KR20050028453A - Forming method of metal-corrugated pipe - Google Patents
Forming method of metal-corrugated pipe Download PDFInfo
- Publication number
- KR20050028453A KR20050028453A KR1020030064707A KR20030064707A KR20050028453A KR 20050028453 A KR20050028453 A KR 20050028453A KR 1020030064707 A KR1020030064707 A KR 1020030064707A KR 20030064707 A KR20030064707 A KR 20030064707A KR 20050028453 A KR20050028453 A KR 20050028453A
- Authority
- KR
- South Korea
- Prior art keywords
- forming
- hollow tube
- corrugated pipe
- rib
- die
- Prior art date
Abstract
Description
본 발명은 금속주름관 성형방법에 관한 것으로서, 특히 주름성형시 금속제 중공관을 성형리브에 의하여 일정 깊이로 눌러 산과 골을 형성함과 아울러 상기의 산과 골을 좌굴시켜 주름을 형성하는 금속 주름관 성형방법에 관한 것이다.The present invention relates to a method for forming a metal corrugated pipe, and in particular, in forming a corrugated pipe by pressing a metal hollow tube to a predetermined depth by a forming rib to form an acid and a valley, and buckling the acid and a valley to form a corrugation. It is about.
일반적으로 금속주름관은 도 1, 2에 도시된 바와 같이 중공관(1)(2)의 외주면에 골(1a)(2a)과 산(1b)(2b)이 교호로 반복된 주름이 환형으로 형성된 주름관과 상기 주름이 나선형으로 형성된 주름관으로 대별되는데, 상기 주름은 등피치(P)간격을 갖는다. 한편 상기 금속주름관은 신축 및 굽힘이 가능하여 배관장소가 미로처럼 복잡하게 얽혀있는 경우 적절하게 사용될 수 있고, 탄력적으로 변형 가능하므로 유체 또는 기체의 유동에 따른 진동 및 외부로부터 전달되는 진동을 흡수하며, 굽힘과 비틀림 시험을 통해 측정된 최대 굽힘 가능한 횟수와 최대 비틀림 가능한 횟수에 의해 내구성, 즉 품질이 결정된다.Generally, as shown in FIGS. 1 and 2, the metal corrugated pipe has an annular pleat formed in an annular shape on the outer circumferential surface of the hollow tube 1, 2, in which the valleys 1a, 2a and the acid 1b, 2b are alternately repeated. The corrugated pipe and the corrugated pipe are roughly divided into corrugated pipes, and the corrugations have equal pitch (P) spacing. On the other hand, the metal corrugated pipe can be stretched and bent to be appropriately used when the piping place is intricately entangled like a maze, and can be elastically deformed to absorb vibrations from the flow of fluid or gas and vibrations transmitted from the outside. Durability, or quality, is determined by the maximum number of bends and the maximum number of bends measured by bending and torsion tests.
한편, 종래기술에 따른 금속주름관은 대한민국 특허공고번호 제 89-2878호 및 제 89-5250호에 개시된 바와 같이, 오스테나이트계 스테인리스 강으로 제조된 중공관(1)을 일정속도로 전진시키면서 다이스 내주면에 설치된 성형리브가 상기 중공관에 압입되게 한 다음, 상기 다이스를 편심회전시키면 상기 성형리브에 의하여 중공관(1)의 표면에 골(1a)과 산(1b)을 갖는 주름이 형성되는데, 상기 중공관(1)의 수평이송속도는 상기 다이스의 편심회전에 따라 상기 성형리브에 압입되어 형성되는 중공관의 주름이 소정의 등피치간격을 갖도록 설정되어, 상기 중공관(1)이 전진된다. 상기한 금속주름관의 성형장치를 도 3a 내지 도 3d를 참조하여 더욱 상세하게 설명하면 다음과 같다.On the other hand, the metal corrugated pipe according to the prior art is a die inner peripheral surface while advancing the hollow tube (1) made of austenitic stainless steel at a constant speed, as disclosed in Korean Patent Publication Nos. 89-2878 and 89-5250 When the forming ribs installed in the hollow tube are pressed into the hollow tube, and the die is eccentrically rotated, wrinkles having a valley 1a and an acid 1b are formed on the surface of the hollow tube 1 by the forming ribs. The horizontal conveying speed of the tube 1 is set so that the pleats of the hollow tube formed by being pressed into the forming ribs according to the eccentric rotation of the die have a predetermined equal pitch interval, and the hollow tube 1 is advanced. Referring to Figure 3a to 3d the forming apparatus of the metal corrugated pipe in more detail as follows.
