KR20100057373A - The clad metal having coating layer by copper thermal spray and the method for the same - Google Patents

The clad metal having coating layer by copper thermal spray and the method for the same Download PDF

Info

Publication number
KR20100057373A
KR20100057373A KR1020080116388A KR20080116388A KR20100057373A KR 20100057373 A KR20100057373 A KR 20100057373A KR 1020080116388 A KR1020080116388 A KR 1020080116388A KR 20080116388 A KR20080116388 A KR 20080116388A KR 20100057373 A KR20100057373 A KR 20100057373A
Authority
KR
South Korea
Prior art keywords
layer
coating layer
copper
blasting
spray coating
Prior art date
Application number
KR1020080116388A
Other languages
Korean (ko)
Other versions
KR101206754B1 (en
Inventor
조용래
Original Assignee
조용래
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 조용래 filed Critical 조용래
Priority to KR1020080116388A priority Critical patent/KR101206754B1/en
Publication of KR20100057373A publication Critical patent/KR20100057373A/en
Application granted granted Critical
Publication of KR101206754B1 publication Critical patent/KR101206754B1/en

Abstract

PURPOSE: A clad plate having a copper thermal spray coating layer and a method for manufacturing the same are provided to increase a heating rate using same heat energy when the clad plate is applied to a container by forming the copper thermal spray coating layer having more excellent thermal conductivity on a stainless board surface. CONSTITUTION: A clad plate(100) having a copper thermal spray coating layer comprises: a clad metal layer which is composed of an aluminum layer(10) and a stainless layer(20); a blasting side which is formed on the surface of the stainless layer by blasting the stainless layer with an abrasion material made of high-carbon steel material; and the copper thermal spray coating layer(40) which is formed on the blasting side.

Description

동용사 코팅층을 갖는 클래드판과 그 제조방법{The clad metal having coating layer by copper thermal spray and the method for the same} Clad plate having copper spray coating layer and its manufacturing method {The clad metal having coating layer by copper thermal spray and the method for the same}

본 발명은 동용사 코팅층을 갖는 클래드판과 그 제조방법에 관한 것이다.The present invention relates to a clad plate having a copper spray coating layer and a method of manufacturing the same.

일반적으로, 클래드메탈은 여러 가지 다양한 금속을 함께 결합하여 각 금속의 장점만을 취하는 신소재로서, 그 중에서도 열전도율, 열보존율 및 열효율성이 뛰어난 알루미늄 판과 내염성, 내산성, 내알카리성 및 내식성이 뛰어난 스테인레스 판을 접합시킨 것이 가장 널리 쓰이고 있다.In general, clad metal is a new material that combines various metals together to take advantage of each metal only. Among them, aluminum plate having excellent thermal conductivity, heat preservation rate and thermal efficiency, and stainless steel plate having excellent flame resistance, acid resistance, alkali resistance and corrosion resistance Bonding is the most widely used.

이러한 클래드판 제조방법은, 2겹 이상의 스테인레스 판 사이에 알루미늄 판을 삽입하고, 열과 함께 눌러서 접합 제조한다. 스테인레스 판의 열전도율은 0.04cal/㎝.sec℃ 이지만 클래드판의 열전도율은 0.35cal/㎝.sec℃ 로 매우 높아 밥솥에 사용되는 내솥 따위의 용기를 비롯하여, 열교환기, 자동차 용품, 건축내외장재, 주방용품 등에 널리 사용되고 있다.In this clad plate manufacturing method, an aluminum plate is inserted between two or more layers of stainless plates, and pressed together with heat to produce a joint. The thermal conductivity of stainless steel plate is 0.04cal / cm.sec ℃, but the thermal conductivity of clad plate is very high, 0.35cal / cm.sec ℃, including the inner pots used in rice cookers, heat exchangers, automobile supplies, building interior and exterior materials, and kitchen utensils. It is widely used for such purposes.

