KR20090106263A - Colorant composition for heat shielding film containing near infrared adsorption dyes - Google Patents
Colorant composition for heat shielding film containing near infrared adsorption dyes Download PDFInfo
- Publication number
- KR20090106263A KR20090106263A KR1020080031848A KR20080031848A KR20090106263A KR 20090106263 A KR20090106263 A KR 20090106263A KR 1020080031848 A KR1020080031848 A KR 1020080031848A KR 20080031848 A KR20080031848 A KR 20080031848A KR 20090106263 A KR20090106263 A KR 20090106263A
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- shielding film
- heat shielding
- absorbing dye
- infrared absorbing
- Prior art date
Abstract
Description
본 발명은 근적외선 흡수 염료를 함유한 열 차폐필름용 색재 조성물에 관한 것으로서, 더욱 상세하게는 본 발명은 폴리에스테르 수지에 가시광선 영역의 파장을 투과하고, 근적외선 영역의 파장을 선택적으로 차폐하고, 고온 안정성이 우수한 근적외선 흡수염료를 제조공정 단계 또는 별도의 마스터 배치 형태로 제공하여 제조함으로써, 종래 코팅방식의 필름보다 선택적인 근적외선 차폐효과가 우수하고, 염료의 균일한 염색이 가능한 열 차폐필름용 색재 조성물에 관한 것이다.The present invention relates to a color material composition for a heat shield film containing a near infrared absorbing dye, and more particularly, the present invention transmits the wavelength of the visible light region to the polyester resin, selectively shields the wavelength of the near infrared region, By providing a near-infrared absorbing dye with excellent stability in a manufacturing process step or in a separate master batch form, the selective near-infrared shielding effect is superior to that of the conventional coating method, and color material composition for heat shielding film which enables uniform dyeing of dyes. It is about.
폴리에스테르 필름은 우수한 화학적, 물리적 성질을 가지고 있기 때문에 고분자 가공제품으로 광범위하게 사용되고 있다. 특히, 폴리에틸렌테레프탈레이트 필름은 건축물, 자동차 등의 창유리 면에 부착됨으로써, 자외선 및 적외선을 차단하고 충격으로 유리가 파손될 경우 파편이 분산되지 않도록 보호하는 용도의 공업용 소재로서 이용되고 있다. Polyester films are widely used as polymer processed products because of their excellent chemical and physical properties. In particular, the polyethylene terephthalate film is used as an industrial material for the purpose of blocking the ultraviolet rays and infrared rays by being attached to the surface of the window glass of buildings, automobiles, and the like so as not to scatter the fragments when the glass is broken by the impact.
착색 폴리에스테르 필름을 이용한 윈도우 필름에 대하여는 대한민국 등록특허 제252022호에 폴리에스테르 필름에 염료 혼합물을 피복시켜 피막층을 형성하는 방법 이 개시되어 있는바, 상세하게는 1개 층의 착색 접착층을 가지는 접착필름에, 수성호료 용액 중 최소 1종류의 분산염료를 사용하여 분산시킨 분산액으로 구성되는 염료 혼합물을 피복시킨 피막층 형성방법을 제안하고 있다. Regarding the window film using a colored polyester film, a method of forming a coating layer by coating a dye mixture on a polyester film is disclosed in Korean Patent No. 252022. Specifically, an adhesive film having a colored adhesive layer of one layer is disclosed. A coating layer formation method is proposed which coats a dye mixture composed of a dispersion liquid dispersed using at least one dispersion dye in an aqueous paint solution.
