KR20090130746A - Adhesive composition for optical filter, method of manufacturing adhesive sheet using the composition and display manufactured by using the adhesive sheet - Google Patents
Adhesive composition for optical filter, method of manufacturing adhesive sheet using the composition and display manufactured by using the adhesive sheet Download PDFInfo
- Publication number
- KR20090130746A KR20090130746A KR1020080056514A KR20080056514A KR20090130746A KR 20090130746 A KR20090130746 A KR 20090130746A KR 1020080056514 A KR1020080056514 A KR 1020080056514A KR 20080056514 A KR20080056514 A KR 20080056514A KR 20090130746 A KR20090130746 A KR 20090130746A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- adhesive composition
- pressure
- sensitive adhesive
- parts
- Prior art date
Abstract
Description
본 발명은 광학필터용 점착제 조성물에 관한 것으로, 보다 상세하게는 오토 클레이브에 의한 고온·고압 처리를 필요로 하지 않고 실온에서 광학 필터와 접합이 가능하며, 내충격성 및 광학 특성이 우수한 재작업이 가능한 광학필터용 점착제 조성물, PDP용 광학 필터 및 점착시트 제조방법에 관한 것이다.The present invention relates to a pressure-sensitive adhesive composition for an optical filter, more specifically, it is possible to bond with an optical filter at room temperature without requiring high temperature and high pressure treatment by an autoclave, and rework excellent in impact resistance and optical properties is possible. The present invention relates to a pressure-sensitive adhesive composition for an optical filter, an optical filter for a PDP, and a pressure-sensitive adhesive sheet manufacturing method.
범용적인 PDP용 광학필터는 글라스 필터와 필름 필터로 구분이 된다. 디스플레이 장치가 대형화 되어 갈수록, 전면 필터로서 필름 필터보다는 글라스 필터가 그 비중이 높아진다. 필름 필터의 경우 대형화되면, 전면 모듈의 내충격성이 감소하여, 작은 충격에도 모듈이 파손되는 단점이 있어, 대형 디스플레이에는 글라스 필터가 일반적으로 사용된다. 하지만, 글라스 필터는 필터와 모듈 사이에 공간이 있어, 명실명암비가 떨어지고, 이중상이 발생하며, 시인성이 떨어지는 단점이 있다. 이에 일부에서는 글라스 필터와 모듈을 접착제로 접합하는 것에 대한 연구가 진행되고 있다. 구체적으로는, 표시 패널과 보호 패널 사이에 액상 수지를 주입한 후 실온에서 경화시키는 방법, 핫 멜트 접착제로 가열 용융하여 접착 처리하는 방법, 시판 중인 연질의 투명 점착 시트를 이용하여 압착 처리하는 방법 등이 제안되었다. General purpose optical filter for PDP is divided into glass filter and film filter. As the display device becomes larger, the specific gravity of the glass filter is higher than that of the film filter as the front filter. In the case of a large sized film filter, the impact resistance of the front module is reduced, so that the module is broken even with a small impact, and a glass filter is generally used for a large display. However, the glass filter has a space between the filter and the module, so that the contrast ratio is low, a double phase occurs, and the visibility is inferior. In some cases, research on bonding the glass filter and the module with an adhesive is in progress. Specifically, a liquid resin is injected between the display panel and the protective panel, and then cured at room temperature, heated and melted with a hot melt adhesive, and bonded, or pressed using a commercially available soft transparent adhesive sheet. This has been proposed.
그러나 상기의 방법들은 다음과 같은 문제점을 가지고 있다. 표시 패널과 보호 패널 사이에 액상 수지를 주입한 후 실온에서 경화시키는 방법은 재작업성의 문제와 생산속도 저감의 문제가 있고, 핫 멜트 접착제로 가열 용융항 접착처리하는 방법은 내열특성 저하 문제와 재작업시 잔사의 문제가 있으며, 연질의 투명 점착 시트를 이용하여 압착처리하는 방법은 고온 내구성 Test에서 표면의 Glass의 밀림 현상이 발생하는 문제가 있다.However, the above methods have the following problems. The method of hardening at room temperature after injecting a liquid resin between the display panel and the protection panel has problems of reworkability and reducing production speed. The method of hot melt adhesive bonding with a hot melt adhesive reduces the heat resistance and When working, there is a problem of residue, and the method of compressing by using a soft transparent adhesive sheet has a problem that the surface of the glass in the high temperature durability test occurs.
따라서, 이러한 문제점들을 해결하고자 하는 노력이 관련 분야에서 꾸준히 이루어져 왔으며, 본 발명은 이러한 기술적 배경하에서 안출된 것이다. Accordingly, efforts to solve these problems have been steadily made in the related field, and the present invention has been devised under this technical background.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로, 오토 클레이브에 의한 고온·고압 처리를 필요로 하지 않고, 실온에서 광학 필터의 접합이 가능하고, 고온에서 재작업이 용이한 적층체의 제조가 가능하고, 또한 판 어긋남이 잘 일어나지 않고, 우수한 내충격성을 갖는 광학필터용 점착제 조성물을 제공하는데 그 목적이 있다. SUMMARY OF THE INVENTION The present invention has been made to solve the above problems, and does not require high temperature and high pressure treatment by an autoclave, enables the bonding of optical filters at room temperature, and the manufacture of laminates that are easy to rework at high temperatures. It is an object to provide a pressure-sensitive adhesive composition for an optical filter which can be used and plate misalignment hardly occurs and has excellent impact resistance.
