KR20060105954A - Grinding aid for minuteness shatter of mineral - Google Patents
Grinding aid for minuteness shatter of mineral Download PDFInfo
- Publication number
- KR20060105954A KR20060105954A KR1020050027810A KR20050027810A KR20060105954A KR 20060105954 A KR20060105954 A KR 20060105954A KR 1020050027810 A KR1020050027810 A KR 1020050027810A KR 20050027810 A KR20050027810 A KR 20050027810A KR 20060105954 A KR20060105954 A KR 20060105954A
- Authority
- KR
- South Korea
- Prior art keywords
- grinding
- glycol
- group
- mineral
- reducing agent
- Prior art date
Abstract
본 발명은 광물 미분쇄용 분쇄조제에 관한 것으로, 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄특성과 수화특성을 향상시킬 수 있도록 함에 그 목적이 있다. 이를 위해 구성되는 본 발명은 시멘트를 제조하기 위한 광물의 분쇄시 그 분쇄 효율을 향상시키기 위해 일정량 첨가 사용되는 광물 미분쇄용 분쇄조제에 있어서, 광물의 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제 단독 또는 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜과 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 콘크리트용 고성능 감수제와 단독 또는 둘 이상 혼합한 구성으로 이루어진다.The present invention relates to a grinding aid for the fine grinding of minerals, and to improve the grinding characteristics and hydration characteristics of minerals by mixing a high-performance water-reducing agent for concrete alone or a single or two or more selected from glycol and amine in a certain ratio. There is a purpose. The present invention constituted for this purpose is a grinding aid for fine grinding of minerals used in addition to a certain amount in order to improve the grinding efficiency during the grinding of minerals for producing cement, mineral grinding aids are sodium gluconate, poly High performance water reducing agent alone or monoethylene glycol (monoethylene) for at least one concrete selected from the group consisting of naphthalene sulfonate, polymelamine sulfonate, polycarboxylate, and lignin at least one glycol selected from the group consisting of glycol, diethylene glycol, propylene glycol, polyethylene glycol, monoethanolamine, diethanolamine, Triethanolamine, triisopropanolamine propanol amine) consists of at least one amine selected from the group consisting of a high performance water reducing agent for concrete alone or in combination of two or more.
광물, 미분쇄, 분쇄조제, 감수제, 글리콜, 아민, 아마이드 Minerals, fine grinding, grinding aids, water reducing agents, glycols, amines, amides
Description
본 발명은 광물 미분쇄용 분쇄조제에 관한 것으로, 더욱 상세하게는 콘크리트용 고성능 감수제(소디움글루코네이트, 폴리나프탈렌설포네이트, 폴리멜라민설포네이트, 폴리카르복실레이트, 리그닌) 단독 또는 글리콜(모노에틸렌글리콜, 디에틸렌글리콜, 프로필렌글리콜, 폴리에틸렌글리콜)과 아민(모노에탄올아민, 디에탄올아민, 트리에탄올아민, 트리이소프로판올아민) 중 선택된 단독 또는 둘 이상을 감수제와 혼합하여 광물의 분쇄특성과 수화특성을 향상시킬 수 있도록 하는 광물 미분쇄용 분쇄조제에 관한 것이다.The present invention relates to a grinding aid for fine grinding of minerals, and more particularly, a high performance water reducing agent for sodium (sodium gluconate, polynaphthalenesulfonate, polymelaminesulfonate, polycarboxylate, lignin) alone or glycol (monoethylene glycol , Diethylene glycol, propylene glycol, polyethylene glycol) and amines (monoethanolamine, diethanolamine, triethanolamine, triisopropanolamine) may be mixed with a water reducing agent to improve the grinding and hydration properties of minerals. The present invention relates to a grinding aid for grinding minerals.
일반적으로 광물산업 중 대표적인 것은 시멘트 산업으로, 시멘트 제조시 사용되는 원료로는 석회석, 규석, 점토, 철광석, 슬래그 또는 이들의 혼합물 등과 부속원료로 코우크스, 슬러지, 더스트 등을 사용하고, 이들 원료를 배합하여 미세하게 분쇄한 후에 킬른내에서 1,450℃로 처리를 하면 원료 중의 석회석 성분이 실리카, 알루미나, 철 성분 등과 결합하여 클링커 광물로 생성된다. 이 광물들이 물과 반응하면 단단하게 굳는 성질을 갖는다. 이들을 시멘트 클링커라 하며, 클링커는 석고와 같이 혼합 분쇄과정을 통하여 최종 제품인 시멘트로 생산된다. In general, the typical mineral industry is the cement industry. As raw materials used in cement production, coke, sludge, dust, and the like are used as raw materials for limestone, silica, clay, iron ore, slag, or mixtures thereof. When the mixture is finely pulverized and treated at 1,450 ° C. in the kiln, the limestone component in the raw material is combined with silica, alumina, iron, and the like to form a clinker mineral. When these minerals react with water, they harden. These are called cement clinker, and the clinker is produced as a final product cement through mixed grinding process like gypsum.
