KR20120028695A - Coating for waterproof and breathable, coating method and fabric for waterproof and breathable - Google Patents
Coating for waterproof and breathable, coating method and fabric for waterproof and breathable Download PDFInfo
- Publication number
- KR20120028695A KR20120028695A KR1020100090698A KR20100090698A KR20120028695A KR 20120028695 A KR20120028695 A KR 20120028695A KR 1020100090698 A KR1020100090698 A KR 1020100090698A KR 20100090698 A KR20100090698 A KR 20100090698A KR 20120028695 A KR20120028695 A KR 20120028695A
- Authority
- KR
- South Korea
- Prior art keywords
- coating
- fabric
- waterproof
- film
- water
- Prior art date
Abstract
Description
본 발명은 투습방수용 코팅물, 코팅방법 및 이를 이용한 투습방수 직물에 관한 것으로 코팅층을 형성한 후에 직물을 접착하여 투습도 및 내수압이 우수한 투습방수용 코팅물, 코팅방법 및 그로 제조되는 투습방수 직물에 관한 것이다.
The present invention relates to a water-permeable waterproof coating, a coating method, and a water-permeable waterproof fabric using the same, and to a moisture-permeable waterproof coating, a coating method, and a water-permeable waterproof fabric having excellent moisture permeability and water resistance by adhering the fabric after forming a coating layer. .
일반적으로 투습방수 직물은 100㎛의 빗방울이 섬유 밖에서 섬유 안으로 통과 못하게 하고 몸의 체내에서 방출되는 0.004㎛의 수분을 섬유 안에서 섬유 밖으로 나갈 수 있도록 피막층을 직물위에 형성시켜 투습성과 방수성 등이 우수한 스포츠웨어, 군복, 텐트 등에 사용되는 직물을 의미한다.In general, moisture-permeable fabric is a sportswear that has excellent moisture permeability and waterproofness by forming a coating layer on the fabric so that raindrops of 100 μm do not pass into the fiber from the outside of the fiber and 0.004 μm of moisture released from the body can flow out of the fiber in the fiber. Means fabrics used in military uniforms, tents, etc.
투습방수 기능을 갖도록 하는 방법은 라미네이팅(Laminating) 방식에 의한 PTFE 미세다공 성막법과 다이렉트 코팅방식에 의한 폴리우레탄 미다공 성막법, 그리고 초고밀도 직쳔물에 의한 방법 등으로 크게 나눌 수 있다. 폴리우레탄을 이용한 다이렉트 코팅방식에 의한 종래의 투습방수직물은 DMF(디메칠포름아미드) 및 MEK(메틸에틸케톤) 등과 같이 환경에 유해한 솔벤트를 사용함으로써 환경오염을 초래하는 원인이 되어 최근에는 수분산형 폴리우레탄 코팅액을 이용하고 다단 건조하여 건식다공형 투습방수포를 제작법과 친수무공형의 폴리우레탄을 이용한 건식코팅법이 연구되고 있다.Methods to have a moisture-permeable waterproof function can be broadly divided into a PTFE microporous film forming method by the laminating method, a polyurethane microporous film forming method by the direct coating method, and a method using an ultra high density fabric. The conventional moisture-permeable waterproof fabric by direct coating method using polyurethane is the cause of environmental pollution by using environmentally harmful solvents such as DMF (dimethylformamide) and MEK (methyl ethyl ketone). The method of manufacturing a dry porous permeable waterproof fabric by using a polyurethane coating solution and drying in multiple stages and a dry coating method using a hydrophilic non-porous polyurethane have been studied.
