KR20100118689A

KR20100118689A - Construction materials

Info

Publication number: KR20100118689A
Application number: KR1020090037503A
Authority: KR
Inventors: 이시다히로아키
Original assignee: 이시다히로아키; 가부시키가이샤 젠
Priority date: 2009-04-29
Filing date: 2009-04-29
Publication date: 2010-11-08

Abstract

PURPOSE: A construction material is provided to prevent the material from becoming twisted or bent by preventing dew condensation and to absorb humidity using carbon based materials. CONSTITUTION: A construction material is composed as follows. A rectangular or square frame body(3), surface and back plates(7a,7b), polypropylene resin based nonwoven fabric with air permeability are formed. Multiple small holes(6) are formed on the surface and back plates. Multiple partition parts(5) are formed by dividing a space formed by the frame body and the surface and back plates.

Description

Building materials {CONSTRUCTION MATERIALS}

본 발명은 건물의 옥내에 사용하는 내장 구획재나, 마루·천장재로서 이용하는 건축 판재에 관한 것으로, 특히 단열성이 요구되는 부분, 혹은 습기·악취가 발생하는 장소에 사용하기에 적합한 습기 방지ㆍ탈취 및 단열 기능을 갖춘 건축재에 관한 것이다.BACKGROUND OF THE INVENTION Field of the Invention [0001] The present invention relates to interior partitions used for indoors of buildings and building plates used as floors and ceilings. In particular, the present invention relates to moisture prevention, deodorization, and heat insulation suitable for use in areas where thermal insulation is required or where moisture and odor are generated. It is about building materials with function.

종래, 한랭지 등에 있는 건물의 옥내에 설치하는 구획재나 도어 등에 사용하는 건축재는, 직사각형 등의 프레임체 내에 내부 보강재로서 허니콤 코어를 감합시키고, 상기 프레임체와 허니콤 코어의 표, 이면의 적어도 한 쪽을 알루미늄박으로 덮고, 프레임체의 표, 이면에 표면, 이면판의 외주부를 프레임체에 직접 또는 상기 알루미늄 박을 개재시켜 접착한 단열성 건축재가 이용되고 있다.Conventionally, building materials used for partitions, doors, and the like installed indoors of buildings in cold districts or the like fit a honeycomb core into an internal reinforcement in a frame such as a rectangle, and at least one of the table and the back of the frame and the honeycomb core. The heat-insulating building material which covered the side with aluminum foil and adhere | attached the outer periphery of the surface and a back plate on the table | surface and the back surface of a frame body directly to a frame body through the said aluminum foil is used.

그러나 건물의 실내가 따뜻하고 실외가 추운 경우나, 실내가 춥고 실외가 따뜻한 경우에, 실내외의 온도차에 의해 단열성 건축재의 알루미늄박에 결로가 생기고, 프레임체에 뒤틀림이나 휨이 발생하고, 프레임체와 허니콤 코어 사이에 간극이 생기거나, 프레임체에서 표면, 이면판의 외주부가 벗겨지거나, 또한 실내의 복수의 구획재 사이나 구획재와 도어 사이에 간극이 생기는 등, 충분히 단열할 수 없다고 하는 문제점이 있었다. 또, 주방, 욕실에 사용되는 건축재, 혹은 현관에 구비된 신발장 등에 사용되는 건축재에 있어서는 건축재 자체가 습기 방지·탈취 및 단열 기능을 갖추지 않기 때문에 습기 혹은 악취 등이 대기 중에 충만하여 불쾌감을 주고 있는 현상황이다. However, if the interior of the building is warm and the outside is cold, or the interior is cold and the outside is warm, condensation will occur on the aluminum foil of the insulating building material due to the temperature difference between the inside and the outside, and the frame and the warping will occur. There is a problem that the insulation cannot be sufficiently insulated, such as a gap between the comb cores, the outer peripheral part of the surface and the back plate being peeled off from the frame body, and a gap between a plurality of compartments in the room or between the compartments and the door. there was. In addition, in building materials used in kitchens, bathrooms, or shoeboxes installed in the entrance hall, the building materials themselves do not have moisture prevention, deodorization, and heat insulation functions. to be.

