KR20120120835A - Eco-friendly tile - Google Patents

Eco-friendly tile Download PDF

Info

Publication number
KR20120120835A
KR20120120835A KR1020110038621A KR20110038621A KR20120120835A KR 20120120835 A KR20120120835 A KR 20120120835A KR 1020110038621 A KR1020110038621 A KR 1020110038621A KR 20110038621 A KR20110038621 A KR 20110038621A KR 20120120835 A KR20120120835 A KR 20120120835A
Authority
KR
South Korea
Prior art keywords
layer
butyl
tertiary
tile
tert
Prior art date
Application number
KR1020110038621A
Other languages
Korean (ko)
Inventor
선현대
Original Assignee
(주)두일
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)두일 filed Critical (주)두일
Priority to KR1020110038621A priority Critical patent/KR20120120835A/en
Publication of KR20120120835A publication Critical patent/KR20120120835A/en

Abstract

PURPOSE: An environmentally-friendly tile is provided to improve the adhesion of a color printing layer, a top layer, a middle layer, and a bottom layer. CONSTITUTION: An environmentally-friendly tile(100) comprises a color printing layer(12), a top layer(14), a middle layer(20), and a bottom layer(30). The top layer is attached to the bottom surface of the color printing layer. The middle layer is attached to the bottom surface of the top layer. The bottom layer is attached to the bottom surface of the middle layer. The middle layer comprises 10-20wt% of elastomer, 55-70wt% of environmentally-friendly main material, 3-5wt% of slip material, 1-3wt% of UV stabilizer, 1-3wt% of antioxidant, and 15-20wt% of filler.

Description

환경친화적인 타일{ECO-FRIENDLY TILE}Eco-Friendly Tiles {ECO-FRIENDLY TILE}

본 발명은 환경친화적인 타일에 관한 것으로, 본 발명은 인체에 무해한 PP나 CPP를 주제로 하여 친환경적인 타일을 제공함과 동시에 수축팽창이 방지됨과 아울러 재활용이 가능하고 안착성이 우수한 타일을 제공하는 것을 목적으로 한다.The present invention relates to an environmentally friendly tile, the present invention is to provide an environmentally friendly tile on the theme of PP or CPP harmless to the human body and at the same time to provide a tile that can be recycled and excellent in seatability while preventing shrinkage expansion. The purpose.

본 발명은 칼라인쇄층; 상기 칼라인쇄층 하면에 합지되는 상지층; 상기 상지층 하면에 합치되는 중지층; 상기 중지층 하면에 합지되는 상지층으로 이루어진 타일에 있어서, 상기 중지층은 탄성체 10-20중량%; 환경친화적 주제 55-70중량%; 슬립제 3-5중량%; 자외선안정제 1-3중량%; 산화방지제 1-3중량%; 충진제 15-20중량%를 포함하여 이루어진다.The present invention is a color printing layer; An upper layer laminated on the lower surface of the color printing layer; A stop layer conforming to the lower surface of the upper layer; In the tile consisting of an upper layer laminated on the lower surface of the stop layer, the stop layer is 10-20% by weight of the elastomer; Environmentally friendly topics 55-70%; 3-5 wt% of a slip agent; 1-3 wt% of ultraviolet stabilizers; 1-3 wt% antioxidant; It comprises 15-20% by weight of filler.

본 발명의 실시예에서는 본 발명은 타일에 한정하여 설명하였지만, 본 발명은 타일에 한정되는 것이 아니라 장판등에도 적용이 가능하다고 할 것이다.In the embodiment of the present invention, the present invention has been described with reference to tiles, but the present invention is not limited to tiles, but may be applied to a floor covering or the like.

일반적으로 타일의 경우에는 재료비가 상대적으로 저렴한 PVC를 주제로 하여 타일을 제조하는 것이 일반적이고, 이러한 타일의 경우에는 PVC재질로 이루어지고 소정의 문양이 형성된 칼라인쇄필름층; 상기 칼라인쇄필름층 하면에 합지되고 PVC재질로 이루어진 상지층; 상기 상지층 하면에 합지되고 PVC 분말 60%와 필러 40%를 혼합하여 제조된 중지층, 상기 중지층 하면에 합지되고 PVC로 이루어진 하지층을 포함하여 이루어지고, 상기 칼라인쇄필름층, 상기 상지층, 상기 중지층, 상기 하지층을 열과 압력으로 합지하여 타일을 제조하여 사용하는 것이 일반적이다.In general, in the case of tiles, it is common to manufacture tiles based on PVC, which is relatively inexpensive in material cost. In the case of such tiles, a color printing film layer made of PVC material and formed with a predetermined pattern; An upper layer layer laminated on the lower surface of the color print film layer and made of PVC material; A stop layer made of a mixture of 60% of PVC powder and 40% of a filler, the bottom layer of which is laminated on the bottom of the stop layer, and includes a base layer made of PVC, wherein the color printing film layer and the top layer It is common to manufacture and use a tile by laminating the stop layer and the base layer with heat and pressure.