친수무공형 폴리우레탄을 이용한 투습방수직물의 종래기술로써 대한민국 등록특허 제0795386호의 '친수무공형 투습방수포'에서는 폴리에틸렌글리콜(Polyethylene Glycol) 또는 폴리프로필렌글리콜(Polyprophylene Glycol)의 소프트세그먼트(soft segment)의 폴리올(Polyol)을 갖는 친수무공형 폴리우레탄 수지를 사용하여 건식코팅법에 의한 투습성이 우수한 방수포를 기재하였고, 대한민국 공개특허 제2008-0042309호는 '투습방수용 코팅조성물, 이를 이용한 건식무공형투습 방수원단 및 이의 제조방법'에는 친수무공형 폴리우레탄을 원단-코팅층의 2단계 제조공정으로 코팅하여 생산성 향상, 환경오염 감소 및 우수한 코팅 품질을 확보할 수 있는 코팅법을 제안한다.As a conventional technology of a moisture-permeable waterproof fabric using a hydrophilic non-porous polyurethane, in the 'hydrophilic non-porous moisture-proof cloth' of Korean Patent No. 0795386, a soft segment of polyethylene glycol or polyproplyylene glycol is used. Using a hydrophilic non-porous polyurethane resin having a polyol, a waterproof cloth having excellent moisture permeability by a dry coating method has been described. Fabric and its manufacturing method is proposed a coating method that can be coated with a hydrophilic non-porous polyurethane in a two-step manufacturing process of the fabric-coating layer to improve productivity, reduce environmental pollution and ensure excellent coating quality.
또한, 대한민국 등록특허 제0823630호 투습 및 발수성이 우수한 직물 및 그의 제조과정에서는 광경화형 불소계 발수발유제를 패딩처리한 후 스크린 메쉬를 이용하여 선택적 자외선 조사에 의한 투습발수직물을 제조하는 방법을 제안하였다.In addition, the Republic of Korea Patent No. 0831630 has excellent water vapor permeability and water-repellent fabric and a process of manufacturing the water-repellent water-repellent fabric by selective ultraviolet irradiation using a screen mesh after padding the photo-curing fluorine-based water and oil repellent was proposed. .
상기의 친수무공형 폴리우레탄을 이용한 건식코팅법은 환경오염 문제에서는 자유롭지만 세탁 내구성이 약한 단점을 지니고, 코팅 표면에 맺힌 물방울을 친수무공형 폴리우레탄이 흡수하여 팽윤현상을 일으키는 단점을 지니게 된다. 또한, 상기의 선택적 자외선 조사에 의한 투습방수직물 개발에 있어 스크린 메쉬를 올려놓은 후 바로 자외선 조사를 할 경우 스크린 메쉬의 격자부분이 미경화부분으로 존재하여 투습로를 형성시킴으로 내수압이 낮은 단점을 지니게 된다.
The dry coating method using the hydrophilic non-porous polyurethane has a disadvantage in that it is free from environmental pollution problems but weak in washing durability, and the hydrophilic non-porous polyurethane absorbs water droplets formed on the surface of the coating to cause swelling. In addition, in the development of the moisture-permeable waterproof fabric by the selective ultraviolet irradiation, when the UV irradiation immediately after placing the screen mesh, the lattice portion of the screen mesh is present as a non-hardened portion to form a moisture-permeable path has the disadvantage of low water pressure do.
상기와 같은 문제점을 해결하기 위해 본 발명은 투습도 및 내수압을 개선하는 투습방수용 코팅물 및 그 코팅방법을 제공하는 것을 목적으로 한다.
In order to solve the above problems, an object of the present invention is to provide a moisture-permeable waterproof coating and a coating method for improving moisture permeability and water pressure.
상기 목적을 달성하기 위해 본 발명은 투습방수용 코팅물에 있어서, 직물로 이루어진 표면층; 및 상기 직물의 상면에 폴리우레탄 아크릴레이트에 다관능성 모노머가 첨가된 수지로 코팅된 코팅층으로 이루어지되, 상기 코팅층은 UV경화로 이루어진 투습방수용 코팅물을 제공한다.In order to achieve the above object, the present invention provides a coating for moisture-permeable waterproof, the surface layer made of a fabric; And a coating layer coated with a resin in which a polyfunctional monomer is added to polyurethane acrylate on the upper surface of the fabric, wherein the coating layer provides a moisture-permeable waterproof coating made of UV curing.
또한 본 발명은 상기 모노머가 TMPTA(Trimethylolpropane triacrylate), TPGDA(Tripropyleneglycol diacrylate), DPHA(Dipentaerythritol hexaacrylate)로 이루어진 군에서 1이상 선택되는 것을 특징으로 하는 투습방수용 코팅물을 제공한다.In another aspect, the present invention provides a coating for moisture-permeable waterproof, characterized in that at least one monomer is selected from the group consisting of trimethylolpropane triacrylate (TMPTA), tripropyleneglycol diacrylate (TPGDA), and dipentaerythritol hexaacrylate (DPHA).