본 발명은 상기와 같은 종래의 문제를 해결하기 위해 이루어진 것으로, 직사각형 또는 정사각형의 프레임체와, 이 양면에 각각 고착된 표면, 이면판에 의해 형성되는 공간부 내에 탄소계 물질을 충전함으로써 습기 방지 기능과 탈취 및 해충 방지 기능을 발휘시킴과 함께, 상기 공간부 내의 탄소계 물질을 복수로 분리할 수 있도록 한 건축재를 제공하는 것을 목적으로 하고 있다. SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned conventional problems. The present invention provides a moisture prevention function by filling a carbon-based material into a rectangular or square frame, a surface fixed to each of the two surfaces, and a space formed by a back plate. An object of the present invention is to provide a building material capable of exerting excessive deodorization and pest control and separating a plurality of carbonaceous substances in the space portion.

본 발명에 관련된 건축재는, 세로재와 가로재를 조합하여 이루어지는 직사각형 또는 정사각형의 프레임체와, 상기 프레임체의 양면에 고착되는 표면, 이면판과, 그 표면, 이면판의 내면측에 통기성을 가지는 폴리프로필렌 수지계의 부직포를 개재시킴과 함께, 상기 표면, 이면판에 각각 관통하는 복수의 작은 구멍을 형성하고, 상기 프레임체와 상기 표면, 이면판에 의해 형성되는 공간 내를 상기 프레임체의 가로재 사이에 배치한 적어도 하나의 세로 살과 상기 프레임체의 세로재 사이에 그 세로재의 길이 방향으로 등간격으로 배치한 복수의 가로 살에 의해 가로세로 복수로 구획하여 복수의 구획부를 형성함과 함께, 통기성을 가지는 폴리프로필렌 수지계의주머니형 부직포 내에 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말로 이루어지는 탄소계 물질을 충전하여 상기 각 구획부의 공간 내에 장전한 것을 특징으로 한다.The building material which concerns on this invention has a rectangular or square frame body which combines a longitudinal material and a horizontal material, and has the air permeability to the surface fixed to both surfaces of the said frame body, a back plate, the surface, and the inner surface side of a back plate. While interposing a nonwoven fabric of polypropylene resin, a plurality of small holes penetrating the surface and the back plate are formed, respectively, and the horizontal member of the frame is formed in the space formed by the frame, the surface and the back plate. A plurality of partitions are formed by dividing a plurality of partitions vertically and horizontally by a plurality of horizontal ribs arranged at equal intervals in the longitudinal direction of the vertical member between at least one longitudinal rib disposed between the vertical member of the frame and the plurality of partitions. Carbon-based small pieces or powders such as charcoal and activated carbon in a polypropylene resin-pocketed nonwoven fabric That the filled quality loaded in each of the compartment space features.

본 발명에 따른 또 다른 건축재는, 상기 건축재에 있어서, 상기 표면, 이면판 중 한 쪽 또는 양쪽 모두를 구멍 뚫린 화장판으로 한 것을 특징으로 한다.Another building material which concerns on this invention WHEREIN: The building material WHEREIN: It is characterized by the one or both of the said surface, a back plate made into the decorative board which perforated.

