KR20120081724A - Alloy composite for low purity gold and low purity gold using the same - Google Patents
Alloy composite for low purity gold and low purity gold using the same Download PDFInfo
- Publication number
- KR20120081724A KR20120081724A KR1020110003001A KR20110003001A KR20120081724A KR 20120081724 A KR20120081724 A KR 20120081724A KR 1020110003001 A KR1020110003001 A KR 1020110003001A KR 20110003001 A KR20110003001 A KR 20110003001A KR 20120081724 A KR20120081724 A KR 20120081724A
- Authority
- KR
- South Korea
- Prior art keywords
- gold
- weight
- purity
- low
- purity gold
- Prior art date
Abstract
Description
본 발명은 저순도 골드용 합금조성물 및 그것을 이용한 저순도 골드에 관한 것으로, 더욱 상세하게는 구리(Cu)와 아연(Zn)의 합금인 황동(黃銅)과 구리(Cu)와 주석(Sn)과 인(P)의 합금인 인청동(燐靑銅)과 은(Ag), 구리(Cu),를 정해진 비율로 혼합함으로써 2K(Karat) 또는 4K의 미량의 금(Au)을 첨가하는 경우에도 골드의 색상이 그대로 발현(發顯)되고, 인체에 착용시 전혀 산화되거나 퇘색이 되지않고 알러지를 유발시키지 않는 등 높은 순도의 골드의 특성을 그대로 나타냄과 동시에 고순도의 골드에 비하여 비중이 가볍고 연성이 좋아 귀금속 장신구재료와 치과 크라운 합금재료 등에 사용하며 가격이 저렴하여 신체용 각종 악세사리, 안경테, 수저, 가방이나 핸드백 등의 장식물로 폭넓게 사용할 수 있도록 한 저순도 골드용 합금조성물 및 그것을 이용한 저순도 골드에 관한 것이다.The present invention relates to an alloy composition for low purity gold and low purity gold using the same, and more particularly, brass (Cu) and copper (Cu) and tin (Sn), which are alloys of copper (Cu) and zinc (Zn). In the case of adding a small amount of 2K (Karat) or 4K of gold (Au) by mixing phosphorous bronze, silver (Ag), copper (Cu), which are alloys of phosphorus (P), in a predetermined ratio Its color is expressed as it is, it is not oxidized or discolored when worn on the human body, and it does not cause allergies. It shows the characteristics of high purity gold as it is, and its specific gravity is lighter and softer than high purity gold. It is used for precious metal jewelry materials and dental crown alloy materials, and it is low in price, so it can be widely used as decoration for various accessories, glasses frames, cutlery, bags, handbags, etc. It is about de.
일반적으로, 금(金, Gold)은 빛나는 노란색의 무른 금속으로 연성과 가단성이 있는 전이 금속으로서, 금은 색깔이 화려하고 잘 변색되지 않으며, 희소성(稀少性)이 높아 재산적 가치와 귀금속 장신구으로서 많이 이용되고 있으며, 또한 순금(24K)은 연성이 좋은 금속으로 귀금속 장신구를 만드는데 정밀 작업을 하는데 한계가 있고 가격이 너무 비싸서 재산적 가치로써만 사용되는 금속이며,In general, gold is a shiny yellow soft metal that is ductile and malleable transition metal. Gold is brilliant and hardly discolored, and its scarcity is high, so it is a property value and precious metal ornament. It is also widely used, and pure gold (24K) is a ductile metal. It is a metal that is used only as a property value because it is limited in precision work for making precious metal jewelry and is too expensive.
금은 쉽게 얻을 수 없을 뿐만 아니라, 물리적인 성질이 매우 물러 순금만으로는 작은 충격에도 모양이 쉽게 변하기 때문에 금을 이용하여 각종 장신구나 장식품을 만들려면 불가피하게 다른 금속과 결합하여 저순도 합금을 이용한다. Not only gold is not easily obtained, but its physical properties are so low that pure gold alone changes its shape even with a small impact. Therefore, in order to make various ornaments or ornaments using gold, a low-purity alloy is inevitably combined with other metals.
