KR101056526B1 - Anionic waterproof cardboard and its manufacturing method - Google Patents
Anionic waterproof cardboard and its manufacturing method Download PDFInfo
- Publication number
- KR101056526B1 KR101056526B1 KR1020090013100A KR20090013100A KR101056526B1 KR 101056526 B1 KR101056526 B1 KR 101056526B1 KR 1020090013100 A KR1020090013100 A KR 1020090013100A KR 20090013100 A KR20090013100 A KR 20090013100A KR 101056526 B1 KR101056526 B1 KR 101056526B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating composition
- weight
- corrugated cardboard
- tourmaline
- liner paper
- Prior art date
Abstract
본 발명은 음이온 내수골판지 및 이의 제조방법에 관한 것으로, 골판지를 구성하는 라이너지의 내측면을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 토르마린의 음이온 발생이나 원적외선 방사 기능을 통해 포장상자의 내측에 포장되는 야채 및 과일 등과 같은 식품의 신선도를 장기간 유지시킬 수 있도록 함에 그 목적이 있다. 이를 위해 구성되는 본 발명의 음이온 내수골판지는 폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 제조한 접착제 50∼85중량%, 폴리우레탄 에멀젼(polyurethane emulsion) 10∼45중량% 및 토르마린 분말 5∼40중량%의 비율로 혼합 조성된 코팅제 조성물을 골판지를 구성하는 라이너지의 내측면 또는 양측면에 일정두께 도포하여 열경화시킨 후 골심지와 라이너지를 접착시키는 구성으로 이루어진다. 이처럼 구성된 골판지를 이용하여 제조된 포장상자를 통해 식품류를 포장하게 되면 토르마린으로부터 음이온과 원적외선이 방사되어 야채 및 과일 등과 같은 식품의 신선도를 장기간 유지시키고, 잔류 농약 성분을 제거시키는 효과를 얻을 수 있게 된다.The present invention relates to an anion-resistant corrugated cardboard and a method for manufacturing the same, wherein the inner surface of the liner paper constituting the corrugated cardboard is coated with a tourmaline-containing coating composition, thereby packing the inside of the packaging box through anion generation or far-infrared radiation function of tourmaline. The purpose is to be able to maintain the freshness of foods such as vegetables and fruits for a long time. Anionic water-resistant corrugated cardboard of the present invention configured for this is 50 to 85% by weight of an adhesive prepared by dissolving polyvinyl alcohol and water in the presence of benzoyl peroxide and a mixture of vinyl acetate and an emulsifier, and a polyurethane emulsion (polyurethane). emulsion) A composition in which the coating composition, mixed at a ratio of 10 to 45% by weight and tourmaline powder 5 to 40% by weight, is applied to a predetermined thickness on the inner side or both sides of the liner paper constituting the corrugated paper, followed by thermosetting to bond the core core and the liner paper. Is done. When food is packaged through a packaging box manufactured using such a cardboard, negative ions and far-infrared rays are radiated from tourmaline to maintain the freshness of foods such as vegetables and fruits for a long time, and remove residual pesticides. .
골판지, 골판지 라이너, 토르마린, 음이온, 원적외선 Corrugated cardboard, corrugated liner, tourmaline, anion, far infrared
Description
본 발명은 음이온 내수골판지 및 이의 제조방법에 관한 것으로, 더욱 상세하게는 골판지를 구성하는 라이너지의 내측면을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리하여 토르마린의 음이온 발생이나 원적외선 방사기능을 제공함으로써 포장상자의 방수기능을 제공함은 물론 포장상자의 내측에 포장되는 야채 및 과일 등과 같은 식품의 신선도를 장기간 유지시킬 수 있도록 하는 음이온 내수골판지 및 이의 제조방법에 관한 것이다.The present invention relates to an anion-resistant corrugated cardboard and a method for manufacturing the same, and more particularly, to package the inner surface of the liner paper constituting the corrugated cardboard through a coating composition containing tourmaline to provide anion generation or far-infrared radiation function of tourmaline It provides a waterproof function of the box as well as an anion-resistant corrugated cardboard and a method of manufacturing the same to be able to maintain the freshness of foods such as vegetables and fruits that are packaged inside the packaging box for a long time.
일반적으로 골판지는 물결 모양으로 골을 만든 골심지에 라이너지라고 하는 면이 반듯하고 빳빳한 판지를 접착시켜 완충도를 높인 것으로, 이러한 골판지는 완충도를 더욱 높이기 위하여 이중으로 만든 것도 있으며, 주로 물품을 포장하기 위한 포장상자를 만드는데 쓰인다.In general, corrugated cardboard is a corrugated corrugated cardboard made of corrugated corrugated paper, which is lined with soft, firm cardboard to increase the cushioning. Used to make packing boxes for
특히, 전술한 바와 같은 골판지로 만든 포장상자를 사용하는 목적은 같은 크기의 나무상자에 비하여 목재의 사용량이 1/10 이하이므로, 목재 자원의 이용 합리 화라는 측면에서도 매우 유익할 뿐만 아니라 값이 저렴하기 때문이다.In particular, the purpose of using the packaging box made of corrugated cardboard as described above is that the use of wood is less than 1/10 compared to the wooden box of the same size, it is very advantageous in terms of rationalization of the use of wood resources and low cost Because.
