KR20060091151A - Shock absorbing materials for inter layer noise proofing of a construction, manufacturing method thereof and floor forming method using the shock absorbing materials - Google Patents

Abstract

The present invention is made of a multi-layer, such as an apartment or office, to prevent the transmission of noise between each layer, including porous minerals, waste tires, waste styrofoam, waste paper, cement and gypsum, foaming agent, organic binder, etc. As well as the buffering effect of the high sound, environmentally friendly, and floor buffer material for preventing the noise between the floor to prevent environmental pollution by recycling waste resources, and a method of manufacturing the same and a floor layer forming method using the same, for the floor The buffer material is 1 to 10 parts by weight of tributary crushed material, 30 to 300 parts by weight of cement, 2 to 20 parts by weight of buffered pulverized product consisting of EVA vinyl (Ethylene vinyl acetate chip), tire pulverized, styrofoam pulverized or mixture thereof, porous 5 to 10 parts by weight of mineral, aqueous acrylic, ethylene vinyl acetate (EVA), polyvinyl alcohol (PVA) It comprises 0.5 to 1.5 parts by weight of an organic binder selected from the group consisting of and 0.5 to 1.5 parts by weight of a blowing agent.

Cement, gypsum, paper, porous minerals, air bubbles, voids, interlayer noise prevention

Description

Shock absorbing materials for inter layer noise proofing of a construction, manufacturing method etc and floor forming method using the shock absorbing materials}

The present invention relates to a floor cushion material for preventing noise between floors of a building, a method of manufacturing the same, and a method of forming a floor layer using the same. More specifically, the present invention is made of a multi-layer, such as an apartment or office, to prevent the transmission of noise between each layer, porous minerals, waste tires, waste styrofoam, waste paper, cement and gypsum, foaming agent, organic binder, etc. Of the floor buffer material for preventing the interlayer noise of a building that can prevent environmental pollution by recycling waste resources as well as the buffering effect of the interlayer noise by mixing them, and a method of manufacturing the same and a method of forming the floor layer using the same. .

Floor impact sound is a sound radiated into a lower generation through floor slabs, ceilings, or walls when an impact such as a person walking or falling objects is applied on the upper floor of a multi-family house such as an apartment. In general, the concrete slab structure is a good sound insulation material because it blocks air propagation well, but if it directly impacts or vibrates the concrete structure, it becomes solid wave sound and is hardly attenuated and is transmitted to other adjacent generations. It has the property of being radiated to. Floor impact sound is divided into light impact sound that generates a lot of high frequency components such as falling sounds of bowls, golf balls, and chair movements, and heavy impact sound that generates a lot of low frequency components such as adult walking and children's skipping. It is becoming.

In the case of houses in Europe and the United States, the floor shock sound is mainly designed to prevent heavy impact sound because a lot of people walk and wear shoes, that is, the impact sound caused by women's high heels. Because habits have a sedentary lifestyle, it should be a structure that can prevent light impact sounds in addition to the heavy impact sounds.

In multi-family houses, such as apartments and townhouses, disputes are constantly being caused by vibrations and noises between floors and upper floors. To solve this problem, each construction company is trying to reduce the noise between floors of apartment houses by placing shock absorbing pads on slabs, foaming concrete on them, and applying mortar on them. However, such a construction method is complicated and takes a lot of time, causing labor costs to rise, which has a problem in that a large portion of the presale price rises. In addition, the existing construction method does not absorb both lightweight shock and heavy impact sound by installing only the floor as a shock absorber, so it is delivered directly to the lower floor by the wall, and the wall serves as a medium for transmitting noise and vibration to the lower floor and the lower floor. It is known that the actual effect is not so great. In fact, even though the samples were made and tested by the method of KS F 2810 1,2 and received the first grade performance, most of them do not appear in the actual apartment house. This test does not match the actual case because only the floor is to be tested and the effect of the wall is not considered.

In addition, due to the tenant's request, many wood is used as a surface finishing material of the floor of a multi-family house, in particular, the floor of a living room. The conventional floor structure using the wood as a floor surface finishing material is insulated on a concrete slab including reinforcing bars. Light-weight foam concrete for, the light-weight foam concrete is applied on the finishing mortar is installed heating pipe, and consists of a solid wood attached as a surface finish by an adhesive on the finishing mortar. As described above, the floor structure using wood as a surface finishing material has a problem in that the wood itself does not effectively block the floor impact sound because it performs a sound insulation function to some extent and does not use a cushioning material. In addition, in the case of using monolium instead of solid wood as a surface finishing material, the floor structure blocks polyester shocks by constructing a buffer material such as polyester between the concrete slab and lightweight foam concrete, but the buffer material is far from the floor surface. There was a problem that the sound insulation efficiency, as well as the construction performance is poor because the sound is not blocked directly after the floor impact sound is delivered directly to the light-weight concrete.

