KR20080051237A - Packing box with antibiotic and deodorizing function - Google Patents

Packing box with antibiotic and deodorizing function Download PDF

Info

Publication number
KR20080051237A
KR20080051237A KR1020060121957A KR20060121957A KR20080051237A KR 20080051237 A KR20080051237 A KR 20080051237A KR 1020060121957 A KR1020060121957 A KR 1020060121957A KR 20060121957 A KR20060121957 A KR 20060121957A KR 20080051237 A KR20080051237 A KR 20080051237A
Authority
KR
South Korea
Prior art keywords
silver
modified
modified zeolite
zeolite
paper
Prior art date
Application number
KR1020060121957A
Other languages
Korean (ko)
Inventor
이진교
Original Assignee
이진교
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이진교 filed Critical 이진교
Priority to KR1020060121957A priority Critical patent/KR20080051237A/en
Publication of KR20080051237A publication Critical patent/KR20080051237A/en

Abstract

A packing box with antibiotic and deodorizing functions is provided to keep contents inside the packing box for a long time by coating an inner surface of the box with modified zeolite. A packing box with antibiotic and deodorizing functions is made of a corrugated cardboard. The corrugated cardboard is composed of a base paper(22), a corrugated paper(21), and a print paper(20). The corrugated paper or the base paper is coated with coating material at a thickness of 50 to 200mum. The coating material contains silver ion-modified zeolite or silver and hydrogen-modified zeolite. The silver ion-modified zeolite or the sliver and hydrogen-modified zeolite is modified from ca-type clinoptilolite zeolite.

Description

항균 및 소취 기능을 가진 포장 박스{Packing Box with Antibiotic and Deodorizing Function}Packing Box with Antibiotic and Deodorizing Function

도 1의 (가)는 본 발명에 따른 코팅제를 골판지에 도포하는 과정을 개략적으로 도시한 것이고 그리고 (나)는 완성된 골판지의 단면도를 도시한 것이다. 1 (a) schematically shows the process of applying the coating agent to the cardboard according to the invention and (b) shows a cross-sectional view of the finished cardboard.

본 발명은 개질 제올라이트를 포함하는 항균 및 소취 기능을 가진 기능성 코팅제로 내부 면이 처리된 포장 박스에 관한 것이다. The present invention relates to a packaging box in which the inner surface is treated with a functional coating agent having an antibacterial and deodorizing function including a modified zeolite.

농산물 또는 수산물의 원거리 수송을 위하여 사용되는 포장 박스는 장시간 동안 포장 박스 내부에 보관되는 포장물의 신선도를 유지할 수 있어야 한다. 포장물의 신선도는 포장 박스 그 자체로부터 발생하는 화학물질 및 보관되는 내용물로부터 발생하는 균 또는 화학물질로 인하여 손상이 될 수 있다. 그러므로 포장 박스는 포장 박스의 제조 과정에서 첨가된 화학물질이 포장 박스의 내부로 발산되는 것을 방지하고 그리고 보관된 내용물로부터 발생하는 균 또는 화학물질을 흡수할 수 있도록 처리되어야 한다. Packaging boxes used for remote transport of agricultural or aquatic products should be able to maintain the freshness of the packages stored inside them for a long time. The freshness of a package can be damaged by chemicals from the box itself and bacteria or chemicals from the contents stored. Therefore, the packing box should be treated to prevent the chemicals added during the manufacturing of the packing box from being released into the packing box and to absorb bacteria or chemicals from the stored contents.

항균성을 가지는 다양한 물질이 공지되어 있다. 은은 대표적인 항균성 물질 로 알려져 있고 그리고 제올라이트는 강한 흡착성으로 인하여 항균 및 소취 작용제로 사용될 수 있다는 것이 공지되어 있다. 은은 콜로이드 또는 용액 상태로 제조되어 포장 박스의 제조 과정에서 첨가되거나 또는 포장 박스의 표면에 코팅 처리가 될 수 있다. 한편 제올라이트는 알칼리 및 알칼리토금속의 규산알루미늄 수화물인 광물을 말한다. 다양한 형태의 제올라이트 광물이 존재하지만 함수량이 많고 그리고 높은 온도에서 결정 구조를 유지하여 흡착성이 강하다는 특징을 공유한다. 이와 같이 은 또는 제올라이트는 벽지 또는 포장지의 기능성을 향상시키기 위하여 사용될 수 있다. Various materials having antimicrobial properties are known. Silver is known as a representative antimicrobial material and it is known that zeolites can be used as antimicrobial and deodorant agents due to their strong adsorption properties. Silver may be prepared in colloidal or solution state and added during the manufacture of the packaging box or coated on the surface of the packaging box. Zeolite, on the other hand, refers to minerals that are aluminum silicate hydrates of alkali and alkaline earth metals. There are various types of zeolite minerals, but they share a high water content and strong crystallinity at high temperatures, making them highly adsorptive. As such, silver or zeolite may be used to improve the functionality of the wallpaper or wrapping paper.

