KR20070007754A - The ondol sheet and its manufacturing method - Google Patents

The ondol sheet and its manufacturing method Download PDF

Info

Publication number
KR20070007754A
KR20070007754A KR1020060135110A KR20060135110A KR20070007754A KR 20070007754 A KR20070007754 A KR 20070007754A KR 1020060135110 A KR1020060135110 A KR 1020060135110A KR 20060135110 A KR20060135110 A KR 20060135110A KR 20070007754 A KR20070007754 A KR 20070007754A
Authority
KR
South Korea
Prior art keywords
mixed
stone
ondol
ocher
jute
Prior art date
Application number
KR1020060135110A
Other languages
Korean (ko)
Other versions
KR100814352B1 (en
Inventor
이석안
김춘남
Original Assignee
이석안
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이석안 filed Critical 이석안
Priority to KR1020060135110A priority Critical patent/KR100814352B1/en
Publication of KR20070007754A publication Critical patent/KR20070007754A/en
Application granted granted Critical
Publication of KR100814352B1 publication Critical patent/KR100814352B1/en

Abstract

A hypocaust flooring material using volcanic stones and ocher and a manufacturing method thereof are provided to improve heat insulation performance and to supply the comfortable surrounding through the far infrared ray radiation and antimicrobial, sterilizing, and deodorant functions. A hypocaust flooring material(100) using volcanic stones and ocher is shaped like a plate having a predetermined thickness by consecutively laminating a jute cloth(1), mixed stones(2) mixed with the volcanic stones and ocher, a jute cloth(1'), and a natural flooring material(3) through the medium of a binder and an adhesive(5) by the heating compression. The mixed stones are mixed with shells and ocher. A charcoal, a germanium and a tourmaline are also added in the mixed stones.

Description

화산석과 황토를 이용한 온돌바닥재 및 그 제조방법{The ondol sheet and its manufacturing method}Ondol flooring material using volcanic stone and loess and its manufacturing method

도 1은 본 발명의 일부분을 절결한 상태를 도시한 사시도1 is a perspective view showing a state in which a part of the present invention is cut out

도 2는 본 발명의 제조과정을 도시한 단면도2 is a cross-sectional view showing a manufacturing process of the present invention.

※ 도면의 주요부분에 대한 부호의 설명※ Explanation of code for main part of drawing

1, 1': 황마천 2: 혼합석1, 1 ': jute cloth 2: mixed stone

3: 천연바닥재 4: 바인더3: natural flooring material 4: binder

5: 접착제 6: 테프론테이프5: adhesive 6: teflon tape

7: 오일 100: 온돌바닥재7: oil 100: warm floor

P: 프레스금형P: Press mold

본 발명은 화산석과 황토를 이용한 온돌바닥재 및 그 제조방법에 관한 것으로, 더욱 상세하게는 황마천과 황토와 화산석 및 천연바닥재를 바인더와 접착제를 매개로 가열 압착시켜 판체형상으로 구성함으로써, 중량이 가볍고 시공이 용이한 온돌침대 또는 온돌방의 바닥재로 사용할 수 있도록 하여 함으로써, 우수한 온돌기능을 발휘할 뿐만 아니라 화산석과 황토의 효능이 조화롭게 어우러져 건강에 많은 도움을 주는 화산석과 황토를 이용한 온돌바닥재 및 그 제조방법에 관한 것이다. The present invention relates to an ondol floor using volcanic stone and loess, and a method of manufacturing the same. More specifically, jute cloth, ocher, volcanic stone, and natural flooring are heat-compressed through a binder and an adhesive to form a plate body, thereby reducing the weight. Lightweight and easy to use as an ondol bed or floor of an ondol room, which not only exerts excellent ondol function but also harmoniously combines the effects of volcanic stone and loess, and contributes to health.Ondol flooring material using volcanic stone and loess and its manufacturing method It is about.

