KR200416470Y1 - A Upper Plate for Sink - Google Patents

A Upper Plate for Sink Download PDF

Info

Publication number
KR200416470Y1
KR200416470Y1 KR2020060005856U KR20060005856U KR200416470Y1 KR 200416470 Y1 KR200416470 Y1 KR 200416470Y1 KR 2020060005856 U KR2020060005856 U KR 2020060005856U KR 20060005856 U KR20060005856 U KR 20060005856U KR 200416470 Y1 KR200416470 Y1 KR 200416470Y1
Authority
KR
South Korea
Prior art keywords
sink
top plate
sink top
oxide
coating film
Prior art date
Application number
KR2020060005856U
Other languages
Korean (ko)
Inventor
이정훈
Original Assignee
주식회사 백조씽크
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 백조씽크 filed Critical 주식회사 백조씽크
Priority to KR2020060005856U priority Critical patent/KR200416470Y1/en
Application granted granted Critical
Publication of KR200416470Y1 publication Critical patent/KR200416470Y1/en

Abstract

본 고안은 싱크대 상판에 관한 것으로서, 더욱 상세하게는 싱크대 상부에 결합되어 사용되며, 그 표면에 고경도를 가지며, 오염 물질 제거가 용이한 고경도 코팅막이 형성되는 싱크대 상판에 관한 것이다. The present invention relates to a sink top plate, and more particularly, is used in conjunction with the top of the sink, and has a high hardness on the surface, and relates to a sink top plate is formed with a high hardness coating film is easy to remove contaminants.

본 고안은, 싱크대 본체 상부에 결합되어 싱크대의 상면을 이루는 싱크대 상판에 있어서, 상기 싱크대 상판의 표면에는, 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트(alkali silicate)로 이루어지는 경화제와 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate)로 이루어지는 기제를 교반하여 코팅한 고경도 코팅막이 형성되는 것을 특징으로 하는 싱크대 상판을 제공한다.The present invention is a sink top plate coupled to the top of the sink body to form a top surface of the sink, the surface of the sink top plate, the curing agent and metal oxide (alkali silicate) consisting of alkali metal oxide (alkali metal oxide) and alkali silicate (alkali silicate) It provides a sink top plate characterized in that a high-hardness coating film is formed by stirring the base consisting of an oxide) and a metal phosphate (metal phosphate).

싱크대, 싱크대 상판, 코팅, 고경도 Countertops, Countertops, Coatings, Hardness

Description

싱크대 상판{A Upper Plate for Sink}A Upper Plate for Sink

도 1은 일반적인 싱크대의 구조를 도시하는 정면도이다. 1 is a front view showing the structure of a general sink.

도 2는 싱크대 상판의 구조를 도시하는 평면도이다. 2 is a plan view showing the structure of the sink top plate.

도 3은 종래의 싱크대 상판 표면에 형성되는 스크래치 및 오염물질의 상태를 도시하는 부분 단면도이다. 3 is a partial cross-sectional view showing a state of scratches and contaminants formed on the surface of a conventional sink top plate.

도 4는 본 고안의 일 실시예에 따른 코팅막의 구조를 도시하는 단면도이다. 4 is a cross-sectional view showing the structure of a coating film according to an embodiment of the present invention.

도 5, 6은 본 고안의 일 실시예에 따른 코팅막 표면에 오염물질이 묻은 경우의 상태를 도시하는 단면도이다. 5 and 6 are cross-sectional views showing a state in which contaminants are deposited on the surface of the coating film according to an embodiment of the present invention.

본 고안은 싱크대 상판에 관한 것으로서, 더욱 상세하게는 싱크대 상부에 결합되어 사용되며, 그 표면에 고경도를 가지며, 오염 물질 제거가 용이한 고경도 코팅막이 형성되는 싱크대 상판에 관한 것이다. The present invention relates to a sink top plate, and more particularly, is used in conjunction with the top of the sink, and has a high hardness on the surface, and relates to a sink top plate is formed with a high hardness coating film is easy to remove contaminants.

