KR20070119205A - Surfaced material for sports ground - Google Patents
Surfaced material for sports ground Download PDFInfo
- Publication number
- KR20070119205A KR20070119205A KR1020060053522A KR20060053522A KR20070119205A KR 20070119205 A KR20070119205 A KR 20070119205A KR 1020060053522 A KR1020060053522 A KR 1020060053522A KR 20060053522 A KR20060053522 A KR 20060053522A KR 20070119205 A KR20070119205 A KR 20070119205A
- Authority
- KR
- South Korea
- Prior art keywords
- surface layer
- coat
- garnet
- court
- binder
- Prior art date
Abstract
Description
도 1은 본 발명의 체육시설코트의 표면층재가 구비된 학교운동장의 단면도이다.1 is a cross-sectional view of the school playground with the surface layer material of the athletic facility coat of the present invention.
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>
10 : 표면층 20 : 표층10: surface layer 20: surface layer
30 : 중층 40 : 하층30: middle layer 40: lower layer
본 발명은 체육시설코트용 표면층재에 관한 것으로 보다 상세하게는 석류석, 바인더를 포함하는 체육시설코트용 표면층재에 관한 것이다.The present invention relates to a surface layer material for a sports equipment coat, and more particularly to a surface layer material for sports equipment coat including a garnet, a binder.
학교운동장, 테니스코트, 게이트볼코트, 농구장, 배드민턴장과 같은 체육시설코트의 하층은 100∼150mm, 하층 위에 중층 50∼100mm, 중층 위에 50∼100mm의 표층, 표층 위에 3∼5mm의 표면층을 구성하는 체육시설코트를 형성하고 있다.The lower layers of the sports facilities courts such as school grounds, tennis courts, gate ball courts, basketball courts, and badminton courts are 100-150 mm, 50-100 mm above the middle layer, 50-100 mm above the middle layer, and 3-5 mm above the surface layer. A sports facility coat is formed.
상기의 체육시설코트 바닥에서 제일 깊은 하층은 체육시설 코트의 용이한 배수를 위해 주로 자갈을 사용하고, 중층은 필터층으로 마사, 표층은 마사토 또는 사질점토, 표면층은 마사토와 모래를 주로 사용하고 있다.The deepest floor in the bottom of the athletic facility coat mainly uses gravel for easy drainage of the athletic court coat, the middle layer is used as a filter layer, and the surface layer is mainly used as masato or sand clay, and the surface layer is used as masato and sand.
학교운동장, 테니스코트, 게이트볼장, 농구장, 배드민턴장과 같은 체육시설코트에서 표면층은 마사토 또는 모래로 표면층을 마감하고 있어 건조시 비산먼지의 분진으로 호흡장애와 마사토 또는 모래의 백색계열로 햇빛이 반사되어 눈부심으로 인해 눈의 피로가 많이 발생한다. 더욱이 볼(ball)을 사용하는 경기가 자주 실시되는 학교운동장과 테니스코트, 게이트볼, 농구장의 경우 백색계열의 색깔로 인해 볼(ball)의 선명함이 감소되어 경기에 지장을 주는 경우가 많이 있다. In sports facility courts such as school grounds, tennis courts, gate ball courts, basketball courts, and badminton courts, the surface layer is finished with masato or sand, so when it dries, the dust is scattered in dust. The glare causes a lot of eye fatigue. In addition, in the case of the school playground where tennis is frequently used, and the tennis court, gate ball, and basketball court, the color of the white system reduces the sharpness of the ball, which often interferes with the game.
따라서 비산 먼지의 방지, 옥외체육시설 이용자의 시력보호와 경기력 향상 등 체육시설, 특히 옥외체육시설코트의 표면층에 사용되고 있는 표면층재에 대한 연구가 절실한 실정이나 아직 이에 대한 연구가 많이 이루어지지 않고 있다.Therefore, research on surface layer materials used in the surface layer of sports facilities, especially outdoor sports facility coats, such as prevention of scattering dust, protecting the eyesight of users of outdoor sports facilities, and improving athletic performance, is not necessary.