본 발명의 다른 목적은 상기의 광학필터용 점착제 조성물을 이용하여 제조된 투명 점착시트의 제조방법을 제공하는 것이다. Another object of the present invention to provide a method for producing a transparent pressure-sensitive adhesive sheet prepared using the pressure-sensitive adhesive composition for an optical filter.
본 발명의 또 다른 목적인 상기의 제조방법에 의하여 제조된 점착시트를 이용한 디스플레이를 제공하는 것이다.Another object of the present invention to provide a display using a pressure-sensitive adhesive sheet prepared by the above manufacturing method.
본 발명은 상기의 목적을 달성하기 위한 것으로, 호모폴리머로 중합시 유리전이온도가(Tg)가 0℃ 이하인 연성 아크릴계 모노머 70 ~ 99 중량% 및 호모폴리머로 중합시 유리전이온도가(Tg)가 80℃ 이상인 경성 아크릴게 모노머 1 ~ 30 중량%로 이루어지는 아크릴계 모노머 100중량부; 라디칼 개시제 0.1 ~ 5 중량부; 및 가교제 0.01 ~ 20 중량부를 포함하는 광학필터용 점착제 조성물을 제공한다. The present invention is to achieve the above object, the glass transition temperature (Tg) when the polymerization in the homopolymer (Tg) is 70 ~ 99% by weight of the flexible acrylic monomer having a temperature of 0 ℃ or less and the glass transition temperature (Tg) when polymerization with the homopolymer 100 parts by weight of an acrylic monomer composed of 1 to 30% by weight of a hard acrylic crab monomer having a temperature of 80 ° C. or higher; 0.1 to 5 parts by weight of radical initiator; And it provides a pressure-sensitive adhesive composition for an optical filter comprising 0.01 to 20 parts by weight of a crosslinking agent.
또한, 상기 점착제 조성물의 점도가 25℃에서 500 ~ 3000cps의 범위에 있는 것을 특징으로 한다. In addition, the pressure-sensitive adhesive composition is characterized in that in the range of 500 ~ 3000cps at 25 ℃.
또한, 상기 연성 아크릴계 모노머는 부틸아크릴레이트, 부틸메타크릴레이트, 헥실아크릴레이트, 헥실메타크릴레이트, n-옥틸아크릴레이트, n-옥틸메타크릴레이트, 이소옥틸아크릴레이트, 이소옥틸메타크릴레이트, 2-에틸헥실아크릴레이트, 2-에틸헥실메타크릴레이트, 이소노닐아크릴레이트, 이소노닐메타크릴레이트 또는 이들의 혼합물인 것을 특징으로 한다.In addition, the soft acrylic monomer is butyl acrylate, butyl methacrylate, hexyl acrylate, hexyl methacrylate, n-octyl acrylate, n-octyl methacrylate, isooctyl acrylate, isooctyl methacrylate, 2 -Ethylhexyl acrylate, 2-ethylhexyl methacrylate, isononyl acrylate, isononyl methacrylate or a mixture thereof.
또한, 상기 경성 아크릴계 모노머는 아크릴산, 메타크릴산, 말레인산, 푸마르산, 아크릴아미드, N-비닐피롤리돈, N-비닐 카프로락탐, 아크릴로니트릴 또는 이들의 혼합물인 것을 특징으로 한다.In addition, the hard acrylic monomer is characterized in that the acrylic acid, methacrylic acid, maleic acid, fumaric acid, acrylamide, N-vinylpyrrolidone, N-vinyl caprolactam, acrylonitrile or a mixture thereof.
또한, 상기 라디칼 개시제는 벤조인메틸에테르, 벤조인이소프로필에테르, 아니소인메틸에테르, 벤조인 또는 벤질케탈인 것을 특징으로 한다.In addition, the radical initiator is characterized in that benzoin methyl ether, benzoin isopropyl ether, anisoin methyl ether, benzoin or benzyl ketal.
또한, 상기 가교제는 디아크릴레이트계 가교제, 트리아크릴레이트계 가교제, 아지리딘계 가교제 또는 에폭시계 가교제인 것을 특징으로 한다.The crosslinking agent may be a diacrylate crosslinking agent, a triacrylate crosslinking agent, an aziridine crosslinking agent, or an epoxy crosslinking agent.
