KR20120108271A - Multi-layer film and method for manufacturing the same - Google Patents

Abstract

PURPOSE: A multi-layer film and manufacturing method thereof are provided to include a good sealing property and a good opening property by providing easy peeling property to a sealant layer. CONSTITUTION: A multi-layer film includes a core layer(10), a sealant layer(20), and a barrier layer(30). The core layer includes polyolefin as base resin. The sealant layer a weight unit including 30~90 sealing resin, another weight unit including 5~50 thermoplastic elastomer, and other weight unit including 2~50 acrylate. The barrier layer includes a resin layer(31) and a deposition layer(32).

Description

Multilayer film and its manufacturing method {MULTI-LAYER FILM AND METHOD FOR MANUFACTURING THE SAME}

The present invention relates to a multilayer film used as a packaging material and a method for manufacturing the same, and more particularly, to provide an easy peel property to a sealant layer, and to have a good sealing property (heat sealing property) while being easy to open. A multilayer film and a method for producing the same.

Multilayer films are mainly used as packaging materials for packing foods (such as confectionery) and medicines. In particular, polyolefin-based films such as polypropylene (PP) and polyethylene (PE) are useful as food packaging materials. The polyolefin-based film is not only advantageous in terms of economy and reproducibility, but also excellent in mechanical properties such as tensile strength, surface hardness, impact resistance, optical properties such as glossiness and transparency, and food hygiene such as non-toxic and odorless, and thus is widely used as a food packaging material. .

Figure 1 shows a cross-sectional configuration of a conventional general polyolefin-based multilayer film.

Referring to FIG. 1, a multilayer film generally includes a core layer 1, a sealant layer formed on one side of the core layer 1, and the core layer 1. Barrier layer 3 formed on the other side of the substrate.

The core layer 1 serves as a substrate, which is mainly composed of polypropylene (PP). The sealant layer 2 is sealed (heat-sealed) by heat after packaging the contents (food, etc.) to give sealing property, which is generally low temperature adhesiveness capable of heat-sealing (heat-sealing) at low temperature. Resin, that is, low melting point resin. The barrier layer 3 is to block entry of external gas such as moisture or air, and the barrier layer 3 is formed of a deposition film having a deposition layer 3b formed on the PP film 3a. In this case, the deposition layer 3b is for gas barrier properties, and is mainly formed by depositing a metal such as aluminum (Al).

The sealant layer 2 is required to be easily melted by heat to facilitate sealing after packaging the contents of food and the like, and to have excellent heat adhesion strength. To this end, the sealant layer 2 is generally used an adhesive resin such as polypropylene (PP) or polyethylene (PE).

However, the sealant layer 2 of the multilayer film according to the prior art has a problem that the adhesive strength is too strong, so that opening is difficult and a manufacturing process is added. For example, in the case of a packaging material (cookie bag) for packaging confectionery, it is difficult to separate the sealing part because of having a very high adhesive strength, usually 1.5kgf. Thereby, it is manufactured by adding the process of forming a sheath to a sealing part, and is designed to tear and open the said sheath part.

On the other hand, in the conventional manufacturing of the multilayer film as described above is manufactured through a coextrusion process and a lamination process. Specifically, the core layer 1 and the sealant layer 2 are manufactured by inflation or co-extrusion using a T-Die method. The barrier layer 3 is manufactured separately through a deposition process and then laminated to the core layer 1 using an adhesive. Although a deposition process for imparting a gas barrier property is inevitable, the conventional manufacturing method forms a barrier layer 3 through a separate lamination process, and the manufacturing process is complicated.

Accordingly, the present invention provides an easy peel property to a sealant layer, thereby providing a multilayer film having a good sealing property (heat sealing property) and being easy to open, and having a simplified manufacturing process, and a method of manufacturing the same. The purpose is.

The present invention to achieve the above object,

A core layer and a sealant layer,

The sealant layer,

Sealing resins;

Thermoplastic elastomers; And

Provided is a multilayer film comprising acrylates.

