KR20050071306A - A method of manufacturing an irregular wrinkled textile fabric and a textile fabric manufactured by thereof

Info

Publication number: KR20050071306A
Application number: KR1020040009131A
Authority: KR
Inventors: 정재민
Original assignee: 정재민
Priority date: 2004-02-11
Filing date: 2004-02-11
Publication date: 2005-07-07
Also published as: KR100513964B1

Abstract

본 발명은 주름이 형성된 직물지의 제조방법 및 직물지에 관한 것으로, 특히 트리코트스웨드(Tricot suede) 내피와 폴리우레탄의 외피를 접착하여 제조하는 인조가죽 대용품인 직물지에 불규칙한 주름을 형성하여 천연가죽과 같은 질감과 형상을 갖도록 하는 불규칙한 주름이 형성된 직물지의 제조방법 및 직물지에 관한 것이다. The present invention relates to a method of manufacturing woven paper and wrinkled paper, and in particular to form irregular wrinkles on the fabric paper, which is a substitute for artificial leather manufactured by adhering the outer layer of the tricot suede (Tricot suede) and the polyurethane skin, such as natural leather The present invention relates to a method of manufacturing a woven paper having irregular wrinkles having a texture and shape, and a woven paper.

따라서 본 발명에 의하면, 내피를 형성하는 트리코트스웨드(Tricot suede) 원단에서 기모를 형성하는 단계와, 상기 트리코트스웨드 원단을 염색 또는 나염하는 단계와, 외피를 형성하는 폴리우레탄 합성수지필름을 접착방식에 의해 상기 트리코트스웨드(Tricot suede)에 코팅하는 코팅단계와, 상기 코팅된 직물지에 주름을 형성하는 주름형성 단계를 포함하는 불규칙한 주름이 형성된 직물지의 제조방법에 있어서, 상기 주름형성 단계는 탈수기에 의해 회전시킴에 따라 상기 직물지를 꼬이게 만들어 불규칙한 주름을 형성하는 비틀림 단계와, 상기 직물지를 120℃에서 건조하는 단계와, 상기 직물지를 150℃ 내지 170℃에서 프레스 압착하여 주름을 완성하는 단계를 포함하는 것을 특징으로 한다.Therefore, according to the present invention, the step of forming a brush in the tricot suede (Tricot suede) fabric to form the inner skin, the step of dyeing or printing the tricot suede fabric, and the polyurethane synthetic resin film to form the outer skin In the tricot suede (Tricot suede) by the coating step, and the method of manufacturing irregular wrinkled fabric paper comprising a wrinkle forming step of forming a wrinkle on the coated fabric paper, the wrinkle forming step is a dehydrator A twisting step of twisting the fabric paper to form irregular wrinkles as it is rotated by rotation, drying the fabric paper at 120 ° C., and pressing the fabric paper at 150 ° C. to 170 ° C. to complete wrinkles. It is characterized by.

Description

Method of manufacturing an irregular wrinkled textile fabric and a textile fabric manufactured by

본 발명은 불규칙한 주름이 형성된 직물지의 제조방법 및 직물지에 관한 것으로, 트리코트 원단에 화학약품 처리를 코팅함으로써 가죽피막층을 형성하고, 상기 가죽피막층에 불규칙적인 주름을 형성하여 다양한 형태의 주름을 가지는 가죽대용품으로 사용가능한 주름을 형성한 불규칙한 주름이 형성된 직물지의 제조방법 및 그에 의해 제조된 직물지에 관한 것이다.The present invention relates to a method of manufacturing a fabric paper and irregularly formed wrinkled paper, to form a leather coating layer by coating a chemical treatment on the tricoat fabric, leather having a variety of wrinkles by forming an irregular wrinkle on the leather coating layer The present invention relates to a method for producing a paper cloth having irregular wrinkles formed with wrinkles usable as a substitute, and a fabric paper produced thereby.

일반적으로 주름직물지는 직물지 상에 일방향으로 간격을 일정하게 주름을 연속적으로 형성한 형태로, 그 주름의 간격에 따라 좁은 주름과 넓은 주름의 형태가 있다.In general, wrinkled woven paper is a form in which the wrinkles are continuously formed at regular intervals in one direction on the fabric paper, and there are narrow and wide wrinkles according to the gaps of the wrinkles.

이러한 주름직물지는 단순히 무늬나 색상만을 나염한 직물지에 비해 세련되고 새로운 개성을 표현할 수 있어, 여성들의 주름치마나 주름 스카프 등으로 활용되어 왔다.Such pleated fabric paper can express a sophisticated and new personality compared to woven paper that simply prints patterns or colors, and has been utilized as women's pleated skirts or pleated scarves.