통상적인 환형 금속주름관의 성형장치는 프레임(31)과, 상기 프레임(31)의 내부에 설치된 모터(4)와, 상기 프레임(3)의 상측에 착설된 지지대(6)에 회전 가능하게 설치되고 상기 모터(4)와 풀리(7), 벨트(8)로 연결되어 회전력을 전달받는 관형축(10)과, 상기 관형축(10)의 전단에 착설된 성형통(12)과, 상기 성형통(12)의 내부에 형성된 슬라이드홈(12a)을 따라 이동 가능하게 끼워진 회전체(14)와, 상기 성형통(12)에 나사 결합되고 일단이 상기 회전체(14)와 일체로 결합된 조절나사봉(16)과, 상기 조절나사봉(16)의 타단에 체결되어 상기 조절나사봉(16)을 성형통(12)에 고정시키는 너트(18)와, 상기 회전체(14)의 중앙에 위치되고 내경이 중공관(1)보다 2배정도 더 큰 내주면에 1리드의 성형리브(20a)가 형성되어 상기 중공관(1)에 감겨 돌아가면서 주름을 형성하는 다이스(20)와, 상기 중공관(1)을 상기 관형축(10)을 통해 축방향으로 전진시키는 공지의 이송수단을 포함하여 구성된다. 상기 이송수단은 여기에 도시된 바는 없으나, 대한민국 실용신안공고 번호 제 88-2611호에 개시되어 있는 파이프협지 이송장치를 사용하여 흔들림없이 중공관이 일정 속도로 이동될 수 있다.A conventional apparatus for forming an annular metal corrugated pipe is rotatably installed on a frame 31, a motor 4 installed inside the frame 31, and a support 6 mounted on an upper side of the frame 3. A tubular shaft 10 connected to the motor 4, a pulley 7, and a belt 8 to receive rotational force, a forming cylinder 12 mounted at a front end of the tubular shaft 10, and the forming cylinder The rotary body 14 is movably fitted along the slide groove 12a formed in the inside of the 12, and the adjustment is screwed to the molding cylinder 12, one end is integrally coupled to the rotary body 14 A nut 18 and a nut 18 fastened to the other end of the adjusting screw rod 16 to fix the adjusting screw rod 16 to the forming cylinder 12, and positioned at the center of the rotating body 14. And a die 20 formed on the inner circumferential surface of which the inner diameter is twice as large as that of the hollow tube 1, and forming a corrugation while being wound around the hollow tube 1. It comprises a known conveying means for advancing the hollow tube (1) in the axial direction through the tubular shaft (10). The conveying means is not shown here, but the hollow tube may be moved at a constant speed without shaking by using the pipe clamping conveying device disclosed in Korean Utility Model Publication No. 88-2611.
상기한 금속주름관 성형장치에 의하여 중공관에 환형주름이 성형되는 방법을 설명하면 다음과 같다.Referring to the method of forming the annular wrinkles in the hollow tube by the metal wrinkle tube forming apparatus as follows.
먼저, 조절나사봉(16)으로 너트(18)를 풀어낸 후 다이스(20)의 성형리브(20a)가 중공관(1)에 형성될 골(1a)의 성형깊이(D′)까지 압입될 수 있도록 상기 조절나사봉(16)을 사용하여 상기 다이스(20)의 위치를 조절한다.First, after loosening the nut 18 with the adjusting screw rod 16, the forming rib 20a of the die 20 is press-fitted to the forming depth D 'of the bone 1a to be formed in the hollow tube 1. Adjust the position of the dice 20 using the adjusting screw rod 16 to be.
