KR20070108494A - Hydrophilic and non-porous type fabric with water-proof and vapor-peameable properties - Google Patents
Hydrophilic and non-porous type fabric with water-proof and vapor-peameable properties Download PDFInfo
- Publication number
- KR20070108494A KR20070108494A KR1020070106405A KR20070106405A KR20070108494A KR 20070108494 A KR20070108494 A KR 20070108494A KR 1020070106405 A KR1020070106405 A KR 1020070106405A KR 20070106405 A KR20070106405 A KR 20070106405A KR 20070108494 A KR20070108494 A KR 20070108494A
- Authority
- KR
- South Korea
- Prior art keywords
- porous
- hydrophilic
- polyurethane resin
- coating layer
- hydrophilic non
- Prior art date
Abstract
Description
본 발명은 친수무공형 투습방수포에 관한 것으로서, 보다 구체적으로는 수증기를 순간적으로 배출하는 기능이 뛰어나고 가볍고 생산공정이 간소한 친수무공형 투습방수포에 관한 것이다.The present invention relates to a hydrophilic non-porous moisture-proof blister, and more particularly, to a hydrophilic non-porous moisture-proof blister having an excellent function of instantaneously discharging water vapor and having a light production process.
투습방수포는 스포츠웨어, 등산복 및 스키웨어 등과 같이 비교적 가혹한 기상조건 하에서 격렬한 운동을 할 때 착용하는 스포츠용 의류 원단 등으로 널리 사용되고 있다.Moisture-proof tarpaulin is widely used as sports clothing fabrics to wear when violent exercise under relatively harsh weather conditions, such as sportswear, mountaineering clothes and skiwear.
종래 투습방수포는 원단상에 유기용제에 용해될 수 있는 습식 폴리우레탄 수지 조성물을 플로팅 나이프(Floating Knife) 또는 나이프 오버 롤(Knife Over Roll) 방식으로 직접도포한 다음 건식 또는 습식공정으로 응고시켜 코팅층 상에 미세기공을 형성하는 방법으로 제조되어 왔다.Conventional moisture-permeable tarpaulin directly coated the wet polyurethane resin composition which can be dissolved in an organic solvent on a fabric by a floating knife or knife over roll method, and then solidified by a dry or wet process to form a coating layer. It has been produced by the method of forming micropores in the.
이와 같은 종래의 다공형 투습방수포는 인체에 유해하고 수질 및 대기 공해를 유발하는 디메틸포름아마이드, 메틸에틸케톤, 톨루엔 등의 유기용제를 다량 사 용하여 제조함으로 인해 가공 공장의 작업환경을 저해하고 환경오염을 초래하는 원인이 되어 왔다.The conventional porous moisture-permeable blister is manufactured by using a large amount of organic solvents such as dimethyl formamide, methyl ethyl ketone, and toluene, which are harmful to the human body and cause water and air pollution. It has been a cause.
최근 이런 문제점들을 해결하기 위하여 원단상에 수분산형 발수제를 함유하는 유중수분산형(이하 w/o형 이라고 한다) 에멀젼 폴리우레탄 수지코팅액, 저분자형 수용성 아크릴수지 코팅액 또는 수용성폴리우레탄수지 코팅액 등을 나이프 오버 롤(Knife Over Roll) 방식으로 코팅한 후 다단 건조하여 건식다공형 투습방수포를 제조하였다.In order to solve these problems, knife-over water-in-oil dispersion (hereinafter referred to as w / o type) emulsion polyurethane resin coating liquid, low molecular weight water-soluble acrylic resin coating liquid or water-soluble polyurethane resin coating liquid containing water-dispersible water repellent agent on the fabric After coating in a roll (Knife Over Roll) method was dried in multiple stages to prepare a dry porous moisture-proof waterproof cloth.
상기 방법으로 제조된 종래의 건식다공형 투습방수포는 환경오염의 문제를 해결할 수 있지만, 내수압 및 투습도 등의 기능성이 저하되는 문제가 있다.Conventional dry porous permeable waterproof fabric prepared by the above method can solve the problem of environmental pollution, but there is a problem that the functionality such as water pressure and moisture permeability is lowered.