포장지의 기능을 향상시키기 위하여 은이 사용된 선행기술로 특허등록번호 제427863호 “은이 코팅된 포장지와 그의 제조방법 및 그 장치”가 있다. 제시된 선행 기술은 PE 시트층, 종이시트층, 탄산칼슘코팅층, 및 은 코팅층을 포함하는 포장지를 개사하고 있다. 제시된 발명의 경우 탄산칼슘코팅층에 의하여 은 입자가 포장지의 표면에 고정되어 항균 성질이 지속적으로 유지될 있도록 하고 그리고 은 입자는 100 내지 500 ㎛로 탄산칼슘코팅층 위에 코팅이 된다. A prior art in which silver is used to improve the function of the wrapping paper is Patent Registration No. 427863, "Packing paper coated with silver and its manufacturing method and apparatus thereof. The prior art presented discloses a wrapping paper comprising a PE sheet layer, a paper sheet layer, a calcium carbonate coating layer, and a silver coating layer. In the case of the present invention, the silver carbonate is fixed to the surface of the wrapping paper by the calcium carbonate coating layer so that the antibacterial property is continuously maintained, and the silver particles are coated on the calcium carbonate coating layer at 100 to 500 μm.

포장지에 사용될 수 있는 다른 기능성 물질로 토르말린, 맥반석 또는 황토와 같은 광물질이 있다. 이와 같은 광물질은 사용하여 포장지의 기능성을 향상시킨 선행기술로 특허번호 제581364호 “식품포장지 코팅 조성물 및 그 식품포장지”가 있다. 제시된 발명은 식품의 신선도를 유지하기 위하여 토르말린 및 맥반석과 같은 광석 분말이 3 내지 30 중량%로 분리대두단백 및 전분으로 형성된 5 내지 20 중량%의 접착제로 코팅이 된 식품 포장지를 개시하고 있다. 이와 같이 은 또는 맥반석으 로 코팅이 된 포장지뿐만 아니라 제올라이트를 포함하는 포장재도 또한 공지되어 있다. Other functional materials that can be used in the packaging include minerals such as tourmaline, elvan or loess. Such a mineral is a prior art that improves the functionality of the packaging by using the Patent No. 581364 "food packaging paper coating composition and its food packaging paper". The present invention discloses a food wrapper coated with 5 to 20% by weight of an ore powder such as tourmaline and elvan to 3 to 30% by weight of isolated soy protein and starch to maintain food freshness. As well as packaging papers coated with silver or elvan, as well as packaging materials comprising zeolites are also known.

제올라이트를 포함하는 포장재는 특허공개번호 제1993-8241호 “소수성 제올라이트를 함유한 포장재 및 그 용도”에 개시되어 있다. 제시된 발명은 소수성 제올라이트를 포함하는 마분지에 대하여 개시하고 있다. 마분지에 포함된 제올라이트는 포장재의 제조 과정에서 포장재에 포함될 수 있는 염소화 유기 화합물과 같은 유해한 물질이 포장재로부터 내부 보관 물질로 전달되는 것을 방지하는 기능을 한다. 그러므로 내부 보관물질로부터 발생이 될 수 있는 유해한 성분을 흡수하는 기능을 가지는 것은 아니다. Packaging materials comprising zeolites are disclosed in Patent Publication No. 1993-8241 “Packaging Materials Containing Hydrophobic Zeolites and Their Uses”. The invention presented discloses cardboard comprising hydrophobic zeolites. Zeolites contained in cardboard serve to prevent the transmission of harmful substances from packaging materials to internal storage materials, such as chlorinated organic compounds, which may be included in packaging materials during the manufacture of packaging materials. Therefore, it does not have the function of absorbing harmful components that may arise from internal storage materials.

