KR200413900Y1 - Composite functional panel with corrugated structure for hose array (functional) pipe for boiler construction. - Google Patents

Composite functional panel with corrugated structure for hose array (functional) pipe for boiler construction. Download PDF

Info

Publication number
KR200413900Y1
KR200413900Y1 KR2020050034996U KR20050034996U KR200413900Y1 KR 200413900 Y1 KR200413900 Y1 KR 200413900Y1 KR 2020050034996 U KR2020050034996 U KR 2020050034996U KR 20050034996 U KR20050034996 U KR 20050034996U KR 200413900 Y1 KR200413900 Y1 KR 200413900Y1
Authority
KR
South Korea
Prior art keywords
panel
construction
bone
floor
corrugated
Prior art date
Application number
KR2020050034996U
Other languages
Korean (ko)
Inventor
송태기
Original Assignee
송태기
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 송태기 filed Critical 송태기
Priority to KR2020050034996U priority Critical patent/KR200413900Y1/en
Application granted granted Critical
Publication of KR200413900Y1 publication Critical patent/KR200413900Y1/en

Abstract

본 고안은 주택 및 사무실의 바닥난방을 위한 보일러 시공을 할때 소용이 되는 호스배열을 할수 있는 골구조를 가진 바닥용 패널에 관한것으로 모래와 함께 시멘트나 석고 등의 혼합물로 제품생산이 가능하며 무게를 다소 경량화 시킬 목적으로 섬유질을 첨가하며 섬유질 첨가로 인해 경량화는 물론 단열기능도 증대되고 가로와 세로 및 높이형의 사각형태로 된 적당한 크기의 패널판이 되면서 보일러 호스가 배열될수 있는 직선형과 곡선형의 골을 구조로 한 패널들이 각각으로 만들어지는 것인데 호스의 곡선배열 부위에 소용되는 반원형이 포함되는 곡선형 골패널과 직선배열 부위에 소용이 되는 직선형 골패널인 것이다. 다음단계로 골패널 윗면전체에 5미리 철사줄 굵기의 골을 가로와 세로로 5cm 간격이 되게 구성하여 보일러 호스배열이 끝난 패널위에 시멘트 혼합물로 바닥미장을 하지않고 옥판재. 맥반석 판재 등의 석재류 판재를 깔아주는 시공을 할 경우에는 철사줄 굵기의 낮은골 통로로 열이 순환이 잘되어 신속한 난방이 이루어 질수 있으며 다음단계로 패널 밑면 바닥의 2∼3곳 이상에 길게 길이형태로 적당한 크기의 홈으로 구성하여 시공바닥과의 접착에 도움되게하여 시공되는 패널의 유동이 방지되게 하는 특성을 지니게 한 것이다.The present invention relates to a floor panel with a corrugated structure that can be used for the construction of a boiler for floor heating in homes and offices. It is possible to produce products with a mixture of cement or plaster with sand. Fiber is added for the purpose of making the weight lighter, and the addition of fiber increases the light weight as well as the insulation function, and it becomes the right sized panel board in the shape of square, horizontal, vertical and height. The bone-structured panels are each made of a curved bone panel that contains a semicircle that is useful for the curved array of the hose and a straight bone panel that is useful for the straight array. The next step is to construct the 5mm thick wires on the top of the corrugated panel so that they are 5cm apart from each other horizontally and vertically so that the floor is not plastered with cement mixture on the finished boiler hose. In case of laying stone plate such as elvan plate, the heat is well circulated through the low valley passage of the thickness of wire, so the heating can be done quickly and the next step is longer than 2 ~ 3 places on the bottom of the panel. It has the property of preventing the flow of the panel to be constructed by assisting the adhesion with the construction floor by forming a groove of a suitable size in the form.