상기의 건식무공형 투습방수포의 문제점을 해결하기 위한 또다른 종래 기술로서 원단상에 친수무공형 2액형 폴리우레탄 수지조성물을 코팅하여 베이스층을 형성시킨 다음, 상기 베이스층 위에 다시 친수무공형 일액형 폴리우레탄 수지조성물을 코팅하여 톱(Top)코팅층을 형성하여 친수무공형 투습방수포를 제조하는 방법도 제안된바 있다.As another conventional technique for solving the problems of the above-mentioned dry non-porous moisture-proof blister, a hydrophilic non-porous two-component polyurethane resin composition is coated on a fabric to form a base layer, and then the hydrophilic non-porous one-component type on the base layer again. There has also been proposed a method of manufacturing a hydrophilic non-porous moisture-proof waterproof fabric by coating a polyurethane resin composition to form a top coating layer.
친수무공형 투습방수포는 다공형 투습방수포와는 달리 연속적인 비다공질의 고체상(Solid) 코팅 층으로 구성되어진다. 이러한 비다공질 막은 물에 대하여 내수압이 뛰어나며 투습도는 친수성 피막의 두께에 반비례하는 특징을 가지고있다. 고체상 필름을 통과하는 수증기의 확산은 폴리우레탄 수지 전체 분자쇄에 걸쳐 분포하는 친수성 작용기(-O-, -CO-, -OH, 또는 -NH2)의 결합에 의해 이루어지며 이러 한 작용기는 물분자와 가역적인 수소결합을 한다.Hydrophilic non-porous moisture barrier is composed of a continuous non-porous solid coating layer, unlike the porous moisture-permeable foam. The non-porous membrane has excellent water pressure against water and its moisture permeability is inversely proportional to the thickness of the hydrophilic coating. Diffusion of water vapor through the solid phase film is achieved by the bonding of hydrophilic functional groups (-O-, -CO-, -OH, or -NH 2 ) distributed throughout the entire molecular chain of the polyurethane resin. And reversible hydrogen bonding.
기존의 친수무공형 투습방수포 제조에 사용되었던 친수무공형 폴리우레탄 수지의 경우 소프트 세그멘트(Soft segment)의 폴리올(Polyol)로 폴리에틸렌글리콜(Polyethylene Glycol)/ 폴리프로필렌글리콜(Polypropylene Glycol)의 랜덤 공중합체(Random copolymer)를 주로 사용하였다. 따라서 형성된 폴리우레탄의 소프트세그멘트 사슬은 도 4에 도시된 바와 같이 마구잡이로 엉켜있는 코일(Coil)형의 구조로 되어있어서 흡수된 수분이 투과되는데 시간이 오래 걸린다. 도 4는 소프트 세그멘트 사슬이 코일 구조인 폴리우레탄 수지의 모식도이다. 이 경우 ASTM E96-00 BW법과 같이 코팅 층과 물이 직접 접촉하는 방식의 투습도 측정방법에서는 우수한 투습도를 가질 수 있으나, ISO 11092법과 BS 7209법과 같이 코팅 원단이 수증기를 배출할 수 있는 순간적인 능력이나 실제 투습정도를 측정하는 방법에서는 우수한 투습도를 가질 수 없는 문제가 있었다. 구체적으로 종래의 친수무공형 투습방수포는 도 2에 도시된 바와 같이 원단(1) 상에 소프트 세그멘트의 사슬이 코일형 구조인 2액형의 폴리우레탄 수지의 베이스 코팅층(3)이 코팅되어 있고, 상기 베이스 코팅층(3) 상에 일액형의 폴리우레탄 수지의 톱 코팅층(4)이 코팅된 단면 구조를 갖는다.In the case of the conventional hydrophilic non-porous moisture-resistant foam, the hydrophilic non-porous polyurethane resin is a soft segment of polyol (polyol) of the polyethylene glycol (Polyethylene Glycol) / polypropylene glycol (Polypropylene Glycol) random copolymer ( Random copolymer) was mainly used. Therefore, the soft segment chain of the polyurethane is formed as a coil-like structure tangled in random as shown in Figure 4 takes a long time to absorb the absorbed moisture. It is a schematic diagram of the polyurethane resin whose soft segment chain is a coil structure. In this case, in the method of measuring moisture permeability in which the coating layer is in direct contact with water, as in ASTM E96-00 BW, it may have excellent moisture permeability.However, the instantaneous ability of the coated fabric to discharge water vapor, such as ISO 11092 and BS 7209, In the method of measuring the actual moisture permeability there was a problem that can not have excellent moisture permeability. Specifically, as shown in FIG. 2, the conventional hydrophilic non-porous moisture-proof blister is coated with a
도 2는 종래 친수무공형 투습방수포의 단면 개략도이다.Figure 2 is a schematic cross-sectional view of a conventional hydrophilic non-porous moisture-proof waterproof cloth.