본 발명은 공지된 발명에서 개시되지 않는 개질 제올라이트가 코팅된 기능성 박스를 제안한다. 제안된 기능성 박스에 포함된 개질 제올라이트는 특허공개번호 제1993-8241호의 소수성 제올라이트와는 달리 용기 내부의 보관물로부터 발생할 수 있는 유해 성분을 흡수하는 기능을 가진다. 그러므로 특별히 소수성일 필요가 없고 함수율이 높을수록 유리하다. The present invention proposes a functional box coated with a modified zeolite which is not disclosed in the known invention. The modified zeolite contained in the proposed functional box has a function of absorbing harmful components that may arise from the storage inside the container, unlike the hydrophobic zeolite of Patent Publication No. 1993-241. Therefore, it does not need to be particularly hydrophobic and a higher moisture content is advantageous.

본 발명의 목적은 내부 표면이 개질 제올라이트로 코팅이 된 기능성 박스를 제공하는 것이다. It is an object of the present invention to provide a functional box having an inner surface coated with a modified zeolite.

본 발명의 적절한 실시 형태에 따르면, 원지, 골심지, 및 인쇄지로 형성된 골판지로 제조되는 기능성 박스는 골심지 또는 원지가 은 이온-개질 제올라이트, 또는 은 및 수소-개질 제올라이트를 포함하는 코팅제로 50 내지 200 ㎛의 두께로 코팅이 된다. According to a preferred embodiment of the present invention, a functional box made of corrugated paper formed of paper, corrugated paper, and printed paper is 50 to 200 μm with corrugated paper or paper coated with silver ion-modified zeolite, or silver and hydrogen-modified zeolite. It is coated with a thickness of.

본 발명의 다른 적절한 실시 형태에 따르면, 은 이온-개질 제올라이트, 또는 은 및 수소 개질 제올라이트는 Ca-형 클리놉티라이트 천연 제올라이트로부터 개질된다. According to another suitable embodiment of the present invention, silver ion-modified zeolites, or silver and hydrogen-modified zeolites are modified from Ca-type clinoptilite natural zeolites.

본 발명의 또 다른 적절한 실시 형태에 따르면, 은 이온-개질 제올라이트 또는 은 및 수소 개질 제올라이트는 질산은으로 개질이 되고 그리고 5 내지 20 ㎛의 분말 형태가 된다. According to another suitable embodiment of the present invention, the silver ion-modified zeolite or silver and the hydrogen-modified zeolite are modified with silver nitrate and are in powder form of 5-20 μm.

본 발명의 또 다른 적절한 실시 형태에 따르면, 코팅제는 물 또는 용제; 물 또는 용제 중량 대비 40 내지 60 중량 %의 은 또는 은 및 수소 개질 제올라이트; 개질 제올라이트 중량 대비 5 내지 15 중량 %의 보존제를 포함할 수 있고, 상기에서 보존제는 전분, 탄산칼슘, 명반, 염화알루미늄, 또는 질산알루미늄이 된다. According to another suitable embodiment of the present invention, the coating agent is water or a solvent; 40 to 60% by weight of silver or silver and hydrogen modified zeolites by weight of water or solvent; 5 to 15% by weight relative to the weight of the modified zeolite may comprise a preservative, wherein the preservative is starch, calcium carbonate, alum, aluminum chloride, or aluminum nitrate.

본 발명의 또 다른 적절한 실시 형태에 따르면, 상기 코팅제는 개질 제올라이트 중량 대비 3 내지 5 중량%의 토르말린을 더 포함한다.According to another suitable embodiment of the invention, the coating further comprises from 3 to 5% by weight of tourmaline relative to the weight of the modified zeolite.

아래에서 본 발명은 실시 예를 이용하여 상세하게 설명이 된다. 제시된 실시 예는 본 발명의 명확한 이해를 위한 것이며 본 발명의 범위를 제한하기 위한 것은 아니다. Hereinafter, the present invention will be described in detail by using an embodiment. The examples presented are for a clear understanding of the invention and are not intended to limit the scope of the invention.

본 발명에 따른 기능성 박스의 제조를 위하여 먼저 개질 제올라이트가 제조 되어야 한다. 제올라이트는 다양한 형태로 개질이 될 수 있지만 본 발명에 따른 기능성 박스의 제조를 위하여 제올라이트는 수소 또는 금속물질로 복합 이온 교환 형태로 개질이 될 수 있다. 개질을 위하여 사용한 금속은 은(Ag), 금(Au), 및 백금(Pt)과 같은 귀금속을 포함하지만 항균성을 고려할 때 바람직하게는 은(Ag)로 개질이 될 수 있다. Modified zeolites must first be prepared for the production of the functional box according to the invention. Zeolites can be modified in a variety of forms, but for the manufacture of the functional box according to the invention the zeolites can be modified in complex ion exchange form with hydrogen or metal. Metals used for the modification include precious metals such as silver (Ag), gold (Au), and platinum (Pt), but may be modified to silver (Ag), preferably in view of antimicrobial properties.