최근 들어, 상기와 같은 클래드판의 열전도율과 열보존율을 더욱 개선하기 위하여 클래드판의 스테인레스 판재 표면에 황동용사 코팅층을 형성시키는 기술이 적용되고 있으나, 동의 열전도율 333 kcal/mh°c 에 비하여 1/3에도 못미치는 85 kcal/mh°c 의 열전도율을 갖는 황동으로써 스테인레스 판재 표면에 용사시키는 이유는, 동으로써 스테인레스 판재에 용사시키면 접착이 잘 되지 않을 뿐만 아니라, 밥솥에 사용되는 내솥같이 고온의 열이 가해지면, 동용사 코팅층이 클래드판의 스테인레스 판재로부터 박리되는 문제점이 있었다. Recently, in order to further improve the thermal conductivity and heat retention of the clad plate as described above, a technique of forming a brass spray coating layer on the surface of the stainless plate of the clad plate has been applied, but it is 1/3 compared to the copper thermal conductivity of 333 kcal / mh ° c. Brass with a thermal conductivity of less than 85 kcal / mh ° C, which sprays on the surface of a stainless steel plate, is not easily adhered to when sprayed on a stainless steel plate, and is heated by a high temperature like an inner pot used in a rice cooker. There was a problem that the copper spray coating layer was peeled off from the stainless plate of the clad plate.

본 발명이 해결하고자 하는 과제는, 클래드판의 스테인레스 판재로부터 용이하게 박리되지 않을 뿐만 아니라, 클래드판의 열전도율과 열보존율이 더욱 개선될 수 있는 동용사 코팅층을 갖는 클래드판과 그 제조방법을 제공하는 것이다. The problem to be solved by the present invention is to provide a clad plate having a copper spray coating layer that can not only be easily peeled off from the stainless plate of the clad plate, but also the heat conductivity and heat retention of the clad plate can be further improved. will be.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판은, 알루미늄층과 스테인레스층으로 이루어진 클래드메탈층, 고탄소강 소재로 이루어진 연마재로 블라스팅하여 상기 스테인레스층 표면에 형성되어 있는 블라스팅면, 그리고 상기 블라스팅면에 형성되어 있는 동용사층을 포함한다.Clad plate having a copper spray coating layer according to an embodiment of the present invention, the blasting surface formed on the surface of the stainless layer by blasting with a clad metal layer consisting of an aluminum layer and a stainless layer, an abrasive made of a high carbon steel material, and the And a thermal sprayed layer formed on the blasting surface.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판에서, 상기 동용사층은, 10kg/㎠ 이상의 압축공기로 세척제를 분사하여 블라스팅면에 부착되어 있는 이물질을 제거한 다음 형성될 수 있다.In the clad plate having a copper spray coating layer according to an embodiment of the present invention, the copper spray layer may be formed after spraying the cleaning agent with compressed air of 10kg / ㎠ or more to remove the foreign matter attached to the blasting surface.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판에서, 상기 동용사층은, 스테인레스의 변태점까지 가열된 상태에서 형성될 수 있다.In the clad plate having a copper spray coating layer according to an embodiment of the present invention, the copper spray layer may be formed in a state heated to the transformation point of stainless steel.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판으로 이루어진 용기는, 알루미늄층과 스테인레스층으로 이루어진 클래드메탈층, 고탄소강 소재로 이루어진 연마재로 블라스팅하여 상기 스테인레스층 표면에 형성되어 있는 블라스팅면, 그리고 상기 블라스팅면에 형성되어 있는 동용사층을 가지며, 상기 알루미늄층 표면에는 불소수지 코팅층이 형성되어 있고, 상기 동용사층 표면에는 클리어 코팅층이 형성되어 있다.A container made of a clad plate having a copper spray coating layer according to an embodiment of the present invention is a blasted surface formed on the surface of the stainless layer by blasting with a clad metal layer made of an aluminum layer and a stainless layer, and an abrasive made of a high carbon steel material. And a copper sprayed layer formed on the blasting surface, a fluororesin coating layer is formed on the surface of the aluminum layer, and a clear coating layer is formed on the surface of the copper sprayed layer.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판의 제조방법은, 스테인레스층 표면을 블라스팅하는 단계, 블라스팅면을 세척하는 단계, 클래드메탈을 가열하는 단계, 가열된 클래드메탈의 블라스팅면에 동용사층을 형성하는 단계, 그리고 동용사층 표면을 연마하는 단계를 포함한다. Method for producing a clad plate having a copper spray coating layer according to an embodiment of the present invention, the step of blasting the stainless layer surface, washing the blasting surface, heating the clad metal, on the blasting surface of the heated clad metal Forming a copper sprayed layer, and polishing the surface of the copper sprayed layer.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판의 제조방법은, 동용사층 표면을 연마한 다음 클리어 코팅층을 형성하는 단계와 알루미늄층에 불소수지 코팅층을 형성하는 단계를 더 포함할 수 있다.The method of manufacturing a clad plate having a copper spray coating layer according to an embodiment of the present invention may further include forming a clear coating layer after polishing the surface of the copper spray layer and forming a fluororesin coating layer on the aluminum layer. have.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판의 제조방법에서, 스테인레스층 표면을 블라스팅하는 단계는, 고탄소강 소재로 이루어진 연마재로써 블라스팅하는 동용사 코팅층을 가질 수 있다.In the method of manufacturing a clad plate having a copper spray coating layer according to an embodiment of the present invention, the blasting of the stainless layer surface may have a copper spray coating layer blasted with an abrasive made of a high carbon steel material.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판의 제조방법에서, 블라스팅면을 세척하는 단계는, 10kg/㎠ 이상의 압축공기로 세척제를 분사하여 블라스팅면(21)에 부착되어 있는 이물질을 제거할 수 있다.In the method of manufacturing a clad plate having a copper spray coating layer according to an embodiment of the present invention, the step of cleaning the blasting surface, by spraying a cleaning agent with compressed air of 10kg / ㎠ or more compressed foreign matter attached to the blasting surface 21 Can be removed.