전술한 바와 같은 시멘트 제조 공정에서 분쇄는 품질관리의 마지막 단계이며, 이 공정을 거치면서 제품으로서 최종 성능이 결정되기 때문에 시멘트 제조 과정에서 분쇄는 매우 중요한 과정이라고 할 수 있다. 분쇄의 목적은 시멘트 클링커 표면적을 크게 하여 반응성을 높이고 미립자 입자를 쉽게 만들게 할 뿐만 아니라 암석을 분쇄하여 유용성분을 취하고 혼합효과를 높게 하기 위한 것이다. 이때, 분쇄의 효율을 극대화시키기 위해 사용하는 것이 분쇄조제(Grinding Aid)이다.In the cement manufacturing process as described above, the grinding is the final step of quality control, and the grinding is a very important process in the cement manufacturing process because the final performance as a product is determined during this process. The purpose of the grinding is to increase the surface area of the cement clinker to increase the reactivity and make the particulate particles easily, as well as to grind the rocks to take useful ingredients and increase the mixing effect. At this time, the grinding aid used to maximize the efficiency of the grinding (Grinding Aid).
한편, 전술한 바와 같은 분쇄조제는 분체의 응집 및 밀 내부 코팅 방지 외에 분체유동특성 및 그에 따른 피 분쇄물의 밀 잔류시간에 영향을 미치게 되는데 분쇄가 진행됨에 따라 미분쇄된 입자 파단면에 이온이 편기하여 서로 응집하려는 현상이 발생하게 되고, 입자간 인력의 원인이 되는 표면에너지를 제거함으로써 분체유동성을 향상시키며, 이미 분쇄된 미분들을 통풍공기와 함께 밀 밖으로 원활하게 배출시킨다. 또한, 밀로 재순환되는 미립분의 양을 감소시켜 줌으로써 시멘트 클링커 분쇄시 생산성을 증진시켜 주는 역할을 한다.On the other hand, as described above, the grinding aid not only affects the agglomeration of the powder and coating the inside of the mill, but also affects the powder flow characteristics and the mill residence time of the milled product. As a result, the phenomenon of agglomeration with each other is generated, and powder fluidity is improved by removing surface energy that causes attraction between particles, and the finely ground fine powder is discharged out of the mill together with the ventilation air. In addition, by reducing the amount of fines recycled to the mill serves to improve the productivity of the cement clinker grinding.
전술한 바와 같이 분쇄조제시 분쇄조제의 투입량은 분쇄조제의 성분에 따라 사용하는 양이 다르며, 통상적으로 사용되는 분쇄조제 성분은 아민아세테이트계, 에틸렌글리콜계 및 프로필렌글리콜계 등이 있다. 광물의 분쇄조제에 대한 기술로는 "폐부동액을 이용한 광물의 미분쇄 방법(대한민국 등록특허 제222776호)"에 관한 기술, 디에틸렌글리콜이나 트리에탄올아민을 이용한 분쇄조제방법을 서술한 "광물의 미분쇄 방법(대한민국 등록특허 제44210호)"에 대한 기술, 분쇄조제로 사용되는 2성분계에 대한 혼합비율을 변수로 분쇄조제를 사용한 경우 미국 등록특허 제 4828624호와 시멘트 수화시 지연을 목적으로 분쇄조제를 사용한 미국 등록특허 제4204877호 등의 기술이 있다.As described above, the amount of the grinding aid used in the grinding aid is different depending on the components of the grinding aid, and the grinding aid components commonly used include amine acetate, ethylene glycol and propylene glycol. As a technique for the grinding aid of minerals, a technique related to the "pulverization method of minerals using waste antifreeze (Korean Patent No. 222776)", and a "grinding of minerals" describing a grinding aid method using diethylene glycol or triethanolamine Technology for Grinding Method (Korean Registered Patent No. 444210), Grinding Aids for the Delay of Cement Hydration and U.S. Patent No. 4828624 US Pat. No. 4,048,77 and the like.