Further, according to the present invention,

Extrusion molding a film comprising a sealant layer, a core layer formed on the sealant layer, and a resin layer formed on the core layer; And

Depositing one or more selected from metals and metal oxides on the resin layer of the extruded film to form a deposition layer,

The sealant layer,

Sealing resins;

Thermoplastic elastomers; And

It provides a method for producing a multilayer film that is molded to include an acrylate.

At this time, the sealant layer, 30 to 90 parts by weight of the sealing resin based on 100 parts by weight of the total sealant layer; 5 to 50 parts by weight of thermoplastic elastomer; And 2 to 50 parts by weight of acrylate.

In addition, the thermoplastic elastomer may include a polyolefin-based thermoplastic elastomer, and more specifically, may include one or more selected from polypropylene thermoplastic elastomer and polyethylene thermoplastic elastomer.

According to the present invention, an easy peel property is imparted to the sealant layer, so that it is easy to open while having good sealing property (heat sealing property). And the manufacturing process is improved.

1 is a cross-sectional configuration diagram of a conventional polyolefin multilayer film.
2 is a cross-sectional configuration diagram of a multilayer film according to an exemplary embodiment of the present invention.

Hereinafter, with reference to the accompanying drawings will be described in detail the present invention.

Referring to FIG. 2, the multilayer film according to the present invention includes a core layer 10 as a substrate and a sealant layer 20 formed on the core layer 10. The sealant layer 20 may be formed on one side or both sides of the core layer 10, and FIG. 2 illustrates a state formed on one side (lower side) of the core layer 10.

The multilayer film according to the present invention preferably further includes a barrier layer 30, and as shown in FIG. 2, the sealant layer 20 formed on one surface of the core layer 10 and the core layer 10. ) And a barrier layer 30 formed on the other surface of the core layer 10. That is, the sealant layer 20, the core layer 10, and the barrier layer 30 have a multilayered structure sequentially stacked.

In addition, the multilayer film according to the present invention has a laminated structure of at least two or more layers including the core layer 10 and the sealant layer 20, but is not particularly limited, and has a laminated structure of, for example, two to nine layers. Can be. In addition, the multilayer film according to the present invention includes unstretched and stretched films. That is, it may not be extended | stretched after extrusion molding and may be uniaxially or biaxially stretched.

The core layer 10 may be composed of a plurality of layers of one or two or more layers. The core layer 10 may be composed of, for example, one to seven layers, and the number of layers is not limited. In addition, when the core layer 10 is composed of a plurality of layers, the layers may be the same material or different materials.

Although the said core layer 10 does not specifically limit, It is preferable to contain a polyolefin type as base resin. Specifically, the core layer 10 is preferably formed by extrusion molding a polyolefin resin composition containing at least a polyolefin resin. More preferably, the core layer 10 is co-extruded with the sealant layer 20 in an inflation or T-Die manner and simultaneously formed integrally.

The polyolefin resin composition contains at least one polyolefin resin as a base resin (main raw material). The polyolefin resin is not particularly limited as long as it is a polyolefin, but preferably at least one resin selected from polypropylene (PP), polyethylene (PE), and the like may be used. In another example, the polyolefin resin is one or more copolymers selected from ethylene and propylene, and specific examples thereof may include ethylene-methacrylic acid binary copolymer or ethylene-methacrylic acid-ester terpolymer. However, it is not limited by these.

In addition, the polyolefin-based resin composition includes at least a polyolefin-based resin, but may further include other resins or other additives, if necessary. At this time, although not particularly limited, the polyolefin resin composition may include 0 to 40 parts by weight of other resins or other additives, specifically 5 to 20 parts by weight, based on 100 parts by weight of the polyolefin resin. The additive may include at least one selected from an antifogging agent and a tackifier, and the additive may be selected from various functional components depending on the purpose of use and use of the film.

The antifogging agent prevents condensation of moisture in the air on the surface of the core layer 10, and may be selected from, for example, a surfactant. Antifoaming agents include, for example, sorbitan fatty acid esters such as sorbitan monooleate, sorbitan monolaurate, sorbitan monobehenate and sorbitan monostearate; Glycerin fatty acid esters such as glycerin monooleate and glycerin monostearate; Aliphatic amines such as lauryl diethanolamine; And fatty acid amides such as oleic acid amide. The antifogging agent is not particularly limited, but may be included in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of the polyolefin resin.