본 발명에 의한 건축재는, 세로재와 가로재를 조합하여 이루어지는 직사각형 또는 정사각형의 프레임체와, 상기 프레임체의 양면에 고착되는 표면, 이면판과, 그 표면, 이면판의 내면측에 통기성을 가지는 폴리프로필렌 수지계의 부직포를 개재시킴과 함께, 상기 표면, 이면판에 각각 관통하는 복수의 작은 구멍을 형성하고, 상기 프레임체와 상기 표면, 이면판에 의해 형성되는 공간 내를 상기 프레임체의 가로재 사이에 배치한 적어도 하나의 세로 살과 상기 프레임체의 세로재 사이에 그 세로재의 길이 방향으로 등간격으로 배치한 복수의 가로 살에 의해 가로세로 복수로 구획하여 복수의 구획부를 형성함과 함께, 통기성을 가지는 폴리프로필렌 수지계의 주머니형 부직포 내에 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말로 이루 어지는 탄소계 물질을 충전하여 상기 각 구획부의 공간 내에 장전한 구성으로 하였기 때문에, 건물 내의 방 구획재로서 사용하는 경우에는, 단열성 건축재로서의 기능을 가지며, 한랭지 등에서 동계에 건물의 다른 방이나 건물 밖이 저온이 되어도 방 안의 온도 저하를 줄일 수 있다.The building material according to the present invention has a rectangular or square frame body formed by combining a longitudinal material and a cross member, and a surface fixed to both surfaces of the frame body, a back plate, and a surface thereof, and an inner surface side of the back plate. While interposing a nonwoven fabric of polypropylene resin, a plurality of small holes penetrating the surface and the back plate are formed, respectively, and the horizontal member of the frame is formed in the space formed by the frame, the surface and the back plate. A plurality of partitions are formed by dividing a plurality of partitions vertically and horizontally by a plurality of horizontal ribs arranged at equal intervals in the longitudinal direction of the vertical member between at least one longitudinal rib disposed between the vertical member of the frame and the plurality of partitions. Carbon-based water composed of carbon-based small pieces or powders such as charcoal and activated carbon in a polypropylene resin-bag nonwoven fabric having breathability In order to use as a room partition material in a building, it has a function as a heat insulating building material, and even if it is cold in another room or outside of a building in the cold season in winter, etc. The temperature drop in the room can be reduced.

또, 종래와 같이 건축재의 내부 공간에 알루미늄박을 사용하고 있지 않으므로, 구획재로서 형성한 건축재의 내면에 결로가 발생하지 않고, 건축재의 프레임체가 뒤틀리거나 휘는 등 변형하는 것을 방지할 수 있다. Moreover, since aluminum foil is not used for the interior space of building materials as in the related art, condensation does not occur on the inner surface of the building materials formed as partitions, and the frame body of the building materials can be prevented from being deformed or warped.

그리고, 본 발명의 건축재를, 습기가 많이 발생하는 주방·욕실·붙박이장에, 또한 악취가 발생하는 신발장이나 화장실에 건축재로서 사용한 경우에는, 건축재의 내부 공간부에 충전한 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말 등의 탄소계 물질에 의해 흡습·탈취할 수 있어, 쾌적한 방을 제공할 수 있다. When the building material of the present invention is used as a building material in kitchens, bathrooms, and built-in cabinets where moisture is generated, as well as in shoeboxes and toilets where odors are generated, carbon-based carbon, such as charcoal and activated carbon, charged in the interior space of the building materials It can absorb and deodorize by carbonaceous substance, such as a small flake or powder, and can provide a comfortable room.

또, 청구항 1의 발명에 의하면, 프레임체와 표면, 이면판에 의해 형성되는 공간부 내가 세로 살과 가로 살로 구획되는 것에 의해 공간부 내에 충전된 통기성을 가지는 주머니형의 부직포 내에 장전된 탄소계 물질을 확실하게 분리하여 유지함과함께, 미세한 탄소계 분말이 상기 표면, 이면판에 형성한 복수의 작은 구멍으로부터 외방으로 비산하거나 넘쳐 나오는 문제를 상기 폴리프로필렌 수지계의 부직포 및 주머니형 부직포에 의해 완전히 방지할 수 있다. 또, 건축재를 도어 등에 사용하는 경우, 자물쇠를 부착하는 부분의 구획부로부터 탄소계 물질의 충전을 제외하는 일도 용이하게 행할 수 있다. According to the invention of claim 1, a carbon-based material loaded in a bag-shaped nonwoven fabric having air permeability filled in the space portion by partitioning the space portion formed by the frame body, the surface, and the back plate into vertical and horizontal flesh portions. In addition, the polypropylene resin-based nonwoven fabric and the bag-shaped nonwoven fabric can be completely prevented from being scattered or overflowed from the plurality of small holes formed on the surface and the back plate. Can be. In addition, when building materials are used in doors and the like, it is also possible to easily remove the filling of the carbonaceous material from the partition portion of the portion to which the lock is attached.