또한, 본 발명은 호모폴리머로 중합시 유리전이온도가(Tg)가 0℃ 이하인 연성 아크릴계 모노머 70 ~ 99 중량% 및 호모폴리머로 중합시 유리전이온도가(Tg)가 80℃ 이상인 경성 아크릴게 모노머 1 ~ 30 중량%로 이루어지는 아크릴계 모노머 100중량부; 라디칼 개시제 0.1 ~ 5 중량부; 및 가교제 0.01 ~ 20 중량부를 혼합하여 점착제 조성물을 제조하는 단계; 상기 점착제 조성물을 베이킹 필름 상에 코팅하는 단계; 및 상기 베이킹 필름 위에 코팅된 점착제 조성물을 자외선 경화기에서 경화시키는 단계를 포함하는 점착시트의 제조방법을 제공한다.In addition, the present invention is 70 ~ 99% by weight of a flexible acrylic monomer having a glass transition temperature (Tg) of 0 ° C. or less upon polymerization with a homopolymer, and a hard acrylic crab monomer having a glass transition temperature (Tg) of 80 ° C. or more during polymerization with a homopolymer. 100 parts by weight of an acrylic monomer composed of 1 to 30% by weight; 0.1 to 5 parts by weight of radical initiator; And 0.01 to 20 parts by weight of a crosslinking agent to prepare an adhesive composition. Coating the pressure-sensitive adhesive composition on a baking film; And it provides a method for producing a pressure-sensitive adhesive sheet comprising the step of curing the pressure-sensitive adhesive composition coated on the baking film in an ultraviolet curing machine.
또한, 상기의 제조방법에 의하여 제조된 점착시트를 제공한다.In addition, it provides an adhesive sheet prepared by the above production method.
또한, 상기의 점착시트를 이용하여 제조된 디스플레이를 제공한다.In addition, the present invention provides a display manufactured using the adhesive sheet.
본 발명 광학필터용 점착제 조성물에 의하면, 오토 클레이브에 의한 고온·고압 처리를 필요로 하지 않고, 실온에서 광학 필터 등의 적층체의 제조가 가능하며, 본 발명의 광학필터용 점착제 조성물을 이용하여 제조된 점착시트 및 광학필터는 판 어긋남이 잘 일어나지 않고, 우수한 내충격성, 박리강도 및 전단력을 가질 뿐만 아니라, 고온 또는 고습하에서 가시영역에 특정한 흡수가 나타나 착색 또는 변색되어 보이지 않고 크랙 발생에 의해 광학특성이 저하되지 않는다. According to the adhesive composition for optical filters of this invention, manufacture of laminated bodies, such as an optical filter, is possible at room temperature, without the need for the high temperature and high pressure process by an autoclave, and is manufactured using the adhesive composition for optical filters of this invention. The adhesive sheet and the optical filter do not easily exhibit plate displacement, have excellent impact resistance, peeling strength and shearing force, and exhibit specific absorption in the visible region under high temperature or high humidity, so that they are not colored or discolored and are not visible. This does not degrade.
본 발명은 호모폴리머로 중합시 유리전이온도(Tg)가 0℃ 이하인 연성 아크릴계 모노머 및 호모폴리머로 중합시 유리전이온도(Tg)가 80℃ 이상인 경성 아크릴계 모노머로 이루어지는 아크릴계 모노머; 라디칼 개시제; 가교제를 포함하여 이루어지는 것을 특징으로 한다. The present invention is an acrylic monomer consisting of a flexible acrylic monomer having a glass transition temperature (T g ) of 0 ° C. or less upon polymerization with a homopolymer and a rigid acrylic monomer having a glass transition temperature (T g ) of 80 ° C. or more during polymerization with a homopolymer; Radical initiators; It comprises a crosslinking agent.
연성 아크릴계 모노머로는 부틸아크릴레이트, 부틸메타크릴레이트, 헥실아크릴레이트, 헥실메타크릴레이트, n-옥틸아크릴레이트, n-옥틸메타크릴레이트, 이소옥틸아크릴레이트, 이소옥틸메타크릴레이트, 2-에틸헥실아크릴레이트, 2-에틸헥실 메타크릴레이트, 이소노닐아크릴레이트 또는 이소노닐메타크릴레이트가 바람직하게 사용될 수 있으며, 이들은 단독으로 또는 2종 이상을 혼용하여 사용할 수 있다. 아크릴계 모노머 중 연성 아크릴계 모노머의 함량이 70 중량% 미만이면 Tg가 높아져서 표면 경도가 높아지고 내충격성이 감소하며, 헤이즈(haze)가 발생하는 문제가 있다. 또한, 그 함량이 99 중량%를 초과하면 Tg가 지나치게 낮아져서 내스크레치성이 떨어지는 문제가 있어 바람직하지 못하다. 본 발명에서는 중합시 유리전이온도가 0℃ 이하인 것을 사용하는데, 유리전이온도의 온도가 0℃보다 높게 되면, 제조된 점착시트의 경도가 매우 올라가 내충격성이 감소할뿐 아니라, 상온에서 끈적임이 거의 사라져 점착시트로서 기능을 수행할 수 없다.As the soft acryl-based monomer, butyl acrylate, butyl methacrylate, hexyl acrylate, hexyl methacrylate, n-octyl acrylate, n-octyl methacrylate, isooctyl acrylate, isooctyl methacrylate, 2-ethyl Hexyl acrylate, 2-ethylhexyl methacrylate, isononyl acrylate or isononyl methacrylate may be preferably used, and these may be used alone or in combination of two or more thereof. If the content of the soft acrylic monomer in the acrylic monomer is less than 70% by weight, the Tg is increased to increase the surface hardness, impact resistance is reduced, there is a problem that haze (haze) occurs. In addition, when the content is more than 99% by weight, the Tg is too low and there is a problem that the scratch resistance is poor, which is not preferable. In the present invention, the glass transition temperature is used when the polymerization is 0 ℃ or less, when the temperature of the glass transition temperature is higher than 0 ℃, the hardness of the prepared pressure-sensitive adhesive sheet is very high, not only the impact resistance is reduced, it is almost sticky at room temperature It disappears and cannot function as an adhesive sheet.