이와 같은 금 합금은 원래의 순금에 다른 금속을 혼합한 것으로, 순금의 혼합비율에 따라 통상 22K, 20K, 18K, 14K, 등이 있으며 지금현재 한국 귀금속에서는 함량을 떨어뜨린 18K, 14K 이 두가지만이 유통되고 있다. 그러나 10K, 8K 등이 과거에 있었으나 색상이 변질이되고 연성이 없어 작업성이 없고 세공인으로 부터 인정받지 못하고 있었다. 금 합금을 만들때 순금과 혼합되는 기본 금속으로서 통상 적갈색의 광택을 띠는 구리가 많이 사용되고 있다.Such a gold alloy is a mixture of other metals with the original pure gold, there are usually 22K, 20K, 18K, 14K, etc., depending on the mixing ratio of pure gold, and now there are only 18K, 14K, which have decreased content in Korean precious metals. It is in circulation. However, 10K, 8K, etc. were used in the past, but because of the color change and ductility, it was not workable and was not recognized by craftsmen. When making gold alloys, reddish brown gloss copper is commonly used as a base metal mixed with pure gold.
18K의 금 합금은 순금 75%에 구리 25%를 혼합하여 만드는데 색상이 붉은 색을 띠기 때문에 적금이라 불리우고, 14K의 금 합금은 역시 구리를 넣어서 만드는데 색상이 청동과 같은 색깔을 띤다. The 18K gold alloy is made of 75% pure gold and 25% copper, which is called red gold because it is red in color. The 14K gold alloy is also made of copper and has the same color as bronze.
한편, 금 합금을 만들 때 구리 이외에 다른 금속이 첨가되기도 하는데, 순금에 철(Fe)을 혼합하여 만들면 자색금이 되고, 순금에다 알루미늄을 혼합하여 만들면 푸른 빛을 띠는 청금이 된다. On the other hand, when making a gold alloy, other metals other than copper may be added, and when it is made by mixing iron (Fe) with pure gold, it becomes purple gold, and when it is made by mixing aluminum with pure gold, it becomes blueish blue gold.
또, 14K와 18K의 금 합금에 은(Ag)를 혼합하면 녹색을 띠는 녹금이 되고, 순금에다가 17.3%의 니켈과 5.5%의 아연 및 2.2%의 구리와 소량의 은을 넣어서 제조하면, 백색 18K의 금 합금(일명 화이트골드)가 만들어진다.In addition, when silver (Ag) is mixed with 14K and 18K gold alloys, it becomes greenish green gold, and when pure gold is added with 17.3% nickel, 5.5% zinc, 2.2% copper and a small amount of silver, white 18K gold alloy (aka white gold) is made.
그러나, 이와 같이 만들어지는 종래의 금 합금의 경우 첨가되는 금의 함량이 적어질 수록 금 고유의 색상이 전혀 발현되지 못한다는 문제가 있고, 사람의 독성 성분인 황과 인체에서 나오는 염분에 의해 산화되면서 녹이 슬고 색상이 검게 변하는 등의 문제가 있다.However, in the case of the conventional gold alloy made as described above, as the amount of gold added is less, there is a problem that the color of gold is not expressed at all, and it is oxidized by sulfur, which is a toxic component of humans, and salts from the human body. There are problems such as rust and color change.
또, 상기 저순도의 금이 함유된 금 합금으로 만들어진 장신구의 변색을 막기 의하여 도금을 하는데 사람의 신체 구조상 알러지를 유발하는 사람은 착용부위의 피부에 발적(發赤)현상이 발생되거나 심한 경우 피부염 등의 알러지가 발생되기 때문에 그 사용이 극히 미미하다는 문제가 있다. In addition, plating is performed by preventing discoloration of jewelry made of a gold alloy containing gold of low purity, and a person who causes allergy in the human body structure causes redness on the skin of the worn part or in severe cases, dermatitis Since allergies, etc., occur, there is a problem that its use is extremely small.