In addition, conventional methods harden the cement through four to five steps, such as placing gravel on the slab and placing cement on it, and constructing a separate elastic mat to reduce noise between layers such as cushioning material. Although there was a method, it takes a lot of time and effort in construction because it goes through a lot of processes, such as labor costs are added, so there is a lot of construction costs.

On the other hand, in the case of lightweight foam concrete, which is currently commonly used, there are many cases of “cracks” occurring after construction, which do not actually help insulation or layer sound absorption. In addition, the existing "light foam concrete" is a situation in which a lot of bubbles are broken during construction, it takes more than 20 to 30% more than the amount of design at the time of construction.

An object of the present invention is made of a multi-layer, such as an apartment or an office, to prevent the transmission of noise between each layer, mixed porous minerals, waste tires, waste styrofoam, waste paper, cement and gypsum, foaming agent, organic binder, etc. It is to provide a floor cushioning material for preventing floor noise of a building that can prevent environmental pollution by recycling waste resources as well as buffering effect between floor noises, a method of manufacturing the same, and a method of forming a floor layer using the same. .

Floor cushioning material for preventing the noise between floors of the building according to the present invention, 1 to 10 parts by weight of feed mill, 30 to 300 parts by weight of cement, EVA chip, tire grinding, styrofoam grinding or a mixture thereof Organic binder selected from the group consisting of 2 to 20 parts by weight of water, 5 to 10 parts by weight of porous minerals, aqueous acryl, ethylene vinyl acetate (EVA), and polyvinyl alcohol (PVA) 0.5 To 1.5 parts by weight and 0.5 to 1.5 parts by weight of blowing agent.

Method for producing a floor cushioning material for preventing the noise between floors of the building according to the invention, (1) 1 to 10 parts by weight of feed mill, 30 to 300 parts by weight of cement, EVA chip, tire mill, styrofoam mill or From 2 to 20 parts by weight of a buffer grind composed of a mixture of 5 to 10 parts by weight of porous minerals, aqueous acryl, ethylene vinyl acetate (EVA) and polyvinyl alcohol (PVA). A mixing step of mixing 0.5 to 1.5 parts by weight of the selected organic binder, 0.5 to 1.5 parts by weight of blowing agent and 200 to 350 parts by weight of water; And (2) a drying step of pouring the mixture obtained in the mixing step into a plate-shaped mold and drying it to about 70 to 80% of the original moisture content.

In addition, the method for forming a floor layer according to the present invention comprises: (1) a stationary step of allowing the floor cushioning material for preventing the noise between floors of the building according to the present invention on the surface of the slab constituting the floor of the building; And (2) a mortar coating step of applying mortar on the floor cushioning material which is left on the slab.

Hereinafter, the present invention will be described in detail with reference to specific examples.

Floor cushioning material for preventing the noise between the floors of the building according to the present invention, 1 to 10 parts by weight of feed mill, 30 to 300 parts by weight of cement, EVA vinyl (Ethylene vinyl acetate chip), tire grinding, styrofoam grinding or these From 2 to 20 parts by weight of a buffer grind composed of a mixture of 5 to 10 parts by weight of porous minerals, aqueous acryl, ethylene vinyl acetate (EVA) and polyvinyl alcohol (PVA). 0.5 to 1.5 parts by weight of the selected organic binder and 0.5 to 1.5 parts by weight of the blowing agent is characterized in that it is made.

Hereinafter, the components constituting the floor cushioning material according to the present invention as described above will be described.

The tributary pulverized product is pulp and conventional paper, in particular, in terms of saving of resources and recycling of waste resources, pulverized waste paper, dissociated waste paper into water, sludge from paper production process in a paper mill. And the like can all be used. The tributary pulverized material is a material on the basis of fibrous material, which is lightweight and excellent in thermal insulation, and in particular, increases the binding strength of the solidified composition, thereby improving the impact resistance. The tributary pulverized product may be used in a dry powder state, and may also be used in the form of sludge dispersed in water. When the feeder pulverized material is included in less than 1 part by weight, there may be a problem that the effect of improving the horizontal drag and the impact resistance of the bottom to be formed is not sufficient, on the contrary, when included in excess of 10 parts by weight, other components In particular, there may be a problem in that the mechanical properties are reduced by reducing the content of the organic binder.

