KR20110068435A - Hairline decoration sheet having excellent metallic effect - Google Patents

Hairline decoration sheet having excellent metallic effect Download PDF

Info

Publication number
KR20110068435A
KR20110068435A KR1020090125393A KR20090125393A KR20110068435A KR 20110068435 A KR20110068435 A KR 20110068435A KR 1020090125393 A KR1020090125393 A KR 1020090125393A KR 20090125393 A KR20090125393 A KR 20090125393A KR 20110068435 A KR20110068435 A KR 20110068435A
Authority
KR
South Korea
Prior art keywords
layer
hairline
decorative sheet
transparent resin
release film
Prior art date
Application number
KR1020090125393A
Other languages
Korean (ko)
Other versions
KR101281430B1 (en
Inventor
김형곤
이민호
김기정
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020090125393A priority Critical patent/KR101281430B1/en
Publication of KR20110068435A publication Critical patent/KR20110068435A/en
Application granted granted Critical
Publication of KR101281430B1 publication Critical patent/KR101281430B1/en

Abstract

PURPOSE: A decoration sheet with metal effect of a hair line is provided to form the hair line on a release film. CONSTITUTION: A decoration sheet(100) comprises: a transparent resin layer(10) having a hair line(H); a metal layer(20) formed at the opposite side of the hair line; an adhesive layer(30) formed at the lower portion of the metal layer; and a substrate layer(40) formed at the lower part of the adhesive layer. The decoration sheet further comprises a primer layer between the transparent resin layer and metal layer and print layer between the adhesive layer and substrate layer.

Description

헤어라인 금속효과가 우수한 장식시트 및 그 제조방법 {HAIRLINE DECORATION SHEET HAVING EXCELLENT METALLIC EFFECT}Decorative sheet with excellent hairline metal effect and manufacturing method {HAIRLINE DECORATION SHEET HAVING EXCELLENT METALLIC EFFECT}

본 발명은 헤어라인 금속효과가 우수한 장식시트 및 그 제조방법에 관한 것으로, 보다 상세하게는 헤어라인을 형성함에 있어서, 이형필름에 헤어라인을 형성한 다음, 이를 투명수지층에 전이되도록 함으로써, 미려한 헤어라인 금속효과(금속질감)를 가지면서 치수안정성 및 성형성 등이 우수한 장식시트 및 그 제조방법에 관한 것이다. The present invention relates to a decorative sheet having excellent hairline metal effect and a method of manufacturing the same, and more particularly, in forming a hairline, by forming a hairline on a release film and then transferring it to a transparent resin layer, The present invention relates to a decorative sheet having a hairline metal effect (metal texture) and excellent in dimensional stability and formability, and a manufacturing method thereof.

제품의 디자인은 구매에 매우 높은 영향을 준다. 이에 따라, 대부분의 산업 제품은 표면에 다양한 디자인이 구현되고 있다. 특히, 플라스틱 제품의 경우에는 그 부가가치를 높이기 위해, 예를 들어 천연소재의 디자인이 구현되도록 표면에 장식시트를 부착하고 있다. 장식시트는 생활 가전제품, 자동차 내ㆍ외장재, 가구 및 건축물의 내ㆍ외장재 등의 표면 마감재로 다양하게 이용되고 있다. 특히, 금속질감(금속효과)과 헤어라인 무늬를 가지는 장식시트는 높은 심미적 효과를 제공하여 장식성 마감소재로 각광을 받고 있다. The design of the product has a very high impact on the purchase. Accordingly, most industrial products have various designs implemented on their surfaces. In particular, in the case of plastic products, in order to increase the added value, for example, a decorative sheet is attached to the surface to implement a natural material design. Decorative sheets are widely used as surface finishing materials for household appliances, automobile interior and exterior materials, furniture and buildings interior and exterior materials. In particular, the decorative sheet having a metallic texture (hair effect) and hairline pattern has been spotlighted as a decorative finishing material by providing a high aesthetic effect.

장식시트는 플라스틱 제품, 특히 플라스틱 사출 제품의 경우에는 인서트 성형 공법으로 적용되고 있다. 일반적으로, 인서트 성형 공법은 다음과 진행된다. 먼저, 장식효과(헤어라인 및 금속효과)를 갖도록 장식시트를 제조한 후, 사출 제품의 크기 및 모양에 맞도록 재단한다. 그리고 사출기 금형 안에 장식시트를 투입한 다음, 장식시트의 배면에 사출 제품용 용융 수지를 사출, 고화시킴으로써, 사출 부품의 표면에 원하는 장식효과를 부여한다. 이러한 인서트 성형 공법은 여러 장점을 제공한다. 인서트 성형용 장식시트를 이용한 제품은 도장 등의 방식으로 사출물에 직접 장식효과를 부여하거나, 점착시트 등을 부착하는 공법과 비교하여, 구현할 수 있는 장식효과가 다양하고, 제품 형상의 제약이 적은 장점이 있다. 이에 따라, 인서트 성형용 장식시트는 자동차의 내ㆍ외장재, 가전제품의 케이스 등에 주로 이용되고 있다. Decorative sheets are applied to the insert molding process in the case of plastic products, especially plastic injection products. In general, the insert molding process proceeds as follows. First, the decorative sheet is manufactured to have a decorative effect (hairline and metal effect), and then cut to fit the size and shape of the injection product. Then, the decorative sheet is put into the injection molding machine mold, and then injected and solidified molten resin for injection products on the back of the decorative sheet, thereby imparting a desired decorative effect on the surface of the injection part. This insert molding process provides several advantages. The product using the decorative sheet for insert molding has a variety of decorative effects that can be implemented and compared with the method of attaching an adhesive directly to an injection product by painting or attaching an adhesive sheet. There is this. Accordingly, the insert molding decorative sheet is mainly used for interior and exterior materials of automobiles, cases of home appliances, and the like.

일반적으로, 헤어라인 금속효과를 가지는 장식시트는 연마지를 이용하여 헤어라인 무늬를 투명필름에 직접 긁어내어 헤어라인을 구현한 후, 금속층을 증착하고 기재시트를 합판하는 방법으로 제조되고 있다. 표면 장식효과로서 미려한 헤어라인 금속효과를 갖기 위해서는 금속질감과 함께 뚜렷한 헤어라인 무늬를 가져야 한다. 이때, 뚜렷한 헤어라인 무늬를 갖도록 상기 투명필름은 우수한 성형성을 가져야 한다. 즉, 투명필름은 연마지를 통해 헤어라인 무늬가 잘 구현되도록 소정의 유연성을 가져야 한다. 또한, 투명필름은 제조공정에서 수반되는 치수안정성을 가져야 한다. In general, a decorative sheet having a hairline metal effect is produced by scraping a hairline pattern directly onto a transparent film using an abrasive paper to implement a hairline, then depositing a metal layer and plywood the base sheet. In order to have a beautiful hairline metallic effect as a surface decoration effect, it must have a distinctive hairline pattern with a metallic texture. In this case, the transparent film should have excellent moldability to have a distinct hairline pattern. That is, the transparent film should have a certain flexibility so that the hairline pattern is well realized through the abrasive paper. In addition, the transparent film should have dimensional stability accompanying the manufacturing process.