또한 본 발명은 상기 친수무공형 폴리우레탄 아크릴레이트 수지가 분자량 200 내지 2000의 PEG가 합성된 것을 특징으로 하는 투습방수용 코팅물을 제공한다.In another aspect, the present invention provides a coating for moisture-permeable waterproof, characterized in that the hydrophilic non-porous polyurethane acrylate resin is synthesized PEG having a molecular weight of 200 to 2000.
또한 본 발명은 상기 표면층 및 코팅층이 핫멜트필름으로 접착하는 것을 특징으로 하는 투습방수용 코팅물을 제공한다.In another aspect, the present invention provides a coating for moisture-permeable waterproof, characterized in that the surface layer and the coating layer is bonded by a hot melt film.
또한 본 발명은 상기 코팅물로 코팅되는 것을 특징으로 하는 투습방수 코팅방법을 제공한다.In another aspect, the present invention provides a waterproof coating method characterized in that the coating is coated with the coating.
또한 본 발명은 상기 직물이 나일론6 및 나일론66로 이루어진 폴리아미드계 합성섬유; 폴리에틸렌테레프탈레이트 및 폴리프로필렌테레프탈레이트로 이루어진 폴리에스테르계 합성섬유; 폴리아크릴니트릴계 합성섬유; 폴리비닐알코올계 합성섬유; 트리아세테이트의 반합성섬유 및 폴리에틸렌테레프탈레이트/천연섬유의 혼합섬유로 이루어진 군에서 선택되는 어느 하나인 것을 특징으로 하는 투습방수 In another aspect, the present invention is a polyamide synthetic fiber made of nylon 6 and nylon 66; Polyester-based synthetic fibers composed of polyethylene terephthalate and polypropylene terephthalate; Polyacrylonitrile-based synthetic fibers; Polyvinyl alcohol-based synthetic fibers; Water permeable waterproof, characterized in that any one selected from the group consisting of semi-synthetic fiber of triacetate and mixed fibers of polyethylene terephthalate / natural fiber
또한 본 발명은 투습방수용 코팅물의 코팅방법에 있어서, 테프론 처리된 필름 준비단계; 상기 필름상에 폴리우레탄 아크릴레이트와 다관능성 모노머가 첨가된 수지로 코팅하는 단계; 상기 코팅된 필름을 UV경화, 수세 및 건조하는 단계; 상기 코팅된 필름을 코팅층과 필름으로 박리하는 단계; 및 상기 코팅층을 직물상에 접착하는 단계로 이루어지는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법을 제공한다.In another aspect, the present invention, the coating method of the waterproof coating for water vapor transmission, Teflon-treated film preparation step; Coating with a resin to which polyurethane acrylate and a polyfunctional monomer are added on the film; UV curing, washing and drying the coated film; Peeling the coated film into a coating layer and a film; And it provides a coating method of the moisture-permeable waterproof coating comprising the step of adhering the coating layer on the fabric.
또한 본 발명은 상기 코팅단계에서 10 내지 30㎛의 코팅층을 형성하고, 100 내지 160℃에서 건조하여 베이스층을 형성하는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법을 제공한다.In another aspect, the present invention provides a coating method of the waterproof coating for forming a base layer by forming a coating layer of 10 to 30㎛ in the coating step, and dried at 100 to 160 ℃.
또한 본 발명은 상기 친수무공형 폴리우레탄 아크릴레이트 수지가 분자량 200 내지 2000의 PEG가 합성된 것을 특징으로 하는 투습방수용 코팅물의 코팅방법을 제공한다.In another aspect, the present invention provides a method for coating a water-permeable waterproof coating, characterized in that the hydrophilic non-porous polyurethane acrylate resin is a PEG having a molecular weight of 200 to 2000.
또한 본 발명은 상기 접착하는 단계가 핫멜트필름으로 접착하는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법을 제공한다.In another aspect, the present invention provides a coating method of the moisture-permeable waterproof coating, characterized in that the step of adhering with a hot melt film.
또한 본 발명은 상기 자외선 경화가 1.0 내지 5.0J/㎠의 조사에너지로 경화하는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법을 제공한다.In another aspect, the present invention provides a coating method of the moisture-permeable waterproof coating, characterized in that the ultraviolet curing is cured with irradiation energy of 1.0 to 5.0J / ㎠.
