KR20060006366A - The composition of self-leveling mortar by using a magnetite powder - Google Patents

The composition of self-leveling mortar by using a magnetite powder Download PDF

Info

Publication number
KR20060006366A
KR20060006366A KR1020040055319A KR20040055319A KR20060006366A KR 20060006366 A KR20060006366 A KR 20060006366A KR 1020040055319 A KR1020040055319 A KR 1020040055319A KR 20040055319 A KR20040055319 A KR 20040055319A KR 20060006366 A KR20060006366 A KR 20060006366A
Authority
KR
South Korea
Prior art keywords
total weight
cement
floor
present
magnetite
Prior art date
Application number
KR1020040055319A
Other languages
Korean (ko)
Inventor
박호규
Original Assignee
박종진
박진희
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박종진, 박진희 filed Critical 박종진
Priority to KR1020040055319A priority Critical patent/KR20060006366A/en
Publication of KR20060006366A publication Critical patent/KR20060006366A/en

Abstract

본 발명은 자철광 분말을 이용한 자동수평몰탈 조성물에 관한 것이다.The present invention relates to an automatic horizontal mortar composition using magnetite powder.

본 발명의 목적은 현재 사용중인 시멘트, 모래 및 레미콘 몰탈이 필요 없이 공장에서 모든 원자재를 일정한 배합 비율로 혼합한 뒤 지대에 포장하여 신축·보수 공사현장에 조달하여 현장에서는 본 발명품에 물만 혼합하여 바닥에 부으면 유동성과 제품의 안정성이 좋아 미장기능공이 필요 없이 스스로 바닥 수평과 면을 형성할 수 있는 제품의 개발에 있다.The object of the present invention is to mix all the raw materials at a constant mixing ratio in the factory without the need for cement, sand and ready-mix mortar currently in use and then packaged in a zone to procure to the construction and construction site, in the field to mix only water with the present invention floor It is in the development of products that can form the floor horizontally and face by themselves without the need of plastering workers because of its good fluidity and stability of the product.

지금까지는 대부분 아파트, 일반 주택, 방바닥 및 모든 건물 바닥에 일반 시멘트를 이용하여 바닥 마감 미장을 해 왔으나 바닥의 시멘트 양성 과정에서 발생한 독성으로 인해 새집 증후군이 발병하여 인체에 해가 되며 환경에도 위협적으로 작용하여 친환경성 제품의 필요성이 대두되어 왔다.Until now, most apartments, general houses, floors and all building floors have been plastered with general cement, but the toxicity of the cement-positive process on the floor causes sick house syndrome, which is harmful to the human body and threatens the environment. Therefore, the need for eco-friendly products has emerged.

본 제품은 이러한 문제점을 해결하기 위해서 탈취 기능 및 항균 작용 등으로 인체에 해가 없는 함티탄을 함유한 자철광을 이용하여 발명된 제품으로 자력으로 바닥미장이 되고 친환경성 바닥 미장재 조성물을 제공함에 있다.In order to solve this problem, this product is invented by using magnetite containing titanium containing no harm to human body due to deodorizing function and antibacterial effect.

상기 목적을 달성하기 위해서 본 발명의 구성은 전체 중량에 대한 백분율 30∼50％의 자철광 분말, 상기 전체 중량에 대한 백분율 20∼40％의 규사(SiO2), 상기 전체 중량에 대한 백분율 1∼1.5％의 알루미나 시멘트, 상기 전체 중량에 대한 백분율 0.8∼1.2％의 조강시멘트, 상기 전체 중량에 대한 백분율 0.5∼1.5％의 유동 화재, 상기 전체 중량에 대한 백분율 0.02∼0.6％의 소포재, 상기 전체 중량에 대한 백분율 0.1∼4％의 분말 접착제, 상기 전체 중량에 대한 0.05∼0.6％의 MC,상기 전체 중량에 대한 5∼10％의 보통 포틀랜트 시멘트, 상기 전체 중량에 대한 2∼5％의 슬래그 시멘트, 상기 전체 중량에 대한 백분율 1∼6％의 일반수지로 배합되어 이루어지는 것을 특징으로 한다.In order to achieve the above object, the composition of the present invention is 30% to 50% magnetite powder based on the total weight, 20% to 40% silica sand (SiO 2 ) based on the total weight, and 1 to 1.5 percentage based on the total weight. % Alumina cement, 0.8-1.2% crude steel cement percentage, total flow 0.5% to 1.5% flow fire, 0.02 to 0.6% antifoam material, total weight 0.1 to 4% powder adhesive, 0.05 to 0.6% MC to the total weight, 5 to 10% ordinary portland cement to the total weight, 2 to 5% slag cement to the total weight It is characterized by consisting of a general resin of 1 to 6% by weight based on the total weight.