종래의 철판이나 알미늄 골판 등의 금속류 골패널과는 가격면에서도 차별을 이루며 플라스틱의 골페널과는 습기조정 측면으로도 우월할 수 있으며 레미콘 회사의 시멘트 혼합물을 이용한 시공법과는 시공시간 및 시공비 등과 차별될 수 있는, 보다 저렴하고 용이한 시공을 할 수 있도록 하는 특성을 지닌것이다.It is different from conventional corrugated metal panel such as iron plate or aluminum corrugated board in terms of price, and it can be superior to plastic corrugated panel in terms of moisture control, and it is different from construction method and construction cost with construction method using cement mixture of ready-mixed concrete company. It can be a cheaper and easier construction.

또한 목재류 마루판 시공의 밑면 받침 패널로도 이용이 가능한 특성을 지닌 복합기능 패널인 것이다.In addition, it is a composite function panel with the characteristics that can be used as a base support panel of wood floorboard construction.

직선부위 및 곡선부위형 골구조 패널. 섬유질. 경량화. 단열기능증대 낮은골구조. 골페널의 옆면부위 및 밑면 홈. Straight and curvilinear bone panels. Fibrous. Light weight. Increased insulation function Low bone structure. Lateral and bottom grooves of the golf panel.

Description

보일러 시공용 호스배열(기능)관 골구조의 복합기능패널.{omitted}Composite functional panel of corrugated structure of hose arrangement (functional) pipe for boiler construction. {Omitted}

도 1은 본 고안에 의한 패널의 곡선부위용과 직선부위용 패널이 연결되어 부착되면서 붉은색선으로 표시된 보일러 호스가 골에 끼워져 있는 형태를 나타낸 사시도.1 is a perspective view showing a boiler hose shown in the red line is inserted into the bone while the panel for the curved portion and the linear portion of the panel according to the present invention is attached and attached.

도 2는 곡선부위용 패널이 반쪽씩 쪼개어져 분리 및 결합이 가능하도록 한 형태의 사시도. 중간부위의 청색선(6)은 분리되는 부위의 선을 나타낸것임.Figure 2 is a perspective view of a form that allows the curved panel to be split in half so as to be separated and combined. The middle blue line (6) shows the line of separation.

도 3은 본 고안에 의한 곡선부위용 패널의 사시도.3 is a perspective view of a panel for curved portions according to the present invention;

도 4는 본 고안에 의한 직선부위용 패널의 사시도.Figure 4 is a perspective view of a panel for straight parts according to the present invention.

도 5는 본 고안에 의한 직선부위용 패널의 반쪽과 반쪽을 분리 및 결합이 가능하도록 한 형태를 나타낸 사시도.Figure 5 is a perspective view showing a form to enable separation and coupling of the half and half of the panel for a straight portion according to the present invention.

〈도면의 주요부분에 대한 부호의 설명〉<Explanation of symbols for main parts of drawing>

1-1∼10 : 열흐름 통로가 되는 낮은 골 구조들.1-1 to 10: Low bone structures that serve as heat flow paths.

2-1∼2 : 호스배열이 되기 위해 끼워지는(호스가) 골 구조2-1 ~ 2: bone structure to be fitted for hose arrangement

3-1∼4 : 옆면끼리의 패널이 배열 부착될때 접착고정용 몰탈을 채워주기 위한 홈.3-1 to 4: grooves for filling the mortar for fixing adhesives when the panels are arranged side by side.

4-1∼3 : 패널 밑면의 긴홈.4-1 to 3: Long groove at the bottom of the panel.

5-1∼4 : 보일러 호스가 끼워져 있는 형태를 나타낸 것.5-1 to 4: Boiler hoses are fitted.

6- : 패널이 분리 및 결합되는 부위를 선으로 표시.6-: Line showing the area where the panel is separated and joined.

7- : 패널의 호스 삽입되는 골7-: Corrugated Hose of Panel

8- : 밑면 홈.8-: Bottom groove.

9- : 옆면 홈.9-: Side groove.

10- : 곡면부위용 패널의 반쪽들.10-: halves of the panel for the curved area.

