KR20120042409A - Water-tissue for packing and method of making the same - Google Patents

Water-tissue for packing and method of making the same Download PDF

Info

Publication number
KR20120042409A
KR20120042409A KR1020100104098A KR20100104098A KR20120042409A KR 20120042409 A KR20120042409 A KR 20120042409A KR 1020100104098 A KR1020100104098 A KR 1020100104098A KR 20100104098 A KR20100104098 A KR 20100104098A KR 20120042409 A KR20120042409 A KR 20120042409A
Authority
KR
South Korea
Prior art keywords
film
adhesive
hole
pack
outlet
Prior art date
Application number
KR1020100104098A
Other languages
Korean (ko)
Other versions
KR101230476B1 (en
Inventor
이승현
Original Assignee
이승현
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이승현 filed Critical 이승현
Priority to KR1020100104098A priority Critical patent/KR101230476B1/en
Publication of KR20120042409A publication Critical patent/KR20120042409A/en
Application granted granted Critical
Publication of KR101230476B1 publication Critical patent/KR101230476B1/en

Abstract

PURPOSE: A method for manufacturing a packing pack of water tissue is provided to simplify the whole manufacturing process of the packing pack. CONSTITUTION: A method for manufacturing a packing pack of water tissue is as follows. A pack body film, a reinforcement film, and an opening and shutting film are prepared(S100). The pack body film and reinforcement film are laminated(S200). A through-hole having larger diameter than an outlet is formed in the reinforcement film(S300). The opening and closing film is attached to the reinforcement film(S400).

Description

물티슈용 포장팩 제조방법{WATER-TISSUE FOR PACKING AND METHOD OF MAKING THE SAME}WATER-TISSUE FOR PACKING AND METHOD OF MAKING THE SAME}

본 발명은 물티슈가 수용되는 포장팩의 제조방법에 관한 것이다.The present invention relates to a manufacturing method of a packaging pack in which the wet tissue is accommodated.

일반적으로 유아용 등으로 사용되는 물티슈는 일반 티슈에 클리닝성분(AHA)이 함유되어 축축하게 젖어 있는 상태로 별도 비닐포장팩 안에 보관된다.In general, wet tissues used for infants, etc., are contained in a separate plastic packaging pack in a wet state in which a cleaning ingredient (AHA) is contained in a general tissue.

이때 사용되는 비닐포장팩은 수용본체 상부면에 티슈 인출을 위한 인출공이 형성되어 있고 인출공 상에는 물티슈의 수분증발을 막기 위한 개폐커버가 덮혀진 구조로 이루어진다.At this time, the plastic packing pack used has a drawing hole formed on the upper surface of the accommodating body for drawing out tissue, and an opening cover is covered on the drawing hole to prevent moisture evaporation of the wet tissue.

최근에는 포장팩 상부면 중 인출구 테두리 주변에 별도의 보강필름을 형성시킴에 따라 인출구 주변의 주름발생 및 찢어짐 등을 방지하도록 하는 기술이 제안되어 있다.Recently, as a separate reinforcing film is formed around the edge of the outlet of the packing pack upper surface, a technique for preventing wrinkles and tearing around the outlet is proposed.

이때 사용되는 보강필름은 단순 판재 상태에서 인출구와 연결되는 통공이 형성된 구조이다.At this time, the reinforcement film used is a structure in which a through hole connected to the outlet in a simple plate state.

그런데 이러한 구조는 수용본체의 인출구와 보강필름의 통공 형성공정이 별도로 이루어진 상태에서 보강필름의 부착공정을 실시함에 따라 전체공정이 복잡해질 뿐만 아니라 인출구와 통공의 위치가 불일치 되는 불량이 많이 발생된다.However, such a structure is not only complicated in the overall process as the reinforcing film is attached in a state where the through-hole of the receiving body and the through-hole forming process of the reinforcing film are made separately, but also a lot of defects in which the positions of the outlet and the through-hole are inconsistent.

본 발명은 포장팩의 전체 제작공정을 간소화 함과 동시에 불량발생을 방지할 수 있는 포장팩을 제공하고자 한다.The present invention is to provide a packaging pack that can simplify the entire manufacturing process of the packaging pack and at the same time prevent the occurrence of defects.

본 발명의 실시예는,An embodiment of the present invention,

팩본체필름과 보강필름 및 개폐필름을 준비하는 필름준비공정, 상기 팩본체필름과 보강필름을 적층시키는 합지공정, 상기 합지상태에서 팩본체필름에 인출구를 형성시키고 상기 보강필름에 통공을 형성시키는 타공공정, 상기 보강필름 상에 개폐필름을 부착시키는 마감공정을 포함한다.Film preparation process for preparing the pack body film, reinforcement film and opening / closing film, lamination process for laminating the pack body film and reinforcement film, perforation to form outlets in the pack body film in the lamination state and to form holes in the reinforcement film Process, and finishing the step of attaching the opening and closing film on the reinforcement film.