다음, 공지의 이송수단을 사용하여 상기 중공관(1)을 관형 축(10) 및 상기 다이스(20)를 관통하도록 일정 속도로 축방향 이송시킴과 아울러 상기 다이스(20)를 회전시키면, 상기 다이스(20)가 이송중인 상기 중공관(1)에 감겨 돌아가면서 상기 중공관(1)이 상기 성형리브(20a)에 의해 눌려진 부위에 해당되는 중공관(1)의 부위에 성형깊이(D′)를 갖는 골(1a)이 형성되어 상기 중공관(1)에 환형의 주름이 성형된다. Next, the hollow tube 1 is axially conveyed at a constant speed to penetrate the tubular shaft 10 and the die 20 by using a known conveying means, and the die 20 is rotated. (20) is wound around the hollow tube (1) being transported while the hollow tube (1) forming depth (D ') to the portion of the hollow tube (1) corresponding to the portion pressed by the forming rib (20a) A valley 1a having a shape is formed in an annular pleat in the hollow tube 1.
이를 더욱 구체적으로 설명하면, 도 3b, 3d에 도시된 바와 같이 상기 다이스(20)는 내주면에 1리드(ℓ)간격의 나선형의 성형리브(20a)가 돌출형성되어 있고, 상기 다이스(20)는 상기 중공관(1)의 중심을 회전 중심으로 하여 제자리에서 편심 회전되기 때문에 상기 다이스(20)의 회전시 상기 성형리브(20a)는 상기 중공관(1)의 둘레를 따라 상기 중공관(1)을 압입하기 시작하는 리딩 에지(L)부터 트레일링 에지(T)까지 연속적으로 상기 중공관(2)에 점 접촉되면서 상기 중공관(1)을 누르고, 상기 중공관(1)을 누르는 성형리브(20a)의 부위는 회전되면서 축방향으로 후퇴됨과 아울러 상기 중공관(1)은 이송수단(미도시)에 의하여 상기 성형리브(20a)의 축방향 후퇴속도와 동일한 속도로 전진되므로 중공관(1)에 환형의 주름이 형성된다.More specifically, as shown in FIGS. 3B and 3D, the die 20 has a helical forming rib 20a having a one-lead (L) spacing on the inner circumferential surface thereof, and the die 20 is formed in the die 20. Since the center of the hollow tube 1 is rotated eccentrically in place, the forming rib 20a is rotated along the circumference of the hollow tube 1 when the die 20 is rotated. Pressing the hollow tube (1) while continuously contacting the hollow tube (2) from the leading edge (L) to the trailing edge (T) starting to press the forming ribs pressing the hollow tube (1) The portion of 20a is retracted in the axial direction while being rotated, and the hollow tube 1 is advanced at the same speed as the axial retracting speed of the forming rib 20a by a conveying means (not shown). An annular pleat is formed in the.
즉, 상기 다이스(20)의 내경이 대략 중공관(2)의 외경의 2배인 경우에 상기 다이스(20)가 상기 중공관(2)의 둘레를 따라서 2회전하는 동안 상기 성형리브(20a)에 의하여 압입되는 중공관(1)의 지점은 리딩에지(L)로 부터 트레일링 에지(T)까지 환형의 궤적을 형성하기 때문에 상기 중공관(1)은 상기 성형리브(20a)가 압입된 부위가 내측방향으로 신장되어 함몰됨으로써 1피치의 환형주름이 형성되는데, 도 3b에서 성형리브(20a)의 리딩 에지(L)가 중공관에 압입되기 시작하여 다이스가 중공관(1)의 둘레를 1회전하면 상기 리딩 에지(L)와 반대편에 위치한 C점이 중공관(1)에 압입되고, 그 다음 다이스가 1회전하면 트레일링 에지(T)가 중공관(2)에 압입되어 하나의 환형주름의 성형이 완료된다.That is, when the inner diameter of the die 20 is approximately twice the outer diameter of the hollow tube 2, the die 20 is rotated along the circumference of the hollow tube 2 to the forming ribs 20a. Since the point of the hollow tube 1 press-fitted forms an annular trajectory from the leading edge L to the trailing edge T, the hollow tube 1 has a portion into which the forming rib 20a is pressed. By extending inwardly and recessed, an annular wrinkle of 1 pitch is formed. In FIG. 3B, the leading edge L of the forming rib 20a starts to press into the hollow tube, and the die is rotated about one round of the hollow tube 1. When C point opposite to the leading edge (L) is pressed into the hollow tube (1), and then the die is rotated once, the trailing edge (T) is pressed into the hollow tube (2) to form one annular wrinkle Is complete.
