KR20050047050A - Wood perm-rod coated mixing nano silver - Google Patents
Wood perm-rod coated mixing nano silver Download PDFInfo
- Publication number
- KR20050047050A KR20050047050A KR1020050032594A KR20050032594A KR20050047050A KR 20050047050 A KR20050047050 A KR 20050047050A KR 1020050032594 A KR1020050032594 A KR 1020050032594A KR 20050032594 A KR20050032594 A KR 20050032594A KR 20050047050 A KR20050047050 A KR 20050047050A
- Authority
- KR
- South Korea
- Prior art keywords
- wood
- rod
- permanent
- resin composition
- antimicrobial
- Prior art date
Abstract
본 발명은 퍼머넌트 로드에 관한 것으로, 특히 열전도율이 우수한 친환경 소재인 목재로 성형되는 몸체 표면에, 나노실버(Ag) 콜로이드를 유효량 첨가한 수지조성물을 함침시켜 줌으로서, 퍼머시 사용되는 약품으로부터 모발의 손상을 방지함은 물론, 몸체의 변색 및 세균의 번식을 억제하여 제품수명을 향상시킬 수 있도록 하는 항균성 목재 퍼머넌트 로드에 관한 것이다. The present invention relates to a permanent rod, and in particular, by impregnating a resin composition containing an effective amount of nano silver (Ag) colloid on the body surface formed of wood, an environmentally friendly material having excellent thermal conductivity, In addition to preventing damage, the present invention relates to an antimicrobial wood permanent rod capable of improving product life by inhibiting discoloration and growth of bacteria.
본 발명의 항균성 목재 퍼머넌트 로드는, 나무에 함침되는 수지로 인해 가열에 따른 갈라짐이나 균열등이 효과적으로 방지할 수 있어 로드의 가공두께를 1.5㎜~3.0㎜ 범위까지 얇고도 가볍게 성형하면서도 우수한 내구성을 유지할 수 있음은 물론, 로드의 경량화를 통해 모발에 가해지는 충격을 최소화하는데에 매우 유익하며, 더욱이 상기 수지조성물에 첨가되는 나노실버(Nano silver)에 의해 항균 및 살균효과가 반영구적으로 유지되는 고부가가치의 퍼머넌트 로드를 제공할 수 있게 되는 것이다.The antimicrobial wood permanent rod of the present invention can effectively prevent cracking or cracking due to the resin impregnated in the wood, thereby maintaining excellent durability while forming a thin and lightly processed thickness of the rod in the range of 1.5 mm to 3.0 mm. Of course, it is very beneficial to minimize the impact on the hair through light weight of the rod, and furthermore, the high value added that the antimicrobial and bactericidal effect is maintained semi-permanently by nano silver added to the resin composition. Permanent load can be provided.
Description
본 발명은 퍼머넌트 로드에 관한 것으로, 더욱 상세하게는 열전도율이 우수한 친환경 소재인 목재로 구성되는 몸체 표면에, 나노실버(Ag) 콜로이드를 유효량 첨가한 수지를 함침시켜 줌으로서, 퍼머시 사용되는 약품으로부터 모발의 손상을 방지함은 물론, 몸체의 변색 및 세균의 번식을 억제하여 제품수명을 향상시킬 수 있도록 하는 항균성 목재 퍼머넌트 로드에 관한 것이다. The present invention relates to a permanent rod, and more particularly, by impregnating a resin surface having an effective amount of nano silver (Ag) colloid on a body surface made of wood, which is an environmentally friendly material having excellent thermal conductivity, The present invention relates to an antimicrobial wood permanent rod that prevents damage to the hair, as well as inhibits discoloration and propagation of bacteria, thereby improving product life.