그리고, 최근에는 분체 공학 발달 및 품질의 요구에 의해 밀 효율의 증가 등과 같은 기존 개념의 효과 외에 품질의 최적화와 수화특성을 향상시키거나 영향을 미칠 수 있는 분쇄조제 연구가 계속되고 있다. 따라서, 본 개발품은 기존의 제품과는 다른 별도의 혼합물로 품질의 최적화와 수화특성을 향상시키거나 영향을 미칠 수 있는 광물의 분쇄조제를 개발하고자 하였다.Recently, in addition to the effects of conventional concepts such as the increase in mill efficiency due to the development of powder engineering and the demand for quality, researches on grinding aids that can improve or influence the optimization of the quality and the hydration characteristics are continued. Therefore, the present product was intended to develop a mineral pulverization aid that can improve or influence the optimization of quality and hydration properties in a mixture different from the existing products.
본 발명은 전술한 바와 같이 기존의 제품과는 다른 별도의 혼합물로 품질의 최적화와 수화특성을 향상시키기 위한 것으로, 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄시 일정량을 투입함으로써 광물의 분쇄특성과 수화특성을 향상시킬 수 있도록 하는 광물 미분쇄용 분쇄조제를 제공함에 그 목적이 있다.The present invention is to improve the optimization and hydration properties of the quality as a separate mixture different from the existing product as described above, the high performance water reducing agent for concrete alone or two or more selected from glycol and amine in a certain ratio with the water reducing agent It is an object of the present invention to provide a fine grinding powder for pulverizing minerals that can improve the grinding characteristics and hydration characteristics of the minerals by mixing a predetermined amount during the grinding of the minerals.
본 발명에 따른 기술의 다른 목적은 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄특성과 수화 특성을 향상시킬 수 있도록 함으로써 광물의 품질을 최적화하는 동시에 제조원가를 낮추면서 미분쇄시킬 수 있도록 함에 있다.Another object of the technology according to the present invention is to optimize the quality of minerals by improving the grinding properties and hydration properties of the minerals by mixing a high-performance water-reducing agent for concrete alone, or a single or two or more selected from glycol and amine at a certain ratio with the water-reducing agent At the same time, it can be pulverized while lowering the manufacturing cost.
아울러, 본 발명에 따른 기술은 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄특성과 수화 특성을 향상시킬 수 있도록 함으로써 시멘트의 압축강도를 보다 향 상시킬 수 있도록 함에 있다.In addition, the technique according to the present invention by mixing a high-performance water-reducing agent for concrete alone or two or more selected from glycol and amine in a certain ratio with the water-reducing agent to improve the grinding strength and hydration characteristics of the minerals to improve the compressive strength of the cement To improve it.
전술한 목적을 달성하기 위해 구성되는 본 발명은 다음과 같다. 즉, 본 발명에 따른 광물 미분쇄용 분쇄조제는 시멘트를 제조하기 위한 광물의 분쇄시 그 분쇄 효율을 향상시키기 위해 일정량 첨가 사용되는 광물 미분쇄용 분쇄조제에 있어서, 광물의 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상으로 이루어진 1성분계의 콘크리트용 고성능 감수제 단독 또는 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜과 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 콘크리트용 고성능 감수제와 단독 또는 둘 이상 혼합한 2성분계 또는 3성분계의 구성으로 이루어진다.The present invention configured to achieve the above object is as follows. That is, the mineral grinding mill according to the present invention, in the grinding mill for grinding minerals used in addition to a certain amount to improve the grinding efficiency when grinding the mineral for manufacturing cement, the mineral grinding aid is sodium gluconate (sodium gluconate), polynaphthalene sulfonate (polynaphthalene sulfonate), polymelamine sulfonate (polymelamine sulfonate), polycarboxylate (polycarboxylate), at least one selected from the group consisting of lignin (lignin) High performance water reducing agent for concrete alone or at least one glycol and monoethanolamine selected from the group consisting of monoethylene glycol, diethylene glycol, propylene glycol, polyethylene glycol (monoethanolamine), diethanolamine, triethanolamine thanolamine), triisopropanolamine (triisopropanol amine) is composed of a two-component or three-component composition of at least one or more amines selected from the group consisting of a high performance water reducing agent for concrete alone or two or more.
전술한 바와 같은 구성에서 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜을 혼합한 2성분계 분쇄조제는 2.5∼97.5 : 2.5∼97.5 wt%의 조성비로 이루어지고, 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 혼합한 2성분계 분쇄조제는 2.5∼97.5 : 2.5∼97.5 wt%의 조성비로 이루어질 수 있다.Sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, and lignin in the configuration as described above At least one high performance water reducing agent for concrete and at least one glycol selected from the group consisting of monoethylene glycol, diethylene glycol, dipropylene glycol, propylene glycol, polyethylene glycol The mixed two-component grinding aid consists of a composition ratio of 2.5 to 97.5: 2.5 to 97.5 wt%, sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, and polycarbox. Selected from the group consisting of polycarboxylate, lignin At least one high-performance water reducing agent for concrete and at least one amine selected from the group consisting of monoethanolamine, diethanolamine, triethanolamine, and triisopropanol amine The two-component grinding aid may be composed of a composition ratio of 2.5 to 97.5: 2.5 to 97.5 wt%.