또, 탄소계 물질을 장전하는 통기성을 가지는 주머니형 부직포 및 표면, 이 면판의 내면측에 배치하는 통기성을 가지는 부직포는, 각각 폴리프로필렌 수지계라서 소각에 있어서도 탄산 가스와 물로 분해되므로, 산업 폐기물이 되어도 유독 가스를 발생시키는 일이 없다. 그리고, 상기 구획부 내에 상기 탄소계 물질의 미분말을 작업성 좋게 충전할 수 있다. In addition, the bag-shaped nonwoven fabric having air permeability for loading carbon-based materials and the surface, and the nonwoven fabric having air permeability disposed on the inner surface side of the face plate are each polypropylene resins, so they are decomposed into carbon dioxide and water even in incineration, and thus may be industrial wastes. No toxic gas is generated. In addition, the fine portion of the carbonaceous material may be filled in the partition with good workability.

이하, 본 발명의 실시 형태에 대해, 도면을 참조하여 설명한다. EMBODIMENT OF THE INVENTION Hereinafter, embodiment of this invention is described with reference to drawings.

도 1에 나타내는 제1 실시 형태의 건축재 1은, 좁은 폭의 목재, 합판, 집합재 혹은 플라스틱 등, 바람직하게는 좁은 폭의 목재를 세로재 2a, 2b, 가로재 2c, 2d로 재단하고, 이들을 서로 조합하여 상하 방향으로 긴 직사각형의 프레임체 3을 형성하고, 프레임체 3 내에 프레임체 3의 두께와 동일한 두께를 가지는 상하 3개의 목제의 가로 살 4를 등간격, 예를 들면 30mm~100mm, 바람직하게는 50mm의 등간격으로 배치하고, 가로 살 4의 왼쪽, 오른쪽 바깥단부 4a, 4b를 프레임체 3의 세로재 2a, 2b에 각각 고정하고 있다. 그리고 상기 프레임체 3의 표, 이면 측에는, 표, 이면의 전체면을 덮는 형상으로 형성되고, 복수의 관통공 6을 가지는 구멍 뚫린 표면, 이면판 7a, 7b가 배치되며, 상기 구멍 뚫린 표면, 이면판 7a, 7b의 내면 외주부가 프레임체 3의 세로, 가로재 2a~2d의 표, 이면측에 접착되게 되어 있다. The building material 1 of 1st Embodiment shown in FIG. 1 cuts narrow timber, such as narrow timber, a plywood, an assembly material, or plastics, Preferably it is a longitudinal material 2a, 2b, a horizontal material 2c, 2d, In combination with each other to form a long rectangular frame 3 in the up and down direction, and the upper and lower three wooden ribs 4 having the same thickness as the thickness of the frame 3 in the frame 3, such as 30mm ~ 100mm, preferably It is arrange | positioned at equal intervals of 50 mm, and the left and right outer ends 4a, 4b of the rib 4 are fixed to the vertical members 2a, 2b of the frame 3, respectively. And the table | surface and back surface side of the said frame body 3 are formed in the shape which covers the whole surface of a table | surface and a back surface, and the perforated surface which has a some through hole 6, the back plate 7a, 7b is arrange | positioned, The perforated surface, the back surface The inner periphery of the inner surface of the plates 7a and 7b is adhered to the length of the frame 3, the table of the horizontal members 2a to 2d, and the back surface side.

그리고 상기 프레임체 3과 가로 살 4로 둘러싸인 구획부 5의 공간부 내에는 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말 등의 탄소계 물질 8이 충전된 것이다. The carbonaceous material 8 such as carbon-based small pieces or powders such as charcoal, activated carbon, or the like is filled in the space portion of the partition 5 surrounded by the frame 3 and the lateral flesh 4.

