KR20060001947A - The plastic multi-wall pipe with high durability - Google Patents

The plastic multi-wall pipe with high durability Download PDF

Info

Publication number
KR20060001947A
KR20060001947A KR1020050125414A KR20050125414A KR20060001947A KR 20060001947 A KR20060001947 A KR 20060001947A KR 1020050125414 A KR1020050125414 A KR 1020050125414A KR 20050125414 A KR20050125414 A KR 20050125414A KR 20060001947 A KR20060001947 A KR 20060001947A
Authority
KR
South Korea
Prior art keywords
cross
synthetic resin
profile
section
pipe
Prior art date
Application number
KR1020050125414A
Other languages
Korean (ko)
Inventor
장병익
Original Assignee
주식회사천마산업사
장병익
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사천마산업사, 장병익 filed Critical 주식회사천마산업사
Priority to KR1020050125414A priority Critical patent/KR20060001947A/en
Publication of KR20060001947A publication Critical patent/KR20060001947A/en

Abstract

본 발명은 내구성이 강화된 합성수지 다중벽관에 관한 것으로, 이는 그 내부에 중공층(12)이 형성된 사각 단면의 외벽(11)을 형성하되, 그 각 모서리에 수평으로 돌출된 결속날개부(13)가 형성되어, 대략 그 단면이 ‘

Figure 112005074173876-PAT00001
’형상을 가진 합성수지 프로파일(10)을 연속으로 압출하고, 이를 드럼상으로 감아 일정 길이를 형성하되, 각 사이는 용융된 합성수지(20)의 주입으로 ‘
Figure 112005074173876-PAT00002
’의 단면 형태로 경화되어 감긴 프로파일(10) 사이를 접합·연결한 합성수지 다중벽관(30)을 구성하여, 이를 매설용 파이프로 쓰임에 따라, 길이 방향의 결속력이 높여 프로파일(10) 간의 전단 파괴를 방지하고, 굽힘 및 외력에 대한 강성을 높여, 이에 대한 변형을 최소화한 것이다.The present invention relates to a durable reinforced plastic multi-wall tube, which forms an outer wall (11) of a rectangular cross section in which a hollow layer (12) is formed therein, wherein the binding wings (13) protrude horizontally at each corner thereof. Is formed, roughly its cross section is'
Figure 112005074173876-PAT00001
'A continuous extrusion of the shape of the synthetic resin profile 10, and wound around the drum to form a certain length, between each injection of molten synthetic resin 20'
Figure 112005074173876-PAT00002
The composite resin multi-wall tube 30 is formed by joining and connecting the profiles 10 cured and wound in the cross-sectional shape of the cross section, and as the pipe is used as a buried pipe, the binding force in the longitudinal direction is increased to shear shear between the profiles 10. To prevent bending, increase rigidity against bending and external force, and minimize deformation thereof.

다중벽관, 합성수지, 내구성, 강성, 파이프, 보강, 전단파괴, 결속력 Multi-walled pipe, synthetic resin, durability, rigidity, pipe, reinforcement, shear failure, binding force

Description

내구성이 강화된 합성수지 다중벽관 { the plastic multi-wall pipe with high durability }Plastic multi-wall pipe with high durability}

도 1은 본 발명의 실시예에 따른 합성수지 다중벽관의 사시도 및 일부 확대도.1 is a perspective view and a partially enlarged view of a synthetic resin multi-wall tube according to an embodiment of the present invention.

도 2는 본 발명의 실시예에 따른 합성수지 다중벽관의 단면도.Figure 2 is a cross-sectional view of a synthetic resin multi-walled tube according to an embodiment of the present invention.

도 3은 본 발명의 다른 실시예에 따른 합성수지 다중벽관의 단면도.Figure 3 is a cross-sectional view of a synthetic resin multi-walled tube according to another embodiment of the present invention.

도 4는 도 3의 A부분 확대도.4 is an enlarged view of a portion A of FIG. 3;

도 5는 본 발명과 관련한 종래도.Figure 5 is a conventional view related to the present invention.

