KR20060085324A - Ceramic - Google Patents

Ceramic Download PDF

Info

Publication number
KR20060085324A
KR20060085324A KR1020050006047A KR20050006047A KR20060085324A KR 20060085324 A KR20060085324 A KR 20060085324A KR 1020050006047 A KR1020050006047 A KR 1020050006047A KR 20050006047 A KR20050006047 A KR 20050006047A KR 20060085324 A KR20060085324 A KR 20060085324A
Authority
KR
South Korea
Prior art keywords
ceramic
degrees
glaze
colors
color development
Prior art date
Application number
KR1020050006047A
Other languages
Korean (ko)
Inventor
김현숙
Original Assignee
김현숙
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김현숙 filed Critical 김현숙
Priority to KR1020050006047A priority Critical patent/KR20060085324A/en
Publication of KR20060085324A publication Critical patent/KR20060085324A/en

Abstract

본 발명은 세라믹 도자기에 발색도가 뛰어난 칠보안료를 결합하여 표면 착색처리를 하는것으로, 더욱 상세하게는 규석,사삼산화연,질산칼륨을 주성분으로한 유색 불투명인 분말상태의 유리질유약을 (도자기 유약이 묻지않은)1250도 정도에 고온 환원 소성해낸 세라믹 표면에 착색하여 800도 정도의 온도에 소성해냄으로서 기존의 세라믹 안료에서는 얻기 어려운 발색도가 뛰어난 다양하고도 화려한 색채를 얻어내는 것이다.The present invention is to surface-treat the surface of the ceramic pottery by combining the paint security paint with excellent color development, and more specifically, colored opaque powdery glaze (ceramic glaze) mainly composed of silica, lead trioxide, potassium nitrate This undivided) is colored on the surface of the ceramic, which has been hot-reduced and baked at about 1250 degrees, and calcined at about 800 degrees to obtain various and brilliant colors excellent in color development, which is difficult to obtain with conventional ceramic pigments.

세라믹, 칠보, 안료, 소성, 발색도Ceramic, Cloisonne, Pigment, Calcined, Color

Description

세라믹에 발색도가 뛰어난 칠보안료를 결합한 표면 처리{ceramic}Surface treatment that combines ceramic and lacquer paint with excellent color development {ceramic}

본 발명은 세라믹 도자기에 발색도가 뛰어난 칠보안료를 결합하여 표면 착색처리를 하는것이다. 일반적으로는 도자기에 색감을 표현할때 도자 표면에 투명, 불투명의 도자기 전용 유약을 시유하여 색상과 광택을 내어 사용하고 있다. 그러나 이와 같이 제조되는 경우 백자, 청자, 흑색, 갈색 등 제한적 색채로인해 도자기에 다양한 색채를 얻기어려운 문제점이 있다.The present invention is to perform a surface coloring process by combining a ceramic security paint with excellent color development. In general, when expressing the color of ceramics, they use color and luster by applying transparent and opaque ceramic glaze on the surface of ceramics. However, when manufactured in this way, due to the limited colors such as white porcelain, celadon, black, brown, there is a problem that it is difficult to obtain a variety of colors in ceramics.

본 발명은 상기와 같은 문제점을 해소하기위해 칠보 안료를 세라믹 표면에 착색함으로서 (일반적으로 교육용 물감에서 얻을 수 있는 20가지 표준 색과 이를 혼합하여 얻을 수 있는 색상 등) 표현 가능한 색상의 범위가 확대되어짐으로서 화려하고도 다양한 색채 표현이 가능하게된 것에 특징이 있다.
The present invention is to solve the above problems by coloring the cloisonne pigment on the ceramic surface (typically 20 kinds of colors that can be obtained from educational paints and colors obtained by mixing them, etc.) is expanded the range of colors that can be expressed It is characterized by being able to express colorful and various colors.

유색 불투명인 분말상태의 유리질유약을 세라믹 표면에 착색하여 800도정도 의 온도에 환원 소성함으로서 기존의 세라믹 안료에서는 얻기 어려운 발색도가 뛰어난 다양하고도 화려한 색채를 얻어내는 것이다.Color opaque powdery glass glaze is colored on the ceramic surface and reduced and calcined at a temperature of around 800 degrees to obtain a variety of colorful colors with excellent color development that is difficult to obtain with conventional ceramic pigments.

이상 상술한 바와같이 본 발명은, 세라믹에 발색도가 칠보 안료를 표면처리하는 방법으로서 도자기에서 (20가지 표준색상에서 얻을 수있는 색상과 그 혼합색 모두를) 다양하고도 화려한 색채를 얻어내는 것이다.As described above, the present invention is to obtain various and brilliant colors in ceramics (both of the colors obtainable from 20 standard colors and mixed colors thereof) in ceramics as a method of surface-treating cloisonne pigments on ceramics.

Claims (1)

세라믹을 700~800도에 소성해낸 후 실온건조하는 단계,Calcining the ceramic at 700 to 800 degrees and drying at room temperature, 세라믹에 1250도 정도에 고온 환원 소성해내낸 후 실온 건조하는 단계,High temperature reduction calcining the ceramic at about 1250 degrees and drying at room temperature, 유약이 묻지않은 세라믹 표면에 유색 불투명인 분말상태의 유리질유약인 칠보 안료를 착색하는 단계, Coloring the lacquered pigment, a glassy glaze of colored opaque powder, on a glaze-free ceramic surface, 상기 단계 후 800도 정도의 온도에 소성 표면처리하는 방법  Method of firing the surface at a temperature of about 800 degrees after the step
KR1020050006047A 2005-01-22 2005-01-22 Ceramic KR20060085324A (en)