The tackifier is for reinforcing the adhesive property with the sealant layer 20, which is, for example, an aliphatic hydrocarbon resin mainly containing isoprene and 1,3-pentadiene, low molecular weight styrene resin, rosin And hydrocarbon hydrocarbon resins can be used. Such a tackifier is not particularly limited, but may be included in an amount of 0.1 to 10 parts by weight based on 100 parts by weight of the polyolefin resin.

The sealant layer 20 is sealed (heat-sealed) by heat after packaging the contents (food, etc.) to provide sealing property, which is an easy peel property with heat sealability according to the present invention. Has In the present invention, 'easy peel property' means that the film is easily peeled off by an external force (hand), that is, the sealing part of the packaging material formed by the sealant layer 20 is peeled off by the external force (hand) and opened.

According to the present invention, the sealant layer 20 includes a sealing resin, a thermoplastic elastomer and an acrylate so as to have an easy peel property with heat sealing property. The sealant layer 20 is formed by extruding a sealant composition containing at least these three components. Preferably it is formed integrally with the core layer 10 through coextrusion as described above.

The sealing resin is not particularly limited as long as it is an adhesive resin that can be melted and sealed by heat to impart sealing property (heat sealing property). The sealing resin is preferably selected from low-temperature adhesive resins, that is, low melting point resins, which can be heat sealed at a low temperature. The sealing resin should just have melting | fusing point of 180 degrees C or less, Preferably it is 150 degrees C or less, More specifically, what is necessary is just to be melted and heat-sealed at 120-150 degreeC. As the sealing resin, one or more selected from, for example, polypropylene (PP), polyethylene (PE), ethylene vinyl acetate (EVA), and the like can be used. As the sealing resin, as a terpolymer, for example, a resin having a low melting point and excellent sealing property, such as a terpolymer of ethylene / propylene / butadiene, can be used.

The thermoplastic elastomer is melt plasticized by heat and has elasticity, which may be melt plasticized by heat of, for example, 180 ° C. or lower, preferably 150 ° C. or lower. According to the present invention, the sealant layer 20 has an easy peel property by the addition of the thermoplastic elastomer. That is, the thermoplastic elastomer adjusts the adhesive strength of the sealant layer 20 to enable peeling by external force (hand) (to facilitate opening). In addition, a clean peeling surface is obtained while leaving no residues during peeling.

The thermoplastic elastomer may be selected from polyolefin-based, polyurethane-based and polyester-based thermoplastic elastomers, and the like, and may be preferably selected from polyolefin-based thermoplastic elastomers. The polyolefin-based thermoplastic elastomer may include polyolefin-based as a plasticizing component and rubber-based as an elastic component. In this case, the polyolefin may be selected from polypropylene (PP), polyethylene (PE), and the like, and the rubber system may be selected from ethylene-propylene rubber (EPR) and ethylene-propylene-diene rubber (EPDM). It is not limited by these. In addition, the polyolefin-based thermoplastic elastomer may be one in which the polyolefin-based rubber is blended, a part of which is crosslinked by a peroxide, or the like, and the polyolefin-based rubber is vulcanized by a vulcanizing agent.

According to a preferred embodiment, the thermoplastic elastomer is preferably polyolefin-based, and includes at least one selected from polypropylene (PP) thermoplastic elastomer, polyethylene (PE) thermoplastic elastomer, and the like. When polypropylene (PP) or polyethylene (PE) is used as the sealing resin, such a polyolefin-based thermoplastic elastomer has good compatibility with the sealing resin, is good in easy peel properties, and is preferable in the present invention. . In addition, the thermoplastic elastomer is more preferably a polypropylene (PP) thermoplastic elastomer, it is preferable to use a polypropylene (PP) thermoplastic elastomer having a density of 0.86 ~ 0.89 g / cm3.

The acrylate is added to control the adhesive strength, which also improves the miscibility of the sealing resin and the thermoplastic elastomer. The adhesive strength can be determined by the content of acrylates. Increasing the content of acrylate reduces the adhesive strength. That is, since the content of the acrylate and the adhesive strength are inversely related, it is possible to control the adhesive strength by controlling the content of the acrylate.