또한, 대한민국 등록특허 제145057호에서는 마그네슘화합물을 0.1 내지 0.01 중량% 투입하고, 통상의 방법으로 축중합시킨 폴리에스테르 수지에 안트라퀴논계 염료를 착색제로 하여 전체 폴리에스테르 수지에 대하여, 100 내지 1000ppm 첨가한 폴리에스테르 수지와 착색제를 첨가하지 않은 폴리에스테르 수지를 일정비율로 혼합하고 이를 제막, 연신, 열처리하여 제조되는 이축 연신 폴리에스테르 필름을 공지하고 있다.In addition, in Korean Patent No. 145057, 0.1 to 0.01% by weight of a magnesium compound is added, and 100 to 1000 ppm of the total polyester resin is added to the polyester resin condensation-polymerized by a conventional method using an anthraquinone dye as a colorant. BACKGROUND ART A biaxially stretched polyester film produced by mixing a polyester resin and a polyester resin without adding a colorant at a constant ratio and forming, stretching, and heat treating the same is known.
미합중국 특허 제5,338,318호에서는 폴리에스테르 필름의 염색방법에 있어서, 캐리어로서, 글리세롤 트리아세테이트(Glycerol triacetate)를 사용하여 염색하고, 세정, 건조하는 연속식 염색방법이 개시되어 있다.U.S. Patent No. 5,338,318 discloses a continuous dyeing method of dyeing, washing and drying using a glycerol triacetate as a carrier in a dyeing method of a polyester film.
그러나, 상기의 방법은 분산성 염료 또는 용제형 염료를 사용하기 때문에 염색 속도가 느리고, 특히 짙은 색의 염색일 경우 폴리에스테르에 균일한 염색이 어려워, 다단계의 가공공정이 요구된다.However, since the above method uses a dispersible dye or a solvent type dye, the dyeing speed is slow, and in the case of dark dyeing, it is difficult to uniformly dye the polyester, and a multi-stage processing step is required.
이에, 본 발명자들은 폴리에스테르 수지 염색 방법을 개선하고, 나아가 가시광선 영역의 파장을 투과하고, 근적외선 영역의 파장을 선택적으로 차폐하는 근적외선 흡수염료를 사용하여 기능성이 부여된 폴리에스테르 필름을 제공하고자 노력한 결과, 상기 근적외선 흡수염료를 폴리에스테르 수지의 제조공정 단계 또는 별도의 마스터 배치 형태로 제공하여 제조함으로써, 종래 코팅방식의 필름보다 선택적인 근 적외선 차폐효과가 우수하고, 염료의 균일한 염색이 가능한 열 차폐 폴리에스테르 필름 제조를 확인함으로써, 본 발명을 완성하였다.Accordingly, the present inventors have tried to provide a polyester film imparted with functionality using a near-infrared absorbing dye which improves the polyester resin dyeing method, further transmits the wavelength in the visible light region and selectively shields the wavelength in the near infrared region. As a result, by providing the near-infrared absorbing dye in the manufacturing process step of the polyester resin or in the form of a separate master batch, the near-infrared shielding effect is superior to the conventional coating method film, the heat can be uniform dyeing The present invention was completed by confirming the shielding polyester film production.
본 발명의 목적은 폴리에스테르 수지에 근적외선 흡수 염료가 함유된 열 차폐필름용 색재 조성물을 제공하는 것이다.It is an object of the present invention to provide a color material composition for a heat shielding film containing a near infrared absorbing dye in a polyester resin.
본 발명의 다른 목적은 상기 근적외선 흡수염료를 폴리에스테르 수지 제조단계에 첨가하거나, 별도의 마스터 배치 형태로 폴리에스테르 수지와 혼합하여, 근적외선 차폐효율이 개선된 열 차폐필름용 색재 조성물 및 그를 이용하여 제조된 열 차폐필름을 제공하는 것이다.Another object of the present invention is to add the near-infrared absorbing dye to the polyester resin manufacturing step, or mixed with the polyester resin in the form of a separate master batch, the color material composition for heat-shielding film improved near-infrared shielding efficiency and manufactured using the same It is to provide a heat shield film.