일반적으로 온돌침대 또는 온돌방에 적용되는 온돌바닥재로는 미려한 무늬를 가진 천연목재로 된 것을 주로 많이 사용하고 있다. 이러한 천연목재로 된 온돌바닥재는 미려한 무늬로 인하여 외관이 미려하고 중량이 가벼워 시공은 용이하지만, 그 두께가 제한적이므로 온돌의 효과가 그리 뛰어나지 못하였다. In general, the ondol flooring material applied to the ondol bed or ondol room is mainly used of natural wood with a beautiful pattern. Ondol flooring material made of natural wood has a beautiful appearance and light weight due to its beautiful pattern, making construction easy, but its thickness was limited, so the effect of ondol was not so excellent.

이러한 천연목재로 된 온돌바닥재의 단점을 보완하기 위해 이 보다 큰 두께를 가지고 있어 온돌의 효과가 보다 뛰어난 천연석재로 된 온돌바닥재를 사용하기도 하였는데, 상기의 천연석재로 된 온돌바닥재는 온돌의 효과는 뛰어나지만 그 중량이 많이 나가고 크기에 제약이 있어 시공이 용이하지 못한 문제점이 있었다. 이에 따라 천연석재로 된 온돌바닥재는 온돌방에 적용하지 않고 대체로 규모가 작은 온돌침대에만 적용하여 사용하였다. In order to make up for the shortcomings of such natural wood ondol flooring materials, the ondol flooring material made of natural stone having a greater thickness than the ondol effect has been used. Excellent but the weight is much and there is a problem in that the construction is not easy because the size is limited. Accordingly, natural stone ondol flooring was not applied to the ondol room but was generally applied to only small ondol beds.

본 발명은 상기와 같은 문제점을 해결하기 위하여 발명된 것으로, 온돌침대나 온돌방의 바닥재로 사용되는 온돌바닥재가 우수한 온돌의 효과를 발휘할 수 있고 시공을 용이하게 행할 수 있어, 규모가 작은 온돌침대에는 물론 규모가 큰 온돌방에도 적용할 수 있도록 하기 위하여, 황마천과, 화산석과 황토가 혼합된 혼합석 과, 황마천과, 천연바닥재가 물이 혼합된 바인더와 접착제를 매개로 한 가열 압착을 통해 차례대로 적층된 소정두께를 갖는 판형으로 형성된 화산석과 황토를 이용한 온돌바닥재 및 그 제조방법을 제공함에 그 목적이 있다. The present invention has been invented to solve the above problems, the ondol flooring material used as an ondol bed or a flooring floor of the ondol room can exert the excellent effect of the ondol and can be easily carried out construction, as well as a small ondol bed In order to be applied to a large ondol room, jute springs, mixed stones mixed with volcanic stones and loess, jute springs, and natural flooring materials are sequentially heated and pressed through a binder and adhesive mixed with water. An object of the present invention is to provide an ondol floor using volcanic stone and loess formed in a plate shape having a predetermined thickness laminated and a method of manufacturing the same.

이하 본 발명의 바람직한 실시예를 첨부한 도면을 참조하여 상세하게 설명하면 다음과 같다. Hereinafter, described in detail with reference to the accompanying drawings, preferred embodiments of the present invention.

도 1은 본 발명의 일부분을 절결한 상태를 도시한 사시도이고, 도 2는 본 발명의 제조과정을 도시한 단면도이다. 1 is a perspective view showing a state in which a part of the present invention is cut away, and FIG. 2 is a cross-sectional view illustrating a manufacturing process of the present invention.

본 발명의 화산석과 황토를 이용한 온돌바닥재(100)는 황마천(1)과, 화산석과 황토가 혼합된 혼합석(2)과, 황마천(1')과, 천연바닥재(3)가 물이 혼합된 바인더(4)와 접착제(5)를 매개로 한 가열 압착을 통해 차례대로 적층된 소정두께를 갖는 판형으로 형성됨을 특징으로 한다. Ondol flooring material 100 using volcanic stone and loess of the present invention is jute stream (1), mixed stone (2) mixed with volcanic stone and ocher, jute stream (1 '), and natural flooring material (3) It is characterized in that it is formed in a plate shape having a predetermined thickness laminated in sequence through heat pressing through the mixed binder (4) and the adhesive (5).