한편 본 발명과 관련된 종래기술로서 한국공개특허 2004-0034971호에 테니스 코트용 표층재의 제조방법에 있어서, 자연상태의 황토를 태양열에서 자연건조 또는 열풍기를 이용하여 건조시킨 후, 이를 통상의 롤러장치로 분쇄하여 황토가루만을 채취한 다음, 상기 황토가루와 마사토, 모래, 석회, 옥가루, 그리고 구운소금을 혼합하여 표층재를 제조하는 과정으로 이루어짐을 특징으로 하는 테니스 코트용 표층재의 제조방법에 대한 내용이 있다.Meanwhile, in the method of manufacturing the surface layer material for tennis courts according to the prior art related to the present invention, Korean Patent Laid-Open Publication No. 2004-0034971, after drying the natural yellow soil in solar heat using a natural drying or a hot air fan, and then using the conventional roller device After collecting only the ocher powder by pulverization, the contents of the method for manufacturing the surface material for a tennis court, characterized in that the process consisting of the ocher powder and masato, sand, lime, jade powder, and baked salt to produce a surface material. have.
그러나 상기 선행기술은 표층재이며 석류석, 염화계 바인더를 포함하는 체육시설코트 표면층재를 주요 구성으로 하는 본 발명과는 기술적 구성이 서로 상이하 다.However, the prior art is a surface material and the technical configuration is different from the present invention, the main configuration of the surface layer material of the athletic facilities coat including garnet, chloride-based binder.
본 발명은 다양한 색상을 지니며 종래 체육시설코트 표면층에 사용되고 있는 마사토, 모래에 비해 비중이 높아 비산 먼지의 방지, 다양한 색채감으로 이용자의 시력보호, 볼의 선명함으로 경기력 향상 등 체육시설코트 표면층재의 제공을 목적으로 한다.The present invention has a variety of colors and has a higher specificity than masato and sand, which are conventionally used for the surface layer of a sports equipment coat. For the purpose.
상기에서 언급한 목적을 달성하기 위한 본 발명의 체육시설코트 표면층재는 석류석(garnet), 바인더를 포함한다.Athletic facility coat surface layer material of the present invention for achieving the above-mentioned object includes a garnet (garnet), a binder.
본 발명의 옥외시설용 표층재의 구성성분인 석류석은 비중 3.4∼4.6, 경도 6.5∼7.5 입도가 0.01∼2.0mm인 것을 사용할 수 있다.Garnet, which is a constituent of the surface material for outdoor facilities of the present invention, may have a specific gravity of 3.4 to 4.6 and a hardness of 6.5 to 7.5 having a particle size of 0.01 to 2.0 mm.
상기에서 석류석은 비중이 3.4∼4.6인 것을 사용하여 종래 표면층재에 사용하는 모래의 비중 2.2 보다 높아 유동이 적어 건조시 모래 또는 마사토를 재료로 하는 표면층재에 비해 먼지의 비산을 보다 적게 발생시킨다. In the above, the garnet has a specific gravity of 3.4 to 4.6, which is higher than the specific gravity of sand used in the conventional surface layer material, so that the flow is less, resulting in less dust scattering than the surface layer material made of sand or masato during drying.
상기에서 석류석은 경도가 6.5∼7.5로 커서 쉽게 부서지지 않아 사진(沙塵) 화 되기 어려워 먼지의 비산을 억제할 수 있다. In the above, garnet has a hardness of 6.5-7.5, so that it is not easily broken, so that it is difficult to be photographed, and thus scattering of dust can be suppressed.
상기에서 석류석은 입도가 0.01∼2.0mm인 구립형을 사용하므로 고결을 방지해 코트시설 이용자가 넘어져도 과도한 부상을 방지할 수 있어 안전하다.In the above, the garnet is used as a granule having a particle size of 0.01 ~ 2.0mm to prevent the solidification and can prevent excessive injuries even if the user of the court facility falls.
본 발명의 체육시설코트용 표면층재의 구성성분인 석류석은 색상을 가진 것을 포함하도록 하여 표면층재의 색상을 백색계열이 아닌 보다 다양한 색상을 지니도록 할 수 있다.Garnet, which is a constituent of the surface layer material for a sports equipment coat of the present invention, may include one having a color, so that the color of the surface layer material may have various colors rather than white.