자철광 바닥 미장재Magnetite Floor Plaster

Description

자철광 분말을 이용한 자동수평몰탈 조성물{The composition of self-leveling mortar by using a magnetite powder}The composition of self-leveling mortar by using a magnetite powder}

본 발명은 자철광 분말을 이용한 자동수평몰탈 조성물에 관한 것이다. 현재 아파트 방바닥 공사 및 신축·보수 공사에서 바닥 마감 미장 작업을 미장기능공이 하고 있으나 숙련된 미장 기능공일지라도 기존 재료로 쓰인 일반시멘트와 모래를 혼합하여 만든 몰탈(Mortar)을 가지고는 마감 미장 공사를 할 때 바닥면을 정확하게 평탄하게 시공하지는 못한다. 또한 골재(모래) 품질이 균일하지 못하여 바닥면에 강도 저하와 균열 발생으로 마감 미장공사 후에 이루어지는 최종 마감 공사에 지장을 주고 있으며 현장 여건에 따라 재시공을 하여 마감 미장면을 보수한 후 최종 마감재를 시공하고 있다.The present invention relates to an automatic horizontal mortar composition using magnetite powder. Plasterer is doing floor finishing in apartment floor construction and new construction and repair work, but even a skilled plasterer is using mortar made of a mixture of general cement and sand used as existing materials. It is not possible to install the floor correctly and flatly. In addition, the quality of aggregate (sand) is not uniform, which affects the final finishing work after finishing plastering due to the decrease in strength and cracks on the bottom surface, and the final finishing work after repairing the finishing plastering surface according to the site conditions. Doing.

이런 각종 바닥 공사와 특히 아파트 및 주택 방바닥 미장 공사를 하는데 있어 시공방법과 원자재를 공사현장에서 손쉽고 빠르게 사용할 수 있도록 하여 시공 능률 향상과 자철광 분말을 혼합하여 현장에서는 시멘트 모래 등이 필요 없이 발명한 제품에 물만 부어 사용하면 바닥 미장 공사와 친환경성으로 인체에 해가 없는 자철광 자동수평 바닥 공사의 효과를 동시에 얻을 수 있으며 따라서 공사의 원가 절감 및 인건비 공사시간 단축을 가져 올 수 있도록 하는 취지로 연구에 착수하게 되었다. 본 발명은 각종 신축 ·보수 공사시 아파트, 주택, 연구실, 지하실 바닥, 공장 바닥, 교실 바닥, 공공시설 바닥 등 다용도로 이용된다. 현재 각종 신축·보수 공사시 방바닥 및 넓은 바닥 미장 공사를 하기 위해서는 현장에서 레미콘 몰탈을 사용하거나 시멘트와 모래를 혼합하여 사용하고 있는데 현재 사용중인 몰탈 자재는 유동성이 없어 숙련된 미장공이 쇠손(미장칼)으로 면을 잡아 시공하고 있는 실정이다. 그러나 기능공의 시공 능력에 큰 차이가 있고 바닥면이 정확히 고르지 못하고 강도 저하로 응결 후 균열 발생과 표면이 일어나는 현상이 발생하는 것과 시멘트 양생 기간동안 독성이 나와 인체에 해로움을 주고 있는 문제점이 있다.In the construction of various types of flooring, especially apartment and house floor plastering, construction methods and raw materials can be used easily and quickly at the construction site, improving construction efficiency and mixing magnetite powder. If only water is used, it can be applied to the floor plastering and eco-friendliness, and it is possible to achieve the effect of self-magnetizing auto-horizontal flooring without harming the human body at the same time. It became. The present invention is used for various purposes such as apartments, houses, laboratories, basement floors, factory floors, classroom floors, public facilities floors, etc. during various new construction and repair work. At the time of construction and renovation of various types of floor and wide-floor plastering, we are using ready-mixed concrete mortar or mixing cement and sand on the site. It is a situation that is holding the cotton. However, there is a big difference in the construction ability of the craftsman, the bottom surface is not exactly, there is a problem that the occurrence of cracks and surface occurs after condensation due to the decrease in strength and the toxicity caused during the cement curing period to harm the human body.