또한 본 발명은 상기 직물이 나일론6 및 나일론66로 이루어진 폴리아미드계 합성섬유; 폴리에틸렌테레프탈레이트 및 폴리프로필렌테레프탈레이트로 이루어진 폴리에스테르계 합성섬유; 폴리아크릴니트릴계 합성섬유; 폴리비닐알코올계 합성섬유; 트리아세테이트의 반합성섬유 및 폴리에틸렌테레프탈레이트/천연섬유의 혼합섬유로 이루어진 군에서 선택되는 어느 하나인 것을 특징으로 하는 투습방수 직물을 제공한다.
In another aspect, the present invention is a polyamide synthetic fiber made of nylon 6 and nylon 66; Polyester-based synthetic fibers composed of polyethylene terephthalate and polypropylene terephthalate; Polyacrylonitrile-based synthetic fibers; Polyvinyl alcohol-based synthetic fibers; It provides a moisture-permeable waterproof fabric, characterized in that any one selected from the group consisting of a semi-synthetic fiber of triacetate and a mixed fiber of polyethylene terephthalate / natural fiber.
본 발명에 의한 투습방수직물은 친수무공형 폴리우레탄 아크릴레이트의 코팅층을 따로 형성한 후 직물에 접착함으로써 투습도와 내수압이 우수한 코팅물로 성능이 우수한 투습방수 직물을 제조할 수 있는 효과가 있다.The moisture-permeable waterproof fabric according to the present invention has an effect of forming a moisture-permeable waterproof fabric having excellent moisture permeability and water pressure resistance by forming a coating layer of hydrophilic non-porous polyurethane acrylate separately and then adhering to the fabric.
또한, 코팅액으로 친수무공형 폴리우레탄 아크릴레이트를 사용하여 솔벤트의 사용이 없고, 저탄소 녹색성장을 위한 친환경 섬유가공기술을 제공할 수 있는 효과가 있다.
In addition, using a hydrophilic non-porous polyurethane acrylate as a coating solution, there is no use of solvent, and there is an effect that can provide an eco-friendly fiber processing technology for low carbon green growth.
도 1는 본 발명에 따른 투습방수용 코팅물의 코팅방법을 나타낸 공정도이다.1 is a process chart showing a coating method of the waterproof coating for waterproofing according to the present invention.
이하 본 발명에 첨부된 도면을 참조하여 본 발명의 바람직한 일실시예를 상세히 설명하기로 한다. 우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 발명을 설명함에 내수압이 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, it should be noted that, in the drawings, the same components or parts have the same reference numerals as much as possible. In describing the present invention, a detailed description of a known function or configuration in which water pressure is associated will be omitted in order not to obscure the subject matter of the present invention.
본 명세서에서 사용되는 정도의 용어 "약", "실질적으로" 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.The terms "about "," substantially ", etc. used to the extent that they are used herein are intended to be taken to mean an approximation of, or approximation to, the numerical values of manufacturing and material tolerances inherent in the meanings mentioned, Accurate or absolute numbers are used to help prevent unauthorized exploitation by unauthorized intruders of the referenced disclosure.
본 발명은 투습방수용 코팅물, 코팅방법 및 이를 이용한 코팅직물에 관한 것으로 투습방수용 코팅물의 코팅방법에 있어서, 테프론 처리된 필름 준비단계; 상기 필름상에 폴리우레탄 아크릴레이트와 다관능성 모노머가 첨가된 수지로 코팅하는 단계; 상기 코팅된 필름을 UV경화, 수세 및 건조하는 단계; 상기 코팅된 필름을 코팅층과 필름으로 박리하는 단계; 및 상기 코팅층을 직물상에 접착하는 단계로 이루어지는 것을 특징으로 하는 투습방수용 코팅물 및 코팅방법을 제공한다.
The present invention relates to a moisture-permeable waterproof coating, a coating method and a coating fabric using the same, The method for coating the moisture-permeable waterproof coating, Teflon-treated film preparation step; Coating with a resin to which polyurethane acrylate and a polyfunctional monomer are added on the film; UV curing, washing and drying the coated film; Peeling the coated film into a coating layer and a film; And it provides a moisture-permeable waterproof coating and coating method comprising the step of adhering the coating layer on the fabric.