Therefore, according to the present invention, the sealant layer 20 includes the above-mentioned sealing resin, thermoplastic elastomer, and acrylate, and has an easy peel property with good sealing property, and thus easy to open. That is, separation (opening) by external force (hand) is possible.

Meanwhile, the sealant layer 20 has 30 to 90 parts by weight of a sealing resin, 5 to 50 parts by weight of thermoplastic elastomer, and 2 to 50 parts by weight of acrylate based on 100 parts by weight of the sealant layer 20 in its composition content. It is good to include. In this case, when the content of the sealing resin is less than 30 parts by weight, the sealing property is inferior, and when it exceeds 90 parts by weight, the adhesive strength may be too strong to reduce the easy peel property. In addition, if the content of the thermoplastic elastomer is less than 5 parts by weight, the easy peeling property is inferior, and if the content of more than 50 parts by weight, the content of the sealing resin may be relatively small and the sealing property may be deteriorated. And when the content of the acrylate is less than 2 parts by weight, the adhesive strength control ability and miscibility according to the content thereof may be insignificant, and when the content of the acrylate exceeds 50 parts by weight, the content of the sealing resin may be relatively small and the sealing property may be deteriorated.

In addition, it is possible to control the adhesive strength through the content control of the three components. For example, based on 100 parts by weight of the total sealant layer 20, in the case of including 35 to 80 parts by weight of the sealing resin, 10 to 30 parts by weight of the thermoplastic elastomer and 10 to 35 parts by weight of the acrylate, the adhesive strength of 0.15 to 0.5 kgf It can have (peel strength). In addition, the sealing resin is used to mix polypropylene (PP) and polyethylene (PE), based on 100 parts by weight of the total sealant layer 20 polypropylene (PP) 30 to 80 parts by weight, polyethylene (PE) is 5 It can be used at ~ 50 parts by weight.

The sealant layer 20 may further include additives in addition to the three components, that is, the sealing resin, the thermoplastic elastomer, and the acrylate. For example, it may further include one or more additives selected from antifogging agents, tackifiers, slip agents, antiblocking agents and the like. The additive is not particularly limited and may be selected from those conventionally used in the art in addition to those mentioned above or other functional ingredients.

The antifogging agent and the tackifier may be used as described above, the antifog agent based on 100 parts by weight of the total sealant layer 20 may be included in 0.01 to 5 parts by weight, tackifier may be included in 0.05 to 10 parts by weight.

The slip agent is capable of imparting slip property (or releasability) upon extrusion, and may use at least one selected from, for example, silicone, siloxane, silane, wax, and oleic acid amide. In addition to those listed above, any slip agent can be used as long as it can provide lubricity to the surface of the film and reduce the coefficient of friction. More specifically, it may be included in 0.1 to 10 parts by weight.

The anti-blocking agent may prevent adhesion between the films by forming a small space with the adjacent film when the film is wound, which may use, for example, one or more selected from inorganic particles such as silica, diatomaceous earth, kaolin and talc. have. The anti-blocking agent is preferably included in the sealant layer 20 as much as possible, and is not particularly limited, but may be included in an amount of 0.05 to 20 parts by weight, more specifically 0.1 to 15 parts by weight based on 100 parts by weight of the total sealant layer 20. have.

The barrier layer 30 is not limited as long as the barrier layer 30 has a barrier property, and specifically, it can block the access of gas such as external moisture or air. The barrier layer 30 may include at least one selected from a metal thin film, a deposition layer 32, and the like. In this case, the metal thin film may use, for example, a metal foil having a thickness of 1 μm (micrometer) to 300 μm, and the like, which may be laminated on the core layer 10 through an adhesive. In addition, the deposition layer 32 is formed by depositing one or more selected from a metal and a metal oxide, which may be formed by vacuum deposition on the core layer 10, for example, from 1 nm (nanometer) to 300 It may have a thickness of μm.

