KR20050015843A - Powdering test equipment of coated steel sheet and test method to use this - Google Patents
Powdering test equipment of coated steel sheet and test method to use thisInfo
- Publication number
- KR20050015843A KR20050015843A KR1020030054978A KR20030054978A KR20050015843A KR 20050015843 A KR20050015843 A KR 20050015843A KR 1020030054978 A KR1020030054978 A KR 1020030054978A KR 20030054978 A KR20030054978 A KR 20030054978A KR 20050015843 A KR20050015843 A KR 20050015843A
- Authority
- KR
- South Korea
- Prior art keywords
- jig
- steel sheet
- test
- frame
- bending
- Prior art date
Abstract
Description
본 발명은 도금강판의 도금박리성 평가장치 및 이를 이용한 평가방법에 관한 것으로서, 더욱 상세하게는 도금층의 기계적 특성에 따라 굽힘 및 편평시험이 동시에 가능하고, 굽힘각도 및 굽힘모서리 반경, 압축응력의 가압정도를 일정하게 유지하여 도금강판의 도금박리성을 정밀하게 평가함으로써, 평가의 신뢰도를 향상시키고, 안정적인 품질을 확보할 수 있는 도금강판의 도금박리성 평가장치 및 이를 이용한 평가방법에 관한 것이다. The present invention relates to an apparatus for evaluating the plating peelability of a plated steel sheet and an evaluation method using the same. More specifically, bending and flatness tests are possible simultaneously according to the mechanical properties of the plating layer, and bending angle, bending edge radius, and compression stress are applied. The present invention relates to an evaluation method of a plating peelability of a plated steel sheet capable of improving the reliability of evaluation and securing stable quality by precisely evaluating the plating peelability of the plated steel sheet by maintaining a constant degree.
일반적으로, 도금강판은 전기 아연도금강판과 용융 아연도금강판 등 크게 두 가지로 분류되어 있다. In general, galvanized steel sheet is classified into two types, electro galvanized steel sheet and hot dip galvanized steel sheet.
상기와 같은 일반적인 도금강판은 자동차, 가전제품 및 건축자재 등에서 다양하게 사용되고 있으며, 용도를 보다 확대시키기 위해서는 기본적인 내식성 외에 도장성, 가공성 및 용접성 등의 특성이 필요하게 된다. The general plated steel sheet as described above is widely used in automobiles, home appliances, and building materials, and the like, in order to further expand its use, properties such as paintability, processability, and weldability are required in addition to basic corrosion resistance.
또한, 상기와 같은 도금강판의 가공성은 매우 중요한 요소가 되는데, 일반적으로 상기 도금강판을 대량으로 사용하는 자동차 산업의 경우에 있어서, 강판의 성형 즉, 프레스 방법이 크게 발달하여, 성형속도가 매우 빠른 고속 성형 기술이 일반화되는 추세이고, 이로 인하여 도금강판도 일반 가공용 냉연강판과 동등한 수준의 가공성을 갖출 필요가 있게 된다. In addition, the processability of the plated steel sheet as described above is a very important factor, generally in the case of the automotive industry using a large amount of the plated steel sheet, the forming of the steel sheet, that is, the press method is greatly developed, the forming speed is very fast High-speed forming technology is a general trend, and therefore, plated steel sheets also need to have the same level of workability as cold rolled steel sheets for general processing.
또한, 일반강판과는 달리 도금강판을 가공할 경우, 도금층의 마찰계수가 일반강판에 비해 크기때문에, 가공시 마찰응력이 증가되어 국부적인 가공불균일 현상에 의한 도금층의 박리현상이 가공중에 발생하는 문제가 나타난다.In addition, unlike ordinary steel, when the plated steel sheet is processed, the friction coefficient of the plated layer is larger than that of the general steel sheet, so that the frictional stress is increased during machining, so that the peeling phenomenon of the plated layer due to local processing irregularities occurs during processing. Appears.