그리고 상기 타공공정은 상기 하나의 커팅날을 이용해 상기 팩본체필름과 상기 보강필름을 동시에 관통시켜, 상기 인출구와 상기 통공이 동일한 면적으로 형성될 수 있다.The perforation process may simultaneously pass the pack body film and the reinforcement film by using the one cutting blade, and the outlet and the through hole may be formed in the same area.

또한 상기 타공공정은 제1커팅날을 이용해 상기 보강피름만을 관통시켜 상기 통공을 먼저 형성시키는 통공형성단계 및 제2커팅날을 이용해 상기 팩본체필름을 관통시켜 상기 통공보다 작은 면적의 인출구를 형성시키는 인출구형성단계로 나뉘어 진행될 수 있다.In addition, the perforation process is a through-hole forming step of forming the through hole by first penetrating the reinforcing pitch only by using the first cutting blade and through the pack body film using the second cutting blade to form an outlet having a smaller area than the through hole. It can be divided into the outlet formation step.

그리고 상기 합지공정은 상기 보강필름과 상기 팩본체필름 사이에 형성된 접착층을 이용해 진행되고, 상기 접착층은 상기 통공이 형성될 지점에는 형성되지 않도록 함에 따라, 상기 타공공정에서 상기 통공 내 인출구 주변에는 비 접착구간이 형성될 수 있다.The lamination process is performed by using an adhesive layer formed between the reinforcement film and the pack body film, and the adhesive layer is not formed at a point where the through hole is to be formed, and thus is not adhered around the outlet in the through hole in the perforation process. A section may be formed.

또한 상기 개폐필름 중 상기 보강필름과 마주보는 면 에는 접착제가 형성되어 있고, 상기 접착제가 형성되어 있는 면 중 상기 비 접착구간과 대응되는 지점에는 접착제 비 도포구간이 형성될 수 있다.In addition, an adhesive is formed on a surface of the opening and closing film facing the reinforcement film, and an adhesive non-coating section may be formed at a point corresponding to the non-adhesive section of the surface on which the adhesive is formed.

이러한 여러 실시예에 의한 본 발명은,The present invention according to these various embodiments,

기본적으로 팩본체필름과 보강필름이 합지된 상태에서 인출구와 통공이 동시에 타공되므로 전체 공정을 간소화 할 수 있는 장점이 있다.Basically, the outlet body and the through hole are simultaneously drilled in the state where the pack body film and the reinforcement film are laminated, so that the entire process can be simplified.

또한 인출구와 통공이 한 공정상에서 형성되기 때문에 인출구와 통공의 위치가 정확히 일치된 상태로 형성되는 장점도 갖는다.In addition, since the outlet and the through-hole are formed in one process, it has the advantage that the position of the outlet and the through-hole is formed in exactly the same state.

그리고 통공 내 인출구 주변의 비 접착구간과 개폐커버의 접착제 비 도포구간에 의해 통공 내 인출구 주변에 접착성분이 존재하지 않으므로, 티슈 인출과정에서 티슈에 접착성분이 묻는 현상을 방지할 수 있는 장점도 있다.In addition, since there is no adhesive component around the outlet in the through hole by the non-adhesive section around the outlet in the through hole and the adhesive non-coating section of the opening / closing cover, there is an advantage that the adhesive component may be prevented from being applied to the tissue during the tissue extraction process. .

도1은 전체 공정도
도2는 전체 분해사시도
도3은 비 접착구간 및 접착제 비 도포구간이 형성된 상태의 분해사시도
도4는 보강필름과 팩본체필름간 합지상태를 나타낸 단면도
도5는 비 접착구간이 형성된 경우에서의 보강필름과 팩본체필름 간 합지상태를 나타낸 단면도
도6은 타공공정을 나타낸 단면도
도7 및 도8은 타공공정의 변형예를 나타낸 단면도
도9는 타공공정이 완료된 상태를 나타낸 단면도
도10 및 도11은 마감공정을 나타낸 사시도 및 단면도
도12는 비 접착구간과 접착제 비 도포구간이 형성된 상태에서 마감공정이 완료된 상태를 나타낸 단면도
도13은 비 접착구간이 형성되지 않고 접착제 비 도포구간만 형성된 경우를 나타낸 단면도1 is an overall process diagram
2 is an exploded perspective view of the whole
Figure 3 is an exploded perspective view of the non-adhesive section and the adhesive non-coating section is formed
Figure 4 is a cross-sectional view showing the laminated state between the reinforcement film and the pack body film
Figure 5 is a cross-sectional view showing the laminated state between the reinforcement film and the pack body film when the non-adhesive section is formed;
6 is a cross-sectional view showing a drilling process
7 and 8 are cross-sectional views showing a modification of the drilling process
9 is a cross-sectional view showing a state in which the perforation process is completed
10 and 11 are a perspective view and a cross-sectional view showing a finishing process
12 is a cross-sectional view showing a state in which the finishing process is completed in a state in which the non-adhesive section and the adhesive non-coating section are formed;
FIG. 13 is a cross-sectional view illustrating a case in which only a non-adhesive section is formed without a non-adhesive section formed thereon; FIG.