그러나 종래 기술에 따른 장식시트는 치수안정성이 떨어져 제조공정에 한계를 갖거나, 성형성이 떨어져 헤어라인 무늬가 뚜렷하지 않고 사출 제품에 적용이 어려운 문제점이 있다. However, the decorative sheet according to the prior art has a limitation in the manufacturing process, the dimensional stability is poor, or the moldability is not clear, there is a problem that it is difficult to apply to injection products.

구체적으로, 성형성을 높이기 위해서는 그 만큼 투명필름의 치수안정성이 떨어지기 때문에 치수안정성의 Trade-Off 관계로 인해 고온의 환경에서 이루어지는 제조공정에 여러 제약(한계)이 따른다. 또한, 이와 반대로 치수안정성이 높은 투명필름의 경우 연마제를 통한 헤어라인 구현 시 경도가 높아 뚜렷한 헤어라인 무늬를 형성하기 어렵다. 이와 함께 치수안정성이 높은 경우 성형성이 떨어져 사출 제품에 적용 시 사출 제품의 형상과 일치(융합)되기 어렵다. 이에 따라, 종래 기술에 따른 장식시트는 치수안정성이 없거나, 성형성이 떨어지고, 미려한 헤어라인 금속효과를 갖지 못하는 문제점이 있다. Specifically, in order to increase the formability, the dimensional stability of the transparent film is reduced by that much, due to the trade-off relationship of the dimensional stability there are various restrictions (limitations) in the manufacturing process made in a high temperature environment. On the contrary, in the case of the transparent film having high dimensional stability, it is difficult to form a clear hairline pattern due to the high hardness when the hairline is realized through the abrasive. In addition, when the dimensional stability is high, moldability is poor, and when applied to an injection product, it is difficult to match (fusion) the shape of the injection product. Accordingly, the decorative sheet according to the prior art has a problem that there is no dimensional stability, poor formability, and does not have a beautiful hairline metal effect.

본 발명은 상기한 바와 같은 종래 기술의 문제점을 해결하기 위한 것으로, 종래와 같이 투명필름에 헤어라인을 직접 구현하지 않고, 이형필름에 헤어라인을 형성한 다음, 이를 투명수지층에 전이시킴으로써, 우수한 치수안정성 및 성형성 등을 가지면서 헤어라인 무늬가 뚜렷하여 헤어라인 금속효과(금속질감)가 우수한 장식시트 및 그 제조방법을 제공하는 데에 그 목적이 있다. The present invention is to solve the problems of the prior art as described above, by forming a hairline on the release film, and then transfer it to the transparent resin layer, without implementing the hairline directly on the transparent film as in the prior art, It is an object of the present invention to provide a decorative sheet excellent in hairline metal effect (metal texture) and a method of manufacturing the same, having dimensional stability and moldability and having a clear hairline pattern.

상기 목적을 달성하기 위하여 본 발명은, The present invention to achieve the above object,

헤어라인이 형성된 투명수지층; A transparent resin layer on which a hairline is formed;

상기 투명수지층의 헤어라인이 형성된 면의 반대쪽 면에 형성된 금속층; A metal layer formed on a surface opposite to a surface on which the hairline of the transparent resin layer is formed;

상기 금속층의 하부에 형성된 접착제층; 및 An adhesive layer formed under the metal layer; And

상기 접착제층의 하부에 형성된 기재층을 포함하고, It includes a base layer formed on the lower portion of the adhesive layer,

상기 투명수지층에 형성된 헤어라인은, 이형필름에 형성된 헤어라인이 전이되어 형성된 장식시트를 제공한다. The hairline formed on the transparent resin layer provides a decorative sheet formed by transferring the hairline formed on the release film.

이때, 본 발명에 따른 장식시트는, 상기 투명수지층과 금속층의 사이에 형성된 프라이머층을 더 포함하거나, 상기 접착제층과 기재층의 사이에 형성된 인쇄층을 더 포함할 수 있다. In this case, the decorative sheet according to the present invention may further include a primer layer formed between the transparent resin layer and the metal layer, or may further include a printing layer formed between the adhesive layer and the base layer.

또한, 본 발명은, In addition, the present invention,

이형필름에 헤어라인을 형성하는 단계; Forming a hairline on the release film;

상기 이형필름의 헤어라인이 형성된 면에 투명수지층을 형성하는 단계; Forming a transparent resin layer on a surface on which the hairline of the release film is formed;

상기 투명수지층 상에 금속층을 형성하는 단계; Forming a metal layer on the transparent resin layer;

상기 금속층 상에 접착제층을 형성하는 단계; Forming an adhesive layer on the metal layer;

상기 접착제층 상에 기재층을 형성하는 단계; 및 Forming a base layer on the adhesive layer; And

상기 이형필름을 제거하여 투명수지층의 표면에 헤어라인이 전이되게 하는 단계를 포함하는 장식시트의 제조방법을 제공한다. Removing the release film provides a method of manufacturing a decorative sheet comprising the step of causing the hairline to be transferred to the surface of the transparent resin layer.

이때, 본 발명에 따른 장식시트의 제조방법은, 상기 투명수지층과 금속층의 사이에 프라이머층을 형성하는 단계를 더 포함하거나, 상기 접착제층과 기재층의 사이에 인쇄층을 형성하는 단계를 더 포함할 수 있다. At this time, the manufacturing method of the decorative sheet according to the present invention further comprises the step of forming a primer layer between the transparent resin layer and the metal layer, or further comprising the step of forming a printing layer between the adhesive layer and the base layer. It may include.

본 발명에 따르면, 이형필름에 헤어라인을 형성한 다음, 이를 투명수지층에 전이시키는 캐스팅 방법으로 헤어라인이 뚜렷하게 구현되어, 우수한 헤어라인 금속효과를 갖는다. 또한, 투명수지층은 치수안정성 및 성형성이 높은 재질의 사용이 가능하여 장식시트의 제조공정에 제약이 따르지 않고, 사출 제품에 적용시 성형성이 우수하다. 따라서 본 발명에 따르면, 우수한 치수안정성 및 성형성 등을 가지면서 헤어라인 금속효과(금속질감)가 우수한 효과를 갖는다. According to the present invention, a hairline is formed on the release film, and then the hairline is clearly implemented by a casting method of transferring it to the transparent resin layer, thereby having an excellent hairline metal effect. In addition, the transparent resin layer is capable of using a material having high dimensional stability and formability, so that the manufacturing process of the decorative sheet is not restricted, and excellent moldability when applied to the injection product. Therefore, according to the present invention, the hairline metal effect (metal texture) has an excellent effect while having excellent dimensional stability and formability.

이하, 첨부된 도면을 참조하여 본 발명을 보다 상세히 설명한다. 첨부된 도면은 본 발명의 예시적인 실시예를 도시한 것으로서, 이는 본 발명의 이해를 돕도록 하기 위해 제공되는 것일 뿐, 이에 의해 본 발명의 기술적 범위가 한정되는 것은 아니다. Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings. The accompanying drawings show exemplary embodiments of the present invention, which are provided only to assist in understanding the present invention, and thus the technical scope of the present invention is not limited thereto.