상기 혼합석(2)은 화산석을 대신하여 조개껍질과 황토를 혼합하여 구성하는 것도 가능하다. The mixed stone (2) may be configured by mixing a clam shell and ocher in place of volcanic stone.

상기 혼합석(2)에는 숯, 게르마늄, 토르말린 등을 첨가하여 구성하는 것도 가능하다. It is also possible to add charcoal, germanium, tourmaline, or the like to the mixed stone 2 to be configured.

도면 중 미설명 부호 P는 프레스금형이고, 6은 테프론테이프이며, 7은 오일이다. In the figure, reference numeral P denotes a press mold, 6 denotes Teflon tape, and 7 denotes oil.

이와 같이 구성된 본 발명의 화산석과 황토를 이용한 온돌바닥재(100)는 황 마천(1)(1')과 화산석과 황토로 구성된 혼합석(2) 및 천연바닥재(3)가 일체 적층된 판형으로 이루어짐에 따라 온돌침대 또는 온돌방의 바닥재로 사용할 수 있도록 한 것이다. The hot stone flooring material 100 using volcanic stone and loess of the present invention configured as described above is composed of a plate shape in which a stack of yellow horse cloth (1) (1 '), a mixed stone (2) composed of volcanic stone and loess, and a natural floor material (3) are integrally laminated. Depending on the floor, it can be used as flooring for ondol beds or ondol rooms.

특히, 본 발명은 황마천(1)(1')과 화산석과 황토 및 천연바닥재(3)가 바인더(4)와 접착제(5)를 매개로 가열압착되어 15mm이상의 두께를 가짐으로써 천연목재로 구성된 종래의 온돌바닥재 보다 월등히 향상된 온돌기능을 발휘할 수 있게 된다. In particular, the present invention is jute cloth (1) (1 ') and volcanic stone, loess and natural flooring material 3 is made of natural wood by having a thickness of 15mm or more by heat-compression through the binder (4) and the adhesive (5) It is possible to exhibit a significantly improved ondol function than the conventional ondol flooring material.

그리고 본 발명은 황마천(1)(1')과 화산석과 황토의 가벼운 중량으로 인해 천연석재로 구성된 종래의 온돌바닥재 보다 가벼워 시공을 위한 취급이 용이하고, 크기에 대한 제약도 없어 크기의 대형화를 실현할 수 있게 된다. In addition, the present invention is lighter than the conventional ondol floor made of natural stone due to the light weight of jute stream (1) (1 ') and volcanic stone and loess, and is easy to handle for construction, and there is no restriction on the size to increase the size. It can be realized.

또한, 상기 화산석은 약알카리성 자원으로 미세한 독립기포가 형성되어 보온성과 단열성이 우수하고, 이산화티타늄이 천연상태로 존재하여 반영구적인 향균기능과 살균기능 및 탈취기능을 하며, 다량의 원적외선을 방사한다. 상기 화산석을 대신하여 구성할 수 있는 조개껍질도 인체에 유해한 미네랄을 함유하고 있고 다량의 원적외선을 방사한다. In addition, the volcanic stone is a weak alkaline resource, fine insulated bubbles are formed, excellent in warmth and heat insulation, and titanium dioxide is present in a natural state, semi-permanent antibacterial function, sterilization function and deodorizing function, and emits a large amount of far infrared rays. Shells that can be configured in place of the volcanic stone also contains minerals harmful to the human body and emits a large amount of far infrared rays.

그리고 상기 황토는 널리 알려진 바와 같이 다층 다공질 구조로 다량의 유해한 미생물이 살고 있어 해독작용이 우수하고, 다종의 효소가 함유되어 다량의 원적외선을 방사한다. And the loess is a multi-layered porous structure, as it is widely known to live in a large amount of harmful microorganisms are excellent detoxification, and contains a large number of enzymes to emit a large amount of far infrared rays.