상기와 같은 도금강판의 가공시 발생되는 문제는 강판보다 가공성이 취약한 도금층이 강판의 가공을 따라가지 못하기 때문에 발생하는 것과, 도금층과 강판간의 밀착성이 불량하기 때문에 발생된다.The problem that occurs during the processing of the plated steel sheet as described above occurs because the plating layer, which is less workable than the steel sheet, cannot follow the processing of the steel sheet, and because the adhesion between the plating layer and the steel sheet is poor.
특히, 합금화된 용융아연도금강판의 경우에는 취약한 감마()층 생성으로 인한 파우더 발생으로 자동차 공정상에서 표면품질에 악영향을 끼치게 되므로 강판제조사는 이의 해결을 위해 공정개선 및 정확한 평가방법 연구 등에 많은 노력을 기울여야 하며, 이러한 사전평가를 통해 실제 사용시 발생되는 불량을 최소화할 수 있어야 한다.In particular, in the case of alloyed hot-dip galvanized steel sheets, fragile gamma ( Due to the powder generation due to the formation of layers, the surface quality is adversely affected in the automotive process. Therefore, the steel plate manufacturer should make a lot of efforts to improve the process and research the exact evaluation method to solve this problem. It should be possible to minimize it.
그러나, 아직도 이러한 도금박리 문제는 강판을 사용하는 자동차 업체의 중요한 품질문제가 되고 있으며, 특히 실제 재현성이 우수하고, 정확하며 신속한 평가방법 및 기준 정립이 요구되고 있는 현실이다.However, the plating peeling problem is still an important quality problem for automobile companies using steel sheets, and in particular, it is a reality that excellent reproducibility, accurate and rapid evaluation methods and standards are required.
현재, 도금강판의 도금박리 평가방법 및 장치에 있어서, 지그 및 프레스 장치를 이용한 60˚V-벤딩 테스트 및 원형 컵 드로잉 테스트, 그리고 이를 개선하여 신속하게 측정이 가능한 스크래치 테스트 및 자동화 장치등이 주를 이루고 있으나, 이러한 방법은 대부분 강판 제조 공정상에 이루어지는 평가방법 등으로 도금박리 정도의 비교 테스트 수행 및 신속한 평가방법의 적용 목적으로 실제 강판 사용이 가능한 재현성 평가에는 다소 문제가 되고 있다. At present, in the method and apparatus for evaluating the plating peeling of plated steel sheet, the 60˚V bending test and the circular cup drawing test using the jig and the press device, and the scratch test and the automation device that can be quickly measured by improving it, etc. However, such a method has been a problem in the evaluation of reproducibility that can be used in the actual steel sheet for the purpose of performing a comparative test of the degree of plating peeling and the application of a rapid evaluation method, such as the evaluation method made on the steel sheet manufacturing process.
또한, 기존에 사용되는 원형 컵 드로잉 평가방법은 수치적으로 판정하기 양호 하지만, 평가시험 시간이 오래 걸리는 불편이 있고 재현성이 떨어지는 단점이 있다. In addition, the conventional method for evaluating the circular cup drawing used in the numerical value is good to determine, but there is a disadvantage that the evaluation test takes a long time and there is a disadvantage inferior reproducibility.
기존에 널리 사용되는 V-벤딩 평가시험의 경우, 지그 형상 및 가공정도, 굽힘하중에 따라 평가결과가 다양하게 나오는 문제점으로 인해, 실제 재현성을 확보하기 위해서는 명확한 방법 및 장치등의 설정과 더불어 판정해독이 양호한 기준설정등이 매우 중요시 된다. In the case of the V-bending evaluation test widely used, the evaluation results vary depending on the shape of the jig, the degree of processing, and the bending load. This good reference setting is very important.
따라서, 이의 정확한 기준 및 재현 가능한 평가방법 설정의 중요성이 요구되고 있다. Therefore, the importance of setting accurate criteria and reproducible evaluation methods thereof is required.