그리고, 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜 및 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아 민을 혼합하여 이루어진 3성분계 분쇄조제는 2.5∼95 : 2.5∼95 : 2.5∼95 wt%의 조성비로 이루어질 수 있다.And at least one selected from the group consisting of sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, lignin High performance concrete water reducing agent and at least one glycol and monoethanolamine selected from the group consisting of monoethylene glycol, diethylene glycol, propylene glycol, polyethylene glycol ( mono-ethanolamine), diethanolamine (diethanolamine), triethanolamine (triethanolamine), triisopropanolamine (triisopropanol amine) tri-component grinding aid consisting of a mixture of at least one selected from the group consisting of 2.5 to 95: 2.5 to 95 It may consist of a composition ratio of 2.5-95 wt%.
한편, 전술한 바와 같은 본 발명의 구성에서 제조된 분쇄조제는 광물의 전체 중량에 대하여 0.005∼0.20 wt%가 투입됨이 보다 양호하다.On the other hand, the grinding aid prepared in the configuration of the present invention as described above is more preferably added 0.005 ~ 0.20 wt% relative to the total weight of the mineral.
이하에서는 본 발명의 바람직한 실시 예에 따른 본 발명의 광물 미분쇄용 분쇄조제에 대하여 상세하게 설명하기로 한다.Hereinafter will be described in detail with respect to the grinding mill for the fine grinding of the present invention according to a preferred embodiment of the present invention.
먼저, 본 발명에 따른 광물 미분쇄용 분쇄조제는 앞서의 목적에서도 기술한 바와 같이 광물의 분쇄특성과 수화특성을 향상시킬 수 있도록 하기 위한 조성물로, 이 광물 미분쇄용 분쇄조제는 1성분계의 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 콘크리트용 고성능 감수제와 일정 비율로 혼합한 2성분계 또는 3성분계로 구성되어진다. 즉, 광물 미분쇄용 분쇄조제는 콘크리트용 고성능 감수제 단독의 1성분계, 콘크리트용 고성능 감수제와 글리콜의 2성분계, 콘크리트용 고성능 감수제와 아민의 2성분계, 콘크리트용 고성능 감수제와 글리콜 및 아민의 3성분계로 이루어진다.First, the grinding mill for grinding minerals according to the present invention is a composition for improving the grinding and hydration properties of the mineral as described in the above object, the grinding mill for grinding the mineral is a one-component concrete High performance water reducing agent alone or selected from glycol and amine alone or two or more is composed of a two-component or three-component system mixed with a high performance water reducing agent for concrete in a certain ratio. That is, the grinding mill for grinding minerals is composed of one component system of high performance water reducing agent alone, two components system of high performance water reducing agent and glycol for concrete, two components system of high performance water reducing agent and amine for concrete, and three components system of high performance water reducing agent for concrete and glycol and amine. Is done.
본 발명에 따른 광물 미분쇄용 분쇄조제를 보다 상세하게 설명하면 다음과 같다. 먼저, 광물 미분쇄용 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제 단독의 1성분계, 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜 (diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜과 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 콘크리트용 고성능 감수제와 단독 또는 둘 이상을 혼합한 2성분계 또는 3성분계 광물 미분쇄용 분쇄조제의 구성으로 이루어진다.Referring to the grinding aid for the fine grinding of the mineral according to the invention in more detail as follows. First, the grinding mill for grinding minerals is composed of sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, and lignin From the group consisting of one-component, monoethylene glycol, diethylene glycol, propylene glycol, polyethylene glycol alone of at least one high performance water reducing agent for concrete selected from the group At least one selected from the group consisting of at least one glycol, monoethanolamine, diethanolamine, triethanolamine, and triisopropanol amine; Two-component or single or mixed two or more 3-component system comprises a non-mineral structure of a grinding aid for grinding.
다시 말해서, 본 발명에 따른 광물 미분쇄용 분쇄조제는 다음과 같이 분류할 수 있다. 첫째로, 본 발명에 따른 광물 미분쇄용 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제 단독의 1성분계로 이루어질 수 있다.In other words, the grinding aid for grinding minerals according to the present invention can be classified as follows. First, the grinding mill for grinding minerals according to the present invention is sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, lignin ( lignin) may be composed of a one-component system of at least one or more high performance water reducing agents for concrete selected from the group consisting of.