상기 PVC로 이루어진 합성타일의 경우에는 PVC를 부드럽게 하는 유연제 프탈레이트는 di(2-ethylhexyl) phthalate (DEHP)를 사용해야 하고, 이 유연제는 내분비선을 교란하여 고환 성장을 저해하는 등 발달, 생식 기능 장애를 유발하고, 특히 태아에게 악영향을 미치고 생식 능력을 저하시키는 공식 독성 물질로 분류되는 문제점이 있다.In the case of the synthetic tile made of PVC, softener phthalate for softening PVC should use di (2-ethylhexyl) phthalate (DEHP), and this softener causes developmental and reproductive dysfunction such as disturbing the testicle growth by disturbing endocrine glands. In particular, there is a problem that is classified as an official toxic substance that adversely affects the fetus and lowers the fertility.

또한, PVC는 온도에 민감하여 여름철에는 타일이 신장되고, 겨울철에는 타일이 수축되는 문제점이 있어 온도 변화에 따라 타일이 뒤틀리거나 타일이 바닥에서 들뜨는 현상을 발생하고, 이러한 문제점을 극복하기 위하여 바닥면에 접착력이 강한 본드를 사용하는데 이 경우에는 본드의 악취가 발생하고 추후 타일 교체시 타일을 바닥에서 분리하는데 상당히 힘들어지는 문제점이 있다. In addition, PVC is sensitive to temperature, which causes the tiles to elongate in the summer and the shrinkage of the tiles in the winter, causing the tiles to be distorted or lifted off the floor in response to temperature changes. In this case, a bond having a strong adhesive strength is used. In this case, there is a problem in that the odor of the bond is generated and it is difficult to separate the tile from the floor when the tile is replaced later.

또한, 중지층에 충진제를 40% 이상 혼합하여 사용하므로 PVC 타일을 재활용하기 어려운 문제점이 있을 뿐만 아니라 많은 충진제 사용으로 인하여 타일의 안착성이 떨어지는 문제점이 있어왔다.
In addition, since the filler is used by mixing more than 40% in the stop layer, there is a problem that it is difficult to recycle the PVC tile, as well as a problem that the seatability of the tile is poor due to the use of many fillers.

본 발명은 상기한 문제점을 극복하기 위한 것으로,The present invention is to overcome the above problems,

본 발명은 인체에 무해한 PP나 CPP를 주제로 하여 친환경적인 타일을 제공함과 동시에 수축팽창이 방지됨과 아울러 재활용이 가능하고 안착성이 우수한 타일을 제공하는 것을 목적으로 한다.
An object of the present invention is to provide an environmentally friendly tile on the subject of PP or CPP harmless to the human body and at the same time to provide a tile that is prevented from shrinkage expansion and is recyclable and has excellent seating properties.

본 발명은 상기한 목적을 달성하기 위하여 다음의 구성으로 이루어진다.The present invention has the following configuration in order to achieve the above object.

본 발명의 친환경적 타일은 칼라인쇄층; 상기 칼라인쇄층 하면에 합지되는 상지층; 상기 상지층 하면에 합지되는 중지층; 상기 중지층 하면에 합지되는 상지층으로 이루어진 타일에 있어서,Eco-friendly tile of the present invention is a color printing layer; An upper layer laminated on the lower surface of the color printing layer; A stop layer laminated on a lower surface of the upper layer; In the tile made of the upper layer laminated on the lower surface of the stop layer,

상기 중지층은 탄성체 10-20중량%; 환경친화적 주제 55-70중량%; 슬립제 3-5중량%; 자외선안정제 1-3중량%; 산화방지제 1-3중량%; 충진제 15-20중량%를 포함하여 이루어진다.
The stop layer is 10-20% by weight of an elastomer; Environmentally friendly topics 55-70%; 3-5 wt% of a slip agent; 1-3 wt% of ultraviolet stabilizers; 1-3 wt% antioxidant; It comprises 15-20% by weight of filler.