이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 첨부한 도면을 참고로 하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 명세서 전체를 통하여 유사한 부분에 대해서는 동일한 도면 부호를 붙였다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art may easily implement the present invention. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Like parts are designated by like reference numerals throughout the specification.

이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태도 본 발명의 권리범위에 속하는 것이다.Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements of those skilled in the art using the basic concepts defined in the following claims are also within the scope of the present invention. It belongs to.

본 발명 물티슈용 포장팩 제작방법은 [도 1]에 도시된 것처럼 크게 필름준비공정(S100)과 합지공정(S200), 타공공정(S300) 및 마감공정(S400)을 포함하여 이루어진다.The present invention is a manufacturing method for a wet pack packaging pack as shown in Figure 1 largely comprises a film preparation step (S100) and lamination step (S200), the punching step (S300) and the finishing step (S400).

먼저 필름준비공정(S100)은 포장팩을 구성하는 팩본체필름(100)과 보강필름(200) 및 개폐필름(300)을 준비하는 단계로, [도 2] 와 같이 그 중 팩본체필름(100)은 티슈가 수용될 팩 본체 형성을 위한 것으로, 얇은 비닐재 필름 상태이고 보강필름(200)은 추후 형성될 인출구(110) 주변의 주름방지 및 강도보강 기능을 하는 것이며, 개폐필름(300)은 티슈 인출과정에서 인출구(110)의 개폐기능을 하는 것이다.First, the film preparation process (S100) is a step of preparing a pack body film 100 and the reinforcement film 200 and the opening and closing film 300 constituting the packaging pack, of which the pack body film 100 as shown in FIG. ) Is for forming the pack body to accommodate the tissue, a thin vinyl film state and the reinforcement film 200 is to function to prevent wrinkles and strength around the outlet 110 to be formed later, the opening and closing film 300 The opening and closing function of the outlet 110 during the tissue withdrawal process.

보강필름(200)은 팩본체필름(100) 보다 작은 면적을 갖는 비닐재 필름형태가 사용되고 일측에는 팩본체필름(100)과의 합지를 위한 제1접착면(210)이 형성되어 있다.The reinforcement film 200 has a vinyl film having a smaller area than the pack body film 100, and a first adhesive surface 210 for lamination with the pack body film 100 is formed at one side.

참고로 보강필름(200)은 위에서 언급한 것처럼 팩본체필름(100)의 주름방지 및 강도향상기능을 하는 것이므로, 팩본체필름(100)보다 두꺼운 비닐재가 사용되거나 플라스틱 판재 형태 등으로도 적용될 수 있다.For reference, since the reinforcement film 200 functions to prevent wrinkles and enhance the strength of the pack body film 100 as mentioned above, a thicker vinyl material than the pack body film 100 may be used or may be applied in the form of a plastic sheet. .

그리고 개폐필름(300)은 역시 얇은 비닐재 필름형태이고 일측에는 보강필름(200)보다 면적이 작거나 큰 형태로 제작되며, 일측에는 보강필름과의 접착을 위한 접착제가 도포된 제2접착면이 형성되어 있다.And the opening and closing film 300 is also made of a thin vinyl film form on one side is smaller or larger than the area of the reinforcement film 200, one side is a second adhesive surface coated with an adhesive for bonding with the reinforcement film Formed.

이때 개폐필름(300)과 보강필름(200)은 상호 분리된 낱장의 상태로 제작되거나 보강필름(200)이 개폐필름(300)의 제2접착면(310)에 접착된 상태, 즉 적층된 상태로 준비될 수 있다.In this case, the opening and closing film 300 and the reinforcement film 200 are manufactured in a state of being separated from each other or the reinforcement film 200 is bonded to the second adhesive surface 310 of the opening and closing film 300, that is, in a laminated state. Can be prepared as

이러한 필름준비공정(S100)은 비 접착구간 형성단계(S110)와 접착제 비 도포구간 형성단계(S120)를 더 포함한다.The film preparation process (S100) further includes a non-adhesive section forming step (S110) and an adhesive non-coating section forming step (S120).