본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판의 제조방법에서, 클래드메탈을 가열하는 단계는, 스테인레스의 변태점까지 가열된 상태에서 형 성될 수 있다.In the method of manufacturing a clad plate having a copper spray coating layer according to an embodiment of the present invention, the heating of the clad metal may be formed in a heated state to the transformation point of stainless steel.

본 발명의 실시예에 따르면, 고탄소강의 작은 입자로써 블라스팅하여 표면에 작은 요철부가 형성되어 있는 클래드메탈의 스테인레스층을 변태점까지 가열시킨 상태에서 동용사 공정을 거치므로, 코팅되어 있는 동용사층이 클래드메탈로부터 박리되는 것을 방지할 수 있어, 클래드판의 신뢰성을 제고할 수 있다.According to an embodiment of the present invention, since the stainless steel layer of the clad metal, which is blasted with small particles of high carbon steel, is heated to the transformation point by heating the stainless layer of the clad metal on which the small irregularities are formed, the coated copper thermal spray layer is coated. Peeling from the clad metal can be prevented and the reliability of the clad plate can be improved.

그리고, 본 발명의 실시예에 따르면, 스테인레스 판재표면에 황동용사 코팅층 보다 우수한 열전도율을 갖는 동용사층이 형성되므로, 열전도율이 더욱 높아 용기 따위에 적용되는 경우 동일한 열에너지를 가하더라도 가열속도가 더욱 빨라져서, 연료 소비를 줄일 수 있을 뿐만 아니라, 동용사 코팅층이 스테인레스층의 열을 빨리 전달 받아 보유하게 되고, 보유한 열은 동용사 코팅층 전체가 스테인레스층 전체를 감싸면서, 스테인레스 층의 온도를 보다 신속하게 상승시키므로, 열보존율이 우수하여 에너지 낭비를 방지할 수 있다.In addition, according to the embodiment of the present invention, since the copper thermal spray layer having a higher thermal conductivity than the brass thermal spray coating layer is formed on the surface of the stainless steel plate, the heating rate is faster even when the same thermal energy is applied when the thermal conductivity is higher, such as when applied to a container. In addition to reducing fuel consumption, the copper thermal coating layer receives heat from the stainless layer quickly and retains it, and the retained heat raises the temperature of the stainless layer more quickly as the entire copper coating layer covers the entire stainless layer. In addition, the heat preservation rate is excellent to prevent energy waste.

또한, 제조공정이 단순하며, 재료비를 절감할 수 있다.In addition, the manufacturing process is simple, and the material cost can be reduced.

이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록, 본 발명의 실시예에 대하여 첨부한 도면을 참고로 하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 여기에서 설명하는 실시예에 한정되지 않는다. 명세서 전체를 통하여 유사한 부분에 대해서는 동일한 도면 부호를 붙였다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art may easily implement the present invention. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present invention. Like parts are designated by like reference numerals throughout the specification.