In the present invention, the metal applied to the barrier layer 30, specifically, the metal constituting the metal thin film or the deposition layer 32 is, for example, aluminum (Al), copper (Cu), nickel (Ni), tin ( Sn), one or more selected from the group consisting of zinc (Zn), indium (In), silver (Ag), tungsten (W) and iron (Fe) (single metal or a mixture of single metal), or selected from them Two or more alloys may be exemplified, but is not limited thereto. The metal is preferably selected from aluminum (Al) or aluminum alloy (Al alloy). In addition, the metal oxide that may be used as the deposition layer 32 is, for example, aluminum oxide (Al ₂ O ₃ ), silicon oxide (SiO ₂ ), tin oxide (SnO ₂ ), indium oxide (In ₂ O ₃ ), and the like. Zinc oxide (ZnO) and the like.

According to a preferred embodiment, the barrier layer 30 is a resin layer 31 formed on the core layer 10 and the deposition layer 32 formed on the resin layer 31 as illustrated in FIG. It is good to include. At this time, although the said resin layer 31 is not specifically limited, It is good to contain polyolefin type as a base resin. The resin layer 31 may be a polyolefin-based base resin, and may further include other components such as additives. The resin layer 31 may be made of the same material as the core layer 10 as described above. In addition, the resin layer 31 may be simultaneously formed integrally with the core layer 10 and the sealant layer 20 through coextrusion. In addition, as another exemplary embodiment of the present invention, the barrier layer 30 may further include a protective layer (not shown) formed on the deposition layer 32 to protect the deposition layer 32.

The multilayer film according to the present invention has a multilayer structure in which the sealant layer 20, the core layer 10, and the barrier layer 30 are sequentially stacked as described above, and the thickness of the sealant layer 20 (T20). ) Is 5 to 30% of the total film thickness (T), the thickness (T10) of the core layer 10 is 40 to 90% of the film total thickness (T), and the thickness (T30) of the barrier layer (30) May be formed to be 5 to 30% of the total film thickness (T).

In addition, the multilayer film according to the present invention may be formed on the barrier layer 30, and may further include one or more selected from a printing layer (not shown) and a surface coating layer (not shown). As a specific example, it may have a laminated structure including a sealant layer 20 / core layer 10 / barrier layer 30 / printing layer / surface coating layer. In this case, the printed layer may include a character or a pattern, and the surface coating layer may have abrasion resistance and scratch resistance.

On the other hand, the method for producing a multilayer film according to the present invention, as a preferred method for producing a multilayer film of the present invention as described above, includes an extrusion molding step and a deposition step.

In the extrusion molding step, a film including a sealant layer 20, a core layer 10 formed on the sealant layer 20, and a resin layer 31 formed on the core layer 10 is extruded. Preferably, the three layers 20, 10 and 31 are integrally molded simultaneously through coextrusion.

In this case, the sealant layer 20 is molded to include three components as described above, that is, a sealing resin, a thermoplastic elastomer, and an acrylate. Specifically, the sealant composition including the three components in an appropriate amount is injected into an extruder and extruded. In this case, the sealant composition may further include additives, solvents, and the like, in addition to the three components. In addition, as described above, the sealant layer 20 includes 30 to 90 parts by weight of the sealing resin, 5 to 50 parts by weight of the thermoplastic elastomer, and 2 to 50 parts by weight of the acrylate based on 100 parts by weight of the total sealant layer 20. It is preferable to mold as much as possible.

As described above, after a film including three layers, that is, a sealant layer 20 / core layer 10 / resin layer 31, a deposition step is performed, in which the resin layer 31 of the film is used. The deposition layer 32 is formed on the (). The deposition layer 32 is formed by vacuum depositing one or more selected from metals and metal oxides. Specific types of the metal and the metal oxide are as described above.

In addition, the manufacturing method according to the present invention is carried out before the deposition step, it may further comprise a corona treatment step. Specifically, the surface of the resin layer 31 may be corona treated to improve adhesion between the resin layer 31 and the deposition layer 32, which may be performed by a conventional method. In addition, the manufacturing method according to the present invention is carried out before the deposition step, it may further include a stretching step of uniaxially or biaxially stretching the extruded film.