한편, 전술한 바와 같은 골판지의 일반적인 제조방법은 판지초지기에 의하여 생산된 평량 180∼400g/㎡의 라이너지와 평량 120∼150g/㎡의 골심지 두루마리를 코르게이터(Corrugator)에 걸어 기계를 작동시키면 골심지에 물결 모양의 일정한 골이 만들어짐과 동시에 라이너지와 접착되어 골판지가 만들어진다. 이러한 골판지는 용도에 따라서 외부포장용 및 내부포장용 골판지로 나누어진다.On the other hand, the general manufacturing method of the corrugated paper as described above is to operate the machine by hanging the corrugator (line corrugator) with a liner paper of 180 ~ 400g / ㎡ basis weight and 120 ~ 150g / ㎡ corrugated paper produced by cardboard paper machine Corrugated cardboard is made by adhering to the liner paper at the same time as the regular wavy shape is made. Such corrugated cardboard is divided into corrugated cardboard for external packaging and internal packaging, depending on the application.
아울러, 전술한 바와 같은 골판지로 포장상자를 만드는 과정은 포장될 내용물에 따라서 먼저 일정한 상자의 양식을 결정한 다음, 골판지 표면에 필요한 것들을 인쇄하고, 그것을 슬로터에서 전개도대로 재단하거나 꺾을 곳에 선을 넣고 평철사나 풀 또는 점착 테이프로 접합하게 된다.In addition, the process of making a packaging box from corrugated cardboard as described above first determines the form of a certain box according to the contents to be packaged, and then prints the necessary items on the surface of the cardboard, and cuts them according to the flat pattern in the slotter, or puts a line into a flat wire or It is glued with glue or adhesive tape.
전술한 바와 같이 골판지를 통해 제조된 포장상자의 장점은 무게가 가벼워서 겹쳐쌓기가 쉬울 뿐만 아니라, 운반과 저장에 편리함은 물론, 접을 수 있고, 외부 충격에 쉽게 손상을 입지 않는다는데 있다. 그리고, 골판지로 제조된 포장상자의 용도로는 식품, 전기제품, 기계부품, 잡화. 청과물, 육류 및 어류 등 매우 광범위하나 초중량 화물의 포장에는 적합하지 않다. As described above, the advantages of the packaging box manufactured by corrugated cardboard are light and easy to stack, and are convenient for transport and storage, as well as being foldable and not easily damaged by external impact. And, the use of the packaging box made of cardboard, food, electrical appliances, mechanical parts, miscellaneous goods. Very wide range of fruits and vegetables, meat and fish, but not suitable for the packaging of very heavy cargo.
한편, 종래의 골판지로 만든 골판지 상자는 골판지가 갖고 있는 완충성에 의하여 상자에 보관된 물품이 손상되지 않도록 하는 기능에 주안점을 두고 제작된 것이어서 상자에 보관되는 농산물, 축산물, 수산물 및 임산물과 같은 각종 자연 식품의 신선도를 장기간 유지하는 역할은 기대하기 어려웠다. 더욱이, 농산물을 재배할 때 해충이나 잡초를 제거하기 위하여 농약을 많이 사용하므로 수확된 농산물에 는 농약성분이 잔류하는 On the other hand, the cardboard box made of conventional cardboard is made with a focus on the function of preventing damage to the goods stored in the box by the buffering properties of the cardboard, so that various natural products such as agricultural products, livestock, fishery products and forest products stored in the box The role of maintaining food freshness for a long time was difficult to expect. In addition, when growing agricultural products, pesticides are used to remove pests and weeds.
또한, 종래의 골판지가 가지는 문제점을 해결하기 위한 방안으로 특허 제777083호에는 옥수수 전분 68.5∼79.5중량%, 옥수수 전분과 동일한 입경을 갖는 제올라이트 분말 20∼30중량%, 미생물이 포함된 황토, 가성소다와 박스강화제 0.5∼2중량%로 이루어진 혼합물을 물에 넣고 혼합하여 이루어진 접착제를 이용한 골판지 상자가 제공되고는 있으나, 효과가 만족스럽지 못하였다.In addition, in order to solve the problems of the conventional corrugated cardboard, Patent No. 777083, 68.5-79.5% by weight of corn starch, 20-30% by weight of zeolite powder having the same particle size as corn starch, ocher containing microorganisms, caustic soda Corrugated cardboard box using an adhesive made by mixing a mixture of 0.5 to 2% by weight with a box strengthening agent was provided, but the effect was not satisfactory.