금의 순도를 나타내는 "K"는 "캐럿(Karat)"의 약자로서, 상기 순금의 혼합비율에서는 24진법을 사용하기 때문에 다음의 계산법에서 알 수 있는 바와 같이, 1K는 1/24로서 순금의 함량이 4.1666..%인 것을 나타내며, 24K는 24/24(=4.1666 X 24)즉, 순금을 지칭하는 것이다. "K", which represents the purity of gold, is an abbreviation of "Karat". Since the mixing ratio of pure gold uses the binary system, 1K is 1/24 as the following calculation method. This represents 4.1666 ..%, where 24K refers to 24/24 (= 4.1666 X 24), that is, pure gold.
1K = 4.1666...%의 순금 함량1K = 4.1666 ...% pure gold content
14K = 4.1666 X 14 = 약 58.5%14K = 4.1666 X 14 = about 58.5%
18K = 4.1666 X18 = 약 75%18K = 4.1666 X18 = about 75%
24K = 4.1666 X 24 = 100%24K = 4.1666 X 24 = 100%
본 발명은 이와 같은 종래의 문제점을 해결하기 위한 것으로, 그 목적은 구리(Cu)와 아연(Zn)의 합금인 황동(黃銅)과 구리(Cu)와 주석(Sn)과 인(P)의 합금인 인청동(燐靑銅)과 은(Ag), 구리(Cu)에 정해진 비율로 혼합함으로써 2K(Karat) 또는 4K의 미량의 금(Au)을 첨가하는 경우에도 골드의 색상이 그대로 발현(發顯)되고, 인체에 착용시 전혀 산화되거나 퇘색이 되지않고 알러지를 유발시키지 않는 등 높은 순도의 골드의 특성을 그대로 나타냄과 동시에 고순도의 골드에 비하여 비중이 가볍고 연성이 좋아 귀금속 장신구재료와 치과 크라운 합금재료 등에 사용하며 가격이 저렴하여 신체용 각종 악세사리, 안경테, 수저, 가방이나 핸드백 등의 장식물로 폭넓게 사용할 수 있도록 한 저순도 골드용 합금조성물 및 그것을 이용한 저순도 골드에 관한 것이다.The present invention is to solve such a conventional problem, the purpose of which is an alloy of copper (Cu) and zinc (Zn) of brass (黄銅) and copper (Cu), tin (Sn) and phosphorus (P) Even when a small amount of 2K (Karat) or 4K of gold (Au) is added by mixing the alloy with phosphor bronze, silver (Ag), and copper (Cu) at a predetermined ratio, the color of the gold remains as it is.顯), it is not oxidized or discolored and does not cause allergy when worn on the human body, and it shows the characteristics of high purity gold as it is, and it is lighter and softer than the high purity gold. The present invention relates to an alloy composition for low-purity gold and low-purity gold using the same, which are widely used for materials such as materials, glasses, frames, cutlery, bags and handbags.
상기의 목적을 달성하기 위하여, 본 발명에 따른 저순도 골드용 합금조성물은 아연(Zn) 35중량%와 구리(Cu) 65중량% 가 혼합된 합금인 황동 69.0중량%에 구리(Cu) 91.0~93.0중량%과 주석(Sn) 7.0~9.0중량%과 인(P) 0.03중량%이 혼합된 합금인 인청동(燐靑銅) 4.0중량%, 99.99%순도의 은(Ag) 20.0중량%, 99.99%순도의 구리 7.0중량% 이 혼합된 특징을 갖는다.In order to achieve the above object, the alloy composition for low-purity gold according to the present invention is a copper (Cu) 91.0 ~ to 69.0% by weight of brass (Zn) is an alloy mixed with 35% by weight of zinc (Zn) and 65% by weight of copper (Cu) 4.0% by weight of phosphor bronze, a mixture of 93.0% by weight, 7.0-9.0% by weight of tin (Sn), and 0.03% by weight of phosphorus (P), 20.0% by weight of silver (Ag) of 99.99%, 99.99% 7.0 wt% of pure copper has mixed features.
