KR20090073680A - Dent remover of roll - Google Patents
Dent remover of roll Download PDFInfo
- Publication number
- KR20090073680A KR20090073680A KR1020070141695A KR20070141695A KR20090073680A KR 20090073680 A KR20090073680 A KR 20090073680A KR 1020070141695 A KR1020070141695 A KR 1020070141695A KR 20070141695 A KR20070141695 A KR 20070141695A KR 20090073680 A KR20090073680 A KR 20090073680A
- Authority
- KR
- South Korea
- Prior art keywords
- roll
- remover
- fiber coating
- polymer resin
- layer
- Prior art date
Abstract
Description
본 발명은 롤의 표면 이물질 제거용 리무버에 관한 것으로서, 더욱 상세하게는 전기아연도금공정 중에서 스트립(Strip) 진행시 여러 종류의 이물질 등이 스트립을 통해 롤에 부착되게 되는데, 이 롤에 부착된 이물질을 충분히 제거하면서 롤의 표면을 매끄럽게 코팅할 수 있도록 닥터 블레이드의 재질을 카본으로 변경함으로써 스트립의 불량을 줄이고자 하는 생산량을 증대할 수 있도록 함과 더불어 닥터 블레이드의 내구성을 향상시키기 위한 롤의 표면 이물질 제거용 리무버에 관한 것이다.The present invention relates to a remover for removing foreign substances on a surface of a roll, and more particularly, various kinds of foreign substances, etc. are attached to a roll through a strip during a strip during an electrogalvanizing process. By changing the material of the doctor blade to carbon so that the surface of the roll can be smoothly coated while removing enough, the foreign material on the surface of the roll to improve the durability of the doctor blade as well as increasing the yield to reduce the defect of the strip. It relates to a removal remover.
일반적으로 전기아연강판은 표면의 내식성을 위해 전기아연도금을 하며, 표면이 미려하여 전기제품 및 가전용으로 사용되고 있다. In general, the galvanized steel sheet is electro-galvanized for corrosion resistance of the surface, the surface is beautiful and is used for electrical appliances and household appliances.
이점 때문에 전기아연도금강판은 표면상태가 중요한 변수이며 표면 결함을 줄이기 위해 매우 엄격한 관리가 필요하다.Because of this, the surface condition is an important parameter for electrogalvanized steel sheets and requires very strict control to reduce surface defects.
그래서, 전기아연도금 공정 중에 작업자들에 의해 롤 표면이나 스트 립(Strip)에 묻어 있는 이물질을 제거할 수 없기 때문에 공정 중에 적당한 개수의 닥터 블레이드(doctor blade)를 설치하여 롤을 통해 나타나는 표면결함 등을 관리하였다.Therefore, foreign matters on the roll surface or strip cannot be removed by the workers during the electro-zinc plating process. Therefore, surface defects such as surface defects appearing through the roll by installing a proper number of doctor blades during the process are not provided. Was administered.
그런데, 기존의 스틸 재질의 닥터 블레이드는 우레탄(Urethand) 재질의 롤과 접촉시 상대적으로 강도가 큰 닥터 블레이드와의 마찰로 인해 롤의 거친 둘레면 부위에 걸려 롤을 파손시켰다.By the way, the conventional doctor blade made of steel caught on the rough circumferential surface of the roll due to friction with the doctor blade having a relatively high strength when contacted with a urethane (Urethand) roll to break the roll.
또한, 롤 걸림 파손을 방지하기 위해 개선된 고분자 폴리에스테르(Polyester) 닥터 블레이드가 사용되었다.In addition, an improved polymer polyester doctor blade was used to prevent roll jam breakage.