1. 개질 제올라이트의 제조 1. Preparation of Modified Zeolites

A. 은 이온(A. Silver ions ( AgAg ++ ) 개질 제올라이트의 제조) Preparation of Modified Zeolites

천연 제올라이트는 Ca-형 클리놉티라이트(Clinoptilolite), 페리라이트(ferrierite) 또는 율란다이트(heulandite)와 같은 형태로 존재하지만 양이온 교환 능력이 우수한 Ca-형 클리놉티라이트 천연 제올라이트가 Ag로 개질이 되는 것이 바람직하다. 본 발명에 따른 개질 제올라이트의 제조를 위하여 Ca-형 클리놉티라이트 구조를 가지는 천연 제올라이트를 100 내지 300 메시(mesh)의 평균 입경을 가지는 미세한 분말로 만든 후 1.0 내지 2.0 × 10-3 M 질산은(AgNO3) 수용액에 투입하였다. 질산은 수용액의 양 및 투입되는 천연 제올라이트의 양은 특별히 제한이 되는 것은 아니지만, 적절하게 이온 교환 반응이 진행되도록 하게 위하여 질산은 용액 100 ㎖에 대하여 천연 제올라이트의 양이 3 내지 8 그램(g)이 되는 것이 적절하다. 반응의 촉진을 위하여 질산은 용액은 20 내지 30 시간 동안 교반이 된다. 이후 질산은 용액을 필터로 여과하여 Ag 양이온으로 이온 교환이 된 개질 제올라이트를 분리하여 90 내지 120 ℃의 오븐에서 10 내지 20 시간 동안 건조한다. 건조된 개질 제올라이트를 분쇄하여 평균 입경이 5 내지 20 ㎛가 되는 개질 제올라이트 분말로 제조하였다. Natural zeolites exist in the form of Ca-type Clinoptilolite, ferrierite or helandite, but Ca-type Clinoptilite natural zeolites with excellent cation exchange ability are modified with Ag. It is preferable. For the preparation of the modified zeolite according to the present invention 1.0 to 2.0 × 10 -3 M silver nitrate (AgNO) after making a natural zeolite having a Ca-type clinoprite structure of fine powder having an average particle diameter of 100 to 300 mesh (AgNO) 3 ) was added to an aqueous solution. The amount of the silver nitrate solution and the amount of the natural zeolite to be added are not particularly limited, but in order to allow the ion exchange reaction to proceed properly, it is appropriate that the amount of the natural zeolite is 3 to 8 grams (g) per 100 ml of the silver nitrate solution. Do. The silver nitrate solution is stirred for 20-30 hours to facilitate the reaction. Thereafter, the silver nitrate solution was filtered through a filter to separate the modified zeolite ion-exchanged with Ag cations, and dried in an oven at 90 to 120 ° C. for 10 to 20 hours. The dried modified zeolite was ground to prepare a modified zeolite powder having an average particle diameter of 5 to 20 µm.

B. 은 및 수소(B. silver and hydrogen ( AgAg /H) 개질 제올라이트/ H) modified zeolite

은 및 수소(Ag/H)로 개질된 제올라이트를 제조하기 위하여 먼저 수소로 이온 교환 반응을 시켜 H-형 개질 제올라이트로 제조하고, 그리고 H-형 개질 제올라이트를 Ag로 이온 교환 반응을 시켜 은 및 수소 개질 제올라이트를 제조할 수 있다. In order to prepare a zeolite modified with silver and hydrogen (Ag / H), an ion exchange reaction is first performed with hydrogen to prepare an H-type modified zeolite, and the H-type modified zeolite is subjected to an ion exchange reaction with Ag to obtain silver and hydrogen. Modified zeolites can be prepared.