따라서, 본 발명은 상기와 같은 문제점을 해결하기 위해 발명한 것으로서, 도금층의 기계적 특성에 따라 굽힘 및 편평시험이 동시에 가능하고, 굽힘각도 및 굽힘모서리 반경, 압축응력의 가압정도를 일정하게 유지하여 도금강판의 도금박리성을 정밀하게 평가할 수 있는 도금강판의 도금박리성 평가장치 및 이를 이용한 평가방법을 제공하는데 그 목적이 있다.Therefore, the present invention has been invented to solve the above problems, it is possible to simultaneously bend and flat test according to the mechanical properties of the plating layer, plating by maintaining a constant degree of pressing angle and bending corner radius, compression stress It is an object of the present invention to provide an evaluation method using a plating peeling property of a plated steel sheet capable of precisely evaluating the plating peelability of a steel sheet.
이하, 상기와 같은 목적을 달성하기 위한 본 발명의 특징에 대해 설명하면 다음과 같다. Hereinafter, the features of the present invention for achieving the above object are as follows.
본 발명에 따른 도금강판의 도금박리성 평가장치는 일정한 간격을 두고 적층형성되어 있으며, 각 모서리에 수직으로 가이드링크(17)가 지지되어 있는 상부프레임(10) 및 중간프레임(11) 그리고, 하부프레임(12)과;Apparatus for evaluating the plating peelability of the plated steel sheet according to the present invention is formed laminated at regular intervals, the upper frame 10 and the intermediate frame 11 and the lower support guide guide 17 perpendicular to each corner, and A frame 12;
상기 상부프레임(10)의 상측에 설치된 가압기(13)와;A pressurizer 13 installed on an upper side of the upper frame 10;
상기 가압기(13)의 하부에 설치되고, 상기 중간프레임(11)에 걸쳐서 차례로 연결, 고정되어 상하이동이 가능한 유압실린더장치(14)와;A hydraulic cylinder device (14) installed at a lower portion of the pressurizer (13) and connected and fixed in turn over the intermediate frame (11) to be movable;
상기 유압실린더장치(14)의 하단에 연결되어 굽힘 및 편평시험을 실시할 수 있도록 선택적으로 회전가능한 상부지그(15)와;An upper jig 15 rotatably connected to the lower end of the hydraulic cylinder device 14 to perform bending and flatness tests;
상기 하부프레임(12)에 상부지그(15)와 상하로 대응되도록 일치되게 설치되어 있는 V자형 홈(16a)을 갖는 하부지그(16)를 포함하여 구성된 것을 특징으로 한다.The lower frame 12 is characterized in that it comprises a lower jig 16 having a V-shaped groove (16a) is installed to match the upper jig 15 to correspond to up and down.
특히, 상기 상부지그(15)는 굽힘시험을 실시가능토록 하는 수직형 지그(15b)와, 편평시험을 실시가능토록 하는 평판형 지그(15a)로 이루어진 구조인 것을 특징으로 한다.In particular, the upper jig 15 is characterized in that the structure consisting of a vertical jig (15b) for performing a bending test, and a flat jig (15a) for performing a flat test.
상기 수직형 지그(15b)는 그 선단의 굽힘각도가 30 ~ 90°이고, 굽힘모서리의 반경이 0.5mm인 것을 특징으로 한다. The vertical jig 15b is characterized in that the bending angle of the tip is 30 ~ 90 °, the radius of the bending edge is 0.5mm.