도 1은 본 발명의 제1실시예에 따른 장식시트 및 이의 제조과정을 보인 단면도이다. 그리고 도 2는 본 발명의 제2실시예에 따른 장식시트를 보인 단면도이다. 1 is a cross-sectional view showing a decorative sheet and a manufacturing process thereof according to a first embodiment of the present invention. 2 is a cross-sectional view showing a decorative sheet according to a second embodiment of the present invention.

먼저, 도 1을 참조하여 설명하면, 본 발명에 따른 장식시트(100)는 헤어라인(H)이 형성된 투명수지층(10); 상기 투명수지층(10)의 하부에 형성된 금속층(20); 상기 금속층(20)의 하부에 형성된 접착제층(30); 및 상기 접착제층(30)의 하부에 형성된 기재층(40)을 포함한다. First, referring to FIG. 1, the decorative sheet 100 according to the present invention includes a transparent resin layer 10 on which a hairline H is formed; A metal layer 20 formed under the transparent resin layer 10; An adhesive layer 30 formed under the metal layer 20; And a base layer 40 formed under the adhesive layer 30.

또한, 도 2를 참조하여 설명하면, 본 발명에 따른 장식시트(100)는 본 발명의 다른 형태에 따라서, 상기 투명수지층(10)과 금속층(20)의 사이에 형성된 프라이머층(50)을 더 포함할 수 있다. 아울러, 본 발명에 따른 장식시트(100)는 본 발명의 또 다른 형태에 따라서, 상기 접착제층(30)과 기재층(40)의 사이에 형성된 인쇄층(60)을 더 포함할 수 있다. 2, the decorative sheet 100 according to the present invention is a primer layer 50 formed between the transparent resin layer 10 and the metal layer 20 according to another embodiment of the present invention. It may further include. In addition, the decorative sheet 100 according to the present invention may further include a printing layer 60 formed between the adhesive layer 30 and the base layer 40 according to another embodiment of the present invention.

이때, 도 1 및 도 2에 도시한 바와 같이, 상기 투명수지층(10)의 일면(상부면)에는 헤어라인(H)이 형성되어 있고, 반대쪽 다른 면(하부면)에는 금속층(20)이 형성된 구조(도 1)를 갖거나 프라이머층(50)이 형성된 구조(도 2)를 가질 수 있다. 즉, 상기 금속층(20)과 프라이머층(50)은 투명수지층(10)의 하부에 형성되어 있되, 투명수지층(10)의 헤어라인(H)이 형성된 면의 반대쪽 면에 형성되어 있다. 1 and 2, the hairline H is formed on one surface (upper surface) of the transparent resin layer 10, and the metal layer 20 is formed on the other surface (lower surface) on the opposite side. It may have a structure (FIG. 1) formed or a structure (FIG. 2) in which the primer layer 50 is formed. That is, the metal layer 20 and the primer layer 50 are formed under the transparent resin layer 10, but are formed on the opposite side of the surface on which the hairline H of the transparent resin layer 10 is formed.

또한, 상기 투명수지층(10)에 형성된 헤어라인(H)은, 본 발명에 따라서 이형필름(200)에 형성된 헤어라인(H)이 캐스팅 방법으로 전이되어 형성된다. 이를 본 발명에 따른 제조방법을 통하여 설명하면 다음과 같다. In addition, the hairline H formed on the transparent resin layer 10 is formed by transferring the hairline H formed on the release film 200 according to the present invention by a casting method. This will be described through the manufacturing method according to the present invention.

본 발명에 따른 장식시트(100)의 제조방법은, 이형필름(200)에 헤어라인(H)을 형성하는 단계; 상기 이형필름(200)의 헤어라인(H)이 형성된 면에 투명수지층(10)을 형성하는 단계; 상기 투명수지층(10) 상에 금속층(20)을 형성하는 단계; 상기 금속층(20) 상에 접착제층(30)을 형성하는 단계; 상기 접착제층(30) 상에 기재층(40)을 형성하는 단계; 및 상기 이형필름(200)을 제거하여 투명수지층(10)의 표면에 헤어라인(H)이 전이되게 하는 단계를 포함한다. Method for producing a decorative sheet 100 according to the present invention, forming a hairline (H) on the release film 200; Forming a transparent resin layer 10 on a surface on which the hairline H of the release film 200 is formed; Forming a metal layer (20) on the transparent resin layer (10); Forming an adhesive layer (30) on the metal layer (20); Forming a base layer (40) on the adhesive layer (30); And removing the release film 200 so that the hairline H is transferred to the surface of the transparent resin layer 10.

또한, 본 발명에 따른 장식시트(100)의 제조방법은, 투명수지층(10)과 금속층(20)의 사이에 프라이머층(50)을 형성하는 단계를 더 포함할 수 있다. 아울러, 본 발명에 따른 장식시트(100)의 제조방법은, 접착제층(30)과 기재층(40)의 사이에 인쇄층(60)을 형성하는 단계를 더 포함할 수 있다. In addition, the manufacturing method of the decorative sheet 100 according to the present invention may further comprise the step of forming a primer layer 50 between the transparent resin layer 10 and the metal layer 20. In addition, the manufacturing method of the decorative sheet 100 according to the present invention may further comprise the step of forming a printing layer 60 between the adhesive layer 30 and the base layer 40.

본 발명에 따라서, 상기 헤어라인(H)은 종래와 같이 투명필름에 헤어라인을 직접 구현하지 않고, 별도의 이형필름(200)에 헤어라인(H)을 형성한 다음, 이를 투명수지층(10)에 전이시키는 캐스팅 방법으로 투명수지층(10)에 헤어라인(H)이 구현된다. 이때, 상기 이형필름(200)에 헤어라인(H)을 형성함에 있어서는, 특별히 한정하는 것은 아니지만 다음과 같은 방법이 고려될 수 있다. According to the present invention, the hairline (H) does not directly implement a hairline on the transparent film as in the prior art, and forms a hairline (H) on a separate release film 200, and then the transparent resin layer 10 Hairline (H) is implemented in the transparent resin layer 10 by a casting method to transfer to. At this time, in forming the hairline (H) in the release film 200, although not particularly limited, the following method may be considered.

예를 들어, 연마지를 이용하여 긁어내는 방법으로 이형필름(200)에 헤어라인(H)을 형성시킬 수 있다. 또한, 다른 예를 들어, 이형필름(200) 상에 별도의 수지를 헤어라인 무늬로 코팅, 경화시켜 헤어라인(H)을 형성시킬 수 있다. 이때, 상기 헤어라인 형성용 수지는, 예를 들어 열경화형 수지 또는 UV 수지 등을 이용할 수 있다. For example, the hairline H may be formed on the release film 200 by scraping off the abrasive paper. In addition, for example, a separate resin may be coated and cured with a hairline pattern on the release film 200 to form a hairline (H). At this time, the resin for hairline formation may use, for example, a thermosetting resin or a UV resin.