퍼머넌트 로드는, 퍼머롤시 퍼머약을 발라 원하는 스타일로 모발에 웨이브를 연출하는데 사용하는 것으로, 퍼머는 로드에 감기어지는 모발의 감김상태와 약품의 분포정도 및 가열 온도에 영향을 받게 되는 것이며, 온도에 의한 영향을 가장 많이 받으므로 퍼머롤에 적절한 온도유지를 위해선 퍼머넌트 로드의 열전달 효능 및 이러한 열에 견딜 수 있는 내구성이 무엇보다 중요시 된다.Permanent rods are used to perm the hair in a desired style by applying permanent pills, and the perm is affected by the wound condition of the hair wound on the rod, the degree of distribution of the chemicals, and the heating temperature. Because it is most affected, the heat transfer efficiency of permanent rods and the durability to withstand such heat are of paramount importance to maintain the proper temperature for the permroll.
종래의 퍼머넌트 로드는 적절한 내구성을 가지면서도 제조원가를 낮추기 위해 합성수지 재질이 널리 사용되어 왔다. 그러나 이같이 합성수지로 성형된 헤어로드의 경우 열전도율이 낮아 퍼머롤에 적합한 히팅효과의 구현이 곤란하였으며, 이와함께 인체에 해로운 환경호르몬을 다량 배출하게 됨으로서 모발과 두피에 좋지 않은 영향을 미치고 있는 것이었다.Conventional permanent rod has been widely used synthetic resin material to reduce the manufacturing cost while having a suitable durability. However, in the case of the hair rod molded with synthetic resin, it was difficult to implement a heating effect suitable for permol due to the low thermal conductivity, and at the same time, a large amount of environmental hormone harmful to the human body was discharged, which adversely affected the hair and the scalp.
이러한 종래의 문제점을 해소하고자 열전도율이 우수한 친환경 소재로서 퍼머약에서 발생하는 유해성분을 흡착하고 맑은 산소를 공급함으로 인해 모발의 손상을 방지할 수 있도록 하는 목재를 소재로하여 가공된 우드 퍼머넌트 로드가 국내외에서 널리 사용되기도 하였다. In order to solve these problems, wood permanent rod processed by wood is used as the eco-friendly material with excellent thermal conductivity, which prevents hair damage by adsorbing harmful components generated from permanent medicine and supplying clean oxygen. It was also widely used.
국내특허 제10-468060호는 그 일예로서 나무의 갈라짐 특성을 고려하여 두께를 줄일 수 없는 문제를 해결하기 위한 노력을 소개하고 있는데, 이에 따르면 초벌 가공된 원목을 삶아 건조시킴으로서 재료의 성질을 연화시킨 다음, 헤어로드의 형상을 정밀하게 가공하고, 이를 다시 삶아 염분처리하는 과정을 통해 내구성을 향상시킴으로서 두께가 3㎜~5㎜인 가볍고도 견고한 우드 퍼머넌트 로드를 제공할 수 있다고 소개하고 있다.As an example, Korean Patent No. 10-468060 introduces an effort to solve the problem of not being able to reduce the thickness in consideration of the cracking characteristics of trees, and accordingly, softens the properties of the material by boiling and drying the first processed wood. Next, by improving the durability through the process of precisely processing the shape of the hair rod, re-boiling the salt to improve the durability, it is introduced to provide a light and durable wood permanent rod having a thickness of 3 mm ~ 5 mm.
다시말해, 상기한 우드 퍼머넌트 로드는, 종래의 제품에 비해 두께를 1/2로 줄이기는 하였으나 나무의 특성상 그 내구성의 한계로 인하여 3.0㎜이하의 두께로 제작하는 것이 불가능하다고 소개하고 있는 것이다.In other words, the wood permanent rod described above, although the thickness is reduced to 1/2 compared to the conventional products, due to the characteristics of wood, it is impossible to produce a thickness of 3.0 mm or less due to the durability.
더욱이 이같은 종래의 우드 퍼머넌트 로드는, 반복 사용시 나무에 퍼머액이 스며들어 검게 탈색되는 동시에 약품 냄새가 배어 악취를 유발하는 등 비위생적인 문제점을 가지고 있었다. Moreover, such a conventional wood permanent rod has an unsanitary problem such as perme liquid penetrating the wood upon repeated use and discoloring black, and at the same time, the smell of the chemical soaks and causes odor.
