KR20040089222A - Manufacture method of exercise taking medicine material to discharge permanent domicile outer line - Google Patents
Manufacture method of exercise taking medicine material to discharge permanent domicile outer line Download PDFInfo
- Publication number
- KR20040089222A KR20040089222A KR1020030022906A KR20030022906A KR20040089222A KR 20040089222 A KR20040089222 A KR 20040089222A KR 1020030022906 A KR1020030022906 A KR 1020030022906A KR 20030022906 A KR20030022906 A KR 20030022906A KR 20040089222 A KR20040089222 A KR 20040089222A
- Authority
- KR
- South Korea
- Prior art keywords
- mixer
- textile
- fabric
- mixing
- dryer
- Prior art date
Abstract
Description
본 발명은 원적외선을 방출하는 운동복용 원단의 제조방법에 관한 것으로, 특히 해송(海松)잎, 삼백초(三白草), 황금(黃芩), 백리향(白里香)을 동일한 분량으로 혼합하여 그늘에서 건조하여 물에 끓인 액체와, 맥반석이나 맥섬석과 같이 원적외선을 발생하는 세라믹 원석을 미분화한 원석 가루를 50% 혼합한 수용액을, 1:1로 혼합한 용액에 원단을 6시간 이상 함침시켰다가 가열하여 탈수, 건조시키고, 상기의 원단을 다시 아로마 서로피(aroma therapy)의 향기치료제와 제오라이트 가루 및 숯가루를 1:2;3 정도의 비율로 혼합한 혼합물의 30% 수용액에 6시간 이상 함침시켰다가 냉각 건조시키도록 한 원적외선을 방출하는 운동복용 원단의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a sportswear fabric that emits far infrared rays, in particular, seaweed leaves, three hundred seconds (三 白草), golden (黄 芩), thyme (白 里 香) by mixing in the same amount and dried in the shade The solution mixed with 50% of the liquid boiled in water and the undifferentiated gemstone powder, such as elvan or macsomite, which is far-infrared ceramic gemstone, was impregnated with the fabric in a 1: 1 mixture for 6 hours or more and dehydrated. After drying, the fabric was again impregnated in a 30% aqueous solution of a mixture of aroma therapy aroma therapy and zeolite powder and charcoal powder in a ratio of about 1: 2; 3 and then cooled. It relates to a method for producing a sportswear fabric that emits far-infrared radiation to be dried.
일반적으로 원적외선은 적외선 중 파장이 긴 것으로서, 물체의 깊숙한 곳까지 침투가 가능하고, 공진, 공명 작용과 함께 열을 만드는 것으로 확인되고 있다.In general, far infrared rays have a long wavelength among infrared rays, which can penetrate deep into the object and generate heat with resonance and resonance.
이러한 열작용은 각종 질병의 원인이 되는 세균을 없애는데 도움이 되고, 모세혈관을 확장시켜 혈액순환과 세포조직 생성에 도움을 준다.This heat action helps to eliminate the bacteria that cause various diseases, and helps to expand the capillaries and blood circulation and tissue formation.
또한, 세포를 구성하는 수분과 단백질 분자에 닿으면 세포를 1분에 2,000번씩 미세하게 진동시킴으로써 세포조직을 활성화하여 노화방지, 신진대사 촉진, 만성 피로 등 각종 성인병 예방에 효과가 있다.In addition, when it touches the moisture and protein molecules constituting the cells, the cells are vibrated finely 2,000 times per minute, thereby activating cell tissues, which is effective in preventing various adult diseases such as aging, promoting metabolism, and chronic fatigue.
그밖에도 발한작용 촉진, 통증완화, 중금속 제거, 숙면, 탈취, 방균, 곰팡이 번식방지, 제습, 공기정화 등의 효과가 있어 주택 및 건축자재, 주방기구, 섬유, 의류, 침구, 의료기구, 찜질방 등의 여러 분야에 쓰이고 있다.In addition, it promotes sweating, pain relief, heavy metal removal, sleep, deodorization, antibacterial, mold propagation prevention, dehumidification, and air purification, so it is effective in housing and construction materials, kitchen utensils, textiles, clothing, bedding, medical equipment, jjimjilbang, etc. It is used in many fields.