H-형 개질 제올라이트의 제조Preparation of H-Type Modified Zeolites

H-형 개질 제올라이트를 제조하기 위하여 약 1 M 염화암모늄(NH4Cl) l 리터(L)에 Ca-형 클리놉티라이트 형태의 천연 제올라이트 200 그램(g)을 투입하고, 그리고 10 내지 15 시간 동안 교반을 하였다. 이후 필터로 개질 제올라이트를 분리시킨 후 과량의 염을 제거하기 위하여 약 5 L의 증류수로 3 내지 5회에 걸쳐 세척을 하였다. 세척된 개질 제올라이트를 100 ℃의 온도로 유지되는 오븐에서 10 내지 15시간 동안 건조를 시켰다. 건조된 개질 제올라이트로부터 암모니아를 제거하기 위하여 약 450 ℃의 온도로 열처리를 하고 그리고 평균 입경이 5 내지 20 ㎛가 되도록 분쇄를 하여 H-형 개질 제올라이트 분말을 제조하였다. To prepare an H-type modified zeolite, 1 liter (L) of about 1 M ammonium chloride (NH 4 Cl) was charged with 200 grams (g) of natural zeolite in the form of Ca-type clinoptilite, and for 10 to 15 hours. Stirring was performed. Thereafter, the modified zeolite was separated by a filter, and then washed three to five times with about 5 L of distilled water in order to remove excess salt. The washed modified zeolite was dried for 10-15 hours in an oven maintained at a temperature of 100 ° C. In order to remove ammonia from the dried modified zeolite, heat treatment was performed at a temperature of about 450 ° C., and ground to an average particle diameter of 5 to 20 μm to prepare an H-type modified zeolite powder.

AgAg /H-형 개질 제올라이트의 제조Preparation of / H-Type Modified Zeolites

제조된 H-형 개질 제올라이트를 이용하여 Ag 및 H(Ag/H)-형 개질 제올라이트를 제조하였다. 위에서 설명한 방법에 따라 제조된 H-형 개질 제올라이트 5 g을 1.0 내지 2.0 × 10-3 M 질산은(AgNO3) 수용액 약 100 ㎖에 투입하여 약 24시간 동안 교반을 하면서 이온 교환 반응이 진행되도록 하였다. 이후 약 100 ℃의 온도에서 10 내지 15시간 동안 건조를 시킨 후 평균 입경이 5 내지 20 ㎛가 되도록 분쇄를 하여 Ag 및 H-형 개질 제올라이트 분말을 제조하였다. Ag and H (Ag / H) -type modified zeolites were prepared using the prepared H-type modified zeolites. 5 g of the H-type modified zeolite prepared according to the method described above was added to about 100 ml of an aqueous solution of 1.0 to 2.0 × 10 −3 M silver nitrate (AgNO 3 ) to allow an ion exchange reaction to proceed while stirring for about 24 hours. After drying for 10 to 15 hours at a temperature of about 100 ℃ and pulverized to an average particle diameter of 5 to 20 ㎛ to prepare Ag and H-type modified zeolite powder.

2. 코팅제 제조 2. Manufacture of coating

위에서 설명한 방법에 따라 제조된 은 이온-개질 제올라이트, 또는 은 및 수소- 개질 제올라이트를 사용하여 코팅제를 제조하였다. Coatings were prepared using silver ion-modified zeolites or silver and hydrogen-modified zeolites prepared according to the methods described above.

코팅제는 포장지의 사용과정에서 사용될 수 있는 결합제 또는 보존제와 혼합될 수 있고, 그리고 토르말린과 같은 기능제가 추가될 수 있다. The coating may be mixed with a binder or preservative that may be used in the use of the wrapper, and a functional agent such as tourmaline may be added.

결합제 또는 보존제는 아크릴, PVC(polyvinyl chloride) 또는 EVA( Ethylene-vinyl acetate)와 같은 공지의 공중합 수지로 제조될 수 있지만 바람직하게는 유해 성분의 방출 가능성을 가지지 않는 전분 또는 탄산칼슘이 될 수 있다. 사용 가능한 보존제는 셀룰로오스 유도체, 폴리아크릴아미드, 폴리염화디알릴디메틸 암모늄, 폴리에틸렌아민 또는 폴리에틸렌옥사이드(PEO)과 같은 중합체를 포함한다. 또한 보존제는 결합력을 개선하기 위하여 명반, 염화알루미늄 또는 질산알루미 늄과 같은 알루미늄 화합물 또는 옥시에틸렌 지방아민과 같은 유화제를 포함할 수 있다. The binder or preservative may be made from a known copolymerized resin such as acrylic, polyvinyl chloride (PVC) or ethylene-vinyl acetate (EVA), but may preferably be starch or calcium carbonate that does not have the potential for release of harmful components. Preservatives that can be used include polymers such as cellulose derivatives, polyacrylamides, polyallyldimethyldimethyl ammonium, polyethyleneamines or polyethylene oxides (PEO). Preservatives may also include emulsifiers such as alum, aluminum compounds such as aluminum chloride or aluminum nitrate or oxyethylene fatty amines to improve binding.