즉 우드 퍼머넌트 로드는, 퍼머롤에 적합한 히팅효과를 유지하고, 환경호르몬의 배출을 방지할 수 있는 등 목재가 가지는 우수한 장점들에도 불구하고, 내구성이 매우 약해 퍼머롤시 노출되는 고열의 누적에 의해 목재에 균열이나 갈라짐이 쉽게 발생되고, 그 사용횟수의 경과에 따라 퍼머약의 화학성분이 목재에 다량 함침되어 목재가 변색되며, 세균이나 박테리아의 서식이 용이해 시각적으로나 위생상으로 품질이 저하되는 중대한 문제점이 지적되고 있는 것이어서, 이로 인해 재사용이 어려워지는 등 제품의 수명이 단축되는 결과가 발생되는 것이었다.In other words, the wood permanent rod is very durable because of its excellent strength, such as maintaining a heating effect suitable for perma- roll and preventing the release of environmental hormones. The cracks and cracks are easily generated in the wood, and the chemical composition of the permanent medicine is impregnated into the wood with the passage of the number of times of use, and the wood is discolored. The problem was pointed out, which resulted in shortening the life of the product, such as making it difficult to reuse.
본 발명은 상기와 같은 문제점들을 감안하여 안출된 것으로서, 열전도율이 우수한 친환경 소재인 목재로 구성되는 몸체 표면에, 나노실버(Ag) 콜로이드를 유효량 첨가한 수지조성물을 함침시켜 줌으로서, 퍼머시 사용되는 약품으로부터 모발의 손상을 방지함은 물론, 몸체의 변색 및 세균의 번식을 억제하여 제품수명을 향상시킬 수 있도록 하는 항균성 목재 퍼머넌트 로드를 제공하는데 그 목적이 있다.The present invention has been made in view of the above problems, by impregnating a resin composition containing an effective amount of nano silver (Ag) colloid on the body surface made of wood, which is an environmentally friendly material with excellent thermal conductivity, It is an object of the present invention to provide an antimicrobial wood permanent rod that prevents hair damage from chemicals, as well as inhibits discoloration and propagation of bacteria to improve product life.
본 발명의 다른 목적은, 3.0㎜이하의 두께를 유지하면서도 우수한 내구성과 항균성을 동시에 제공하는 초경량의 목재 퍼머넌트 로드를 제공하는데 있다.Another object of the present invention is to provide an ultra-light wood permanent rod that simultaneously provides excellent durability and antimicrobial properties while maintaining a thickness of 3.0 mm or less.
본 발명의 또 다른 목적은, 퍼머롤시 헤어로드에 감기는 모발의 미끄러짐을 방지하여 퍼머작업효율을 향상시킬 수 있도록 한 항균성 목재 퍼머넌트 로드를 제공하는데 있다.Still another object of the present invention is to provide an antimicrobial wood permanent rod that can improve the perm working efficiency by preventing the hair from being wound on the hair rod when perma- luring.
상기 목적을 달성하기 위한 본 발명의 항균성 목재 퍼머넌트 로드는, 열전도율이 우수한 목재로 구성되고, 그 내부에 통공(1)이 형성되는 원통형의 몸체(2)와; 상기 몸체(2) 양단에 돌출 형성되는 돌기부(5)를 포함 구성되고; 상기 몸체(2) 표면에는 나노실버(Ag) 콜로이드를 유효량 첨가하여 교반한 수지조성물(11)을 함침(코팅)한 것을 특징으로 한다. Antimicrobial wood permanent rod of the present invention for achieving the above object, the cylindrical body (2) is made of wood with excellent thermal conductivity, the through-hole (1) is formed therein; It comprises a protrusion (5) protruding on both ends of the body (2); The surface of the body 2 is characterized in that the impregnated (coated) the resin composition 11 by adding an effective amount of nano silver (Ag) colloid.
중앙에 통공(1)이 형성된 상기 원통형의 몸체(2)는, 바람직하게 1.5㎜~3.0㎜의 두께로 가공되는 것을 특징으로 한다.The cylindrical body 2 in which the through hole 1 is formed in the center is preferably characterized in that it is processed to a thickness of 1.5 mm to 3.0 mm.