상기 이형필름(200)은 여기에 형성된 헤어라인(H)이 투명수지층(10)에 전이되게 한 후, 박리 제거된다. 즉, 이형필름(200)은 최종 제품에 포함되지 않는다. 이에 따라, 이형필름(200)은 그 재질이 제한되지 않으며, 바람직하게는 치수안정성을 가지면 것이면 좋다. 상기 이형필름(200)은, 예를 들어 치수안정성을 가지는 합성수지 필름 등을 사용할 수 있다. 이형필름(200)은, 바람직하게는 특별히 한정하는 것은 아니지만 폴리에스테르 필름 또는 폴리에틸렌테레프탈레이트 필름 등을 사용할 수 있으며, 보다 바람직하게는 폴리에틸렌테레프탈레이트 필름을 사용하면 좋다. The release film 200 allows the hairline H formed thereon to be transferred to the transparent resin layer 10 and then peeled off. That is, the release film 200 is not included in the final product. Accordingly, the release film 200 is not limited in its material, and preferably may have dimensional stability. As the release film 200, for example, a synthetic resin film having dimensional stability may be used. Although the release film 200 is not specifically limited, A polyester film, a polyethylene terephthalate film, etc. can be used preferably, More preferably, a polyethylene terephthalate film may be used.

상기 투명수지층(10)은 본 발명에 따른 장식시트(10)의 헤어라인 효과를 제공하는 역할을 한다. 또한, 투명수지층(10)은 본 발명에 따른 장식시트(10)를 인서트 성형 공법으로 사출 제품에 적용할 때, 또는 장식시트(100)의 제조공정 시의 외부 환경으로부터 하부의 금속층(20) 및 선택적으로 포함되는 인쇄층(60)을 보호하는 역할을 한다. The transparent resin layer 10 serves to provide a hairline effect of the decorative sheet 10 according to the present invention. In addition, the transparent resin layer 10 is the lower metal layer 20 from the external environment when the decorative sheet 10 according to the present invention is applied to the injection product by the insert molding method, or during the manufacturing process of the decorative sheet 100 And it serves to protect the printed layer 60 optionally included.

상기 투명수지층(10)은, 헤어라인(H)이 구현된 이형필름(200)에 수지 조성물이 도포된 후 건조(경화)되어 형성된다. 이때, 투명수지층(10)을 구성하는 수지 수 성물은 이형필름(200)의 헤어라인(H)이 형성된 면에 도포된다. 그리고 투명수지층(10)의 형성(도포, 건조) 후, 이형필름(200)은 박리, 제거된다. 이에 따라, 투명수지층(10)의 표면에는 이형필름(200)에 형성된 헤어라인(H) 무늬가 전이되어 형성된다. 아울러, 상기 이형필름(200)은 투명수지층(10)의 하부에 순차적으로 금속층(20), 접착제층(30) 및 기재층(40) 등을 적층, 형성한 후에 박리, 제거될 수 있다. The transparent resin layer 10 is formed by drying (curing) after the resin composition is applied to the release film 200, the hairline (H) is implemented. At this time, the resin aqueous material constituting the transparent resin layer 10 is applied to the surface on which the hairline (H) of the release film 200 is formed. After the formation (coating and drying) of the transparent resin layer 10, the release film 200 is peeled off and removed. Accordingly, the hairline (H) pattern formed on the release film 200 is transferred to the surface of the transparent resin layer 10 is formed. In addition, the release film 200 may be peeled off and removed after sequentially laminating and forming the metal layer 20, the adhesive layer 30, the base layer 40, and the like under the transparent resin layer 10.

상기 투명수지층(10)은 헤어라인(H) 무늬가 뚜렷하게 구현될 수 있고, 치수안정성 및 성형성이 우수한 재질로부터 선택되면 좋다. 상기 투명수지층(10)은 예를 들어 폴리메틸메타크릴레이트, 폴리에틸메타크릴레이트, 폴리부틸메타크릴레이트, 폴리우레탄 및 폴리에스테르 등으로 이루어진 군중에서 선택된 하나 이상을 포함할 수 있다. 구체적으로, 투명수지층(10)은 상기 나열한 수지 중에서 선택된 하나 또는 2 이상의 수지가 적절한 조성비로 포함된 수지 조성물을 이형필름(200)에 코팅하여 형성할 수 있다. 이때, 코팅 방법은 제한되지 않으며, 예를 들어 그라비아 코팅, 마이크로 그라비아 코팅, 콤마 코팅, 슬롯다이 코팅, 롤 코팅, 리버스 롤 코팅 등의 다양한 코팅 방식이 적용될 수 있다. The transparent resin layer 10 may be embodied with a distinctive hairline (H) pattern, it may be selected from a material excellent in dimensional stability and formability. The transparent resin layer 10 may include, for example, one or more selected from the group consisting of polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, polyurethane, polyester, and the like. Specifically, the transparent resin layer 10 may be formed by coating the release film 200 with a resin composition containing one or two or more resins selected from the above-listed resins in an appropriate composition ratio. At this time, the coating method is not limited, and for example, various coating methods such as gravure coating, micro gravure coating, comma coating, slot die coating, roll coating, reverse roll coating and the like may be applied.

또한, 상기 투명수지층(10)은 이형필름(200)에 수지 조성물을 코팅하여 형성하되, 수지 조성물 전체 100중량부에 대하여 상기 나열한 수지(고형분) 15 ~ 40중량부 및 유기용제 60 ~ 85중량부를 포함하는 수지 조성물을 코팅하여 형성할 수 있다. 이때, 상기 유기용제는, 특별히 한정하는 것은 아니지만 메틸에틸케톤, 메틸부틸케톤, 톨루엔, 크실렌, 이소프로필알코올 및 에틸아세테이트 등으로 이루어진 군 중에서 선택된 하나 이상(선택된 1종 또는 2종 이상의 혼합)을 사용할 수 있다. 또한, 바람직한 구현예에 따라서, 상기 투명수지층(10)은 금속층(20) 및 인쇄층(60)의 보호능이 향상되도록 내화학성 및 내스크래치성 등이 우수하면 좋다. 이때, 내화학성 및 내스크래치성 등이 향상되도록 투명수지층(10)을 구성하는 상기 수지 조성물은 이소시아네이트계 경화제를 더 포함할 수 있다. 상기 이소시아네이트계 경화제는, 예를 들어 헥사메틸렌 디이소아네이트(HMDI ; Hexamethylene Diisocyanate), 톨루엔 디이소시아네이트(TDI ; Toluene Diisocyanate), 디페닐메탄 디이소시아네이트(MDI ; Diphenylmethane Diisocyanate) 및 이소프론 디이소시아네이트(IPDI ; Isophorone Diisocyanate) 등으로 이루어진 군중에서 선택된 하나 이상을 사용할 수 있다. 이러한 이소시아네이트 경화제는 수지 조성물 전체 100중량부에 대하여 0 ~ 10중량부의 범위로 포함될 수 있으며, 보다 구체적으로는 0.2 ~ 10중량부로 포함될 수 있다. 아울러, 상기 투명수지층(10)을 구성하는 수지 조성물은, 각 성분의 중량비에 있어서 최종제품의 요구물성 및 공정조건에 따라 변동될 수 있으며, 내스크래치성, 내화학성, 내광성, 성형성, 치수안정성, 깨짐성, 코팅방법, 경화시간 등을 고려하여 적절하게 조절될 수 있다. 예를 들어, 성형성을 높이기 위해서는 상기 경화제 함량을 3중량부 이하로 제한하는 것이 바람직하다. In addition, the transparent resin layer 10 is formed by coating the resin composition on the release film 200, 15 to 40 parts by weight of the resin (solid content) listed above with respect to 100 parts by weight of the total resin composition and 60 to 85 weight of the organic solvent It can form by coating the resin composition containing a part. In this case, the organic solvent is not particularly limited, but may be one or more selected from the group consisting of methyl ethyl ketone, methyl butyl ketone, toluene, xylene, isopropyl alcohol, ethyl acetate, and the like (selected one or a mixture of two or more selected). Can be. In addition, according to a preferred embodiment, the transparent resin layer 10 may be excellent in chemical resistance, scratch resistance and the like to improve the protection of the metal layer 20 and the printing layer 60. In this case, the resin composition constituting the transparent resin layer 10 may further include an isocyanate-based curing agent to improve chemical resistance and scratch resistance. The isocyanate-based curing agent is, for example, hexamethylene diisocyanate (HMDI; Hexamethylene Diisocyanate), toluene diisocyanate (TDI; Toluene Diisocyanate), diphenylmethane diisocyanate (MDI; Diphenylmethane Diisocyanate) and isopron diisocyanate (IPDI; You can use one or more selected from a crowd consisting of Isophorone Diisocyanate). Such isocyanate curing agent may be included in the range of 0 to 10 parts by weight with respect to 100 parts by weight of the total resin composition, more specifically may be included in 0.2 to 10 parts by weight. In addition, the resin composition constituting the transparent resin layer 10 may vary depending on the required physical properties and process conditions of the final product in the weight ratio of each component, scratch resistance, chemical resistance, light resistance, moldability, dimensional stability It may be appropriately adjusted in consideration of cracking property, coating method, curing time, and the like. For example, in order to increase moldability, it is preferable to limit the content of the curing agent to 3 parts by weight or less.