상기 목적을 달성하기 위하여, 본 발명은 폴리에스테르 수지 100 중량부에, In order to achieve the above object, the present invention is 100 parts by weight of a polyester resin,
400∼780nm의 가시광선 영역의 파장을 투과하고, 780∼1500nm의 근적외선 영역의 파장을 선택적으로 차폐하는 근적외선 흡수염료 1 내지 15 중량부가 함유된 열 차폐필름용 색재 조성물을 제공한다. Provided is a color material composition for a heat shielding film containing 1 to 15 parts by weight of a near infrared absorbing dye that transmits a wavelength in a visible light region of 400 to 780 nm and selectively shields a wavelength in a near infrared region of 780 to 1500 nm.
이때, 상기 근적외선 흡수염료가 200 내지 350℃에서 열적 안정성을 가지며며, 디티올계 화합물, 디이모늄계 화합물, 프탈로시아닌계 화합물 및 나프탈로시아닌계 화합물로 이루어진 군에서 선택되는 1종 이상이다.In this case, the near-infrared absorbing dye has thermal stability at 200 to 350 ° C., and is at least one selected from the group consisting of dithiol compounds, dimonium compounds, phthalocyanine compounds, and naphthalocyanine compounds.
상기 근적외선 흡수염료가 투명 플라스틱 고내열성 수지 90∼98중량% 및 근적외선 흡수염료 2∼10중량%로 이루어진 마스터 배치 형태로 제공된다.The near infrared absorbing dye is provided in the form of a master batch consisting of 90 to 98% by weight of the transparent plastic high heat resistant resin and 2 to 10% by weight of the near infrared absorbing dye.
상기 투명 플라스틱 고내열성 수지는 폴리에스테르계 수지, 아크릴계 수지, 셀룰로오스계 수지, 폴리올레핀계 수지, 폴리염화비닐계수지, 페놀계 수지, 우레탄계 수지, 폴리카보네이트계 수지, 폴리에틸렌-2,6-나프탈레이트, 폴리에틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트 및 폴리카보네이트 수지로 이루어진 군에서 선택되는 1종 이상이다.The transparent plastic high heat resistance resin is polyester resin, acrylic resin, cellulose resin, polyolefin resin, polyvinyl chloride resin, phenol resin, urethane resin, polycarbonate resin, polyethylene-2,6-naphthalate, At least one selected from the group consisting of polyethylene terephthalate, polybutylene terephthalate and polycarbonate resin.
이때, 본 발명의 열 차폐필름용 색재 조성물에 의한 필름은 이축 연신 폴리에스테르 필름이며, 5%이하의 헤이즈 값을 갖는다.At this time, the film by the color material composition for heat shielding films of this invention is a biaxially stretched polyester film, and has a haze value of 5% or less.
나아가, 본 발명의 열 차폐필름용 색재 조성물에 의한 필름은 선택적인 근적외선 차폐효과가 우수하고, 염료의 균일한 염색으로 인하여 품질이 개선됨에 따라, 종래의 건축물 유리 또는 자동차 유리대체용 필름으로 유용하다.Furthermore, the film by the color material composition for heat shielding film of the present invention is excellent as a selective near-infrared shielding effect, and as the quality is improved due to the uniform dyeing of the dye, it is useful as a conventional building glass or automotive glass replacement film. .
본 발명은 폴리에스테르 수지에 고온 안정성이 우수하고, 가시광선 영역의 파장을 투과하고, 근적외선 영역의 파장을 선택적으로 차폐하는 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 제공할 수 있다.The present invention can provide a color material composition for a heat shielding film containing a near-infrared absorbing dye excellent in high temperature stability to a polyester resin, transmitting a wavelength in a visible light region and selectively shielding a wavelength in a near infrared region.