또한, 본 발명의 상기 탄성체는 스티렌 에틸렌 또는 스티렌 부타디엔 중 어느 하나이고,In addition, the elastic body of the present invention is any one of styrene ethylene or styrene butadiene,

상기 환경친화적 주제는 PP(폴리프로필렌)이고,The environmentally friendly theme is PP (polypropylene),

상기 슬립제는 스테아르산아연, 올레아미드, 에루카미드, 스테아르아미드 및 베헨아미드로 이루어진 그룹으로부터 선택된 하나인 것을 특징으로 하고,The slip agent is characterized in that the one selected from the group consisting of zinc stearate, oleamide, erucamide, stearamide and behenamide,

상기 자외선 안정제는 벤조페논계, 페닐실리케이트계, 비스(2,2,6,6-테트라메틸-4-피페리디닐)세바케이트, 2-(3',5'-디-터셔리-부틸-2'-히드록시페닐)-5-클로로벤조트리아졸, 2-(3,5-디-터셔리-페닐-2-히드록시페닐)벤조트리아졸, 2-(2'-히드록시-5-메틸페닐)벤조트리아졸, 2-(3'-터셔리-부틸-2'-히드록시-5'-메틸페닐)-5-클로로벤조트리아졸 및 힌다드아민계로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지고,The ultraviolet stabilizer is benzophenone series, phenyl silicate series, bis (2,2,6,6-tetramethyl-4-piperidinyl) sebacate, 2- (3 ', 5'-di-tertiary-butyl- 2'-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di-tertiary-phenyl-2-hydroxyphenyl) benzotriazole, 2- (2'-hydroxy-5- Methylphenyl) benzotriazole, 2- (3'-tertiary-butyl-2'-hydroxy-5'-methylphenyl) -5-chlorobenzotriazole and one or more selected from the group consisting of under,

상기 산화방지제는 1,1,3-트리스(2-메틸-4-히드록시-5-터셔리-부틸페닐)부탄,1,3,5-트리메틸-2,4,6-트리스(3,5-디-터셔리-부틸-4-히드록시벤질)벤젠, 테트라키스-[메틸렌-3-(3'5'-디-터셔리-부틸-4-히드록시페닐)프로피네이트], 비스[3,3'-비스-(4'-하이드록시-3'-터셔리-부틸페닐)부틸릭엑시드]글리콜에스테르, 1,3,5-트리스(3',5'-디-터셔리-부틸-4'-히드록시벤질)-SEC-트리아진-2,4,6-트리온, 3,5-디-터셔리-부틸-4-히드록시히드로시나메이트 옥타데실, 트리스(2,4-디-터셔리-부틸페닐)포스페이트, 시클로 네오펜탄테트라일 비스(2,4-디-터셔리-부틸페닐)포스페이트 및 1,2-비스(3,5-디-터셔리-부틸-4-히드록시히드로시나모일)히드라진으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지고,The antioxidant is 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5 -Di-tert-butyl-4-hydroxybenzyl) benzene, tetrakis- [methylene-3- (3'5'-di-tert-butyl-4-hydroxyphenyl) propinate], bis [3 , 3'-bis- (4'-hydroxy-3'-tertiary-butylphenyl) butylic acid] glycol ester, 1,3,5-tris (3 ', 5'-di-tertiary-butyl- 4'-hydroxybenzyl) -SEC-triazine-2,4,6-trione, 3,5-di-tertiary-butyl-4-hydroxyhydrocinnamate octadecyl, tris (2,4-di Tert-butylphenyl) phosphate, cyclo neopentanetetrayl bis (2,4-di-tert-butylphenyl) phosphate and 1,2-bis (3,5-di-tert-butyl-4-hydride Hydroxyhydrocinnamoyl) hydrazine, including one or more selected from the group consisting of

상기 충진제는 탄산칼슘인 것을 특징으로 한다.
The filler is characterized in that the calcium carbonate.

또한, 본 발명의 상기 칼라인쇄층 및 상기 상지층은 PP(폴리프로필렌 필름) 또는 CPP(무연신 폴리프로필렌 필름)인 것을 특징으로 한다.
In addition, the color printing layer and the upper limb layer of the present invention is characterized in that the PP (polypropylene film) or CPP (non-stretched polypropylene film).