투습도는 투습방수포의 기능을 평가하는 가장 기본적인 항목으로 인체가 배출하는 땀을 얼마나 효과적으로 빠른시간에 방출할 수 있는가를 나타내는 지표이다. 투습도는 단위면적당 하루에 방출하는 총 수증기량(g/㎡ day)을 측정하 는 방법이 일반적이나, 현재 유럽을 중심으로 코팅하지 않은 표준시료의 투습능력대비 보유 투습량(%)을 평가하거나, 일정한 수증기 분압하에서 수증기의 투과에 대한 저항값(㎡ Pa/W)을 평가하는 방법이 사용되고 있다.Moisture permeability is the most basic item for evaluating the function of the moisture-permeable tarpaulin. It is an index indicating how effectively the human body releases sweat quickly. The moisture permeability is generally measured by measuring the total amount of water vapor released per day (g / ㎡ day) per unit area.However, the current moisture permeability (%) compared to the moisture permeability of a standard sample not coated in Europe, or The method of evaluating the resistance value (m <2> Pa / W) with respect to permeation | transmission of steam under partial pressure of steam is used.
상기의 투습도 측정방법 각각을 보다 구체적으로 살펴보면 아래와 같다.Looking at each of the above moisture permeability measurement method in more detail.
▶ ASTM E96-00 BW법▶ ASTM E96-00 BW Method
현재 미주 지역과 아시아 지역에서 친수무공형 투습방수포의 투습도를 측정하는데 주로 사용하는 규격으로서 Inverted cup 방식으로 친수무공형 코팅제품에 유리한 방식이다. 항온·항습기의 온도는 32℃, 상대습도는 50%RH의 상태에서 측정을 한다.It is the standard that is mainly used to measure the moisture permeability of hydrophilic non-wetting waterproof blisters in the Americas and Asia. Temperature and humidity of constant temperature and humidity are measured at 32 ℃ and relative humidity at 50% RH.
▶ ISO 11092법▶ ISO 11092
최근 각 국가별 표준 시험법이 국제적으로 통합되는 추세에서 주목을 받고 있는 투습도 측정 방법이며, 특히 유럽지역에서는 ASTM E96-00 BW법을 크게 신뢰하지 않으며 이 규격을 신뢰하고 있다. 종래의 방법이 표준조건하에서 수증기의 총 투과량을 측정하는 방식인데 반해 이 방법은 인체의 실제적 발한 작용에 근거해서 의복이 수증기를 배출할 수 있는 순간적 능력을 측정하는 방법이다. 측정 결과는 의복의 수증기 투과 저항(Water Vapour Resistance, Ret)로 표시되는데 Ret값이 작을수록 투습능력이 우수하다고 볼 수 있다.In recent years, the standard test method of each country has been attracting attention in the internationally integrated trend, and in Europe, the ASTM E96-00 BW method does not rely heavily on this standard. The conventional method is to measure the total permeation of water vapor under standard conditions, whereas the method is to measure the instantaneous ability of the garment to release water vapor based on the actual sweating of the human body. The measurement results are expressed as water vapor resistance (R et ) of clothes. The smaller the R et value, the better the moisture permeability.