본 발명의 열 차폐필름용 색재 조성물은 상기 근적외선 흡수염료를 폴리에스테르 수지 제조단계에 첨가하거나, 별도의 마스터 배치 형태로 제공함으로써, 종래 코팅 방식의 열 차폐필름에 비하여 선택적인 근적외선 차폐효과가 우수하고, 염료의 균일한 염색이 가능하다.Coloring material composition for heat shielding film of the present invention by adding the near-infrared absorbing dye to the polyester resin manufacturing step, or provided in a separate master batch form, it is excellent in selective near-infrared shielding effect compared to the heat shielding film of the conventional coating method , Uniform dyeing of dye is possible.
본 발명의 열 차폐필름용 색재 조성물은 태양광 중 자외선과 열선의 투과를 차단하고, 가시광선만 선택적으로 투과시키고, 에너지 차단 및 갑작스러운 충격에 유리가 파괴되었을 때 보호할 수 있는 윈도우 필름용도에 적합하다.The color material composition for heat shielding film of the present invention blocks the transmission of ultraviolet rays and heat rays in sunlight, selectively transmits only visible light, and for window film use that can protect when glass is broken by energy blocking and sudden impact. Suitable.
이하, 본 발명을 상세히 설명하고자 한다.Hereinafter, the present invention will be described in detail.
본 발명은 폴리에스테르 수지 100 중량부에, 400∼780nm의 가시광선 영역의 파장을 투과하고, 780∼1500nm의 근적외선 영역의 파장을 선택적으로 차폐하는 근적외선 흡수염료 1 내지 15 중량부가 함유된 열 차폐필름용 색재 조성물을 제공한다. The present invention is a heat shielding film containing 1 to 15 parts by weight of a near-infrared absorbing dye, which transmits a wavelength in the visible light region of 400 to 780 nm and selectively shields the wavelength in the near infrared region of 780 to 1500 nm in 100 parts by weight of a polyester resin. It provides a coloring material composition for.
본 발명은 폴리에스테르 수지 100 중량부에 근적외선 흡수염료가 1 내지 15 중량부, 바람직하게는 2 내지 7 중량부가 함유되어 열 차폐 효과를 발현하는 것으로, 근적외선 흡수염료가 1 중량부 미만이면, 근적외선 흡수 능력이 저하되어 열 차폐 효과가 충분하지 않고, 15 중량부 초과이면, 염료의 재분산이 불가능한 문제가 있다. The present invention exhibits a heat shielding effect by containing 1 to 15 parts by weight, preferably 2 to 7 parts by weight of a near infrared absorbing dye, in 100 parts by weight of a polyester resin, and when the near infrared absorbing dye is less than 1 part by weight, absorbing near infrared rays If the capacity is lowered, the heat shielding effect is not sufficient, and if it is more than 15 parts by weight, there is a problem that redispersion of the dye is impossible.
본 발명에서 사용되는 근적외선 흡수염료는 폴리에스테르 수지와 혼합되어 고온의 용융 및 압출단계를 거침으로 고온에서의 열안정성이 요구된다. 이에, 본 발명의 근적외선 흡수염료는 200 내지 350℃에서 분해 또는 물성의 변화가 없는 열적 안정성을 갖는 염료를 사용한다. 따라서, 폴리에스테르 수지와의 반응과정 중 용융시 열에 의한 변형이 없으므로, 고온에서도 색소 파괴가 일어나지 않는다. The near-infrared absorbing dye used in the present invention is mixed with a polyester resin and undergoes a high temperature melting and extruding step, thereby requiring thermal stability at high temperature. Thus, the near-infrared absorbing dye of the present invention uses a dye having thermal stability without decomposition or change in physical properties at 200 to 350 ℃. Therefore, since there is no deformation due to heat during melting during the reaction with the polyester resin, pigment breakage does not occur even at a high temperature.