(1∼4)(1 to 4)

본 고안은 주택 및 사무실의 바닥난방을 하기 위한 보일러 시공을 할때 소용이 되는, 가로 30cm 세로 30cm 높이 10cm 정도로도 또 더 이상의 규격으로도 만들어서 실용되어 질수 있는, 호스배열을 할 수 있도록 패널에 호스를 끼워 넣을수 있는 적정한 깊이와 넓이의 골구조가 있는 패널인 것이다. 시공바닥에 보일러 호스시공을 할려면 호스가 직선으로 또는 곡선으로 깔려지며 배열이 되는데 이를 위하여 직선부위에는 직선형 골구조 패널이, 곡선부위에는 반원형 곡선형의 골이 구성된 곡선부위용 패널이 각각으로 생산되는것이 사용되는데 바닥전체가 이들 패널로 짜여지면서 보일러 호스의 배열시공이 되는 것이다. 참고적으로 패널위에 시공되는것을 기술해보면 상기와 같이 본 고안의 패널을 이용하여 호스배열시공이 끝나면 다음 공정으로 방바닥이나 마루바닥이 되는 윗면시공을 하게되는데, 시멘트 혼합물에 의한 미장기능사들의 미장시공법을 하던지 또 다르게는 옥판, 맥반석 판재 등과 같 은 석재류 판재를 깔면서 시공을 하는 경우도 있고 또 다르게는 황토. 맥반석. 옥분말 등과 석고를 혼합하여 바닥마감시공을 하는 경우도 있는데 이와 같은 여러가지 용도에 사용이 가능한 것으로서, 호스배열을 손쉽게 해주는 밑면 시공용 패널인 것이다.This design makes it possible to make a hose arrangement on the panel to make a practical use by making the boilers for floor heating of houses and offices. It is a panel with a corrugated structure of appropriate depth and width that can be inserted. In order to construct a boiler hose on the construction floor, the hose is laid out in a straight line or in a curved line. For this purpose, a straight corrugated panel is produced at the straight part and a semi-circular curved corrugated panel is formed at the curved part. The whole floor is woven into these panels, and the boiler hose is arranged. For reference, when describing the construction on the panel, when the hose arrangement construction is completed using the panel of the present invention as described above, the construction of the top surface, which becomes the floor or the floor, is performed in the next process. In other cases, they are installed while laying stone materials such as octane, elvan, and others. Elvan. In some cases, the floor finishing construction by mixing jade powder and gypsum, which can be used for such various purposes, it is a panel for the bottom construction to facilitate the arrangement of the hose.

상기의 패널을 생산하기 위하여 필요한 기초재료로는 모래. 시멘트. 석고 등이나 맥반석. 황토. 옥. 일라이트 등의 무기물질 분말종류도 혼합 사용될 수 있으며 비중이 큰 이들 혼합물에 의한 패널을 다소 경량화 할 목적으로 본 고안은 적정한 양의 섬유질을 혼합 사용하므로서 다소 가벼워지는 효과를 얻게하며 이를 위하여 본 고안의 패널제조에 식물성 및 광물성 섬유를 사용함에 있어서, 이들 종류로는 펄프. 목분. 왕겨분말. 폐지. 폐솜 등의 식물성 섬유질이, 광물성 섬유로는 질석. 펄라이트. 암면. 운모 등의 것이 혼합 이용되게하며 이로 인하여 콘크리트 바닥으로의 열손실을 줄이기도 하여 단열기능 증대효과도 얻게된다. 다음 단계로서 본 고안의 패널 윗면에 가로와 세로로 5cm 정도씩의 간격으로 3∼5미리 정도되는 철사줄 굵기의 낮은골을 구성해주는 패널이 되면 석판재나 마루판재 등의 시공에 호스배열을 하게 되는 밑면쪽 패널로 폭넓게 이용될 수 있으며 상기의 낮은골 골구조로 인하여 열의 순환을 원할하게 해줄 수도 있는 것이다.Sand is the basic material needed to produce the panel. cement. Plaster and elvan. ocher. jade. Inorganic powders such as illite may also be mixed and used, and for the purpose of lightening the panel by the mixture having a high specific gravity, the present invention obtains a lighter effect by using an appropriate amount of fiber. In the use of vegetable and mineral fibers in panel production, these types are pulp. Wood powder. Chaff powder. abolition. Vegetable fiber such as waste cotton is vermiculite as mineral fiber. Pearlite. Rock wool. Mica and the like are mixed and used, thereby reducing heat loss to the concrete floor and increasing the insulation function. As a next step, when the panel is composed of wire ribs having a thickness of 3 to 5 mm at intervals of about 5 cm on the top of the panel of the present invention, the hose is arranged in the construction of slabs or floorboards. It can be widely used as a base panel, and because of the low bone bone structure, it can also facilitate the circulation of heat.