도 6은 본 발명에 따른 합성수지 다중벽관 제조 장치의 실시예 단면도.6 is a cross-sectional view of an embodiment of a synthetic resin multi-wall tube manufacturing apparatus according to the present invention.

도 7은 도 6의 BB′부분 단면도.7 is a partial cross-sectional view taken along line BB ′ of FIG. 6.

[ 도면의 주요 부분에 대한 부호의 설명 ][Description of Code for Major Parts of Drawing]

10 : 프로파일 12 : 중공층 13 : 결속날개부10 profile 12 hollow layer 13 binding wing portion

14 : 보강부 20 : 합성수지 30 : 다중벽관14: reinforcement 20: synthetic resin 30: multi-wall pipe

본 발명은 내구성이 강화된 합성수지 다중벽관에 관한 것으로,‘

Figure 112005074173876-PAT00003
’형상의 단면으로 압출된 프로파일을 드럼상으로 감아 일정 길이를 형성하되, 각 감긴 틈새는 용융된 합성수지의 주입으로 접합한 합성수지 다중벽관을 구성하여, 이를 매설용 파이프로 쓰임에 따라, 원주 방향에 따른 전단 파괴를 방지하고, 길이 방향에 따른 결속력을 높여, 굽힘 및 외력에 의한 변형을 방지하는 것이다.The present invention relates to a synthetic resin multi-wall tube with enhanced durability,
Figure 112005074173876-PAT00003
'The profile extruded into the cross-section of the shape is rolled into a drum to form a certain length, each of which is formed of a synthetic multi-walled pipe joined by injection of molten synthetic resin, which is used as a buried pipe, To prevent shear failure and increase the binding force along the longitudinal direction, to prevent deformation due to bending and external force.

일반적으로, 파이프는 속이 빈 가늘고 긴 관으로, 수도관, 가스관, 송유관 등과 같이 매설되어 기체 또는 액체와 같은 유체 및 분체를 수송하거나, 또는, 땅 속이나 옥내에 배선을 할 때, 전선·케이블의 보호용으로 이용되고 있으며, 그 종류를 재료로 분류하면, 강관, 주철관, 구리관, 황동관, 알루미늄과 같은 금속관과, 합성수지관, 철근콘크리트관, 석면시멘트관, 고무관, 목관 등과 같은 비금속관으로 크게 나눌 수 있다.Generally, a pipe is a hollow, long, thin tube, which is buried such as a water pipe, a gas pipe, an oil pipe, or the like for transporting fluids and powders such as gases or liquids, or for wiring of wires or cables in the ground or indoors. The materials are classified into materials, and they are broadly divided into steel pipes, cast iron pipes, copper pipes, brass pipes, metal pipes such as aluminum, and non-metallic pipes such as synthetic resin pipes, reinforced concrete pipes, asbestos cement pipes, rubber pipes, and wood pipes. Can be.

특히, 상기 비금속관 중에서, 합성수지 파이프는 폴리프로필렌, 폴린에틸렌, 폴리염화비닐과 같은 열가소성 수지를 이용하여 제작한 것으로, 대체로 가볍고, 내식성이 좋으며, 접합이 용이하여 많이 이용되는데, 굽힘에 대한 강도를 증가시키기고, 관의 지름방향의 변형에 대한 버팀력 증강 및 내부 물질의 보온 등을 위해 이중벽 또는 다중벽을 가지는 합성수지 다중벽관의 사용이 두드러지고 있다.Particularly, among the non-metallic pipes, synthetic resin pipes are manufactured by using thermoplastic resins such as polypropylene, polyethylene, polyvinyl chloride, and are generally used because they are light, have good corrosion resistance, and are easily bonded. Increasingly, the use of double walled or multiwalled synthetic resin multi-walled pipes is prominent for increasing the strength of the tube against deformation in the radial direction and keeping the inner material warm.

