KR20080110236A

KR20080110236A - Method for menufacturing method of jewel decorated ceramics having

Info

Publication number: KR20080110236A
Application number: KR1020070058733A
Authority: KR
Inventors: 김영목; 유덕상; 진수경; 김기수
Original assignee: 한국도자기주식회사
Priority date: 2007-06-15
Filing date: 2007-06-15
Publication date: 2008-12-18

Abstract

Provided is a manufacturing method of a jewelry decorated porcelain which can maintain product values consistently by solidly adhering a plurality of jewels onto a porcelain such that the jewels are not easily separated from the porcelain by the external force. A manufacturing method of a jewelry decorated porcelain(10) comprises: a first step of drawing a rough sketch(30) on a porcelain(20); a second step of coating an epoxy resin on the rough sketch or jewelry(40), and adhering the jewelry to the rough sketch; a third step of injecting the jewelry-adhered porcelain into an electric oven and heating the jewelry-adhered porcelain to adhere the jewelry to the porcelain; and a fourth step of naturally cooling the heated porcelain.

Description

Method for menufacturing method of jewel decorated ceramics having}

도 1은 본 발명에 따른 보석장식 도자기의 제조방법에 의해 제조된 도자기를 나타낸 사시도이다.1 is a perspective view showing a pottery manufactured by the method for manufacturing a jewelery ware according to the present invention.

도 2a 내지 2c는 본 발명에 따른 보석장식 도자기의 제조방법의 제조과정을 나타낸 순서도이다.Figure 2a to 2c is a flow chart showing the manufacturing process of the method of manufacturing a jewelry ware according to the present invention.

도 3은 본 발명에 따른 보석장식 도자기의 제조방법의 다른 실시예에 의해 제조된 도자기를 나타낸 사시도이다.Figure 3 is a perspective view showing the ceramics produced by another embodiment of a method of manufacturing a jewelry decorative ceramics according to the present invention.

<도면의 주요 부분에 대한 설명>Description of the main parts of the drawing

10 : 보석장식 도자기 20 : 도자기10: jeweled porcelain 20: porcelain

21 : 체결공 30 : 밑그림21: fastener 30: sketch

40 : 보석40: jewelry

본 발명은 보석장식 도자기의 제조방법에 관한 것으로서, 보다 상세하게는 다수개의 보석이 도자기에 견고하게 부착되어 외력에 의해 쉽게 분리되지 않음으로 상품가치를 지속적으로 유지할 수 있음은 물론 사용자의 인체에 투입되는 것을 방지할 수 있는 보석장식 도자기의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a jeweled porcelain, more specifically, a plurality of jewels are firmly attached to the porcelain and can not be easily separated by an external force, thereby maintaining the value of the product as well as putting it into the human body of the user. It relates to a method of manufacturing a jewelery pottery that can be prevented.

일반적으로 식기 등에 사용되는 그릇은 살균력이 우수하고 변형이 없는 다양한 형상과 모양의 도자기가 주로 사용되어 왔다.Generally, bowls used in tableware, etc. have been mainly used in ceramics of various shapes and shapes having excellent sterilizing power and no deformation.

이러한 도자기의 도자기를 제조하기 위한 방법은, 먼저 점토등의 도자기원료에 물과 매용재(예를들면 규산소오다)를 소정의 비율로 혼합하여 반죽상태로 만든후, 회전하는 원판에 올려놓고 손으로 임의 형상으로 성형물을 만들거나, 혹은 임의 형상으로 만든 모형에 반죽을 부어 모형과 동일한 형상의 성형물을 만든다.In order to manufacture such ceramic pottery, first, water and burying materials (for example, sodium silicate) are mixed in a predetermined ratio with a raw material such as clay, and then made into a dough state, and then placed on a rotating disc. The molding is made into an arbitrary shape, or the dough is poured into a model made of an arbitrary shape to form a molding having the same shape as the model.

그 후, 성형물의 외관을 조각하여 예술적으로 디자인한 다음 가마에 수납시킨 다음 고온으로 굽게 됨으로써 도자기 특유의 광택과 강도를 가지게 된다.After that, the appearance of the molding is carved and artistically designed, stored in a kiln, and then baked at a high temperature, thereby bringing the luster and strength peculiar to ceramics.

최근에는 예술적인 아름다움을 갖도록 현대적인 보석이 구비된 식기 도자기들이 대거 출시되거나 개발되고 있어 사용자의 식욕을 증진시킴은 물론 심리적인 안정감을 주고 있다.Recently, a large number of tablewares equipped with modern jewelry have been released or developed to have artistic beauty, thereby enhancing user's appetite and giving psychological stability.