따라서, 종래 닥터 블레이드는 우레탄 재질의 롤과 접촉시 우레탄 재질의 롤을 보호하면서 약간의 표면결함(dent) 제거 효과는 있으나, 고분자 재질을 사용함에 따라 기존의 스틸 재질에 비해 경도가 부족하여 효과가 거의 없었다.Therefore, the conventional doctor blade has a slight surface defect removal effect while protecting the urethane roll when it comes in contact with the urethane roll. However, due to the use of a polymer material, the hardness is insufficient due to the lack of hardness. There was little.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출한 것으로, 본 발명의 목적은 닥터 블레이트의 재질을 카본섬유층으로 형성하여 롤의 표면을 카본화함에 따라 전기아연 도금 전후에 나타나는 롤의 표면에 이물질이 부착되는 것을 줄임과 더불어 카본섬유층 사이에 고분자수지층을 형성하여 카본섬유층 단독보다 강성도를 향상시킴에 따라 닥터 블레이드의 내구성을 향상시키고자 한 롤의 표면 이물질 제거용 리무버를 제공함에 있다.The present invention has been made to solve the above problems, an object of the present invention is to form a carbon fiber layer of the material of the doctor blade to carbonize the surface of the roll foreign matter on the surface of the roll before and after the electro-zinc plating The present invention provides a remover for removing foreign substances on a roll to reduce the adhesion and to improve the durability of the doctor blade by forming a polymer resin layer between the carbon fiber layers to improve rigidity than the carbon fiber layer alone.
상기한 과제를 해결하기 위한 본 발명은 중심축에 의해 일방향으로 회전되며 강판 등의 이송체를 이송시키는 롤의 둘레면에 접하도록 고정 설치되어 회전되는 상기 롤의 표면에 묻은 이물질을 제거하여 상기 이송체의 스크래치 발생을 방지하기 위한 리무버를 구비하되, 상기 롤은 완충성을 갖는 수지재로 형성되며, 상기 리무버는 상기 롤의 둘레면에 형성된 핀홈을 채움과 동시에 상기 롤의 둘레면에 매끄러운 코팅막을 형성하여 이물질의 제거를 용이하게 하도록 복수의 섬유코팅층 및 상기 섬유코팅층의 내구성을 향상시키기 위해 각 상기 섬유코팅층 사이에 개재되는 고분자수지층으로 이루어진 롤의 표면 이물질 제거용 리무버를 특징으로 한다.The present invention for solving the above problems is rotated in one direction by the central axis and fixed to contact the circumferential surface of the roll for transporting the conveying body such as steel plate to remove the foreign matter on the surface of the roll to be rotated and transported A remover is provided to prevent the occurrence of scratches of the sieve, wherein the roll is formed of a resin material having a buffer property, and the remover fills the pin groove formed on the circumferential surface of the roll and at the same time provides a smooth coating film on the circumferential surface of the roll. It characterized in that the remover for removing the surface foreign matter of the roll made of a plurality of fiber coating layer and the polymer resin layer interposed between the fiber coating layer to improve the durability of the fiber coating layer to facilitate the removal of foreign matter.
상기와 같이 구성되는 본 발명에 의한 롤의 표면 이물질 제거용 리무버에 따르면, 닥터 블레이트의 재질을 카본섬유층으로 형성하여 롤의 표면을 카본화함에 따라 전기아연 도금 전후에 나타나는 롤의 표면에 이물질이 부착되는 것을 줄일 수 있는 효과가 있다.According to the remover for removing foreign substances on the surface of the roll according to the present invention configured as described above, the foreign material is formed on the surface of the roll before and after electro zinc plating as the material of the doctor blade is formed of a carbon fiber layer to carbonize the surface of the roll. There is an effect to reduce the adhesion.
아울러, 본 발명에 의한 롤의 표면 이물질 제거용 리무버는 카본섬유층 사이에 고분자수지층을 형성하여 카본섬유층 단독보다 강성도를 향상시킴에 따라 닥터 블레이드의 내구성을 향상시킬 수 있는 효과가 있다.In addition, the remover for removing foreign matter on the surface of the roll according to the present invention has an effect of improving the durability of the doctor blade by forming a polymer resin layer between the carbon fiber layers to improve rigidity than the carbon fiber layer alone.
이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 롤과 접촉하는 리무버의 설치 개략도이다.1 is a schematic view of installation of a remover in contact with a roll according to the invention.
그리고, 도 2a는 본 발명에 따른 리무버를 롤에 초기 접촉된 상태를 보인 단면도이며, 도 2b는 본 발명에 따른 리무버로 롤의 둘레면에 부착된 이물질을 제거함과 아울러 롤의 둘레면을 코팅한 상태를 보인 단면도이다.2A is a cross-sectional view showing a state in which the remover according to the present invention is initially in contact with a roll, and FIG. 2B is a remover according to the present invention, which removes foreign substances attached to the circumferential surface of the roll and coats the circumferential surface of the roll. It is sectional view which showed state.