또한, 본 발명의 상기 하지층은 PP(폴리프로필렌 필름) 또는 CPP(무연신 폴리프로필렌 필름)인 것을 특징으로 한다.
In addition, the base layer of the present invention is characterized in that the PP (polypropylene film) or CPP (non-stretched polypropylene film).

본 발명에 의하면,According to the present invention,

본 발명은 인체에 무해한 PP나 CPP를 주제로 한 중지층, 칼라인쇄층, 상지층, 하지층을 PP나 CPP로 합지하여 칼라인쇄층, 상지층, 중지층 및 하지층의 접착이 우수할 뿐만 아니라 PVC와 달리 제조시 인체에 해로운 유연제를 사용하지 않아 친환경적인 타일을 제공할 수 있고,The present invention is excellent in adhesion of the color printing layer, the upper layer, the middle layer and the base layer by laminating PP or CPP-based stop layer, color printing layer, upper layer, and base layer with PP or CPP, which is harmless to human body. However, unlike PVC, it does not use a softener that is harmful to the human body in manufacturing, and thus can provide environmentally friendly tiles.

폴리프로필렌은 PVC와 달리 온도에 따른 수축팽창률이 적어 타일이 두틀리거나 바닥에서 들뜨는 현상을 방지할 수 있고, 폴리프로필렌에 소정의 탄산칼슘을 혼합함으로써 타일의 발랜스를 좋게 안착성이 우수해 지며, 아울러 재활용이 가능한 효과가 있다.
Unlike PVC, polypropylene has a small shrinkage expansion coefficient due to temperature, which prevents warping or lifting of tiles. Also, by mixing predetermined calcium carbonate with polypropylene, the tile has a good balance. In addition, there is an effect that can be recycled.

도 1은 본 발명의 실시예인 타일의 사시도.
도 2는 도 1에 도시된 타일의 분해 사시도.1 is a perspective view of a tile that is an embodiment of the invention.
FIG. 2 is an exploded perspective view of the tile shown in FIG. 1. FIG.

이하, 본 발명의 바람직한 실시예를 첨부된 도면 1 및 2에 의거하여 상세히 설명하면 다음과 같다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the attached drawings 1 and 2 as follows.

본 발명의 일시예인 타일(100)은 칼라인쇄층(12); 상기 칼라인쇄층(12) 하면에 합지되는 상지층(14); 상기 상지층(14) 하면에 합지되는 중지층(20); 상기 중지층(20) 하면에 합지되는 상지층(30)으로 이루어진 타일에 있어서, 상기 중지층(20)은 탄성체 10-20중량%; 환경친화적 주제 55-70중량%; 슬립제 3-5중량%; 자외선안정제 1-3중량%; 산화방지제 1-3중량%; 충진제 15-20중량%를 포함하여 이루어진다.
Tile 100, which is one example of the present invention, includes a color printing layer 12; An upper limb layer 14 laminated on a lower surface of the color printing layer 12; A stop layer 20 laminated on a lower surface of the upper limb layer 14; In the tile made of the upper limb layer 30 laminated on the lower surface of the stop layer 20, the stop layer 20 is 10-20% by weight of the elastomer; Environmentally friendly topics 55-70%; 3-5 wt% of a slip agent; 1-3 wt% of ultraviolet stabilizers; 1-3 wt% antioxidant; It comprises 15-20% by weight of filler.

본 발명의 칼라인쇄층(12) 및 상지층(14)은 PP 또는 CPP를 사용하는 것이 바람직한데, 폴리프로필렌 내지 무연신폴리프로필렌의 경우에는 PVC에서 사용되는 내분비선을 교란하여 고환 성장을 저해하는 등 발달, 생식 기능 장애를 유발하고, 특히 태아에게 악영향을 미치고 생식 능력을 저하시키는 독성 물질인 유연제 프탈레이트는 di(2-ethylhexyl) phthalate (DEHP)를 사용하지 않기 때문이다.Preferably, the color printing layer 12 and the upper limb layer 14 of the present invention use PP or CPP. In the case of polypropylene or non-stretched polypropylene, the endocrine gland used in PVC is disturbed to inhibit testicular growth. Softener phthalate, a toxic substance that causes developmental and reproductive dysfunction, especially adversely affects the fetus and reduces fertility, does not use di (2-ethylhexyl) phthalate (DEHP).

