KR20060064155A - Composition for artificial marble having a fiber - Google Patents

Composition for artificial marble having a fiber Download PDF

Info

Publication number
KR20060064155A
KR20060064155A KR1020040102858A KR20040102858A KR20060064155A KR 20060064155 A KR20060064155 A KR 20060064155A KR 1020040102858 A KR1020040102858 A KR 1020040102858A KR 20040102858 A KR20040102858 A KR 20040102858A KR 20060064155 A KR20060064155 A KR 20060064155A
Authority
KR
South Korea
Prior art keywords
weight
parts
artificial marble
fibers
composition
Prior art date
Application number
KR1020040102858A
Other languages
Korean (ko)
Other versions
KR100609988B1 (en
Inventor
박응서
나도춘
전재욱
Original Assignee
제일모직주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 제일모직주식회사 filed Critical 제일모직주식회사
Priority to KR1020040102858A priority Critical patent/KR100609988B1/en
Publication of KR20060064155A publication Critical patent/KR20060064155A/en
Application granted granted Critical
Publication of KR100609988B1 publication Critical patent/KR100609988B1/en

Abstract

본 발명의 섬유질을 함유한 인조 대리석 조성물은 (a)아크릴 수지 시럽 100 중량부; (b) 0.1 내지 7 cm 길이의 섬유 0.001 내지 10 중량부; (c) 무기 충전물 100 내지 200 중량부; (d) 가교제 0.1 내지 10 중량부; 및 (e) 중합 개시제 0.1 내지 10 중량부로 이루어진다. 본 발명의 인조 대리석 조성물은 전통 한지 패턴을 연출할 수 있다. Artificial marble composition containing the fiber of the present invention (a) 100 parts by weight of acrylic resin syrup; (b) 0.001 to 10 parts by weight of fibers having a length of 0.1 to 7 cm; (c) 100 to 200 parts by weight of the inorganic filler; (d) 0.1 to 10 parts by weight of a crosslinking agent; And (e) 0.1 to 10 parts by weight of a polymerization initiator. The artificial marble composition of the present invention can produce a traditional Hanji pattern.

인조 대리석, 무기 충전물, 마블칩, 섬유, 섬유질, 한지Artificial marble, inorganic fillers, marble chips, fibers, fibres, Korean paper

Description

섬유질을 함유한 인조 대리석 조성물{Composition for Artificial Marble Having a Fiber} Composition for Artificial Marble Having a Fiber             

제1도는 본 발명에 따른 섬유질을 함유한 인조 대리석을 나타낸 사진이다. 1 is a photograph showing the artificial marble containing the fiber according to the present invention.

발명의 분야Field of invention

본 발명은 섬유질을 함유하는 인조 대리석 조성물에 관한 것이다. 보다 구체적으로, 본 발명은 아크릴계 인조대리석용 조성물에 특정 길이의 섬유를 첨가시킴으로써, 전통 한지 패턴을 연출한 인조 대리석 조성물에 관한 것이다. The present invention relates to artificial marble compositions containing fibers. More specifically, the present invention relates to an artificial marble composition which produces a traditional Korean paper pattern by adding a fiber of a specific length to the acrylic artificial marble composition.

발명의 배경Background of the Invention

인조대리석은 최근 건축 내장재로 많이 사용되고 있으며, 그 사용되는 베이스 레진(Base resin)에 따라 크게 아크릴계와 불포화 폴리에스터계의 두 가지 종류 로 구분된다. 이 중 아크릴계 인조 대리석은 수지 자체의 은은한 투명성과 고급스러운 질감 및 우수한 내후성 등의 장점으로 인해 여러 가지 용도로 사용되고 있으며, 그 수요가 계속 증가하고 있다.Artificial marble has recently been widely used as a building interior material, and is classified into two types, acrylic and unsaturated polyester, depending on the base resin used. Among them, acrylic artificial marble is used for various purposes due to its soft transparency, luxurious texture, and excellent weather resistance, and its demand is continuously increasing.

예를 들면, 씽크대 상판, 세면 화장대의 상판, 은행 및 일반 매장의 접수대 등 각종 카운터의 상판, 내벽재, 각종 인테리어 조형물 등의 소재로서 그 사용이 확대되고 있다.For example, its use is being expanded as a material for counter tops, interior walls, various interior sculptures, such as sink tops, vanity tops, banks and reception desks in general stores.