그러나, 종래에 사용되어온 주름직물지는 항상 일정한 패턴으로 형성되기 때문에 소비자 개개인의 다양한 개성을 살려주기 어려웠으며, 이로인해 자기만의 개성이 뚜렷하고 패션을 통해 독특함을 연출하고 싶어하는 현대인들의 욕구를 충족시키지 못하는 문제점이 있다.However, since the wrinkled fabrics used in the past are always formed in a certain pattern, it is difficult to make use of various personalities of individual consumers, and thus it is difficult to satisfy the desires of modern people who want to express their own individuality and create uniqueness through fashion. There is a problem.

또한, 좁은 주름과 넓은 주름의 단순한 간격 조절만이 가능하였기 때문에, 가공과정에서 주름을 형성하기 전에 형성된 무늬나 도안에만 국한되어 이러한 무늬나 도안이 역주름으로 돌출되거나 입체감있게 표현될 수 없었으며, 내구성이 떨어지고, 세탁 후 주름의 모양이 처음과 같지 않아 다름질로 세심하게 손질해 주어야하는 불편함이 있어왔다.In addition, since only a simple gap adjustment between narrow and wide wrinkles was possible, only the pattern or pattern formed before the formation of the wrinkles in the processing process could not be protruded or inverted in three folds. Durability is poor, and after washing, the appearance of the wrinkles are not the same as the first has been inconvenient to care carefully by the ironing.

뿐만 아니라, 주름직물지의 제조과정에서도, 공급되는 원단이 직선으로 공급되지 않으면 룰에 감거나 주름을 형성하는 과정에서 제동현상이 발생하기 때문에, 직물지가 투입되는 입구측에 사람이 지키고 서서 투입되는 직물지를 일일이 확인하면서 공급해야 하므로 일손이 많이 들고 작업속도가 느리게 될뿐만 아니라, 인건비가 많이 들어서 생산원가가 높아지는 등의 결점이 있었다.In addition, even in the manufacturing process of wrinkled fabric paper, if the supplied fabric is not supplied in a straight line, a braking phenomenon occurs in the process of winding the rule or forming the wrinkles, so that the paper is placed and standing by the human guard at the entrance side where the paper is fed. Since it is necessary to supply them while checking them one by one, labor is slow and work speed is slow, and labor costs are high, resulting in high production costs.

특히, 특수직물지인 인조가죽의 경우 동물의 가죽을 사용하지 않고 식물로 만든 섬유에 피막을 입힘으로써 인조가죽을 제조하는데, 이와 같은 인조가죽은 그 표면이 이미 코팅되어 있어 상술한 바와 같은 주름을 형성하는 것이 용이하지 않다.Particularly, in the case of artificial leather, which is a special fabric paper, the artificial leather is manufactured by coating a fiber made of plants without using animal skin. Such artificial leather is already coated to form wrinkles as described above. It is not easy to do.

즉, 인조가죽은 내피를 형성하는 폴라플리스와 외피를 형성하는 인조스웨드로 구성되는데, 폴라플리스는 폴리에스터계열 직물원단이 원조이며, 천연섬유보다 가벼운데다 물에 쉽게 젖지 않고 빨리 마르며 염색이 용이한 점 등이 특징이고, 인조스웨드는 폴리에스테르나 폴리아미드 등 열가소성 합성섬유로써 상기 열가소성 합성섬유를 0.3 데니어 이하의 초극세 섬유로 만들고, 직물, 편물 또는 부직포 등의 웨브(Web)를 형성한 다음 상기 웨브를 천연스웨드와 유사한 구조 및 질감을 갖도록 폴리우레탄 탄성체 용액에 함침하고, 표면 입모 또는 연마가공을 한 후 염색을 하는 방법으로 제작된다(한국특허96-1669).In other words, the artificial leather is composed of polar fleece forming the inner skin and artificial suede forming the outer skin. The polar fleece is made of polyester-based fabric, which is lighter than natural fiber, dries quickly and is easy to dye and easy to dye. The artificial suede is a thermoplastic synthetic fiber such as polyester or polyamide, and the thermoplastic synthetic fiber is made of ultrafine fibers of 0.3 denier or less, and a web such as a woven fabric, a knitted fabric or a nonwoven fabric is formed, and then the web It is prepared by impregnating a polyurethane elastomer solution to have a structure and texture similar to that of natural suede, and dyeing after surface preparation or polishing (Korean Patent 96-1669).