The cement is substantially the main constituent of the floor, which is hydraulically mixed with water to form a mechanically hard floor. In addition, it is inexpensive, can be formed into a slurry by mixing with water and other subsidiary materials, can be molded into a desired shape, it is cured as formed to form a rigid structure, it is widely used in the construction of buildings Known enough to be commercially available for purchase. Portland cement or the like commonly supplied commercially can be used. When the cement is used less than 30 parts by weight, there may be a problem that the mechanical strength is too weak and easily broken, when exceeding 300 parts by weight, the mechanical strength is too strong to have a problem that the buffering and sound-absorbing effect is lowered have. Preferably the cement can be appropriately adjusted according to the use of gypsum and the amount of gypsum to be described later.

The buffer grinding material is selected from the group consisting of tire grinds, styrofoam grinds or mixtures thereof, and these are particularly through the provision of impact resistance by shock absorption and the damping of vibration and the suppression of secondary noise by shock absorption. It provides effects such as noise suppression. In particular, the buffer pulverized product is preferably recycled waste materials such as waste tires and waste styrofoam. The buffer pulverized product preferably has an average diameter of 10 mm or less. In particular, the recycling of waste tires is economical because it uses waste tires generated in large quantities as resources and recycles waste resources, and is economical, and has excellent physical properties as a buffer material. In addition, the waste styrofoam also has excellent physical properties as a cushioning material because of its light weight and excellent thermal insulation and impact absorption capacity. As described above, the buffered pulverized product has a cushioning effect such as foamed EVA chips or styrofoam manufacturing plants foamed in scrap from a shoe manufacturing plant as well as the styrofoam or waste tires, and then molded into a plate shape. It can be understood by those skilled in the art that all kinds of foams can be used. When the buffered pulverized product is used in less than 2 parts by weight, there may be a problem that the buffering effect is not sufficient, on the contrary, if it exceeds 20 parts by weight, physical properties such as mechanical strength is reduced due to the decrease in the content of other components There may be a problem.

The porous mineral functions to absorb and disperse noise and to absorb and disperse shock due to a plurality of pores included therein. In addition, the porous mineral material serves to increase the thermal insulation. In the above, the porous mineral material may be selected from the group consisting of tuff, volcanic rock, pumice, pumice, pearlite or a mixture of two or more thereof. In addition, it will be understood by those skilled in the art that other porous or other known or newly developed porous minerals can be used in addition to the above-described porous minerals, which means that the present invention is limited to the porous minerals described above. Of course it can be understood. When the porous mineral material is included in less than 5 parts by weight, there is a problem that the thermal insulation is lowered, noise reduction effect and impact reduction effect is lowered, on the contrary, when included in excess of 10 parts by weight, other components, in particular organic There may be a problem of decreasing the binding force by reducing the content of the binder. Preferably, the porous mineral material has an average particle diameter of 1 to 10 mm.

The organic binder is selected from the group consisting of aqueous acrylic, ethylene vinyl acetate, polyvinyl alcohol (PVA), which binds other components such as cement and tributary grind to each other, It not only helps to improve the mechanical properties and increase the watertightness, and to generate bubbles, but also prevents bubbles from bursting to maintain the overall volume so that the physical properties after curing are not affected. If the organic binder is contained in less than 0.5 parts by weight, there may be a problem that the binding force is not sufficient, if the content is contained in excess of 1.5 parts by weight, there may be a problem that it is not economical without a special improved effect. As the organic binder, all other commercially available binders and adhesives having a bonding function including other aqueous organic binders having elasticity may be used in addition to those mentioned above.

The blowing agent is a material which forms bubbles in water by reaction with water, and natural or synthetic known blowing agents may be used. Such blowing agents are those known to be commercially available and used by leading manufacturers at home and abroad. Representatively, aluminum foaming agents are used in cement compositions. When the foaming agent is used in less than 0.5 parts by weight, there may be a problem that the foaming effect is low and the weight and sound absorption, sound insulation effect is not enough, on the contrary, if it exceeds 1.5 parts by weight, the foaming agent for the floor obtained too high foaming agent content Too many voids may be formed in the mechanical properties such as mechanical strength may be reduced.