이처럼 인조대리석의 용도가 다양해짐에 따라 다양한 패턴 및 디자인을 갖는 인조대리석이 개발되었으나, 기존의 천연대리석의 패턴에서 벗어나지는 못하였고, 다양한 소비자의 욕구에 부응하기에는 역부족이었다. 또한 지금까지 개발되어온 인조대리석은 차가운 느낌의 대리석 패턴이 일색이었고, 전통 한지 패턴을 연출하는 것은 아직까지 시도된 바 없다. As the use of artificial marble is diversified as described above, artificial marble having various patterns and designs has been developed, but it has not been released from the existing natural marble pattern, and it has been insufficient to meet various consumer needs. In addition, the artificial marble that has been developed so far has a cold marble pattern, and no traditional Korean paper pattern has been attempted.

따라서 본 발명자는 기존의 대리석 패턴에서 벗어나 아크릴계 인조대리석용 조성물에 특정 길이의 섬유질을 첨가시킴으로써, 전통 한지 패턴을 연출한 인조 대리석 조성물을 개발하기에 이른 것이다. Therefore, the present inventors have led to the development of artificial marble compositions that produce a traditional Korean paper pattern by adding fibers of a specific length to the composition for acrylic artificial marble, away from the existing marble pattern.

본 발명의 목적은 전통 한지 패턴을 갖는 인조 대리석 조성물을 제공하기 위한 것이다.An object of the present invention is to provide an artificial marble composition having a traditional Hanji pattern.

본 발명의 상기 목적 및 기타의 목적들은 하기 설명되는 본 발명에 의해 모두 달성될 수 있다. The above and other objects of the present invention can be achieved by the present invention described below.                         

이하, 본 발명의 내용을 하기에 상세히 설명한다.
Hereinafter, the content of the present invention will be described in detail below.

본 발명의 섬유질을 함유한 인조 대리석 조성물은 (a)아크릴 수지 시럽 100 중량부; (b) 0.1 내지 7 cm 길이의 섬유 0.001 내지 10 중량부; (c) 무기 충전물 100 내지 200 중량부; (d) 가교제 0.1 내지 10 중량부; 및 (e) 중합 개시제 0.1 내지 10 중량부로 이루어진다. 이하, 본 발명의 각 성분을 하기에 상세히 설명한다. Artificial marble composition containing the fiber of the present invention (a) 100 parts by weight of acrylic resin syrup; (b) 0.001 to 10 parts by weight of fibers having a length of 0.1 to 7 cm; (c) 100 to 200 parts by weight of the inorganic filler; (d) 0.1 to 10 parts by weight of a crosslinking agent; And (e) 0.1 to 10 parts by weight of a polymerization initiator. Hereinafter, each component of this invention is demonstrated in detail below.

(a) 아크릴 수지 시럽 (a) acrylic resin syrup

본 발명에 사용되는 아크릴 수지 시럽은 아크릴계 단량체와 이들의 중합물인 폴리아크릴레이트가 용해되어 있는 수지 시럽이다. The acrylic resin syrup used in the present invention is a resin syrup in which an acrylic monomer and a polyacrylate which is a polymer thereof are dissolved.

상기 아크릴계 단량체로는 메타 아크릴산, 메틸 메타 아크릴레이트, 에틸 메타 아크릴레이트, 이소 프로필 메타 아크릴레이트, n-부틸 메타 아크릴레이트, 2-에틸 헥실 메타 아크릴레이트 등이 있다. The acrylic monomers include methacrylic acid, methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, 2-ethyl hexyl methacrylate, and the like.

상기 폴리아크릴레이트는 메틸 메타크릴레이트, 에틸 메타크릴레이트, 이소 프로필 메타크릴레이트, n-부틸 메타크릴레이트, 2-에틸 헥실 메타크릴레이트 등의 중합체이며 이중 폴리메틸메타크릴레이트(PMMA)가 가장 바람직하다. The polyacrylate is a polymer such as methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, 2-ethyl hexyl methacrylate, and the most preferred of which is polymethyl methacrylate (PMMA). desirable.

본 발명의 아크릴 수지 시럽은 아크릴 단량체의 함량이 65 중량% 이상이고, 폴리아크릴레이트 함량이 35 중량% 이하인 것이 바람직하다.The acrylic resin syrup of the present invention preferably has an acrylic monomer content of 65% by weight or more and a polyacrylate content of 35% by weight or less.