최근에, 고효율의 원적외선 방사재로서, 세라믹이 주목받고 있다. 원적외선은 방사, 복사 파장이 수 ㎛ ~ 약 400㎛ 정도의 전자파이고, 가열 효과, 건조 효과가 우수하다. 이러한 이유로, 원적외선 방사재로서, 세라믹과 세라믹을 코팅한 금속체는 스토브, 히터 및 코타쓰(kotatsu) 등의 난방 용도에 사용되어 왔고, 더욱이, 식품의 표면을 과잉으로 가열하지 않고 내부까지 균일하게 가열 할 수 있어, 고품질의 식품 가공 분야에도 활용되어 왔다.Recently, ceramics have attracted attention as high-efficiency far-infrared radiating materials. Far-infrared rays are electron waves whose radiation and radiation wavelengths are about several micrometers to about 400 micrometers, and are excellent in a heating effect and a drying effect. For this reason, as a far-infrared radiating material, ceramics and metals coated with ceramics have been used for heating applications such as stoves, heaters and kotatsu, and moreover, evenly to the inside without excessively heating the surface of food. It can be heated and utilized in the field of high quality food processing.
상기의 원적외선 방사재를 광범위한 파장역에서 원적외선을 방사할 수 있는 고효율이 되도록 하는 연구가 적극적으로 수행되어져왔다.Research has been actively carried out to make the far-infrared radiant material such that the far-infrared radiation emitter has a high efficiency capable of emitting far-infrared radiation in a wide range of wavelengths.
그 결과, 백금을 첨가한 원적외선 방사용 세라믹 분체(일본 공개 특허공보 쇼 62-184088호 및 일본 공개 특허 공보 평 3-190990호 참조)와 이와 같은 원적외선 방사용 분체 세라믹을 합성 섬유에 분산시켜 혼입시킨 발명(일본 공개 특허 공보 평 3-190990호 참조), 원적외선 방사용 분체를 나일론 용액이나 폴리에스테르 용액에 배합하고, 이를 노즐분사에 의해 실-형태물(thread-form product)로 성형하여, 기존의 실 재료와 함께 꼬아 직물용 꼬임사(twisted thread)를 형성하는 발명(일본 공개 특허 공보 제 1991-241025 및 1992-73226 참조)이 개시되어 있다.As a result, platinum-added far-infrared radiation ceramic powder (see Japanese Laid-Open Patent Publication No. 62-184088 and Japanese Unexamined Patent Publication No. Hei 3-190990) and such far-infrared radiation ceramic powder were dispersed and mixed in a synthetic fiber. Invention (see Japanese Unexamined Patent Publication No. Hei 3-190990), a powder for far-infrared radiation is blended into a nylon solution or a polyester solution, and it is formed into a thread-form product by nozzle spraying. An invention (see Japanese Laid-Open Patent Publications 1991-241025 and 1992-73226) is disclosed which twists together with a yarn material to form a twisted thread for a fabric.
이들 원적외선 방사용의 분체 세라믹은, 모두 파장 4㎛ 이상의 영역의 에너지 비율이 높고, 일반적으로 3 내지 12㎛의 파장역에서 유효하다. 그러나, 광범위한 파장 영역을 가지는, 고효율의 원적외선 방사가 가능하며, 흑체 바디에 가까운 균일한 방사 성능을 갖는 원적외선 방사용 세라믹 분체나 조성물이 요망된다.These powder ceramics for far-infrared radiation all have a high energy ratio in the region having a wavelength of 4 µm or more, and are generally effective in a wavelength range of 3 to 12 µm. However, high-efficiency far-infrared radiation having a wide wavelength range is possible, and a ceramic powder or composition for far-infrared radiation having a uniform radiation performance close to a black body body is desired.