상기 금속관(1)에 하나의 환형주름이 형성된 후, 상기 성형리브(20a)의 리딩 에지(L)는 바로 전에 주름을 형성한 트레일링 에지(T)보다 1리드간격(ℓ) 앞에 있기 때문에 상기 중공관(1)에는 새로운 환형주름이 연속적으로 형성되며, 상기 성형리브(20a)의 1리드간격(ℓ)은 주름이 1피치간격(P)과 일치한다.After one annular wrinkle is formed in the metal tube 1, the leading edge L of the forming rib 20a is one lead interval ℓ ahead of the trailing edge T which has been corrugated just before. New annular wrinkles are continuously formed in the hollow tube 1, and the one-lead spacing ℓ of the forming rib 20a coincides with the one-pitch spacing P.
그러나, 상기한 종래기술에 따른 환형 주름관 성형방법은, 상기 다이스(20)가 2회전 할 경우 초래되는 이동거리인 상기 리딩에지(L)와 트레일링 에지(T)의 1리드 간격(ℓ)에 해당되는 거리 즉, 주름의 1피치간격에 해당되는 중공관의 길이가 수평이동 되도록 이송수단에 의하여 상기 중공관(1)이 전진되므로, 중공관에 연속적으로 환형주름이 형성됨과 아울러 골(1a)의 깊이(D′)는 중공관(1)에 압입된 부위의 성형리브(20a)의 깊이와 동일하게 형성된다.However, in the annular corrugated pipe forming method according to the prior art, one lead interval (L) of the leading edge (L) and the trailing edge (T), which is the moving distance caused when the die 20 is rotated two times. Since the hollow tube 1 is advanced by a conveying means so that the length of the hollow tube corresponding to the distance, that is, one pitch interval of the corrugation, is moved horizontally, the annular wrinkle is continuously formed on the hollow tube and the valley 1a is also provided. The depth D 'is formed to be equal to the depth of the forming rib 20a of the portion pressed into the hollow tube 1.
따라서, 중공관(1)에 형성된 골(1a)과 산(1b)은 성형리브(20a) 압입에 의해서만 중공관(1)의 내측방향으로 압착, 신장되어 형성되므로, 상기 주름관의 각 부위의 두께는 도 4에 도시된 바와 같이 중공관의 두께(A1)보다, 산의 두께(B1) 및 골의 두께(C1)가 작고, 더욱 골의 두께(C1)가 산의 두께(B1) 보다 작게 형성된다.Therefore, the valleys 1a and the peaks 1b formed in the hollow tube 1 are formed by pressing and extending inwardly of the hollow tube 1 only by pressing the molded ribs 20a. 4 is smaller than the thickness A 1 of the hollow tube, the thickness of the peak B 1 and the thickness of the valley C 1 , and the thickness of the valley C 1 is the thickness of the peak B. 1 ) smaller than
한편, 여기에 도시된 바는 없으나 상기 다이스에 나선형 성형리브 대신에 환형리브를 형성하고, 상기 다이스를 수직방향으로 부터 일측으로 편향되게 설치하여 다이스를 편심회전함과 아울러, 상기 다이스가 2회전하는 동안 상기 중공관이 주름의 1피치간격만큼 연속적으로 수평이동되게 하여 중공관에 나선형 주름을 형성할 수 있다. 그러나, 상기의 방법으로 형성된 나선형 주름도 성형리브의 압입에 의해서만 주름이 형성되므로 골의 두께가 다른 부위보다 가장 얇게 형성된다.Meanwhile, although not shown here, an annular rib is formed on the die in place of the helical molded rib, and the die is installed so as to be deflected from the vertical direction to one side so that the die is eccentrically rotated and the die is rotated two times. While the hollow tube is continuously horizontally moved by one pitch interval of the corrugation, it is possible to form a spiral corrugation in the hollow tube. However, since the wrinkles are formed only by the indentation of the molding ribs, the spiral wrinkles formed by the above method are thinner than the other sites.