상기에서 석류석은 적색, 갈색, 녹색, 연두색, 노랑, 흑갈색 중에서 선택된 어느 하나 이상의 색상을 가진 것을 사용할 수 있다.The garnet may be used having one or more colors selected from red, brown, green, grass green, yellow, and black brown.
이러한 다양한 색상을 지닌 석류석을 표면층재로 사용함으로써 체육시설코트 에 다양한 색상을 나타내는 표면층재를 시공하여 체육시설코트 이용자의 눈부심을 방지하고, 볼(ball)과 여러 가지 기구를 가지고 코트를 사용시 볼(ball)과 여러 가지 기구와 대비되어 코트의 표면층재를 선명하게 하여 경기력 향상에 일조할 수 있다. By using garnets with various colors as surface layer materials, the surface layer materials showing various colors are installed in the sports facility coats to prevent glare from users of the sports facility coats, and when using the courts with balls and various devices In contrast to the ball and other devices, the surface layer of the court can be sharpened to help improve performance.
본 발명의 체육시설코트 표면층재 중에서 석류석은 체육시설코트 표면층 1m2를 기준시 체육시설코트 표면층 1m2를 2∼5mm 두께로 도포할 수 있는 함량을 사용할 수 있다. Garnet of the athletic facility coat surface layer material of the present invention may be used to apply the content of the athletic facility coat surface layer 1m 2 to 2 to 5mm thickness based on 1m 2 of the athletic facility coat surface layer.
본 발명의 체육시설코트 표면층재는 상기의 석류석 이외에 바인더를 사용하여 표면층재의 보습효과를 향상시킬 수 있다. The surface layer material of the athletic facility coat of the present invention can improve the moisturizing effect of the surface layer material by using a binder in addition to the garnet.
표면층재에 바인더를 사용하여 보습성을 향상시킴으로써 건조에 따른 비산 먼지의 발생을 더욱 감소시킬 수 있다.By using a binder for the surface layer material to improve the moisture retention, it is possible to further reduce the generation of scattering dust due to drying.
본 발명의 체육시설코트 표면층재에서 바인더는 체육시설코트 표면층 1m2 기 준시 체육시설코트 표면층 1m2 대하여 0.5∼1.0kg 사용할 수 있다.The binder in the athletic facility coat surface layer material of the present invention based on 1 m 2 of the athletic facility coat surface layer 0.5 ~ 1.0kg may be used for 1m 2 of the surface layer of the sports equipment court.
본 발명의 체육시설코트 표면층재에서 체육시설코트 표면층 1m2 기준시 체육시설코트 표면층 1m2에 대하여 바인더를 0.5kg 미만 사용하면 표면층의 보습효과가 미미하고, 1.0kg 초과하여 사용하면 과량의 바인더 사용에 따른 표면층의 보습효과 향상이 과하다. 따라서 본 발명의 체육시설코트용 표면층재에서 바인더는 체육시설코트 표면층 1m2 기준시 체육시설코트 표면층 1m2 대하여 0.5∼1.0kg 사용하는 것이 좋다. 1 m 2 of the athletic facility coat surface layer in the athletic facility coat surface layer material of the present invention If less than 0.5 kg of binder is used for 1 m 2 of the surface layer of the sports facilities coat, the moisturizing effect of the surface layer is insignificant. Therefore, the binder in the surface layer material for the athletic facility coat of the present invention based on 1 m 2 of the athletic facility coat surface layer It is recommended to use 0.5 ~ 1.0kg for 1m 2 of the surface layer of the sports equipment court.
본 발명에서 바인더는 표층재의 보습효과를 발생시킬 수 있고 환경친화적 이라면 염화계라면 어떠한 것이로 사용할 수 있다.In the present invention, the binder may generate a moisturizing effect of the surface material and may be used as long as it is chloride-based if it is environmentally friendly.
본 발명에서 이러한 바인더의 일예로 염화계 바인더를 사용할 수 있다. In the present invention, a chloride binder may be used as an example of such a binder.
상기에서 염화계 바인더는 염화나트륨, 염화마그네슘, 염화칼슘, 염화칼륨 중에서 선택된 어느 하나 이상을 사용할 수 있다.The chloride-based binder may be any one or more selected from sodium chloride, magnesium chloride, calcium chloride, potassium chloride.