상기 수지조성물(11)은, 락카계, 우레탄계, 알키드계 도료를 포함하여, 천연수지 도료와 합성수지 도료 및 수성 도료 중 어느 하나가 선택적으로 사용되는 것을 특징으로 한다.The resin composition 11 is characterized in that any one of natural resin paints, synthetic resin paints and aqueous paints, including lacquer, urethane, and alkyd paints are selectively used.
상기 수지조성물(11)은, 우드로드 전체 두께에 대하여 균일하게 함침되도록 구성할 수 있음은 물론, 우드로드 몸체(2) 외면 및 통공(1) 내면 중 적어도 어느 한면에 함침하여 0.02㎜이하의 두께로 코팅되는 표피층(12)을 구성하여도 좋다. 이는 모발권취시 미끄러짐을 방지하는데 유용하다.The resin composition 11 may be configured to be impregnated uniformly with respect to the entire thickness of the wood rod, as well as a thickness of 0.02 mm or less by impregnating at least one of the outer surface of the wood rod body 2 and the inner surface of the through hole 1. The skin layer 12 to be coated may be configured. This is useful to prevent slipping when winding the hair.
뿐만 아니라, 상기 수지조성물(11)에 첨가되는 나노실버(Ag) 콜로이드는, 수지 100중량부에 대하여 0.001~30중량부의 비율로 첨가하는 것이 바람직하다.In addition, the nano-silver (Ag) colloid added to the resin composition 11 is preferably added in a ratio of 0.001 to 30 parts by weight with respect to 100 parts by weight of the resin.
이하, 본 발명의 바람직한 실시예를 첨부한 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, with reference to the accompanying drawings, preferred embodiments of the present invention will be described in detail.
도 1은 본 발명에 의한 목재 퍼머넌트 로드를 도시한 사시도, 도 2는 도 1의 횡단면도, 도 3은 도 1의 종단면도이다.1 is a perspective view showing a wood permanent rod according to the present invention, Figure 2 is a cross-sectional view of Figure 1, Figure 3 is a longitudinal cross-sectional view of FIG.
도 1 내지 도 3에 도시한 바와 같이, 본 발명의 목재 퍼머넌트 로드(10)는, 퍼머롤시 퍼머약의 흐름을 원활히 하여 모발이 권취되는 외면에 퍼머약이 고이는 것을 방지하고 퍼머약이 전체적으로 골고루 발라지도록 내부에 소정 직경의 통공(1)이 형성된 원통형의 관체로 이루어진 목재 재질의 몸체(2)와, 고무줄을 끼워 상기 몸체(2) 표면에 권취된 모발을 단단히 고정하도록 상기 몸체(2) 양단에 소정의 이격된 간격을 두고 돌출 형성되는 다수 개의 돌기부(5)를 포함 구성된다.As shown in Figures 1 to 3, the wood permanent rod 10 of the present invention, to facilitate the flow of the permanent medicine during the permroll to prevent the perm drug is accumulated on the outer surface of the hair is wound and the perm medicine is spread evenly throughout A body 2 made of a cylindrical tubular body having a through hole 1 of a predetermined diameter formed therein, and a predetermined length at both ends of the body 2 so as to firmly fix the hair wound on the surface of the body 2 by inserting a rubber band. It is configured to include a plurality of protrusions 5 protruding at spaced intervals.
상기 몸체(2)는 그 길이 및 통공(1)의 직경이 퍼머넌트 로드(10)의 치수에 따라 선택적으로 조절할 수 있으며, 바람직하게는 1.5㎜~3.0㎜의 두께로 가공된다. The length of the body 2 and the diameter of the through-hole 1 can be selectively adjusted according to the dimensions of the permanent rod 10, and preferably processed to a thickness of 1.5mm ~ 3.0mm.