둘째로, 본 발명에 따른 광물 미분쇄용 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜을 일정 비율로 혼합한 2성분계로 이루어질 수 있다. 즉, 콘크리트용 고성능 감수제와 글리콜을 일정 비율로 혼합한 2성분계로 이루어질 수 있다.Second, the grinding mill for grinding minerals according to the present invention is sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, lignin ( high performance water reducing agent for at least one concrete selected from the group consisting of lignin, monoethylene glycol, diethylene glycol, propylene glycol, polyethylene glycol At least one glycol selected from may be composed of a two-component system mixed in a predetermined ratio. That is, it can be made of a two-component system mixed with a high performance water-reducing agent and glycol for a certain ratio.
셋째로, 본 발명에 따른 광물 미분쇄용 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 일정 비율로 혼합한 2성분계로 이루어질 수 있다. 즉, 콘크리트용 고성능 감수제와 아민을 일정 비율로 혼합한 2성분계로 이루어질 수 있다.Third, the grinding mill for grinding minerals according to the present invention is sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, lignin ( at least one high performance water reducing agent for concrete selected from the group consisting of lignin and at least one selected from the group consisting of monoethanolamine, diethanolamine, triethanolamine, and triisopropanol amine. It may consist of a two-component system in which one or more amines are mixed in a proportion. That is, it may be made of a two-component system in which a high performance concrete for concrete and an amine are mixed at a predetermined ratio.
넷째로, 본 발명에 따른 광물 미분쇄용 분쇄조제는 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜 및 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어 진 군으로부터 선택된 적어도 1종 이상의 아민을 일정 비율로 혼합한 3성분계로 이루어질 수 있다. 즉, 콘크리트용 고성능 감수제와 글리콜 및 아민을 일정 비율로 혼합한 3성분계로 이루어질 수 있다.Fourth, the grinding mill for grinding minerals according to the present invention is sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, lignin ( high performance water reducing agent for at least one concrete selected from the group consisting of lignin, monoethylene glycol, diethylene glycol, propylene glycol, polyethylene glycol At least one glycol selected from the group consisting of monoethanolamine, diethanolamine, diethanolamine, triethanolamine, triisopropanolamine and at least one amine selected from the group consisting of It may consist of a mixed three component system. That is, it may be made of a three-component system mixed with a high performance water reducing agent for the concrete and glycol and amine in a predetermined ratio.
한편, 전술한 바와 같은 본 발명에 따른 광물 미분쇄용 분쇄조제의 분류에서 콘크리트용 고성능 감수제와 글리콜을 일정 비율로 혼합한 2성분계 광물 미분쇄용 분쇄조제 및 콘크리트용 고성능 감수제와 아민을 일정 비율로 혼합한 2성분계 광물 미분쇄용 분쇄조제 각각의 조성비는 2.5∼97.5 : 2.5∼97.5 wt%로 이루어진다.On the other hand, in the classification of the mineral grinding mill according to the present invention as described above, a two-component mineral grinding mill and a high performance water-reducing agent and amine for the concrete mixed with a certain ratio of a high performance concrete reducing agent and glycol for a certain ratio The composition ratio of each of the mixed two-component mineral grinding mills is 2.5 to 97.5: 2.5 to 97.5 wt%.
다시 말해서, 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜을 혼합한 2성분계 분쇄조제는 2.5∼97.5 : 2.5∼97.5 wt%의 조성비로 이루어진다.In other words, at least one member selected from the group consisting of sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, and lignin 2, a mixture of the above-mentioned high performance water reducing agent for concrete and at least one glycol selected from the group consisting of monoethylene glycol, diethylene glycol, propylene glycol, and polyethylene glycol The component grinding aid consists of a composition ratio of 2.5 to 97.5: 2.5 to 97.5 wt%.
또한, 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민 (triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 혼합한 2성분계 분쇄조제는 2.5∼97.5 : 2.5∼97.5 wt%의 조성비로 이루어진다.In addition, at least one selected from the group consisting of sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, lignin A two-component grinding aid comprising a mixture of a high performance water reducing agent for concrete and monoethanolamine, diethanolamine, triethanolamine, and triisopropanol amine It consists of a composition ratio of 2.5-97.5: 2.5-97.5 wt%.
그리고, 전술한 바와 같은 본 발명에 따른 광물 미분쇄용 분쇄조제의 분류에서 콘크리트용 고성능 감수제와 글리콜 및 아민을 일정 비율로 혼합한 3성분계 광물 미분쇄용 분쇄조제의 조성비는 2.5∼95 : 2.5∼95 : 2.5∼95 wt%로 이루어진다.In addition, the composition ratio of the three-component mineral fine grinding powder mixed with a high performance concrete reducing agent and glycol and an amine in a predetermined ratio in the classification of the fine grinding powder for grinding according to the present invention as described above is 2.5 to 95: 2.5 to 95: 2.5-95 wt%.