본 발명은 전술한 종래 기술의 제반 문제점을 해결하기 위한 것으로, 골판지를 구성하는 라이너지의 내측면을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 토르마린의 음이온 발생이나 원적외선 방사 기능을 통해 포장상자의 내측에 포장되는 야채 및 과일 등과 같은 식품의 신선도를 장기간 유지시킬 수 있도록 하는 음이온 내수골판지 및 이의 제조방법을 제공함에 그 목적이 있다.The present invention is to solve the above-mentioned problems of the prior art, by coating the inner surface of the liner paper constituting the corrugated cardboard with a coating composition containing tourmaline to generate an anion or far-infrared radiation function of the tourmaline inside the packaging box It is an object of the present invention to provide an anion-resistant corrugated cardboard and a method of manufacturing the same to be able to maintain the freshness of foods such as vegetables and fruits to be packaged for a long time.
본 발명에 따른 기술의 다른 목적은 골판지를 구성하는 라이너지의 내측을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 토르마린의 음이온 발생이나 원적외선 방사 기능을 통해 포장상자의 내측에 포장되는 야채 및 과일 등과 같은 식품의 잔류 농약 성분을 일정농도 제거할 수 있도록 함에 있다.Another object of the technology according to the present invention is to coat the inside of the liner constituting the corrugated cardboard through the coating composition containing tourmaline such as vegetables and fruits to be packaged inside the packaging box through the generation of negative ions or far-infrared radiation of the tourmaline The purpose is to remove a certain concentration of residual pesticides in food.
아울러, 본 발명에 따른 기술은 골판지를 구성하는 라이너지의 내측을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 코팅제 조성물의 방수기능을 통해 포장상자에 방수성을 제공하여 액체가 발생하는 식품류의 포장이 가능하도 록 함에 그 목적이 있다.In addition, the technology according to the present invention by coating the inside of the liner paper constituting the corrugated cardboard with a coating composition containing tourmaline to provide a waterproofing to the packaging box through the waterproofing function of the coating composition to enable the packaging of foods in which liquid is generated Its purpose is to do so.
전술한 바와 같은 목적을 달성하기 위해 구성되는 본 발명은 다음과 같다. 즉, 본 발명에 따른 음이온 내수골판지는 폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 제조한 접착제 50∼85중량%, 폴리우레탄 에멀젼(polyurethane emulsion) 10∼45중량% 및 토르마린 분말 5∼40중량%의 비율로 혼합 조성된 코팅제 조성물을 골판지를 구성하는 라이너지의 내측면 또는 양측면에 일정두께 도포하여 열경화시킨 후 골심지와 라이너지를 접착시키는 구성으로 이루어진다.The present invention is configured to achieve the object as described above is as follows. That is, the anionic water-resistant corrugated paper according to the present invention is a 50 to 85% by weight adhesive prepared by dissolving polyvinyl alcohol and water in the presence of benzoyl peroxide and a mixture of vinyl acetate and an emulsifier, polyurethane emulsion (polyurethane emulsion 10) to 45% by weight of tourmaline powder and 5 to 40% by weight of the tourmaline powder coating composition is applied to a certain thickness on the inner side or both sides of the liner paper constituting the corrugated sheet and heat-set to bond the core core and the liner paper Is done.
전술한 바와 같은 본 발명의 구성에서 코팅제 조성물의 점도는 30∼2000cps로 함이 보다 양호하고, 그리고 코팅제 조성물의 도포량은 3∼15g/m2의 양으로 도포됨이 보다 양호하다.In the composition of the present invention as described above, the viscosity of the coating composition is more preferably 30 to 2000 cps, and the coating amount of the coating composition is more preferably applied in an amount of 3 to 15 g / m 2 .
그리고, 본 발명에 따른 구성에서 라이너지에 도포된 코팅제 조성물의 경화조건은 140∼180℃의 온도조건하에서 1∼10초간 열을 가하여 코팅제 조성물을 열경화시키는 구성으로 이루어질 수 있다.In addition, the curing conditions of the coating composition applied to the liner in the configuration according to the present invention may be configured to heat the coating composition by applying heat for 1 to 10 seconds under a temperature condition of 140 ~ 180 ℃.
한편, 본 발명의 다른 특징인 음이온 내수골판지 제조방법은 (a) 폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 접착제를 제조하는 단계; (b) 접착제 50∼85중량%, 폴리우레탄 에멀젼 10∼45중량% 및 토르마린 분말 5∼40중량%의 비율로 혼합하여 코팅제 조성물을 제조하는 단계; (c) 코팅제 조성물을 골판지를 구성하는 라이너지의 내측면 또는 양측면 상에 일정두께로 도포하는 단계; (d) 라이너지에 도포된 코팅제 조성물을 일정온도조건하에서 열경화시키는 단계; 및 (e) 코팅제 조성물이 도포되어 열경화된 라이너지를 골심지의 내외측에 접착시켜 골판지를 제조하는 단계를 포함한 구성으로 이루어진다.On the other hand, the method of producing an anionic water-resistant corrugated cardboard of another feature of the present invention comprises the steps of: (a) preparing an adhesive by polymerizing a mixture of polyvinyl alcohol and water in the presence of benzoyl peroxide and a mixture of vinyl acetate alcohol and an emulsifier; (b) mixing the adhesive in an amount of 50 to 85% by weight, 10 to 45% by weight of polyurethane emulsion, and 5 to 40% by weight of tourmaline powder to prepare a coating composition; (c) applying the coating composition to a predetermined thickness on the inner side or both sides of the liner paper constituting the cardboard; (d) thermally curing the coating composition applied to the liner under constant temperature conditions; And (e) applying a coating composition to adhere the thermosetting liner to the inside and outside of the corrugated cardboard to produce a corrugated cardboard.