The multilayer film according to the present invention described above can be usefully used for the purpose of sealing or vacuum. For example, it may be used as a packaging material or a vacuum material, preferably may be usefully used as a soft packaging material for packaging food or medicine.

According to the present invention, as described above, the sealant layer 20 includes the above three components, that is, a sealing resin, a thermoplastic elastomer, and an acrylate, and has an easy peel property with good sealing properties. Thereby, separation (opening) by external force (hand) is possible without forming a sheath in a sealing part like conventionally. Specifically, the adhesive strength (peel strength) of 0.15 to 0.8 kgf, preferably 0.15 to 0.5 kgf, which has a good sealing structure (sealing property) required in the packaging material, and can be peeled off by external force (hand). Peel strength).

In addition, according to the present invention, by including the above three components in the sealant 20, the difference (deviation) of the adhesive strength according to the heat sealing temperature is small. That is, in the case of using only the sealing resin as in the prior art, the adhesive strength shows a large difference depending on the heat sealing temperature, but when the three components are included according to the present invention, the difference in the adhesive strength according to the heat sealing temperature (deviation) Is less. This can be seen in the following examples.

Further, according to the present invention, the packaging process and the manufacturing process are improved. That is, separation (opening) by external force (hand) is possible, and the same sheath forming process can be eliminated, and packaging processes, such as confectionery, are simplified. In addition, in forming the barrier layer 30, a film including the sealant layer 20 / core layer 10 / resin layer 31 is produced by extruding (preferably coextrusion), and then deposited through Formation improves the manufacturing process. That is, a separate lamination process as in the prior art is eliminated and the manufacturing process is simplified.

Hereinafter, examples and comparative examples of the present invention will be exemplified. The following examples are merely provided to aid the understanding of the present invention, whereby the technical scope of the present invention is not limited.

[Examples 1 to 5]

A film having a sealant layer / core layer / resin layer was prepared by a coextrusion method using T-Die, and then Al was deposited and coated on the resin layer of the film using a vacuum evaporator.

At this time, the sealant layer was composed of components and contents as shown in the following [Table 1]. In Table 1, the content is based on 100 parts by weight of the total sealant layer (based on solids). The core layer and the resin layer were both made of polypropylene (PP).

Comparative Example 1

In contrast to the above embodiment, the sealant layer was carried out in the same manner except that the sealant layer was composed only of a terpolymer.

<Component and content of sealant layer, unit: parts by weight> Remarks Example 1 Example 2 Example 3 Example 4 Example 5 Comparative Example 1 PP - - 60 60 50 - PE - - 20 12 15 - Terpolymer 80 65 - - - 100 PP-TE 5 5 10 18 25 - Acrylate 15 30 10 10 10 - PP: Polypropylene
PE: polyethylene
Terpolymer: Ternary copolymer of ethylene / propylene / butadiene
PP-TE: Polypropylene Elastomer, Density 0.87 g / cm3, DoW Corporation (VERSIFY)

For the film specimens according to the Examples and Comparative Examples prepared above, the adhesive strength (peel strength) was evaluated as follows and the results are shown in the following [Table 2]. At this time, the specimens were thermally bonded so that the sealant layers adhered to each other, and then the adhesive strength according to the heat sealing temperature was evaluated.

* Heat seal  Strength (peel strength)

(1) A sample cut into a width (15 mm) x length (15 mm) using a cutter bar was prepared for each of the specimens heat-bonded so that the sealant layer was bonded.

(2) The sealing portions (between the sealant layers) of the samples cut to a constant size were only interlaminarly peeled with a razor.

(3) The adhesive strength (peel strength) of the sample was measured at a peel angle of 180 degrees using a tensile strength machine.