먼저 비 접착구간 형성단계(S110)는 후술하는 타공공정(S300)에서 팩본체필름(100) 중 인출구(110) 주변에 접착성분이 형성되지 않도록 하는 단계로 [EH 3]에 도시된 바와 같이 보강필름(200)의 제1접착면(210) 중 후술하는 통공(220)이 형성될 지점의 접착제를 제거하는 방식으로 이루어진다.First non-adhesive section forming step (S110) is a step to prevent the adhesive component is formed around the outlet opening 110 of the pack body film 100 in the punching process (S300) to be described later as shown in [EH 3] The first adhesive surface 210 of the film 200 is made of a method of removing the adhesive at the point where the through-hole 220 to be described later to be formed.

이때 접착제의 제거는 별도의 제거 약품을 해당지점의 접착제에 도포시켜 제거하거나 보강필름(200)에 접착제를 도포하는 과정에서 해당지점을 제외한 지점에만 접착제를 도포하는 방식으로 이루어질 수 있다.In this case, the removal of the adhesive may be performed by applying a separate removal chemical to the adhesive at the corresponding point, or applying the adhesive only to the point except for the corresponding point in the process of applying the adhesive to the reinforcing film 200.

따라서 제1접착면(210) 중 인출구(110)와 대응되는 지점에는 접착제가 제거된 상태의 비 접착구간(212)이 형성되고, 비 접착구간(212)은 인출구(110)의 면적보다 넓게 형성된 상태가 된다.Therefore, at the point corresponding to the outlet 110 of the first adhesive surface 210, the non-adhesive section 212 is formed with the adhesive removed, the non-adhesive section 212 is formed wider than the area of the outlet 110 It becomes a state.

그리고 접착제 비 도포구간 형성단계(S120)는 개폐필름(300)의 개폐과정에서 제2접착면(310)의 접착제가 인출구 주변에 묻지 않도록 하는 단계로, 개폐필름(300)의 제2접착면(310) 중 통공(220)과 마주보는 지점의 접착제를 제거하는 방식으로 이루어진다.And the adhesive non-coating section forming step (S120) is a step of preventing the adhesive of the second adhesive surface 310 is buried around the outlet in the opening and closing process of the opening and closing film 300, the second adhesive surface of the opening and closing film 300 ( 310 is made by removing the adhesive of the point facing the through-hole 220.

이때에도 제거 약품을 이용하거나 제2접착면(310)에 접착제를 도포하는 과정에서 해당지점을 제외한 지점에만 접착제를 도파하는 방식으로 이루어 질 수 있다.In this case, the removal agent may be used or a method of guiding the adhesive only at the point except for the corresponding point in the process of applying the adhesive to the second adhesive surface 310.

따라서 제2접착면(310) 중 보강필름(200)의 비 접착구간(212)과 대응되는 지점에는 접착제가 제거된 상태의 접착제 비 도포구간(312)이 형성된다.Therefore, at the point corresponding to the non-adhesive section 212 of the reinforcing film 200 of the second adhesive surface 310, an adhesive non-coating section 312 in a state where the adhesive is removed is formed.

참고로 후술하겠지만 인출구 주변에 접착성분이 형성될 우려가 없거나, 형성되더라도 인체에 무해한 접착제를 사용한다면 비 접착구간 형성단계(S110)와 접착제 비 도포구간 형성단계(S120)는 생략될 수 있다.For reference, as will be described later, if there is no concern that the adhesive component is formed around the outlet, or if the adhesive is harmless to the human body, the non-adhesive section forming step (S110) and the adhesive non-coating section forming step (S120) may be omitted.

그리고 이유는 후술하겠지만 비 접착구간 형성단계(S110)와 접착제 비 도포구간 형성단계(S120)는 둘 중 어느하나만 실시할 수 있다.And the reason will be described later, but the non-adhesive section forming step (S110) and the adhesive non-coating section forming step (S120) can be performed only one of the two.

만약 접착제 비 도포구간 형성단계(S120)만 실시할 경우 접착제 비 도포구간(312)의 면적은 후술할 통공(220)의 면적보다 크게 형성되도록 한다. If only the adhesive non-coating section forming step (S120) is carried out so that the area of the adhesive non-coating section 312 is larger than the area of the through-hole 220 to be described later.

이렇게 필름준비공정(S100)이 완료되면 합지공정(S200)을 실시한다.When the film preparation step (S100) is completed, the lamination step (S200) is performed.

합지공정(S200)은 후술하는 인출구(110)와 통공(220)의 동시형성을 위해 실시되는 전단계로, 보강필름(200)을 팩본체필름(100) 중 인출구(110)가 형성될 지점 상에 부착시키는 방식으로 이루어진다.The lamination process (S200) is a preliminary step performed for the simultaneous formation of the outlet 110 and the through-hole 220 which will be described later. The reinforcement film 200 is formed on the point where the outlet 110 of the pack body film 100 is formed. It is made by attaching.