전술한 바와 같은 본 발명에 따른 단계(b)의 과정에서 코팅제 조성물의 점도는 30∼2000cps로 함이 보다 양호하고, 그리고 단계(c)의 과정에서 코팅제 조성물의 도포량은 3∼15g/m2의 양으로 도포됨이 보다 양호하다.In the process of step (b) according to the present invention as described above, the viscosity of the coating composition is more preferably 30 to 2000cps, and in the process of step (c), the coating amount of the coating composition is 3 to 15 g / m 2 . It is better to apply in amounts.
아울러, 본 발명에 따른 단계(d)의 코팅제 조성물을 열경화시키는 조건은 140∼180℃의 온도조건하에서 1∼10초간 열을 가하여 코팅제 조성물의 열경화가 이루어질 수 있도록 한 구성으로 이루어질 수 있다.In addition, the conditions for thermosetting the coating composition of step (d) according to the present invention may be made of a configuration that allows the thermal curing of the coating composition by applying heat for 1 to 10 seconds under a temperature condition of 140 ~ 180 ℃.
본 발명에 따른 음이온 내수골판지는 라이너지의 내측면을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 토르마린의 음이온 발생이나 원적외선 방사 기능을 통해 포장상자의 내측에 포장되는 야채 및 과일 등과 같은 식품의 신선도를 장기간 유지시킬 수 있는 효과가 발현된다.Anionic water-resistant cardboard according to the present invention by coating the inner surface of the liner through a coating composition containing tourmaline to improve the freshness of foods such as vegetables and fruits to be packaged inside the packaging box through the generation of anion or far-infrared radiation of the tourmaline An effect that can be maintained for a long time is expressed.
또한, 본 발명의 기술에 따르면 골판지를 구성하는 라이너지의 내측을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 토르마린의 음이온 발생이나 원적외선 방사 기능을 통해 포장상자의 내측에 포장되는 야채 및 과일 등과 같 은 식품의 잔류 농약 성분을 일정농도 제거할 수가 있다.In addition, according to the technology of the present invention by coating the inside of the liner paper constituting the corrugated cardboard through the coating composition containing tourmaline, such as vegetables and fruits to be packaged inside the packaging box through the generation of negative ions or far-infrared radiation of the tourmaline The residual pesticide content of the food can be removed at a certain concentration.
아울러, 본 발명에 따른 기술의 또 다른 효과로는 골판지를 구성하는 라이너지의 내측을 토르마린이 함유된 코팅제 조성물을 통해 코팅처리함으로써 코팅제 조성물의 방수기능을 통해 포장상자에 방수성을 제공하여 액체가 발생하는 식품류의 포장이 가능하다는 장점이 있다.In addition, another effect of the technology according to the present invention by coating the inside of the liner paper constituting the corrugated cardboard through the coating composition containing tourmaline to provide a waterproof to the packaging box through the waterproof function of the coating composition to generate liquid There is an advantage in that food packaging is possible.
이하에는 본 발명에 따른 음이온 내수골판지 및 이의 제조방법에 대하여 상세하게 설명하기로 한다.Hereinafter will be described in detail with respect to the anion-resistant corrugated cardboard according to the present invention and its manufacturing method.
본 발명에 따른 음이온 내수골판지는 폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 제조한 접착제 50∼85중량%, 폴리우레탄 에멀젼(polyurethane emulsion) 10∼45중량% 및 토르마린 분말 5∼40중량%의 비율로 혼합 조성되는 코팅제 조성물을 골심지와 접합되는 라이너지의 내측면 또는 양측면 상에 도포하여 열경화시킨 다음, 코팅제 조성물이 코팅처리된 라이너와 골심지를 접합한 것으로 특징지워진다.Anionic water-resistant corrugated cardboard according to the present invention is a 50 to 85% by weight adhesive prepared by dissolving polyvinyl alcohol and water in the presence of benzoyl peroxide and a mixture of vinyl acetate and an emulsifier, polyurethane emulsion (polyurethane emulsion) 10 The coating composition mixed at a ratio of ˜45% by weight and tourmaline powder 5-40% by weight is applied on the inner side or both sides of the liner paper to be bonded to the core wick and thermally cured, and then the liner and the core wick coated with the coating composition are coated. It is characterized by bonding.