Floor buffer according to the present invention as described above may further include gypsum or waste gypsum in an amount of 50 to 220 parts by weight. In the above gypsum can be preferably used to recycle the waste gypsum generated in the fertilizer factory or power plant. The use of such waste gypsum can be of great economic benefit as well as prevention of environmental pollution. Gypsum from sludge from fertilizer plants and power plants is in two-gyre gypsum, which can be recycled to semi-mineral gypsum or anhydrous gypsum using conventional equipment such as rotary kilns. The waste gypsum may be used alone or in combination with cement in a ratio of 1: 1 or 1: 2. The gypsum has a high soundproofing effect, and can improve economics in place of cement. In addition, when used with the organic binder as in the present invention, there is no problem in the water resistance, etc., but may not have a problem in the water resistance when not used together with the organic binder. When the gypsum is included in less than 50 parts by weight, there may be a problem that the sound insulation effect and economic efficiency is lowered, may be more than 220 parts by weight, but may have a problem in terms of mechanical properties.

Floor buffer according to the present invention as described above may further comprise a curing agent in an amount of 0.5 to 1.5 parts by weight. The curing agent is included in the buffer for the floor according to the present invention as described above to promote the curing of solids, such as cement, when the curing agent is included in less than 0.5 parts by weight, there may be a problem that the curing effect is not sufficient. On the contrary, if it exceeds 1.5 parts by weight, there may be a problem that waste of expensive curing agent without improving the special curing effect.

The buffer material may further include a preservative in an amount of 0.1 to 0.2 parts by weight. The preservative is to provide long-term storage stability by protecting components that can be decomposed by microorganisms such as organic binders and tributaries, and those skilled in the art can be purchased commercially available to properly use for the purpose of preservation of organic substances Of course it can be understood. When the preservative is included in less than 0.1 part by weight, there may be a problem that the preservative effect is not enough, on the contrary, if the amount of the preservative exceeds 0.2 part by weight, there may be a problem that waste of expensive preservatives without improving the special antiseptic effect.

In addition, a separate rubber layer may be further formed on both surfaces or at least one surface of the floor cushioning material. The rubber layer may be made of other rubbers having excellent elasticity such as general natural rubber, synthetic rubber, or silicone rubber, and the rubber layer may be bonded to the floor cushioning material by a general adhesive. Alternatively, during the curing of the composition constituting the floor cushioning material in the manufacture of the floor cushioning material, the rubber layer may be formed by sprinkling pieces of rubber or the like in a completely uncured state to cure together.

The thickness of the floor cushioning material as described above may preferably be 10 to 50 mm. This may be a problem that if the thickness of the cushioning material is too thin (10 mm or less) to obtain a sufficient buffering and sound insulation effect even when laminated using a plurality of sheets, on the contrary, if it exceeds 50mm, it becomes too thick to buffer and sound insulation effect May be improved, but the height of the floor is increased so that the interior space of the building is too narrow, and when the floor height is low, there may be a problem that the number of floors is limited when viewed as a whole.

In addition, the manufacturing method of the floor cushioning material for preventing the noise between the floors of the building according to the present invention, (1) 1 to 10 parts by weight of feed mill crushed, 30 to 300 parts by weight of cement, EVA chips, tire crushed, styrofoam crushed 2 to 20 parts by weight of a buffer grind composed of water or a mixture thereof, 5 to 10 parts by weight of porous minerals, aqueous acrylics, ethylene vinyl acetate (EVA), polyvinyl alcohol (PVA) A mixing step of mixing 0.5 to 1.5 parts by weight of an organic binder, 0.5 to 1.5 parts by weight of blowing agent and 200 to 350 parts by weight of water, selected from the group consisting of: And (2) pouring the mixture obtained in the mixing step into a plate-like mold and drying the material to about 70 to 80% of its original moisture content.

Each component used in the mixing step of (1) is as described above.

In addition, the amount of water used above may be defined as an amount sufficient to dissolve the water-soluble organic binder and to be mixed with the solid mixture and the like to have a viscosity that can be poured like a conventional cement slurry. Naturally, it can be understood that it can be determined theoretically or by repeated experiments or empirically. In particular, the present invention can be used in an amount of 200 to 350 parts by weight based on the sum of the other components as described above. It can be understood that the amount of water used is only sufficient to aid in proper mixing and shaping into a plate, and then to achieve curing by drying and hydration of the cement.

The mixing step of (1) is a step of mixing the above-described components, and in this step, it is necessary to mix sufficiently evenly to obtain a floor buffer material having even physical properties.