<Adhesive strength (peel strength) evaluation result according to heat sealing temperature, unit: kgf> Heat seal temperature Example 1 Example 2 Example 3 Example 4 Example 5 Comparative Example 1 120 DEG C 0.30 0.15 0.22 0.25 0.40 0.10 125 ℃ 0.20 0.15 0.22 0.25 0.40 0.25 130 ℃ 0.20 0.15 0.22 0.25 0.40 0.85 135 ℃ 0.20 0.15 0.22 0.30 0.40 1.50 ↑ 140 ° C 0.20 0.15 0.25 0.30 0.40 1.80 ↑ 145 ℃ 0.20 0.15 0.25 0.30 0.45 1.80 ↑ 150 ℃ 0.20 0.15 0.25 0.35 0.48 1.80 ↑

As shown in [Table 1] and [Table 2], in Examples (1 to 5) according to the present invention, the adhesive strength (peel strength) to the extent that peeling (opening) by hand is possible, and 0.15 to It can be seen that it has an appropriate adhesive strength (peel strength) in the range of 0.5 kgf. However, in Comparative Example 1, which was used only as a terpolymer, it was found that the peeling was difficult due to a very high adhesive strength (peel strength) of 0.85 kgf or more at a temperature of 130 ° C or higher, and particularly 1.5 kgf or more at a temperature of 135 ° C or higher. .

In addition, when compared with Example 1 and Example 2, as shown in the results of Table 2, it can be seen that the adhesive strength decreases as the content of the acrylate increases. In contrast to Examples 3 to 5, it can be seen that as the content of the thermoplastic elastomer, that is, polypropylene elastomer (PP-TE) increases, the adhesive strength increases. Therefore, it can be seen that the adhesive strength can be appropriately adjusted by controlling the addition amount of the acrylate and the thermoplastic elastomer.

In addition, as shown in [Table 2], in the case of Comparative Example 1 it can be seen that the adhesive strength increases significantly as the heat sealing temperature increases. However, in Examples 1 to 5 according to the present invention, it can be seen that even if the heat-sealing temperature is increased, the adhesive strength is almost uniformly evaluated without a large difference (deviation). That is, according to the present invention, even if the heat-sealing temperature is varied, uniform adhesive strength (peel strength) within the range of 0.15 to 0.5 kgf can be achieved.

10 core layer 20 sealant layer
30 barrier layer 31 resin layer
32: deposition layer

Claims (12)

A core layer and a sealant layer,
The sealant layer,
Sealing resins;
Thermoplastic elastomers; And
Multilayer film comprising acrylate.
The method of claim 1,
The multi-layer film further comprises a barrier layer.
The method of claim 2,
The barrier layer comprises a resin layer, and a deposition layer formed on the resin layer.
The method of claim 1,
The sealant layer is based on 100 parts by weight of the entire sealant layer,
30 to 90 parts by weight of the sealing resin;
5 to 50 parts by weight of thermoplastic elastomer; And
Multilayer film comprising 2 to 50 parts by weight of acrylate.
The method according to any one of claims 1 to 4,
The thermoplastic elastomer is a multilayer film, characterized in that it comprises a polyolefin-based thermoplastic elastomer.
The method of claim 5,
Wherein said thermoplastic elastomer comprises at least one selected from polypropylene thermoplastic elastomer and polyethylene thermoplastic elastomer.
The method according to claim 6,
The polypropylene thermoplastic elastomer, the multilayer film, characterized in that the density is 0.86 ~ 0.89 g / cm 3.
Extrusion molding a film comprising a sealant layer, a core layer formed on the sealant layer, and a resin layer formed on the core layer; And
Depositing one or more selected from metals and metal oxides on the resin layer of the extruded film to form a deposition layer,
The sealant layer,
Sealing resins;
Thermoplastic elastomers; And
Method for producing a multilayer film molded to include an acrylate.
9. The method of claim 8,
The sealant layer is based on 100 parts by weight of the entire sealant layer,
30 to 90 parts by weight of the sealing resin;
5 to 50 parts by weight of thermoplastic elastomer; And
Method for producing a multilayer film, characterized in that molded to include 2 to 50 parts by weight of acrylate.
10. The method according to claim 8 or 9,
The thermoplastic elastomer is a method of producing a multilayer film, characterized in that it comprises a polyolefin-based thermoplastic elastomer.
The method of claim 10,
The thermoplastic elastomer comprises at least one selected from polypropylene thermoplastic elastomer and polyethylene thermoplastic elastomer.
The method of claim 11,
The polypropylene thermoplastic elastomer, the density is 0.86 ~ 0.89 g / cm 3 The method for producing a multilayer film.