또한, 본 발명에 따른 음이온 내수골판지의 제조방법은 (a) 폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 접착제를 제조하는 단계; (b) 접착제 50∼85중량%, 폴리우레탄 에멀젼 10∼45중량% 및 토르마린 분말 5∼40중량%의 비율로 혼합하여 코팅제 조성물을 제조하는 단계; (c) 코팅제 조성물을 골판지를 구성하는 라이너지의 내측면 또는 양측면 상에 일정두께로 도포하는 단계; (d) 라이너지에 도포된 코팅제 조성물을 일정온도조건하에서 열경화시키는 단계; 및 (e) 코팅제 조성물이 도포되어 열경화된 라이너지를 골심지의 내외측에 접착시켜 골판지를 제조하는 단계를 포함한 구성으로 특징지워진다.In addition, the method for producing an anionic water-resistant corrugated cardboard according to the present invention comprises the steps of: (a) dissolving polyvinyl alcohol and water in the presence of benzoyl peroxide and mixing vinyl acetate alcohol with an emulsifier to prepare an adhesive; (b) mixing the adhesive in an amount of 50 to 85% by weight, 10 to 45% by weight of polyurethane emulsion, and 5 to 40% by weight of tourmaline powder to prepare a coating composition; (c) applying the coating composition to a predetermined thickness on the inner side or both sides of the liner paper constituting the cardboard; (d) thermally curing the coating composition applied to the liner under constant temperature conditions; And (e) applying a coating composition to bond the thermosetting liner paper to the inside and outside of the corrugated cardboard to produce a corrugated cardboard.
한편, 본 발명에서 사용되는 접착제는 폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 제조한 것으로, 폴리비닐알콜과 물은 중량비로 9 : 1의 비율로 사용하며, 과산화벤조일은 촉매로서 사용된다. 이때, 폴리비닐알콜과 초산비닐알콜은 동일 당량으로 사용되는 것이 효과적이며, 통상의 중합 반응 조건하에서 반응시켜 제조한다.On the other hand, the adhesive used in the present invention is prepared by polymerizing a mixture of polyvinyl alcohol and water in the presence of benzoyl peroxide and a mixture of vinyl acetate and an emulsifier, and polyvinyl alcohol and water in a weight ratio of 9: 1. In proportions, and benzoyl peroxide is used as catalyst. At this time, it is effective to use polyvinyl alcohol and vinyl acetate alcohol in the same equivalents, and they are prepared by reacting under normal polymerization conditions.
특히, 본 발명에 따른 기술서는 접착제로써 폴리졸(상품명)을 시중에서 구입하여 사용하였다.In particular, the technique according to the present invention was purchased commercially available polysol (trade name) as an adhesive.
본 발명에서 접착제의 사용량이 50중량% 미만일 경우에는 토르마린의 접착력이 만족스럽지 못하여 토르마린이 탈리되는 문제점이 있고, 85중량%를 초과할 경우에는 다른 성분들의 사용량이 상대적으로 감소되어 본 발명에서 목적하는 효과를 얻을 수 없거나 작업성이 좋지 못한 단점이 있다.In the present invention, when the amount of the adhesive is less than 50% by weight, there is a problem in that the tourmaline is desorbed due to unsatisfactory adhesion of the tourmaline, and when the amount of the adhesive exceeds 85% by weight, the amount of the other components is relatively reduced, which is required in the present invention. There is a drawback that the effect is not obtained or the workability is poor.
또한, 본 발명에서 사용되는 폴리우레탄 에멀젼은 접착제, 폴리우레탄 에멀젼 및 토르마린 분말 구성되는 코팅제 조성물이 라이너지에 도포되기 용이하도록 하며, 골심지와의 접착이 용이하도록 하고, 내수성을 향상시키는 역할을 하는 것으로 전체 코팅제 조성물에 대하여 10∼45중량% 사용하는 것이 효과적이다.In addition, the polyurethane emulsion used in the present invention is to facilitate the coating composition consisting of adhesives, polyurethane emulsion and tourmaline powder to the liner, to facilitate adhesion with the core core, and to improve the water resistance as a whole It is effective to use 10 to 45% by weight based on the coating composition.
전술한 바와 같은 폴리우레탄 에멀젼의 사용량이 10중량% 미만일 경우에는 접착제, 폴리우레탄 에멀젼 및 토르마린 분말 구성되는 코팅제 조성물이 라이너지 에 도포되지 않거나 라이너지가 골심지와 잘 접착되지 않으며, 내수성이 만족스럽지 못한 단점이 있으며, 45중량%를 초과할 경우에는 본 발명에서 목적하는 효과를 얻을 수 없거나 토르마린이 탈리되는 경향이 있다.When the amount of the polyurethane emulsion as described above is less than 10% by weight, the coating composition consisting of the adhesive, the polyurethane emulsion and the tourmaline powder is not applied to the liner paper or the liner paper does not adhere well to the core core, and the water resistance is not satisfactory. If there is more than 45% by weight, the effect desired in the present invention may not be obtained or the tourmaline tends to detach.