상기 칼라인쇄층(12),상지층(14) 및 하지층(30)을 PP 또는 CPP 필름을 사용함으로써 후술할 주제가 폴리프로필렌인 중지층(20)과 열과 압력에 의한 합지가 용이해진다.
By using the PP or CPP film for the color printing layer 12, the upper layer 14, and the base layer 30, lamination with heat and pressure with the stop layer 20 whose main theme is polypropylene will be facilitated.

상기 폴리프로필렌은 프로필렌(CHCH=CH)의 중합체로서, 가장 가벼운 플라스틱(비중 0.82~0.92)이며, 연화점(軟化點)도 높고 가공성(加工性)도 좋으며, 폴리에틸렌?폴리염화비닐?폴리스티렌과 함께 4대 플라스틱의 하나. 프로필렌의 중합을 라디칼 개시제(開始劑) 중합이나 이온 중합으로 양이온 중합시키면 분자량이 작은 연한 그리스(grease) 모양의 물질만이 얻어진다.The polypropylene is a polymer of propylene (CHCH = CH), is the lightest plastic (specific gravity 0.82 ~ 0.92), has a high softening point, good processability, and together with polyethylene, polyvinyl chloride, polystyrene 4 One of the great plastics. When cationic polymerization of propylene is carried out by radical initiator polymerization or ionic polymerization, only a light grease-like substance having a small molecular weight is obtained.

상기 폴리프로필렌은 트리에틸알루미늄과 삼염화티탄의 복합고체촉매(나타촉매)를 써서 종합시키면, 분자구조적으로 매우 규칙적인 배열을 갖고 결정성(結晶性)도 좋으며 연화점이 170℃인 중합체가 형성된다.When the polypropylene is synthesized using a complex solid catalyst (tricatalyst) of triethylaluminum and titanium trichloride, a polymer having a very regular arrangement in molecular structure, good crystallinity and a softening point of 170 ° C is formed.

상기 폴리프로필렌은 기계적 성질은 폴리에틸렌보다 뛰어나지만, 산소의 존재하에서 빛 또는 열에 의해 산화열화(酸化劣化)하는 결점이 있어 산화안정제가 필요하다.Although the polypropylene is superior in mechanical properties to polyethylene, an oxidative stabilizer is required because of the drawback of oxidation deterioration by light or heat in the presence of oxygen.

또한, 폴리프로필렌은 propylene이 연결된 구조이므로 환경호르몬인 배출될 수 없는 인체에 무해한 성질을 가지고 있고, 공정상에 첨가제를 넣는데, 극 소량일 뿐더러, 무해하다.
In addition, polypropylene has a propylene-connected structure, so it is harmless to the human body, which cannot be discharged as an environmental hormone, and it is very small and harmless to add additives in the process.

CPP 필름은 PP(Polypropylene)를 연신하지 않은 것으로, 무연신 (casting polypropylene) 필름을 CPP필름이라고 하고, CPP Film은 티다이(T-Die) 공법으로 제조되어 두께가 균일하며 투명도와 광택이 우수할뿐 아니라 인쇄적성이 뛰어나고 매우 위생적인 필름이므로 식품포장등 유연포장의 소재로서 폭넓게 이용되고 있다.CPP film is not drawn from PP (Polypropylene) .Casting polypropylene film is called CPP film, and CPP film is manufactured by T-Die method so that it has uniform thickness and excellent transparency and gloss. In addition, the film has excellent printability and is very hygienic, so it is widely used as a material for flexible packaging such as food packaging.

CPP는 열봉함 온도가 150℃ ~ 160℃ 이상일 경우에 열봉합이 이루어지므로 타일 재료로 열과 압력을 가할 경우엔 합지되는 우수한 물성을 가지고 있으며, 투명성이 우수하고 방습성이 우수하며, 표면경도가 크고 내열성이 LDPE 등에 대해 높다. 또한, CPP는 방습성이 우수하다.
CPP is heat sealed when the heat sealing temperature is over 150 ℃ ~ 160 ℃, so it has excellent physical properties that are laminated when heat and pressure are applied to the tile material.It has excellent transparency, excellent moisture resistance, high surface hardness and high heat resistance. This is high for LDPE and the like. In addition, CPP is excellent in moisture resistance.

슬립제는 스테아르산아연, 올레아미드, 에루카미드, 스테아르아미드 및 베헨아미드로 이루어진 그룹으로부터 선택된 하나로 이루어지는데, 1 중량부를 초과하여 사용하게 되면 데코타일 기재층의 접착력이 감소하게 된다.The slip agent consists of one selected from the group consisting of zinc stearate, oleamide, erucamide, stearamide and behenamide, and when used in excess of 1 part by weight, the adhesion of the decorate base layer is reduced.