도 1은 본 발명에 따른 투습방수용 코팅물의 코팅방법을 나타낸 공정도이다.1 is a process chart showing a coating method of the waterproof coating for waterproofing according to the present invention.
본 발명은 테프론 처리된 필름 준비단계, 코팅층 형성단계, UV 경화, 수세 및 건조 단계, 필름과 코팅층 박리단계, 접착단계로 이루어진다.The present invention comprises a Teflon-treated film preparation step, coating layer forming step, UV curing, washing and drying step, the film and the coating layer peeling step, adhesion step.
본 발명은 코팅층을 형성하여 직물상에 접착하는 것으로 코팅층을 형성하기 위한 필름을 준비한다.The present invention prepares a film for forming a coating layer by forming a coating layer and adhering onto a fabric.
테프론 처리된 필름을 준비하여 상기 필름 일면에 코팅층을 형성할 수 있다. 상기 코팅층에 사용되는 코팅액은 폴리우레탄 아크릴레이트와 다관능성 모노머가 첨가된 것으로 친수무공형 타입의 폴리우레탄 아크릴레이트 수지를 사용하는 것이 바람직하다. 상기 폴리우레탄 아크릴레이트 수지는 분자량 200 내지 2000의 PEG가 합성된 친수무공형 타입의 폴리우레탄 아크릴레이트 수지이다.A Teflon-treated film may be prepared to form a coating layer on one surface of the film. The coating liquid used for the coating layer is a polyurethane acrylate and a polyfunctional monomer is added, it is preferable to use a hydrous non-porous type polyurethane acrylate resin. The polyurethane acrylate resin is a hydrophilic non-porous type polyurethane acrylate resin synthesized with a PEG having a molecular weight of 200 to 2000.
상기 모노머는 TMPTA(Trimethylolpropane triacrylate), TPGDA(Tripropyleneglycol diacrylate), DPHA(Dipentaerythritol hexaacrylate) 등으로 이루어진 군에서 1이상 선택될 수 있다.The monomer may be at least one selected from the group consisting of trimethylolpropane triacrylate (TMPTA), tripropyleneglycol diacrylate (TPGDA), dipentaerythritol hexaacrylate (DPHA), and the like.
상기 코팅액으로 사용되는 폴리우레탄 아크릴레이트 수지는 고형분에 대하여 5 내지 20 중량%의 다관능성 모노머로 이루어져 있으며 코팅층 두께 약 10 내지 30㎛인 것이 바람직한데, 상기 두께의 코팅층에서 투습도 15,000 내지 20,000g/㎡/24hr, 내수압 4,000 내지 15,000mmH2O인 것을 특징으로 한다.Polyurethane acrylate resin used as the coating solution is composed of 5 to 20% by weight of a multifunctional monomer with respect to the solid content, and the coating layer thickness is preferably about 10 to 30㎛, the moisture permeability of the coating layer of the thickness of 15,000 to 20,000g / ㎡ / 24hr, water pressure is 4,000 to 15,000mmH 2 O, characterized in that.
상기 테프론 처리된 필름에 코팅층을 형성한 후에 UV 경화처리를 하는 단계를 거치는 데, 상기 UV 경화단계에서 자외선 출력강도는 1.0 내지 5.0J/cm2의 조사에너지로 경화하는 것이 바람직하다. 또한, 자외선 조사 시간은 0.5 내지 10분이 바람직하며, 1 내지 5분이 더욱 바람직하다.After forming a coating layer on the Teflon-treated film is subjected to a UV curing process, the UV output strength in the UV curing step is preferably cured with irradiation energy of 1.0 to 5.0J / cm 2 . Moreover, as for ultraviolet irradiation time, 0.5 to 10 minutes are preferable, and 1 to 5 minutes are more preferable.
또한, 상기 UV 경화단계 이후에 수세 및 건조하는 과정을 거치는 데, 상기 UV 경화 처리후에 수세공정은 온수 60 내지 100℃에서 약 3분간 수세하여 경화되지 않은 부분을 제거한다. 또한, 수세공정 이후에 80 내지 130℃의 온도로 약 1분간 건조한다.In addition, after the UV curing step, the process of washing with water and drying, after the UV curing process, the washing process is washed with water for about 3 minutes at 60 to 100 ℃ hot water to remove the uncured portion. In addition, it is dried for about 1 minute at the temperature of 80-130 degreeC after a washing process.