따라서 본 발명은 화산석과 황토의 효능이 어우러져 온돌기능을 더욱 효과적으로 발휘할 수 있게 되고, 세균의 감염이나 세균의 번식도 예방할 수 있게 되며, 인체의 신진대사를 원활하게 하고 혈액순환을 촉진시키는 등 효능을 발휘하여 건강에 많은 도움을 줄 수 있게 되는데, 이의 제조방법을 설명하면 다음과 같다. Therefore, the present invention can be combined with the efficacy of volcanic stone and loess more effectively to the ondol function, and also to prevent the infection of bacteria and breeding of bacteria, to facilitate the metabolism of the human body and promote blood circulation Exercising will be able to help a lot of health, the manufacturing method of the same as follows.

먼저, 제1단계는 도 2의 (a)에 도시된 바와 같이 황마천(1)과 혼합석(2)과 황마천(1')을 차례대로 적층시킨 상태에서 130~150℃정도의 온도에서 30~50분정도 동안 프레스금형(P)으로 가열 압착하는 단계이다. First, the first step is at a temperature of about 130 ~ 150 ℃ in a state in which the jute cloth (1), mixed stone (2) and jute cloth (1 ') are sequentially laminated as shown in Figure 2 (a) It is a step of heat pressing with a press mold (P) for about 30 to 50 minutes.

상기 혼합석(2)은 잘게 분쇄한 화산석 35~45중량%와, 황토 35~45중량%와, 적정량의 물에 혼합한 바인더(4)인 혼합습분 10~30중량%으로 구성하는데, 이를 황마천(1)의 상부에 평평하고 조밀하게 적층시키는 것이 바람직하다. The mixed stone (2) is composed of 35 to 45% by weight finely crushed volcanic stone, 35 to 45% by weight ocher and 10 to 30% by weight of the mixed moisture of the binder (4) mixed in an appropriate amount of water, sulfur It is preferable to stack it flatly and densely on top of the cloth.

이때 혼합석(2)을 구성하는 화산석을 대신하여 화산석과 같이 중량이 가벼운 잘게 분쇄한 조개껍질로 구성할 수 있다. 그리고 황마천(1)(1')은 혼합석(2)의 상면과 하면에 고착되도록 혼합석(2)과 마찬가지로 상기의 혼합습분에 침적시킨 후 적층시켜야 한다. At this time, instead of the volcanic stone constituting the mixed stone (2) it may be composed of lightly ground finely crushed shells such as volcanic stone. And jute cloth (1) (1 ') should be laminated after being deposited on the mixed moisture as in the mixed stone (2) to be fixed to the top and bottom of the mixed stone (2).

또한, 황마천(1)과 혼합석(2)과 황마천(1')을 프레스금형(P)으로 가열 압착시킨 후 가열압착물을 용이하게 프레스금형(P)으로부터 탈형할 수 있도록 프레스금형(P)에는 오일(7)을 도포하고 프레스금형(P)과 황마천(1)(1')의 사이에는 테프론테이프(6)를 도포한다. In addition, after pressing the hot jute cloth (1), mixed stone (2) and jute cloth (1 ') by pressing the mold (P), the press mold (P) so that the hot press can be easily demolded from the press mold (P) ( Oil (7) is applied to P) and teflon tape (6) is applied between the press mold (P) and jute cloth (1) (1 ').

따라서 프레스금형(P)의 가열 압착을 통해 혼합석(2)의 화산석과 황토는 혼합수분의 물이 증발되고 바인더(4)의 경화로 인해 일체로 고형화되고, 황마천(1)도 혼합수분의 물이 증발되고 바인더(4)의 경화로 인해 혼합석(2)에 일체로 고착되게 된다. Therefore, the volcanic stone and ocher of the mixed stone (2) through the heat pressing of the press mold (P) is solidified integrally due to evaporation of water of the mixed moisture and curing of the binder (4), jute cloth (1) also Water is evaporated and fixed to the mixed stone 2 due to the hardening of the binder 4.