본 발명에 따른 저순도 골드는 황동 69.0중량%에 인청동(燐靑銅) 4.0중량%, 99.99%순도의 은(Ag) 20.0중량%, 99.99%순도의 구리 7.0중량% 가 혼합된 합금조성물에 대하여 0.834중량% 또는 1.666중량%의 순금이 첨가,혼합되어 2K 또는 4K의 순도를 갖는 특징을 갖는다.Low purity gold according to the present invention is an alloy composition in which 69.0% by weight of brass, 4.0% by weight of phosphor bronze, 20.0% by weight of silver (Ag) of 99.99%, and 7.0% by weight of copper of 99.99% purity are mixed. 0.834% or 1.666% by weight pure gold is added and mixed to have a purity of 2K or 4K.
본 발명을 적용하면, 금 합금으로서 금고유의 색상과 매우 유사한 황동과 인청동, 은, 구리가 적절한 배합에 의해 적은 양의 순금이 혼합되는 경우에도 이러한 합금배율 이어야만이 서로의 특성을 살려 사람의 인체에서 나오는 황성분과 염분을 이겨 낼수가 있다.According to the present invention, even when a small amount of pure gold is mixed by a suitable combination of brass, phosphor bronze, silver, and copper, which is very similar to the color of the vault oil as a gold alloy, such alloy magnification should be utilized in the human body by utilizing the characteristics of each other. Can overcome the sulfur content and salt coming out.
고순도의 금과 같은 색상이 그대로 발현(發顯)되고, 인체에 착용시 전혀 산화되거나 퇘색이 되지않고 알러지를 유발시키지 않는 등 높은 순도의 골드의 특성을 그대로 나타냄과 동시에 고순도의 골드에 비하여 비중이 가볍고 연성이 좋아 귀금속 장신구재료와 치과 크라운 합금재료 등에 사용할 수 있으며 가격이 저렴하여 신체용 각종 악세사리, 안경테, 수저, 가방이나 핸드백 등의 장식물로 폭넓게 사용 할수있기 때문에 그 적용범위가 크게 확장 된다는 효과가 있다.The color of high purity gold is expressed as it is, it is not oxidized or discolored when worn on the human body and does not cause allergy. It is light and ductile, so it can be used for precious metal trinkets and dental crown alloy materials, and it is inexpensive, so it can be widely used as accessories for body accessories, glasses frames, cutlery, bags, handbags, etc. have.
도1은 저순도 골드 조성물에 필요한 재료및 작업 공정과 용해 과정을 나타낸것이다.
도2는 저순도 골드 조성물에 2K 골드와 4K골드를 함유한 저순도 골드를 용해하는 과정이다.Figure 1 shows the materials and work processes and dissolution processes required for low purity gold compositions.
2 is a process for dissolving low purity gold containing 2K gold and 4K gold in a low purity gold composition.
이하, 본 발명의 바람직한 실시예를 보다 상세하게 설명한다.Hereinafter, preferred embodiments of the present invention will be described in more detail.
본 발명에 따른 저순도 골드용 합금조성물은 황동과 인청동, 은, 구리가 각각 정해진 비율로 혼합,용융된다.In the alloy composition for low purity gold according to the present invention, brass, phosphor bronze, silver, and copper are mixed and melted at predetermined ratios, respectively.