경성 아크릴계 모노머로는 아크릴산, 메타크릴산, 말레인산, 푸마르산, 아크릴아미드, N-비닐피롤리돈, N-비닐 카프로락탐 또는 아크릴로니트릴이 바람직하게 사용될 수 있으며, 이들은 단독으로 또는 2종 이상을 혼용하여 사용할 수 있다. 아크릴계 모노머 중 경성 아크릴계 모노머의 함량이 1 중량% 미만이면 Tg가 너무 낮아져서 점착 내구성이 감소하는 문제가 있고, 그 함량이 30 중량%를 초과하면 초기 점착력이 감소하고 Haze 값이 크게 증가하는 문제가 있어 바람직하지 못하다. 본 발명에서는 중합시 유리전이온도가 80℃ 이상인 것을 사용하는데, 중합시 유리전이온도가 80℃ 미만인 경우, 연질 정도가 매우 심한 점착시트가 제조되어, 재작업성이 불리할 뿐 아니라, PDP가 구동되는 높은온도에서 점착시트에 변형이 오게되어, PDP용 Glass에서 자칫 분리될 우려가 있다. As the hard acrylic monomer, acrylic acid, methacrylic acid, maleic acid, fumaric acid, acrylamide, N-vinylpyrrolidone, N-vinyl caprolactam or acrylonitrile may be preferably used, and these may be used alone or in combination of two or more thereof. Can be used. If the content of the hard acrylic monomer in the acrylic monomer is less than 1% by weight Tg is too low, there is a problem that the adhesive durability is reduced, if the content exceeds 30% by weight there is a problem that the initial adhesive force is reduced and the Haze value is greatly increased Not desirable In the present invention, a glass transition temperature of 80 ° C. or more is used in the polymerization. When the glass transition temperature is less than 80 ° C. in the polymerization, an adhesive sheet having a very high degree of softness is manufactured, and the reworkability is disadvantageous, and the PDP is driven. At high temperature, the adhesive sheet is deformed, and there is a fear of being separated from the glass for PDP.
라디칼 개시제는 아크릴계 모노머의 중합을 위해 사용되는데, 상용화된 라디칼 개시제들이 사용될 수 있다. 바람직한 라디칼 개시제로는 광개시제로서, 벤조인메틸에테르, 벤조인이소프로필에테르, 아니소인메틸에테르, 벤조인 또는 벤질케탈이 바람직하게 사용될 수 있으며, 이들은 단독으로 또는 2종 이상을 혼용하여 사용할 수 있다.Radical initiators are used for the polymerization of acrylic monomers, and commercialized radical initiators may be used. As a preferable radical initiator, benzoin methyl ether, benzoin isopropyl ether, anisoin methyl ether, benzoin or benzyl ketal can be used preferably, These can be used individually or in mixture of 2 or more types.
라디칼 개시제는 상기 아크릴계 모노머 100 중량부에 대하여 0.1 ~ 5 중량부를 사용하는 것이 바람직하며, 0.1 중량부 미만이면 미반응 모노머가 잔존하는 문제가 있고, 그 함량비가 5 중량부를 초과하면 분자량이 낮아지고, 재현성이 떨어지는 문제가 있어 바람직하지 못하다.The radical initiator is preferably used 0.1 to 5 parts by weight based on 100 parts by weight of the acrylic monomer, if less than 0.1 parts by weight there is a problem that the unreacted monomers remain, if the content ratio exceeds 5 parts by weight, the molecular weight is lowered, It is not preferable because of the problem of poor reproducibility.