한편, 인조가죽의 외피를 형성하는 인조스웨드로는 트리코스웨드(Tricot Suede)를 사용하는데, 트리코스웨드는 편물의 일반적인 형태로 손으로 쉽게 분해(올빠짐)되지 않는 조직이 견고한 경편물의 일종으로, 위 메리야스처럼 풀어지기 쉬운 결점이 없으며, 섬세하고 치밀한 짜임새로 레이스와 같은 투명무늬까지 넣을 수 있는 변화가 쉬운 뜨기로 형성한 것으로 일반적인 겉옷 및 내의, 양말 등 신축성이 요구되는 의복까지도 이용되고, 이 외에도 자동차 시트 등 자동치 내장재, 벨보아(Velvoa)라는 시중에 많이 알려져 있는 제품인 완구용 천(인형), 수용복으로 많이 사용되는 스판 그리고 벨벳과 난스판 등으로 겨울철은 물론 여름철 의류용, 매쉬(Mesh) 나 망사와 같은 신발용, 소파, 의자, 가방 등에 적용되는 일반산업자원용으로 적용범위가 매우 다양하다.Meanwhile, the artificial suede that forms the outer skin of artificial leather uses Tricot Suede, which is a general type of knitted fabric that is a hard-knitted fabric with a hard-to-dissolve tissue. It has no flaws that are easy to loosen like Maryas, and is formed with a changeable knit that can be inserted into transparent patterns such as lace with a delicate and detailed texture.It is also used for garments that require elasticity such as general outerwear, underwear, and socks. Auto tooth interior materials such as seats, toy cloth (doll), a popular product known as Velvoa, spans frequently used for receiving clothes, and velvet and non-span plates. For general industrial resources applied to shoes such as mesh, sofas, chairs and bags, the scope of application is very diverse.

따라서, 내피와 외피를 상호 접착시켜 제작한 인조가죽은 비록 천연가죽의 우수한 성질을 거의 대부분 재현한다고는 하지만, 외견적으로는 그 재질의 특성상 획일적인 인공미나 촉감을 제공할 수밖에 없어서, 천연가죽에서 느낄 수 있는 자연스러운 거친 감촉이나 형상의 미를 느낄 수 없었다. 이에 따라, 주름이 형성된 인조가죽을 제작하려는 노력이 계속 되어왔으며, 한국공개특허 02-94451에서는 내피에 열가소성 발포수지를 가열 융착하고, 숙성시켜 다시 가열융화하는 방법을 여러번 반복하여 외피와 접촉하는 방법이 제시되었으나 주름이 인조스웨드 외면에 균일하게 형성되었다. Therefore, although artificial leather produced by bonding the inner skin and the outer skin almost reproduces the excellent properties of the natural leather, the appearance of the material has no choice but to provide a uniform artificial or tactile feel. I could not feel the natural rough texture or the beauty of the shape. Accordingly, efforts have been made to fabricate wrinkled artificial leather, and in Korean Patent Laid-Open Publication No. 02-94451, a method of contacting the outer skin by repeatedly heating and melting the thermoplastic foamed resin on the endothelium and maturing again by heat fusion. Although presented, wrinkles were formed uniformly on the outer surface of the artificial suede.

이외에도 직물지에 주름을 형성한 주름직물지는 한국등록특허 382283호에 소개되었는데, 상, 하로 설치된 가열압착로울러 사이로 직물지가 공급되면서 직물지가 상기 가열압착로울러 사이를 진퇴작용을 반복함으로써 주름을 형성하도록 하였고, 한국등록특허 383316호에서 소개된 주름직물지의 제조방법은 직물지를 여러차례 롤링공정을 통과함으로써 넓고, 미세한 파형의 주름을 형성하도록 하였으나, 본 발명과는 다른 형태로 주름이 형성되었다.In addition to the wrinkled fabric paper that was formed wrinkled in the fabric paper was introduced in Korea Patent No. 382283, while the fabric paper is supplied between the heating compression roller installed up and down, the fabric paper to form a wrinkle by repeating the retreat action between the heating compression roller, In the method of manufacturing a wrinkled fabric paper introduced in Korean Patent No. 383316, the fabric paper has been passed through a rolling process several times to form a wide, fine corrugation, but the wrinkles are formed in a different form from the present invention.

따라서 본 발명의 목적은 종래의 문제점을 해결하기 위한 것으로, 내피인 트리코트스웨드 원단에 외피인 폴리우레탄 합성수지필름을 접착방식에 의해 식물성 섬유에 코팅하여 만든 인조가죽에 불규칙한 주름을 형성함으로써, 천연가죽에서 느낄 수 있는 자연스러운 거친 감촉이나 형상의 미를 느낄 수 있는 주름이 형성된 특수직물지 및 그의 제조방법을 제공하는 데 목적이 있다.Therefore, an object of the present invention is to solve the conventional problems, by forming an irregular wrinkle in the artificial leather made by coating the polyurethane fiber resin film on the vegetable fiber by the adhesive method on the inner coat of the tricot suede fabric, natural leather An object of the present invention is to provide a special fabric paper and wrinkles formed therein to feel the natural rough texture or shape that can be felt at.