그러나, 도자기의 특성상 주로 식기에 사용됨으로, 접착제에 의해 도자기에 부착된 보석이 도자기를 세척하는 과정에서 세척도구와의 마찰에 의해 탈거되어 상품가치를 떨어뜨리는 문제점이 있으며, 사용자가 도자기에 담겨진 음식물을 먹는 도중 부주위로 인해 수저 또는 젓갈이 보석을 타격,탈거시킴으로써, 도자기에서 분 리된 보석이 음식물과 함께 인체로 투입되어 사용자의 건강을 위협하는 심각한 문제점이 상존하게 된다.However, due to the nature of ceramics, mainly used in tableware, there is a problem in that the jewelry attached to the porcelain by the adhesive is removed by friction with the cleaning tool in the process of washing the porcelain, thereby lowering the value of the product, the user has food in the porcelain While eating, hitting and removing the cutlery or salted gemstones due to the circumference, a serious problem that threatens the user's health as the gems separated from the porcelain are introduced into the human body with food.

본 발명의 목적은 다수개의 보석이 도자기에 견고하게 부착되어 외력에 의해 쉽게 분리되지 않음으로 상품가치를 지속적으로 유지할 수 있음은 물론 사용자의 인체에 투입되는 것을 방지할 수 있도록 한 보석장식 도자기의 제조방법을 제공하는데 그 목적이 있다.It is an object of the present invention that a number of jewelry is firmly attached to the porcelain is not easily separated by external force to maintain the value of the commodity as well as to manufacture the jewelry decorative porcelain to prevent being put into the human body of the user The purpose is to provide a method.

본 발명은 도자기에 있어서, 상기 도자기에 밑그림을 그리는 1단계와 상기 밑그림 또는 보석에 에폭시수지(epoxy resin)를 도포 후 그 밑그림에 보석을 부착하는 2단계와 보석이 부착된 도자기를 전기오븐에 투입하여 보석을 도자기에 가열,접착시키는 3단계와 가열된 도자기를 자연냉각시키는 4단계로 이루어진 것을 특징으로 한다.In the present invention, in the ceramics, the first step of drawing a sketch on the porcelain and the epoxy resin (epoxy resin) to the sketch or jewelry and then the second step of attaching the jewelry to the sketch and the porcelain is attached to the jewelry is put into the electric oven. It is characterized by consisting of three steps of heating and bonding the jewelry to the porcelain and four steps of natural cooling the heated porcelain.

또한, 상기 1단계에서는 밑그림을 그린 후 그 밑그림에 다수개의 체결공을 형성하여 상기 보석이 그 체결공에 삽입,고정되도록 하는 것을 특징으로 한다.In addition, in the first step, after drawing the sketch, a plurality of fastening holes are formed in the sketch so that the jewelry is inserted and fixed in the fastening hole.

또한, 상기 2단계에서는 상기 밑그림 또는 상기 보석에 세라믹접착제 또는 흑연접착제가 도포되어 그 밑그림에 상기 보석이 부착되게 하는 것을 특징으로 한다.In the second step, a ceramic adhesive or a graphite adhesive is applied to the sketch or the jewel so that the jewel is attached to the sketch.

이하, 첨부된 도면들을 참조하여 본 발명에 따른 보석장식 도자기의 제조방법의 바람직한 실시예를 첨부된 도면을 참조하여 설명한다. 이 과정에서 도면에 도시된 선들의 두께나 구성요소의 크기 등은 설명의 명료성과 편의상 과장되게 도시되어 있을 수 있다. 또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있다. 그러므로, 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.Hereinafter, with reference to the accompanying drawings will be described with reference to the accompanying drawings a preferred embodiment of a method of manufacturing a jewelry ware according to the present invention. In this process, the thickness of the lines or the size of the components shown in the drawings may be exaggerated for clarity and convenience of description. In addition, terms to be described below are terms defined in consideration of functions in the present invention, which may vary according to the intention or convention of a user or an operator. Therefore, definitions of these terms should be made based on the contents throughout the specification.

또한, 하기 실시예는 본 발명의 권리범위를 한정하는 것이 아니라 단지 예시로 제시하는 것이며, 본 기술 사상을 통해 구현되는 다양한 실시예가 있을 수 있다.In addition, the following examples are not intended to limit the scope of the present invention but merely presented by way of example, and there may be various embodiments implemented through the present invention.