상기 슬립제는 압출기 실런더 및 스크류와 데코타일 기재층 제조용 조성물 간에 마찰계수를 낮춰주기 때문에 압출 공정시에 원활한 압출을 제공하게 하고, 실린더 및 스크류에 조성물 잔존물이 남는 것을 차단하여 잔존물이 탄화되는 것을 예방하기 때문에 데코타일 기재층의 불량률을 감소시킨다.Since the slip agent lowers the coefficient of friction between the extruder cylinder and the screw and the composition for preparing the decotile base layer, it provides a smooth extrusion during the extrusion process, and blocks the residue of the composition in the cylinder and the screw to prevent carbonation of the residue. Since it prevents, the defect rate of a decorate base material layer is reduced.

상기 슬립제는 3-5중량%를 사용하는 것이 바람직한데, 3% 중량 이하로 슬립제를 혼합할 경우에는 중지층을 압출(칼렌더 포함) 공정시 원활한 압출이 이루어지지 않으며, 5중량%를 혼합시에는 수지 간의 접착력을 떨어트리는 문제점이 있다.
Preferably, the slip agent is used in an amount of 3-5% by weight. When the slip agent is mixed in an amount less than or equal to 3%, the stop layer is not extruded smoothly during the extrusion (including the calendar) process, and 5% by weight is mixed. There is a problem in that the adhesion between the resin drops.

상기 자외선안정제는 타일 표면층의 내광성을 향상시켜 변색을 막아주는 기능을 하며,The UV stabilizer improves the light resistance of the tile surface layer to prevent discoloration,

상기 자외선안정제는 1-3중량%를 사용하는 것이 바람직하고, 상기 자외선방지제를 3중량% 이상 혼합할 경우에는 수지 간의 접착력을 떨어트릴 뿐만 아니라 자외선안정제가 인체에 해롭기 때문에 3중량% 이하로 사용하는 것이 바람직하다.It is preferable to use 1-3% by weight of the UV stabilizer, and when mixing more than 3% by weight of the UV stabilizer not only reduces the adhesive strength between the resin but also used by 3% by weight or less because the UV stabilizer is harmful to the human body It is desirable to.

상기 자외선안정제는 벤조페논계, 페닐실리케이트계, 비스(2,2,6,6-테트라메The ultraviolet stabilizer is benzophenone-based, phenyl silicate-based, bis (2,2,6,6-tetrameth

틸-4-피페리디닐)세바케이트, 2-(3',5'-디-터셔리-부틸-2'-히드록시페닐)-5-클로로벤조트리아졸, 2-(3,5-디-터셔리-페닐-2-히드록시페닐)벤조트리아졸, 2-(2'-히드록시-5-메틸페닐)벤조트리아졸, 2-(3'-터셔리-부틸-2'-히드록시-5'-메틸페닐)-5-클로로벤조트리아졸 및 힌다드아민계 자외선 안정제로 이루어진 그룹으로부터 선택된 하나이상을 포함하여 이루어진다.
Tyl-4-piperidinyl) sebacate, 2- (3 ', 5'-di-tertiary-butyl-2'-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di Tertiary-phenyl-2-hydroxyphenyl) benzotriazole, 2- (2'-hydroxy-5-methylphenyl) benzotriazole, 2- (3'-tertiary-butyl-2'-hydroxy- 5'-methylphenyl) -5-chlorobenzotriazole and a hindered amine based ultraviolet stabilizer.

상기 산화방지제는 타일 표면의 산화를 방지하는 기능을 할 뿐만 아니라 상술한 바와 같이 폴리프로필렌이 산소의 존재하에서 빛 또는 열에 의해 산화열화(酸化劣化)하는 결점을 보강한다.The antioxidant not only functions to prevent oxidation of the tile surface, but also reinforces the drawback that the polypropylene is oxidatively degraded by light or heat in the presence of oxygen as described above.