코팅제의 제조를 위하여 은 이온-개질 제올라이트 또는 은 및 수소-개질 제올라이트는 5 내지 20 ㎛, 바람직하게는 10 내 15 ㎛의 분말 상태로 만들어진다. 분말 상태의 개질 제올라이트는 물 또는 용제에 물 또는 용제 대비 40 내지 60 중량%로 물 또는 용제와 혼합이 된다. 용제는 예를 들어 크실렌, 케톤, 또는 메틸 에틸 케톤이 될 수 있다. 이후 전분 또는 탄산칼슘과 같은 보존제가 제올라이트 중량 대비 5 내지 15 중량 %로 첨가된다. 그리고 필요한 경우 개질 제올라이트 중량 대비 3 내지 5 wt%의 토르말린이 첨가될 수 있다. Silver ion-modified zeolites or silver and hydrogen-modified zeolites are made in powder form of 5 to 20 μm, preferably 10 to 15 μm for the preparation of coatings. Powdered modified zeolite is mixed with water or solvent in water or solvent at 40 to 60% by weight relative to water or solvent. The solvent can be, for example, xylene, ketone, or methyl ethyl ketone. Preservatives such as starch or calcium carbonate are then added at 5 to 15% by weight relative to the zeolite weight. And, if necessary, 3 to 5 wt% of tourmaline based on the weight of the modified zeolite may be added.

이와 같이 코팅제는 물 또는 용제; 물 또는 용제 중량 대비 40 내지 60 중량 %의 개질 제올라이트; 개질 제올라이트 중량 대비 5 내지 15 중량 %의 보존제를 포함할 수 있고, 추가로 필요한 경우 물 또는 용제 중량 대비 1 내지 3 wt%의 유화제, 또는 개질 제올라이트 중량 대비 3 내지 5 중량%의 토르말린을 포함할 수 있다. 그리고 용제 및 보존제는 위에서 제시된 물질 중 적어도 하나의 물질 또는 이 분야에서 공지된 임의의 물질이 될 수 있고, 그리고 개질 제올라이트는 은 이온-개질 제올라이트, 또는 은 및 수소-개질 제올라이트가 될 수 있다.Thus, the coating agent is water or a solvent; 40 to 60 weight percent modified zeolite by weight of water or solvent; May contain from 5 to 15% by weight of preservatives based on the weight of the modified zeolite, and may further comprise 1 to 3% by weight of emulsifier, or 3 to 5% by weight of tourmaline by weight of the modified zeolite, if necessary. have. And the solvent and preservative may be at least one of the materials set forth above or any material known in the art, and the modified zeolite may be silver ion-modified zeolite, or silver and hydrogen-modified zeolite.

아래에서 위와 같이 제조된 코팅제를 박스의 내면에 코팅하는 과정을 상세하게 설명한다.In the following it will be described in detail the process of coating the inner coating of the coating prepared as described above.

본 발명에 따른 코팅제는 임의의 포장지에 코팅이 될 수 있지만 바람직하게는 박스(box) 형태로 만들어지는 포장지의 내면에 코팅이 될 수 있다. 박스 형태의 포장지는 예를 들어 아래의 도 1에 제시된 것과 같은 골판지가 될 수 있다. 일반적인 포장지에 본 발명에 따른 코팅제가 도포되는 과정은 골판지에 도포되는 과정과 유사하므로 골판지를 예를 들어 설명을 하기로 한다. The coating agent according to the invention can be coated on any wrapping paper but preferably on the inner surface of the wrapping paper made in the form of a box. The wrapping paper in the form of a box may be, for example, corrugated paper as shown in FIG. 1 below. Since the process of applying the coating agent according to the present invention on a general packaging is similar to the process applied to the corrugated cardboard will be described as an example.

도 1의 (가)는 본 발명에 따른 코팅제를 골판지에 도포하는 과정을 개략적으로 도시한 것이고 그리고 (나)는 완성된 골판지의 단면도를 도시한 것이다. 1 (a) schematically shows the process of applying the coating agent to the cardboard according to the invention and (b) shows a cross-sectional view of the finished cardboard.