본 발명은 상기의 제반 문제점을 해소하기 위해서 현장에서 시멘트, 모래 및 레미콘 몰탈이 필요 없이 공장에서 모든 원자재를 일정한 배합 비율로 혼합한 뒤 지대에 포장하여 현장에 조달하고 현장에서 본 발명품에 물만 혼합하여 바닥에 부으면 유동성과 접착력, 안정성 등이 좋아 스스로 바닥 미장이 되게 하고 시멘트 독성이 나오지 않아 탈취 및 항균 작용 등으로 모든 사람들에게 쾌적한 주거 생활을 제공함을 목적으로 한다.The present invention is to eliminate all the above problems in the field without the need for cement, sand and ready-mixed mortar in the factory to mix all the raw materials in a constant mixing ratio, packed in the field to procure to the site and to mix the water with the present invention in the field When it is poured on the floor, it has good fluidity, adhesiveness, and stability, so that it becomes a plasterer on its own, and cement toxicity does not come out.

이와 같은 목적을 달성하기 위한 본 발명의 구성은 전체 중량에 대한 백분율 30∼50％의 자철광 분말, 상기 전체 중량에 대한 백분율 20∼40％의 규사(SiO2), 상기 전체 중량에 대한 백분율 1∼1.5％의 알루미나 시멘트, 상기 전체 중량에 대한 백분율 0.8∼1.2％의 조강시멘트, 상기 전체 중량에 대한 백분율 0.5∼1.5％의 유동화재, 상기 전체 중량에 대한 백분율 0.02∼0.6％의 소포재, 상기 전체 중량에 대한 백분율 0.1∼4％의 분말 접착제, 상기 전체 중량에 대한 0.05∼0.6％의 MC, 상기 전체 중량에 대한 5∼10％의 보통 포틀랜트 시멘트, 상기 전체 중량에 대한 2∼5％의 슬래그 시멘트, 상기 전체 중량에 대한 백분율 1∼6％의 일반수지로 배합되어 이루어지는 것을 특징으로 한다.The composition of the present invention for achieving the above object is 30 to 50% magnetite powder, 30% to 40% silica sand (SiO 2 ), 1 to 20% by weight of the total weight. 1.5% alumina cement, 0.8-1.2% crude steel cement as a percentage of the total weight, 0.5 to 1.5% fluidizing agent as a percentage of the total weight, 0.02 to 0.6% antifoam material as the total weight, the total 0.1 to 4% by weight powder adhesive, 0.05 to 0.6% MC to the total weight, 5 to 10% ordinary portland cement to the total weight, 2 to 5% slag to the total weight Cement, characterized in that it is formulated with a general resin of 1 to 6% by weight based on the total weight.

본 발명인 자철광 분말을 이용한 자동수평몰탈 바닥 미장재 조성물에 대해 상세히 설명한다.The automatic horizontal mortar floor plastering composition using the present magnetite powder will be described in detail.

실시 예) 자철광 분말을 이용한 자동수평몰탈 바닥 미장재 조성물의 구성은 다음의 표1과 같다.Example) The composition of the automatic horizontal mortar floor plastering composition using magnetite powder is shown in Table 1 below.