▶ BS 7209법▶ BS 7209 Act
영국의 투습도 측정 규격으로 유럽에서 ISO 11092법과 함께 투습방수포의 투습도 측정 규격으로 많이 사용되고 있다. 이 규격은 물의 증발을 측정하는 워터법으로서 코팅하지 않은 표준시료와 코팅된 시료를 동일한 조건(20±2℃, 65±5%RH)에서 측정하여 투습능력대비 보유 투습량(%)을 평가하는 방법이다.As a measure of moisture permeability in the United Kingdom, it is widely used in Europe as a measure of moisture permeability of the moisture-permeable waterproofing bubble along with the ISO 11092 method. This standard is a water method to measure evaporation of water. The standard and uncoated samples are measured under the same conditions (20 ± 2 ℃, 65 ± 5% RH) to evaluate the moisture permeability (%) compared to the moisture permeability. Way.
한편, 기존의 친수무공형 투습방수포는 코팅제와 섬유와의 접착력 향상을 위해 앞에서 설명한 바와 같이 2액형의 베이스(Base) 코팅을 먼저 한 후, 그 위에 1액형의 톱(Top) 코팅을 실시하여 제조한다. 이 경우 베이스/톱의 2번의 코팅에 의해 완성이 되기 때문에 생산공정이 복잡하게되고, 코팅층이 두꺼워지고, 친수무공형의 특성상 코팅층의 두께가 두꺼워질수록 투습도가 낮아지고, 스웰링(Swelling) 현상이 많이 일어나고 촉감이 축축해 지는 (Wet해 지는)등 여러문제가 발생 되었다.On the other hand, the conventional hydrophilic air-permeable waterproof fabric is manufactured by first performing a two-component base coating as described above to improve the adhesion between the coating agent and the fiber, and then subjected to a one-component top coating thereon. do. In this case, since the coating is completed by the two coatings of the base / top, the production process is complicated, the coating layer is thick, and as the thickness of the coating layer becomes thick due to the hydrophilic non-porous nature, the moisture permeability decreases, and the swelling phenomenon Many problems occurred, such as a lot of wetness and wetness.
본 발명은 코팅층(2)을 이루는 폴리우레탄 수지의 소프트 세그멘트 사슬이 선형구조이기 때문에 수증기를 순간적으로 배출하는 기능이 뛰어나고, 베이스 코팅층 없이 한개의 코팅층만으로 구성되어 생산공정이 간소화되며 두께가 얇아 가볍고 투습도가 우수한 친수무공형 투습방수포를 제공하고자 한다.In the present invention, since the soft segment chain of the polyurethane resin constituting the
또한 본 발명은 스웰링(Swelling) 현상이 적고, 경량감이 우수하고, 드라 이(Dry)한 촉감이 뛰어난 친수무공형 투습방수포를 제공하고자 한다.In another aspect, the present invention is to provide a hydrophilic non-porous moisture-proof waterproof foam having less swelling (phenomena), excellent lightness, excellent dry (Dry) touch.
이와같은 과제를 달성하기 위한 본 발명의 친수무공형 투습방수포는 원단(1) 상에 소프트 세그멘트의 사슬이 선형(Linear) 구조인 친수무공형 폴리우레탄 수지로 이루어진 1개의 코팅층(2)이 형성되어 ISO 11092 방법으로 측정한 투습도가 5.0~9.9㎡ Pa/watt 인 것을 특징으로 한다.Hydrophilic non-porous moisture-proof waterproof fabric of the present invention for achieving this problem is formed on the fabric (1) one coating layer (2) made of a hydrophilic non-porous polyurethane resin having a linear structure of a chain of soft segments is formed The water vapor transmission rate measured by the ISO 11092 method is characterized in that the 5.0 ~ 9.9㎡ Pa / watts.