이와 같은 종래의 합성수지 이중관을 도5를 참조하여 설명하면, 이는 용융된 합성수지를 공급받아 금형으로 통과시켜, 일정 단면 형상으로 압출하는 압출기를 통해, 내부가 빈 사각형의 단면을 가지는 프로파일(1)을 연속적으로 압출하고, 이 프로파일(1)을 드럼상에 권취하면서, 감긴 프로파일(1) 사이를 용융된 합성수지(3)의 주입으로 접합하며, 이들은 냉각기를 거쳐 경화되어 합성수지 이중관(1)을 제작한다.Referring to FIG. 5, such a conventional synthetic resin double tube is provided. A profile 1 having an empty rectangular cross section is formed through an extruder that receives molten synthetic resin and passes the result in a mold to extrude a predetermined cross-sectional shape. While extruding continuously, the profile 1 is wound on a drum, and the wound between the wound profiles 1 is joined by injection of molten synthetic resin 3, which is cured through a cooler to produce a synthetic resin double tube 1. .

이러한 구조의 합성수지 이중관은, 권취되는 프로파일 사이가 밋밋함에 따라, 이를 접합하는 합성수지가 대략 ‘I’자의 단면 형태로 접합되어, 각 프로파일 사이의 긴밀성이 떨어져 길이 방향에 따른 굽힘에 약하고, 원주 방향에 따른 외력 및 내압에 대해, 합성수지로 접합한 부분의 전단 파괴가 일어나는 문제점이 있었다.Synthetic resin double tube of such a structure, as the winding between the profile is flat, the synthetic resin to join it is bonded in the form of 'I' cross-section, the tightness between each profile is weak and weak in bending along the longitudinal direction, in the circumferential direction According to the external force and the internal pressure, there was a problem that the shear failure of the portion joined with the synthetic resin occurs.

따라서 본 발명은 상기의 문제점을 해결하고자,‘

Figure 112005074173876-PAT00004
’형상의 단면으로 압출된 합성수지 프로파일을 드럼상으로 감아 일정 길이를 형성하되, 각 감긴 틈새는 용융된 합성수지의 주입으로 접합한 합성수지 다중벽관을 구성하여, 이를 매설용 파이프로 쓰임에 따라, 이중 구조에 따른 내구성과 강성이 높아 외력에 따른 변형 을 최소화하고, 접합된 합성수지의 단면이 대략 ‘
Figure 112005074173876-PAT00005
’의 단면 형태로 형성되어, 길이 방향에 따른 결속력을 높이고, 기존 ‘I’자 단면의 접합 구조보다 굽힘 및 외력에 대한 강성을 높이며, 감긴 프로파일 간의 전단 파괴를 방지하는데 그 목적이 있다.Therefore, the present invention is intended to solve the above problems,
Figure 112005074173876-PAT00004
'The resin profile extruded into the cross-section of the shape is wound around the drum to form a certain length, and each of the wound gaps constitutes a resin multi-walled pipe joined by injection of molten synthetic resin, which is used as a buried pipe. It has high durability and rigidity and minimizes deformation due to external force.
Figure 112005074173876-PAT00005
It is formed in the cross-sectional shape of ', to increase the binding force along the longitudinal direction, and to increase the rigidity against bending and external force than the conventional' I 'cross-section structure, and to prevent shear fracture between the wound profile.

또한, 상기 프로파일의 내부에는 십(十)자 단면의 보강부를 더 형성하여, 전체적인 강성을 더욱 높이는데 또 다른 목적이 있다. In addition, there is another object to further increase the overall rigidity by further forming a cross-sectional reinforcement inside the profile.