도 1의 (가)를 참조하면, 골판지를 형성하기 위한 인쇄지, 골심지, 원지는 각각 인쇄지 롤러(11a), 골심지 롤러(11b), 및 원지 롤러(11c)를 통하여 공급된다. 골심지 롤러(11b)를 통하여 공급되는 골심지의 한쪽 면은 스프레이 장치(12a)에 의하여 본 발명에 따른 코팅제에 의하여 코팅이 된다. 코팅제는 위에서 이미 설명을 한 것처럼 은 이온-개질 제올라이트 또는 은 및 수소 개질 제올라이트를 포함할 수 있고, 선택적으로 토르말린을 포함할 수 있다. 골심지는 골 형성기(13)를 통과하면서 골이 형성되고 그리고 접착기(14)로 투입이 된다. 접착기(14)는 골심지의 필요한 부분에 접착제를 부여한다. 접착제가 부여된 골심지는 히터(15)에 의하여 가열이 되면서 가압 롤러(16)에 의하여 인쇄지 및 원지에 접착이 된다. 이후 냉각기(17)에 의하여 냉각이 되고 그리고 정해진 모양으로 절단이 되어 박스(box) 형태로 제작되는 것은 공지된 공정에 따라 진행이 될 수 있다. 본 발명에 따른 골판지의 제조 공정의 경우 코팅제는 스프레이 장치(12b)에 의하여 골이 생성되기 이전에 골심지의 아래쪽 면에 코팅이 되지만, 도 1의 (가)에 도시된 것처럼, 원지의 아래쪽 면에 코팅 장치(12b)에 의하여 골판지에 코팅이 될 수도 있다. 이와 같이 코팅 장치(12b)에 의하여 원지의 아래쪽 면에 코팅이 되는 경우 이 분야에서 공지된 방 법에 따라 롤 코팅법, 침지법 또는 스프레이 법와 같은 방법으로 코팅이 될 수 있다. 이와 같은 방법에 따라 제조된 골판지가 도 1의 (나)에 도시되어 있다. 도 1의 (나)는 박스로 제조되는 경우 안쪽 면에 해당하는 원지의 아래쪽에 코팅제가 도포된 경우를 도시한 것이다. 인쇄지(20)에 인쇄 및 골심지(21)의 형성은 이 분야에서 공지된 방법에 따라 이루어지고 그리고 원지(22)의 아래쪽에 도포되는 코팅 면(23)의 두께는 50 내지 200 ㎛가 될 수 있다. 실질적으로 골심지의 아래쪽 면에 코팅이 되는 경우 본 발명에 따른 코팅제 자체의 보존성이 우수하지만 내용물의 변형 방지와 같은 코팅제 본연의 효과는 원지(22)의 아래쪽에 코팅 면(23)이 형성되는 것이 유리하다. Referring to Fig. 1A, printing paper, corrugated paper, and base paper for forming corrugated paper are supplied through the printing paper roller 11a, the corrugated paper roller 11b, and the paper roller 11c, respectively. One side of the core core supplied through the core core roller 11b is coated by the coating agent according to the present invention by the spray device 12a. The coating may include silver ion-modified zeolites or silver and hydrogen-modified zeolites, as described above, and may optionally include tourmaline. The bone wick is formed while passing through the bone forming machine 13 and is fed into the bonding machine 14. The gluer 14 imparts adhesive to the required portion of the core core. The core coated with the adhesive is heated by the heater 15 and adhered to the printing paper and the base paper by the pressure roller 16. After being cooled by the cooler 17 and cut into a predetermined shape, the box may be manufactured according to a known process. In the manufacturing process of the corrugated cardboard according to the present invention, the coating agent is coated on the lower surface of the corrugated medium before the bone is produced by the spray device 12b, but as shown in (a) of FIG. It may be coated on the corrugated cardboard by the coating device 12b. As such, when the bottom surface of the base is coated by the coating apparatus 12b, the coating may be performed by a method such as a roll coating method, an immersion method or a spray method according to a method known in the art. Corrugated cardboard produced according to this method is shown in FIG. Figure 1 (b) shows the case where the coating is applied to the lower side of the base paper corresponding to the inner side when manufactured in a box. The printing on the printing paper 20 and the formation of the corrugated paper 21 are made according to methods known in the art and the thickness of the coating surface 23 applied on the underside of the base paper 22 may be 50 to 200 μm. have. When the coating on the lower surface of the corrugated material is substantially excellent in the preservation of the coating itself according to the present invention, the inherent effect of the coating such as preventing deformation of the contents is advantageous that the coating surface 23 is formed on the lower side of the base paper 22 Do.

골판지가 다층으로 형성되는 경우, 코팅 면은 가장 아래쪽 면에 형성될 수 있고, 만약 골심지에 코팅이 되는 경우라면 가장 아래쪽에 위치하는 골심지의 아래쪽 면이 코팅이 되거나 또는 각각의 골심지가 코팅이 될 수 있다. In the case where the corrugated cardboard is formed in multiple layers, the coating surface may be formed at the bottom surface. If the coating is applied to the core core, the bottom surface of the core core located at the bottom may be coated or each core core may be coated. have.