또한, 본 발명에 따른 도금강판의 도금박리성 평가장치의 평가방법은 도금강판의 도금박리성을 평가함에 있어서, In addition, the evaluation method of the plating peelability evaluation apparatus of the plated steel sheet according to the present invention in evaluating the plating peelability of the plated steel sheet,
도금층에 압축응력을 변경하면서 가할 수 있도록 가압기(13)를 통해 압축응력을 조절하는 단계와;Adjusting the compressive stress through the pressurizer 13 so as to apply the compressive stress to the plating layer;
수직항력을 부여하는 상부지그(15)의 수직형 지그(15b)의 굽힘각도 및 굽힘모서리의 반경에 따라 상기 시험편에 굽힘시험을 실시하여 도금층을 박리시키는 단계와;Performing a bending test on the test piece according to the bending angle of the vertical jig 15b of the upper jig 15 to impart a vertical drag and a radius of the bending edge to peel off the plating layer;
하부지그(16)의 편탄부위에 시험편을 올려놓고, 평판형 지그(15a)를 이용하여 편평시험을 실시하는 단계를 포함하여 이루어진 것을 특징으로 한다. The test piece is placed on the flat portion of the lower jig 16, and a flat test is performed using the flat jig 15a.
상기 시험편에 가변적으로 가해지는 가압기(13)의 압축응력은 30 ~ 200kgf/cm2 인 것을 특징으로 한다.The compressive stress of the pressurizer 13 variably applied to the test piece is characterized in that 30 ~ 200kgf / cm 2 .
이하, 첨부도면을 참조하여 본 발명의 구성에 대해 상세하게 설명하면 다음과 같다. Hereinafter, the configuration of the present invention with reference to the accompanying drawings in detail.
도 1은 본 발명에 따른 도금강판의 도금박리성 평가장치를 나타내는 정면도이고, 도 2는 본 발명에 따른 도금강판의 도금박리성 평가장치의 상부지그 및 하부지그를 나타내는 사시도이다. 1 is a front view showing a plating peeling evaluation apparatus of a plated steel sheet according to the present invention, Figure 2 is a perspective view showing an upper jig and a lower jig of the plating peeling evaluation apparatus of a plated steel sheet according to the present invention.
본 발명에 따른 도금강판의 도금박리성을 평가하기 위한 평가방법을 구현하기 위한 도금박리성 평가장치는, 도 1에 도시된 바와 같이, 일정한 간격을 두고 적층형성된 상부프레임(10) 및 중간프레임(11) 그리고, 하부프레임(12)이 형성되어 있는 바, 상기 상부프레임(10)의 상측에는 유압에 의한 가압기(13)가 설치되고, 상기 가압기(13)의 하부에는 상하이동가능한 유압실린더장치(14) 및 상부지그(15)가 상기 중간프레임(11)에 걸쳐서 차례로 연결, 고정되어 있다.Plating peelability evaluation apparatus for implementing the evaluation method for evaluating the plating peelability of the plated steel sheet according to the present invention, as shown in Figure 1, the upper frame 10 and the intermediate frame (laminated formed at regular intervals ( 11) And the lower frame 12 is formed, the upper side of the upper frame 10 is provided with a hydraulic pressurizer 13, the lower portion of the pressurizer 13 is a hydraulic cylinder device (movable) ( 14) and the upper jig 15 are connected and fixed in turn over the intermediate frame 11.
이때, 상기 가압기(13)를 통해 압축응력을 조절가능하게 되는 바, 도금층의 도금을 박리시킬시 필요한 수직항력은 30 ~ 200kgf/cm2으로 변화시키면서 굽힘하는 것이 바람직하다. 즉, 상기 수직항력이 너무 작으면 일반적으로 항복강도가 13 ~ 25kgf/mm2인 일반강판의 소성 굽힘변형이 불가능하고, 너무 크면 접착테이프의 손상 등으로 인해 정확한 평가가 불가능하게 된다.At this time, the compressive stress can be adjusted through the pressurizer 13, and the vertical force required to peel off the plating of the plating layer is preferably bent while changing to 30 ~ 200kgf / cm 2 . That is, if the vertical drag is too small, plastic bending deformation of a general steel sheet having a yield strength of 13 to 25 kgf / mm 2 is generally impossible, and if too large, accurate evaluation is impossible due to damage of adhesive tape.