상기 산화방지제는 1 내지 3 중량부가 함유되며,The antioxidant contains 1 to 3 parts by weight,

상기 산화방지제로는 1,1,3-트리스(2-메틸-4-히드록시-5-터셔리-부틸페닐)부탄, 1,3,5-트리메틸-2,4,6-트리스(3,5-디-터셔리-부틸-4-히드록시벤질)벤젠, 테트라키스-[메틸렌-3-(3'5'-디-터셔리-부틸-4-히드록시페닐)프로피네이트], 비스[3,3'-비스-(4'-하이드록시-3'-터셔리-부틸페닐)부틸릭엑시드]글리콜에스테르, 1,3,5-트리스(3',5'-디-터셔리-부틸-4'-히드록시벤질)-SEC-트리아진-2,4,6-트리온, 3,5-디-터셔리-부틸-4-히드록시히드로시나메이트 옥타데실, 트리스(2,4-디-터셔리-부틸페닐)포스페이트, 시클로 네오펜탄테트라일 비스(2,4-디-터셔리-부틸페닐)포스페이트 및 1,2-비스(3,5-디-터셔리-부틸-4-히드록시히드로시나모일)히드라진으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어진다.
Examples of the antioxidant include 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3, 5-di-tert-butyl-4-hydroxybenzyl) benzene, tetrakis- [methylene-3- (3'5'-di-tert-butyl-4-hydroxyphenyl) propinate], bis [ 3,3'-bis- (4'-hydroxy-3'-tertiary-butylphenyl) butylic acid] glycol ester, 1,3,5-tris (3 ', 5'-di-tertary-butyl -4'-hydroxybenzyl) -SEC-triazine-2,4,6-trione, 3,5-di-tertiary-butyl-4-hydroxyhydrocinnamate octadecyl, tris (2,4- Di-tertiary-butylphenyl) phosphate, cyclo neopentanetetrayl bis (2,4-di-tertiary-butylphenyl) phosphate and 1,2-bis (3,5-di-tertiary-butyl-4- Hydroxyhydrocinnamoyl) hydrazine.

상기 충진제는 탄산칼슘을 사용하는 것이 바람직하고, 상기 충진제는 타일의 밸런스를 잡아주는 기능을 하여 타일 적층시 타일이 들뜨는 현상을 방지할 뿐만 아니라 수지 간의 간극을 충진제로 메움으로써 타일의 경도를 증가시켜 주는 기능을 한다.
The filler is preferably calcium carbonate, and the filler serves to balance the tiles, thereby preventing the tiles from lifting when the tiles are stacked, and increasing the hardness of the tiles by filling the gaps between the resins with fillers. Giving functions.

본 발명의 실시예에서는 본 발명의 실시예를 타일에 한정하여 설명하였지만, 장판 등에도 적용이 가능하다.
In the embodiment of the present invention, the embodiment of the present invention has been described with reference to tiles.

또한, 본 발명의 권리범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허 청구 범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
In addition, the scope of the present invention is represented by the following claims rather than the detailed description, and all changes or modifications derived from the meaning and scope of the claims and equivalent concepts are included in the scope of the present invention. Should be interpreted as

100: 타일 12: 칼라인쇄층
14: 상지층 20: 중지층
30: 하지층100: tile 12: color printing layer
14: upper layer 20: stop layer
30: base layer

Claims (4)