한편 본 발명의 체육시설코트용 표면층재는 체육시설코트 표면층 1m2 기준시 체육시설코트 표면층에 먼저 석류석을 2∼5mm 두께가 되도록 도포한 후 바인더를 체육시설코트 표면층 1m2 대하여 0.5∼1.0kg 도포할 수 있다.Meanwhile, the surface layer material for the sports facility coat of the present invention is based on 1 m 2 of the sports facility coat surface layer. The garnet may be first applied to the surface layer of the sports equipment coat to have a thickness of 2 to 5 mm, and then the binder may be applied to 0.5 to 1.0 kg of 1 m 2 of the sports equipment coat surface layer.
또한 본 발명의 체육시설코트용 표면층재는 체육시설코트 표면층 1m2 기준시 표면층 1m2 대하여 2∼5mm 두께가 되도록 도포할 수 있는 함량의 석류석과 체육시설코트 표면층 1m2 대하여 0.5∼1.0kg 함량의 바인더를 혼합한 후 체육시설코트 표면층 1m2 대하여 2∼5mm 두께가 되도록 도포할 수 있다. In addition, the surface layer material for the athletic facility coat of the present invention is based on 1 m 2 of the athletic facility coat surface layer. A garnet of 2 m to 5 mm thickness is applied to 1 m 2 of the surface layer and 0.5 to 1.0 kg of binder is applied to 1 m 2 of the athletic equipment coat, and then 2 to 5 mm thick to 1 m 2 of the surface layer of the sports equipment coat. can do.
본 발명의 체육시설코트 표면층재는 학교운동장, 테니스코트, 게이트볼장, 농구장, 배드민턴장 중에서 선택된 어느 하나의 옥내외 체육시설코트 표면층재로 사용할 수 있다.The sports facility court surface layer material of the present invention can be used as any one indoor and outdoor athletic facility court surface layer material selected from the school ground, tennis court, gate ball, basketball court, badminton court.
이하 본 발명의 내용을 실시예 및 시험예를 통하여 구체적으로 설명한다. 그러나, 이들은 본 발명을 보다 상세하게 설명하기 위한 것으로 본 발명의 권리범위가 이들에 의해 한정되는 것은 아니다.Hereinafter, the content of the present invention will be described in detail through examples and test examples. However, these are intended to explain the present invention in more detail, and the scope of the present invention is not limited thereto.
<실시예><Example>
1m2에 대하여 3mm 두께로 도포할 수 있는 석류석 함량에 염화나트륨 0.5∼1kg를 첨가하고 100rpm으로 1분 동안 교반시켜서 체육시설코트 표면층재를 제조하였다.Sodium chloride 0.5-1kg was added to the garnet content that can be applied with a thickness of 3mm per 1m 2 and stirred at 100rpm for 1 minute to prepare a surface coating material for the athletic facilities.
상기에서 석류석은 적색, 갈색, 녹색이 각각 1:1:1의 중량비로 혼합되고, 비중 4.0±2, 경도 7.5±0.2, 입도 0.1±0.02mm인 구립형을 사용하였다.In the garnet, red, brown, and green are mixed in a weight ratio of 1: 1: 1, respectively, and specific gravity 4.0 ± 2, hardness 7.5 ± 0.2, and particle size 0.1 ± 0.02mm were used.
<적용예><Application example>
도 1과 같이 하층(40), 중층(30), 표층(20), 표면층(10)으로 이루어지는 학교운동장을 시공하였다. As shown in FIG. 1, a school playground consisting of a
이때 하층(40)은 자갈로 이루어진 자갈층이고, 중층(30)은 마사로 이루어진 마사층이고, 표층(20)은 마사토, 사질점토로 이루어진 표층이다.In this case, the
한편 표면층(10)은 상기 실시예에서 제조한 표면층재를 사용하였다.In addition, the
<시험예 1> 비산 먼지 측정<Test Example 1> measurement of scattering dust
상기 실시예의 표면층재를 표면층에 구비하는 학교운동장을 실험구로 하고, 비중이 2.6인 모래를 표층재로하여 표면층에 구비된 학교운동장을 대조구로 하여 비산 먼지의 발생 정도를 측정하고 그 결과를 아래의 표 1에 나타내었다.Using the surface of the surface layer material of the above embodiment as a test zone, using a sand with a specific gravity of 2.6 as a surface layer as a control surface of the school playground provided in the surface layer to measure the generation of scattering dust and the results Table 1 shows.