또한, 박리단계에서는 필름과 코팅층을 박리하는 것으로 상기 건조과정을 거치면 테프론필름의 일면에 코팅층을 형성하게 된다. 상기 코팅층은 테프론 필름으로 부터 박리하여 코팅물로 활용할 수 있다.In addition, in the peeling step, the film and the coating layer are peeled off to form a coating layer on one surface of the Teflon film through the drying process. The coating layer may be used as a coating by peeling from the Teflon film.
마지막으로 상기 접착단계에서는 상기로 얻어진 코팅층을 직물과 접착한다. 상기 접착은 핫멜트 접착하여 접착하는 것이 바람직하다.Finally, in the bonding step, the obtained coating layer is bonded to the fabric. The adhesion is preferably hot melt adhesion.
상기와 같은 방법으로 제조된 본 발명의 투습방수용 코팅물은 직물에 코팅되어 친수무공형 폴리우레탄 수지는 투습도 및 내수압를 제어해 준다.The moisture-permeable waterproof coating of the present invention prepared by the above method is coated on the fabric, the hydrophilic non-porous polyurethane resin controls the moisture permeability and water pressure.
본 발명의 코팅직물에서 사용하는 직물은 특별히 제한없이 사용할 수 있으나, 바람직하게는 나일론6 및 나일론66로 이루어진 폴리아미드계 합성섬유; 폴리에틸렌테레프탈레이트 및 폴리프로필렌테레프탈레이트로 이루어진 폴리에스테르계 합성섬유; 폴리아크릴니트릴계 합성섬유; 폴리비닐알코올계 합성섬유; 트리아세테이트의 반합성섬유 및 폴리에틸렌테레프탈레이트/천연섬유의 혼합섬유 등을 사용할 수 있다.
Fabrics used in the coating fabric of the present invention can be used without particular limitation, preferably polyamide-based synthetic fibers made of nylon 6 and nylon 66; Polyester-based synthetic fibers composed of polyethylene terephthalate and polypropylene terephthalate; Polyacrylonitrile-based synthetic fibers; Polyvinyl alcohol-based synthetic fibers; Semi-synthetic fibers of triacetate and mixed fibers of polyethylene terephthalate / natural fibers can be used.
이하, 본 발명의 실시예 및 비교예에 대하여 상세히 설명한다. 그러나, 본 발명은 하기 실시예로 의해 권리범위가 한정되는 것은 아니다.
Hereinafter, the Example and comparative example of this invention are demonstrated in detail. However, the present invention is not limited by the following examples.
실시예Example 1 One
테프론 필름을 준비하여 상기 필름의 일면에 코팅을 하는 데, 코팅액으로는 상기 친수무공형 폴리우레탄 아크릴레이트 수지로 분자량 200 내지 2000의 PEG가 합성된 것을 사용하였다.A Teflon film was prepared and coated on one side of the film. As the coating solution, PEG having a molecular weight of 200 to 2000 was synthesized using the hydrophilic non-porous polyurethane acrylate resin.
코팅액을 3mm의 나이프를 이용하여 30㎛의 코팅층을 갖도록 코팅한 후 2.4J/㎠ 의 자외선 조사에너지로 조사하고, 온수 60℃에서 수세하고 120℃의 열텐터에서 약 1분간 건조한다. 건조된 코팅층은 테프론 필름층으로 부터 박리한다.The coating solution was coated to have a coating layer of 30 μm using a knife of 3 mm, irradiated with ultraviolet irradiation energy of 2.4 J / cm 2, washed with hot water at 60 ° C., and dried for about 1 minute in a 120 ° C. thermal tenter. The dried coating layer is peeled off from the Teflon film layer.
직물은 경사, 위사 밀도가 157과 119본이며 경위사 원사는 50 데니어 144 필라멘트의 폴리에스테르직물을 사용하였는 데, 상기 직물에 박리된 코팅층을 핫멜트 접착하여 코팅직물을 제조하였다.