다음 단계로 패널의 밑면 바닥에 2개 이상의 길이형으로 긴홈을 적당한 깊이와 넓이의 규격으로 만들어 주어 시공바닥과의 접착에 도움이 되면서 건조 및 경화된 후의 패널이 움직이지 않도록 하는 고정작용의 특성을 지니게 한 것이다. 참고적으로 기술하는 사항으로는 제품성형에 혼합되는 접착 및 건조. 경화가 가능한 물 질로서 시멘트와 석고 등과 더불어 합성수지계통의 아크릴 수지액. 폴리에스테르 수지액. 기타 열경화성 수지액 등도 혼합사용이 가능한 것이다.The next step is to make the long grooves in the bottom of the panel with two or more lengths in the proper depth and width to help the adhesion with the construction floor and to prevent the panel from moving after being dried and cured. It is to be carried. For reference, mention is made of adhesion and drying mixed into product molding. As a hardenable material, acrylic resin liquid of synthetic resin system together with cement and gypsum. Polyester resin liquid. Other thermosetting resin solutions can also be mixed.

다음 단계로 패널의 옆면쪽 가장자리 부위에 1개 이상의 홈을 만들어주어 옆면쪽 패널들끼리 부착하여 고정되는 작용이 되게 한 것이다.The next step is to make one or more grooves on the side edges of the panels so that the side panels are attached and fixed.

다음 단계로서 도 2와 도 5에서와 같은 직선형, 곡선부위형의 분리 및 결합형 패널이 되게 하여 시공에 다양한 용도로 이용되게 한 것이다.As a next step, as shown in Figures 2 and 5 to be a straight, curved portion of the separation and combination panel to be used in a variety of applications for construction.

상기와 같이 본 고안의 패널은 보다 진보적이고 다양성 있는 건축용품인 것이다.As described above, the panel of the present invention is a more advanced and versatile building article.

종래의 기술시공을 보면 일반적으로 미장기능사에 의해 시멘트와 모래의 혼합물을 사용하여 시공할 경우, 첫째 바닥에 비닐을 깔고 그위에 시멘트 혼합물을 부어 깔고서 다듬은 다음. 어느정도 굳어진 뒤에 다시 그위에 철사망을 펼치고 호스를 배열하면서 필요한 부위마다 일일이 철사망과 보일러호스를 철사로서 묶어주는 작업을 마친뒤에 최종적으로 시멘트 몰탈을 부어넣어 깔고 다듬으며 마지막 미장마감을 하여 바닥시공이 종료되도록 하는것이 보편적인데 시간과 일손이 많이 소용되어 시공비가 부담이되는 단점이 있다.According to the conventional construction, in general, when using a mixture of cement and sand by a plasterer, first put a vinyl on the floor, and then pour the cement mixture on it and trim it. After hardening to some extent, spread the wire mesh on it again and arrange the hoses. After finishing the work of tying the wire mesh and the boiler hose with the wires for each necessary part, finally, cement mortar is poured and laid and polished. It is common to have it terminated, but it takes a lot of time and work and has a disadvantage in that construction costs are burdened.