또한, 이 실시 형태에서는 사용하고 있지 않지만, 상기 탄소계 물질 8이 미 세한 미분말 형태이며, 상기 표면, 이면판 7a, 7b에 형성된 복수의 관통공 6으로부터 외부로 넘쳐 나오는 경우에는 상기 표면, 이면판 7a, 7b 내면측에 파선으로 나타내는 각각 통기성을 가지는 폴리프로필렌계 등의 부직포 50a, 50b를 형성하도록 하고, 상기 부직포 50a, 50b를 일측에 개구가 있는 주머니형으로 해서 주머니형의 부직포 내에 상기 미분말 형태의 탄소계 물질 8을 장전하여 이것을 상기 공간부에 충전하도록 해도 되며, 상기 표면, 이면판 7a, 7b에 형성된 복수의 관통공 6으로부터 상기 미분말 형태의 탄소계 물질이 외부로 넘쳐 나오는 것을 방지할 수 있다. In addition, although not used in this embodiment, when the said carbon-based substance 8 is a fine fine powder form and overflows to the outside from the some through-hole 6 formed in the said surface, backplate 7a, 7b, the said surface, a backplate The fine powder form is formed in the nonwoven fabric of the bag-shaped nonwoven fabric by forming nonwoven fabric 50a, 50b, such as a polypropylene type | mold which has air permeability, respectively shown by a broken line on the inner surface side of 7a, 7b, and making the said nonwoven fabric 50a, 50b the bag type with an opening in one side. The carbonaceous material 8 may be loaded and filled in the space part, and the fine powder-like carbonaceous material may be prevented from overflowing to the outside from the plurality of through holes 6 formed in the surface and back plates 7a and 7b. have.

또, 이 실시 형태에 있어서의 표면, 이면판 7a, 7b로는 각각 복수의 관통공 6을 형성한 구멍 뚫린 표면, 이면판 7a, 7b로 했지만, 사용 목적에 따라 표면, 이면판 7a, 7b 중 어느 한 쪽만을 구멍 뚫린 면판으로 하고, 다른 쪽의 면판에는 관통공이 없는 것을 사용하도록 해도 된다. Moreover, although the surface in this embodiment and the back plate 7a, 7b were set as the perforated surface which formed the some through-hole 6, and the back plate 7a, 7b, respectively, either of the surface, back plate 7a, 7b according to a use purpose. It is also possible to use only one face plate perforated, and use the other face plate without a through hole.

상기 목탄, 활성탄 등의 탄소계의 작은 조각 또는 분말 등의 탄소계 물질 8을 프레임체 3의 구획부 5 내에 충전하기 위해서는, 먼저 프레임체 3의 이면에 구멍 뚫린 이면판 7b를 접착하고, 필요에 따라 부직포를 내재시켜 상기 탄소계 물질 8을 충전하고, 필요에 따라 부직포를 개재시켜 구멍 뚫린 표면판 7a를 프레임체 3의 표면에 접착하여 건축재 1을 형성한다. In order to fill the partition 5 of the frame 3 with a carbon-based material 8 such as carbon-based small pieces or powder such as charcoal and activated carbon, the back plate 7b which is perforated is bonded to the rear surface of the frame 3, As a result, a nonwoven fabric is embedded to fill the carbonaceous material 8, and if necessary, the perforated surface plate 7a is bonded to the surface of the frame 3 through the nonwoven fabric to form the building material 1.

전술한 바와 같이 구성한 제1 실시 형태의 건축재 1은, 프레임체 3의 두께를 20mm로 하고, 구멍 뚫린 표면, 이면판 7a, 7b의 두께를 각각 2.5mm로 하고, 또한 길이는 180mm인 구멍 뚫린 화장판을 사용하고 있다. The building material 1 of 1st Embodiment comprised as mentioned above has the thickness of the frame 3 to 20 mm, the thickness of the perforated surface, the backplates 7a, 7b to 2.5 mm, respectively, and the length of the perforated form which is 180 mm. I'm using a blanket.

도 2에 나타내는 제2 실시 형태의 건축재 10은, 전술한 제1 실시 형태의 것 과 거의 동일한 프레임체 3 및 구멍 뚫린 표면, 이면판 7a, 7b를 가지는 것이며, 동일 부분에는 동일한 부호를 붙이고 그 설명은 생략하지만, 프레임체 3의 공간부 내에는 가로 살이 생략된 것이다. The building material 10 of 2nd Embodiment shown in FIG. 2 has the frame body 3 and the perforated surface and back plate 7a, 7b which are substantially the same as the thing of 1st Embodiment mentioned above, The same code | symbol is attached | subjected, and the description is carried out. Is omitted, but the abscissa is omitted in the space portion of the frame 3.