이같은 몸체(2)는 그 표면에 권취된 모발이 몸체(2) 양단에 형성된 돌기부(5) 밖으로 이탈되지 않도록 몸체(2)의 중간부위로부터 양측으로 갈수록 점진적으로 직경을 증가시켜 형성하는 것이 가장 보편적으로 사용되는 것이며, 몸체(2) 표면에는 퍼머약의 흐름을 원활하게 함과 동시에 공기통로 로서의 역할을 수행할 수 있도록 길이방향을 따라 소정의 절개홈(3)이 복수개 형성된다.This body (2) is most commonly formed by gradually increasing the diameter from the middle portion of the body (2) to both sides so that the hair wound on the surface does not escape out of the protrusion (5) formed on both ends of the body (2) It is to be used as, the surface of the body (2) is a plurality of predetermined cutting grooves (3) are formed along the longitudinal direction to facilitate the flow of permanent medicine and at the same time serve as an air passage.
이러한 상기 몸체(2)의 외면 및 통공(1)의 내면에는 나노실버(Ag) 콜로이드를 유효량 첨가하여 교반한 수지조성물(11)을 함침(코팅)하게 된다. The outer surface of the body 2 and the inner surface of the through hole 1 are impregnated (coated) with the resin composition 11 stirred by adding an effective amount of nano silver (Ag) colloid.
상기 수지조성물(11)은, 다공질의 구조로서 취약한 내구성을 가지는 상기 몸체(2)에 흡착되어, 목재의 공극을 메우는 동시에 부착력을 크게 증대시켜 주어, 1.5㎜~3.0㎜의 두께로 비교적 얇게 가공되는 몸체(2)를 구조적으로 안정화 시키는 역활을 하게 된다. The resin composition 11 is adsorbed on the body 2 having a weak durability as a porous structure, and fills the pores of the wood and greatly increases the adhesion, and is processed relatively thin to a thickness of 1.5 mm to 3.0 mm It serves to structurally stabilize the body (2).
이같은 수지조성물(11)은, 목재의 수축팽창 방지, 방부, 방습 내오염 및 내약품성, 내마모성 등을 부여하는 목적으로 사용되는 락카계, 우레탄계, 알키드계 도료를 포함하여, 천연수지 도료와 합성수지 도료 및 수성 도료가 선택적으로 사용된다. Such resin compositions 11 include natural resin paints and synthetic resin paints, including lacquer, urethane, and alkyd paints used for preventing shrinkage expansion of wood, antiseptic, moisture proof, chemical resistance, abrasion resistance, and the like. And aqueous paints are optionally used.
본 발명에 있어서 상기 수지조성물(11)은, 본 발명의 구성재료인 나무에 흡착이 용이하며, 또한 경화후 몸체(2)의 안정적인 내구성을 유지할 수 있는 것이면 족하므로 그 종류를 특별히 한정할 필요는 없다. In the present invention, since the resin composition 11 is easy to be adsorbed to the wood which is the constituent material of the present invention and can maintain stable durability of the body 2 after curing, it is necessary to specifically limit the type thereof. none.
이같은 수지조성물(11)에는, 목재 퍼머넌트 로드(10)의 항균성을 부여하기 위하여 나노실버(Ag) 콜로이드를 유효량 첨가하게 된다. An effective amount of nano silver (Ag) colloid is added to such a resin composition 11 in order to provide antimicrobial activity of the wood permanent rod 10.
나노실버는, 나노미터(Nano meter) 크기의 미세한 은(Ag)입자(1~100㎚)로 매우 우수한 항균효과를 나타낸다. 특히 나노실버 입자는 이온상태의 은보다 강력한 항균, 항곰팡이, 항바이러스 효과를 나타내는데, 이는 미세입자의 은이 바이러스들의 신진대사를 정지시켜 살균시킴과 동시에 금속의 은으로부터 방출되는 은의 전기적 부하가 바이러스의 생식능력을 억제하기 때문인 것으로 알려져 있다. Nanosilver is very fine antimicrobial effect of nanometer size silver (Ag) particles (1 ~ 100nm). In particular, nanosilver particles exhibit stronger antimicrobial, antifungal, and antiviral effects than silver in ionic state. The silver particles of microparticles kill and sterilize the metabolism of viruses, and the electrical load of silver released from silver of metal It is known to suppress fertility.