(표 1)Table 1

Figure 112004510484684-PAT00002
Figure 112004510484684-PAT00002

본 발명에서 사용하는 자철광 자동수평몰탈 바닥 미장재 조성물은 자철광 분말과 규사(SiO2), 혼화재, 조강시멘트, 유동화재, 일반수지가 첨가된다.Magnetite automatic horizontal mortar floor plastering composition used in the present invention is a magnetite powder and silica sand (SiO 2 ), admixture, crude steel cement, fluidized fire, general resin is added.

상기 재료로 쓰이는 자철광 분말은 우리나라 중부지방에 매장량이 많이 있어 원료구입 및 가격에서도 경쟁력이 되어 원료로 사용하였다. 일반시멘트는 독성 문제로 소량을 사용하여 친환경성 및 쾌적한 주거 생활을 할 수 있도록 한 것이다.Magnetite powder used as the material has a lot of reserves in the central region of Korea, so it is competitive in raw material purchase and price was used as raw materials. General cement is to use ecologically friendly and comfortable living by using small amount because of toxicity.

골재(모래)는 본 발명품의 특성상 일반 모래를 쓰지 않고 세척하고 건조된 상태의 규사((SiO2)를 사용하였으며 유동성과 친밀성을 만족시키기 위해 입자크기는 6∼7호사를 사용하였으며 함량은 전체 중량비의 20∼40％이며 가장 적정한 함량은 중량비의 40％이다.Aggregate (sand) was washed without using sand due to the characteristics of the present invention and dried silica sand ((SiO 2 ) was used. To satisfy fluidity and intimacy, particle size 6 to 7 yarn was used. 20-40% by weight and the most suitable content is 40% by weight.

본 발명품의 조강 시멘트는 초속경성의 성질을 가지고 초기 고강도 및 내화 학성의 기능을 가지고 있으며 일반 시멘트 및 자철광 분말과 혼합 사용이 가능하고 혼합 비율은 중량비의 0.8∼1.2％로 조절되어 사용하여야 하며 가장 적정한 함량은 중량비의 0.8％이다.The crude steel cement of the present invention has the property of ultra-high hardness and has the function of initial high strength and chemical resistance, and can be mixed with general cement and magnetite powder, and the mixing ratio should be adjusted to 0.8 to 1.2% of the weight ratio, and the most suitable The content is 0.8% of the weight ratio.

제품의 유동성을 좋게 하는 유동화재로는 우수한 유동성으로 미세한 틈새까지 침투가 되고 자기 스스로 평탄성을 가지고 있는 멜라민계를 사용하였다.As a fluid fire to improve the fluidity of the product, melamine was used, which penetrates into fine gaps with excellent fluidity and has flatness itself.

나머지 조성물은 소포재 0.02∼0.6％, 일반수지 1∼6％, MC 0.05∼0.6％와 보통 포틀랜트 시멘트 5∼10％로 되어 있다.The remaining compositions consist of 0.02 to 0.6% of antifoam material, 1 to 6% of general resin, 0.05 to 0.6% of MC, and 5 to 10% of ordinary portland cement.

현장에서 본 발명품과 혼합될 최적의 물 함량은 중량비의 24∼27％이다.The optimum water content to be mixed with the invention in the field is 24 to 27% by weight.

상기 조성된 자철광 분말을 이용한 자동수평몰탈 바닥 미장재 조성물을 사용하려면 시공하고자 하는 바닥을 불순물이 없도록 깨끗이 청소하여야 하고 청소가 끝나면 접착제를 바닥에 도포하여야 한다.In order to use the automatic horizontal mortar floor plastering composition using the magnetite powder prepared above, the floor to be constructed should be cleaned to be free of impurities, and after cleaning, an adhesive should be applied to the floor.

접착제 도포가 끝나면 본 발명품인 자철광 분말을 이용한 자동수평몰탈 바닥 미장재 조성물을 물과 함께 교반시킨 다음 바닥에 타설을 하고 양생과정이 지나면 바닥미장 작업이 완료된다.After the adhesive is applied, the auto horizontal mortar floor plastering composition using magnetite powder of the present invention is stirred with water, and then poured on the floor, and the floor plastering operation is completed after the curing process.