The drying step of (2) consists of pouring the mixture obtained in the mixing step of (1) into a plate-shaped mold and drying it to about 70 to 80% of the original moisture content, where drying is the usual natural drying. Any method of removing moisture contained in the mixture, such as hot air drying by hot air and forced drying by microwaves or the like, can be used. Hot air drying or forced drying is preferable to dry efficiently within a limited space. In this drying step, the mixture is preferably dried to about 70 to 80% of the original moisture content, and then left to allow the remaining moisture to hydrate and harden the cement among the components.

In addition, after performing the drying step, it is cured to the extent that it can be handled and left on the slab as a floor of the building directly, and even if it is formed by pouring ordinary mortar on the floor, hydration and Curing proceeds to harden.

In addition, the method of manufacturing the floor cushioning material may further include a rubber layer forming step of further forming a separate rubber layer on both surfaces or at least one surface of the floor buffer material. The rubber layer forming step is combined with other rubbers having excellent elasticity, such as ordinary natural rubber, synthetic rubber or silicone rubber to the floor cushioning material by a common adhesive or otherwise constitute the floor cushioning material in the manufacture of the floor cushioning material. At the time of curing of the composition, it may be formed by sprinkling pieces of rubber or the like to harden together in a state that is not completely cured.

In addition, the method for forming a floor layer according to the present invention comprises: (1) a stationary step of allowing the floor cushioning material for preventing the noise between floors of the building according to the present invention on the surface of the slab constituting the floor of the building; And (2) a mortar coating step of applying mortar on the floor cushioning material which is left on the slab.

The step (1) of the step (1) is to set the floor cushioning material for preventing the noise between floors of the building according to the present invention on the surface of the slab constituting the floor of the building obtained in accordance with the present invention. This can be achieved sufficiently by placing on the slab what has already been formed into a plate. Then, the mortar coating step of (2) consists of applying a conventional mortar on the floor buffer. The above-mentioned mortar is a slurry made by pouring ordinary cement, such as portland cement, into water, and commonly used in a construction site, and by applying and smoothing the mortar layer, it is possible to form a flat and even bottom. This mortar layer serves to protect the floor cushioning material according to the invention as described above while providing a flat bottom.

In addition, the stationary step may be achieved by placing one thick floor cushioning material or stacking two or more thin floor cushioning materials.

In addition, after the stationary step, the polyurethane layer may be further formed on the stationary floor cushioning material. The polyurethane layer may be cured by applying a conventional urethane oligomer or a liquid polyurethane having a relatively low molecular weight by spraying and leaving it to form a polyurethane layer, such as polyurethane or urethane oligomer Is understood to be well known to those skilled in the art can be purchased and used commercially.

By using the floor cushioning material according to the present invention as described above, it is possible to build an excellent apartment house that satisfies all of the sound insulation performance, heat insulation performance, structural stability, economical and constructability, as well as can be easily applied to general buildings. There is an advantage.

In addition, although the above-described floor cushioning material according to the present invention is used only as interior and exterior materials of a building, it can be naturally understood by those skilled in the art that it can be used as an interior wall partitioning an interior space of a building.

Hereinafter, preferred embodiments and comparative examples of the present invention will be described.

The following examples are intended to illustrate the invention and should not be understood as limiting the scope of the invention.

division water tributary foot room bar circa All gypsum city Wan Example 1 250 50 One 0.2 One One 7 220 30 2 Example 2 220 50 One 0.2 One One 7 220 30 7 Example 3 300 5 (*) One - One - 7 - 300 2 Example 4 350 50 One 0.1 One - 7 200 50 2 Example 5 350 50 One 0.1 One - 7 200 50 7 Example 6 350 50 One 0.1 One - 7 200 50 20 Example 7 200 50 One 0.1 One - 7 - 250 7 Example 8 200 50 One 0.1 One - 7 50 200 7  unit ; g feeder; As a tributary pulverized product, sludge contains water, and powder (*) does not contain water; Blowing agent, room; Preservative bar; Organic binders; Curing agent; Porous mineral city; Cement Wan; Buffer Grinding

Examples 1-4

The ingredients shown in Table 1 are mixed, poured into a plate-shaped mold, dried by an amount corresponding to 75% in the original moisture content using hot air, and left to cure (curing) to the floor buffer according to the present invention. Obtained.

Example 5

The ingredients shown in Example 5 of Table 1 were mixed, poured into a plate-shaped mold, and dried using an microwave in an amount corresponding to 75% of the original moisture content, and then rubber pieces were placed thereon 3 mm. After spraying to a thickness of, it was left to cure (cure) to obtain a floor buffer according to the present invention.