상기 금속층(20)은 투명수지층(10)의 하부에 형성되어 장식시트(10)의 금속효과(금속질감)를 부여해주는 것으로서, 이는 다양한 금속 코팅 방법으로 형성될 수 있다. 상기 금속층(20)을 구성하는 금속은 예를 들어 알루미늄, 크롬, 니켈, SUS, 구리, 은, 금 및 백금 등으로 이루어진 군중에서 선택된 하나 이상일 수 있 다. 아울러, 상기 금속층(20)은 진공증착, 스퍼터링(Sputtering), 페이스트(paste) 코팅 등의 다양한 방식으로 형성될 수 있으며, 바람직하게는 스퍼터링 공법이 적용되면 좋다. The metal layer 20 is formed under the transparent resin layer 10 to impart a metal effect (metal texture) of the decorative sheet 10, which may be formed by various metal coating methods. The metal constituting the metal layer 20 may be, for example, at least one selected from the group consisting of aluminum, chromium, nickel, SUS, copper, silver, gold, platinum, and the like. In addition, the metal layer 20 may be formed by various methods such as vacuum deposition, sputtering, paste coating, and the like, and preferably, a sputtering method may be applied.

상기 접착제층(30)은 금속층(20)과 기재층(40)의 접착력을 높이기 위한 것으로, 이는 금속층(20)과 기재층(40)의 견고한 접착력을 제공할 수 있는 것이면 제한되지 않는다. 상기 접착제층(30)은 예를 들어 폴리우레탄, 폴리에스테르, 폴리아마이드, 아크릴 수지 및 에폭시 수지 등으로 이루어진 군중에서 선택된 하나 이상(선택된 1종 또는 2종 이상의 혼합)의 접착성 수지를 포함할 수 있다. 구체적으로, 접착제층(30)은 상기 나열한 접착성 수지 중에서 선택된 하나 또는 2 이상의 수지가 적절한 조성비로 포함된 접착성 수지 조성물을 금속층(20)에 코팅하여 형성할 수 있다. 이때, 코팅 방법은 제한되지 않으며, 예를 들어 그라비아 코팅, 마이크로 그라비아 코팅, 콤마 코팅, 슬롯다이 코팅, 롤 코팅, 리버스 롤 코팅 등의 다양한 코팅 방식이 적용될 수 있다. The adhesive layer 30 is to increase the adhesion between the metal layer 20 and the base layer 40, which is not limited as long as it can provide a firm adhesion between the metal layer 20 and the base layer 40. The adhesive layer 30 may include at least one adhesive resin selected from the group consisting of polyurethane, polyester, polyamide, acrylic resin, epoxy resin, and the like, for example, one or more selected materials. have. Specifically, the adhesive layer 30 may be formed by coating the metal layer 20 with an adhesive resin composition containing one or two or more resins selected from the above-mentioned adhesive resins in an appropriate composition ratio. At this time, the coating method is not limited, and for example, various coating methods such as gravure coating, micro gravure coating, comma coating, slot die coating, roll coating, reverse roll coating and the like may be applied.

또한, 상기 접착제층(30)은 접착성 수지 조성물이 금속층(20)에 코팅되어 형성되되, 접착성 수지 조성물 전체 100중량부에 대하여 상기 나열한 접착성 수지(고형분) 15 ~ 50중량부 및 유기용제 50 ~ 85중량부를 포함하는 접착성 수지 조성물이 코팅되어 형성될 수 있다. 이때, 상기 유기용제는, 특별히 한정하는 것은 아니지만 메틸에틸케톤, 메틸부틸케톤, 톨루엔, 크실렌, 이소프로필알코올 및 에틸아세테이트 등으로 이루어진 군중에서 선택된 하나 이상(선택된 1종 또는 2종 이상의 혼합)을 사용할 수 있다. 또한, 바람직한 구현예에 따라서, 상기 접착제층(30)을 구성하 는 접착성 수지 조성물은, 접착력이 향상되도록 이소시아네이트계 경화제가 선택적으로 더 포함될 수 있다. 상기 이소시아네이트계 경화제는, 예를 들어 헥사메틸렌 디이소아네이트(HMDI), 톨루엔 디이소시아네이트(TDI), 디페닐메탄 디이소시아네이트(MDI) 및 이소프론 디이소시아네이트(IPDI) 등으로 이루어진 군중에서 선택된 하나 이상을 사용할 수 있다. 그리고 이러한 이소시아네이트 경화제는 접착성 수지 조성물 전체 100중량부에 대하여 0 ~ 5중량부의 범위로 포함될 수 있으며, 보다 구체적으로는 0.1 ~ 2중량부로 포함될 수 있다. In addition, the adhesive layer 30 is formed by coating the adhesive resin composition on the metal layer 20, 15 to 50 parts by weight of the adhesive resin (solid content) listed above with respect to 100 parts by weight of the entire adhesive resin composition and the organic solvent The adhesive resin composition including 50 to 85 parts by weight may be formed by coating. At this time, the organic solvent is not particularly limited, but may be one or more selected from the group consisting of methyl ethyl ketone, methyl butyl ketone, toluene, xylene, isopropyl alcohol, ethyl acetate and the like (selected one or two or more selected) Can be. In addition, according to a preferred embodiment, the adhesive resin composition constituting the adhesive layer 30 may optionally further include an isocyanate-based curing agent to improve the adhesion. The isocyanate-based curing agent, for example, at least one selected from the group consisting of hexamethylene diisocyanate (HMDI), toluene diisocyanate (TDI), diphenylmethane diisocyanate (MDI) and isopron diisocyanate (IPDI) Can be used. And such an isocyanate curing agent may be included in the range of 0 to 5 parts by weight with respect to 100 parts by weight of the entire adhesive resin composition, more specifically may be included in 0.1 to 2 parts by weight.