또한, 가교제는 상기 연성 아크릴계 모노머 및 경성 아크릴계 모노머를 중합시킴에 의해 얻어지는 아크릴레이트계 공중합체를 가교시키기 위해 첨가되는 것으로서, 예를 들어 헥산디올디아크릴레이트, 에틸렌글리콜디아크릴레이트, 디에틸렌글리콜디아크릴레이트 및 트리에틸렌글리콜디아크릴레이트, 프로필렌글리콜디아크릴레이트, 디프로필렌글리콜디아크릴레이트, 트리프로필렌디아크릴레이트 등을 포함하는 디아크릴레이트계 가교제, 트리아크릴레이트계 가교제, 아지리딘계 가교제, 에폭시계 가교제 등을 사용할 수 있으나, 이에 한정하는 것은 아니다. 가교제는 상기 아크릴계 모노머 100 중량부에 대하여 0.01 ~ 20 중량부를 사용하는 것이 바람직하며, 0.01 중량부 미만이면 시트가 유연해져서 작업성이 떨어지는 문제가 있고, 그 함량비가 20중량부를 초과하면 딱딱해져서 내충격성이 감소하고, 절단 공정에 문제가 있어 바람직하지 못하다.In addition, the crosslinking agent is added to crosslink the acrylate copolymer obtained by polymerizing the soft acrylic monomer and the hard acrylic monomer, for example, hexanediol diacrylate, ethylene glycol diacrylate, diethylene glycol di Diacrylate crosslinking agent containing triacrylate glycol triacrylate, propylene glycol diacrylate, dipropylene glycol diacrylate, tripropylene diacrylate, etc., triacrylate crosslinking agent, aziridine crosslinking agent, epoxy type Crosslinking agents and the like can be used, but are not limited thereto. It is preferable to use 0.01-20 weight part with respect to 100 weight part of said acryl-type monomers, and when it is less than 0.01 weight part, there exists a problem that a sheet becomes soft and workability falls, and when the content ratio exceeds 20 weight part, it becomes hard and impact resistance. This decreases and there is a problem in the cutting process, which is undesirable.
상기와 같은 구성성분으로 이루어진 점착제 조성물의 25℃에서의 점도는 500~3000Cps인 것이 코팅 작업성 측면에서 바람직한데, 점도가 500미만인 경우 코팅성이 나빠지며, 3000을 초과하면 고속 코팅 작업이 어려워지기 때문에 바람직하지 못하기 때문이다. The viscosity at 25 ° C. of the pressure-sensitive adhesive composition composed of the above components is preferably 500 to 3000 Cps in terms of coating workability. If the viscosity is less than 500, the coating property is deteriorated. This is because it is not preferable.
본 발명의 광학필터용 점착제 조성물을 이용하여 점착시트를 제조하는 방법은 다음과 같다.The method of manufacturing an adhesive sheet using the pressure-sensitive adhesive composition for an optical filter of the present invention is as follows.
본 발명에 따른 상기의 점착시트 조성물을 제조한 후, 상기 점착제 조성물을 배킹필름 상에 코팅하고, 상기 배킹필름 위에 코팅된 점착제 조성물을 자외선 경화기에서 경화시켜 제조할 수 있다. 또한 상기의 방법 이외에도 공지된 여러가지 다양한 방법에 의하여 제조하는 것이 가능하다.After preparing the pressure-sensitive adhesive sheet composition according to the present invention, the pressure-sensitive adhesive composition may be coated on a backing film, and the pressure-sensitive adhesive composition coated on the backing film may be prepared by curing in an ultraviolet curing machine. In addition to the above method, it is possible to manufacture by various known methods.
일반적으로 종래의 점착시트의 경우 경도가 높으면 판어긋남이 감소하기는 하지만, 접착의 경우 탈착이 어렵게 된다. 그러나 상기와 같은 방법에 의하여 제조된 본 발명에 따른 점착시트에 의하면, 높은 경도와 양호한 내충격성, 접착성을 동시에 가지며, 200℃에서 재작업이 가능하다. 접착제의 경우 한번 부착하면 탈착이 어려워, 생산 수율이 낮지만, 본 발명의 점착시트는 초기의 우수한 재작업성 및 작업후의 높은 내구성과 치수안정성, 접착성을 갖는다. 또한, 고온 또는 고습하에서 벌어짐 현상이 없고, 가시영역에 특정한 흡수가 나타나 착색되거나 변색되어 보이지 않고, 크랙 발생에 의해 광학특성이 저하되지 않는다.In general, in the case of a conventional pressure-sensitive adhesive sheet, the hardness is reduced, but the plate shift is reduced, but in the case of adhesion it becomes difficult to detach. However, according to the pressure-sensitive adhesive sheet according to the present invention prepared by the above method, it has a high hardness and good impact resistance, adhesiveness at the same time, it is possible to rework at 200 ℃. In the case of the adhesive, once attached, it is difficult to detach and produce a low yield. However, the adhesive sheet of the present invention has excellent initial reworkability and high durability, dimensional stability and adhesiveness after work. In addition, there is no spreading phenomenon under high temperature or high humidity, specific absorption appears in the visible region, coloration or discoloration does not appear, and optical characteristics are not deteriorated by crack generation.
본 발명의 광학필터용 점착제 조성물 및 점착시트는 각종 용도로 이용 가능 하다. 예를 들면, 투명 창 재료, 액정(LCD) 표시, 플라즈마 디스플레이(PDP) 표시 등의 평면형 화상 표시장치, 내충격성, 균열 방지, 진동 흡수 등이 요구되는 표면 구조의 구성 부재로서 사용할 수 있다. The pressure-sensitive adhesive composition and pressure-sensitive adhesive sheet for an optical filter of the present invention can be used for various purposes. For example, it can be used as a constituent member of a planar image display device such as a transparent window material, a liquid crystal (LCD) display, a plasma display (PDP) display, a surface structure requiring impact resistance, crack prevention, vibration absorption, and the like.