도 1에 도시된 바와 같이, 본 발명에 따른 롤의 표면 이물질 제거용 리무버(20)는 중심축(11)에 의해 일방향으로 회전되며 강판 등의 이송체(도시하지 않음)를 이송시키는 롤(10)의 둘레면에 접하도록 고정 설치되어 회전되는 롤(10)의 표면에 묻은 이물질을 제거함에 따라 롤(10)에 의해 이송체에 발생되는 스크래치를 방지하는 역할을 한다.As shown in FIG. 1, the
이때, 상기 리무버(20)는 일반적인 방식에 의해 임의의 고정체(도시하지 않음)됨에 따라 상세한 설명을 생략하고, 도시하지 않는다.At this time, the
또한, 상기 롤(10)은 이송체의 이송시 완충을 위해 완충력을 갖는 수지재, 특히 우레탄 수지로 형성된다.In addition, the
상기 롤(10)은 중심축(11)에 회전 가능하게 장착되어 회전되는데, 상기 중심축(11)이 임의의 프레임(도시하지 않음)에 지지되는 구조는 일반적인 것으로 한다.The
특히, 상기 롤(10)은 강판 등의 이송체를 이송하면서 이송체에 묻은 이물질을 부착하게 된다.In particular, the
따라서, 상기 리무버(20)는 롤(10)의 둘레면에 접촉하여 고정됨에 따라 롤(10)의 회전으로 인해 롤(10)의 표면에 묻은 이물질을 제거하게 된다.Therefore, as the
이때, 상기 롤(10)은 우레탄 수지로 형성되는 바, 상기 리무버(20)는 롤(10)의 재질보다 약한 재질일 경우 부서지기 쉬우며 롤(10)의 재질보다 강한 재질일 경우 롤(10)의 표면에 상해를 입히게 된다.At this time, the
그래서, 상기 리무버(20)는 충분한 자체 경도를 갖음과 동시에 롤(10)의 표면에 상해를 입히지 않는 재질로 이루어져야 한다.Thus, the
결과적으로, 도 2a에 도시된 바와 같이, 상기 리무버(20)는 롤(10)의 표면에 상해를 입히지 않으면서 롤(10)의 표면에 부착된 이물질층(13)을 제거하기 위한 복수의 섬유코팅층(22) 및 상기 섬유코팅층(22) 사이에 형성되어 인접한 섬유코팅층(22)을 접착함에 따라 모든 섬유코팅층(22)의 충분한 자체 경도를 갖도록 하는 고분자수지층(24)으로 이루어진다.As a result, as shown in FIG. 2A, the
특히, 상기 섬유코팅층(22)은 카본섬유 재질의 층으로 이루어져 우레탄 수지 재질의 롤(10) 표면에 접촉되면서 롤(10)에 상해를 가하지 않으면서 롤(10)의 표면에 부착된 이물질을 제거하게 된다.In particular, the
또한, 도 2b에 도시된 바와 같이, 상기 섬유코팅층(22)은 카본섬유 재질의 층이기 때문에 지속적으로 롤(10)의 표면에 접하면서 롤(10)의 표면에 코팅막(30)을 형성하게 된다.In addition, as shown in Figure 2b, because the
이로 인해, 상기 롤(10)은 매끈한 표면을 갖기 때문에 코팅막(30) 표면에 부착된 이물질은 쉽게 제거된다.Because of this, the
이때, 상기 롤(10)은 표면에 미세한 핀홈(12)을 다수 개 형성한다.In this case, the
따라서, 상기 섬유코팅층(22)은 이 핀홈(12)을 채움과 동시에 롤(10)의 표면에 코팅막(30)을 형성하게 되고, 이에 따라 상기 코팅막(30)에 부착된 이물질은 더욱 쉽게 제거된다.Therefore, the
그리고, 상기 고분자수지층(24)은 섬유코팅층(22)이 충분한 경도를 갖도록 인접한 섬유코팅층(22)끼리 부착할 수 있는 에폭시수지로 함이 바람직하다.The
한편, 서로 접착된 섬유코팅층(22)과 고분자수지층(24)은 롤(10)의 회전방향에 대해 접선을 기준으로 20 내지 40도 각도(θ)로 기울어지게 구비됨이 바람직하다.Meanwhile, the
즉, 상기 리무버(20)가 롤(10)의 접선 방향에 대해 기울어진 각도(θ)를 20 내지 40도 유지하도록 기울어지게 구비된다.That is, the
이때, 상기 리무버(20)의 기울어짐 각(θ)이 20도 미만일 경우, 상기 리무버(20)는 롤(10)의 접선에 대해 너무 뉘게 됨에 따라 롤(10)의 둘레면 이물질층(13)을 충분히 제거하지 못하게 된다.At this time, when the inclination angle θ of the