본 발명에서 황동은 아연(Zn)과 구리(Cu)가 각각 35중량%와 65중량%로 혼합된 합금으로서, 금 고유의 색상을 나타내기 위하여 69.00중량%로 첨가되는데, 황동이 69.0중량% 미만으로 첨가되면 금 색상이 제대로 발현되지 못하며, 황동이 69.0중량%를 초과하여 첨가되면 시간이 흐를수록 산화가되어 색이 변화가 온다.In the present invention, brass is an alloy in which zinc (Zn) and copper (Cu) are mixed at 35% by weight and 65% by weight, respectively, and are added at 69.00% by weight in order to exhibit a unique color of gold, and brass is less than 69.0% by weight. When added as, gold color is not properly expressed, and when brass is added in excess of 69.0% by weight, the color is changed by oxidation as time passes.
본 발명에서 은과 구리는 황동과 혼합되어 금고유의 색상을 발현시키고, 연성(軟性)을 부여하기 위하여 첨가되는 것으로 각각 99.99%순도의 것이 사용된다.In the present invention, silver and copper are mixed with brass to express the color of the vault oil and are added to impart ductility, and 99.99% pure ones are used.
상기 은이 20.0중량%가 첨가되고, 구리는 7.0중량%가 첨가가 된다,20.0 wt% of silver is added, and 7.0 wt% of copper is added.
또한 인청동은 탄성 내식성, 내마모성을 보강하기 위하여 구리(Cu) 91.0~93.0중량%와 주석(Sn) 7.0~9.0중량%과 인(P) 0.03중량%으로 혼합된 합금인 인청동(燐靑銅) 4중량%, 만이 첨가하여야한다.Phosphor Bronze is a phosphor bronze composed of 91.0 to 93.0% by weight of copper, 7.0 to 9.0% by weight of Sn, and 0.03% by weight of phosphorus to enhance elastic corrosion resistance and wear resistance. Only weight percent should be added.
상기와 같이 정해진 비율 이상,이하로 첨가되는 경우는 금고유의 색상을 발현하는데 문제가 있고, 정해진 비율을 초과하여 첨가되는 경우 경제적으로 불리하며,연성이 커지면서 가공상의 문제가 발생한다. If it is added above or below a predetermined ratio, there is a problem in expressing the color of the vault oil, and when it is added in excess of a predetermined ratio, it is economically disadvantageous, and ductility increases and processing problems occur.
본 발명에 따른 저순도 골드용 합금은 각각 정확하게 계량된 황동과 인청동,은, 구리를 전기용해로인 흑연 도가니에 넣은 후 혼합물 100g을 기준하여 900~1,150℃에서 10~30초 동안 흑연봉으로 잘저어주며 용해시켜 얻어진다.The alloy for low purity gold according to the present invention is placed in a graphite crucible, which is precisely measured brass, phosphor bronze, silver and copper, and then stired with a graphite rod for 10-30 seconds at 900-1,150 ° C based on 100 g of the mixture. It is obtained by dissolving.
한편, 본 발명에 따른 저순도 골드는 위에서 얻어진 저순도 골드용 합금조성물에 미량의 순금을 혼합하여 용해시켜 얻어지는 것으로, 상기의 황동 69.0중량%에 인청동 4.0중량%과 99.99%순도의 은(Ag) 20.0중량%, 99.99%순도의 구리 7.0중량%가 혼합된 합금조성물에 대하여 0.834중량% 또는 1.668중량%의 순금을 첨가하여 함께 용융시키면 2K 또는 4K의 순도를 갖는 저순도의 골드가 얻어진다.On the other hand, low-purity gold according to the present invention is obtained by mixing and dissolving a trace amount of pure gold in the alloy composition for low-purity gold obtained above, 4.0% by weight of phosphor bronze and 99.99% of silver (Ag) in 69.0% by weight of the brass A low purity gold having a purity of 2K or 4K is obtained by adding together 0.834% by weight or 1.668% by weight of pure gold to an alloy composition containing 20.0% by weight and 7.0% by weight of 99.99% pure copper.