이때 [도 4]와 같이 기본적으로 보강필름(200)의 제1접착면(210)이 팩본체필름(100)에 접착되는데, 만약 비 접착구간 형성단계(S110)를 진행하였을 경우에는 [도 5]처럼 제1접착면(210) 중 비 접착구간(212) 지점에서는 팩본체필름(100)과의 접착이 이루어지지 않은 상태가 된다.In this case, as shown in FIG. 4, the first adhesive surface 210 of the reinforcement film 200 is basically bonded to the pack body film 100. If the non-adhesive section forming step S110 is performed, [FIG. 5] In the non-adhesive section 212 of the first adhesive surface 210 as described above, the adhesion with the pack body film 100 is not performed.

이렇게 합지공정(S200)이 완료되면 타공공정(S300)을 실시한다.When the lamination process (S200) is completed in this way is carried out a drilling process (S300).

타공공정(S300)은 팩본체필름(100)에 인출구(110)를 형성시키고 보강필름(200)에 통공(220)을 동시에 형성시키는 단계로,The punching process (S300) is a step of forming the through-holes 220 in the pack body film 100 and the outlet 110 in the reinforcement film 200 at the same time,

기본적으로 [도 6]과 같이 커팅날(C)이 팩본체필름(100) 아래에서 상승하여 팩본체필름(100)과 보강필름(200)을 동시에 관통함에 따라, 팩본체필름(100)에는 인출구(110)가 형성되고 보강필름(200) 중 인출구(110)와 동일선상 지점에는 통공(220)이 동시에 형성된다.Basically, as shown in FIG. 6, the cutting blade C rises under the pack body film 100 and simultaneously passes through the pack body film 100 and the reinforcement film 200. 110 is formed and the through-hole 220 is formed at the same point on the same line as the outlet 110 of the reinforcing film 200.

이렇게 하나의 커팅날(C)로 팩본체필름(100)과 보강필름(200)을 동시에 관통시킴에 따라 인출구(110)와 통공(220)은 동일한 면적으로 형성된다.Thus, as the cutting body (C) through the pack body film 100 and the reinforcing film 200 at the same time through the outlet 110 and the through hole 220 is formed in the same area.

이처럼 타공공정(S300)이 완료되면 통공(220)을 갖는 보강필름(200)이 팩본체필름(100)의 인출구(110) 및 그 주변을 덮고 있는 상태에서 인출구(110)와 통공(220)이 동일선상으로 연통된 상태가 된다.When the perforation process (S300) is completed as described above, the reinforcement film 200 having the through-hole 220 has the outlet 110 and the through-hole 220 in the state covering the outlet 110 of the pack body film 100 and its periphery. It is in a state of being in line with each other.

이처럼 합지공정(S200)을 통해 팩본체필름(100)과 보강필름(200)이 적층된 상태에서 한번의 타공을 통해 인출구(110)와 통공(220)이 동시에 형성됨에 따라, 그만큼 전체공정이 간소해 지는 효과를 갖게 된다.As such, as the pack body film 100 and the reinforcement film 200 are laminated through the lamination process (S200), the outlet 110 and the through-hole 220 are simultaneously formed through one punch, the overall process is simplified. The effect is termination.

또한 도면과 같이 인출구(110)와 통공(220)의 위치가 어긋나지 않고 정확히 일치되므로 위치의 어긋남에 의한 제품불량이 방지되는 효과도 갖게 된다.In addition, since the positions of the outlet 110 and the through-hole 220 are exactly matched without shifting, as shown in the drawing, product defects due to misalignment of the position can be prevented.

만약 팩본체필름(100)과 보강필름(200)이 분리된 상태에서 인출구와 통공을 별도 공정을 통해 형성시킨 뒤 합지시킬 경우 인출구와 통공의 위치를 정확하게 일치시키기 어려워 위치가 어긋나는 불량발생이 실제 빈번하게 발생되고 있다.If the pack body film 100 and the reinforcement film 200 are separated from each other after forming the outlet and the through-hole through a separate process and laminating, it is difficult to accurately match the positions of the outlet and the through hole, so that the occurrence of defects that are out of position frequently occurs frequently. It is happening.

본 발명은 이렇게 인출구(110)와 통공(220)이 동일한 크기로 형성시키는 경우 외에도 비 접착구간 형성단계(S110)를 실시할 경우에는, 한 공정에서 인출구(110)와 통공(220)의 크기를 달리 형성시킬 수 있다.In the present invention, in addition to the case where the outlet 110 and the through-hole 220 are formed in the same size, when the non-adhesive section forming step S110 is performed, the size of the outlet 110 and the through-hole 220 in one process is determined. Can be formed otherwise.