본 발명에 따른 코팅제 조성물의 구성에서 토르마린(Tourmaline)은 지구상에 존재하는 광물 중에서 유일하게 영구적인 전기 특성을 가지고 있는 것으로, 극성결정체라고도 불려진다. 이러한 토르마린 광석에서 생성되는 음이온과 미약전류, 원적외선은 건강과 환경을 위해 세계적인 대학과 연구소에서 활발하게 연구가 진행되고 있는 획기적인 신물질이다.Tourmaline in the composition of the coating composition according to the present invention has the only permanent electrical properties among the minerals present on the earth, also called polar crystals. Negative ions, weak currents, and far-infrared rays generated from tourmaline ores are groundbreaking new materials being actively researched at universities and research institutes around the world for health and the environment.
전술한 바와 같은 토르마린은 굳기 : 7.0∼7.5, 비중 : 2.98∼3.20, 화학성분은 철·마그네슘·알칼리금속 등과 알루미늄의 복잡한 붕규산염이고, 형태는 다각형으로 입상, 괴상, 상하가 편평한 능면체 등 다양하다. 그리고, 토르마린의 쪼개짐은 분명하지 않고, 마찰에 의해서 전기가 생기며, 가열하면 양끝이 양·음으로 대전(帶電)하기 때문에 전기석이라는 이름이 붙여졌다. The tourmaline as described above has a hardness of 7.0-7.5, specific gravity of 2.98-3.20, and chemical composition of complex borosilicates of iron, magnesium, alkali metals, and aluminum, and various shapes such as polygonal, granular, blocky, flat and rhombohedral. Do. The tourmaline cleavage is not obvious, and electricity is generated by friction, and when heated, the tourmaline is named as a tourmaline because both ends are positively and negatively charged.
한편, 유전체라는 것은 전기장에 놓으면 전기분극이 생겨서 표면에 전하를 띄는 물질이지만 외부로부터 전기장이 가해지지 않더라도 처음부터 전기분극을 갖고 있는 극성결정체는 그 결정의 단위격자의 플러스 전하의 중심과 마이너스 전하의 중심이 본래 위치로부터 약간 벗어나 있기 때문에 결정의 양단이 전극을 만든다.On the other hand, a dielectric material is a substance that causes electric polarization when placed in an electric field and charges on the surface, but a polar crystal having electric polarization at the beginning even if an electric field is not applied from the outside is the center of the positive charge and the negative charge of the unit lattice of the crystal. Since the center is slightly off the original position, both ends of the crystal make up the electrode.
그리고, 토르마린의 플러스 전극과 마이너스 전극은 반드시 평행을 취해 있는 것이 아니고, 항상 불안정한 상태가 되어 마이너스 극으로부터 끊임없이 플러스 극을 향하여 전자가 흐르는 것이다. 또한, 토르마린이 직류 정전기를 계속 발생하는 것은 태양으로부터 전자가 끊임없이 들어오고 있기 때문이다. 이러한 전자에는 양이온과 음이온이 함께 있으나, 플로톤이라 불리우는 양이온은 지구의 대기권을 통과하지 못하고 태양풍 중 음이온만 통과한다. 태양으로부터 온 음이온이 토르마린의 플러스 전극에 흡수되어 마이너스 극으로 운반된다. 자연적으로 마이너스 전극측에서 음이온 전자 하나가 밀려나게 되어 이것이 플러스전극의 전기력선을 따라 튀어나가서 영구적인 전기의 흐름이 되는 것이다. 이 전류는 0.06mA의 미약전류이고, 인간의 신체에 가장 적합한 전술한 바와 같이 토르마린의 결정은 미약 전류를 계속 발생시키므로, 결정에 수분(H2O)이 닿으면 순간적으로 물을 전기분해한다. 또한, 토르마린은 공기 중에 포함된 수분(H2O)에도 작용하여 전기분해를 일으킨다. 이때의 전기분해는 물리작용에 의한 것으로 지속적이며, 안전하므로 활력있는 물로 변화시킨다. 토르마린에 의하여 물은 전기분해되고, 물분자(H2O)는 수소이온(H+)과 수산이온(OH-)로 분리되며, 분리된 수소이온은 마이너스 전극에 끌려서 거기에서 방출되는 전자와 결합되어 중화되고, 수소가스(H2)가 되어 증발하고, 수산이온(OH-)은 주변의 물 분자와 결합하여 히드록실(H3O2) 음이온이라고 하는 계면활성물질이 된다. 히드록실 이온은 산성화된 인체를 환원시키는 역활을 하며, 물을 최적의 pH7.4로 약 알카리화 시킬 뿐만 아니라 체내에 들어오면 면역기능(살균능력, 항균능력)이 높아지고, 혈액을 정화하며, 자율신경을 자극하여 교감신경의 흥분을 억제한다. 또한, 전술한 바와 같은 토르마린에서는 원적외선이 발생되는데 원적외선 발생량이 경이적으로 높은 수치로 나타내며, 강력한 열효과와 높은 침투력으로 인체에 혈액순환촉진 및 혈전용해 효과가 있다.The positive electrode and the negative electrode of tourmaline are not necessarily parallel, but are always in an unstable state, and electrons continuously flow from the negative pole toward the positive pole. In addition, tourmaline continues to generate direct current static electricity because electrons are constantly coming in from the sun. These electrons have a cation and an anion together, but a cation called Floton does not pass through the earth's atmosphere, but only an anion in the solar wind. Negative ions from the sun are absorbed by the tourmaline's positive electrode and transported to the negative pole. Naturally, anion electrons are pushed out of the negative electrode side, which then sticks out along the electric field line of the positive electrode and becomes a permanent flow of electricity. This current is a weak current of 0.06 mA, and as described above, which is most suitable for the human body, tourmaline crystals continue to generate a weak current, so when water (H 2 O) comes into contact with