구체적으로, 본 발명은 도 1에 도시된 바와 같이 원단(1) 상에 소프트 세그멘트의 사슬이 선형 구조인 친수무공형 폴리우레탄 수지로 이루어진 1개의 코팅층(2)이 형성된 단면 구조를 갖는다.Specifically, as shown in FIG. 1, the present invention has a cross-sectional structure in which one
도 1은 본 발명에 따른 친수무공형 투습방수포의 단면 개략도이다.1 is a schematic cross-sectional view of a hydrophilic non-porous moisture-proof waterproof cloth according to the present invention.
도 3은 소프트 세그멘트의 사슬이 선형(Linear) 구조인 친수무공형 폴리우레탄 수지의 모식도이다.3 is a schematic view of a hydrophilic non-porous polyurethane resin having a linear structure of chains of soft segments.
본 발명은 상기와 같이 코팅층(2)이 1개만 형성되어 있기 때문에 생산공정이 간소화되고, 최종제품의 두께가 얇아져 투습도가 향상되고, 경량감과 드라이(Dry)한 촉감도 뛰어나다.In the present invention, since only one
상기 코팅층(2)을 이루는 친수무공형 폴리우레탄 수지는 도 3과 같이 소프트세그멘트의 사슬이 선형(Linear) 구조로서, (ⅰ) 폴리에틸렌글리콜과 폴리테트라메틸렌글리콜의 공중합 폴리올, (ⅱ) 톨리엔디이소시아네이트와 4,4디페닐메탄디이소시아네이트로 구성된 폴리이소시아네이트 및 (ⅲ) 부탄디올과 에틸렌글리콜로 구성 된 쇄연장제(Chain extender)의 부가 중합반응으로 제조된 1.5액형 하이브리드(Hybrid) 타입 폴리우레탄 수지이다.The hydrophilic non-porous polyurethane resin constituting the coating layer (2) is a linear structure of the chain of soft segments as shown in Figure 3, (i) copolymerized polyol of polyethylene glycol and polytetramethylene glycol, (ii) tolyenediisocyanate And a 1.5-component hybrid type polyurethane resin prepared by addition polymerization of a polyisocyanate composed of 4,4 diphenylmethane diisocyanate and a chain extender composed of butanediol and ethylene glycol.
상기 코팅층(2) 두께는 30~40㎛이고, 원단(1) 상에 도포된 상기의 친수무공형 폴리우레탄 수지의 도포량은 30~40g/㎡인 것이 경량감 및 투습도 등의 개선에 바람직하다.The
그러나, 본 발명에서는 상기 코팅층(2)의 두께 및 폴리우레탄 수지의 도포량을 특별하게 한정하는 것은 아니며, 원단(1)의 물성 및 조직에 따라 이들을 적절하게 조절할 수 있다.However, in the present invention, the thickness of the
상기와 같이 본 발명은 코팅층(2)을 이루는 폴리우레탄 수지의 소프트 세그멘트 사슬의 선형구조이기 때문에 수증기를 순간적으로 배출하는 능력이 뛰어나 ISO 11092 방법으로 측정한 투습도가 5.0~9.9㎡ Pa/watt 이다.As described above, the present invention is a linear structure of the soft segment chain of the polyurethane resin constituting the coating layer (2) is excellent in the ability to discharge water vapor instantaneously measured by the ISO 11092 method is 5.0 ~ 9.9
이에 반해, 소프트 세그멘트의 사슬이 코일구조인 폴리우레탄 수지로 이루어진 베이스 코팅층과 톱 코팅층을 포함하는 종래의 친수무공형 투습방수포는 ISO 11092 방법으로 측정한 투습도가 10~15 Pa/watt 수준에 불과하다.On the other hand, the conventional hydrophilic air-permeable waterproof foam including a base coating layer and a top coating layer made of polyurethane resin having a chain of soft segments coiled is only 10-15 Pa / watt level measured by the ISO 11092 method. .