또한, 시험편의 굽힘부위에 적당한 압축응력이 작용해야 도금층의 박리가 일어나고, 그 응력하중에 따라 도금층의 박리정도가 차이가 나므로 더욱 정확한 평가를 실시가능하게 된다. In addition, peeling of the plating layer occurs only when an appropriate compressive stress acts on the bent portion of the test piece, and the degree of peeling of the plating layer varies depending on the stress load, thereby enabling a more accurate evaluation.
한편, 상기 상부지그(15)는 상기 유압실린더장치(14)의 하단에 회전가능하도록 되어 있으며, 이로인해 굽힘 및 편평시험을 선택적으로 결정하게 된다. On the other hand, the upper jig 15 is rotatable at the lower end of the hydraulic cylinder device 14, thereby determining the bending and flatness test selectively.
상기 상부지그(15)의 형상은 각각의 시험을 실시할 수 있도록 평판형 지그(15a)와, 선단이 굽힘각도 30 ~ 90°, 바람직하게는 60°로 이루어져 있으며, 굽힘모서리의 반경이 0.5mm로 이루어진 수직형 지그(15b)로 이루어져 있다.The shape of the upper jig 15 is a flat jig (15a) and the tip is made of a bending angle 30 ~ 90 °, preferably 60 °, so that each test can be carried out, the radius of the bending edge is 0.5mm It consists of a vertical jig 15b.
여기서, 상기 수직형 지그(15b)의 지그 굽힘각도 및 굽힘모서리의 반경은 동일 소재의 평가시 중요한 변수가 된다. Here, the jig bending angle and the radius of the bending edge of the vertical jig 15b are important variables when evaluating the same material.
다시 말해서, 상기 굽힘모서리의 반경이 작을 경우, 굽힘시 강판의 파손을 일으키게 되고, 반대로 굽힘모서리의 반경이 클 경우, 압축응력의 작용이 약해 전기 도금강판의 경우에 도금박리가 잘 일어나지 않아 평가시 변별력이 약해지게 된다. In other words, when the radius of the bending edge is small, it causes breakage of the steel sheet when bending. On the contrary, when the radius of the bending edge is large, the compressive stress is weak and the plating peeling does not occur in the case of electroplating steel sheet. Discrimination will weaken.
또한, 상기 수직형 지그(15b)의 지그 굽힘각도 역시, 상기 굽힘모서리의 반경과 유사한 역할을 하여 각도가 너무 작을 경우, 강판 파손 등이 일어나며, 특히 항복강도가 높은 고장력강판의 경우에 평가가 불가능하게 된다. In addition, the jig bending angle of the vertical jig (15b) also plays a role similar to the radius of the bending edge, if the angle is too small, breakage of the steel sheet, etc. occurs, particularly in the case of high tensile strength steel sheet yield is impossible to evaluate Done.
반대로, 상기 굽힘각도가 클 경우, 실제 환경과의 차이에 의해 재현성이 저하되는 문제점이 있다. On the contrary, when the bending angle is large, there is a problem that the reproducibility is lowered due to a difference from the actual environment.
한편, 각각의 프레임(10,11,12)의 모서리에는 가이드링크(17)가 수직으로 설치되어 있으며, 이는 상기 프레임(10,11,12)을 일치시켜 지지가능하도록 되어 있고, 상기 하부프레임(12)에는 상기 상부지그(15)와 상하로 대응되도록 일치되게 하부지그(16)가 설치되어 있다. On the other hand, the guide link 17 is vertically installed at the corners of each of the frames 10, 11, 12, which is to be supported by matching the frame (10, 11, 12), the lower frame ( 12, the lower jig 16 is installed to correspond to the upper jig 15 so as to correspond up and down.
상기 하부지그(16)는 편평시험시 상기 평판형 지그와(15a) 일치될 수 있도록 형성되어 있으며, 또한 굽힘시험시 상기 수직형 지그(15b)와 일치될 수 있도록 V자형 홈(16a)이 형성되어 있다.The lower jig 16 is formed to match the flat jig 15a during the flat test, and the V-shaped groove 16a is formed to match the vertical jig 15b during the bending test. It is.