(b) 섬유질(b) fiber

본 발명에 사용되는 섬유질은 0.1 내지 7 cm 길이의 섬유를 사용한다. The fiber used in the present invention uses a fiber of 0.1 to 7 cm long.

상기 섬유질은 천연 섬유, 재생섬유 또는 합성섬유 어느 것이든 가능하다. 예컨대 천연섬유로 코코넛 껍질, 면, 마, 견 및 모 등을 사용할 수 있으며, 상기 합성 섬유의 예는 폴리에스테르, 폴리아미드, 폴리우레탄 및 아크릴 섬유 등을 사용할 수 있다. The fibers can be any of natural fibers, recycled fibers or synthetic fibers. For example, coconut shell, cotton, hemp, silk and wool may be used as the natural fiber, and examples of the synthetic fiber may include polyester, polyamide, polyurethane, and acrylic fiber.

본 발명에서는 인조대리석 조성물에 섬유질을 첨가함으로써, 한지 느낌이 나는 대리석을 연출할 수 있다. In the present invention, by adding fiber to the artificial marble composition, it is possible to produce a marble with a feeling of cold.

섬유질의 크기는 0.1 내지 7 cm가 바람직하다. 0.1 cm 미만의 섬유를 사용할 경우, 마블칩 분말하고 구분되지 않아 본 발명에서 원하고자 하는 미감을 얻을 수 없으며, 7 cm를 초과할 경우, 섬유간에 엉킴 현상이 일어나 공정상 문제점이 있다. The size of the fiber is preferably 0.1 to 7 cm. When using less than 0.1 cm fiber, it is not distinguished from the marble chip powder can not obtain the desired aesthetics in the present invention, if it exceeds 7 cm, there is a problem in the process entangled between the fibers occur.

사용되는 섬유의 직경은 특별한 제한이 없으며, 통상 의류용으로 제조되고 있는 섬유를 그대로 사용하여도 좋다. The diameter of the fiber to be used is not particularly limited, and may be used as is, which is usually manufactured for clothing.

본 발명에서 섬유질의 바람직한 함량은 아크릴 수지 시럽 100 중량부에 대하여 0.001 내지 10 중량부로 사용된다. 0.001 미만의 범위로 사용할 경우, 한지 느낌을 연출할 수 없으며, 10 중량부를 초과하여 사용할 경우, 지나친 섬유함량으로 섬유간에 서로 엉킴 현상이 일어난다. In the present invention, the preferred amount of fiber is used in 0.001 to 10 parts by weight based on 100 parts by weight of the acrylic resin syrup. When used in the range of less than 0.001, it can not produce a feeling of Hanji, when used in excess of 10 parts by weight, entanglement between the fibers occurs due to excessive fiber content.

(c) 무기 충전물(c) inorganic filler

본 발명의 무기 충전물은 탄산칼슘, 수산화 알루미늄, 실리카, 알루미나, 수 산화 마그네슘과 같이 당 분야에서 통상적으로 사용되는 무기 분말 중 어느 것도 사용 가능하며, 1 내지 100 ㎛의 크기를 갖는 것이 바람직하다. The inorganic filler of the present invention may be any of inorganic powders commonly used in the art, such as calcium carbonate, aluminum hydroxide, silica, alumina, magnesium hydroxide, and preferably has a size of 1 to 100 μm.

상기 무기 분말 중 특히, 수산화 알루미늄은 투명하고 미려한 대리석 형상의 외관을 갖는 인조대리석을 제조 할 수 있다는 점에서 바람직하다.Among the inorganic powders, aluminum hydroxide is particularly preferable in that it can produce artificial marble having a transparent and beautiful marble appearance.

본 발명의 무기 충전물의 혼합비는 아크릴 수지 시럽 100 중량부를 기준으로 무기 충전물이 100∼200 중량부, 더욱 바람직하기로는 120∼160 중량부로 첨가되는 것이 바람직하다. The mixing ratio of the inorganic filler of the present invention is preferably 100 to 200 parts by weight, more preferably 120 to 160 parts by weight of the inorganic filler, based on 100 parts by weight of the acrylic resin syrup.

(d) 가교제(d) crosslinking agent

본 발명의 가교제는 다 관능성 메타 아크릴레이트가 사용되며, 구체적인 예로는 에틸렌 글리콜 디 메타 아크릴레이트, 프로필렌 글리콜 디 메타 아크릴레이트, 글리세롤 트리 메타 아크릴레이트, 트리메틸 프로판 트리 메타 아크릴레이트 및 비스페놀 A 디 메타 아크릴레이트를 들 수 있다.As the crosslinking agent of the present invention, polyfunctional methacrylate is used, and specific examples thereof include ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, trimethyl propane trimethacrylate and bisphenol A dimethacrylate. The rate is mentioned.