본 발명은 내구성이 강화된 합성수지 다중벽관에 관한 것으로, 이는 그 내부에 중공층(12)이 형성된 사각 단면의 외벽(11)을 형성하되, 그 각 모서리에 수평으로 돌출된 결속날개부(13)가 형성되어, 대략 그 단면이 ‘

Figure 112005074173876-PAT00006
’형상을 가진 합성수지 프로파일(10)을 연속으로 압출하고, 이를 드럼상으로 감아 일정 길이를 형성하되, 각 사이는 용융된 합성수지(20)의 주입으로 ‘
Figure 112005074173876-PAT00007
’의 단면 형태로 경화되어 감긴 프로파일(10) 사이를 접합·연결한 합성수지 다중벽관(30)을 구성하여, 이를 매설용 파이프로 쓰임에 따라, 길이 방향의 결속력이 높여 프로파일(10) 간의 전단 파괴를 방지하고, 굽힘 및 외력에 대한 강성을 높여, 이에 대한 변형을 최소화한 것이다.The present invention relates to a durable reinforced plastic multi-wall tube, which forms an outer wall (11) of a rectangular cross section in which a hollow layer (12) is formed therein, wherein the binding wings (13) protrude horizontally at each corner thereof. Is formed, roughly its cross section is'
Figure 112005074173876-PAT00006
'A continuous extrusion of the shape of the synthetic resin profile 10, and wound around the drum to form a certain length, between each injection of molten synthetic resin 20'
Figure 112005074173876-PAT00007
The composite resin multi-wall tube 30 is formed by joining and connecting the profiles 10 cured and wound in the cross-sectional shape of the cross section, and as the pipe is used as a buried pipe, the binding force in the longitudinal direction is increased to shear shear between the profiles 10. To prevent bending, increase rigidity against bending and external force, and minimize deformation thereof.

상기와 같이 본 발명에 따른 합성수지 다중벽관(30)은 일정 단면의 프로파일 (10)과 이를 접합하는 합성수지(20)로 구성되며, 먼저, 프로파일(10)을 도1 및 도2를 참조하여 상세히 설명하면, 이는 대략 ‘

Figure 112005074173876-PAT00008
’형상의 단면으로 연속 압출되어 형성하는 것으로, 자세하게는, 사각 형상의 단면을 가지는 외벽(11)을 형성하되, 그 내부는 비어 중공층(12)을 형성하고, 그 외벽(11)의 네 모서리에서 각각 수평 방향으로 일정 길이 돌출한 결속날개부(13)를 형성한 프로파일(10)을 구성한다.As described above, the synthetic resin multi-walled pipe 30 according to the present invention is composed of a profile 10 having a predetermined cross section and a synthetic resin 20 which bonds it. First, the profile 10 will be described in detail with reference to FIGS. 1 and 2. Which is roughly '
Figure 112005074173876-PAT00008
It is formed by continuous extrusion into the cross-section of the shape, in detail, to form an outer wall 11 having a rectangular cross section, the inside of which forms a hollow hollow layer 12, the four corners of the outer wall 11 In the configuration of the profile (10), each of which forms a binding wing (13) protruding a predetermined length in the horizontal direction.

이러한 프로파일(10) 및 이를 이용한 합성수지 다중벽관(30)의 제조 장치 및 이의 형성 과정을 첨부한 도6 및 도7을 참조하여 설명하면, 이는 대게 상기 프로파일(10)의 단면 형상에 대응하도록, 내부금형(41)과 외부금형(42)을 결합한 금형(40)이 구비되어, 이 금형(40)을 통해 용융된 합성수지를 압출함과 동시에 연속하는 냉각기(50)를 거쳐 프로파일(10)을 구성하며, 각 압출된 프로파일(10)은 각 결속날개부(13)가 마주보도록 드럼(원통형)상에 연속적으로 권취하여 길이 방향으로 일정 길이를 형성하며, 이와 동시에 감긴 프로파일(10) 사이, 즉 이웃하여 마주보는 각 결속날개부(13) 사이에 용융된 합성수지가 주입되어, 감긴 프로파일(10) 사이를 ‘