또한, 본 발명의 근적외선 흡수염료는 400∼780nm의 가시광선 영역의 파장을 투과하고, 780∼1500nm의 근적외선 영역의 파장을 선택적으로 차폐하는 것으로서, 바람직하게는 디티올계 화합물, 디이모늄계 화합물, 프탈로시아닌계 화합물 및 나프탈로시아닌계 화합물로 이루어진 군에서 선택되는 1종 이상을 사용한다. In addition, the near-infrared absorbing dye of the present invention transmits a wavelength in the visible light region of 400 to 780 nm and selectively shields the wavelength in the near infrared region of 780 to 1500 nm, and preferably a dithiol compound, a dimonium compound, and a phthalocyanine. At least one selected from the group consisting of a compound and a naphthalocyanine compound is used.
또한, 근적외선 흡수염료는 파장 850nm부근의 근적외선 차폐 성능을 보충하기 위해서 프탈로시아닌류 또는 디티올계 금속 착제 등의 공지된 흡수염료가 더 사용될 수 있으며, 내광성을 향상시키기 위하여, 벤조페논계 또는 벤조트리아졸계 등의 자외선 흡수염료가 사용될 수 있다. In addition, the near-infrared absorbing dye may further use a known absorbing dye such as phthalocyanines or dithiol-based metal complexes to supplement the near-infrared shielding performance near a wavelength of 850 nm, and to improve light resistance, such as benzophenone or benzotriazole-based UV absorbing dyes may be used.
본 발명의 열 차폐필름용 색재 조성물은 상기 근적외선 흡수염료를 폴리에스테르 제조공정 단계부터 첨가하여 제조하거나, 더욱 바람직하게는 별도의 마스터 배치 형태로 제공하여 제조함으로써, 종래 필름 상에 코팅하여 제조된 방식보다 성능 개선을 구현할 수 있다.The color material composition for heat shielding film of the present invention is prepared by adding the near-infrared absorbing dye from the polyester manufacturing process step, or more preferably by providing in a separate master batch form, the method prepared by coating on a conventional film Better performance can be achieved.
더욱 상세하게는, 바람직한 일 구현으로서, 폴리에스테르 수지에, 별도의 과정을 통해 투명 플라스틱 고내열성 수지 90∼98중량% 및 근적외선 흡수염료 2∼10중량%를 혼합하여 제조된 마스터 배치를 혼합하여 필름으로 제조하는 방법이 바람직하다.More specifically, as a preferred embodiment, the film by mixing a polyester batch, a master batch prepared by mixing 90 to 98% by weight of the transparent plastic high heat-resistant resin and 2 to 10% by weight of the near infrared absorbing dye through a separate process The method of manufacturing is preferable.
상기 투명 플라스틱 고내열성 수지로는 폴리에스테르계 수지, 아크릴계 수지, 셀룰로오스계 수지, 폴리올레핀계 수지, 폴리염화비닐계수지, 페놀계 수지, 우레탄계 수지, 폴리카보네이트계 수지, 폴리에틸렌-2,6-나프탈레이트, 폴리에틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트 및 폴리카보네이트 수지로 이루어진 군에서 선택되는 1종 이상이 사용될 수 있다.The transparent plastic high heat resistance resin is polyester resin, acrylic resin, cellulose resin, polyolefin resin, polyvinyl chloride resin, phenol resin, urethane resin, polycarbonate resin, polyethylene-2,6-naphthalate At least one selected from the group consisting of polyethylene terephthalate, polybutylene terephthalate and polycarbonate resin may be used.
이때, 상기 마스터배치의 원료조성물에 있어서, 필요에 따라 산화방지제, 열안정제, 점도조정제, 가소제, 색상개량제, 윤활제, 핵제, 자외선 안정제, 대전방지제, 산화방지제, 바인더 및 촉매 등의 첨가제를 더 사용할 수 있으며, 근적외선 흡수염 료 2∼10중량%를 유지하는 범위이내에서 첨가제의 함량은 조절될 수 있다.In this case, additives such as antioxidants, heat stabilizers, viscosity adjusters, plasticizers, color improvers, lubricants, nucleating agents, UV stabilizers, antistatic agents, antioxidants, binders, and catalysts may be further used in the raw material composition of the master batch. The content of the additive may be adjusted within the range of maintaining 2 to 10% by weight of the near infrared absorbing dye.