도 1은 본 발명에 따른 보석장식 도자기의 제조방법에 의해 제조된 도자기를 나타낸 사시도이고, 도 2a 내지 2c는 본 발명에 따른 보석장식 도자기의 제조방법의 제조과정을 나타낸 순서도이다.1 is a perspective view showing a pottery manufactured by the method of manufacturing a jewelery ware according to the present invention, Figures 2a to 2c is a flow chart showing the manufacturing process of the manufacturing method of a jewelery ware according to the present invention.

도면에 도시된 바와 같이 본 발명인 보석장식 도자기의 제조방법은 총 4단계로 이루어진다.As shown in the figure, the method of manufacturing the jewelery ware of the present invention comprises a total of four steps.

1단계는 다양한 형상(접시, 컵, 그릇 등)으로 성형된 도자기(20)에 밑그림(30)을 그리는 단계이다. 즉 도 1에 도시된 바와 같이 도자기 접시의 외곽부에 수성물감 등을 이용하여 밑그림(30)을 그리게 된다. 이때, 밑그림을 대신하여 이름이나 기념일 또는 문장,부호 등을 그리는 것도 가능하다.The first step is to draw the sketch 30 on the ceramics 20 formed in various shapes (plates, cups, bowls, etc.). That is, as shown in FIG. 1, the sketch 30 is drawn by using an aqueous paint or the like on the outer portion of the ceramic dish. In this case, it is also possible to draw a name, anniversaries or sentences, symbols, etc. in place of the sketch.

여기서, 본 발명에서는 밑그림(30)을 그리는 것은 통상적인 도자기 제조과정 인 수비→성형(成型)→초벌구이→시유→재벌구이의 과정을 마친 도자기, 즉 최종완성된 도자기에 밑그림을 그리는 것이며, 다르게는 상술된 바와 같이 도자기의 제조과정 중에 초벌구이 후 기물(器物)에 밑그림을 그리고 유약(釉藥)을 바른 다음 재벌구이를 하는 것도 가능하다.Here, in the present invention, to draw the sketch 30 is to draw a sketch on the pottery, that is, the finished porcelain, which is the process of the general ceramic manufacturing process defensive → molding → roasting → shiyu → chaebol, As described above, it is also possible to draw a sketch on the material after applying the glaze during the manufacturing process of the ceramics, apply glaze and then grill the chaebol.

2단계는 도자기(20)의 밑그림(30)에 보석(40)을 부착하는 단계이다. 즉 밑그림(30) 또는 보석(40)의 배면에 에폭시수지를 도포한 후 밑그림(30)에 보석(40)을 부착하게 되는데 이때 밑그림(30) 전체에 보석(40)을 부착할 수 있으며 사용자의 기호에 따라 부분적으로 부착하는 것도 가능하다. 즉 밑그림(30)에 에폭시수지를 도포한 후 보석(40)을 부착하는 것은 그 밑그림 전체에 보석(40)을 부착하는 경우이고, 보석(40)의 배면에 에폭시수지를 도포한 후 밑그림(30)에 부착하는 것은 밑그림(30)에 부분적으로 보석(40)을 부착할 경우에 사용된다.The second step is to attach the jewelry 40 to the sketch 30 of the ceramics 20. In other words, after the epoxy resin is applied to the bottom of the sketch 30 or the jewelry 40, the jewelry 40 is attached to the sketch 30. At this time, the jewelry 40 can be attached to the entire sketch 30. It is also possible to attach it partially according to your preference. In other words, attaching the jewel 40 after applying the epoxy resin to the sketch 30 is a case of attaching the jewel 40 to the entire sketch, and after applying the epoxy resin to the back surface of the jewel 40 ) Is used to attach the jewel 40 partially to the sketch 30.

여기서, 보석은 다양한 색과 다양한 모양의 합성보석 (合成寶石, synthetic stone)이 사용된다.Here, the gemstone is made of synthetic stones of various colors and shapes.