그러면, 본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판에 대하여 도 1 내지 도 3을 참고하여 설명한다.Then, a clad plate having a copper spray coating layer according to an embodiment of the present invention will be described with reference to FIGS.

도 1은 동용사 코팅층을 갖는 클래드판을 나타낸 구성도이고, 도 2는 도1에서 공정별 작업과정을 나타내는 작업상태도이고, 도 3은 동용사 코팅층을 갖는 클래드판 제조방법을 나타낸 공정도이다.1 is a configuration diagram showing a clad plate having a copper spray coating layer, Figure 2 is a working state diagram showing the operation process by process in Figure 1, Figure 3 is a process chart showing a clad plate manufacturing method having a copper spray coating layer.

도 1 내지 도 3을 참고하면, 본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판은, 알루미늄층(10)과 스테인레스층(20)으로 이루어진 클래드메탈층(30), 그리고 동용사층(40)을 포함한다.1 to 3, the clad plate having a copper spray coating layer according to an embodiment of the present invention, the clad metal layer 30 consisting of an aluminum layer 10 and a stainless layer 20, and the copper spray layer And 40.

알루미늄층(10)은, 본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판에서 스테인레스층(20)과 함께 클래드판을 형성한다. 스테인레스층(20) 표면은 고탄소강 소재로 이루어진 연마재로 블라스팅하여 블라스팅면(21)이 형성되어 있다.The aluminum layer 10 forms a clad plate together with the stainless layer 20 in a clad plate having a copper spray coating layer according to an embodiment of the present invention. The surface of the stainless layer 20 is blasted with an abrasive made of a high carbon steel material, and the blasting surface 21 is formed.

클래드메탈층(30)은 두 가지의 금속재료의 표면을 금속학적으로 접합하여 일체 화시킨 적층형의 복합재료로서, 이와 같이 클래드메탈층(30)을 형성함으로써 소재의 성능을 극대화시키고, 고가의 소재를 절약할 수 있기 때문에 경제적으로도 큰 장점이 있다. 따라서, 소재의 조합이 점차 다양해지고 있으며 적용분야도 확대되고 있다.The clad metal layer 30 is a laminated composite material in which two surfaces of two metal materials are bonded by metallization and integrated. The clad metal layer 30 maximizes the performance of the material by forming the clad metal layer 30. There is also a great economic advantage because it can save. Therefore, the combination of materials is gradually diversified and the field of application is expanding.

상기와 같은 스테인리스강-알루미늄 클래드메탈층(30)은 스테인리스강과 알루미 늄의 장점을 적절히 조합시켜 사용하기 위하여 창안되었는데, 알루미늄의 낮은 비중과 높은 열전도도, 스테인리스강의 우수한 내식성 및 가공성 등의 장점을 가지고 있다.As described above, the stainless steel-aluminum clad metal layer 30 was created to use a combination of the advantages of stainless steel and aluminum, and has advantages such as low specific gravity of aluminum, high thermal conductivity, and excellent corrosion resistance and workability of stainless steel. have.

동용사층(40)은, 클래드메탈을 가열하는 단계를 거치면서 스테인레스의 변태점인 780℃까지 가열되어 있는 상기 모재의 표면에 동용사를 실시하여 형성되는 층이다.The copper sprayed layer 40 is a layer formed by applying copper spraying to the surface of the base material heated to 780 ° C, which is a transformation point of stainless steel, while heating the clad metal.

그리고, 본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판으로 이루어진 용기는, 상기 클래드판(100)을 갖는 용기 내면에 형성되는 불소수지 코팅층(50) 및 클리어 코팅층(60)을 더 포함한다. In addition, the container made of a clad plate having a copper spray coating layer according to an embodiment of the present invention further includes a fluororesin coating layer 50 and a clear coating layer 60 formed on an inner surface of the container having the clad plate 100. do.

불소수지 코팅층(50)은, 동용사 코팅층을 갖는 클래드판으로 이루어진 용기(110)의 내측면에 처리하여, 알루미늄층(10)을 보호함과 동시에 설거지가 용이하도록 하기 위하여 형성시킨 층이다.The fluororesin coating layer 50 is treated on the inner surface of the container 110 made of a clad plate having a copper spray coating layer, The layer is formed to protect the aluminum layer 10 and to facilitate washing.