일반적으로 식당이나 가정의 주방에서는 설거지나 채소를 씻기 위하여 싱크 대가 구비되는데, 이러한 싱크대는 주방의 형태 및 크기에 따라 다양하게 제작되어 설치된다. In general, the kitchen or the kitchen of the kitchen is provided with a sink for washing dishes or vegetables, such a sink is manufactured and installed in various ways depending on the shape and size of the kitchen.

통상적인 싱크대(1)의 구조는 도 1에 도시된 바와 같이, 주방기구, 양념 등을 보관할 수 있는 본체(10)와, 상기 본체(10)의 상부에 장착되어 조리대의 역할을 하는 상판(20)과, 이 상판(20)에 형성되어 일정한 내부 공간을 갖추어 식기 등을 세척할 수 있도록 이루어진 개수대(30)로 이루어진다. As shown in FIG. 1, the conventional sink 1 has a main body 10 capable of storing kitchen utensils, condiments, and the like, and an upper plate 20 mounted on an upper part of the main body 10 to serve as a kitchen counter. And a sink 30 formed on the top plate 20 to have a predetermined internal space to wash dishes.

이때 상기 싱크대 상판(20)은 도 2에 도시된 바와 같이, 일정한 면적을 가지는 조리대(22); 일정량의 물을 일시적으로 받아서 식기 세척 등을 할 수 있는 개수통을 설치하는 개수통 설치공(24); 가열 기구가 장착될 수 있는 가열 기구 장착공(26); 등으로 구성된다. At this time, the sink top plate 20, as shown in Figure 2, the countertop 22 having a predetermined area; A water tank installation hole 24 for installing a water tank capable of temporarily receiving a certain amount of water and washing dishes; A heating mechanism mounting hole 26 into which the heating mechanism can be mounted; And the like.

이러한 싱크대 상판(20)에서는 금속 또는 도자기 소재로 이루어진 식기, 조리 도구 등 높은 경도를 가지는 도구를 사용하는 경우가 많다. 그런데 종래의 싱크대 상판은 그 표면 경도가 약해서, 계속적인 사용과정에서 싱크대 상판(20)의 표면이 긁혀서 스크래치(21)가 많이 발생되는 문제점이 있다. 이 스크레치 부분(21)은 도 3에 도시된 바와 같이, 싱크대 상판(20)의 표면이 손상되어 미세한 홈이 형성되는 것이므로, 전술한 오염물질(23)이 더욱 많이 잔존하게 되고, 일정한 깊이의 홈에 오염물질이 잔존하므로 청소과정에서 제거가 더욱 어려워지는 문제점이 있다. In such a sink top plate 20, tools having high hardness, such as tableware and cooking tools made of metal or porcelain materials, are often used. However, the conventional sink top plate has a weak surface hardness, so that the surface of the sink top plate 20 is scratched in a continuous use process, causing a lot of scratches 21. As shown in FIG. 3, the scratch portion 21 is damaged because the surface of the sink top plate 20 is damaged to form fine grooves, and thus, the above-described contaminants 23 remain more, and grooves having a constant depth. There is a problem in that it is more difficult to remove during the cleaning process because contaminants remain.

또한 상기 싱크대 상판(20)은 조리 과정 등에서 기름 등의 오염물질에 반복적으로 노출되어 쉽게 오염된다. 따라서 여러번 반복하여 싱크대 상판을 사용하는 경우에는 그 표면에 다량의 오염물질이 묻어서 오염되며, 청소 과정에서 용이하게 제거되지 아니한다. 이러한 오염물질은 미관상 좋지 않은 것 뿐만아니라, 위생상으로도 많은 문제점을 발생시킨다. In addition, the sink top plate 20 is easily contaminated by being repeatedly exposed to contaminants such as oil during cooking. Therefore, when the sink top plate is used repeatedly, a large amount of contaminants are contaminated on the surface and contaminated, and are not easily removed during the cleaning process. These pollutants not only look aesthetically bad, but also cause many problems in hygiene.