이 경우 타공공정(S300)은 다시 통공 형성단계(S310)와 인출구 형성단계(S320)로 나뉘어 실시된다.In this case, the perforation process (S300) is carried out again divided into a through-hole forming step (S310) and the outlet opening forming step (S320).

구체적으로 설명하면 통공 형성단계(S310)는 [도 7]과 같이 타공공정에서 보강필름(200)이 팩본체필름(100) 아래에 위치된 상태에서 제1커팅날(C1)을 상승시켜 보강필름(200)만을 관통시켜 보강필름(200)의 비 접착구간(212)에 통공(220)을 형성시키는 방식으로 이루어진다.Specifically, the through-hole forming step (S310) is the reinforcement film by raising the first cutting blade (C1) in the state that the reinforcement film 200 is located below the pack body film 100 in the perforation process as shown in FIG. Only through 200 is made in a manner to form a through-hole 220 in the non-adhesive section 212 of the reinforcing film 200.

그리고 인출구 형성단계(S320)는 이 상태에서 [도 8]과 같이 제2커팅날(C2)을 상승시켜 통공(220)을 통과한 뒤 팩본체필름(100)을 관통하여 팩본체필름(100)에 통공(220) 보다 상대적으로 면적이 작은 인출구(110)를 형성시키는 방식으로 이루어진다.And the outlet opening forming step (S320) in this state, as shown in [Figure 8] by raising the second cutting blade (C2) through the through-hole 220 and through the pack body film 100 through the pack body film 100 In the through-hole 220 is formed in such a way to form the outlet 110 is smaller than the area.

따라서 인출구 형성단계(S320)까지 완료되면 [도 9] 및 [도 10]과 같이 팩본체필름(100)의 상면 중 보강필름(200)의 통공(220) 내 지점에는 이보다 작은 면적의 인출구(110)가 형성되고, 따라서 통공(220) 내부의 인출구(110) 테두리 주변에는 보강필름(200)과 접촉되지 않고 외부로 노출된 비 접착면(112)이 형성된 구조를 갖게 된다.Therefore, when the outlet opening forming step (S320) is completed, the outlet opening 110 having a smaller area than that in the through hole 220 of the reinforcement film 200 among the upper surfaces of the pack body film 100 as shown in FIGS. 9 and 10. ) Is formed, and thus has a structure in which a non-adhesive surface 112 is exposed to the outside without contact with the reinforcement film 200 around the edge of the outlet 110 inside the through hole 220.

이때 비 접착면(112)은 보강필름(200)의 비 접착구간(212)과 대응되는 부분이므로, 비 접착면(112)에는 접착성분이 전혀 묻어 있지 않은 상태가 된다.At this time, since the non-adhesive surface 112 is a portion corresponding to the non-adhesive section 212 of the reinforcing film 200, the non-adhesive surface 112 is in a state where no adhesive component is buried at all.

참고로 이렇게 타공공정(S300)을 두 단계로 나누어 실시할 경우 사용되는 커팅날은 위 설명처럼 크기별로 별도 구비되거나 하나의 커팅날로 인출구와 통공을 모두 형성시킬 수 있도록 할 구도 있다.For reference, when the punching process (S300) is divided into two steps, the cutting blades used may be provided separately by size as described above, or may form both the outlet and the through hole as one cutting blade.

이렇게 타공공정(S300)이 완료되면 마감공정(S400)실시한다.When the perforation process (S300) is completed, the finishing process (S400) is performed.

마감공정(S400)은 준비된 개폐필름(300)을 보강필름(200) 상에 접착시키는 방식으로 이루어지는데, 비 접착구간 형성단계와 접착제 비 도포구간을 실시하지 않은 기본 구조에서는 [도 11]처럼 보강필름(200)의 제2접착면(310)을 보강필름(200) 상면에 접착됨에 따라 개폐필름(300) 전체가 통공(220)을 비롯해 보강필름(200) 전체를 덮고 있는 상태가 된다.Finishing process (S400) is made of a method of bonding the prepared opening and closing film 300 on the reinforcement film 200, the non-adhesive section forming step and the non-adhesive base structure is not subjected to the reinforcement as shown in Figure 11 As the second adhesive surface 310 of the film 200 is adhered to the upper surface of the reinforcement film 200, the entire opening / closing film 300 covers the entire reinforcement film 200 including the through-hole 220.

만약 비 접착구간 형성단계(S110)와 개폐필름(300)에 접착제 비 도포구간 형성단계(S120)를 모두 실시하였을 경우에는 [도 12]와 같이 개폐필름(300)의 제2접착면(310) 중 통공(220)과 마주보는 지점에는 접착제 비 도포구간(312)이 위치된다.If the non-adhesive section forming step (S110) and the opening and closing film 300, both of the non-adhesive non-coating section forming step (S120) is performed, as shown in Figure 12 the second adhesive surface 310 of the opening and closing film 300 At the point facing the through hole 220, the non-adhesive section 312 is positioned.