아울러, 상기 접착제층(20)은 핫멜트(hot melt) 방식으로 접착성 수지를 직접 압출 코팅하여 형성될 수 있으며, 이때의 접착성 수지는 폴리에스테르, 폴리아마이드, 폴리우레탄 및 열가소성 폴리우레탄(TPU) 등으로부터 선택된 1종 이상일 수 있다. In addition, the adhesive layer 20 may be formed by direct extrusion coating an adhesive resin by a hot melt method, wherein the adhesive resin is polyester, polyamide, polyurethane, and thermoplastic polyurethane (TPU). It may be at least one selected from the like.

상기 기재층(40)은 본 발명에 따른 장식시트(100)의 지지력 및 기계적 물성 등을 위한 것으로서, 이는 합성수지, 섬유, 종이 등으로부터 선택된 기재시트가 사용될 수 있다. 또한, 상기 기재층(40)은 본 발명에 따른 장식시트(10)를 인서트 성형 공법으로 사출 제품에 적용할 경우 투명수지층(10), 금속층(20) 및 인쇄층(60) 등을 보호해 줄 수 있으면 좋다. 구체적으로, 사출 제품의 사출 시 용용수지의 열과 압력으로부터 투명수지층(10), 금속층(20) 및 인쇄층(60) 등을 보호해 줄 수 있으면 좋다. 상기 기재층(40)은 특별히 한정하는 것은 아니지만 예를 들어 아크릴로부타디엔스티렌(ABS) 수지, 폴리카보네이트(PC), 폴리염화비닐(PVC), 폴리우레탄(PU, TPU 등), 및 폴리에틸렌(PE), 폴리프로필렌(PP) 등의 폴리올레핀 등으로 이 루어진 군중에서 선택된 하나 이상을 포함하는 열가소성 기재시트가 사용될 수 있다. 이러한 기재층(40)의 선정은 예를 들어 인서트 성형 공법으로 적용 시 사출 제품에 사용되는 용융수지의 종류에 따라 결정될 수 있다. 기재층(40)은, 예를 들어 자동차 내ㆍ외장재용 사출 제품의 경우에는 ABS 수지나 폴리올레핀계 시트로부터 선택될 수 있으며, 가전제품의 경우에는 ABS, PC 또는 PC/ABS 시트로부터 선택될 수 있다. The base layer 40 is for the bearing capacity and mechanical properties of the decorative sheet 100 according to the present invention, which may be used a base sheet selected from synthetic resin, fiber, paper and the like. In addition, the base layer 40 protects the transparent resin layer 10, the metal layer 20 and the print layer 60, etc. when the decorative sheet 10 according to the present invention is applied to the injection molded product by the insert molding method. I can give it. Specifically, the transparent resin layer 10, the metal layer 20, the print layer 60, and the like may be protected from the heat and pressure of the molten resin during the injection of the injection molded product. The base layer 40 is not particularly limited, but may be, for example, acrylobutadiene styrene (ABS) resin, polycarbonate (PC), polyvinyl chloride (PVC), polyurethane (PU, TPU, etc.), and polyethylene (PE). ), A thermoplastic base sheet including at least one selected from the group consisting of polyolefins such as polypropylene (PP) and the like can be used. The selection of the base layer 40 may be determined according to the type of molten resin used in the injection molded product, for example, when applied by an insert molding method. The base layer 40 may be selected from, for example, ABS resin or polyolefin-based sheet in the case of injection products for automobile interior and exterior materials, and from ABS, PC or PC / ABS sheet in the case of home appliances. .

또한, 상기 기재층(40)은 건식 전사 방식을 통하여 합판될 수 있다. 구체적으로, 이형필름(200), 투명수지층(10), 금속층(20) 및 접착제층(30)이 순차적으로 적층, 형성된 전사필름을 얻고, 상기 전사필름의 접착제층(30) 상에 건식 전사 방식을 통하여 열가소성 기재시트를 적층, 가압하여 기재층(40)이 합판되도록 할 수 있다. 이때, 건식 전사 공정에서는 열가소성 기재시트와 전사필름이 130 ~ 180℃의 온도범위에서 고무재질의 롤과 스틸재질의 롤 사이에 함께 지나가도록 하여 진행될 수 있다. 그리고 냉각 롤을 지나가도록 한 다음, 상기 전사필름의 이형필름(200)을 박리, 제거하여 헤어라인(H) 무늬가 투명수지층(10)이 전이되도록 한다. In addition, the substrate layer 40 may be plywood through a dry transfer method. Specifically, the release film 200, the transparent resin layer 10, the metal layer 20 and the adhesive layer 30 to obtain a transfer film laminated and formed sequentially, dry transfer on the adhesive layer 30 of the transfer film By laminating and pressing the thermoplastic base sheet through the method, the base layer 40 may be laminated. In this case, in the dry transfer process, the thermoplastic base sheet and the transfer film may be allowed to pass together between the roll of rubber material and the roll of steel material in a temperature range of 130 to 180 ° C. After passing through the cooling roll, the release film 200 of the transfer film is peeled and removed so that the hairline H pattern is transferred to the transparent resin layer 10.

한편, 본 발명에 따른 장식시트(100)는 상기 투명수지층(10)과 금속층(20)의 사이에 프라이머층(50)이 형성될 수 있는데, 상기 프라이머층(50)은 투명수지층(10)과 금속층(20)이 낮은 접착 강도를 가질 때, 양자 간의 접착력 증진을 위해 선택적으로 형성될 수 있다. 예를 들어, 상기 프라이머층(50)은 투명수지층(10)과 금속층(20)이 통상적인 테이프 박리 테스트에서 박리가 일어날 때 적용될 수 있다. 아울러, 상기 프라이머층(50)을 구성하는 수지 조성물은 금속층(20)의 종류 및 코 팅 방식에 따라 다양하게 선택될 수 있다. 상기 프라이머층(50)은, 예를 들어 폴리우레탄, 폴리에스테르 및 아크릴 수지 등으로 이루어진 군중에서 선택된 하나 이상의 수지를 포함하는 수지 조성물이 코팅되어 형성될 수 있으며, 상기 수지 조성물에는 경화제 등을 더 포함할 수 있다. On the other hand, the decorative sheet 100 according to the present invention may be a primer layer 50 is formed between the transparent resin layer 10 and the metal layer 20, the primer layer 50 is a transparent resin layer 10 ) And the metal layer 20 may be selectively formed to enhance adhesion between the two and the metal layer 20. For example, the primer layer 50 may be applied when the transparent resin layer 10 and the metal layer 20 are peeled off in a conventional tape peeling test. In addition, the resin composition constituting the primer layer 50 may be variously selected according to the type and coating method of the metal layer 20. The primer layer 50 may be formed by coating a resin composition including at least one resin selected from the group consisting of polyurethane, polyester, and acrylic resin, for example, and the resin composition further includes a curing agent and the like. can do.