본 고안의 목적은 그 표면에 오염물질의 부착을 방지하고 경도가 우수한 고경도 코팅막이 형성된 싱크대 상판을 제공함에 있다. An object of the present invention is to prevent the adhesion of contaminants on the surface and to provide a sink top plate formed with a high hardness coating film excellent in hardness.

전술한 목적을 달성하기 위하여 본 고안은, 싱크대 본체 상부에 결합되어 싱크대의 상면을 이루는 싱크대 상판에 있어서, 상기 싱크대 상판의 표면에는, 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트(alkali silicate)로 이루어지는 경화제와 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate)로 이루어지는 기제를 교반하여 코팅한 고경도 코팅막이 형성되는 것을 특징으로 하는 싱크대 상판을 제공한다.In order to achieve the above object, the present invention, in the sink top plate coupled to the top of the sink body to form the top surface of the sink, the surface of the sink top plate, the alkali metal oxide (alkali metal oxide) and alkali silicate (alkali silicate) It provides a sink top plate characterized in that a high hardness coating film is formed by stirring a curing agent and a base made of a metal oxide (metal oxide) and metal phosphate (metal phosphate).

이하에서는 첨부된 도면을 참조하여 본 고안의 구체적인 구성 및 작용을 상세하게 설명한다. Hereinafter, with reference to the accompanying drawings will be described in detail the specific configuration and operation of the present invention.

먼저 본 고안에 따른 싱크대 상판도 종래의 그것과 마찬가지로 조리판, 개수통 설치홀, 가열기구 장착 홀 등을 구비한다. 이때 본 고안에 따른 싱크대 상판에서는 개수통이 일체로 형성될 수도 있다. 즉, 개수통을 별도로 제작하여 싱크대 상 판의 개수통 설치홀에 설치하는 것이 아니라, 하나의 판재를 가공하여 싱크대 상판과 개수통을 일체로 형성하는 것이다. 이렇게 싱크대 상판과 개수통을 일체로 형성하는 경우에는 싱크대 상판과 개수통 사이에 틈이 발생하지 않아서 누수현상이나 오염물질 삽입 등의 문제가 발생하지 않는 장점이 있다. First, the sink top plate according to the present invention is provided with a cooking plate, a water tank installation hole, a heating mechanism mounting hole and the like as the conventional one. In this case, the sink top plate according to the present invention may be formed integrally. That is, instead of manufacturing the water tank separately and installing in the water tank installation hole of the sink top plate, by processing a single plate material to form the sink top plate and the water tank integrally. In this case, when the sink top plate and the water tank are integrally formed, there is no gap between the top plate and the water tank, so that there is no problem of leakage or insertion of contaminants.

본 고안에 따른 싱크대 상판에서는, 그 표면에 고경도 코팅막이 형성되는 것을 특징으로 한다. 특히, 싱크대 상판에서 상측을 향하는 면에는 반드시 상기 고경도 코팅막이 형성되어야 한다. 따라서 상기 싱크대용 상판이 싱크대에 설치된 상태에서 외부에 노출되지 아니하는 하면에는 상기 고경도 코팅막이 형성되지 않아도 무방하다. In the sink top plate according to the present invention, it is characterized in that the high hardness coating film is formed on the surface. In particular, the high hardness coating film must be formed on the upper surface of the sink top plate. Therefore, when the sink top plate is not exposed to the outside in a state in which the sink top plate is installed, the high hardness coating film may not be formed.

그리고 본 고안에 따른 싱크대 상판은 스테인레스 스틸(stainless steel)로 이루어지는 것이, 가벼우면서도 강도가 우수하며, 가공성이 뛰어나서 바람직하다. And the sink top plate according to the present invention is preferably made of stainless steel (stainless steel), light and excellent in strength, excellent in workability.

이하에서는 상기 고경도 코팅막의 구조 및 그 제조방법을 상세하게 설명한다. Hereinafter, the structure of the high hardness coating film and its manufacturing method will be described in detail.