즉, 소디움글루코네이트(sodium gluconate), 폴리나프탈렌설포네이트(polynaphthalene sulfonate), 폴리멜라민설포네이트(polymelamine sulfonate), 폴리카르복실레이트(polycarboxylate), 리그닌(lignin)으로 구성되는 군으로부터 선택된 적어도 1종 이상의 콘크리트용 고성능 감수제와 모노에틸렌글리콜(monoethylene glycol), 디에틸렌글리콜(diethylene glycol), 프로필렌글리콜(propylene glycol), 폴리에틸렌글리콜(polyethylene glycol)로 구성되는 군으로부터 선택된 적어도 1종 이상의 글리콜 및 모노에탄올아민(monoethanolamine), 디에탄올아민(diethanolamine), 트리에탄올아민(triethanolamine), 트리이소프로판올아민(triisopropanol amine)으로 이루어진 군으로부터 선택된 적어도 1종 이상의 아민을 혼합하여 이루어진 3성분계 분쇄조제는 2.5∼95 : 2.5∼95 : 2.5∼95 wt%의 조성비로 이루어진다.That is, at least one selected from the group consisting of sodium gluconate, polynaphthalene sulfonate, polymelamine sulfonate, polycarboxylate, and lignin High performance concrete water reducing agent and at least one glycol and monoethanolamine selected from the group consisting of monoethylene glycol, diethylene glycol, propylene glycol, polyethylene glycol ( monoethanolamine), diethanolamine (diethanolamine), triethanolamine (triethanolamine), triisopropanolamine (triisopropanol amine) is a three-component grinding aid consisting of a mixture of at least one selected from the group consisting of 2.5 to 95: 2.5 to 95: It consists of a composition ratio of 2.5-95 wt%.
전술한 바와 같은 비율로 제조된 본 발명의 광물 미분쇄용 분쇄조제는 시멘트로 제조할 대상물인 광물의 전체 중량에 대하여 0.005∼0.20 wt%가 투입된다. 보다 양호하게는 광물의 전체 중량에 대하여 0.01 내지 0.03중량% 첨가하는 것이 적당하다. 다음의 표 1 은 본 발명에 따른 광물 미분쇄용 분쇄조제의 혼합비율을 도식화 한 예를 보인 것이다.Grinding aid for grinding the mineral pulverization of the present invention prepared in the ratio as described above is added to 0.005 ~ 0.20 wt% based on the total weight of the mineral to be produced by cement. More preferably, it is appropriate to add 0.01 to 0.03% by weight based on the total weight of the mineral. Table 1 below shows an example of the mixing ratio of the grinding mill for grinding minerals according to the present invention.
표 1 에서와 같이 본 발명에 따른 광물 미분쇄용 분쇄조제는 "A"의 경우처럼 콘크리트용 고성능 감수제(폴리나프탈렌설포네이트) 단독으로 제조할 수 있고, "B"나 "C"의 경우에서와 같이 콘크리트용 고성능 감수제(폴리나프탈렌설포네이트)와 아민(트리에탄올아민) 또는 콘크리트용 고성능 감수제(폴리나프탈렌설포네이트)와 글리콜(디에틸렌글리콜) 각각을 3 : 1 의 비율로 혼합 제조할 수도 있으며, "D∼G"에서와 같이 콘크리트용 고성능 감수제(폴리나프탈렌설포네이트)와 글리콜(디에틸렌글리콜) 및 아민(트리에탄올아민)을 1 : 1 : 1, 1 : 3 : 1, 3 : 1 : 3 또는 1 : 1 : 3 의 비율로 혼합 제조할 수 있다.As shown in Table 1, the grinding mill for grinding minerals according to the present invention may be prepared by a high performance concrete reducing agent (polynaphthalenesulfonate) alone as in the case of "A", and in the case of "B" or "C". Likewise, a high performance water reducing agent (polynaphthalenesulfonate) and an amine (triethanolamine) for concrete or a high performance water reducing agent (polynaphthalene sulfonate) and glycol (diethylene glycol) for concrete may be mixed in a ratio of 3: 1, " As in D to G ", high performance water-reducing agents for polycondensation (polynaphthalenesulfonates), glycols (diethylene glycol) and amines (triethanolamines) are 1: 1: 1, 1: 3: 1, 3: 1: 3 or 1 It can manufacture by mixing in a ratio of 1: 1.