상기 근적외선 흡수염료 함유 마스터 배치 형태로 폴리에스테르에 적용됨으로써, 열 차폐필름에 근적외선 흡수염료의 분산성이 우수하여 염색의 얼룩이 생기지 않고 열 차폐 효율을 향상시킬 수 있다. 따라서, 균일한 품질의 열 차폐필름을 제공할 수 있고, 종래의 염색공정보다 공정이 단순하여 경제적인 효과를 구현할 수 있다. By applying to the polyester in the form of the near-infrared absorbing dye-containing master batch, the heat shielding film is excellent in the dispersibility of the near-infrared absorbing dye can improve the heat shielding efficiency without staining of the dye. Therefore, it is possible to provide a heat shield film having a uniform quality, and the process is simpler than the conventional dyeing process it can implement an economic effect.
또한, 바람직한 다른 구현으로서, 상기 근적외선 흡수염료를 폴리에스테르 수지 제조공정에 첨가하는 것이다. In another preferred embodiment, the near-infrared absorbing dye is added to a polyester resin manufacturing process.
상세하게는, 소정량의 근적외선 흡수염료를 폴리에스테르의 글리콜 성분과 동일한 글리콜, 예를 들면 에틸렌글리콜에 분산 또는 용해시켜 첨가하는 것이다. Specifically, a predetermined amount of near-infrared absorbing dye is added to the same glycol as the glycol component of the polyester, for example, by dispersing or dissolving it in ethylene glycol.
본 발명의 열 차폐필름용 색재 조성물에 의해 제조된 필름은 이축 연신 폴리에스테르 필름이며, 5%이하의 헤이즈 값을 갖는다.The film produced by the color material composition for heat shielding film of the present invention is a biaxially stretched polyester film, and has a haze value of 5% or less.
나아가, 본 발명의 열 차폐필름용 색재 조성물은 400∼780nm 가시광성 영역의 파장범위에서 50∼90%를 투과시키고, 780∼1500nm 근적외선 영역의 파장범위에서 70∼90% 차단시킨다.Furthermore, the color material composition for heat shielding film of the present invention transmits 50 to 90% in the wavelength range of 400 to 780 nm visible light region, and blocks 70 to 90% in the wavelength range of 780 to 1500 nm near infrared region.
도 1은 본 발명의 실시예 1에서 제조된 디티올계 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 이용한 필름의 분광학 스펙트럼 결과를 나타낸 것으로서, 가시광선 투과율이 70%이며, 780∼1500nm에서의 근적외선 차폐율이 90%로 확인되었다. FIG. 1 shows spectroscopic spectra of a film using a colorant composition for a heat shielding film containing a dithiol-based near-infrared absorbing dye prepared in Example 1 of the present invention, and has a visible light transmittance of 70%, at 780 to 1500 nm. NIR shielding rate was found to be 90%.
또한, 도 3은 본 발명의 실시예 1에서 제조된 열 차폐필름의 내열성을 측정한 결과, 250℃에서 중량감소 개시 온도로 확인되었다.In addition, Figure 3 was measured the heat resistance of the heat shield film prepared in Example 1 of the present invention, it was confirmed as the weight loss start temperature at 250 ℃.
또한, 도 2 및 도 4는 본 발명의 실시예 1에서 제조된 디이모늄계 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 이용한 필름의 분광학 스펙트럼 결과 및 내열성을 나타낸 결과로서, 가시광선 투과율이 70%이며, 780∼1500nm에서의 근적외선 차폐율은 90%로 확인되었으며, 280℃ 부근에서 중량감소가 개시됨으로서 내열성을 확인하였다. 2 and 4 show spectroscopic spectral results and heat resistance of a film using a colorant composition for a heat shielding film containing a dimonium-based near infrared absorbing dye prepared in Example 1 of the present invention. 70%, the near-infrared shielding rate at 780-1500nm was found to be 90% and the heat resistance was confirmed by the onset of weight reduction at around 280 ° C.