그러나, 금속제 주름관에 굽힘이나 비틀림 발생시, 금속제 주름관은 골을 중심으로 굴곡되기 때문에 골에 피로가 집중되어 골이 가장 취약하게 되는데 반하여, 주름관 성형시 골이 가장 크게 신장되어 골의 두께가 다른 부위보다 가장 얇게 형성되므로, 사용시 금속제 주름관의 내구성이 크게 저감되는 문제점이 있었고, 이를 해결하기 위하여 금속제 주름관 전체의 두께를 크게 형성하는 경우에는 금속제 주름관의 제조 비용이 증대됨과 아울러 금속제 주름관의 무게가 무거워지는 문제점이 있었다.However, when bending or torsion occurs in the corrugated metal corrugated pipe, the corrugated metal pipe is bent around the bone so that the bone is most vulnerable due to fatigue concentration in the bone. Since the thinnest form, there was a problem that the durability of the metal corrugated pipe is greatly reduced when using, and in order to solve this problem, the manufacturing cost of the metal corrugated pipe is increased and the weight of the metal corrugated pipe becomes heavy when forming a large thickness of the metal corrugated pipe. There was this.
본 발명은 상기한 종래기술의 대한 문제점을 해결하기 위하여 안출된 것으로서, 금속제 주름관의 골 부위의 두께가 다른 부위보다 크게 되도록 금속주름관을 성형하여 금속제 주름관의 내구성을 향상시킬 수 있는 금속주름관의 성형방법을 제공하는데 그 목적이 있다. The present invention has been made to solve the above problems of the prior art, by forming a metal corrugated pipe so that the thickness of the bone portion of the metal corrugated pipe is larger than the other parts, the molding method of the metal corrugated pipe can improve the durability of the metal corrugated pipe The purpose is to provide.
상기의 기술적 과제를 실현하기 위한 본 발명에 따른 금속주름관 성형방법은, 다이스에 형성된 성형리브를 금속주름관에 압입한 상태에서 상기 다이스를 편심회전 시키면서 상기 중공관을 일정한 속도로 전진시켜 등피치(P)간격의 주름을 연속적으로 형성하는 금속주름관 성형방법에 있어서, 상기 성형리브를 금속제 중공관에 주름의 설정깊이보다 높은 위치에 압입하여 상기 중공관에 성형리브가 압입된 깊이까지 주름이 형성되는 제 1단계와, 상기 다이스의 편심회전으로 중공관에 1피치(P)간격의 주름이 형성되는 동안 상기 중공관은 이송수단에 의하여 상기 주름의 1피치(P)간격보다 많이 전진되도록 수평이동되어 상기 성형리브에 의하여 형성되고 있는 주름이 상기 성형리브에 걸려 좌굴되어 주름의 골부의 두께가 두꺼워지면서 주름이 등피치(P)간격으로 상기의 설정깊이까지 형성되는 제 2단계로 이루어진 것을 특징으로 한다.Metal forming tube forming method according to the present invention for realizing the above technical problem, while pressing the forming rib formed in the die into the metal tube, eccentric rotation of the die while advancing the hollow tube at a constant speed and pitch (P In the metal corrugated pipe forming method for continuously forming the corrugation of the gap, the first forming the wrinkles are formed by pressing the forming rib into the metal hollow tube at a position higher than the set depth of the corrugation to the depth to which the forming rib is pressed into the hollow tube Step and the hollow tube is horizontally moved to advance more than 1 pitch (P) interval of the corrugated by the transfer means while the corrugation of the pitch is formed in the hollow tube by the eccentric rotation of the die The wrinkles formed by the ribs are buckled by the forming ribs, so that the thickness of the valleys of the wrinkles becomes thick, and the wrinkles are equal pitch (P). The case characterized by consisting of a second phase is formed by setting the depth of the.
또한, 상기 성형리브가 중공관에 압입되는 깊이는 주름의 설정깊이의 97%이하인 것을 특징으로 한다.In addition, the depth that the molding rib is pressed into the hollow tube is characterized in that less than 97% of the set depth of the wrinkles.
또한, 상기 중공관의 수평이동속도는 상기 중공관이 상기 성형리브에 의하여 1피치(P)간격의 주름이 형성되는 동안 상기 1피치(P)간격의 103~106%배에 해당되는 길이가 이송되는 것을 특징으로 한다.In addition, the horizontal moving speed of the hollow tube is a length corresponding to 103 ~ 106% times the interval of the 1 pitch (P) while the hollow tube is formed wrinkles of 1 pitch (P) interval by the forming ribs It is characterized by.