은(Ag)은 천연의 완벽한 항생물질로서, 일반의 항생물질이 대략 5~6가지의 병원체를 죽이는 반면, 은(銀)은 650여종의 병원체를 일시에 제어하는 등 손상된 세포를 재생하는 기능이 탁월한 것으로 보고되고 있다. Silver (Ag) is a natural, complete antibiotic that kills approximately 5 to 6 pathogens, while silver has the ability to regenerate damaged cells by temporarily controlling over 650 pathogens. It is reported to be excellent.
본 발명에서 수지조성물에 첨가되는 나노실버 콜로이드는, 300㎚ 이하의 은을 여러가지 목적으로 혼합 또는 단독으로 사용할 수 있다. In the present invention, the nanosilver colloid added to the resin composition can be mixed or used singly with silver of 300 nm or less for various purposes.
상기 나노실버 콜로이드의 유효 첨가량은 수지조성물 100중량부에 대하여 0.001~30중량부인 것이 좋다. 상기 사용량이 0.001중량부 미만이면 본 발명이 목적하는 항균기능이 저하되고, 30중량부 이상이면 나노실버를 포함한 전착도막이 내수성 및 내용제성에서 취약하다. The effective amount of the nanosilver colloid is preferably 0.001 to 30 parts by weight based on 100 parts by weight of the resin composition. If the amount is less than 0.001 parts by weight, the antibacterial function of the present invention is lowered, and if more than 30 parts by weight, the electrodeposition coating film including nanosilver is vulnerable in water resistance and solvent resistance.
이같이, 나노실버 콜로이드를 첨가한 수지조성물(11)을 몸체(2) 표면에 코팅시키면, 퍼머롤시 고객의 신체에 유익함을 제공함은 물론 상기 친화성 물질의 유기물 분해, 살균, 항균, 탈취효과를 통해 퍼머넌트 로드(10)의 몸체(2)에 서식하는 세균이나 박테리아를 사멸하고, 담배연기, 각종 기름, 비휘발성 유기화합물 찌꺼기 등의 유해물질 및 악취를 효과적으로 제거함으로써 퍼머넌트 로드(10)의 품질을 현저히 개선할 수 있는 것이다.In this way, coating the resin composition (11) with the addition of the nano-silver colloid on the surface of the body (2), not only provides a benefit to the body of the customer when permalol, but also the decomposition, sterilization, antibacterial, deodorizing effect of the organic material of the affinity material The quality of the permanent rod 10 by killing bacteria or bacteria inhabiting the body 2 of the permanent rod 10 and effectively removing harmful substances and odors such as tobacco smoke, various oils and nonvolatile organic compound residues. This can significantly improve.
나노실버 콜로이드를 유효량 첨가한 상기 수지조성물(11)은, 우드로드 전체 두께에 대하여 함침되도록 구성할 수 있다. 그러나, 더욱 바람직하기로는 우드로드 몸체(2) 외면 및 통공(1) 내면 중 적어도 어느 한면에 함침하여 0.02㎜이하의 두께로 코팅되는 표피층(12)을 이루도록 구성하는 것이 좋다. 이같은 표피층(12)은, 퍼머롤시 헤어로드에 감기는 모발의 미끄러짐을 방지하여 퍼머작업효율을 향상시킬 수 있기 때문이다.The resin composition 11 to which an effective amount of nanosilver colloid is added may be configured to be impregnated with respect to the entire thickness of the wood rod. However, more preferably, it is preferable to impregnate at least one of the outer surface of the wood rod body 2 and the inner surface of the through hole 1 to form a skin layer 12 coated with a thickness of 0.02 mm or less. This is because the epidermal layer 12 can improve the perm working efficiency by preventing the slip of the hair wound on the hair rod during permroll.
이같이 우드로드 몸체(2) 외면에 제공되는 상기 표피층(12)은, 저점성의 우레탄계 수지 또는 실리콘이나 고무액 중 적어도 어느 하나가 바람직하게 사용될 수도 있다.As such, the skin layer 12 provided on the outer surface of the wood rod body 2 may preferably be at least one of a low viscosity urethane resin, silicone, or rubber liquid.