the crystal, water is electrolyzed instantaneously. Tourmaline also acts on the water (H 2 O) contained in the air, causing electrolysis. The electrolysis at this time is a physiologic action, which is continuous and safe, so it is changed to vital water. The water is electrolyzed by tourmaline, the water molecules (H 2 O) is a hydrogen ion (H +) and hydroxyl ions (OH -) are separated, the separated hydrogen ions combine with the electrons in tow emitted from there to the negative electrode is being neutralized, is evaporated to a hydrogen gas (H 2) and hydroxyl ions (OH -), in combination with the surrounding water molecules are surface-active substances, known as hydroxyl (H 3 O 2) anions. Hydroxyl ions play a role in reducing acidified human body, and not only alkalinize water to optimal pH7.4, but also increase immunity (sterilization ability, antibacterial ability) when it enters the body, purify blood, autonomously Stimulates the nerves to suppress the excitability of the sympathetic nerve. In addition, in the tourmaline as described above, far-infrared rays are generated, and the amount of far-infrared rays is generated at a remarkably high value, and there is a strong heat effect and a high penetration force to promote blood circulation and thrombolysis in the human body.
본 발명에서는 전술한 바와 같은 효능을 갖는 토르마린을 코팅제 조성물 전체 중량에 대하여 5∼40중량% 사용함으로써 토르마린의 음이온 발생과 원적외선 방사기능을 통해 야채 및 과일 등과 같은 식품의 신선도를 장기간 유지시키고, 잔류 농약 성분을 제거할 수 있도록 하였다. 이때, 토르마린의 사용량이 5중량% 미만일 경우에는 첨가 효과가 미약하고, 40중량%를 초과할 경우에는 첨가 상승 효과가 미약하여 경제적이지 못하다.
또한, 본 발명에서 토르마린은 평균 입경이 325메시(325mesh)의 입도를 갖도록 분쇄한 분말을 사용하는 것이 효과적이고, 입도가 작을수록 효과적이지만 제조에 곤란한 문제가 있고, 입도가 클수록 본 발명에서 목적하는 효과 발현이 미약해지고 라이너지에 도포하거나 골심지와 접착이 용이하지 못한 단점이 있다.In the present invention, by using 5 to 40% by weight of tourmaline having the above-described efficacy with respect to the total weight of the coating composition, to maintain the freshness of foods such as vegetables and fruits for a long time through the generation of anion and far-infrared radiation of the tourmaline, residual pesticide The ingredients were allowed to be removed. At this time, when the amount of tourmarin used is less than 5% by weight, the addition effect is weak, and when it exceeds 40% by weight, the synergistic effect of the addition is weak and it is not economical.
In addition, in the present invention, the tourmaline is effective to use a powder pulverized so that the average particle size has a particle size of 325 mesh (325 mesh), the smaller the particle size, the more effective but difficult to manufacture, the larger the particle size is the object of the present invention There is a drawback that the effect expression is weak and is not easy to apply to the liner paper or the core core.
전술한 바와 같이 구성되는 코팅제 조성물을 골심지와 접합되는 라이너지의 내측면 또는 양측면 상에 도포하고 열경화시킨 다음, 코르게이터를 이용하여 라이너지와 골심지를 접착시켜 골판지를 제조한다.The coating composition configured as described above is applied on the inner side or both sides of the liner paper to be bonded to the corrugated core and heat cured, and then the corrugator is bonded to the liner paper and the core core to prepare a corrugated cardboard.
한편, 전술한 바와 같이 제조된 코팅제 조성물의 도포는 라이너지 3∼15g/㎡으로 행하는 것이 효과적이고, 도포량이 3g/㎡ 미만일 경우에는 토르마린의 첨가 효과가 미약하고, 15g/㎡를 초과할 경우에는 첨가 상승 효과가 미약하여 경제적이지 못하다.On the other hand, it is effective to apply the coating composition prepared as described above with 3 to 15 g / m 2 of liner paper, and when the coating amount is less than 3 g / m 2, the effect of adding tourmaline is insignificant, and when it exceeds 15 g / m 2, The synergistic effect of addition is weak and not economical.
또한, 코팅제 조성물을 라이너지에 도포시 코팅제 조성물의 점도는 30∼2000cps 정도가 효과적이고, 점도가 낮으면 도포가 용이하지 못하며, 너무 높게 되면 도포 작업성이 만족스럽지 못하다.In addition, when the coating composition is applied to the liner paper, the viscosity of the coating composition is effective at about 30 to 2000 cps, and when the viscosity is low, the coating is not easy, and when the coating composition is too high, the coating workability is not satisfactory.