그리고 상기 공간부 내에는, 상기 가로 살 대신에 종이로 만든 허니콤 코어 11의 모든 구멍부 11a에, 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말 등의 탄소계 물질 8을 필요에 따라 상기 실시 형태와 마찬가지로 부직포를 개재시켜 충전하고, 상기 탄소계 물질 8을 유지한 허니콤 코어 11을 상기 공간부 내에 충전하도록 한 것이다. In the space portion, the carbonaceous material 8 such as carbon-based small pieces or powders such as charcoal and activated carbon, or the like may be applied to all the hole portions 11a of the honeycomb core 11 made of paper instead of the ribs. In the same manner as in the above, the nonwoven fabric is filled and the honeycomb core 11 holding the carbonaceous material 8 is filled in the space part.

도 3에 나타내는 제3 실시 형태의 건축재 20은, 전술한 제1 실시 형태의 것보다 가로로 길게 형성한 직사각형의 프레임체 3 내에, 프레임체 3의 두께와 동일한 두께를 가지는 상하 3개의 목제의 가로 살 4를 등간격, 예를 들면 30mm~100mm, 바람직하게는 50mm의 등간격으로 배치하고, 그리고 프레임체 3의 가로재 2c, 2d 사이에 세로 살 21을 가로지르는 상태로 배치한다. 이것에 의해 가로 살 4의 왼쪽, 오른쪽 바깥단부 4a, 4b는 세로 살 21과 이것에 대응하는 프레임체 3의 세로재 2a 및 2b 세로 살 21과의 사이에 가로지르는 상태로 고정되어 있다. 또, 프레임체 3의 표, 이면에는 그 전체면을 덮는 복수의 관통공 6을 가지는 구멍 뚫린 표면, 이면판 7a, 7b가 배치되고, 상기 구멍 뚫린 표면, 이면판 7a, 7b의 내면 외주부는 프레임체 3의 표, 이면에 접착되어 있다. The building material 20 of 3rd Embodiment shown in FIG. 3 has three horizontal wood top and bottom which have the same thickness as the thickness of the frame 3 in the rectangular frame 3 formed laterally longer than the thing of 1st Embodiment mentioned above. The ribs 4 are arranged at equal intervals, for example, 30 mm to 100 mm, preferably 50 mm, and placed across the longitudinal ribs 21 between the cross members 2c and 2d of the frame 3. As a result, the left and right outer ends 4a and 4b of the rib 4 are fixed in a state intersecting between the rib 21 and the vertical members 2a and 2b of the frame 3 corresponding thereto. Moreover, the perforated surface which has a plurality of through-holes 6 and back plates 7a and 7b are arrange | positioned at the table | surface and the back surface of the frame body 3, The inner peripheral part of the perforated surface and the backplate 7a, 7b is a frame. It is adhere | attached on the table and back surface of the sieve 3.

이와 같이 프레임체 3 내에 설치한 세로 살 21과 가로 살 4는 프레임체 3과 표면, 이면판 7a, 7b로 형성되는 공간 내를 종횡 복수로 구획하여 복수의 구획부 5 를 형성하고, 이 각 구획부 5 내에는 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말로부터의 탄소계 물질 8이 필요에 따라 부직포를 개재시켜 충전되어 있다. In this way, the longitudinal ribs 21 and the horizontal ribs 4 installed in the frame 3 divide the space formed by the frame 3 and the surface and the back plates 7a and 7b into a plurality of vertical and horizontal sections to form a plurality of partitions 5. Part 5 is filled with carbonaceous material 8 from carbon-based small pieces or powder such as charcoal and activated carbon through a nonwoven fabric as necessary.

이와 같은 제3 실시 형태에 나타내는 건축재 20에 있어서는, 프레임체 3과 표면, 이면판 7a, 7b로 형성되는 공간부 내가 세로 살 21과 가로 살 4로 구획되는 것에 의해 공간부 내의 탄소계 물질 8을 확실하게 분리하여 유지할 수 있으며, 이것에 의해, 건축재를 도어 등에 사용하는 경우 자물쇠를 부착하는 부분의 구획부로부터는 탄소계 물질 8의 충전을 제외하는 일도 용이하게 행할 수 있다. In the building material 20 shown in such 3rd embodiment, the carbonaceous material 8 in a space part is divided by the frame 21 and the space part formed from the surface, the back plate 7a, 7b by being divided into the length 21 and the width 4. It is possible to reliably separate and hold, whereby the filling of the carbonaceous material 8 can be easily removed from the partition portion of the portion to which the lock is attached when the building material is used in a door or the like.