상기에서 비산 먼지의 발생 정도는 동일한 체중을 지닌 남녀 학생 20명으로 하여금 실험구 20m 거리 및 대조구 20m 거리를 왕복 2회 뛰도록 한 후 발생되는 먼지를 육안으로 관찰하고 이를 관찰요원 10인(남여 각 5명)으로 하여금 5점 척도법으로 나타내었다.In the above, the generation of scattering dust was made by 20 male and female students with the same weight running two round trips in the 20m distance and the 20m distance of the control group, and then observed the dust generated by the naked eye. 5) was used as a five-point scale.
하기의 표 1의 비산 먼지 관찰 결과는 관찰요원의 총 점수를 관찰요원 수로 나누고 이를 소수 둘째 자리에서 반올림한 값이다. The scattering dust observation results of Table 1 below are the total scores of the observing agents divided by the number of observing agents and rounded up to two decimal places.
표 1. 비산 먼지 관찰Table 1. Scattered Dust Observation
* 수치가 낮을수록 먼지 발생이 적음을 의미한다. * Lower value means less dust.
<시험예 2> 눈부심 측정<Test Example 2> glare measurement
상기 실시예의 표면층재를 표면층에 구비하는 학교운동장을 실험구로 하고, 비중이 2.6인 모래를 표층재로 하여 표면층에 구비된 학교운동장을 대조구로 하여 실험구 및 대조구 운동장 사용시 눈부심을 측정하고 그 결과를 아래의 표 2에 나타내었다.The school ground having the surface layer material of the above embodiment as a test zone, using the sand with a specific gravity of 2.6 as the surface layer as a control zone, the school playground provided in the surface layer as a control, the glare when using the test zone and the control ground playground was measured and the results It is shown in Table 2 below.
상기에서 눈부심 측정은 같은 날에 실험구 및 대조구 운동장에서 축구부 2개팀씩 총 4개팀의 축구부 선수들로 하여금 전반 20분 및 후반 20분 동안 축구시합을 한 후 시합중의 눈부심 정도를 5점 척도법으로 나타내었다.In the above, the glare measurement was performed by four teams of soccer teams, two teams of soccer teams, in the experimental and control fields on the same day. Indicated.
하기의 표 2의 눈부심 측정 결과는 4개팀 축구부 선수들의 총 점수를 선수 수로 나누고 이를 소수 둘째 자리에서 반올림한 값이다. The glare measurement result of Table 2 below is divided by the total number of players of the four football teams divided by the number of players and rounded to two decimal places.
표 1. 눈부심 측정Table 1. Glare Measurement
* 수치가 낮을수록 눈 부심이 적음을 의미한다. * Lower number means less glare.
상술한 바와 같이, 본 발명의 바람직한 실시예를 참조하여 설명하였지만 해당 기술 분야의 숙련된 당업자라면 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. As described above, although described with reference to a preferred embodiment of the present invention, those skilled in the art will be variously modified and modified within the scope of the present invention without departing from the spirit and scope of the present invention described in the claims below. It will be appreciated that it can be changed.
상기 시험예의 결과에서처럼 본 발명의 석류석, 바인더를 포함하는 체육시설코트 표면층재를 구비한 학교운동장은 종래 마사토, 모래를 표면층재로 하는 학교운동장에 비해 비산 먼지가 적고, 눈부심 정도가 적어 체육시설을 이용하는 사용자가 먼지의 발생이 적고 시력보호와 경기력 향상을 할 수 있는 좋은 환경에서 체육시설코트를 사용할 수 있다.As a result of the above test example, the school playground with the surface layer material of the athletic facility coat including the garnet and the binder of the present invention has less scattering dust and less glare than the conventional sports ground with the surface layer material of Masato and sand. The user can use the sports facilities court in a good environment where the dust generation is low and the eyesight protection and athletic performance are improved.
Claims (5)