또한, 본 발명에 따른 장식시트(100)는 상기 접착층(30)과 기재층(40)의 사이에 형성된 인쇄층(60)을 더 포함할 수 있는데, 이는 인쇄무늬를 통한 장식효과를 부여하기 위해 적용되거나, 금속층(20)에 의해 구현되는 장식시트(100)의 색상을 변경하고자 할 때 적용될 수 있다. 이러한 인쇄층(60)은 바인더와 잉크를 포함하는 잉크 조성물이 인쇄되어 형성될 수 있으며, 상기 바인더는 아크릴계 수지 등으로부터 선택될 수 있다. In addition, the decorative sheet 100 according to the present invention may further include a print layer 60 formed between the adhesive layer 30 and the base layer 40, which is to give a decorative effect through the printed pattern It may be applied or when the color of the decorative sheet 100 implemented by the metal layer 20 is to be changed. The print layer 60 may be formed by printing an ink composition including a binder and ink, and the binder may be selected from acrylic resin and the like.

이상에서 설명한 본 발명에 따르면, 우수한 치수안정성 및 성형성 등을 가지면서 헤어라인(H) 무늬가 뚜렷하여 미려한 헤어라인 금속효과(금속질감)를 갖는다. 종래와 같이 투명필름에 헤어라인을 직접 구현하는 경우, 치수안정성을 고려하게 되면 헤어라인 무늬가 뚜렷하지 않고 성형성이 떨어져 사출 제품에 적용이 어렵거나, 성형성을 고려하게 되면 치수안정성이 떨어져 제조공정에 여러 제약(한계)이 따른다. 그러나 투명필름에 헤어라인을 직접 구현하지 않고, 본 발명에 따라서 이형필름(200)에 헤어라인(H)을 형성한 다음, 이를 투명수지층(10)에 전이시키는 캐스팅 방법으로 구현하는 경우, 투명수지층(10)의 재질이 제한되지 않아 우수한 치수안정성 및 성형성을 가지는 재질의 사용이 가능하다. 이에 따라, 본 발명에 따르면 우수한 치수안정성 등을 가져 제조공정에 제약이 따르지 않으면서, 성형성이 우수하여 사출 제품에 적용이 용이하다. 그리고 헤어라인(H) 무늬가 뚜렷하게 구현되어 미려한 장식효과(헤어라인 금속효과)를 갖는다. According to the present invention described above, the hairline (H) pattern is distinct and has a beautiful hairline metal effect (metal texture) while having excellent dimensional stability and formability. When the hairline is directly implemented on the transparent film as in the prior art, when the dimensional stability is considered, the hairline pattern is not clear and the moldability is difficult to be applied to the injection product, or when the moldability is considered, the dimensional stability is not manufactured. There are several restrictions on the process. However, if the hairline (H) is formed on the release film 200 according to the present invention without directly implementing the hairline on the transparent film, and then implemented by a casting method for transferring it to the transparent resin layer 10, the transparent Since the material of the resin layer 10 is not limited, it is possible to use a material having excellent dimensional stability and formability. Accordingly, according to the present invention has excellent dimensional stability and the like without being restricted in the manufacturing process, it is excellent in moldability and easy to apply to injection products. And the hairline (H) pattern is clearly implemented to have a beautiful decorative effect (hairline metal effect).

한편, 본 발명에 따른 장식시트(100)는 금속 제품이나 플라스틱 제품, 예를 들어 생활 가전제품, 자동차 내ㆍ외장재, 가구 및 건축물의 내ㆍ외장재 등의 표면 마감재로 사용될 수 있으며, 그 사용 제품은 제한되지 않는다. On the other hand, the decorative sheet 100 according to the present invention can be used as a surface finish of metal products or plastic products, such as household appliances, interior and exterior materials of automobiles, interior and exterior materials of furniture and buildings, the product used It is not limited.

또한, 본 발명에 따른 장식시트(100)는 자동차 내ㆍ외장재, 가구 및 건축물의 내ㆍ외장재 등의 제품에 적용 시, 예를 들어 접착제(점착제)를 통해 부착되는 방식으로 적용될 수 있다. 이때, 본 발명에 따른 장식시트(100)는, 상기 기재층(40)의 하부에 형성된 점착제층(도시하지 않음)과, 상기 점착제층의 하부에 형성된 이형부재(도시하지 않음)가 더 적층된 구조를 가질 수 있다. 상기 이형부재는 제품에 적용된 후 탈리, 제거되는 것으로서, 이는 이형성의 플라스틱 필름이나 종이 등으로부터 선택될 수 있다. In addition, the decorative sheet 100 according to the present invention may be applied in a manner that is attached through, for example, an adhesive (adhesive) when applied to products such as interior and exterior materials of automobiles, interior materials, furniture and buildings. At this time, the decorative sheet 100 according to the present invention, the pressure-sensitive adhesive layer (not shown) formed in the lower portion of the base layer 40 and the release member (not shown) formed in the lower portion of the pressure-sensitive adhesive layer is further laminated It may have a structure. The release member is to be removed from the product after being applied to the product, which may be selected from a plastic film or paper of the release property.

아울러, 본 발명에 따른 장식시트(100)는 플라스틱 사출 제품의 경우에는 인서트 성형 공법을 통해 적용되는 것이 좋다. 구체적으로, 플라스틱 사출 제품에 적용 시에는 본 발명에 따른 장식시트(100)를 사출 제품의 크기 및 모양에 맞도록 재단한 후, 사출기 금형 안에 본 발명에 따른 장식시트(100)를 투입한 다음, 장식시트(100)의 배면에 사출 제품용 용융 수지를 사출, 고화시키는 방법으로 적용되는 것이 좋다. In addition, the decorative sheet 100 according to the present invention is preferably applied through the insert molding method in the case of plastic injection products. Specifically, when applied to a plastic injection product, after cutting the decorative sheet 100 according to the present invention to fit the size and shape of the injection product, and then put the decorative sheet 100 according to the present invention in the injection molding machine mold, It is good to apply by the method of injecting, solidifying the molten resin for injection products on the back of the decorative sheet 100.

도 1은 본 발명의 제1실시예에 따른 장식시트 및 이의 제조과정을 보인 단면도이다. 1 is a cross-sectional view showing a decorative sheet and a manufacturing process thereof according to a first embodiment of the present invention.

도 2는 본 발명의 제2실시예에 따른 장식시트를 보인 단면도이다. 2 is a cross-sectional view showing a decorative sheet according to a second embodiment of the present invention.