바람직한 용도의 일례로서, 디스플레이 패널의 전면측에 접합시키는 광학 필터에 있어서, 디스플레이 패널의 패널 전면 또는 해당 패널 전면에 적층된 글라스 필터의 모듈 전면에 접합시키기 위한 점착층으로서 사용될 수 있고, 또한 광학 필터를 구성하는 각 층간을 접합시키기 위한 점착층으로서 사용될 수 있다. As an example of a preferable use, in the optical filter bonded to the front side of a display panel, it can be used as an adhesive layer for bonding to the front surface of a panel of a display panel, or the module front surface of the glass filter laminated | stacked on the said panel front, and also an optical filter It can be used as a pressure-sensitive adhesive layer for bonding each layer constituting the.
본 발명은 앞서 설명한 바와 같은 점착제 조성물을 이용하여 제조되는 디스플레이용 광학 필터를 제공한다. 본 발명의 디스플레이용 광학 필터는 디스플레이 패널의 전면측, 즉 시청자측에 접합시키는 디스플레이용 광학 필터로서, 예를 들면 플라즈마 디스플레이(PDP)의 패널 전면측에 직접 접합시키는 데 사용할 수 있다. 상기 광학 필터는, 예를 들어 상기 본 발명의 투명 점착제 조성물을 이용하여 투명 유리 및 합성수지 필름을 접합시킴에 의해 얻어질 수 있다. The present invention provides an optical filter for display manufactured using the pressure-sensitive adhesive composition as described above. The display optical filter of the present invention is a display optical filter which is bonded to the front side of the display panel, that is, the viewer side, and can be used, for example, to be directly bonded to the panel front side of the plasma display (PDP). The optical filter can be obtained, for example, by bonding the transparent glass and the synthetic resin film using the transparent pressure-sensitive adhesive composition of the present invention.
본 명세서에 있어서 디스플레이용 광학 필터를 설명할 때 「전면측」또는 「전면」이라고 하면 시청자측 또는 시청자측의 면을 의미하고, 「이면측」또는 「이면」이란 시청자측과 반대측 또는 시청자측과는 반대측의 면을 의미한다. 또한, 「디스플레이 패널」은 플라즈마 디스플레이(「PDP」라고 함) 외에 액정 디스플레이, 유기 EL 디스플레이, CRT 디스플레이, 그 밖의 디스플레이를 포함하는 의미이다.In the present specification, when describing the optical filter for display, the term "front side" or "front" means the viewer side or the side of the viewer side, and the "back side" or "back side" means the opposite side of the viewer side or the viewer side. Means the opposite side. In addition, a "display panel" is meant to include a liquid crystal display, an organic EL display, a CRT display, and other displays other than a plasma display ("PDP").
이하, 본 발명을 구체적으로 설명하기 위해 실시예를 들어 상세하게 설명하 기로 한다. 그러나, 본 발명에 따른 실시예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 상술하는 실시예들에 한정되는 것으로 해석되어서는 안된다. 본 발명의 실시예들은 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다. Hereinafter, the present invention will be described in detail with reference to Examples. However, embodiments according to the present invention can be modified in many different forms, the scope of the present invention should not be construed as limited to the embodiments described below. The embodiments of the present invention are provided to more completely explain the present invention to those skilled in the art.
실시예Example 1 One
연성 아크릴계 모노머로서 2-에틸헥실아크릴레이트 90 중량부, 경성 아크릴계 모노머로서 아크릴산 10 중량부, 열개시제로서 벤조일퍼옥사이드 0.8 중량부를 이용하여 고분자 벌크 수지를 1차 제조하고, 여기에 라디칼 개시제로서 광개시제인 벤조인메틸에테르 1 중량부, 가교제로서 헥산디올디아크릴레이트 8 중량부를 혼합하여 조성물을 수득하고, 이를 이형필름으로서 PET필름 상에 1mm의 두께로 코팅한 후, 출력 100mW의 자외선을 2분간 조사하여 경화시켜 본 발명에 따른 점착시트를 수득하였다.A polymer bulk resin is primarily prepared using 90 parts by weight of 2-ethylhexyl acrylate as a soft acrylic monomer, 10 parts by weight of acrylic acid as a hard acrylic monomer, and 0.8 parts by weight of benzoyl peroxide as a thermal initiator, and is a photoinitiator as a radical initiator. 1 part by weight of benzoin methyl ether and 8 parts by weight of hexanediol diacrylate as a crosslinking agent were mixed to obtain a composition, which was coated on a PET film with a thickness of 1 mm as a release film, and then irradiated with ultraviolet light having an output of 100 mW for 2 minutes. Curing to obtain an adhesive sheet according to the present invention.