본 발명에 따른 친수무공형 투습방수포는 원단(1) 상에 아래와 같은 조성을 갖는 코팅액을 나이프 오버롤 방식 등으로 30~40㎛의 두께 및 30~40g/㎡의 도포량으로 도포한 후 건조하는 방법으로 제조할 수 있다.Hydrophilic non-porous waterproof waterproof fabric according to the present invention is prepared by applying a coating liquid having a composition as follows on the fabric (1) with a thickness of 30 ~ 40㎛ and a coating amount of 30 ~ 40g / ㎡ by the knife over roll method, etc. can do.
코팅액의 Of coating liquid 조성예Example
본 발명은 코팅층(2)을 이루는 폴리우레탄 수지의 소프트 세그멘트 사슬이 선형구조이기 때문에 수증기를 순간적으로 배출하는 기능이 뛰어나고, 베이스 코팅층 없이 한개의 코팅층만으로 구성되어 생산공정이 간소화되며 두께가 얇아 가볍고 투습도가 우수하다.In the present invention, since the soft segment chain of the polyurethane resin constituting the
또한, 본 발명은 경량감이 우수하고, 드라이(Dry)한 촉감도 우수하다.In addition, the present invention is excellent in light weight and excellent in dry touch.
이하, 실시예 및 비교실시예를 통하여 본 발명을 보다 구체적으로 살펴본다.Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples.
그러나, 본 발명은 하기 실시예에 의해 권리범위가 한정되는 것은 아니다.However, the present invention is not limited by the following examples.
실시예Example 1 One
경사밀도×위사밀도가 160본×90본/인치인 75데니어/72필라멘트로 구성된 폴리에스테르 원단을 테프론계 발수제로 발수처리한 다음 140℃의 온도와 60kg/㎠의 압력으로 시레가공한다.Polyester fabric consisting of 75 denier / 72 filaments having a warp density × weft density of 160 × 90 yarns / inch is subjected to a water repellent treatment with a Teflon-based water repellent, and then processed into a tire at a temperature of 140 ° C. and a pressure of 60 kg /
다음으로는, 상기와 같이 시레가공된 폴리에스테르 원단 상에 아래 조성(Ⅰ)의 폴리우레탄 조성물을 나이프 오버롤 방식으로 30g/㎡의 도포량으로 코팅하여 친수무공형 투습방수포를 제조하였다.Next, the polyurethane composition of the following composition (I) was coated on a sheet of polyester fabric as described above with a coating amount of 30 g /
-조성(Ⅰ)-Composition (Ⅰ)
1.5액형 하이브리드 타입 폴리우레탄 수지 100중량부100 parts by weight of 1.5-component hybrid type polyurethane resin
(소프트 세그멘트의 사슬의 선형구조 임)(Linear structure of the chain of soft segment)
멜라민 가교제 3중량부3 parts by weight of melamine crosslinking agent
수용성 블록크드(Blocked) 이소시아네이트 3중량부3 parts by weight of water-soluble blocked isocyanate
(무황변 가교제)(Yellowing crosslinking agent)
디메틸포름아미드(유기용제) 15중량부15 parts by weight of dimethylformamide (organic solvent)
TiO2 (백색안료) 7중량부7 parts by weight of TiO 2 (white pigment)
상기 1.5액형의 하이브리드 타입 폴리우레탄 수지는 (ⅰ) 폴리에틸렌글리콜과 폴리테트라메틸렌글리콜의 공중합 폴리올, (ⅱ) 톨리엔디이소시아네이트와 4,4디페닐메탄디이소시아네이트로 구성된 폴리이소시아네이트 및 (ⅲ) 부탄디올과 에틸렌글리콜로 구성된 쇄연장제(Chain extender)의 부가 중합반응으로 제조하였다.The 1.5-component hybrid type polyurethane resin includes (i) a copolymerized polyol of polyethylene glycol and polytetramethylene glycol, (ii) a polyisocyanate composed of tolyene diisocyanate and 4,4 diphenylmethane diisocyanate, and (iii) butanediol and ethylene. It was prepared by addition polymerization of a chain extender consisting of glycol.
제조된 친수무공형 투습방수포의 각종 물성을 평가한 결과는 표 1과 같다.The results of evaluating various physical properties of the prepared hydrophilic non-porous moisture-proof waterproof fabric are shown in Table 1.