< 도면의 주요 부분에 대한 부호의 설명 > <Description of Symbols for Main Parts of Drawings>

10 : 투명수지층 20 : 금속층10: transparent resin layer 20: metal layer

30 : 접착제층 40 : 기재층30: adhesive layer 40: base material layer

50 : 프라이머층 60 : 인쇄층50: primer layer 60: printing layer

100 : 장식시트 200 : 이형필름100: decorative sheet 200: release film

H : 헤어라인 H: Hairline

Claims (15)

헤어라인이 형성된 투명수지층; A transparent resin layer on which a hairline is formed; 상기 투명수지층의 헤어라인이 형성된 면의 반대쪽 면에 형성된 금속층; A metal layer formed on a surface opposite to a surface on which the hairline of the transparent resin layer is formed; 상기 금속층의 하부에 형성된 접착제층; 및 An adhesive layer formed under the metal layer; And 상기 접착제층의 하부에 형성된 기재층을 포함하고, It includes a base layer formed under the adhesive layer, 상기 투명수지층에 형성된 헤어라인은, 이형필름에 형성된 헤어라인이 전이되어 형성된 것을 특징으로 하는 장식시트. Hairline formed on the transparent resin layer, the decorative sheet, characterized in that the hairline formed on the release film is transferred. 제1항에 있어서, The method of claim 1, 투명수지층과 금속층의 사이에 형성된 프라이머층을 더 포함하는 것을 특징으로 하는 장식시트. The decorative sheet further comprises a primer layer formed between the transparent resin layer and the metal layer. 제1항에 있어서, The method of claim 1, 접착제층과 기재층의 사이에 형성된 인쇄층을 더 포함하는 것을 특징으로 하는 장식시트. A decorative sheet further comprising a printing layer formed between the adhesive layer and the base layer. 제1항 내지 제3항 중 어느 하나의 항에 있어서, The method according to any one of claims 1 to 3, 이형필름은 폴리에스테르 필름 또는 폴리에틸렌테레프탈레이트 필름인 것을 특징으로 하는 장식시트. Release film is a decorative sheet, characterized in that the polyester film or polyethylene terephthalate film. 제1항 내지 제3항 중 어느 하나의 항에 있어서, The method according to any one of claims 1 to 3, 투명수지층은 폴리메틸메타크릴레이트, 폴리에틸메타크릴레이트, 폴리부틸메타크릴레이트, 폴리우레탄 및 폴리에스테르로 이루어진 군중에서 선택된 하나 이상을 포함하는 것을 특징으로 하는 장식시트. The transparent resin layer is a decorative sheet, characterized in that it comprises at least one selected from the group consisting of polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, polyurethane and polyester. 제1항 내지 제3항 중 어느 하나의 항에 있어서, The method according to any one of claims 1 to 3, 접착제층은 폴리우레탄, 폴리에스테르, 폴리아마이드, 아크릴 수지 및 에폭시 수지로 이루어진 군중에서 선택된 하나 이상을 포함하는 것을 특징으로 하는 장식시트. The adhesive sheet is a decorative sheet, characterized in that it comprises at least one selected from the group consisting of polyurethane, polyester, polyamide, acrylic resin and epoxy resin. 제1항 내지 제3항 중 어느 하나의 항에 있어서, The method according to any one of claims 1 to 3, 기재층은 아크릴로부타디엔스티렌 수지, 폴리카보네이트, 폴리염화비닐, 폴리우레탄 및 폴리올레핀계로 이루어진 군중에서 선택된 하나 이상을 포함하는 것을 특징으로 하는 장식시트. The base layer is a decorative sheet, characterized in that it comprises at least one selected from the group consisting of acrylobutadiene styrene resin, polycarbonate, polyvinyl chloride, polyurethane and polyolefin-based. 이형필름에 헤어라인을 형성하는 단계; Forming a hairline on the release film; 상기 이형필름의 헤어라인이 형성된 면에 투명수지층을 형성하는 단계; Forming a transparent resin layer on a surface on which the hairline of the release film is formed; 상기 투명수지층 상에 금속층을 형성하는 단계; Forming a metal layer on the transparent resin layer; 상기 금속층 상에 접착제층을 형성하는 단계; Forming an adhesive layer on the metal layer; 상기 접착제층 상에 기재층을 형성하는 단계; 및Forming a base layer on the adhesive layer; And 상기 이형필름을 제거하여 투명수지층의 표면에 헤어라인이 전이되게 하는 단계를 포함하는 것을 특징으로 하는 장식시트의 제조방법. Removing the release film, the method of manufacturing a decorative sheet comprising the step of transferring the hairline on the surface of the transparent resin layer. 제8항에 있어서, The method of claim 8, 투명수지층과 금속층의 사이에 프라이머층을 형성하는 단계를 더 포함하는 것을 특징으로 하는 장식시트의 제조방법. The method of manufacturing a decorative sheet, characterized in that it further comprises the step of forming a primer layer between the transparent resin layer and the metal layer. 제8항에 있어서, The method of claim 8, 접착제층과 기재층의 사이에 인쇄층을 형성하는 단계를 더 포함하는 것을 특징으로 하는 장식시트의 제조방법. The method of manufacturing a decorative sheet, characterized in that it further comprises the step of forming a printing layer between the adhesive layer and the base layer. 제8항 내지 제10항 중 어느 하나의 항에 있어서, The method according to any one of claims 8 to 10, 이형필름은 폴리에스테르 필름 또는 폴리에틸렌테레프탈레이트 필름인 것을 특징으로 하는 장식시트의 제조방법. Release film is a method for producing a decorative sheet, characterized in that the polyester film or polyethylene terephthalate film. 제8항 내지 제10항 중 어느 하나의 항에 있어서, The method according to any one of claims 8 to 10, 투명수지층은 폴리메틸메타크릴레이트, 폴리에틸메타크릴레이트, 폴리부틸메타크릴레이트, 폴리우레탄 및 폴리에스테르로 이루어진 군중에서 선택된 하나 이상을 포함하는 수지 조성물을 이형필름에 코팅하여 형성하는 것을 특징으로 하는 장식시트의 제조방법. The transparent resin layer is formed by coating on a release film a resin composition comprising at least one selected from the group consisting of polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, polyurethane and polyester Method of manufacturing a decorative sheet. 제12항에 있어서, The method of claim 12, 투명수지층을 형성하는 수지 조성물은 이소시아네이트계 경화제를 더 포함하는 것을 특징으로 하는 장식시트의 제조방법. The resin composition for forming the transparent resin layer further comprises an isocyanate curing agent. 제8항 내지 제10항 중 어느 하나의 항에 있어서, The method according to any one of claims 8 to 10, 접착제층은 폴리우레탄, 폴리에스테르, 폴리아마이드, 아크릴 수지 및 에폭시 수지로 이루어진 군중에서 선택된 하나 이상을 포함하는 수지 조성물을 금속층에 코팅하여 형성하는 것을 특징으로 하는 장식시트의 제조방법. The adhesive layer is a method for manufacturing a decorative sheet, characterized in that the coating is formed by coating a metal layer with a resin composition comprising at least one selected from the group consisting of polyurethane, polyester, polyamide, acrylic resin and epoxy resin. 제14항에 있어서, The method of claim 14, 접착제층을 형성하는 수지 조성물은 이소시아네이트계 경화제를 더 포함하는 것을 특징으로 하는 장식시트의 제조방법. The resin composition forming the adhesive layer further comprises an isocyanate curing agent.
KR1020090125393A 2009-12-16 2009-12-16 Hairline decoration sheet having excellent metallic effect KR101281430B1 (en)