도 4에 나타내는 제4 실시 형태의 건축재 30은, 전술한 제1 실시 형태의 것과 거의 동일한 직사각형의 프레임체 3 공간부 내에 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말 등의 탄소계 물질 8에 멜라민 수지 접착제를 혼합하고 가열·가압하여 패널 상태로 형성하고, 이 카본 패널 9를 상기 공간부 내에 충전한 것이다. The building material 30 of 4th embodiment shown in FIG. 4 is a melamine in the carbon-based substance 8, such as carbon-based small pieces or powders, such as a charcoal and activated carbon, in the space of 3 frame parts of the rectangular shape which are substantially the same as the above-mentioned 1st embodiment. The resin adhesive is mixed, heated and pressed to form a panel, and the carbon panel 9 is filled in the space.

도 5에 나타내는 제5 실시 형태의 건축재 40은, 전술한 제3 실시 형태의 것과 거의 동일한 직사각형의 프레임체 3 공간부 내에 형성한 구획부 5에, 허니콤 코어 41의 구멍부 전부에 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말 등의 탄소계 물질 8에 멜라민 수지 접착제 8a를 혼합하고, 가열·가압에 의해 형성한 소형 카본 패널 9a를 감합 충전한 것이다. The building material 40 of 5th Embodiment shown in FIG. 5 is charcoal and activated carbon in all the hole parts of the honeycomb core 41 in the partition part 5 formed in the frame 3 space part of the substantially rectangular shape similar to the thing of 3rd Embodiment mentioned above. Melamine resin adhesive 8a is mixed with carbonaceous substance 8, such as carbonaceous scraps or powder, and the small carbon panel 9a formed by heating and press fitting is filled.

이상과 같이 하여 형성된 본 발명의 건축재에 의하면, 건물 내의 방 구획재로서 사용한 경우에는 단열성 건축재로서의 기능을 가지며, 한랭지 등에서 동계에 건물의 다른 방이나 건물 밖이 저온이 되어도 방 안의 온도 저하를 줄일 수 있다. According to the building material of the present invention formed as described above, when used as a room partition material in a building, it has a function as a heat insulating building material, and can reduce the temperature drop in the room even in a cold winter or the like in another room or outside the building at a low temperature. have.

또, 종래와 같이 건축재의 내부 공간에 알루미늄박을 사용하고 있지 않으므 로 구획재로서 형성한 건축재의 내면에 결로가 발생하지 않고, 건축재의 프레임체가 뒤틀리거나 휘는 등 변형하는 것을 방지할 수 있다. Further, since aluminum foil is not used in the interior space of the building material as in the prior art, condensation does not occur on the inner surface of the building material formed as the partition material, and the frame body of the building material can be prevented from being warped or warped.

그리고, 본 발명의 건축재를 습기가 많이 발생하는 주방이나 욕실에, 나아가서는 악취가 발생하는 신발장이나 화장실에 건축재로서 사용한 경우에는, 건축재의 내부 공간부에 충전한 목탄, 활성탄 등의 탄소계의 작은 조각 또는 분말 등의 탄소계 물질에 의해 흡습·탈취가 가능하여 쾌적한 방을 제공할 수 있다. In addition, when the building material of the present invention is used as a building material in a kitchen or bathroom in which moisture is generated and furthermore, in a shoe cabinet or a bathroom where odor is generated, carbon-based small particles such as charcoal and activated carbon filled in the interior space of the building material A carbon-based substance such as flakes or powder can absorb and deodorize the dust and provide a comfortable room.