이때 따라서 인출구 주변의 비 접착면(112)과 개폐필름(300) 간에는 접착이 전혀 이루어지지 않으므로, 개폐필름(300)의 개폐과정에서 접착성분이 인출구 주변에 묻지 않음에 따라 휴지 인출과정에서 인출구 주변의 접착제가 휴지에 묻는 현상이 완전히 방지된다.At this time, since no adhesion is made between the non-adhesive surface 112 and the opening / closing film 300 around the outlet, the adhesive component is not buried around the outlet during the opening / closing process of the opening / closing film 300. The glue on the toilet paper is completely prevented.

또한 위에서 설명한 것처럼 개폐필름(300)의 접착제 비 접착구간(212)의 면적이 통공(220)의 면적보다 넓기 때문에, 개폐필름(300)이 보강필름(200)을 덮은 상태에서 보강필름(200) 중 통공(220) 테두리 주변에도 접착제가 묻지 않게 된다.In addition, since the area of the adhesive non-adhesive section 212 of the opening and closing film 300 is larger than that of the through hole 220 as described above, the opening and closing film 300 covers the reinforcing film 200 and the reinforcing film 200. The adhesive is not buried around the periphery of the through hole 220.

그리고 도면에는 도시되지 않았지만 만약 보강필름(200)에 비 접착구간 형성단계(S110)만을 실시하고 개폐필름(300)에 접착제 비 도포구간 형성단계(S120)는 실시하지 않았을 경우에도, 보강필름(200)의 두께로 인해 개폐필름(300)의 제2접착면(310)이 인출구(110) 주변의 비 접착면(112)과 접촉되지 않기 때문에 인출구 주변에 접착제가 묻는 현상이 방지된다.Although not shown in the drawings, even if the non-adhesive section forming step (S110) is performed only on the reinforcing film 200 and the adhesive non-coating section forming step (S120) is not performed on the opening and closing film 300, the reinforcing film 200 is performed. Because of the thickness of the), the second adhesive surface 310 of the opening and closing film 300 is not in contact with the non-adhesive surface 112 around the outlet 110, the adhesive is prevented from around the outlet.

뿐만 아니라 [도 13]처럼 비 접착구간 형성단계(S110)를 실시하지 않아 인출구(110)와 통공(220)의 면적이 동일하게 형성된 상태에서, 개폐필름(300)에 접착제 비 도포구간 형성단계(S120) 만을 실시하였을 경우,In addition, the non-adhesive section forming step (S110) is not performed as shown in FIG. 13, so that the area of the outlet 110 and the through-hole 220 are equally formed, the adhesive non-coating section forming step in the opening / closing film 300 ( If only S120) is performed,

위에서 설명한 것처럼 접착제 비 도포구간(312)의 면적이 통공(220)의 면적보다 크게 형성되기 때문에, 개폐필름(300)의 접착제가 통공(220) 둘레에 묻지 안게 된다.Since the area of the adhesive non-coating section 312 is formed larger than the area of the through hole 220 as described above, the adhesive of the opening and closing film 300 is not buried around the through hole 220.

이렇게 마감공정이 완료되면 팩본체필름(100)이 티슈뭉치를 감싼 상태에서 밀봉시키는 과정을 거침에 따라 모든 제작단계가 완료된다.When the finishing process is completed, all the manufacturing steps are completed as the pack-body film 100 is sealed in a tissue bundle.

이상 설명한 것처럼 본 발명은 기본적으로 팩본체비닐(100)과 보강필름(200)이 합지된 상태에서 인출구(110)와 통공(220)의 동시 타공이 이루어짐에 따라,As described above, according to the present invention, as the pack body vinyl 100 and the reinforcement film 200 are laminated, the simultaneous punching of the outlet 110 and the through-hole 220 is made.

전체 제작 공정이 간소해 짐은 물론, 인출구(110)와 통공(220) 간 위치 불일치 현상을 방지하여 생산성 저하현상도 방지되고, 뿐만 아니라 팩본체필름과 보강필름 및 개폐필름 간 접착제 제거 과정을 통해 티슈 인출과정에서 접착제가 티슈에 묻는 현상도 동시에 방지할 수 있도록 한 것을 특징으로 한다.In addition, the entire manufacturing process is simplified, and productivity loss is prevented by preventing misalignment between the outlet 110 and the through hole 220. In addition, the adhesive is removed between the pack body film, the reinforcement film, and the opening / closing film. It is characterized in that the adhesive is prevented from being caught on the tissue at the same time during the tissue extraction process.