이하, 첨부도면을 참조하여 본 발명의 실시예를 설명하면 다음과 같다. 본 발명에 있어서 종래기술과 동일한 장치의 구성요소를 사용하는 경우에는 종래기술의 도면 및 부호를 원용한다.Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. In the present invention, when using components of the same apparatus as the prior art, the drawings and symbols of the prior art are used.
본 발명에 따른 환형 금속주름관 성형방법은 도 5에 도시된 바와 같이, 중공관(1)에 환형 주름을 형성하는 성형장치(S)와, 상기 중공관(2)을 수평방향으로 전진 이동시키는 이송수단(30)으로 구성된다.As shown in FIG. 5, the method of forming an annular metal corrugated pipe according to the present invention includes a molding apparatus S for forming an annular corrugation in the hollow tube 1, and a forward movement of the hollow tube 2 in a horizontal direction. Means 30.
상기 성형장치(S)는 도 3a 내지 도 3b에 도시된 장치와 동일하게 구성된 것으로서, 회전체(14)에 성형리브(20a)가 형성된 다이스(20)가 설치되어, 다이스(20)가 편심압입 회전되면서 이송수단(30)에 의하여 중공관(12)이 전진되어, 중공관(1)에 환형 주름이 형성된다.The forming apparatus S is configured in the same manner as the apparatus shown in FIGS. 3A to 3B, and a die 20 having a forming rib 20a is installed in the rotating body 14 so that the die 20 is eccentrically press-fitted. As the hollow tube 12 is advanced by the conveying means 30 while being rotated, an annular pleat is formed in the hollow tube 1.
한편, 본 발명은 종래기술과 달리 성형하고자 하는 주름의 골이 깊이(D)보다 높은 위치(1d)에 성형리브(20a)가 중공관(1)에 압입되는데, 상기 성형리브(20a)가 중공관(1)에 압입되는 깊이(d)는 도 3c에 도시된 조절나사봉(16)에 의하여 조절된다.On the other hand, in the present invention, unlike the prior art, the forming rib 20a is press-fitted into the hollow tube 1 at a position 1d higher than the depth D of the wrinkles to be molded, and the forming rib 20a is hollow. The depth d pressed into the tube 1 is adjusted by the adjusting screw rod 16 shown in FIG. 3c.
따라서, 이송수단(30)에 의하여 중공관(1)을 수평방향으로 전진 이동시키면서 회전체(14)를 회전시키면 다이스가 편심회전되므로 중공관(1)에 압입된 성형리브(20a)에 의하여 중공관(1)의 표면에 골과 산을 갖는 환형주름이 형성된다.Therefore, when the rotating body 14 is rotated while the hollow tube 1 is moved forward in the horizontal direction by the transfer means 30, the die is eccentrically rotated, thereby forming the hollow by the molded rib 20a pressed into the hollow tube 1. On the surface of the tube 1, annular wrinkles having bone and acid are formed.
이때, 본 발명에 따른 환형 금속주름관 성형방법은, 다이스의 회전에 따라 성형리브(20a)에 의하여 중공관(1)에 1피치(P)간격을 갖는 하나의 주름이 형성되는 동안에, 상기 중공관(1)은 이송수단(30)에 의하여 1피치(P)간격 보다 큰 간격의 길이가 상기 성형리브(20a)를 향하여 수평방향으로 전진된다.At this time, the annular metal corrugated pipe forming method according to the present invention, while forming one corrugation having a pitch 1 pitch (P) in the hollow tube (1) by the forming rib (20a) in accordance with the rotation of the die, the hollow tube (1) is the length of the interval larger than the interval 1 pitch (P) by the transfer means 30 is advanced in the horizontal direction toward the forming rib (20a).