그리고, 상기 리무버(20)의 기울어짐 각(θ)이 40도 초과할 경우, 상기 리무버(20)는 롤(10)의 접선에 대해 너무 세워짐에 따라 롤(10)과의 마찰력 증가로 인해 중심을 기준으로 대칭되는 방향으로 기울여지려는 힘이 작용함으로써 리무버(20)를 잡고 있는 홀더(도시하지 않음)와의 연결부위에 내부응력이 크게 발생되고, 이에 따라 리무버(20)가 부러지게 된다.In addition, when the inclination angle θ of the
한편, 상기 섬유코팅층(22)과 고분자수지층(24)으로 이루어진 리무버(20)는 동일 단부를 회전되는 롤(10)과 접촉되는 면적을 줄이기 위해 경사면(27)을 형성한다.Meanwhile, the
특히, 상기 롤(10)과 최초 접하는 최하층에 위치한 섬유코팅층(22)은 롤(10)과의 부딪힘에 따른 부서짐을 방지하기 위해 단부를 바닥면에 대해 수직하게 형성함이 바람직하다.In particular, the
아울러, 상기 섬유코팅층(22)은 고분자수지층(24)보다 더 돌출되게 형성되어 고분자수지층(24)과 롤(10)의 접촉을 방지한다.In addition, the
그리고, 적어도 리무버(20)의 최하층에 위치한 섬유코팅층(22)의 두께(t1)는 고분자수지층(24)의 두께(t2)보다 훨씬 두껍게 형성함으로써 섬유코팅층(22)의 마모에 따른 교체기간을 증가시키는 것이 바람직하다.In addition, at least the thickness t1 of the
이는, 리무버(20)의 최하층에 해당되는 섬유코팅층(22)의 두께가 가능한 범위 내에서 최대의 두께로 이루어져야 이 섬유코팅층(22)을 이루는 카본섬유가 많게 되어 롤(10)의 표면 카본화가 보다 빨리 발생하게 된다.This, the thickness of the
본 발명은 도면에 도시된 실시예를 참고로 하여 설명되었으나, 이는 예시적인 것에 불과하며, 당해 기술이 속하는 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. Although the present invention has been described with reference to the embodiments shown in the drawings, this is merely exemplary, and those skilled in the art to which the art belongs can make various modifications and other equivalent embodiments therefrom. Will understand.
따라서, 본 발명의 진정한 기술적 보호범위는 아래의 특허청구범위에 의해서 정하여져야 할 것이다.Therefore, the true technical protection scope of the present invention will be defined by the claims below.
도 1은 본 발명에 따른 롤과 접촉하는 리무버의 설치 개략도.1 is a schematic view of installation of a remover in contact with a roll according to the invention.
도 2a는 본 발명에 따른 리무버를 롤에 초기 접촉된 상태를 보인 단면도.Figure 2a is a cross-sectional view showing a state in which the remover according to the present invention in the initial contact with the roll.
도 2b는 본 발명에 따른 리무버로 롤의 둘레면에 부착된 이물질을 제거함과 아울러 롤의 둘레면을 코팅한 상태를 보인 단면도.Figure 2b is a cross-sectional view showing a state in which the remover attached to the circumferential surface of the roll with a remover according to the present invention while coating the circumferential surface of the roll.
<도면의 주요 부분에 관한 부호의 설명><Explanation of symbols on main parts of the drawings>
10: 롤 12: 핀홈10: roll 12: pin groove
20: 리무버 22: 섬유코팅층 20: remover 22: fiber coating layer
24: 고분자수지층 30: 코팅막24: polymer resin layer 30: coating film
Claims (7)