실시예Example 2 2
연성 아크릴계 모노머로서 2-에틸헥실아크릴레이트 89 중량부, 경성 아크릴계 모노머로서 아크릴산 11 중량부, 열개시제로서 벤조일퍼옥사이드 0.5 중량부를 이용하여 고분자 벌크 수지를 1차 제조하고, 여기에 라디칼 개시제로서 광개시제인 벤조인메틸에테르 1 중량부, 가교제로서 헥산디올디아크릴레이트 10 중량부를 혼합하여 조성물을 수득하고, 이를 이형필름으로서 PET필름 상에 1mm의 두께로 코팅한 후, 출력 100mW의 자외선을 2분간 조사하여 경화시켜 본 발명에 따른 점착시트를 수득하였다.A polymer bulk resin is primarily prepared using 89 parts by weight of 2-ethylhexyl acrylate as a soft acrylic monomer, 11 parts by weight of acrylic acid as a hard acrylic monomer, and 0.5 parts by weight of benzoyl peroxide as a thermal initiator, and is a photoinitiator as a radical initiator. 1 part by weight of benzoin methyl ether and 10 parts by weight of hexanediol diacrylate as a crosslinking agent were mixed to obtain a composition, which was coated on a PET film with a thickness of 1 mm as a release film, and then irradiated with ultraviolet light having an output of 100 mW for 2 minutes. Curing to obtain an adhesive sheet according to the present invention.
실시예Example 3 3
연성 아크릴계 모노머로서 2-에틸헥실아크릴레이트 89 중량부, 경성 아크릴계 모노머로서 아크릴산 11 중량부, 열개시제로서 벤조일퍼옥사이드 0.5 중량부를 이용하여 고분자 벌크 수지를 1차 제조하고, 여기에 라디칼 개시제로서 광개시제로서 벤조인메틸에테르 1 중량부, 가교제로서 헥산디올디아크릴레이트 8 중량부를 혼합하여 조성물을 수득하고, 이를 이형필름으로서 PET필름 상에 1mm의 두께로 코팅한 후, 출력 100mW의 자외선을 2분간 조사하여 경화시켜 본 발명에 따른 점착시트를 수득하였다. A polymeric bulk resin is prepared primarily using 89 parts by weight of 2-ethylhexyl acrylate as a soft acrylic monomer, 11 parts by weight of acrylic acid as a hard acrylic monomer, and 0.5 parts by weight of benzoyl peroxide as a thermal initiator, and as a photoinitiator as a radical initiator. 1 part by weight of benzoin methyl ether and 8 parts by weight of hexanediol diacrylate as a crosslinking agent were mixed to obtain a composition, which was coated on a PET film with a thickness of 1 mm as a release film, and then irradiated with ultraviolet light having an output of 100 mW for 2 minutes. Curing to obtain an adhesive sheet according to the present invention.
비교예Comparative example 1 One
일반적으로 사용되는 델로(Delo)사 또는 트리본드(Threebond)사의 실란트(sealant)를 이용하여 이를 이형필름으로서 PET필름 상에 1mm의 두께로 코팅한 후, 출력 100mW의 자외선을 2분간 조사하여 경화시켜 본 발명에 따른 점착시트를 수득하였다. Using a sealant of Delo or Threebond, which is commonly used, it is coated on a PET film with a thickness of 1mm as a release film, and then cured by irradiating UV light at 100mW for 2 minutes. An adhesive sheet according to the present invention was obtained.
비교예2Comparative Example 2
기존에 사용되는 에폭시계열 접착제를 이용하여 테스트를 하였다. 20um 내외 로 코팅한 후 접합하여 180도에서 3시간 경화하였다.The test was performed using an epoxy-based adhesive used in the past. After coating to around 20um was bonded and cured at 180 degrees for 3 hours.
비교예3Comparative Example 3
기존에 사용되는 범용 아크릴계 점착제를 이용하여 테스트를 하였다. 상기 점착제는 25um로 코팅된 열가소성 점착제로, 톨루엔, 에틸아세테이트 (50/50) 혼합용매에 벤조일퍼옥사이드 1 중량부로 부틸아크릴레이트 25 중량부, 2-에틸헥실아크릴레이트 60 중량부, 아크릴산 5 중량부, 메틸아크릴레이트 10중량부, 커플링제 0.2 중량부를 첨가하여 50~70℃에서 8시간 중합하여 점착제를 수득하고, 이를 이형필름으로서 PET필름 상에 120um의 두께로 코팅한 후, 110℃ 에서 3분간 건조한 후 이를 적층하여 투명 점착시트를 수득하였다.The test was performed using a conventional acrylic adhesive. The pressure-sensitive adhesive is a 25um coated thermoplastic pressure-sensitive adhesive, 25 parts by weight of butyl acrylate, 60 parts by weight of 2-ethylhexyl acrylate, 5 parts by weight of acrylic acid in toluene, ethyl acetate (50/50) mixed solvent with 1 part by weight of benzoyl peroxide. , 10 parts by weight of methyl acrylate, 0.2 parts by weight of a coupling agent was added to polymerize at 50-70 ° C. for 8 hours to obtain a pressure-sensitive adhesive, which was coated on a PET film with a thickness of 120 μm as a release film, followed by 3 minutes at 110 ° C. After drying, it was laminated to obtain a transparent adhesive sheet.
상기와 같은 방법으로 수득된 점착시트의 물성을 다음과 같은 방법으로 테스트하였다.The physical properties of the pressure-sensitive adhesive sheet obtained by the above method was tested by the following method.