그리고 상기의 원적외선 방사재를 섬유에 혼입하거나 표면에 코팅한, 원적외선 효과를 가지는 섬유는, 침구, 의류(clothing), 및 속옷(underwear)등에 광범위하게 사용되고 있다.In addition, the fiber having the far-infrared effect, in which the far-infrared radiant is incorporated into the fiber or coated on the surface, is widely used in bedding, clothing, underwear, and the like.
그러나 상기와 같은 원적외선 방사재를 이용한 섬유에 의하여서는 원적외선이 장기간 지속적으로 발산되지 않거나 세탁한 후에는 원적외선의 발생량이 미미해지게 되는 등의 문제점이 있었다.However, the fiber using the far-infrared radiating material as described above has a problem that far-infrared rays are not continuously diverged for a long time or the amount of generation of far-infrared rays becomes insignificant after washing.
이에, 본 발명은 상기한 바와 같은 문제점을 해결하기 위해 안출된 것으로써, 해송(海松)잎, 삼백초(三白草), 황금(黃芩), 백리향(白里香)을 동일한 분량으로 혼합하여 그늘에서 건조하여 물에 끓인 액체와, 맥반석이나 맥섬석과 같이 원적외선을 발생하는 세라믹 원석을 미분화한 원석 가루를 50% 혼합한 수용액을, 1:1로 혼합한 용액에 원단을 6시간 이상 함침시켰다가 가열하여 탈수, 건조시키고, 상기의 원단을 다시 아로마 서로피(aroma therapy)의 향기치료제와 제오라이트 가루 및 숯가루를 1:2;3 정도의 비율로 혼합한 혼합물의 30% 수용액에 6시간 이상 함침시켰다가 냉각 건조시키도록 한 원적외선을 방출하는 운동복용 원단의 제조방법을 제공하는데 그 목적이 있다.Thus, the present invention has been devised to solve the problems as described above, in the shade by mixing the same amount of haesong (海松) leaves, three hundred vine (三 白草), golden (黄 芩), thyme (白 里 香) in the shade A solution mixed with 50% of the dried and boiled water and undifferentiated gemstone powder, such as elvan or macsumrite, which is far-infrared ceramic gemstone, was impregnated with a fabric in a 1: 1 mixture for 6 hours or more and then heated. After dehydration and drying, the fabric was again impregnated in a 30% aqueous solution of a mixture of aroma therapy aroma therapy, zeolite powder and charcoal in a ratio of about 1: 2; It is an object of the present invention to provide a method for manufacturing a sportswear fabric that emits far infrared rays that are allowed to cool and dry.
상기한 목적을 달성하기 위한 본 발명의 원적외선을 방출하는 운동복용 원단의 제조방법은 해송잎, 삼백초, 황금, 백리향을 같은 분량으로 혼합하는 과정과,In order to achieve the above object, the method of manufacturing a fabric for sportswear that emits far-infrared rays of the present invention comprises the steps of mixing the same amount of sea pine leaves, three hundred seconds, golden, thyme,
상기의 혼합한 해송잎, 삼백초, 황금 및 백리향들을 그늘에서 건조하고 100 ℃ 정도로 가열하는 가열용기에서 물에 3시간 정도 끓이면서 이들의 성분을 포함하는 액체를 생성하는 과정과,The process of producing a liquid containing these components by boiling in water for 3 hours in a heating vessel drying the mixed pine needles, three hundred seconds, golden and thyme in the shade and heated to about 100 ℃,
맥반석이나 맥섬석과 같이 원적외선을 발생하는 세라믹 원석을 미분화하는 과정과,The process of micronizing ceramic ore that generates far infrared rays such as elvan or macsumite,
상기 세라믹 원석의 미분한 가루를 50% 혼합하여 수용액을 생성하는 과정과,Mixing 50% of the fine powder of the ceramic ore to produce an aqueous solution,