또 다르게는 알미늄이나 철판 등으로 만들어진 골구조 패널을 만들어 시공하는 경우가 있으며 본 고안을 이용하는 것과는 자재비 측면에서만 비교를 해도 차별될 수 있으며 재생플라스틱의 골패널로 시공하는 경우와는 습기의 흡습 조정 측면만으로도 본 고안이 우월할 수 있으며 시공내용면에서도 종래의 어느 기술보다 본 고안의 이용시공이 신속하고 용이하며 적정한 무게를 지닌 본 고안의 패널은 시공 바닥에 짜맞추면서 깔기만하면 호스배열을 할수 있는 골모양이 전체적으로 쉽게 형성되며 이렇게 만들어진 골속에 보일러호스를 끼워가며 곧바로 윗면 마감시공도 가능하게 해 준다.In addition, there are cases of constructing and constructing a corrugated panel made of aluminum or iron plate, and it can be differentiated by using only the material cost compared with using the present invention. The present invention can be superior by itself, and in terms of construction content, the use of the present invention is faster, easier and easier to apply than the conventional technology. The panel of the present invention has a proper shape and a bone shape that can be arranged simply by laying it on the floor. It is easily formed as a whole, and the boiler hose is inserted into the bone so that it can be immediately finished.

상기와 같은 종래의 시공을 더욱 다양성 있게 하여 진보시킬 목적으로 본 고안은 섬유질을 이용하여 경량화를 이루고 단열증대 효과를 얻게하며 여러단계의 다양한 특성에 의하여 신속한 시공과 시공비 절감효과를 얻는 목적을 달성케 해주는 특성과 폭넓게 실용되게 하는데 또다른 목적이 있는 것이다In order to improve the conventional construction as described above more diversified, the present invention achieves the purpose of achieving lightweight construction and increasing thermal insulation effect by using fiber, and the purpose of obtaining rapid construction and construction cost saving effect by various characteristics of various stages. It has another purpose to make it more practical and to make it practical.

상기한 목적을 달성하기 위하여 본 고안은 상세한 설명에 기술한대로 비중이 큰 시멘트, 석고 등과 기타 무기질들인 맥반석. 옥. 황토. 일라이트 등의 친환경 물질을 소입자로 가공한것과 다양한 섬유질의 혼합이용이 가능케 하여 본 고안의 페널이 경량화되게 하며 패널을 깔고 짜맞추기만 하면서 호스를 끼워넣기만 해도 호스배열작업이 쉽게되도록 하여 시공시간과 시공비가 절감되게 하였으며 시공된 패널의 유동을 방지할 목적으로 밑면바닥의 홈과 윗면 가장자리의 홈을 구성해주어 패널끼리 고정 부착되는 작용의 특성을 지닌다. 페널제조용 기초재료들의 제품을 위한 혼합비율은 여러방법이 있을 수 있으며 다소 차별이 되는 혼합물들은 제품의 성형에 장애가 되지않는 범위에서는 가능하기에 본 고안의 실험적 혼합내용을 몇가지 기술해보면 아래와 같다.In order to achieve the above object, the present invention has a high specific gravity cement, gypsum and other minerals as described in the detailed description. jade. ocher. It is possible to process the environment-friendly materials such as illite with small particles and mix and use various fibers to make the panel of the present invention lighter, and to arrange the hose easily by simply inserting a hose while laying and paneling. The construction cost is reduced and the construction of the bottom bottom groove and the top edge groove for the purpose of preventing the flow of the constructed panel has the characteristic of fixing the panels. Mixing ratio for the product of the base material for panel manufacturing may be a number of ways, and the somewhat different mixtures are possible in a range that does not interfere with the molding of the product, the following describes a few experimental mixing contents of the present invention.

(실시예 1)(Example 1)

10 wt ％의 모래10 wt% sand

30∼40 wt ％의 시멘트30-40 wt% cement

20∼30 wt ％의 폐지섬유질20-30 wt% waste paper fiber

20∼30 wt ％의 물.20-30 wt% water.

(실시예 2)(Example 2)

10 wt ％의 모래10 wt% sand

30 wt ％의 석고30 wt% gypsum

20∼30 wt ％의 펄프섬유질20-30 wt% pulp fiber

20∼30 wt ％의 물.20-30 wt% water.