또한, 상기 몸체(2) 양측 둘레에는 몸체(2)를 조여 내구성을 향상하도록 고무 등의 재질로 된 탄성링(6)이 결합될 수 있다. 상기 탄성링(6)은 퍼머롤시 웨이브의 굵기를 결정하는 퍼머넌트 로드의 치수를 쉽게 구분할 수 있도록 예를 들어, 적색-1호, 청색-2호, 흰색-3호 등 그 치수에 맞춰 다양한 색상으로 제작됨이 바람직하다. 즉, 퍼머롤시 그 헤어스타일에 따라 여러 크기의 퍼머넌트 로드(10)를 혼합하여 사용하게 되는데, 이때 미용사가 상기 탄성링(6)의 색상을 통해 퍼머넌트 로드(10)의 크기를 쉽게 구분할 수 있는 것이다.In addition, an elastic ring 6 made of a material such as rubber may be coupled to both sides of the body 2 to improve durability by tightening the body 2. The elastic ring 6 is a variety of colors to match the dimensions of, for example, red-1, blue-2, white-3, so as to easily distinguish the dimensions of the permanent rod to determine the thickness of the wave when permaol It is preferable to be manufactured as. That is, when the permroll is used by mixing the permanent rod 10 of different sizes according to the hairstyle, the hairdresser can easily distinguish the size of the permanent rod 10 through the color of the elastic ring (6) will be.
그러나 본 발명에 있어서, 퍼머넌트 로드의 치수를 쉽게 구분할 수 있는 또 다른 수단으로서, 첨가되는 안료를 통해 수지조성물(11)의 색상을 구별하여 주는 경우, 상기한 탄성링(6)이 필요치 않음은 물론이다.However, in the present invention, as another means of easily distinguishing the dimensions of the permanent rod, when the color of the resin composition 11 is distinguished through the added pigment, the elastic ring 6 is not necessary. to be.
이상에서 설명한 바와 같이 나노미터(Nano meter) 크기의 미세한 나노실버(Ag) 입자들을 함유하는 본 발명의 항균성 목재 퍼머넌트 로드는, 나무에 함침되는 수지조성물로 인해 가열에 따른 갈라짐이나 균열등이 효과적으로 방지할 수 있어 로드의 가공두께를 1.5㎜~3.0㎜ 범위까지 얇게 성형하면서도 우수한 내구성을 보존할 수 있음은 물론, 로드의 경량화를 통해 모발에 가해지는 충격을 최소화하는데에 매우 유익하며, 더욱이 상기 수지조성물에 첨가되는 나노실버(Nano silver) 콜로이드에 의해 항균 및 살균효과가 반영구적으로 유지되는 고부가가치의 퍼머넌트 로드를 제공할 수 있게 되는 것이다. As described above, the antimicrobial wood permanent rod of the present invention containing nanometer-sized fine nano silver (Ag) particles effectively prevents cracking or cracking due to heating due to a resin composition impregnated with wood. It is possible to form the processing thickness of the rod thinly in the range of 1.5 mm to 3.0 mm while preserving excellent durability, and also very beneficial in minimizing the impact on the hair through light weight of the rod, and moreover the resin composition Nano silver colloids added to the nano silver colloid can provide a high value permanent rod that is semi-permanently maintained.
도 1은 본 발명에 의한 목재 퍼머넌트 로드를 도시한 사시도.1 is a perspective view showing a wood permanent rod according to the present invention.
도 2는 본 발명에 의한 목재 퍼머넌트 로드의 횡단면도.Figure 2 is a cross-sectional view of the wood permanent rod according to the present invention.
도 3은 본 발명에 의한 목재 퍼머넌트 로드의 종단면도.Figure 3 is a longitudinal sectional view of the wood permanent rod according to the present invention.
* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings
1 ; 통공 2 ; 몸체 3 ; 절개홈 5 ; 돌기부 10 ; 퍼머넌트 로드 11 ; 수지조성물One ; Through-hole 2; Body 3; Incision groove 5; Protrusion 10; Permanent load 11; Resin composition
Claims (4)