박리강도Peel strength
300mm/min 속도로 측정하여 최고, 최저값을 제외한 그 평균값을 나타냈다. 시편은 1in*10cm(폭/길이)로 재단하여 STN Glass에 1kg하중으로 10cm/min합판하여 제조하였다. Measured at 300mm / min speed, the average value was obtained except for the highest and lowest values. The specimens were cut into 1in * 10cm (width / length) and manufactured by plywood 10cm / min with 1kg load on STN Glass.
이때 측정 장비는 TA사의 Texture Analyzer XT plus이다.The measurement equipment is TA's Texture Analyzer XT plus.
전단강도Shear strength
12mm/min 속도로 측정하여 최고값을 나타냈다. The maximum value was obtained by measuring at a speed of 12 mm / min.
이때 측정 장비는 TA사의 Texture Analyzer XT plus이다.The measurement equipment is TA's Texture Analyzer XT plus.
점착제 경도Adhesive hardness
Asker C/A로 적층 두께가 10mm이상으로 하여 테스트하였다.The test was performed with a thickness of 10 mm or more by Asker C / A.
투과도Transmittance
이때 측정 장비는 Murakami社의 HM-150이다.The measuring instrument is Murakami's HM-150.
UVUV 내구성 durability
Q-panel Lab Product사의 QUV를 이용하여, UV 내구성 테스트를 실시하였다. UV Lamp는 UVA-340 Lamp를 사용하였으며, 파장 범위는 310nm~340nm로 조절하였으며, QUV 내부온도는 60℃로 일정하게 유지하였다. 시간은 50h 노화를 진행 후 UV 분광광도계 측정을 통해서 그 값의 변화를 측정하였다.UV durability test was conducted using QUV of Q-panel Lab Product. UV Lamp used UVA-340 Lamp, the wavelength range was adjusted to 310nm ~ 340nm, QUV internal temperature was kept constant at 60 ℃. After 50 hours of aging, the change of the value was measured through UV spectrophotometer measurement.
이 때 분광광도계는 시중에서 사용되는 일반적인 분광광도계를 기본으로 한다.In this case, the spectrophotometer is based on a general spectrophotometer used in the market.
겔 함량Gel content
에틸 아세테이트 용매에 3일간 방치하여 얻어지는 Gel 함량을 측정하여 기재 하였다.Gel content obtained by standing in ethyl acetate solvent for 3 days was measured and described.
내구성durability
80℃, 90% 항온항습기에서 500hr 동안 벌어짐을 테스트하였다.Opening was tested for 500hr at 80 ° C, 90% thermohygrostat.
재작업성Reworkability
투명패드가 합판된 PDP용 광학필터를 PDP용 Glass에 라미네이팅한 후, 80℃, 90% 항온항습기에 500hr 방치 후, 투명패드가 합판된 PDP용 광학필터를 손으로 떼어 내어서 잔사정도를 확인하였다.After laminating the PDP optical filter on which the transparent pad was laminated on the glass for PDP, and leaving it at 80 ° C and 90% in a constant temperature and humidity chamber for 500hr, the PDP optical filter on which the transparent pad was laminated was removed by hand to check the residue. .
(◎ : 잔사 10%이하, ○ : 잔사 20%이하, △:잔사 30%이하, X : 30%이상 또는 광학필터 파손)(◎: residue 10% or less, ○: residue 20% or less, △: residue 30% or less, X: 30% or more, or optical filter damage)
실시예는 용매를 함유하지 않는 3차원 가교 중합체로서 투명한 겔을 포함하고 겔 함량이 95 중량％ 이상으로 나타났으며, 경도(Asker C)가 60 이상인 것으로 측정되었다.The example was a three-dimensional crosslinked polymer containing no solvent, containing a transparent gel, having a gel content of 95% by weight or more, and a hardness (Asker C) of 60 or more.
또한, 실시예들의 점착시트는 높은 경도에도 불구하고 점착력이 우수하였다. 비교예 3의 투명 점착시트는 너무 소프트하여 재단이 어려웠고, 상온에서는 10kg의 글라스 필터(Glass Filter)의 부착 후 떨어지지 않았으나, 고온에서 유리와 분리되어 내구성이 떨어진다.In addition, the pressure-sensitive adhesive sheet of the embodiments was excellent in adhesive strength despite the high hardness. The transparent adhesive sheet of Comparative Example 3 was too soft to be difficult to cut, and was not dropped after attachment of a glass filter of 10 kg at room temperature, but separated from glass at a high temperature, thereby inferior in durability.
또한 본 발명의 실시예는 우수한 재작업성을 가지며, 피착제 면에 잔사를 남기지 않는 특징이 있다. 또한, 제조 공정중에 용매를 사용하지 않는 관계로 휘발성 유기화합물과는 아무런 관계가 없다. In addition, embodiments of the present invention has excellent reworkability, and is characterized by leaving no residue on the surface of the adherend. In addition, there is no relationship with the volatile organic compound because no solvent is used in the manufacturing process.
본 발명의 실시예는 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 본 발명의 범위에 속할 수 있음을 이해하여야 한다. Since the embodiments of the present invention are only the most preferred embodiments of the present invention and do not represent all of the technical ideas of the present invention, various equivalents and modifications that may be substituted for them at the time of the present application may be used. It should be understood that they may fall within the scope.
Claims (9)