전술한 바와 같이 코팅제 조성물의 도포가 완료된 후에는 열롤러를 이용하여 도포된 코팅제 조성물을 열경화시킨다. 이때, 열롤러의 온도는 140∼180℃, 열롤러 접촉시간은 1∼10초 정도로 행하는 것이 효과적이지만 이에 한정되는 것은 아니고, 코팅제 조성물의 특성에 따라 반복실험을 통하여 적절히 조절할 수 있다.As described above, after the application of the coating composition is completed, the applied coating composition is thermosetted using a heat roller. At this time, the temperature of the hot roller is 140 ~ 180 ℃, the heat roller contact time is effective to perform about 1 to 10 seconds, but is not limited to this, can be appropriately adjusted through repeated experiments according to the characteristics of the coating composition.
다음의 실시 예는 본 발명을 좀 더 상세히 설명하는 것이지만 본 발명의 범주를 한정하는 것은 아니다.The following examples illustrate the invention in more detail, but do not limit the scope of the invention.
[실시 예 1][Example 1]
폴리비닐알콜과 물을 과산화벤조일 존재하에 용해시킨 것과 초산비닐알콜을 유화제와 혼합한 것을 중합 반응시켜 제조한 접착제(폴리졸(AE-300)) 70중량%, 폴리우레탄 에멀젼(강남화성(주) 제품, 상품명 "BESTEK KW-501") 20중량% 및 평균입경 325메시(mesh)의 토르마린 분말 10중량%의 비율로 혼합 조성하여 코팅제 조성물을 제조한 다음, 이 코팅제 조성물을 라이너지의 일면에 10g/㎡의 도포량으로 도포하였다.70% by weight of an adhesive (polysol (AE-300)) prepared by polymerizing a polyvinyl alcohol and water dissolved in the presence of benzoyl peroxide and a mixture of vinyl acetate and an emulsifier, a polyurethane emulsion (Gangnam Chemical Co., Ltd.) Product, a brand name "BESTEK KW-501") and a composition of 20% by weight and 10% by weight of tourmaline powder with an average particle diameter of 325 mesh to prepare a coating composition, and then the coating composition 10g / It applied in the application amount of m <2>.
전술한 바와 같이 제조된 코팅제 조성물을 라이너지의 일면에 10g/㎡의 도포량으로 도포한 다음 150℃의 표면 온도를 유지하는 열롤러로 2초간 접촉시켜 도포된 코팅제 조성물을 경화시켜 골판지용 라이너지를 제조하였다.The coating composition prepared as described above was applied to one surface of the liner paper at a coating amount of 10 g / m 2, and then contacted with a heat roller maintaining a surface temperature of 150 ° C. for 2 seconds to cure the coated coating composition to prepare a liner paper for cardboard. .
한편, 전술한 바와 같이 제조된 라이너지와 골심지를 코르게이터(Corrugator)를 이용하여 접착시켜 본 발명에 따른 골판지를 제조하였다.Meanwhile, the corrugated cardboard according to the present invention was manufactured by adhering the liner paper and the corrugated cardboard prepared as described above using a corrugator.
전술한 바와 같이 제조된 본 발명의 골판지를 이용하여 50×30×30cm의 골판지 상자를 제조하고, 대조군(코팅제 조성물이 라이너지에 도포되지 않은 것을 제외하고는 동일한 것)과 본 발명의 골판지 상자에 고구마를 넣고 7℃로 유지되는 항온조에서 보관하면서 1주일 간격으로 고구마의 상태를 확인하였다.A cardboard box of 50 × 30 × 30 cm was prepared using the cardboard of the present invention prepared as described above, and the sweet potato in the cardboard box of the present invention and the control (the same except that no coating agent composition was applied to the liner). Put and check the state of sweet potatoes at intervals of one week while storing in a thermostat maintained at 7 ℃.
전술한 바와 같이 실험 조건의 결과 대조군에 저장된 고구마는 5주후부터 싹이 나기 시작하였으나 본 발명의 골판지 상자에 저장된 고구마는 7주 경과 후에도 싹이 나지 않았으며, 5주후 표면을 육안으로 관찰한 결과 대조군에 저장된 고구마는 건조가 진행되어 표면이 미세하게 쭈글쭈글해졌지만 본 발명의 골판지 상자에 저장된 고구마는 변화가 없었다.As described above, the sweet potatoes stored in the control group started to sprout after 5 weeks, but the sweet potatoes stored in the cardboard box of the present invention did not sprout even after 7 weeks, and the surface was visually observed after 5 weeks. The sweet potato stored in the drying progressed finely crumpled surface, but the sweet potato stored in the cardboard box of the present invention did not change.
본 발명은 전술한 실시 예에 국한되지 않고 본 발명의 기술사상이 허용하는 범위 내에서 다양하게 변형하여 실시할 수가 있다.The present invention is not limited to the above embodiments, and various modifications can be made within the scope of the technical idea of the present invention.
Claims (8)