칼라인쇄층;
상기 칼라인쇄층 하면에 합지되는 상지층;
상기 상지층 하면에 합지되는 중지층;
상기 중지층 하면에 합지되는 상지층으로 이루어진 타일에 있어서,
상기 중지층은
탄성체 10-20중량%;
환경친화적 주제 55-70중량%;
슬립제 3-5중량%;
자외선안정제 1-3중량%;
산화방지제 1-3중량%;
충진제 15-20중량%를 포함하여 이루어진 것을 특징으로 하는 친환경적 타일.
Color printing layer;
An upper layer laminated on the lower surface of the color printing layer;
A stop layer laminated on a lower surface of the upper layer;
In the tile made of the upper layer laminated on the lower surface of the stop layer,
The stop layer
10-20% by weight of elastomer;
Environmentally friendly topics 55-70%;
3-5 wt% of a slip agent;
1-3 wt% of ultraviolet stabilizers;
1-3 wt% antioxidant;
Eco-friendly tile, characterized in that it comprises 15-20% by weight of a filler.
제1항에 있어서,
상기 탄성체는 스티렌 에틸렌 또는 스티렌 부타디엔 중 어느 하나이고,
상기 환경친화적 주제는 PP(폴리프로필렌)이고,
상기 슬립제는 스테아르산아연, 올레아미드, 에루카미드, 스테아르아미드 및 베헨아미드로 이루어진 그룹으로부터 선택된 하나인 것을 특징으로 하고,
상기 자외선 안정제는 벤조페논계, 페닐실리케이트계, 비스(2,2,6,6-테트라메틸-4-피페리디닐)세바케이트, 2-(3',5'-디-터셔리-부틸-2'-히드록시페닐)-5-클로로벤조트리아졸, 2-(3,5-디-터셔리-페닐-2-히드록시페닐)벤조트리아졸, 2-(2'-히드록시-5-메틸페닐)벤조트리아졸, 2-(3'-터셔리-부틸-2'-히드록시-5'-메틸페닐)-5-클로로벤조트리아졸 및 힌다드아민계로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지고,
상기 산화방지제는 1,1,3-트리스(2-메틸-4-히드록시-5-터셔리-부틸페닐)부탄,1,3,5-트리메틸-2,4,6-트리스(3,5-디-터셔리-부틸-4-히드록시벤질)벤젠, 테트라키스-[메틸렌-3-(3'5'-디-터셔리-부틸-4-히드록시페닐)프로피네이트], 비스[3,3'-비스-(4'-하이드록시-3'-터셔리-부틸페닐)부틸릭엑시드]글리콜에스테르, 1,3,5-트리스(3',5'-디-터셔리-부틸-4'-히드록시벤질)-SEC-트리아진-2,4,6-트리온, 3,5-디-터셔리-부틸-4-히드록시히드로시나메이트 옥타데실, 트리스(2,4-디-터셔리-부틸페닐)포스페이트, 시클로 네오펜탄테트라일 비스(2,4-디-터셔리-부틸페닐)포스페이트 및 1,2-비스(3,5-디-터셔리-부틸-4-히드록시히드로시나모일)히드라진으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지고,
상기 충진제는 탄산칼슘인 것을 특징으로 하는 친환경적 타일.
The method of claim 1,
The elastomer is any one of styrene ethylene or styrene butadiene,
The environmentally friendly theme is PP (polypropylene),
The slip agent is characterized in that the one selected from the group consisting of zinc stearate, oleamide, erucamide, stearamide and behenamide,
The ultraviolet stabilizer is benzophenone series, phenyl silicate series, bis (2,2,6,6-tetramethyl-4-piperidinyl) sebacate, 2- (3 ', 5'-di-tertiary-butyl- 2'-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di-tertiary-phenyl-2-hydroxyphenyl) benzotriazole, 2- (2'-hydroxy-5- Methylphenyl) benzotriazole, 2- (3'-tertiary-butyl-2'-hydroxy-5'-methylphenyl) -5-chlorobenzotriazole and one or more selected from the group consisting of under,
The antioxidant is 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5 -Di-tert-butyl-4-hydroxybenzyl) benzene, tetrakis- [methylene-3- (3'5'-di-tert-butyl-4-hydroxyphenyl) propinate], bis [3 , 3'-bis- (4'-hydroxy-3'-tertiary-butylphenyl) butylic acid] glycol ester, 1,3,5-tris (3 ', 5'-di-tertiary-butyl- 4'-hydroxybenzyl) -SEC-triazine-2,4,6-trione, 3,5-di-tertiary-butyl-4-hydroxyhydrocinnamate octadecyl, tris (2,4-di Tert-butylphenyl) phosphate, cyclo neopentanetetrayl bis (2,4-di-tert-butylphenyl) phosphate and 1,2-bis (3,5-di-tert-butyl-4-hydride Hydroxyhydrocinnamoyl) hydrazine, including one or more selected from the group consisting of
The filler is environmentally friendly tile, characterized in that the calcium carbonate.
제1항에 있어서,
상기 칼라인쇄층 및 상기 상지층은 PP(폴리프로필렌 필름) 또는 CPP(무연신 폴리프로필렌 필름)인 것을 특징으로 하는 친환경적 타일.
The method of claim 1,
The color printing layer and the upper layer is an environmentally friendly tile, characterized in that the PP (polypropylene film) or CPP (non-stretched polypropylene film).
제1항에 있어서,
상기 하지층은 PP(폴리프로필렌 필름) 또는 CPP(무연신 폴리프로필렌 필름)인 것을 특징으로 하는 친환경적 타일.The method of claim 1,
The base layer is an environmentally friendly tile, characterized in that the PP (polypropylene film) or CPP (non-stretched polypropylene film).
KR1020110038621A 2011-04-25 2011-04-25 Eco-friendly tile KR20120120835A (en)