Figure 112005074173876-PAT00009
’형상의 단면으로 접합·경화하고, 상기 감긴 프로파일(10)과 주입된 합성수지(20)가 경화되어 합성수지 다중벽관(30)을 형성한다.Referring to FIGS. 6 and 7 attached to the profile 10 and the apparatus for manufacturing the synthetic resin multi-walled tube 30 using the same, and a process for forming the same, this generally corresponds to the cross-sectional shape of the profile 10. A mold 40 is provided which combines the mold 41 and the outer mold 42 to extrude the melted synthetic resin through the mold 40 and form a profile 10 through a continuous cooler 50. Each extruded profile 10 is continuously wound on a drum (cylindrical) such that each of the binding wings 13 faces to form a predetermined length in the longitudinal direction, and at the same time between the wound profiles 10, that is, adjacent The molten synthetic resin is injected between each of the binding wing portions 13 facing each other, so that
Figure 112005074173876-PAT00009
Bonded and cured into a cross-section of the shape, and the wound profile 10 and the injected synthetic resin 20 are cured to form a synthetic resin multi-wall tube 30.

이와 같이 구성한 다중벽관(30)은, 프로파일(10)의 중공층(12)과 외벽(11)의 구조로 원주상을 따라 이중 구조가 형성되므로, 원주 방향에 따른 압력과 외력에 대해 높은 강성을 가지게 됨은 물론, 감긴 프로파일(10) 사이의 합성수지(20)는 마주하여 돌출된 각 결속날개부(13)와 긴밀히 결합하고, 기존 ‘I’형태로 접합된 형상이 아닌, 그 중간 부분이 볼록하게 형성된 ‘

Figure 112005074173876-PAT00010
’의 단면 형상으로 접합함에 따라, 원주 방향의 외력 및 압력에 따른 전단 파괴가 방지되며, 이는 또한, 파이프 길이 방향의 굽힘과 외력에 대해 높은 강성을 가지게 되는 특징이 있다.The multi-wall tube 30 constructed as described above has a double structure formed along the circumference in the structure of the hollow layer 12 and the outer wall 11 of the profile 10, and thus has high rigidity against pressure and external force along the circumferential direction. Of course, the synthetic resin 20 between the wound profile 10 is in close contact with each of the binding wing portions 13 protruding from each other, and the intermediate portion is convex, rather than the shape of the conventional 'I' bonded. Formed '
Figure 112005074173876-PAT00010
By joining in the cross-sectional shape of ', shear failure due to external force and pressure in the circumferential direction is prevented, which is also characterized by having a high rigidity for bending and external force in the longitudinal direction of the pipe.

다음으로, 본 고안의 다른 실시예를 도3 및 도4를 참조하여 설명하면, 이는 상기 프로파일(10)의 중공층(12)에 십(十)자의 단면의 보강부(14)가 더 형성되어, 프로파일(11)의 단면이 대략 ‘

Figure 112005074173876-PAT00011
’을 형성하며, 이러한 프로파일(11)을 이용한 다중벽관(20)의 형성 과정은, 상기 실시예와 대동소이한 과정을 통해 다중벽관(20)을 구성하며, 이렇게 보강부(14)가 더 구비된 다중벽관(20)은 중공층(12)만 형성된 것보다 더 강성이 높아지므로 외력에 대한 변형이 작고, 내구성이 좋은 특징이 있다.Next, another embodiment of the present invention will be described with reference to FIGS. 3 and 4, which are further formed with a reinforcement 14 having a cross section of a cross in the hollow layer 12 of the profile 10. , The cross section of the profile 11 is approximately '
Figure 112005074173876-PAT00011
Forming of the multi-wall tube 20 using the profile 11, forming a multi-wall tube 20 through a process very similar to the above embodiment, so that the reinforcing portion 14 is further provided Since the multi-wall tube 20 is more rigid than only the hollow layer 12 is formed, the deformation against external force is small, and the durability is good.