먼저 본 고안에 따른 고경도 코팅막(50)의 구조는 도 4에 도시된 바와 같이, 싱크대 상판(20) 표면에 이중막으로 형성된다. 즉, 싱크대 상판(20) 표면과 직접 접촉되는 부분인 인산피막(52)과 상기 인산피막 상부에 형성되는 고경도막(54)으로 이루어지는 이중막이 형성되는 것이다. 여기에서 인산피막(52)은, 고경도막(54)과 싱크대 상판(20)을 강력하게 접착시키는 역할을 한다. 즉, 본 고안에 따른 싱크대 상판을 제조함에 있어서, 상기 고경도막의 코팅작업을 진행하기 전에 전처리 공정 으로서, 별도의 하도 공정 및 센딩 공정을 수행하지 않아도 도료 자체의 구성성분의 반응에 의하여 인산 피막이 생성되므로 단 한번의 코팅으로 싱크대 상판과 강력한 밀착도를 가진 고경도막을 형성시킬 수 있는 장점이 있는 것이다. First, the structure of the high hardness coating film 50 according to the present invention is formed as a double film on the top surface of the sink 20 as shown in FIG. That is, a double film is formed of a phosphate coating 52 which is a part in direct contact with the surface of the sink top plate 20 and a high hardness film 54 formed on the phosphate coating. Here, the phosphate film 52 serves to strongly adhere the high hardness film 54 and the sink top plate 20. That is, in manufacturing the sink top plate according to the present invention, as a pretreatment process before the coating operation of the high hardness film, the phosphate film is generated by the reaction of the constituents of the paint itself without performing a separate undercoating process and a sending process Therefore, there is an advantage in that a single coating can form a high hardness film having a strong adhesion with the sink top plate.

그리고 상기 고경도막은 순수한 무기질 재료로 형성되는 코팅막으로서 그 경도가 우수하고, 그 표면에 하이드로필릭(hydrophillic)한 특성을 가지는 분자가 배치되어 기름 같은 유성 오염물질에 의한 오염이 현저하게 감소하며 실제로 오염이 발생하더라도 물에 의하여 용이하게 제거가 가능한 특성을 가진다. In addition, the high hardness film is a coating film formed of a pure inorganic material, its hardness is excellent, and molecules having hydrophilic properties are disposed on the surface thereof, so that contamination by oily contaminants such as oil is greatly reduced and is actually contaminated. Even if this occurs, it is easily removable by water.

이하에서는 이러한 고경도 코팅막을 형성하는 과정을 상세하게 설명한다. Hereinafter, a process of forming such a high hardness coating film will be described in detail.

먼저 코팅막을 형성하기 위한 순수 무기질 도료를 제조하여야 한다. 본 고안에서 사용하는 도료는 경화제와 기제(base)로 이루어진다. 이때 상기 경화제와 기제를 중량 비율로 약 1:1이 되도록 혼합하는 것이 바람직하다. 그리고 상기 경화제와 기제를 혼합할 때에는 경화제와 기제를 물에 혼합한 후, 10 ~ 30 RPM 또는 40 ~ 100 RPM 또는 300 ~ 800 RPM의 속도로 교반한다.First, a pure inorganic paint should be prepared to form a coating film. The paint used in the present invention consists of a hardener and a base. At this time, it is preferable to mix the curing agent and the base to be about 1: 1 by weight ratio. When the curing agent and the base are mixed, the curing agent and the base are mixed with water, followed by stirring at a speed of 10 to 30 RPM or 40 to 100 RPM or 300 to 800 RPM.

이때 경화제는, 코팅막의 경화를 촉진하는 역할을 하며, 코팅막의 주요 구성 물질이 된다. 즉, 경화제는 본 고안에서 사용하는 순수 무기질 도료를 사용하여 코팅하는 경우 코팅막을 형성하는 물질인 알칼리 실리케이트(소성식 : M20·nSiO2·mH2O, M은 알칼리 금속임.)를 형성한다. At this time, the curing agent serves to promote the curing of the coating film, and becomes the main constituent material of the coating film. That is, the curing agent forms an alkali silicate (calcination formula: M 2 0 · nSiO 2 · mH 2 O, where M is an alkali metal) when the coating is performed using the pure inorganic paint used in the present invention. do.