상기한 바와 같은 목적을 달성하기 위한 제1의 기술적 해결수단은, 내피를 형성하는 트리코트스웨드(Tricot suede) 원단에서 기모를 형성하는 단계와, 상기 트리코트스웨드 원단을 염색 또는 나염하는 단계와, 외피를 형성하는 폴리우레탄 합성수지필름을 접착방식에 의해 상기 트리코트스웨드(Tricot suede)에 코팅하는 코팅단계와, 상기 코팅된 직물지에 주름을 형성하는 주름형성 단계를 포함하는 불규칙한 주름이 형성된 직물지의 제조방법에 있어서, 상기 주름형성 단계는 탈수기에 의해 회전시킴에 따라 상기 직물지를 꼬이게 만들어 불규칙한 주름을 형성하는 비틀림 단계와, 상기 직물지를 120℃에서 건조하는 단계와, 상기 직물지를 150℃ 내지 170℃에서 프레스 압착하여 주름을 완성하는 단계를 포함하는 것을 특징으로 한다.The first technical solution to achieve the object as described above, the step of forming a brushed in tricot suede (Tricot suede) fabric forming the endothelial, dyeing or printing the tricot suede fabric, Preparation of irregular wrinkled fabric paper comprising a coating step of coating the polyurethane synthetic resin film forming the outer skin to the Tricot suede by the adhesive method, and the wrinkle forming step of forming a wrinkle on the coated fabric paper In the method, the wrinkle forming step is a torsion step of forming the irregular wrinkles by twisting the fabric paper by rotating by a dehydrator, drying the fabric paper at 120 ℃, and the fabric paper at 150 ℃ to 170 ℃ It characterized in that it comprises a step of pressing the crimp to complete the wrinkles.

이하 본 발명의 바람직한 실시 예를 첨부한 도면을 통해 상세히 설명하도록 한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

트리코트(Tricot)원단은 경편니트의 한 종류로써 말그대로 평평한 기계에서 짜여진 원단이다. 따라서 트리코트원단을 사용하면 가벼울 뿐만 아니라 통풍도 잘되고, 섬세하고 치밀한 짜임새로 레이스와 같은 투명무늬를 넣을 수도 있다. Tricot fabric is a kind of warp knit, literally woven in a flat machine. Therefore, using tricot fabric is not only light, but also well ventilated, and it is also possible to add a transparent pattern like lace with a delicate and dense texture.

그리고 트리코트(Tricot)는 일반직물이나 스웨터와 같은 환편물과는 달리 한번 짜여진 원단은 손으로 쉽게 분해되지 않기 때문에 자동차 시트 등 자동차 내장재, 벨보아(Velvoa)의 완구 인형용, 수영복으로 많이 사용되는 스판, 그리고 벨벳과 난스판등으로 겨울철 및 여름철 의류용 메쉬(Mesh)나 망사와 같은 신발용, 소파, 의자, 가방 등에 이용된다.And tricot is a span that is often used as a swimsuit for car interiors such as car seats, toys for toys in Belvoa, and swimsuits, unlike circular fabrics such as general fabrics and sweaters. It is also used for velvet and non-span plates, such as mesh and winter shoes such as mesh and mesh shoes, sofas, chairs and bags.

본 발명에서는 상술한 트리코트(Trocot)원단을 사용하였다.In the present invention, the above-described tricot fabric (Trocot) fabric was used.

따라서, 본 발명에서는 (a)상기 트리코트 원단에 천연가죽과 같은 질감을 형성하기 위하여 기모를 형성하였고, (b)상기 기모가 형성된 트리코트 원단을 염색 또는 나염 한 후, (c)폴리우레탄 합성수지필름을 접착방식에 의해 코팅하는 코팅을 하였다.Therefore, in the present invention, (a) brushed to form a texture such as natural leather on the tricot fabric, (b) after dyeing or printing the tricot fabric with the brushed, (c) polyurethane synthetic resin The coating was applied to coat the film by an adhesive method.

그리고 상기 코팅된 직물지에 주름을 형성하기 위해 (d)탈수기에서 상기 직물지를 돌려서 불규칙한 주름을 형성하고, (e)상기 직물지를 120℃에서 건조한 후, 마지막으로 (f)상기 직물지를 150℃ 내지 170℃에서 프레스 압착한다.And (d) spin the fabric paper in a dehydrator to form irregular wrinkles to form wrinkles on the coated fabric paper, (e) dry the fabric paper at 120 ° C., and finally (f) 150 ° C. to 170 ° C. Press compression at ℃.