위에서 본 발명에 제시된 실시 예를 이용하여 상세하게 설명이 되었지만, 제시된 실시 예는 본 발명의 이해를 위한 것으로 이 분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상의 범위 내에서 제시된 실시 예에 대한 다양한 변형 및 수정 발명을 만들 수 있을 것이다. 본 발명은 이러한 변형 및 수정 발명에 의하여 제한되지 않으며 다만 아래에 첨부된 청구범위에 의해서만 제한된다. Although described in detail using the embodiments set forth in the present invention above, the presented embodiments are for the understanding of the present invention for those of ordinary skill in the art for the embodiments presented within the scope of the spirit of the present invention Various variations and modifications of the invention may be made. The present invention is not limited by these modifications and variations, but only by the claims appended below.

본 발명에 따른 기능성 박스는 내부 면이 개질 제올라이트로 코팅이 되어 내용물이 본래의 특성을 유지하면서 오랫동안 보관될 수 있도록 한다. 이로 인하여 장거리 수송 또는 장기간의 보관을 필요로 하는 내용물의 포장지로 사용될 수 있다는 이점을 가진다. 이와 같은 효과는 개질된 제올라이트로부터 발생되는 은 이온의 항균성 및 제올라이트 그 자체의 탈취 능력으로 인한 것이다. The functional box according to the present invention is coated on its inner surface with a modified zeolite so that the contents can be stored for a long time while maintaining the original properties. This has the advantage that it can be used as a wrapper for contents requiring long distance transportation or long term storage. This effect is due to the antimicrobial activity of the silver ions generated from the modified zeolite and the deodorizing ability of the zeolite itself.

Claims (5)

원지, 골심지, 및 인쇄지로 형성된 골판지로 제조되는 기능성 박스에 있어서, In the functional box made of corrugated paper formed of paper, corrugated paper, and printing paper, 골심지 또는 원지가 은 이온-개질 제올라이트, 또는 은 및 수소-개질 제올라이트를 포함하는 코팅제로 50 내지 200 ㎛의 두께로 코팅이 된 것을 특징으로 하는 기능성 박스.Functional box, characterized in that the core or base paper is coated with a thickness of 50 to 200 ㎛ with a silver ion-modified zeolite or a coating comprising silver and hydrogen-modified zeolite. 청구항 1에 있어서, 상기 은 이온-개질 제올라이트, 또는 은 및 수소 개질 제올라이트는 Ca-형 클리놉티라이트 천연 제올라이트로부터 개질된 것을 특징으로 하는 기능성 박스. The functional box of claim 1, wherein the silver ion-modified zeolite, or silver and hydrogen modified zeolite, are modified from a Ca-type clinopritelite natural zeolite. 청구항 1에 있어서, 상기 은 이온-개질 제올라이트 또는 은 및 수소 개질 제올라이트는 질산은으로 개질이 되고 그리고 5 내지 20 ㎛의 분말 형태인 것을 특징으로 하는 기능성 박스. The functional box of claim 1, wherein the silver ion-modified zeolite or silver and hydrogen modified zeolite are modified with silver nitrate and are in powder form of 5-20 μm. 청구항 1에 있어서, 상기 코팅제는 물 또는 용제; 물 또는 용제 중량 대비 40 내지 60 중량 %의 은 또는 은 및 수소 개질 제올라이트; 개질 제올라이트 중량 대비 5 내지 15 중량 %의 보존제를 포함할 수 있고, 상기에서 보존제는 전분, 탄산칼슘, 명반, 염화알루미늄, 또는 질산알루미늄이 되는 것을 특징으로 하는 기능성 박스. The method according to claim 1, wherein the coating agent is water or a solvent; 40 to 60% by weight of silver or silver and hydrogen modified zeolites by weight of water or solvent; A functional box comprising 5 to 15% by weight of a preservative based on the weight of the modified zeolite, wherein the preservative is starch, calcium carbonate, alum, aluminum chloride, or aluminum nitrate. 청구항 4에 있어서, 상기 코팅제는 개질 제올라이트 중량 대비 3 내지 5 중량%의 토르말린을 더 포함하는 기능성 박스. The functional box of claim 4, wherein the coating further comprises 3 to 5 wt% of tourmaline based on the weight of the modified zeolite.
KR1020060121957A 2006-12-05 2006-12-05 Packing box with antibiotic and deodorizing function KR20080051237A (en)