여기에서 알칼리 실리케이트(alkali silicate)의 구조는 실리콘으로 이루어 지는 정사면체 구조 내부에 알칼리 금속 원자가 봉해지는 입체구조이다. 이러한 경화제는 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트로 이루어지는 것이 바람직하다. 이때 상기 알칼리 금속 산화물은, 산화 칼륨(K2O), 산화 나트륨(Na2O), 산화 리튬(Li2O) 등으로 이루어지는 군에서 선택되는 어느 하나 또는 둘 이상을 선택하고 혼합하여 형성되는 것이 바람직하다. Here, the structure of the alkali silicate (alkali silicate) is a three-dimensional structure in which the alkali metal atoms are sealed in the tetrahedral structure made of silicon. Such a curing agent is preferably composed of alkali metal oxides and alkali silicates. In this case, the alkali metal oxide is formed by selecting and mixing any one or two or more selected from the group consisting of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O), and the like. desirable.

다음으로 기제(base)는 도 4에 도시된 고경도 코팅막(50) 구조에서 싱크대 상판(20)과 고경도막(54) 사이에 형성되는 인산 피막(52)을 형성시키는 역할을 한다. 본 고안에 따른 기제는 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate) 및 알칼리 실리케이트 등으로 이루어지는 것이 바람직하다. 이때, 상기 금속 산화물은, 산화 아연(ZnO), 산화 알루미늄(Al2O3), 산화 칼슘(CaO), 산화 마그네슘(MgO) 중에서 선택되는 어느 하나로 이루어지거나 또는 둘 이상을 선택하고 혼합하여 형성되는 것이 바람직하다. 그리고 상기 금속 인산화물은, 알루미늄 인산화물 또는 아연 인산화물 중 어느 하나이거나, 그 혼합물로 형성되는 것이 바람직하다. Next, the base serves to form the phosphate film 52 formed between the sink top plate 20 and the high hardness film 54 in the high hardness coating film 50 structure shown in FIG. 4. The base according to the present invention is preferably made of metal oxide (metal oxide), metal phosphate (metal phosphate), alkali silicate and the like. In this case, the metal oxide is formed of one selected from zinc oxide (ZnO), aluminum oxide (Al 2 O 3 ), calcium oxide (CaO), magnesium oxide (MgO), or formed by selecting two or more selected and mixed. It is preferable. The metal phosphate is preferably any one of aluminum phosphate and zinc phosphate or a mixture thereof.

이때 인산 피막이 형성되는 과정은 다음과 같다. At this time, the process of forming the phosphate film is as follows.

H3PO4 + Al(OH)3 -> Al(H2PO4), Al2(HPO4)3, AlPO4 H 3 PO 4 + Al (OH) 3- > Al (H 2 PO 4 ), Al 2 (HPO 4 ) 3 , AlPO 4

Al(H2PO4) + MO -> AlPO4 + M(H2PO4)2 Al (H 2 PO 4 ) + MO-> AlPO 4 + M (H 2 PO 4 ) 2

M(H2PO4)2 -> MHPO4·3H2OM (H 2 PO 4 ) 2- > MHPO 4 , 3H 2 O

이하에서는 전술한 과정에 의하여 얻어진 상기 순수 무기질 도료를 싱크대 상판 표면에 코팅하는 과정을 설명한다. Hereinafter, a process of coating the surface of the sink top plate with the pure inorganic paint obtained by the above-described process will be described.

우선 싱크대 상판 표면에 대한 전처리 공정이 진행된다. 싱크대 상판 표면이 깨끗한 하고 오염되지 않은 경우에는 본 공정이 필요하지 않을 수 있다. 다만, 더 우수한 코팅막을 얻기 위하여 싱크대 상판 표면에 대한 전처리 공정을 수행하는 것이다. First, the pretreatment process is performed on the surface of the sink top plate. This process may not be necessary if the sink top surface is clean and uncontaminated. However, the pretreatment process is performed on the surface of the sink top plate to obtain a better coating film.