이와 같이 본 발명은,‘

Figure 112005074173876-PAT00012
’형상의 단면으로 압출된 합성수지 프로파일을 드럼상으로 감아 일정 길이를 형성하되, 각 감긴 틈새는 용융된 합성수지의 주입으로 접합한 합성수지 다중벽관을 구성하여, 이를 매설용 파이프로 쓰임에 따라, 이중 구조에 따른 내구성과 강성이 높아 외력에 따른 변형을 최소화하고, 접합된 합성수지의 단면이 대략 ‘
Figure 112005074173876-PAT00013
’의 단면 형태로 형성되어, 길이 방향에 따른 결속력을 높이고, 기존 ‘I’자 단면의 접합 구조보다 굽힘 및 외력에 대한 강성을 높이며, 감긴 프로파일 간의 전단 파괴를 방지하는 효과가 있다.Thus, the present invention,
Figure 112005074173876-PAT00012
'The resin profile extruded into the cross-section of the shape is wound around the drum to form a certain length, and each of the wound gaps constitutes a resin multi-walled pipe joined by injection of molten synthetic resin, which is used as a buried pipe. It has high durability and rigidity and minimizes deformation due to external force.
Figure 112005074173876-PAT00013
'Is formed in the cross-sectional shape, to increase the binding force along the longitudinal direction, and to increase the rigidity against bending and external force than the conventional' I 'cross-section structure, there is an effect of preventing shear failure between the wound profile.

또한, 상기 프로파일의 내부에는 십(十)자 단면의 보강부를 더 형성하여, 전체적인 강성이 더욱 높아 내구성이 좋은 효과가 있다.In addition, the profile is further formed inside the cross section (cross) reinforcement, the overall rigidity is higher and there is a good durability effect.

Claims (2)

용융된 합성수지를 일정 단면의 프로파일(10)로 압출하고, 이를 드럼상에 연속적으로 권취하면서, 각 틈새 사이를 용융된 합성수지(20)를 주입하여 접합·경화하여 제작되는 합성수지 다중벽관에 있어서,In the synthetic resin multi-walled tube produced by extruding the molten synthetic resin into the profile 10 of a predetermined cross section, winding it continuously on a drum, and injecting and curing the molten synthetic resin 20 between the gaps. 상기 프로파일(10)의 단면은, 내부가 빈 중공층(12)을 형성한 사각형의 외벽(11)을 형성하고, 그 외벽(11)의 각 모서리에서 수평으로 돌출한 결속날개부(13)가 형성된 ‘
Figure 112005074173876-PAT00014
’형상의 단면으로 형성하며, 이 프로파일(10)을 그 결속날개부(13)가 이웃되게 연속적으로 권취되어, 각 프로파일(10) 사이의 주입된 합성수지(20)가 ‘
Figure 112005074173876-PAT00015
’형상의 단면으로 접합·경화된 합성수지 다중벽관(30)을 구성하여, 프로파일간의 전단 파괴를 방지하고, 굽힙에 따른 강성을 높임을 특징으로 하는 내구성이 강화된 합성수지 다중벽관.The cross section of the profile 10 has a rectangular outer wall 11 having a hollow hollow layer 12 formed therein, and a binding wing portion 13 protruding horizontally from each corner of the outer wall 11 is formed. Formed '
Figure 112005074173876-PAT00014
'Formed into a cross-section, this profile 10 is continuously wound with its binding blades 13 adjacent, so that the injected synthetic resin 20 between each profile 10
Figure 112005074173876-PAT00015
Durable synthetic multi-walled pipe, characterized in that the composite cross-linked and hardened in the cross-sectional shape of the shape (30) to prevent shear fracture between the profile, and to increase the rigidity according to the bending. 제 1항에 있어서,The method of claim 1, 상기 프로파일(10)은, 그 중공층(12)을 따라 십(十)자 단면의 보강부(14)를 더 형성하여, 다중벽관의 강성을 높임을 특징으로 하는 내구성이 강화된 합성수지 다중벽관.The profile (10) is a reinforced synthetic resin multi-wall tube characterized in that it further forms a reinforcing portion (14) of the cross-section along the hollow layer (12), thereby increasing the rigidity of the multi-wall tube.
KR1020050125414A 2005-12-19 2005-12-19 The plastic multi-wall pipe with high durability KR20060001947A (en)