3단계는 보석(40)이 부착된 도자기(20)를 가열하여 에폭시수지를 건조시키는 단계이다. 즉 2단계에서와 같이 도자기(20)에 보석(40)을 부착한 후 그 도자기를 전기오븐에 투입하여 에폭시수지를 건조시킴으로써 보석(40)이 도자기(20)에 견고하게 부착되기 위해 일정시간 가열하게 되는데, 이때 전기오븐의 내부온도는 150℃~200℃가 바람직하며 30분~1시간 동안 가열,건조시키는 것이 바람직하다.The third step is to dry the epoxy resin by heating the porcelain 20 to which the jewelry 40 is attached. That is, as in step 2, the jewel 40 is attached to the porcelain 20, and then the porcelain is put into an electric oven to dry the epoxy resin by heating the jewel 40 to be firmly attached to the porcelain 20 for a predetermined time. In this case, the internal temperature of the electric oven is preferably 150 ℃ ~ 200 ℃, it is preferable to heat, dry for 30 minutes ~ 1 hour.

여기서, 상기 에폭시수지(epoxy resin)를 대신하여 내열성(耐熱性)이 우수한 고리모양 디에폭시수지를 사용하는 것도 가능하며, 세라믹접착제 및 흑연접착제가 사용되는 것도 가능하다.Here, it is also possible to use a ring-shaped diepoxy resin having excellent heat resistance in place of the epoxy resin, it is also possible to use a ceramic adhesive and a graphite adhesive.

4단계는 가열된 보석장식 도자기(10)를 냉각시키는 단계이다. 즉 전기오븐에서 가열된 도자기(10)를 꺼낸 후 보석장식 도자기(10)를 자연냉각시키게 된다.Step 4 is cooling the heated jewelery ware 10. In other words, after removing the heated ceramics (10) in the electric oven will be natural cooling of the jewelry ornaments (10).

여기서, 가열된 보석장식 도자기(10)는 전기오븐에서 냉각시킨 후 외부로 꺼내는 것도 가능하다. 바람직하게는 제조공정상 상술한 바와 같이 가열된 보석장식 도자기(10)를 외부로 꺼낸 후 자연건소시키는 것이 바람직하다.Here, the heated jewelery ware 10 can be taken out after cooling in an electric oven. Preferably, in the manufacturing process, it is preferable to take out the heated jewelery ware 10 as described above and then dry it naturally.

상기에서는 밑그림(30)이 그려진 도자기(20)에 에폭시수지를 이용해 다수개의 보석(40)을 부착하는 것으로 설명 및 도면에 나타내고 있지만 이에 한정되는 것은 아니다.In the above, as shown in the description and drawings to attach a plurality of gemstones 40 using epoxy resin to the porcelain 20, the sketch 30 is drawn, but is not limited thereto.

예를 들면 밑그림(30)이 그려진 도자기(20)에 다수개의 체결공(21)을 형성하고 그 체결공(21)에 보석(40)을 삽입,고정시키게 된다. 이때, 보석(40)은 체결공(21)에 억지끼움될 수 있으며, 상술된 에폭시수지를 체결공(21) 또는 보석(40)의 배면에 도포한 후 그 체결공(21)에 끼움,부착시키는 것도 가능하다.For example, a plurality of fastening holes 21 are formed in the porcelain 20 on which the sketch 30 is drawn, and the jewel 40 is inserted into and fastened to the fastening holes 21. At this time, the jewelry 40 may be fitted into the fastening hole 21, and after applying the epoxy resin described above to the fastening hole 21 or the back surface of the jewelry 40, the fastening hole 21 is fitted, attached It is also possible.

본 발명은 보석장식 도자기의 제조방법은 다수개의 보석이 도자기에 견고하게 부착되어 외력에 의해 쉽게 분리되지 않음으로 상품가치를 지속적으로 유지할 수 있음은 물론 사용자의 인체에 투입되는 것을 방지할 수 있는 효과가 있다.The present invention is a method of manufacturing a jeweled porcelain is a number of jewelry is firmly attached to the porcelain is not easily separated by an external force can maintain the value of the product as well as to prevent the input to the human body of the user There is.

Claims

In pottery,

Drawing a sketch on the ceramics;

2 steps of applying an epoxy resin to the sketch or jewelry and attaching the jewelry to the sketch;

3 steps of heating and bonding the jewelry to the ceramic by putting the jewelry attached to the ceramic oven; And

The method of producing a jewelery ceramics, characterized in that consisting of four steps to naturally cool the heated ceramics.

The method of claim 1,

The first step is to draw a sketch on the porcelain and then to form a plurality of fastening holes in the sketch to the jewelry manufacturing method characterized in that the jewel is inserted into the fastening hole, it is fixed.

The method of claim 1,

In the second step, a ceramic adhesive or a graphite adhesive is applied to the sketch or the jewelry to produce the jewelry decoration ceramics, characterized in that the jewelry is attached to the sketch.