이러한 전처리 공정으로는 먼저 싱크대 상판 표면의 불순물을 제거하기 위한 탈지 세척 공정을 들 수 있다. 즉, 싱크대 상판 표면에 이물질이 묻어 있는 경우에는 그 부분에 대한 코팅이 비정상적으로 발생할 수 있으며, 코팅막면의 평활성 등에 이상이 발생할 수도 있기 때문이다. Such a pretreatment process may include a degreasing washing process for first removing impurities on the top surface of the sink. That is, when foreign matter is deposited on the top surface of the sink, the coating may be abnormally generated on the part, and abnormality may occur on the surface of the coating film.

다음으로는 코팅 공정이 진행된다. 본 고안에서는 이 코팅 공정을 1차 코팅단계, 자연 건조단계, 2차 코팅 단계 등의 소단계로 나누어 수행할 수도 있다. 즉, 한 번에 코팅막을 형성시키는 것이 아니라 2번에 나누어서 도막을 형성시키는 것이다. 이렇게 코팅 공정을 2번에 나누어 실시하게 되면 코팅막이 치밀해지고, 코팅막면의 평활성이 향상되는 장점이 있다. Next, the coating process proceeds. In the present invention, the coating process may be performed by dividing it into small steps such as a first coating step, a natural drying step, and a second coating step. That is, instead of forming a coating film at once, the coating film is formed by dividing in two. When the coating process is carried out in two times, the coating film becomes dense and the smoothness of the coating film surface is improved.

이 코팅 단계는 상온에서 진행되며, 도막의 두께가 약 0.1 ~ 15㎛ 정도 되도록 코팅 공정을 수행하는 것이 바람직하다. 도막의 두께가 0.1㎛ 이하인 경우에는 코팅의 경도가 약해지며, 15㎛ 이상인 경우에는 빛투과도가 낮아져서 투명 코팅의 성질을 얻을 수 없기 때문이다. This coating step is performed at room temperature, it is preferable to perform the coating process so that the thickness of the coating film is about 0.1 ~ 15㎛. If the thickness of the coating film is 0.1㎛ or less, the hardness of the coating is weakened, if it is 15㎛ or more, the light transmittance is low, it is because the properties of the transparent coating can not be obtained.

다음으로는 자연 건조공정이 진행된다. 본 공정을 거치면서 코팅막에 존재하는 수분이 제거되고 개수통 표면에 형성된 코팅막이 1차적으로 경화되는 것이다. 본 고안에서는 이러한 건조 공정을 10 ~ 40 ℃ 정도의 온도에서 10분 이상의 시간동안 진행한다. 온도가 10℃ 이하인 경우에는 건조시간이 길어지고, 건조상태가 불량하며, 40℃ 이상인 경우에는 급격한 건조로 인하여 코팅막에 변형이 발생할 가능성이 있기 때문이다. Next, a natural drying process is performed. Through this process, the water present in the coating film is removed and the coating film formed on the surface of the water bottle is primarily cured. In the present invention, this drying process is carried out at a temperature of about 10 to 40 ℃ for more than 10 minutes. This is because when the temperature is 10 ° C. or less, the drying time becomes long, the drying state is poor, and when the temperature is 40 ° C. or more, deformation may occur in the coating film due to rapid drying.