클리어 코팅층(60)은, 연마된 동용사층의 표면(40)을 보호하며, 동 고유의 색상이 잘 표현되도록 하기 위하여 실리콘 클리어코팅 따위를 형성시킨 층이다.The clear coating layer 60 protects the surface 40 of the polished copper sprayed layer, and is a layer formed with a silicon clear coating in order to express the unique color of the copper spray layer.

또한, 본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판 제조방법에 대하여 도 2 및 도 3을 참고하여 설명한다.In addition, a clad plate manufacturing method having a copper spray coating layer according to an embodiment of the present invention will be described with reference to FIGS. 2 and 3.

도 2 및 도 3을 참고하면, 본 발명의 한 실시예에 따른 동용사 코팅층을 갖는 클래드판 제조방법은, 스테인레스층 표면을 블라스팅하는 단계(S1), 블라스팅면을 세척하는 단계(S2), 클래드메탈을 가열하는 단계(S3), 가열된 클래드메탈의 블라스팅면에 동용사층을 형성하는 단계(S4) 및 동용사층 표면을 연마하는 단계(S5)를 포함하며, 연마된 동용사층에 클리어코팅층을 형성하는 단계(S6)와 알루미늄층에 불소수지 코팅층을 형성하는 단계(S7)를 더 포함할 수 있다.2 and 3, the cladding plate manufacturing method having a copper spray coating layer according to an embodiment of the present invention, the step of blasting the stainless layer surface (S1), the step of washing the blasting surface (S2), clad Heating the metal (S3), forming a copper sprayed layer on the blasted surface of the heated clad metal (S4), and polishing the surface of the copper sprayed layer (S5), and clearing the polished copper sprayed layer. Forming a coating layer (S6) and forming a fluororesin coating layer on the aluminum layer (S7) may be further included.

스테인레스층 표면을 블라스팅하는 단계(S1)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 고탄소강 소재로 이루어진 연마재로 블라스팅하여 상기 스테인레스층(20) 표면에 작은 흠집을 형성시키는 단계로서, 상기와 같이 작은 흠집을 형성되어 있는 표면에 동용사층(40)이 견고하게 결합될 수 있다. Blasting the surface of the stainless layer (S1), in the method of manufacturing a clad plate having a copper spray coating layer of the present invention, by blasting with an abrasive made of a high carbon steel material to form a small scratch on the surface of the stainless layer (20) , The thermal sprayed layer 40 may be firmly coupled to the surface on which the small scratches are formed as described above.

블라스팅면을 세척하는 단계(S2)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 상기 블라스팅하는 단계(S1)에서 형성된 작은 흠집을 갖는 표면의 이물질 따위를 제거하기 위한 단계로서, 10kg/㎠ 이상의 압축공기로 세척제를 분사하여 블라스팅면(21)에 부착되어 있는 이물질을 제거한다.The step (S2) of washing the blasting surface is a step for removing foreign matters on the surface having a small scratch formed in the blasting step (S1) in the method of manufacturing a clad plate having the same thermal spray coating layer of the present invention. The cleaning agent is sprayed with compressed air of / cm 2 or more to remove foreign substances adhering to the blasting surface 21.

클래드메탈을 가열하는 단계(S3)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 블라스팅면을 세척하는 단계(S2)를 거친 모재의 표면에 동용사층(40)이 견고하게 결합될 수 있도록 하기 위한 공정으로서, 상기 모재를 스테인레스의 변태점인 780℃까지 가열하므로써 그 체적이 최대가 되도록 하는 공정이다. Heating the clad metal (S3), in the clad plate manufacturing method having a copper spray coating layer of the present invention, the copper spray layer 40 is firmly bonded to the surface of the base material undergoing the step of washing the blasting surface (S2) As a process to make it possible, the volume is maximized by heating the said base material to 780 degreeC which is a transformation point of stainless steel.

가열된 클래드메탈의 블라스팅면에 동용사층을 형성하는 단계(S4)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 클래드메탈을 가열하는 단계(S3)를 거치면서 스테인레스의 변태점인 780℃까지 가열되어 있는 상기 모재의 표면에 동용사를 실시하는 공정이다.Forming a copper spray layer on the blasting surface of the heated clad metal (S4), in the clad plate manufacturing method having a copper spray coating layer of the present invention, the step of heating the clad metal (S3) is a transformation point of stainless It is a process of copper spraying on the surface of the said base material heated to 780 degreeC.