(실시예 3)(Example 3)

10 wt ％의 모래10 wt% sand

30∼40 wt ％의 시멘트30-40 wt% cement

20∼30 wt ％의 펄라이트20-30 wt% pearlite

10∼20 wt ％의 폐솜섬유질10-20 wt% waste cotton fiber

20∼30 wt ％의 물.20-30 wt% water.

(실시예 4)(Example 4)

30∼40 wt ％의 석고30-40 wt% gypsum

20∼30 wt ％의 질석20-30 wt% vermiculite

10∼15 wt ％의 폐지섬유질.10-15 wt% waste paper fiber.

20∼30 wt ％의 물20-30 wt% water

상기와 같이 혼합조정이 필요한 본 고안의 패널이 성형제조 되는데 장애가 없는 범위내에서 사용된 혼합물들은 본 고안의 패널로서 완성품이 가능한 것으로 판단되어 이행해 본 것이라 참고적으로 기술한다.As described above, the mixtures used within the range without any obstacle in forming the panel of the present invention requiring the mixing adjustment as described above are referred to as the completed products as the panel of the present invention.

이하 본 고안에 의한 복합기능 페널의 진보적인 효과를 보면 섬유질의 혼합사용에 의한 경량화 효과와 콘크리트 바닥으로의 단열효과를 얻게하며 패널에 구성한 골에 의하여 손쉽고 신속한 보일러호스 배열시공이 될수 있게 하며 패널윗면의 철사줄 굵기의 낮은골을 만들어주어 열순환이 잘되면서 신속한 난방이 되게하며 밑면과 옆면부위쪽의 홈을 구성해 줌으로서 패널이 고정부착되도록 하는 작용을 하는것과 분리결합형의 패널이 되게 할 수도 있어 다양성이 있게하여 종합적인 측면에서 보다 진보적인 효과를 얻게한다.According to the progressive effect of the composite function panel according to the present invention, the weight reduction effect by the mixed use of fiber and the insulation effect to the concrete floor can be obtained, and the boiler hose can be easily and quickly arranged by the valley formed on the panel. By making the low trough of the wire thickness of the wire, the heat circulation is good and rapid heating, and the grooves on the bottom and side are formed to make the panel fixed and the panel to be separated and bonded. It can also be diversified, giving a more progressive effect in the overall sense.

Claims (3)

보일러 호스배열을 할수 있는 골구조를 가진 패널에 관한것으로 모래와 시멘트의 혼합물에 섬유질이 혼합이용되어 경량화를 이루는 패널이 되면서 패널의 윗면에 열순환을 돕기위한 통로기능의 낮은 골구조와 밑면과 옆면부위에 패널의 고정부착 목적의 여러개의 홈이 구성되면서 제조되는 복합기능패널.It is a panel with a corrugated structure that can arrange a boiler hose. It is a lightweight panel made of a mixture of sand and cement with fiber, and a low corrugated structure with a passage function to help heat circulation on the top of the panel, and a bottom and a side. A composite functional panel manufactured by forming a plurality of grooves for fixing and attaching a panel to a part. 상기 청구항 1에 있어서 시멘트 대신 석고와 함께 황토. 맥반석. 옥. 일라이트 등 친환경 무기물질이 혼합물에 사용되어 제조되는 무독성의 복합기능페널.The loess with gypsum instead of cement according to claim 1. Elvan. jade. Non-toxic composite functional panel manufactured by using environmentally friendly inorganic materials such as illite in the mixture. 상기 1항 또는 2항에 있어서 반쪽형태의 부분과 부분이 결합도 되고 분리도 되어지는 복합기능패널.The composite functional panel according to claim 1 or 2, wherein the half-shaped part and the part are combined or separated.
KR2020050034996U 2005-08-30 2005-12-13 Composite functional panel with corrugated structure for hose array (functional) pipe for boiler construction. KR200413900Y1 (en)