따라서, 상기 다이스(20)의 내경이 상기 중공관(1)의 외경보다 2배정도 큰 경우, 상기 다이스(20)가 2회전할 때 중공관에는 1리드간격(ℓ)을 갖는 상기 성형리브(20a)에 의하여 소정의 골의 깊이(D)를 갖는 1피치(P)간격의 하나의 환형주름이 형성되는데, 상기 중공관(1)은 이송수단(30)에 의하여 상기 성형리브가 1피치간격의 주름을 형성하는 동안, 1피치간격 보다 큰 길이가 빠른 속도로 상기 성형리브(20a)를 향하여 전진 이동되므로, 성형리브(20a)에 의하여 중공관(1)에 현재 형성되고 있는 주름은 상기 중공관(1)에 압입된 성형리브(20a)에 걸려 상기 골 및 산은 수평방향으로 압착되면서 내, 외측으로 돌출, 좌굴되어 골의 두께(C2) 및 산의 두께(B2)가 중공관 두께(A2)보다 커지게 된다.Therefore, when the inner diameter of the die 20 is about twice as large as the outer diameter of the hollow tube 1, when the die 20 is rotated two times, the forming rib 20a having a one-lead spacing (l) in the hollow tube. One annular wrinkle of one pitch (P) interval having a predetermined depth (D) of the bone is formed, the hollow tube (1) is the wrinkles of the forming ribs by the feed means (30) one pitch interval During the formation, since the length larger than one pitch interval is moved forward toward the forming rib 20a at a high speed, the wrinkles currently formed in the hollow tube 1 by the forming rib 20a is the hollow tube ( 1) The bone and the acid caught by the pressurized rib 20a are pressed in the horizontal direction while protruding and buckling inward and outward so that the thickness of the bone (C 2 ) and the thickness of the acid (B 2 ) are hollow tube thickness (A). Greater than 2 ).
상기에서, 상기 중공관(1)과 다이스(20)의 내면사이에는 상기의 좌굴과정에서 주름관의 산(1b)이 외측으로 돌출될 수 있도록, 주름관의 산의 최상점과 다이스(20)의 내면사이에 소정의 공간부가 형성되도록 다이스(20)가 중공관(1)으로 부터 이격되어 있으며, 산(1b)보다 골(1a)이 많이 좌굴되므로 골(1a)의 두께가 산(1b)의 두께보다 크게 된다.In the above, between the inner surface of the hollow tube (1) and the die 20, the top of the acid of the corrugated tube and the inner surface of the die 20 so that the acid (1b) of the corrugated tube can protrude outward in the buckling process The die 20 is spaced apart from the hollow tube 1 so that a predetermined space is formed therebetween, and since the valley 1a is buckled more than the peak 1b, the thickness of the valley 1a is the thickness of the peak 1b. Becomes larger.
한편, 상기에서 좌굴과정이 수행되지 않은 상태에서 성형리브(20a)에 의해 성형되는 주름의 깊이(d)는 좌굴과정이 완료되어 성형된 주름의 깊이(D)보다 97% 이하인 것이 바람직하며, 상기 이송수단(31)에 의한 중공관의 이송속도는 상기 성형리브(20a)에 의하여 중공관에 1피치간격의 주름이 형성되는 동안 상기 1피치간격의 103~106%배에 해당되는 중공관의 길이가 전진되는 것이 바람직하다.On the other hand, the depth (d) of the wrinkles formed by the forming ribs 20a in the state that the buckling process is not performed in the above state is preferably 97% or less than the depth (D) of the wrinkles formed by the buckling process is completed, The conveying speed of the hollow tube by the conveying means 31 is the length of the hollow tube corresponding to 103 to 106% of the one pitch interval while the corrugation of one pitch interval is formed in the hollow tube by the forming rib 20a. Is preferably advanced.
한편, 상기 다이스를 일측으로 약간 편향되게 설치하고 상기 다이스의 내주면에 환형의 성형리브를 돌출형성하여, 상기 다이스를 편심회전시키면서 상기 중공관을 이송수단에 의하여 일정한 속도로 전진시켜 중공관에 나선형 주름을 연속적으로 성형할 수 있는데, 이경우에 있어서도 상기 성형리브에 의하여 1피치간격의 나선형 주름이 형성되는 동안 상기 중공관을 상기 피치간격보다 많이 이동되게 함으로써 주름이 좌굴되게 하여 골부와 산부의 두께를 중공관의 두께보다 크게 형성할 수 있다.On the other hand, the die is installed slightly deflected to one side and protrudes an annular forming rib on the inner circumferential surface of the die, spirally folds the hollow tube by advancing the hollow tube at a constant speed by a conveying means while rotating the die eccentrically In this case, the hollow tube is moved more than the pitch interval while the helical pleats are formed by the forming ribs so that the pleats are buckled, thereby hollowing the thickness of the valleys and the peaks. It can be formed larger than the thickness of the tube.