Examples 6-8

To prepare a mixture by mixing the components shown in Example 6 of Table 1, first sprinkled rubber pieces to a thickness of 3 mm in a plate-like mold, apply a liquid urethane thereon, and pour the mixture thereon, This was dried by an amount corresponding to 75% in the original moisture content using a microwave, and then left on it (curing) to obtain a floor buffer according to the present invention.

As described above, a plate-like floor cushioning material according to the present invention was obtained, which was found to be light and hard, so as to be suitable for absorbing and cushioning noise and shock.

Therefore, according to the present invention is made of a multi-layer, such as an apartment or an office, and the floor buffer to prevent the transmission of noise between floors in the field can easily form a floor immediately in accordance with the actual situation of the site and the floor buffer material and its manufacture In addition, the flooring can be completed in one place directly on the site, saving time and labor costs, and thus reducing the construction cost and blocking the noise between floors in the building. It is possible to form a quiet indoor atmosphere, and there is an effect of improving durability, such as impact. In addition, if the plate-like product can be used in winter, it can be used for economical use as well as shortening the air. In addition, it is possible to provide a lightweight, high-insulation product at a low price by providing a method that can be manufactured without the phenomenon of floating on the surface or rushing to the surface by injecting a material with excellent low-density thermal insulation such as poles into the slurry. The advantage is that it can contribute to stability.

Although the present invention has been described in detail only with respect to the described embodiments, it will be apparent to those skilled in the art that various changes and modifications can be made within the technical scope of the present invention, and such modifications and modifications belong to the appended claims.

Claims (9)

1 to 10 parts by weight of feed pulverized powder, 30 to 300 parts by weight of cement, 2 to 20 parts by weight of buffered pulverized material consisting of EVA chip, tire crushed, styrofoam pulverized powder or mixtures thereof, 5 to 10 parts by weight of porous mineral material, aqueous 0.5 to 1.5 parts by weight of an organic binder selected from the group consisting of acryl, ethylene vinyl acetate (EVA) and polyvinyl alcohol (PVA) and 0.5 to 1.5 parts by weight of a blowing agent. Floor cushioning material to prevent noise between floors of building. The method of claim 1, In the above, the porous mineral material is selected from the group consisting of tuff, volcanic rock, pumice, pumice, pearlite or a mixture of two or more thereof. The method of claim 1, Gypsum or waste gypsum is further included in an amount of 10 to 75% by weight based on 100% by weight of the buffer mixture, characterized in that the floor cushion for preventing noise between buildings. The method according to any one of claims 1 to 3, Floor cushioning material for preventing noise between floors of the building, characterized in that the rubber layer is further included on both sides or at least one surface of the floor cushioning material. (1) 1 to 10 parts by weight of feed pulverized product, 30 to 300 parts by weight of cement, 2 to 20 parts by weight of buffered pulverized product consisting of EVA chips, tire crushed products, styrofoam pulverized products or mixtures thereof, and 5 to 10 parts by weight of porous minerals. Parts, aqueous acrylic, 0.5 to 1.5 parts by weight of organic binder selected from the group consisting of ethylene vinyl acetate (EVA; ethylene vinyl acetate), polyvinyl alcohol (PVA), 0.5 to 1.5 parts by weight of blowing agent and water 200 Mixing step of mixing to 350 parts by weight; And (2) pouring the mixture obtained in the mixing step into a plate-like mold, and drying step of drying to about 70 to 80% of the original moisture content; floor buffer for preventing noise between floors of a building, characterized in that it comprises a Manufacturing method. The method of claim 5, wherein Method for manufacturing a floor cushioning material for preventing the noise between the floors, characterized in that it comprises the step of further forming a separate rubber layer on both sides or at least one surface of the floor cushioning material. (1) a stationary step of allowing the floor cushioning material for preventing the noise between floors of the building according to any one of claims 1 to 4 on the surface of the slab constituting the floor of the building; And (2) a mortar coating step of applying a mortar on the floor buffer standing on the slab; characterized in that it comprises a. The method of claim 7, wherein The step of forming the bottom layer, characterized in that the stationary step is composed of one or more thick bottom cushioning material or by stacking two or more thin floor buffers. The method according to claim 7 or 8, The method of forming a bottom layer, characterized in that further comprising the step of forming a polyurethane layer on the stationary bottom buffer after the stationary step.