예로서 2K의 순도를 갖는 저순도 골드는 99.166중량%의 합금조성물에 0.834중량%의 순금을 첨가하여 혼합,용융함으로써 얻어지며, 4K의 순도를 갖는 저순도 골드는 98.332중량%의 합금조성물에 1.668중량%의 순금을 첨가하여 혼합,용융하여 얻어진다. For example, low purity gold having a purity of 2K is obtained by mixing and melting 0.834% by weight of pure gold in an alloy composition of 99.166% by weight, and low purity gold having a purity of 4K is 1.668 in an alloy composition of 98.332% by weight. It is obtained by mixing and melting by adding weight% pure gold.
이와 같이 얻어진 2K 또는 4K의 저순도 골드는 순금의 함량이 극히 낮음에도 불구하고, 황동과 혼합되면서 금 고유의 색상이 고스란히 그대로 발현되는 것은 물론, 인체에 착용하거나 공기중에 장시간 노출되어도 전혀 녹슬지 않는 등 고순도 골드의 특성을 그대로 나타낸다.The low purity gold of 2K or 4K thus obtained has a very low content of pure gold, and when mixed with brass, its unique color is expressed as it is, and it does not rust at all when worn on the human body or exposed to air for a long time. It shows the characteristic of high purity gold as it is.
또한 본 발명에 따른 저순도 골드는 고순도 골드 고유의 특성을 그대로 나타내면서도 고순도의 골드에 비하여 비중이 가볍고 연성이 좋아 귀금속 장신구재료와 치과 크라운 재료 등에 사용하며 가격이 저렴하여 신체용 각종 악세사리, 안경테, 수저, 가방이나 핸드백 등의 장식물로 폭넓게 사용 할수있다.In addition, low-purity gold according to the present invention exhibits the characteristics of high-purity gold as it is, but the specific gravity is lighter and more ductile than high-purity gold, and is used for precious metal jewelry materials and dental crown materials, and the price is low. It can be widely used as a decoration for cutlery, bags or handbags.
[도1]의 101번은 황동, 인청동, 구리, 은을 각각의 상기중량% 로 재료를 준비한다.
[도1]의 102번은 전기 용해로에 각 재료를 넣고 900~1150℃의 온도로 가열하여 용해한다.
[도1]의 103번은 저순도 골드용 합금 조성물이 생성 되는 것이다.
[도2]의 105번은 저순도 골드용 합금 조성물에 순금 0.834중량 % 로 재료를 준비한다.
[도2]의 106번은 전기 용해로에 각 재료를 넣고 900~1150℃의 온도로 가열하여 흑연봉으로 잘 저어 용해한다.
[도2]의 107번은 순금 0.834중량%가 함유된 2K골드가 생성된 것이다.
[도2]의 108번은 저순도 골드용 합금 조성물에 순금 1.668중량 %로 재료를 준비한다.
[도2]의 109번은 전기 용해로에 각 재료를 넣고 900~1150℃의 온도로 가열하여 흑연봉으로 잘 저어 용해한다.
[도2]의 110번은 순금 1.668중량%가 함유된 4K골드가 생성된 것이다. No. 101 of FIG. 1 prepares materials of brass, phosphor bronze, copper, and silver at the above weight percents.
In Figure 102, put 102 in the electric melting furnace, each material is heated to a temperature of 900 ~ 1150 ℃ to dissolve.
No. 105 of FIG. 2 prepares a material of 0.834% by weight of pure gold in an alloy composition for low purity gold.
No. 106 in [2] put each material in an electric melting furnace and heated to a temperature of 900 ~ 1150 ℃ stir well with a graphite rod to dissolve.
108 of FIG. 2 prepares a material with 1.668 weight% of pure gold in an alloy composition for low purity gold.
In Figure 109, each material is put in an electric melting furnace and heated to a temperature of 900 ~ 1150 ℃ stir well with a graphite rod to dissolve.
110 in Figure 2 is the production of 4K gold containing 1.668% by weight of pure gold.
Claims (2)