따라서, 본 발명에 의하여 제조된 금속주름관은 종래 방법에 의해 제조된 금속주름관에 비하여 신장변형이 감소됨과 아울러 주름의 산부 및 골부의 두께가 모재인 중공관보다 두꺼워졌고, KSD 3625 굽힘시험(180°굽힘)을 실시한 결과, 주름관에 균열이 발생할 때까지의 굽힘횟수가 2배 내지 3배 증가하였다.Therefore, the metal corrugated pipe manufactured according to the present invention had a reduction in elongation deformation and thicker than the hollow tube of the base material of the corrugations and the valleys of the corrugations, compared to the metal corrugated pipe manufactured by the conventional method, and the KSD 3625 bending test (180 °). As a result of the bending, the number of times of bending until the crease in the corrugated pipe increased two to three times.
본 발명에 따른 금속주름관의 성형방법은 중공관에 압입된 성형리브가 형성된 다이스가 편심회전되어 상기 성형리브에 의하여 중공관에 주름이 설정깊이의 97% 미만의 깊이로 압입 형성되고, 상기 중공관은 상기 다이스가 편심회전되어 상기 성형리브에 의하여 1피치간격의 주름이 형성되는 동안 상기 1피치간격보다 큰 중공관의 길이가 전진되어 상기 성형리브를 향하여 수평이송되기 때문에 현재 형성되고 있는 주름은 압입되어 있는 성형리브에 걸려 압착, 좌굴되어 주름이 내, 외측으로 돌출되면서 주름이 설정깊이로 형성되므로, 주름의 골부의 두께가 두꺼워져 내구성이 향상되는 이점이 있다.In the forming method of the metal corrugated pipe according to the present invention, a die having a forming rib press-fitted into the hollow tube is eccentrically rotated to form a crimp in the hollow tube with a depth less than 97% of a set depth by the forming rib, and the hollow tube is While the die is eccentrically rotated to form a one-pitch interval by the forming ribs, the length of the hollow tube larger than the one-pitch interval is advanced and is horizontally transferred toward the forming ribs. Since the wrinkles are squeezed and buckled by the molded ribs, and the wrinkles protrude outward and outward, the wrinkles are formed to a set depth, so that the thickness of the valleys of the wrinkles is increased and durability is improved.
도 1은 중공관의 일부에 통상적인 환형 주름이 형성된 상태가 표현된 정면도1 is a front view showing a state in which a conventional annular pleat formed on a portion of the hollow tube
도 2는 중공관의 일부에 통상적인 나선형 주름이 형성된 상태가 표현된 정면도Figure 2 is a front view showing a state in which a typical spiral pleat formed in a portion of the hollow tube
도 3a 내지 도 3d는 통상적인 환형 주름관의 성형장치가 표현된 도면3A to 3D are views in which a molding apparatus for a conventional annular corrugated pipe is represented.
도 4는 종래기술에 따른 금속제 주름관의 성형방법에 의하여 제조된 주름관의 단면도Figure 4 is a cross-sectional view of the corrugated pipe manufactured by a method for forming a metal corrugated pipe according to the prior art
도 5는 본 발명에 따른 금속주름관의 성형방법을 실시하기 위한 장치가 표현된 개략도5 is a schematic diagram showing an apparatus for carrying out a method for forming a metal wrinkle tube according to the present invention;
도 6은 본 발명에 따른 금속주름관의 성형방법에 의하여 제조된 금속주름관의 단면이 표현된 도면6 is a cross-sectional view of a metal wrinkle tube manufactured by the method for forming a metal wrinkle tube according to the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
1 : 환형 주름이 형성된 중공관 2 : 나선형주름이 형성된 중공관1: hollow tube with annular corrugation 2: hollow tube with spiral corrugation
14 : 회전부재 20 : 다이스14: rotating member 20: dice
20a : 성형리브 30 : 이송수단20a: forming rib 30: conveying means
Claims (5)