본 발명에 있어서, 카본 패널은 목탄, 활성탄 등 탄소계의 작은 조각 또는 분말 등으로 이루어지는 탄소계 물질을 허니콤 코어에 충전하고 두께 방향으로 가압하기만 하는 것은 탄소계의 미분말을 이용하는 것이 바람직하고, 멜라민 수지 접착제를 이용하지 않는 것에서는 가압만 할 뿐 가열하지 않기 때문에 저가로 할 수 있으며, 또한 상기 탄소계 물질에 분말상의 멜라민 수지 접착제를 혼합시켜 가열 및 가압함으로써 허니콤 코어의 모든 구멍부에 탄소계 물질을 확실하게 유지시켜, 카본 패널의 강도가 크고 탄소계의 작은 조각이나 분말을 이용해도 상기 코어의 구멍부 외로 샐 우려도 없으며, 프레임체에 뒤틀림이나 휨이 발생하는 일이나, 프레임체와 카본 패널 사이에 간극이 생기는 것을 확실히 방지할 수 있다. In the present invention, the carbon panel is preferably a carbon-based fine powder that is filled with a carbon-based material made of carbon-based small pieces or powders such as charcoal and activated carbon in the honeycomb core and pressurized in the thickness direction. In the case where no melamine resin adhesive is used, it can be inexpensively because it only pressurizes and does not heat it. Also, by mixing and heating the powdered melamine resin adhesive with the carbonaceous material, heating and pressurizing the carbon in all the pores of the honeycomb core By keeping the system material securely, even if the carbon panel has a high strength and uses carbon-based small pieces or powders, there is no fear of leaking out of the hole of the core, and distortion or warp occurs in the frame body, It is possible to reliably prevent the gap between the carbon panels.

또한, 프레임체 3의 표, 이면에 접착하는 구멍 뚫린 표면, 이면판은 목재, 합판에 한정되는 일 없이 구멍 뚫린 보드를 이용해도 되는 것은 물론이다. In addition, the table of the frame 3, the perforated surface adhere | attached to the back surface, and a back board may not be limited to wood and plywood, Of course, you may use the perforated board.

도 1은, 본 발명의 제1 실시 형태에 의한 건축재를 나타낸 일부 절결 사시도. 1 is a partially cutaway perspective view showing a building material according to a first embodiment of the present invention.

도 2는, 본 발명의 제2 실시 형태에 의한 건축재를 나타낸 일부 절결 사시도. 2 is a partially cutaway perspective view showing the building material according to the second embodiment of the present invention.

도 3은, 본 발명의 제3 실시 형태에 의한 건축재를 나타낸 일부 절결 평면도. 3 is a partially cutaway plan view of the building material according to the third embodiment of the present invention.

도 4는, 본 발명의 제4 실시 형태의 건축재를 나타낸 일부 절결 평면도. 4 is a partially cutaway plan view showing a building material according to a fourth embodiment of the present invention.

도 5는, 본 발명의 제5 실시 형태의 건축재를 나타낸 일부 절결 평면도. 5 is a partially cutaway plan view showing the building material according to the fifth embodiment of the present invention.

<부호의 설명><Code description>

1 건축재1 building materials

2a, 2b 세로재2a, 2b vertical

2c, 2d 가로재2c, 2d crossbar

3 프레임체3 frame

4 가로 살4 year old

5 구획부5 compartments

6 관통공6 through hole

7a 표면판7a surface plate

7b 이면판7b backplate

8 탄소계 물질8 carbonaceous material

8a 접착제8a glue

9 카본 패널9 carbon panel

10 건축재10 building materials

11 허니콤 코어11 honeycomb core

20 건축재20 building materials

21 세로 살21 years old

30 건축재30 building materials

31 카본 패널31 carbon panel

40 건축재40 building materials

Claims

A rectangular or square frame body formed by combining a longitudinal material and a cross member, a surface adhered to both surfaces of the frame body, a back plate, and a nonwoven fabric of a polypropylene resin-based breathable material on the surface and an inner surface side of the back plate. At least one of forming a plurality of small holes penetrating through the surface and the back plate, and arranging the space formed by the frame and the surface and the back plate between the horizontal members of the frame body. A plurality of partitions are formed by separating a plurality of sections vertically and laterally by a plurality of horizontal bars arranged at equal intervals in the longitudinal direction of the vertical member between the vertical member and the vertical member of the frame member, and forming a plurality of compartments. Each bag is filled with a carbonaceous material made of carbon-based small pieces or powder such as charcoal and activated carbon in a bag-shaped nonwoven fabric. Scaffolding, characterized in that the mounting portion in the space.

The building material according to claim 1, wherein one or both of the surface, the back plate, and the decorative plate are perforated.