The fabric has a warp and weft density of 157 and 119 pieces, and the weft yarn used a polyester fabric of 50 denier 144 filaments. The coated fabric was prepared by hotmelt bonding the peeled coating layer on the fabric.
실시예Example 2 2
상기 실시예 1과 동일하게 실시하되, 자외선 조사를 4.0J/㎠으로 조사하여 코팅직물을 제조하였다.
In the same manner as in Example 1, but irradiated with UV irradiation at 4.0 J / ㎠ to prepare a coated fabric.
실시예Example 3 3
상기 실시예 2와 동일하게 실시하되, 코팅층의 두께를 30㎛로 하여 코팅직물을 제조하였다.
The same process as in Example 2, but the coating fabric was prepared with a thickness of 30㎛ coating layer.
비교예Comparative example 1 One
실시예 1에 사용했던 직물상에 코팅액을 직접 스프레이법을 이용하여 코팅하되, 코팅액은 UV경화가 가능한 폴리우레탄 수지를 이용하였으며, 160℃에서 1분간 열건조 하여 코팅 직물을 제조하였다. 코팅층의 두께는 20㎛로 하였다.
Coating the coating liquid on the fabric used in Example 1 using a direct spray method, the coating liquid was used for the UV curable polyurethane resin, was heat-dried at 160 ℃ for 1 minute to prepare a coated fabric. The thickness of the coating layer was 20 micrometers.
비교예Comparative example 2 2
비교예 1과 동일하게 실시하되, 50㎛ 로 코팅 후 160℃에서 1분간 열건조 하여 코팅직물을 제조하였다.
A coating fabric was prepared in the same manner as in Comparative Example 1, after coating at 50 μm, followed by heat drying at 160 ° C. for 1 minute.
※ 측정방법※ How to measure
1. 투습도 측정 : KS 0594 초산칼륨법에 의해 측정함.1. Measurement of moisture permeability: measured by KS 0594 potassium acetate method.
2. 내수압 측정 : KS 0591 저수압법에 의해 측정함.
2. Water pressure measurement: Measured by KS 0591 low pressure method.
상기 표 1의 결과에서 나타나듯이 본 발명에 따른 투습방수용 코팅물이 코팅된 실시예 1 내지 3의 직물은 비교예 1,2의 직물보다 투습도 및 내수압이 모두 2배이상 높은 것을 알 수 있다.As shown in the results of Table 1, it can be seen that the fabrics of Examples 1 to 3 coated with the moisture-permeable waterproof coating according to the present invention are more than two times higher in both moisture permeability and water pressure than the fabrics of Comparative Examples 1,2.
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the inventions. It will be clear to those who have knowledge of.
Claims (13)
직물로 이루어진 표면층; 및
상기 직물의 상면에 폴리우레탄 아크릴레이트에 다관능성 모노머가 첨가된 수지로 코팅된 코팅층으로 이루어지되, 상기 코팅층은 UV경화로 이루어진 투습방수용 코팅물.In moisture-permeable waterproof coating,
A surface layer made of a fabric; And
A coating layer coated with a resin in which a polyfunctional monomer is added to a polyurethane acrylate on the upper surface of the fabric, wherein the coating layer is UV-curable waterproof coating.
상기 모노머는 TMPTA(Trimethylolpropane triacrylate), TPGDA(Tripropyleneglycol diacrylate), DPHA(Dipentaerythritol hexaacrylate)로 이루어진 군에서 1이상 선택되는 것을 특징으로 하는 투습방수용 코팅물.The method of claim 1
The monomer is water-proof coating for water resistance, characterized in that at least one selected from the group consisting of Trimethylolpropane triacrylate (TMPTA), Tripropyleneglycol diacrylate (TPGDA), Dipoentaerythritol hexaacrylate (DPHA).
상기 친수무공형 폴리우레탄 아크릴레이트 수지는 분자량 200 내지 2000의 PEG가 합성된 것을 특징으로 하는 투습방수용 코팅물.The method of claim 1,
The hydrophilic non-porous polyurethane acrylate resin is a moisture-permeable waterproof coating, characterized in that the PEG of 200 to 2000 molecular weight.
상기 표면층 및 코팅층은 핫멜트필름으로 접착하는 것을 특징으로 하는 투습방수용 코팅물.The method of claim 1,
The surface layer and the coating layer is waterproof coating, characterized in that the adhesive with a hot melt film.
