least one selected from dodecane dicarboxylic acid, phenylsuccinic acid, 1,4-phenylene diacetic acid. 청구항 1 내지 청구항 11 중 어느 한 항에 따른 습식 면도 시스템의 윤활밴드를 포함하는 것을 특징으로 하는 면도기.A razor comprising a lubrication band of a wet shaving system according to any one of the preceding claims. 비수용성의 폴리락티드; 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르; 수용성 폴리머; 및 점도 증진제를 포함하는 윤활밴드 조성물을 준비하는 단계 및
상기 윤활밴드 조성물을 사출하는 단계
를 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법.Water-insoluble polylactide; Water-insoluble aliphatic polyesters or aliphatic-aromatic polyesters; Water soluble polymers; Preparing a lubrication band composition comprising a viscosity enhancer; and
Injecting the lubricating band composition
Method of manufacturing a lubrication band of a wet shaving system comprising a. 청구항 13에 있어서,
상기 윤활밴드 조성물을 준비하는 단계는,
상기 비수용성의 폴리락티드 및 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르를 포함하는 제 1조성물을 제조하는 단계;
상기 제1조성물에 상기 수용성 폴리머를 첨가하여 제2조성물을 제조하는 단계; 및
상기 제2조성물에 상기 점도 증진제를 첨가하여 상기 윤활밴드 조성물을 제조하는 단계를 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법.The method according to claim 13,
Preparing the lubrication band composition,
Preparing a first composition comprising the water-insoluble polylactide and the water-insoluble aliphatic polyester or aliphatic-aromatic polyester;
Preparing a second composition by adding the water-soluble polymer to the first composition; And
Adding the viscosity enhancer to the second composition to produce the lubrication band composition. 청구항 14에 있어서,
상기 제1조성물을 제조하는 단계는, 무기물, 결정화제, 및 분산제 중 선택된 1종 이상의 첨가제를 첨가하여 제조하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법.The method according to claim 14,
The preparing of the first composition may include adding at least one additive selected from an inorganic substance, a crystallizing agent, and a dispersing agent. 청구항 15에 있어서,
상기 제1조성물을 제조하는 단계에서는, 상기 비수용성의 폴리락티드, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르, 및 상기 첨가제를 혼합시켜 상기 비수용성 물질을 개질한 상태로 제조하며,
상기 제2조성물을 제조하는 단계에서는, 상기 제1조성물에 상기 수용성 폴리머를 첨가하여 제조하며,
상기 윤활밴드 조성물을 제조하는 단계에서는, 상기 제2조성물에 상기 점도 증진제를 첨가하여 제조하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법. The method according to claim 15,
In the step of preparing the first composition, the water-insoluble polylactide, the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and the additives are mixed to prepare the water-insoluble material in a modified state,
In the step of preparing the second composition, by adding the water-soluble polymer to the first composition,
In the preparing of the lubrication band composition, the method of manufacturing a lubrication band of a wet shaving system, characterized in that the second composition is added to the viscosity enhancer to produce. 청구항 13에 있어서,
상기 수용성 폴리머는, 산화폴리에틸렌, 폴리비닐 피롤리돈, 아크릴로부타디엔스티렌, 폴리아크릴아미드, 및 폴리하이드록시에틸메타크릴레이트 중에서 선택되는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법.The method according to claim 13,
The water-soluble polymer is selected from polyethylene oxide, polyvinyl pyrrolidone, acrylobutadiene styrene, polyacrylamide, and polyhydroxyethyl methacrylate. 청구항 13에 있어서,
상기 점도 증진제는, 소듐 폴리아크릴레이트, 메틸셀룰로우즈, 하이드록시프로필메틸셀룰로우즈, 카르복시메틸셀룰로우즈, 및 폴리에틸렌글리콜 중에서 선택되는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 제조방법.The method according to claim 13,
The viscosity enhancer, sodium polyacrylate, methyl cellulose, hydroxypropyl methyl cellulose, carboxymethyl cellulose, polyethylene glycol, a method for producing a lubrication band of a wet shaving system, characterized in that the polyethylene glycol. 청구항 15에 있어서,
상기 윤활밴드 조성물 총 100중량부를 기준으로, 상기 비수용성의 폴리락티드 20~50 중량부, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 5~15 중량부, 상기 무기물 1~20 중량부, 상기 결정화제 0.1~5중량부, 상기 분산제 0.1~5중량부, 상기 수용성 폴리머 50~80 중량부, 및 상기 점도 증진제 1~20중량부로 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 윤활밴드의 제조방법.The method according to claim 15,
Based on 100 parts by weight of the total lubrication band composition, 20 to 50 parts by weight of the water-insoluble polylactide, 5 to 15 parts by weight of the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and 1 to 20 parts by weight of the inorganic material. Lubricating the lubrication band of the wet shaving system, characterized in that it comprises 0.1 to 5 parts by weight of the crystallization agent, 0.1 to 5 parts by weight of the dispersant, 50 to 80 parts by weight of the water-soluble polymer, and 1 to 20 parts by weight of the viscosity enhancer. Method of manufacturing the band. 청구항 13에 있어서,
상기 윤활밴드 조성물 총 100중량부를 기준으로, 상기 비수용성의 폴리락티드 20~50 중량부, 상기 비수용성의 지방족 폴리에스테르 또는 지방족-방향족 폴리에스테르 5~15 중량부, 상기 수용성 폴리머 50~80 중량부, 및 상기 점도 증진제 10~20 중량부로 포함하는 것을 특징으로 하는 습식 면도 시스템의 윤활밴드의 윤활밴드의 제조방법.The method according to claim 13,
20 to 50 parts by weight of the water-insoluble polylactide, 5 to 15 parts by weight of the water-insoluble aliphatic polyester or aliphatic-aromatic polyester, and 50 to 80 parts by weight of the water-soluble polymer, based on 100 parts by weight of the lubricating band composition. And a lubrication band of the lubrication band of the wet shaving system, comprising 10 to 20 parts by weight of the viscosity enhancer.
KR1020110105829A 2011-10-17 2011-10-17 Lubricating strip for use in wet shaving systems which comprises a bio-degradable polymer KR20130041524A (en)