상기의 액체와 수용액을 1:1로 혼합하는 과정과,Mixing the liquid and the aqueous solution in a 1: 1 ratio,
상기의 혼합한 용액에 원단을 6시간 이상 함침시켰다가 가열하여 탈수, 건조시키는 과정과,The process of impregnating the fabric in the mixed solution for 6 hours or more, followed by heating to dehydrate and dry,
아로마 서로피(aroma therapy)의 향기치료제와 제오라이트 가루 및 숯가루를 1:2;3 정도의 비율로 혼합하여 혼합물을 생성하는 과정과,Mixing aroma therapy agent of aroma therapy (aroma therapy), zeolite powder and charcoal powder in a ratio of about 1: 2; 3 to produce a mixture,
상기 혼합물의 30% 수용액에 상기의 원단을 6시간 이상 함침시키는 과정과,Impregnating the fabric in a 30% aqueous solution of the mixture for at least 6 hours;
상기의 원단을 -10℃ 이하의 온도에서 냉각 건조시키도록 함으로써 원적외선을 장기간 발생함은 물론, 아로마 서로피에 의한 향기와 제오라이트 및 숯에 의한 탈취작용이 동시에 이루어져 격렬한 운동에도 땀으로 인한 악취를 방지하는 동시에 원단에서 은은한 향기를 발생하도록 구성됨을 특징으로 한다.By cooling and drying the fabric at a temperature below -10 ° C, far-infrared rays are generated for a long time, as well as aroma by aromas and deodorization by zeolite and charcoal at the same time to prevent odors due to sweating during intense exercise. At the same time it is characterized in that it is configured to generate a soft fragrance in the fabric.
도 1은 본 발명의 실시예에 따라 원적외선을 방출하는 원단을 제조하는 과정을 나타낸 개략도.1 is a schematic view showing a process of manufacturing a fabric emitting far infrared rays according to an embodiment of the present invention.
* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings
1, 7 : 건조기 2 : 가열용기1, 7 dryer 2 heating vessel
3 : 분쇄기 4, 8 : 혼합기3: grinder 4, 8 mixer
5 : 가열기 6 : 탈수기5: heater 6: dehydrator
9 : 냉각 건조기9: cooling dryer
이하, 본 발명을 첨부한 예시도면을 참조하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings, the present invention will be described in detail.
도 1은 본 발명의 구성도로서,1 is a block diagram of the present invention,
자연에서 채취한 해송잎, 삼백초, 황금, 백리향을 같은 분량으로 혼합하여 바람이 잘 통하는 제1 건조기(1)에서 건조시킨다.Seaweed leaves, three hundred seconds, golden, thyme collected in nature are mixed in the same amount and dried in a well-ventilated first dryer (1).
상기의 제1 건조기(1)에서 건조시킨 해송잎, 삼백초, 황금 및 백리향들을 가열용기(2)에서 100 ℃ 정도로 가열시킨 물에 3시간 정도 끓이면서 이들의 성분을 포함하는 액체를 생성한다.The pine leaf, three hundred vines, golden and thyme dried in the first dryer 1 is boiled in water heated at about 100 ° C. in the heating vessel 2 for about 3 hours to produce a liquid containing these components.
맥반석이나 맥섬석과 같이 원적외선을 발생하는 세라믹 원석을 분쇄기(3)에서 미분화한다.Ceramic ore, which generates far-infrared rays, such as elvan and maculite, is micronized in the mill 3.
상기 세라믹 원석의 미분한 가루를 제1 혼합기(4)에서 물과 혼합하여 50% 수용액을 생성한다.The fine powder of the ceramic ore is mixed with water in the first mixer 4 to produce a 50% aqueous solution.
상기의 수용액이 담긴 제1 혼합기(4)에 상기의 액체를 1:1의 비율로 혼합한다.The above liquid is mixed in a ratio of 1: 1 in the first mixer 4 containing the aqueous solution.