비교실시예Comparative Example 1 One
경사밀도×위사밀도가 160본×90본/인치인 75데니어/72필라멘트로 구성된 폴리에스테르 원단을 테프론계 발수제로 발수처리한 다음 140℃의 온도와 60kg/㎠의 압력으로 시레가공한다.Polyester fabric consisting of 75 denier / 72 filaments having a warp density × weft density of 160 × 90 yarns / inch is subjected to a water repellent treatment with a Teflon-based water repellent, and then processed into a tire at a temperature of 140 ° C. and a pressure of 60 kg /
다음으로는, 상기와 같이 시레가공된 폴리에스테르 원단 상에 2액형의 폴리우레탄 조성물을 나이프 오버롤 방식으로 60g/㎡의 도포량으로 코팅하여 베이스(Base) 코팅층을 먼저 형성한 다음, 계속해서 상기 베이스(Base) 코팅층 위에 일액형 폴리우레탄 조성물을 나이프 오버롤 방식으로 40g/㎡의 도포량으로 코팅하여 톱(Top) 코팅층을 형성하여 친수무공형 투습방수포를 제조하였다.Next, a two-component polyurethane composition is coated on a sheet of polyester fabric as described above with a coating amount of 60 g /
상기 일액형 및 2액형 폴리우레탄 수지는 (ⅰ) 폴리에틸렌글리콜과 폴리프로필렌글리콜의 랜덤 코폴리머 인 폴리올, (ⅱ) 4,4디메틸메탄디이소시아네이트의 폴리이소시아네이트 및 (ⅲ) 부탄디올과 에틸렌글리콜로 이루어진 쇄연장제(Chain extender)의 부가중합반응으로 제조하였다.The one-component and two-component polyurethane resins are (i) a polyol which is a random copolymer of polyethylene glycol and polypropylene glycol, (ii) a polyisocyanate of 4,4 dimethylmethane diisocyanate, and (iii) a chain consisting of butanediol and ethylene glycol. It was prepared by addition polymerization of a chain extender.
제조된 친수무공형 투습방수포의 각종 물성을 평가한 결과는 표 1과 같다.The results of evaluating various physical properties of the prepared hydrophilic non-porous moisture-proof waterproof fabric are shown in Table 1.
도 1은 본 발명에 따른 친수무공형 투습방수포의 단면 개략도.1 is a schematic cross-sectional view of a hydrophilic air-permeable waterproof tarpaulin according to the present invention.
도 2는 종래 친수무공형 투습방수포의 단면 개략도.Figure 2 is a schematic cross-sectional view of a conventional hydrophilic non-wetting type waterproof tarpaulin.
도 3은 소프트 세그멘트 사슬이 선형(Linear) 구조인 친수무공형 폴리우레탄 수지의 모식도.3 is a schematic diagram of a hydrophilic non-porous polyurethane resin having a soft segment chain in a linear structure.
도 4는 소프트 세그멘트 사슬이 코일(Coil) 구조인 친수무공형 폴리우레탄 수지의 모식도.4 is a schematic view of a hydrophilic non-porous polyurethane resin having a soft segment chain in a coil structure.
* 도면 중 주요부분에 대한 부호설명* Code description for main parts of the drawings
1 : 원단 1: fabric
2 : 소프트 세그멘트의 사슬이 선형(Linear) 구조인 하이브리드형 폴리우레탄 수지 코팅층.2: Hybrid type polyurethane resin coating layer whose chain of soft segment is linear structure.
3 : 소프트 세그멘트의 사슬이 코일(Coil) 구조인 2액형 폴리우레탄 수지의 베이스(Base) 코팅층3: Base coating layer of two-component polyurethane resin whose chain of soft segment is coil structure
4 : 소프트 세그멘트의 사슬이 코일(Coil) 구조인 1액형 폴리우레탄 수지의 톱(Top) 코팅층4: Top coating layer of 1-part polyurethane resin whose chain of soft segment is coil structure
Claims (4)