다음으로는 형성된 코팅막을 완전히 경화시키는 소성 공정이 진행된다. 본 고안에서는 이 소정 공정을, 소성로 내부 온도를 상온에서 최고온도까지 상승시킨 후 다시 상온으로 하강시키는 방식으로 진행한다. 즉, 코팅막이 형성된 싱크대 상판을 소성로에 투입하고, 소성로 내부의 온도를 상승시킨다. 소성로 내부 온도가 제1 소성온도에 도달하면 온도를 더 이상 상승시키지 않고, 소성로 내부 온도를 제1 소성온도로 유지하거나 서서히 상승시키면서 그 온도 영역에서 유지시키는 공정을 10분 이상 진행한다. Next, the baking process which fully hardens the formed coating film is advanced. In the present invention, the predetermined process is carried out in such a manner that the temperature inside the kiln is raised from room temperature to the maximum temperature and then lowered to room temperature again. That is, the sink top plate in which the coating film was formed is thrown into a kiln, and the temperature inside a kiln is raised. When the temperature inside the kiln reaches the first firing temperature, the temperature is no longer increased, and the process of maintaining the temperature in the firing furnace at the first firing temperature or gradually increasing the temperature is maintained for at least 10 minutes.

그리고 1차 소성 공정이 완료되면 다시 소성로 내부의 온도를 상승시킨다. 소성로 내부 온도가 최고온도에 도달하면 온도를 더 이상 상승시키지 않고 소성로 내부 온도를 최고온도로 유지하면서 10분 이상 지속한다. When the primary firing process is completed, the temperature inside the firing furnace is increased again. When the temperature inside the kiln reaches the maximum temperature, the temperature does not increase any more and the temperature lasts at least 10 minutes while maintaining the temperature inside the kiln.

이렇게 하여 1, 2차 소성 공정이 완료되면 소성된 싱크대 상판을 상온으로 식히는 냉각 공정이 진행된다. 이 냉각 공정은 싱크대 상판의 온도를 상온으로 낮추는 과정이다. 이때 이 냉각 공정을 1, 2차 소성 공정과 마찬가지로 온도를 하강시키다가 소정 온도에서 일정시간 동안 머물게 하고 다시 온도를 하강시키는 방법 으로 진행할 수도 있다. In this manner, when the first and second firing processes are completed, a cooling process of cooling the baked sink top plate to room temperature is performed. This cooling process is a process of lowering the temperature of the sink top plate to room temperature. In this case, the cooling process may be carried out by lowering the temperature in the same manner as the first and second firing processes, and then keeping the temperature at a predetermined temperature for a predetermined time and then lowering the temperature again.

본 고안에 의한 싱크대 상판에는, 고경도 코팅막이 형성되어 있으므로, 이 코팅막(50) 표면에 기름때, 음식물, 사람의 지문 등의 유기물질이 묻어서 오염이 발생하더라도, 물로 세척하여 손쉽게 상기 유기물질을 제거할 수 있는 장점이 있다. 즉, 도 5에 도시된 바와 같이, 코팅막(50) 표면에 유기물질(23)로 된 오염이 발생하는 경우, 본 고안의 코팅막(50) 표면에는 기름과는 친하지 않으면서 물과 친한 성질의 분자가 배치되어 있으므로, 유기물질이 코팅막과 강하게 결합하지 못한다. 오히려 도 6에 도시된 바와 같이 물(W)이 묻으면 코팅막(50) 표면이 물과 강하게 결합하여 유기 물질(23)을 띄우는 현상이 발생한다. 따라서 유기물질이 물에 의하여 손쉽게 제거될 수 있는 것이다. Since a high hardness coating film is formed on the sink top plate according to the present invention, even when contamination occurs due to staining of organic materials such as oil, food, or human fingerprints on the surface of the coating film 50, the organic material is easily removed by washing with water. There is an advantage to this. That is, as shown in Figure 5, when the contamination of the organic material 23 occurs on the surface of the coating film 50, the surface of the coating film 50 of the present invention is not in contact with oil but molecules of water-friendly properties Since is disposed, the organic material does not bond strongly with the coating film. Rather, as shown in FIG. 6, when the water (W) is buried, the surface of the coating layer 50 is strongly bonded to the water to float the organic material 23. Therefore, the organic material can be easily removed by water.

또한 본 고안의 코팅막은, 8H이상의 높은 도막경도를 가진다. 따라서 사용과정에서 식기 등 높은 경도를 가지는 물체와 충돌하더라도 개수통 표면에 스크래치가 형성되지 않는 장점이 있다. In addition, the coating film of the present invention has a high coating film hardness of 8H or more. Therefore, there is an advantage that the scratch is not formed on the surface of the water bottle even when colliding with an object having a high hardness, such as tableware in the process of use.