상기 V자형 홈(16a)이 이루는 각도는 상기 수직형 지그(15b)의 선단이 이루는 각도와 동일하게 형성되어 있어 시험편이 상기 각도와 일치되게 굽힘 형성된다. The angle formed by the V-shaped groove 16a is formed to be the same as the angle formed by the tip of the vertical jig 15b, so that the test piece is bent to match the angle.
미설명부호 18은 상기 가압기(13)를 통해 압축응력을 조절가능하도록 그 가압기(13)를 작동시키는 스위치장치를 나타내며, 19는 압력조절계를 나타낸다. Reference numeral 18 denotes a switch device for operating the pressurizer 13 to adjust the compressive stress through the pressurizer 13, and 19 denotes a pressure control system.
이하, 본 발명에 따른 도금강판의 도금박리성 평가장치의 작동원리에 대해 설명하기로 한다. Hereinafter, the operation principle of the plating peelability evaluation apparatus of the plated steel sheet according to the present invention will be described.
하부지그(16)의 상부에 형성된 V자형 홈(16a)에 굽힘부위에 접착테이프가 붙은 시험편을 고정시키고, 스위치장치(18)를 통해 가압기(13)를 작동시키면, 유압실린더장치(14)가 아랫방향으로 이동하게 되고, 상기 유압실린더장치(14)에 고정 연결된 상부지그(15)가 상기 시험편을 누르게 된다.When the test piece with the adhesive tape attached to the bent portion is fixed to the V-shaped groove 16a formed in the upper part of the lower jig 16, and the pressurizer 13 is operated through the switch device 18, the hydraulic cylinder device 14 The upper jig 15 fixedly connected to the hydraulic cylinder device 14 is pressed downward to move the test piece.
이때, 상기 상부지그(15)의 수직형 지그(15b)가 상기 V자형 홈(16a)에 일치되도록 하는 굽힘시험을 먼저 실시하게 된다.At this time, a bending test is performed to make the vertical jig 15b of the upper jig 15 coincide with the V-shaped groove 16a.
다음으로 다시, 동일 상하부지그(15,16)를 이용하는 바, 상기 하부지그(16)의 평탄부위에 굽힘한 시험편을 장착하고, 상기 상부지그(15)를 평판형 지그(15a)로 하여 시험을 실시하게 된다. Next, the same upper and lower jigs 15 and 16 were used again, and a test piece bent was mounted on the flat portion of the lower jig 16, and the test was performed using the upper jig 15 as a flat jig 15a. Will be implemented.
이후, 시험편은 굴곡변형되고, 다시 편평해지게 되는데, 이때 그 굴곡된 시험편의 안쪽면은 압축응력을 받은 상태가 되는데, 이때 상기 시험편의 상면에 접착테이프를 부착하여 변형된 상태에서의 박리된 도금층이 상기 접착테이프에 묻어 나오도록 한다. Thereafter, the test piece is deformed and flattened again, wherein the inner surface of the bent test piece is in a state of being subjected to compressive stress, wherein the peeled plating layer is deformed by attaching an adhesive tape to the upper surface of the test piece. It is to be buried in the adhesive tape.
여기서, 접착테이프에 묻어 나오는 도금박리층은 그 농담과 더불어 박리폭의 정도에 따라 도금강판의 도금박리성을 평가하게 된다. Here, the plating peeling layer buried in the adhesive tape evaluates the plating peelability of the plated steel sheet according to the shade and the degree of peeling width.