상기 다 관능성 단량체는 아크릴 수지 시럽 100 중량부를 기준으로 0.1 내지 10 중량부로 첨가하며, 바람직하기로는 0.3 내지 10 중량부이다. The polyfunctional monomer is added in an amount of 0.1 to 10 parts by weight, preferably 0.3 to 10 parts by weight, based on 100 parts by weight of the acrylic resin syrup.

(e) 중합 개시제(e) polymerization initiator

본 발명의 중합 개시제로는 벤조일 퍼옥사이드, 라우로일 퍼옥사이드, 부틸 하이드로 퍼옥사이드, 큐밀 하이드로 퍼옥사이드등의 과산화물 또는 아조비스이소부틸로니트릴과 같은 아조 화합물을 사용한다.As the polymerization initiator of the present invention, peroxides such as benzoyl peroxide, lauroyl peroxide, butyl hydroperoxide, cumyl hydroperoxide or azo compounds such as azobisisobutylonitrile are used.

상기 중합개시제의 함량은 아크릴 수지 시럽 100 중량부 기준으로 0.1∼10 중량부가 바람직하다.The content of the polymerization initiator is preferably 0.1 to 10 parts by weight based on 100 parts by weight of the acrylic resin syrup.

본 발명은 상기 구성성분 외에도 통상의 0.1 내지 5 mm 크기의 마블칩 0 내지 100 중량부를 선택적으로 더 첨가하여 다양한 패턴을 연출할 수 있다. In addition to the above components, the present invention may selectively add 0 to 100 parts by weight of a conventional marble chip having a size of 0.1 to 5 mm to produce various patterns.

본 발명의 인조 대리석은 상기의 각 구성성분을 혼합하여 인조대리석 슬러리를 제조한 후 성형 셀에 뿌린 다음 통상의 방법으로 경화시켜 제조된다. The artificial marble of the present invention is prepared by mixing each of the above components to prepare an artificial marble slurry, sprinkled in a molding cell and then cured by a conventional method.

본 발명은 하기의 실시예에 의하여 보다 더 잘 이해될 수 있으며, 하기의 실시예는 본 발명의 예시 목적을 위한 것이며 첨부된 특허 청구 범위에 의하여 한정되는 보호범위를 제한하고자 하는 것은 아니다.The invention can be better understood by the following examples, which are intended for the purpose of illustration of the invention and are not intended to limit the scope of protection defined by the appended claims.

실시예 Example

30 %의 폴리메틸 메타 아크릴레이트와 70 %의 메틸메타 아크릴레이트의 혼합물로 이루어진 메틸메타 아크릴레이트 시럽 100 중량부, 3 cm 길이의 폴리에스테르 섬유 0.01 중량부, 수산화 알루미늄 120 중량부, 및 라우로일 퍼옥사이드 2 중량부를 혼합하여 인조대리석 슬러리를 제조하여 성형 셀에 뿌린 후 경화를 시켜 평판상의 인조대리석판을 얻었다. 제조된 인조대리석판은 한지 패턴이 표현되었으며, 도1에 나타내었다. 100 parts by weight of methylmethacrylate acrylate syrup consisting of a mixture of 30% polymethyl methacrylate and 70% methylmethacrylate, 0.01 part by weight of 3 cm polyester fiber, 120 parts by weight of aluminum hydroxide, and lauroyl The artificial marble slurry was prepared by mixing 2 parts by weight of peroxide, sprinkled on a molding cell, and cured to obtain a flat marble sheet. Hanji pattern is expressed in the manufactured artificial stone plate, it is shown in FIG.

본 발명의 인조 대리석 조성물은 기존의 대리석 패턴에서 벗어나 전통 한지 패턴을 연출하는 인조 대리석 조성물을 제공하는 발명의 효과를 갖는다.The artificial marble composition of the present invention has the effect of providing an artificial marble composition which produces a traditional Hanji pattern away from the existing marble pattern.

본 발명의 단순한 변형 내지 변경은 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 실시될 수 있으며, 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.Simple modifications or changes of the present invention can be easily carried out by those skilled in the art, and all such modifications or changes can be seen to be included in the scope of the present invention.