상기 직물은 나일론6 및 나일론66로 이루어진 폴리아미드계 합성섬유; 폴리에틸렌테레프탈레이트 및 폴리프로필렌테레프탈레이트로 이루어진 폴리에스테르계 합성섬유; 폴리아크릴니트릴계 합성섬유; 폴리비닐알코올계 합성섬유; 트리아세테이트의 반합성섬유 및 폴리에틸렌테레프탈레이트/천연섬유의 혼합섬유로 이루어진 군에서 선택되는 어느 하나인 것을 특징으로 하는 투습방수 직물.The method of claim 5,
The fabric is a polyamide synthetic fiber consisting of nylon 6 and nylon 66; Polyester-based synthetic fibers composed of polyethylene terephthalate and polypropylene terephthalate; Polyacrylonitrile-based synthetic fibers; Polyvinyl alcohol-based synthetic fibers; Water permeable waterproof fabric, characterized in that any one selected from the group consisting of semi-synthetic fiber of triacetate and mixed fibers of polyethylene terephthalate / natural fiber.
테프론 처리된 필름 준비단계;
상기 필름상에 폴리우레탄 아크릴레이트에 다관능성 모노머가 첨가된 수지로 코팅하는 단계;
상기 코팅된 필름을 UV경화, 수세 및 건조하는 단계;
상기 코팅된 필름을 코팅층과 필름으로 박리하는 단계; 및
상기 코팅층을 직물상에 접착하는 단계로 이루어지는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법.In the coating method of the waterproof waterproof coating,
Teflon-treated film preparation step;
Coating with a resin to which a polyfunctional monomer is added to polyurethane acrylate on the film;
UV curing, washing and drying the coated film;
Peeling the coated film into a coating layer and a film; And
Coating method of the waterproof coating for water, characterized in that the step of adhering the coating layer on the fabric.
상기 코팅단계에서 10 내지 30㎛의 코팅층을 형성하고, 100 내지 160℃에서 건조하여 베이스층을 형성하는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법.The method of claim 7, wherein
Forming a coating layer of 10 to 30㎛ in the coating step, and drying at 100 to 160 ℃ coating method of the waterproof coating, characterized in that to form a base layer.
상기 친수무공형 폴리우레탄 아크릴레이트 수지는 분자량 200 내지 2000의 PEG가 합성된 것을 특징으로 하는 투습방수용 코팅물의 코팅방법.The method of claim 7, wherein
The hydrophilic non-porous polyurethane acrylate resin is a coating method of the moisture-permeable waterproof coating, characterized in that the PEG with a molecular weight of 200 to 2000.
상기 접착하는 단계는 핫멜트필름으로 접착하는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법.The method of claim 7, wherein
The adhering step is a coating method of the waterproof coating for water vapor transmission, characterized in that the adhesive with a hot melt film.
상기 자외선 경화는 1.0 내지 5.0J/㎠의 조사에너지로 경화하는 것을 특징으로 하는 투습방수용 코팅물의 코팅방법.The method of claim 7, wherein
The ultraviolet curing coating method of the coating for moisture-permeable waterproof, characterized in that curing with irradiation energy of 1.0 to 5.0J / ㎠.
상기 직물은 나일론6 및 나일론66로 이루어진 폴리아미드계 합성섬유; 폴리에틸렌테레프탈레이트 및 폴리프로필렌테레프탈레이트로 이루어진 폴리에스테르계 합성섬유; 폴리아크릴니트릴계 합성섬유; 폴리비닐알코올계 합성섬유; 트리아세테이트의 반합성섬유 및 폴리에틸렌테레프탈레이트/천연섬유의 혼합섬유로 이루어진 군에서 선택되는 어느 하나인 것을 특징으로 하는 투습방수 직물.The method of claim 12,
The fabric is a polyamide synthetic fiber consisting of nylon 6 and nylon 66; Polyester-based synthetic fibers composed of polyethylene terephthalate and polypropylene terephthalate; Polyacrylonitrile-based synthetic fibers; Polyvinyl alcohol-based synthetic fibers; Water permeable waterproof fabric, characterized in that any one selected from the group consisting of semi-synthetic fiber of triacetate and mixed fibers of polyethylene terephthalate / natural fiber.