이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태도 본 발명의 권리범위에 속하는 것이다.Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements of those skilled in the art using the basic concepts defined in the following claims are also within the scope of the present invention. It belongs to.

S100 : 필름준비공정 100 : 팩본체필름
110 : 인출구 200 : 보강필름
210 : 제1접착면 212 : 비 접착구간
220 : 통공 300 : 개폐필름
310 : 제2접착면 312 : 접착제 비 도포구간
S110 : 비 접착구간 형성단계 S120 : 접착제 비 도포구간 형성단계
S200 : 합지공정 S300 : 타공 공정
S310 : 통공 형성단계 S320 : 인출구 형성단계
S400 : 마감공정S100: film preparation process 100: pack body film
110: outlet 200: reinforcement film
210: first bonding surface 212: non-adhesive section
220: through hole 300: opening and closing film
310: second adhesive surface 312: adhesive non-coating section
S110: forming step of non-adhesive section S120: forming step of non-adhesive section
S200: Lamination process S300: Perforation process
S310: through hole forming step S320: outlet opening forming step
S400: Finishing Process

Claims (6)

팩본체필름과 보강필름 및 개폐필름을 준비하는 필름준비공정,
상기 팩본체필름과 상기 보강필름을 적층 시키는 합지공정,
상기 팩본체필름과 상기 보강필름이 합지된 상태에서 상기 팩본체필름에 인출구를 형성시키고 상기 보강필름 중 상기 인출구와 동일선상의 지점에 상기 인출구보다 직경이 큰 통공을 형성시키는 타공공정, 그리고
상기 보강필름 상에 상기 개폐필름을 부착시키는 마감공정을 포함하는
물티슈용 포장팩 제작방법.Film preparation process for preparing pack body film, reinforcement film and opening / closing film,
A lamination process of laminating the pack body film and the reinforcement film,
A perforation process of forming an outlet in the pack body film in the state where the pack body film and the reinforcement film are laminated, and forming a through hole having a diameter larger than that of the outlet in the same line as the outlet of the reinforcement film, and
And a finishing process of attaching the opening and closing film on the reinforcement film.
How to make a packing pack for wet tissue. 제1항에서,
상기 타공공정은,
적어도 하나 이상의 커팅날을 이용해 상기 팩본체필름과 상기 보강필름을 동시에 관통시켜, 상기 인출구와 상기 통공이 동일한 면적으로 형성되도록 하는
물티슈용 포장팩 제작방법.In claim 1,
The perforation process,
Through the pack body film and the reinforcement film at the same time using at least one or more cutting blades, so that the outlet and the through hole is formed in the same area
How to make a packing pack for wet tissue. 제1항에서,
상기 타공공정은,
제1커팅날을 이용해 상기 보강필름만을 관통시켜 상기 통공을 먼저 형성시키는 통공형성단계 및
제2커팅날을 이용해 상기 팩본체필름을 관통시켜 상기 통공보다 작은 면적의 상기 인출구를 형성시키는 인출구형성단계를 포함하는
물티슈용 포장팩 제작방법.In claim 1,
The perforation process,
A through-forming step of forming the through-hole first by penetrating only the reinforcing film using a first cutting blade;
A through-hole forming step of forming the outlet through the pack body film using a second cutting blade to form the outlet through a smaller area than the through hole;
How to make a packing pack for wet tissue. 제1항에서,
상기 필름준비공정은,
상기 팩본체필름에 부착되는 상기 보강필름의 접착면 중 상기 통공이 형성될 지점에 접착제가 도포되지 않도록 하는 비 접착구간 형성단계
를 더 포함하는 물티슈용 포장팩 제작방법.In claim 1,
The film preparation process,
Non-adhesive section forming step of preventing the adhesive is applied to the point where the through-hole is formed in the adhesive surface of the reinforcing film attached to the pack body film
Method for producing a wet pack packaging pack further comprising a. 제1항 또는 제4항에서,
상기 필름준비공정은,
상기 개폐필름의 접착면 중 상기 통공과 대응되는 지점에 접착제 비 도포구간을 형성시키는 단계를
더 포함하는 물티슈용 포장팩 제작방법.The method of claim 1 or 4,
The film preparation process,
Forming an adhesive non-coating section at a point corresponding to the through hole among the adhesive surfaces of the opening and closing film;
Method for producing a wet pack packaging pack further comprising. 제5항에서,
상기 접착제 비 도포구간의 면적은 상기 통공의 면적보다 크게 형성되어 있는
물티슈용 포장팩 제작방법.
The method of claim 5,
The area of the adhesive non-application section is formed larger than the area of the through hole
How to make a packing pack for wet tissue.
KR1020100104098A 2010-10-25 2010-10-25 Water-tissue for packing and method of making the same KR101230476B1 (en)