동용사층 표면을 연마하는 단계(S5)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 클리어 코팅층(60)을 형성하기 위하여 동용사층(40) 표면을 연마하여 이물질을 제거하는 공정이다.Polishing the surface of the thermal sprayed coating layer (S5), in the clad plate manufacturing method having a copper spray coating layer of the present invention, to remove the foreign matter by polishing the surface of the copper sprayed layer 40 to form a clear coating layer (60) It is a process.

연마된 동용사층에 클리어코팅층을 형성하는 단계(S6)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 연마된 동용사층의 표면을 보호하며, 동 고유의 색상이 잘 표현되도록 하기 위하여 실리콘 클리어코팅 따위를 형성시키는 단계이다.Forming a clear coating layer on the polished copper sprayed layer (S6), in the clad plate manufacturing method having a copper sprayed coating layer of the present invention, to protect the surface of the polished copper sprayed layer, so that the unique color of copper In order to form a silicone clear coating.

알루미늄층에 불소수지 코팅층을 형성하는 단계(S7)는, 본 발명의 동용사 코팅층을 갖는 클래드판 제조방법에서, 동용사 코팅층을 갖는 클래드판으로 이루어진 용기(110)의 내측면에 불소수지 코팅층을 형성하여, 알루미늄층(10)을 보호함과 동시에 설거지가 용이하도록 하기 위한 공정이다.Forming a fluorine resin coating layer on the aluminum layer (S7), in the clad plate manufacturing method having a copper spray coating layer of the present invention, a fluorine resin coating layer on the inner surface of the container 110 made of a clad plate having a copper spray coating layer By forming The process for protecting the aluminum layer 10 and at the same time easy to wash dishes.

이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만, 본 발명의 권리범위는 이에 한정되는 것은 아니고, 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.Although the preferred embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements of those skilled in the art using the basic concepts of the present invention defined in the following claims are also provided. It belongs to the scope of the present invention.

도 1은 본 발명에 따른 동용사 코팅층을 갖는 클래드판을 나타낸 구성도이고, 1 is a block diagram showing a clad plate having a copper spray coating layer according to the present invention,

도 2는 도1에서 공정별 작업과정을 나타내는 작업상태도이고, Figure 2 is a working state diagram showing the operation process by process in Figure 1,

도 3은 도1에서 동용사 코팅층을 갖는 클래드판 제조방법을 나타낸 공정도이고,3 is a process chart showing a clad plate manufacturing method having a copper spray coating layer in FIG.

도 4는 본 발명에 따른 동용사 코팅층을 갖는 클래드판으로 이루어진 용기를 나타낸 단면도이고,4 is a cross-sectional view showing a container made of a clad plate having a copper spray coating layer according to the present invention,

도 5는 도4에서 동용사 코팅층을 갖는 클래드판으로 이루어진 용기의 제조방법을 나타낸 공정도이다.Figure 5 is a process chart showing a manufacturing method of a container consisting of a clad plate having a copper spray coating layer in FIG.

<도면에 주요부분에 대한 부호의 설명><Description of the symbols for the main parts in the drawings>

10 : 알루미늄층 20 : 스테인레스층10: aluminum layer 20: stainless layer

21 : 블라스팅면 30 : 클래드메탈21: blasting surface 30: clad metal

40 : 동용사층 50 : 불소수지 코팅층40: copper spray layer 50: fluororesin coating layer

60 : 클리어 코팅층 100 : 클래드판60: clear coating layer 100: clad plate

110 : 용기110: container

Claims (9)