여기서, 상기 도금박리성을 각각 서로 다른 압축응력에 따라 순차적으로 변화시키면서 평가하는 것은 도금박리층이 변형된 단면을 관찰하고, 도금박리층이 변형되는 과정을 평가하여 도금층의 박리가 어떠한 원인에 의하여 발생하는가를 명확하게 판단하기 위함이다. Here, evaluating the plating peelability in order to sequentially change according to different compressive stress, respectively, by observing the cross-section of the plating peeling layer deformed, evaluating the process of deformation of the plating peeling layer due to any cause of peeling of the plating layer This is to clearly determine if it is occurring.
한편, 아래 표 1은 도금박리 판정기준을 나타내는 것으로서, 시험편에 붙여놓은 접착테이프에 박리된 도금층이 묻어나오는 정도를 설정한 것이다. On the other hand, Table 1 below shows the plating peeling determination criteria, and sets the degree to which the peeled plating layer is buried on the adhesive tape pasted on the test piece.
이는 상기 접착테이프를 백지에 부착한 후, 상기 표 1과 비교하여 부착폭 및 농담을 판정하기 위함이다. This is to determine the adhesion width and the light and shade after comparing the adhesive tape on a white paper, compared with Table 1 above.
단, 시험편의 크기는 40mm ×70mm로 한다. However, the test piece shall be 40mm x 70mm in size.
따라서, 본 발명에 따른 도금강판의 도금박리성을 평가장치를 통해 정밀하게 수치화하는 동시에 이러한 데이터를 객관화함으로써, 향후 도금강판의 개발과 관련한 평가자료로 유용하게 활용할 수 있게 되는 것이다. Therefore, by precisely quantifying the plating peelability of the plated steel sheet according to the present invention through the evaluation device, and by objectiveizing such data, it can be usefully used as evaluation data related to the development of plated steel sheet in the future.
상술한 바와 같이, 본 발명에 따른 도금강판의 도금박리성 평가장치 및 이를 이용한 평가방법에 의하면, 객관적이고 수치화된 평가방법 및 장치를 제공함으로써, 도금강판을 사용하는데 있어 도금박리에 대한 사전 평가를 실시하여 양산 적용이 가능하므로 내구성에 대한 신뢰도를 향상시킬 수 있는 효과가 있다. As described above, according to the plating peeling evaluation device and the evaluation method using the same according to the present invention, by providing an objective and numerical evaluation method and apparatus, the pre-evaluation for the plating peeling in using the coated steel sheet Since it can be applied to mass production, there is an effect that can improve the reliability for durability.
특히, 도금박리성이 우수한 전기도금강판의 경우에 명확한 평가방법이 없었으나, 상기 도금박리성 평가방법 및 장치를 이용하여 연료탱크용 아연-니켈계 도금강판에 대한 정량화된 평가가 가능한 장점이 있다.In particular, there was no clear evaluation method in the case of electroplating steel sheet having excellent plating peelability, but there is an advantage that the quantitative evaluation of zinc-nickel-based plated steel sheet for fuel tank can be performed by using the plating peeling evaluation method and apparatus. .
도 1은 본 발명에 따른 도금강판의 도금박리성 평가장치를 나타내는 정면도,1 is a front view showing an apparatus for evaluating plating peelability of a plated steel sheet according to the present invention;
도 2는 본 발명에 따른 도금강판의 도금박리성 평가장치의 상부지그 및 하부지그를 나타내는 사시도이다. Figure 2 is a perspective view showing the upper jig and the lower jig of the plating peeling evaluation apparatus of the plated steel sheet according to the present invention.
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>
10 : 상부프레임 11 : 중간프레임10: upper frame 11: middle frame
12 : 하부프레임 13 : 가압기12: lower frame 13: pressurizer
14 : 유압실린더장치 15 : 상부지그14: hydraulic cylinder device 15: upper jig
15a : 평판형 지그 15b : 수직형 지그15a: flat jig 15b: vertical jig
16 : 하부지그 16a : V자형 홈16: lower jig 16a: V-shaped groove
17 : 가이드링크 18 : 스위치장치17: guide link 18: switch device
19 : 압력조절계19: pressure regulator
Claims (5)