Claims (9)

싱크대 본체 상부에 결합되어 싱크대의 상면을 이루는 싱크대 상판에 있어서, In the sink top plate coupled to the top of the sink body to form the top surface of the sink, 상기 싱크대 상판의 표면에는, 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트(alkali silicate)로 이루어지는 경화제와 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate)로 이루어지는 기제를 교반하여 코팅한 고경도 코팅막이 형성되는 것을 특징으로 하는 싱크대 상판.On the surface of the sink top plate, a hardened surface coated with a hardening agent composed of an alkali metal oxide and an alkali silicate and a base composed of a metal oxide and a metal phosphate is coated with high hardness. Sink top plate, characterized in that the coating film is formed. 제1항에 있어서, 상기 싱크대 상판에는, According to claim 1, The sink top plate, 조리를 할 수 있는 소정 넓이의 조리대가 형성되는 것을 특징으로 하는 싱크대 상판.A sink top board, characterized in that a countertop of a predetermined width capable of cooking is formed. 제1항에 있어서, 상기 싱크대 상판에는, According to claim 1, The sink top plate, 가열 기구가 관통하여 설치될 수 있는 가열 기구 설치공이 형성되는 것을 특징으로 하는 싱크대 상판.A sink top plate, characterized in that a heating mechanism mounting hole is formed through which the heating mechanism can be installed. 제1항에 있어서, 상기 싱크대 상판에는, According to claim 1, The sink top plate, 식기 등을 세척할 수 있게 물을 일시 수용 저장하여 사용하고 사용을 마친 물은 하부로 배수시킬 수 있게 마개에 의해 개폐되는 배수구가 형성된 싱크대용 개 수통이 일체로 형성되는 것을 특징으로 하는 싱크대 상판.A sink top plate, characterized in that the sink canister is formed integrally with the drain can opening and closing by the stopper so as to temporarily store and use the water to wash dishes and used water is drained to the bottom. 제1항에 있어서, 상기 싱크대 상판에는, According to claim 1, The sink top plate, 싱크대용 개수통이 관통하여 설치될 수 있는 개수통 설치공이 형성되는 것을 특징으로 하는 싱크대 상판.Sink top plate is characterized in that the sink installation hole that can be installed through the sink for the sink is formed. 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 알칼리 금속 산화물은, The alkali metal oxide according to any one of claims 1 to 5, 산화 칼륨(K2O), 산화 나트륨(Na2O), 산화 리튬(Li2O) 중에서 선택되는 어느 하나인 것을 특징으로 하는 싱크대 상판.Sink top plate, characterized in that any one selected from potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O). 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 금속 산화물은, The metal oxide of any one of claims 1 to 5, wherein 산화 아연(ZnO), 산화 알루미늄(Al2O3), 산화 칼슘(CaO), 산화 마그네슘(MgO) 중에서 선택되는 어느 하나인 것을 특징으로 하는 싱크대 상판.A sink top plate, characterized in that any one selected from zinc oxide (ZnO), aluminum oxide (Al 2 O 3 ), calcium oxide (CaO), magnesium oxide (MgO). 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 금속 인산화물은, The metal phosphate of any one of claims 1 to 5, wherein 알루미늄 인산화물 또는 아연 인산화물 중 어느 하나이거나 그 혼합물인 것을 특징으로 하는 싱크대 상판.A sink top plate, which is either one of aluminum phosphate or zinc phosphate or a mixture thereof. 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 싱크대 상판은, The sink top plate according to any one of claims 1 to 5, 스테인레스 스틸(stainless steel)로 이루어지는 것을 특징으로 하는 싱크대 상판.Sink top, characterized in that made of stainless steel (stainless steel).
KR2020060005856U 2006-03-03 2006-03-03 A Upper Plate for Sink KR200416470Y1 (en)