알루미늄층과 스테인레스층으로 이루어진 클래드메탈층, Clad metal layer consisting of an aluminum layer and a stainless layer, 고탄소강 소재로 이루어진 연마재로 블라스팅하여 상기 스테인레스층 표면에 형성되어 있는 블라스팅면, 그리고 A blasting surface formed on the surface of the stainless layer by blasting with an abrasive made of a high carbon steel material, and 상기 블라스팅면에 형성되어 있는 동용사층을 가지는 Having a thermal sprayed layer formed on the blasting surface 동용사 코팅층을 갖는 클래드판.Clad plate which has a copper spray coating layer. 제1항에서,In claim 1, 상기 동용사층은, 10kg/㎠ 이상의 압축공기로 세척제를 분사하여 블라스팅면에 부착되어 있는 이물질을 제거한 다음 형성되는 동용사 코팅층을 갖는 클래드판.The copper spray layer is a clad plate having a copper spray coating layer formed by spraying the cleaning agent with compressed air of 10kg / ㎠ or more to remove the foreign matter attached to the blasting surface. 제1항에서In claim 1 상기 동용사층은, 스테인레스의 변태점까지 가열된 상태에서 형성되는 동용사 코팅층을 갖는 클래드판.The copper sprayed layer is a clad plate having a copper spray coating layer formed in a state heated to the transformation point of stainless. 알루미늄층과 스테인레스층으로 이루어진 클래드메탈층, Clad metal layer consisting of an aluminum layer and a stainless layer, 고탄소강 소재로 이루어진 연마재로 블라스팅하여 상기 스테인레스층 표면에 형성되어 있는 블라스팅면, 그리고 A blasting surface formed on the surface of the stainless layer by blasting with an abrasive made of a high carbon steel material, and 상기 블라스팅면에 형성되어 있는 동용사층을 가지며,Has a copper spray layer formed on the blasting surface, 상기 알루미늄층 표면에는 불소수지 코팅층이 형성되어 있고, 상기 동용사층 표면에는 클리어 코팅층이 형성되어 있는A fluororesin coating layer is formed on the surface of the aluminum layer, and a clear coating layer is formed on the surface of the copper sprayed layer. 동용사 코팅층을 갖는 클래드판으로 이루어진 용기.A container consisting of a clad plate with a copper spray coating layer. 스테인레스층 표면을 블라스팅하는 단계,Blasting the stainless layer surface, 블라스팅면을 세척하는 단계,Washing the blasting surface, 클래드메탈을 가열하는 단계,Heating the clad metal, 가열된 클래드메탈의 블라스팅면에 동용사층을 형성하는 단계, 그리고Forming a thermal sprayed layer on the blasted surface of the heated clad metal, and 동용사층 표면을 연마하는 단계Polishing the surface of the thermal sprayed layer 를 포함하는 Containing 동용사 코팅층을 갖는 클래드판 제조방법. Clad plate manufacturing method having a thermal spray coating layer. 제5항에서,In claim 5, 동용사층 표면을 연마한 다음 클리어 코팅층을 형성하는 단계와 알루미늄층에 불소수지 코팅층을 형성하는 단계를 더 포함하는Grinding the surface of the copper sprayed layer and then forming a clear coating layer and forming a fluororesin coating layer on the aluminum layer. 동용사 코팅층을 갖는 클래드판 제조방법.Clad plate manufacturing method having a thermal spray coating layer. 제5항에서,In claim 5, 스테인레스층 표면을 블라스팅하는 단계는, 고탄소강 소재로 이루어진 연마재로써 블라스팅하는 동용사 코팅층을 갖는 클래드판 제조방법.The step of blasting the stainless layer surface, the clad plate manufacturing method having a copper spray coating layer blasted with an abrasive made of a high carbon steel material. 제5항에서,In claim 5, 블라스팅면을 세척하는 단계는, 10kg/㎠ 이상의 압축공기로 세척제를 분사하여 블라스팅면에 부착되어 있는 이물질을 제거하는 동용사 코팅층을 갖는 클래드판 제조방법.The step of washing the blasting surface, the method of manufacturing a clad plate having a spray coating layer to remove the foreign matter attached to the blasting surface by spraying the cleaning agent with compressed air of 10kg / ㎠ or more. 제5항에서,In claim 5, 클래드메탈을 가열하는 단계는, 스테인레스의 변태점까지 가열된 상태에서 형성되는 동용사 코팅층을 갖는 클래드판 제조방법.Heating the clad metal is a clad plate manufacturing method having a copper spray coating layer formed in the state heated to the transformation point of stainless steel.
KR1020080116388A 2008-11-21 2008-11-21 The clad metal having coating layer by copper thermal spray and the method for the same KR101206754B1 (en)