나아가, 본 발명의 열 차폐필름용 색재 조성물을 이용한 열 차폐필름은 태양광 중 자외선과 열선의 투과를 차단하고, 가시광선만 선택적으로 투과시키고, 에너지 차단 및 갑작스러운 충격에 유리가 파괴되었을 때 보호할 수 있는 윈도우 필름용도에 적합하다.Furthermore, the heat shielding film using the color material composition for the heat shielding film of the present invention blocks the transmission of ultraviolet rays and heat rays in sunlight, selectively transmits only visible light, and protects the glass when it is broken by energy blocking and sudden impact. It is suitable for window film use.
따라서, 본 발명의 열 차폐필름은 종래의 건축물 유리 또는 자동차 유리를 대체 사용할 수 있다.Therefore, the heat shielding film of the present invention can replace the conventional building glass or automotive glass.
이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 한다. Hereinafter, the present invention will be described in more detail with reference to Examples.
본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다. This embodiment is intended to illustrate the present invention in more detail, and the scope of the present invention is not limited to these examples.
<실시예 1 ∼ 3> <Examples 1-3>
단계 1: 근적외선 흡수염료 함유 마스터배치 제조Step 1: Preparation of Masterbatch Containing Near Infrared Absorption Dyes
근적외선 흡수염료(A, B, C), 점도조정제(D), 가소제(E), 대전방지제(F) 및 입자 상태의 고유점도 0.65dl/g인 폴리에틸렌테레프탈레이트(PET) 원료를 G라 하고, 하기 표1의 비율로 혼합하여 80℃에서 12시간 건조시킨 후 2단축 피이드 블록이 있는 T다이를 통해 260∼290℃범위에서 압출하고 60℃에서 냉각하여 마스터배치 1∼3을 제조하였다. Near-infrared absorbing dyes (A, B, C), viscosity modifiers (D), plasticizers (E), antistatic agents (F), and polyethylene terephthalate (PET) raw materials having an intrinsic viscosity of 0.65 dl / g in the particulate state are referred to as G, After mixing at a ratio of the following Table 1 and dried for 12 hours at 80 ℃ extruded in a range of 260 ~ 290 ℃ through a T-die with a two-short feed block and cooled at 60 ℃ to prepare a
단계 2: Step 2: 근적외선Near infrared ray 흡수염료 함유 필름 제조 Manufacture of absorbing dye-containing film
폴리에틸렌테레프탈레이트(PET) 수지 100 중량부에 대하여, 상기 단계 1에서 제조된 근적외선 흡수염료 함유 마스터배치 1∼3를 15 중량부를 혼합하여 공압출 다이를 통해 압출하고, 종방향으로 260℃에서 3배 연신, 횡방향으로 280℃에서 4배 연신하여, 평균 두께 25㎛의 폴리에스테르 필름을 얻었다. With respect to 100 parts by weight of polyethylene terephthalate (PET) resin, 15 parts by weight of the
<실험예 1>Experimental Example 1
상기 실시예 1 내지 3에서 제조된 폴리에스테르 필름에 대하여, 자외선ㆍ가시광선ㆍ근적외선 분광광도계(UV-Vis-NIR spectrophotometer)를 이용하여 300 내지 1500nm의 파장영역의 투과율 변화를 측정하였다.For the polyester films prepared in Examples 1 to 3, the change in transmittance in the wavelength region of 300 to 1500 nm was measured by using an ultraviolet, visible and near infrared spectrophotometer (UV-Vis-NIR spectrophotometer).