Claims (7)

(a) 아크릴 수지 시럽 100 중량부;(a) 100 parts by weight of acrylic resin syrup; (b) 0.1 내지 7 cm 길이의 섬유 0.001 내지 10 중량부;(b) 0.001 to 10 parts by weight of fibers having a length of 0.1 to 7 cm; (c) 무기 충전물 100 내지 200 중량부; (c) 100 to 200 parts by weight of the inorganic filler; (d) 가교제 0.1 내지 10 중량부; 및(d) 0.1 to 10 parts by weight of a crosslinking agent; And (e) 중합 개시제 0.1 내지 10 중량부;(e) 0.1 to 10 parts by weight of a polymerization initiator; 로 이루어지는 것을 특징으로 하는 섬유질을 함유한 인조 대리석 조성물.Artificial marble composition containing fibers, characterized in that consisting of. 제1항에 있어서, 상기 아크릴 수지 시럽(a)은 메타 아크릴산, 메틸 메타 아크릴레이트, 에틸 메타 아크릴레이트, 이소 프로필 메타 아크릴레이트, n-부틸 메타 아크릴레이트 및 2-에틸 헥실 메타 아크릴레이트로 이루어진 군으로부터 선택되는 아크릴계 단량체에 이들의 중합물인 아크릴중합물이 용해되어 있는 수지 시럽으로서, 아크릴 단량체 함량이 65 중량%이상, 폴리아크릴레이트 함량이 35 중량%이하인 것을 특징으로 하는 인조 대리석 조성물.The group of claim 1, wherein the acrylic resin syrup (a) is made of methacrylic acid, methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, and 2-ethyl hexyl methacrylate. A resin syrup in which an acrylic polymer of these polymers is dissolved in an acrylic monomer selected from the above, wherein the artificial marble composition is characterized in that the acrylic monomer content is 65% by weight or more and the polyacrylate content is 35% by weight or less. 제1항에 있어서, 상기 섬유(b)는 천연 섬유, 합성 섬유, 재생섬유 또는 이들의 혼합물인 것을 특징으로 하는 인조 대리석 조성물.The artificial marble composition of claim 1, wherein the fibers (b) are natural fibers, synthetic fibers, regenerated fibers, or mixtures thereof. 제3항에 있어서, 상기 천연섬유는 코코넛 껍질, 면, 마, 견 및 모로 이루어진 군으로부터 선택되고; 상기 합성섬유는 폴리에스테르, 폴리아미드, 폴리우레탄 및 아크릴 섬유로 이루어진 군으로부터 선택된 것을 특징으로 하는 인조 대리석 조성물.The method of claim 3, wherein the natural fiber is selected from the group consisting of coconut shell, cotton, hemp, silk and wool; The synthetic fiber is artificial marble composition, characterized in that selected from the group consisting of polyester, polyamide, polyurethane and acrylic fibers. 제1항에 있어서, 상기 무기 충전물(c)은 탄산칼슘, 수산화 알루미늄, 실리카, 알루미나 및 수산화 마그네슘으로 이루어진 군으로부터 선택되고; 상기 가교제(d)는 에틸렌 글리콜 디 메타 아크릴레이트, 프로필렌 글리콜 디 메타 아크릴레이트, 글리세롤 트리 메타 아크릴레이트, 트리메틸 프로판 트리 메타 아크릴레이트 및 비스페놀 A 디 메타 아크릴레이트로 이루어진 군으로부터 선택되는 것을 특징으로 하는 인조 대리석 조성물.The method of claim 1, wherein the inorganic filler (c) is selected from the group consisting of calcium carbonate, aluminum hydroxide, silica, alumina and magnesium hydroxide; Said crosslinking agent (d) is selected from the group consisting of ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, trimethyl propane trimethacrylate and bisphenol A dimethacrylate. Marble composition. 제1항에 있어서, 상기 인조 대리석 조성물은 0.1 내지 5 mm의 마블칩 0 내지 100 중량부를 더 포함하는 것을 특징으로 하는 인조 대리석 조성물.The artificial marble composition of claim 1, wherein the artificial marble composition further comprises 0 to 100 parts by weight of marble chips of 0.1 to 5 mm. 제1항 내지 제6항 중 어느 한 항의 조성물을 사용하여 제조된 인조 대리석.Artificial marble prepared using the composition of any one of claims 1 to 6.
KR1020040102858A 2004-12-08 2004-12-08 Composition for Artificial Marble Having a Korean Traditional Mulberry Paper Pattern KR100609988B1 (en)