이에 따라 도 2의 (b)에 도시된 바와 같이 상기 황마천(1)과 혼합석(2)과 황마천(1)이 일체로 고형화되어 하나의 판체가 형성되게 된다. Accordingly, as shown in (b) of FIG. 2, the jute cloth 1, the mixed stone 2, and the jute cloth 1 are solidified to form a single plate body.

제2단계는 상기 제1단계에서 황마천(1)과 혼합석(2)과 황마천(1')이 일체로 적층된 판체의 황마천(1)(1')에 도포된 테프론테이프(6)를 제거한 후 일측 황마천(1)의 표면을 연마하는 단계이다. The second step is a teflon tape (6) applied to the jute cloth (1) (1 ') of the plate body in which the jute cloth (1), mixed stone (2) and jute cloth (1') are integrally stacked in the first step. After removing the), the surface of one side of the jute cloth (1) is polished.

이는 황마천(1)의 표면을 거칠게 하여 그 마찰력을 증대시켜 황마천(1)에 천연바닥재(3)를 용이하게 접착시키기 위한 단계이다. This step is to roughen the surface of the jute cloth (1) to increase the friction force to easily adhere the natural flooring material (3) to the jute cloth (1).

제3단계는 상기 제2단계에서 표면을 연마한 황마천(1)에 도 2의 (d)에 도시된 바와 같이 열경화성의 접착제(5)를 도포하는 단계이다. The third step is a step of applying a thermosetting adhesive (5) to the jute cloth (1) polished in the second step as shown in (d) of FIG.

이는 다음 단계에서 황마천(1)에 천연바닥재(3)를 적층시키기 위한 단계이다. This is a step for laminating the natural flooring material (3) on the jute cloth (1) in the next step.

제4단계는 상기 제3단계에서 접착제(5)가 도포된 황마천(1)에 도 2의 (e)에 도시된 바와 같이, 천연바닥재(3)를 적층시킨 상태에서 프레스금형으로 70~90℃정도의 온도에서 20~40분정도로 가열 압착한 후 적정크기로 절단하여 온돌바닥재(100)를 완성하는 단계이다. In the fourth step, as shown in FIG. After heating and pressing at about 20 to 40 minutes at a temperature of about ℃ is the step of cutting the appropriate size to complete the ondol floor (100).

따라서 황마천(1)에 도포된 접착제(5)가 열에 의해 경화되면서 황마천(1)에 천연바닥재(3)가 접착되게 된다. 그리고 온돌바닥재(100)의 용도에 알맞게 적정크기로 절단하여 상품화가 가능하게 된다. Therefore, as the adhesive 5 applied to the jute cloth 1 is cured by heat, the natural flooring material 3 is bonded to the jute cloth 1. And it is possible to commercialize by cutting to a suitable size to suit the purpose of the ondol flooring material (100).

이와 같이 구성된 본 발명은 중량이 가벼워 시공을 위한 취급도 용이하게 할 수 있고, 크기에도 제약이 없어 대형화할 수 있으며, 보온성과 단열성이 우수하여 온돌기능을 효과적으로 할 수 있고, 다량의 원적외선의 방사와 향균기능과 살균기능 및 탈취기능 등을 통해 사용자의 건강에 많은 도움을 줄 뿐만 아니라 내부환경도 쾌적하게 할 수 있는 효과가 있다. The present invention configured as described above can be easily handled for construction due to the light weight, and can be enlarged because there is no restriction in size, and excellent thermal insulation and heat insulation can effectively perform the ondol function, and a large amount of far-infrared radiation Through antibacterial function, sterilization function and deodorization function, it not only helps the user's health much but also makes the internal environment comfortable.