상기에서 살펴본 바와 같이, 본 발명은 폴리에스테르 수지에 고온 안정성이 우수하고, 가시광선 영역의 파장을 투과하고, 근적외선 영역의 파장을 선택적으로 차폐하는 근적외선 흡수염료를 함유하는 열 차폐필름용 색재 조성물을 제공함으로써, 보다 투명하고, 보다 효율적인 열 차폐필름을 구현할 수 있다.As described above, the present invention provides a color material composition for a heat shield film containing a near infrared absorbing dye having excellent high temperature stability in a polyester resin, transmitting a wavelength in a visible light region and selectively shielding a wavelength in a near infrared region. By providing a more transparent and more efficient heat shielding film can be realized.
본 발명의 열 차폐필름용 색재 조성물은 상기 근적외선 흡수염료를 폴리에스테르 수지 제조단계에 첨가하거나, 투명 플라스틱 고내열성 수지에 근적외선 흡수염료를 함유시킨 별도의 마스터 배치 형태로 제공함으로써, 종래 코팅 방식의 열 차폐필름에 비하여 내열성, 내습성, 내광성이 우수하고, 균일한 품질과 원가 절감, 구조의 단순화로 인한 기능성 필름 제조를 구현하였다.Coloring material composition for heat shielding film of the present invention by adding the near-infrared absorbing dye to the polyester resin manufacturing step, or in a separate master batch form containing the near-infrared absorbing dye in a transparent plastic high heat-resistant resin, heat of the conventional coating method Compared to the shielding film, it has excellent heat resistance, moisture resistance, and light resistance, and has realized functional film manufacturing due to uniform quality, cost reduction, and structure simplification.
본 발명의 열 차폐필름용 색재 조성물을 이용한 필름은 태양광 중 자외선과 열선의 투과를 차단하고, 가시광선만 선택적으로 투과시키므로, 건축물 유리 또는 자동차 유리용도에 유용하게 적용될 수 있다.The film using the color material composition for heat shielding film of the present invention blocks the transmission of ultraviolet rays and heat rays in sunlight, and selectively transmits only visible light, and thus can be usefully applied to building glass or automotive glass.
또한, 본 발명의 열 차폐 폴리에스테르 필름은 에너지 차단 및 갑작스러운 충격으로 유리가 파괴되었을 때 이를 보호할 수 있는 윈도우 필름용으로 적합하다.In addition, the heat shield polyester film of the present invention is suitable for a window film that can protect the glass when the glass is broken by an energy cut and a sudden impact.
이상에서 본 발명은 기재된 구체예에 대해서만 상세히 설명되었지만 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구 범위에 속함은 당연한 것이다. Although the present invention has been described in detail only with respect to the described embodiments, it will be apparent to those skilled in the art that various modifications and variations are possible within the technical scope of the present invention, and such modifications and modifications belong to the appended claims.
도 1은 본 발명의 디티올계 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 이용한 필름의 분광학 스펙트럼 결과이고, 1 is a spectroscopic spectral result of a film using a colorant composition for a heat shielding film containing a dithiol-based near infrared absorbing dye of the present invention,
도 2는 본 발명의 디이모늄계 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 이용한 필름의 분광학 스펙트럼 결과이고, 2 is a spectroscopy spectrum result of a film using a colorant composition for a heat shielding film containing a dimonium-based near infrared absorbing dye of the present invention,
도 3은 본 발명의 디티올계 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 이용한 필름의 내열성을 나타낸 그래프이고, 3 is a graph showing the heat resistance of the film using the color material composition for heat shielding film containing the dithiol-based near infrared absorbing dye of the present invention,
도 4는 본 발명의 디이모늄계 근적외선 흡수염료를 함유한 열 차폐필름용 색재 조성물을 이용한 필름의 내열성을 나타낸 그래프이다. Figure 4 is a graph showing the heat resistance of the film using the color material composition for heat shielding film containing the dimonium-based near infrared absorbing dye of the present invention.
Claims (9)