전술한 바와 같은 비율로 제조된 본 발명의 광물 미분쇄용 분쇄조제를 시멘트로 제조할 광물의 전체 중량에 대하여 0.005∼0.20 wt%를 투입하게 되면 광물 미분쇄용 분쇄조제는 미분쇄된 입자표면에 흡착되어 입자간의 응집현상을 감소시켜 주게 된다. 따라서, 이미 분쇄된 입자들을 통풍공기와 함께 밀 밖으로 원활히 배출시킴은 물론 미분쇄 입자의 응집현상에 의한 밀 내 벽면의 코팅현상이 제거됨과 동시에 미립분에 의한 쿠션효과를 감소시켜서 분쇄효율을 증진시켜 준다.When the fine grinding mill for grinding the mineral grinding powder of the present invention prepared as described above is added to 0.005 to 0.20 wt% based on the total weight of the mineral to be manufactured in cement, the grinding mill for grinding the mineral grinding powder Adsorption reduces the agglomeration of particles. Therefore, the pulverized particles can be smoothly discharged out of the mill together with the ventilation air as well as the coating effect on the wall surface of the mill due to the agglomeration of the pulverized particles is removed and the crushing effect by the fine powder is reduced to enhance the grinding efficiency. give.
또한, 밀내에서 1차 분쇄된 입자들은 미립분과 조립분으로 분리시키는 공기분급기내에서도 입자와 분산성을 증대시켜(분급기의 분급효율을 향상시키는 결과로) 밀로 재순환되는 미립분의 양을 감소시켜 줌으로써 광물 분쇄시 그 생산성을 증대시켜 준다.In addition, the primary pulverized particles in the mill increase the particle and dispersibility even in the air classifier which separates the fine powder and the granulated powder (as a result of improving the classification efficiency of the classifier), thereby reducing the amount of fine powder recycled to the wheat. By increasing the productivity of the mineral grinding.
한편, 본 발명에 따른 광물 미분쇄용 분쇄조제는 광물의 전체 중량에 대하여 0.005∼0.20 wt%를 투입하는데, 보다 양호하게는 광물의 전체 중량에 대하여 0.01 내지 0.03 wt% 첨가하는 것이 적당하다. 이때, 광물 미분쇄용 분쇄조제를 0.005 wt% 미만으로 사용하게 되면 분쇄촉진효과를 충분히 발휘할 수 없고, 0.20 wt%보다 많이 사용할 경우 더 이상의 분쇄촉진효과가 나타나지 않고 경제성에 큰 영향을 발휘하지 못하기 때문에 바람직하지 못하다.On the other hand, the grinding mill for grinding fine minerals according to the present invention is added to 0.005 to 0.20 wt% based on the total weight of the mineral, more preferably 0.01 to 0.03 wt% based on the total weight of the mineral. At this time, when the grinding aid for the fine grinding of the mineral is used at less than 0.005 wt%, the grinding promoting effect cannot be sufficiently exerted, and when it is used more than 0.20 wt%, no further grinding promoting effect is exhibited and the economic effect is not large. Because it is not desirable.
전술한 바와 같이 본 발명에 따른 광물 미분쇄용 분쇄조제를 전체 광물에 대해 0.005∼0.20 wt%의 양으로 첨가시키는 경우 광물 미분쇄용 분쇄조제를 첨가시키지 않은 경우보다 분쇄효율이 5.0∼10.0% 증진되었으며, 모르타르의 유동성 및 압축강도 또한 향상되었다. 이처럼 시멘트 클링커 미분쇄시에 본 발명의 광물 미분쇄용 분쇄조제를 사용하게 되면 시멘트 클링커 입자 사이에 응집현상을 감소시켜 분쇄효율을 향상시킬 수 있을 뿐만 아니라, 기타 광물 미분쇄용 분쇄조제보다 우수한 효과를 보여 제조원가를 낮출 수 있는 장점이 있다.As described above, in the case of adding the fine grinding powder for grinding the mineral according to the present invention in an amount of 0.005 to 0.20 wt% based on the total minerals, the grinding efficiency is improved by 5.0 to 10.0% compared to the case of not adding the grinding fine grinding powder The mortar's fluidity and compressive strength were also improved. As such, when the grinding aid for the fine grinding of the present invention is used in the grinding of the cement clinker, not only can the coagulation phenomenon be reduced between the cement clinker particles, but also the grinding efficiency can be improved, and it is superior to other grinding for the fine grinding. There is an advantage to lower the manufacturing cost.
이하, 본 발명에 따른 광물 미분쇄용 분쇄조제를 실시 예에 의거하여 더욱 상세히 설명하면 다음과 같다.Hereinafter, the mineral grinding mill according to the present invention will be described in more detail based on the following examples.