이 때, 탈수기에서 불규칙한 주름을 형성할 때, 원하는 방향으로 회전을 시킴으로써 방향을 바꾸도록 한다.At this time, when forming irregular wrinkles in the dehydrator, the direction is changed by rotating in the desired direction.

상기와 같은 제조방법에 의해서 가공된 직물지는 그 질감이 부드럽고 표면에 불규칙한 주름이 주름지지 않은 표면과 어우러져 더욱 자연스럽고 천연가죽에 가까운 인조가죽 이미테이션 직물지가 된다.Woven paper processed by the manufacturing method as described above is smooth, the texture of the irregular wrinkles on the surface is combined with the surface is not more natural and natural leather imitation leather imitation paper.

따라서, 종래의 인조가죽이나 비닐로 형성된 직물지의 경우에는 통풍이 안되는 어려움이 있었으나, 본 발명에 의해 불규칙한 주름이 형성된 직물지를 제조하면, 주름의 형성방법을 단순화 하여 쉽고 빠르게 제작할 수 있고, 또한 트리코트스웨드(Tricot suede)를 사용함으로써 통풍효과가 있고, 높은 온도 하에서 주름을 형성하고, 그보다 더 높은 온도에서 프레스함으로써 가열함으로, 종래의 직물지보다 내열성에도 강한 효과가 있고, 천연가죽에서는 불가능한 물세탁도 가능하므로 매우 경제적이다.Therefore, in the case of the conventional artificial leather or fabric paper formed of vinyl, there is a difficulty in not ventilated, but by manufacturing the woven paper with irregular wrinkles according to the present invention, by simplifying the formation method of wrinkles can be easily and quickly produced, and also tricot By using suede (Tricot suede) has a ventilation effect, by forming wrinkles under a high temperature, and heating by pressing at a higher temperature, it has a stronger effect on heat resistance than conventional textile paper, and water washing is impossible, which is impossible in natural leather It is very economical.

이와 같이, 본 발명이 속하는 기술분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 하고, 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As such, those skilled in the art will appreciate that the present invention can be implemented in other specific forms without changing the technical spirit or essential features thereof. Therefore, the above-described embodiments are to be understood as illustrative and not restrictive in all respects, and the scope of the present invention is indicated by the appended claims rather than the foregoing description, and the meaning and scope of the claims and All changes or modifications derived from the equivalent concept should be interpreted as being included in the scope of the present invention.

이상에서 설명한 바와 같이 본 발명은 트리코트원단에 기모를 형성한 후, 염색 또는 나염을 한 후, 폴리우레탄으로 코팅하고, 탈수기를 이용하여 비틀기 단계를 거치면서 불규칙한 주름을 형성하도록 하여, 단순작업을 통해 천연가죽과 비슷한 질감과 형태를 갖도록 불규칙한 주름을 형성할 수 있고, 또한 통풍효과가 뛰어나고, 내열성도 강하고 물세탁이 가능하도록 하는 효과가 있다.As described above, the present invention is to form a brush on the tricot fabric, and then dyed or printed, coated with polyurethane, and to form irregular wrinkles while going through the twisting step using a dehydrator, a simple operation Through this, irregular wrinkles can be formed to have a texture and form similar to that of natural leather, and also have an excellent ventilation effect, heat resistance, and water washing.

도 1은 트리코트(Tricot) 원단을 나타낸 도.1 is a view showing a tricot (Tricot) fabric.

도 2는 본 발명에 의한 제조과정을 나타낸 도.2 is a view showing a manufacturing process according to the present invention.

Claims

Napping in Tricot suede fabric forming the endothelium,

Dyeing or printing the tricot suede fabric,

A coating step of coating the polyurethane synthetic resin film forming the outer shell on the tricot suede by an adhesive method,

In the manufacturing method of the irregular wrinkled fabric paper comprising a wrinkle forming step of forming a wrinkle on the coated fabric paper,

The wrinkle forming step is a torsion step of forming an irregular wrinkle by twisting the fabric paper by rotating by a dehydrator,

Drying the fabric at 120 ° C .;

The method of producing a fabric paper irregular wrinkles, characterized in that it comprises the step of pressing the fabric paper at 150 ℃ to 170 ℃ complete wrinkles.

The method of claim 1,

Fabric paper with irregular wrinkles, characterized in that the fabric paper is processed by the manufacturing method.