Claims (5)

황마천(1)과, 화산석과 황토가 혼합된 혼합석(2)과, 황마천(1')과, 천연바닥재(3)가 물이 혼합된 바인더(4)와 접착제(5)를 매개로 한 가열 압착을 통해 차례대로 적층되어 수정두께를 갖는 판형으로 형성됨을 특징으로 한 화산석과 황토를 이용한 온돌바닥재. Jute stream (1), mixed stone (2) mixed with volcanic stone and ocher, jute stream (1 '), and natural flooring material (3) through a binder (4) and an adhesive (5) mixed with water Ondol flooring using volcanic stone and loess, which are laminated in order through one heat pressing process to form a plate with a crystal thickness. 제1항에 있어서, 상기 혼합석(2)은 조개껍질과 황토가 혼합된 화산석과 황토를 이용한 온돌바닥재. According to claim 1, wherein the mixed stone (2) is an ondol floor using volcanic stone and ocher mixed with shells and ocher. 제1항에 있어서, 상기 혼합석(2)에 숯, 게르마늄, 토르말린을 첨가한 화산석과 황토를 이용한 온돌바닥재. The flooring material according to claim 1, wherein the mixed stone (2) is made of volcanic stone and ocher added with charcoal, germanium, and tourmaline. 적정량의 물을 혼합한 바인더(4)에 침적시킨 황마천(1)과, 잘게 분쇄한 화산석 35~45중량%와, 황토 35~45중량%와, 적정량의 물을 혼합한 바인더(4)인 혼합습분 10~30중량%으로 구성된 혼합석(2)과, 적정량의 물을 혼합한 바인더(4)에 침적시킨 황마천(1')을 차례대로 적층시킨 상태에서 130~150℃정도의 온도에서 30~50분정도 로 프레스금형(P)으로 가열 압착하여 하나의 판체로 성형하는 제1단계와; 상기 제1단계에서 성형된 판체의 황마천(1)(1')에 도포된 테프론테이프(6)를 제거한 후 일측 황마천(1)의 표면을 연마하는 제2단계와; 상기 제2단계에서 연마한 황마천(1)에 열경화성의 접착제(5)를 도포하는 제3단계와; 상기 제3단계에서 접착제(5)가 도포된 황마천(1)에 천연바닥재(3)를 적층시킨 상태에서 프레스금형으로 70~90℃정도의 온도에서 20~40분정도로 가열 압착한 후 적정크기로 절단하여 온돌바닥재(100)를 완성하는 제4단계를 포함하여 구성됨을 특징으로 한 화산석과 황토를 이용한 온돌바닥재의 제조방법. Jute cloth (1) deposited on a binder (4) mixed with an appropriate amount of water, 35 to 45% by weight finely ground volcanic stone, 35 to 45% by weight ocher and a binder (4) mixed with an appropriate amount of water At a temperature of about 130 to 150 ° C. in a state in which a mixed stone (2) composed of 10 to 30 wt% of mixed moisture and a jute cloth (1 ′) deposited on a binder (4) in which an appropriate amount of water is mixed are sequentially laminated. A first step of forming a plate by heating and pressing it into a press mold P for about 30 to 50 minutes; A second step of removing the teflon tape (6) applied to the jute cloth (1) (1 ') of the plate body formed in the first step and then polishing the surface of one side of the jute cloth (1); A third step of applying a thermosetting adhesive (5) to the jute cloth (1) polished in the second step; In a state in which the natural flooring material (3) is laminated on the jute cloth (1) to which the adhesive (5) is applied in the third step, heat press-compress with a press mold at a temperature of about 70 to 90 ° C. for about 20 to 40 minutes, and then the appropriate size. Method for producing an ondol flooring material using volcanic stone and ocher, characterized in that it comprises a fourth step to complete the ondol flooring material 100 by cutting to. 제4항에 있어서, 상기 제1단계에는 프레스금형(P)으로부터 판체를 용이하게 탈형할 수 있도록, 프레스금형에 오일(7)을 도포하고 각 황마천(1)의 표면에 테프론테이프(6)를 도포하는 과정이 포함된 화산석과 황토를 이용한 온돌바닥재의 제조방법The method according to claim 4, wherein in the first step, the oil (7) is applied to the press mold and the teflon tape (6) is applied to the surface of each jute cloth (1) so that the plate body can be easily demolded from the press mold (P). Method of manufacturing ondol flooring using volcanic stone and loess containing the process of coating
KR1020060135110A 2006-12-27 2006-12-27 The ondol sheet and its manufacturing method KR100814352B1 (en)