본 발명품은 제품을 현장에서 물만 부어 사용하고 미장과 항균 및 탈취기능으로 쾌적한 주거 환경과 인체에 해가 없고 건강 증진에 좋은 효과를 동시에 얻을 수 있다. 또한 복잡한 도심 공간의 신축 및 보수 공사 현장에서는 시멘트, 모래 등 자재를 현장에 보관하거나 레미콘 차량 및 시멘트를 운반하는 대형 트럭 등이 그동안 교통 혼잡을 가중시키고 작업시 많은 소음과 먼지 등 환경 오염을 유발시키고 있고 기존 미장 몰탈은 두께를 얇게 할 수 없으나 본 발명품은 5∼10mm 이하의 두 께로 시공하여도 이상이 없다.The present invention can be used to pour only water in the field, and by using the plastering, antibacterial and deodorizing function, a comfortable living environment and harm to the human body can be obtained at the same time good effect on health promotion. In addition, in the construction and renovation of complex urban spaces, materials such as cement and sand are stored on site or ready-made concrete trucks and heavy trucks carrying cement have increased traffic congestion and caused a lot of noise and dust during work. And the existing plaster mortar can not be thin, but the present invention is no problem even if the construction of a thickness of less than 5 ~ 10mm.

이상에서 진술한 바와 같이 본 발명에서는 자철광 자재와 유동화재 등을 이용하여 아파트 및 주택 방바닥, 실험실, 사무실 등 각종 바닥 마감 공사에서 누구나 손쉽게 현장에서 물만 부어 사용할 수 있고 실내 공간에 공기오염물질이 존재하고 있는 상태에서 본 발명품을 사용하였을 때 시멘트 독성 제거와 항균 및 탈취 효과가 있어 건강에 좋은 효과가 있다.As mentioned above, in the present invention, anyone can easily pour water in the field and use air pollutants in the interior space in various floor finishing works such as apartments, house floors, laboratories, and offices using magnetite materials and fluidized fires. When the present invention is used in the state that there is a cement toxicity removal and antibacterial and deodorizing effect is good for health.

Claims (1)

전체 중량에 대한 백분율 30∼50％의 자철광 분말, 상기 전체 중량에 대한 백분율 20∼40％의 규사(SiO2), 상기 전체 중량에 대한 백분율 1∼1.5％의 알루미나 시멘트, 상기 전체 중량에 대한 백분율 0.8∼1.2％의 조강시멘트, 상기 전체 중량에 대한 백분율 0.5∼1.5％의 유동화재, 상기 전체 중량에 대한 백분율 0.02∼0.6％의 소포재, 상기 전체 중량에 대한 백분율 0.1∼4％의 분말 접착제, 상기 전체 중량에 대한 0.05∼0.6％의 MC, 상기 전체 중량에 대한 5∼10％의 보통 포틀랜트 시멘트, 상기 전체 중량에 대한 2∼5％의 슬래그 시멘트, 상기 전체 중량에 대한 백분율 1∼6％의 일반수지로 배합되어 이루어지는 것을 특징으로 하는 자철광 분말을 이용한 자동수평몰탈 바닥 미장재 조성물30 to 50% magnetite powder, 20% to 40% silica sand (SiO 2 ), 1% to 1.5% alumina cement, 2% to total weight 0.8-1.2% crude steel cement, 0.5-1.5% fluidized material by weight relative to the total weight, 0.02-0.6% antifoam material by weight based on the total weight, 0.1-4% powder adhesive by weight based on the total weight, 0.05 to 0.6% MC to the total weight, 5 to 10% ordinary Portland cement to the total weight, 2 to 5% slag cement to the total weight, 1 to 6% percentage to the total weight Automatic horizontal mortar floor plastering composition using magnetite powder, characterized in that it is formulated with a general resin of
KR1020040055319A 2004-07-15 2004-07-15 The composition of self-leveling mortar by using a magnetite powder KR20060006366A (en)