[실시 예 1]Example 1
각 성분을 일정 비율로 혼합 제조한 광물 미분쇄용 분쇄조제의 분쇄효율 특성을 살펴보았다.The grinding efficiency characteristics of the grinding mill for the fine grinding of minerals prepared by mixing each component at a predetermined ratio were examined.
시험에 사용한 분쇄기는 드럼크기 Φ330×330mm, 회전수 40rpm의 드럼 밀을 사용하여 포틀랜드 시멘트 원료 7.5kg을 투입하였다. 여기에 각 성분비율의 광물 미분쇄용 분쇄조제를 광물의 원료에 대해 0.02 중량% 첨가시켰다. 이때, 15분, 20분, 25분씩 분쇄 시간에 따른 비표면적, 44㎛체를 이용하여 잔사를 측정하였으며, 그 결과를 다음의 표 2 에 나타내었다.The grinder used for the test was loaded with 7.5 kg of Portland cement raw materials using a drum mill having a drum size of Φ330 × 330 mm and a rotation speed of 40 rpm. To this, 0.02% by weight of a mineral grinding mill for each component ratio was added to the raw material of the mineral. At this time, the residue was measured using a specific surface area, 44 μm sieve according to the grinding time for 15 minutes, 20 minutes, 25 minutes, the results are shown in Table 2 below.
전술한 표 2 에서 "Reference"는 일반 시멘트를 의미하고, "A∼G"는 본 발명에 따른 광물 미분쇄용 분쇄조제를 의미하며, "CBA"는 기존의 광물 미분쇄용 분쇄조제를 의미한다.In the above Table 2, "Reference" refers to general cement, "A to G" means a mineral grinding mill according to the present invention, "CBA" refers to a conventional grinding mill for grinding mill. .
한편, 레퍼런스 및 각 광물 미분쇄용 분쇄조제 별로 제조한 시멘트를 이용하여 시멘트 물성시험을 실시하였다. 이때, 물/시멘트 비는 0.48로 하였으며, 재령별(1일, 3일, 7일, 28일) 압축강도, 페이스트 플로어를 측정하였다. 측정한 결과는 다음의 표 3 과 같다.On the other hand, the cement properties test was carried out using the cement prepared by the reference and the grinding aid for each mineral grinding. At this time, the water / cement ratio was 0.48, and the compressive strength and paste floor for each age (1 day, 3 days, 7 days, 28 days) were measured. The measurement results are shown in Table 3 below.
전술한 표에서와 같이 본 발명에 따른 광물 미분쇄용 분쇄조제를 통해 제조된 시멘트의 경우 기존의 시멘트에 비해 시일이 지남에 따라 그 압축강도면에서 보다 향상됨을 알 수 있다.As shown in the above table, it can be seen that the cement produced through the grinding mill for the fine grinding of the present invention is improved in terms of its compressive strength as the seal passes over the conventional cement.
본 발명은 전술한 실시 예에 국한되지 않고 본 발명의 기술사상이 허용하는 범위 내에서 다양하게 변형하여 실시할 수가 있다.The present invention is not limited to the above embodiments, and various modifications can be made within the scope of the technical idea of the present invention.
이상에서와 같이 본 발명에 따르면 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄특성과 수화특성을 향상시킬 수 있는 효과가 있다.As described above, according to the present invention, the high-performance concrete reducing agent alone or selected from glycol and amine alone or two or more are mixed with the water reducing agent at a predetermined ratio, thereby improving the grinding characteristics and the hydration characteristics of the mineral.
본 발명의 기술은 콘크리트용 고성능 감수제 단독 또는 글리콜과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄특성과 수화특성을 향상시킬 수 있도록 함으로써 광물의 품질을 최적화하는 동시에 제조원가를 낮출 수 있는 효과가 있다.The technology of the present invention is to optimize the quality of the minerals at the same time by optimizing the quality of the minerals by mixing the high performance water reducing agent alone or selected from glycol and amines alone or two or more selected from glycols and amines in a certain ratio It can be lowered.
아울러, 본 발명에 따른 기술은 콘크리트용 고성능 감수제 단독 또는 글리콜 과 아민 중 선택된 단독 또는 둘 이상을 감수제와 일정 비율로 혼합하여 광물의 분쇄특성과 수화 특성을 향상시킬 수 있도록 함으로써 시멘트의 압축강도를 보다 향상시키는 효과가 발현된다.In addition, the technology according to the present invention by mixing a high-performance water-reducing agent for concrete alone or at least one selected from glycol and amines in a certain ratio with the water-reducing agent to improve the grinding strength and hydration properties of the minerals to improve the compressive strength of the cement The effect of improving is expressed.
Claims (4)