상기의 혼합한 용액이 담겨진 제1 혼합기(4)에 원단을 6시간 이상 함침시키는 중에 저면에서 가열기(5)로 가열시킨다.The bottom surface of the first mixer 4 containing the mixed solution is impregnated with the heater 5 while the fabric is impregnated for 6 hours or more.
상기의 원단을 탈수기(6)에서 탈수시킨 후 제2 건조기(7)에서 가열하면서 건조시킨다.The fabric is dehydrated in the dehydrator 6 and then dried while heating in the second dryer 7.
아로마 서로피(aroma therapy)의 향기치료제와 제오라이트 가루 및 숯가루를 1:2;3 정도의 비율로 제2 혼합기(8)에 혼합하여 혼합물을 생성한다.The aroma therapy agent of aroma therapy (aroma therapy), zeolite powder and charcoal powder is mixed in the second mixer 8 in a ratio of about 1: 2; 3 to produce a mixture.
상기 혼합물이 담긴 제2 혼합기(8)에 물을 부으면서 30% 수용액을 만든 다음 상기의 원단을 6시간 이상 함침시킨다.30% aqueous solution is prepared by pouring water into the second mixer 8 containing the mixture, and the fabric is impregnated for 6 hours or more.
상기의 원단을 냉각 건조기(9)로 옮겨 -10℃ 이하의 온도에서 냉각 건조시키도록 한 것이다.The fabric is transferred to a cooling dryer (9) to cool and dry at a temperature of -10 ℃ or less.
상기와 같은 본 발명의 원적외선을 방출하는 운동복용 원단의 제조과정을 보다 상세히 기술하면 다음과 같다.Referring to the manufacturing process of the fabric for sportswear emitting far infrared rays of the present invention as described above in more detail.
제 1 공정1st process
해송(海松, 흑송)잎 25%, 삼백초(三白草) 25%, 황금(黃芩, SCUTELLARIAE RADIX) 25%, 백리향(百里香, THYMIHERBA) 25% 들을 15℃~20℃가 유지되는 제1 건조기(1)의 그늘에서 건조한다.The first dryer (15 ℃ ~ 20 ℃) contains 25% of Haesong (Songsong) leaves, 25% of Sanbaekcho, 25%, Golden (Huang), 25% of SCUTELLARIAE RADIX, and 25% of Thyme. 1) to dry in the shade.
제 2 공정2nd process
상기의 제1 건조기(1)에서 건조시킨 해송잎, 삼백초, 황금 및 백리향들을 가열용기(2)에서 100 ℃ 정도로 가열시킨 물에 넣은 상태에서 3시간 정도 더 끓이면서 이들의 성분을 포함하는 액체를 생성한다.Boiled in the water heated to about 100 ℃ in the heating container (2) to the dried pine needles, three hundred seconds, golden and thyme dried in the first dryer (1) for about 3 hours to produce a liquid containing these components do.
제 3 공정3rd process
맥반석이나 맥섬석과 같이 원적외선을 발생하는 세라믹 원석을 분쇄기(3)에서 작은 알갱이의 상태로 부숴 미분화한다.Ceramic gemstones that generate far-infrared rays, such as elvan and maculite, are pulverized and finely divided into small grains in the grinder 3.
제 4 공정4th process
상기 세라믹 원석의 미분한 가루를 제1 혼합기(4)에서 물과 혼합하면서 잘 저어 50% 수용액으로 생성한다.The fine powder of the ceramic ore is stirred well while mixing with water in the first mixer 4 to produce a 50% aqueous solution.
제 5 공정5th process
상기의 수용액이 담긴 제1 혼합기(4)에 상기의 액체를 1:1의 비율로 섞어 주면서 혼합한다.The liquid is mixed in a ratio of 1: 1 in the first mixer 4 containing the aqueous solution.
제 6 공정6th process
상기의 혼합한 용액이 담겨진 제1 혼합기(4)에 원단을 6시간 이상 함침시키는 중에 저면에서 가열기(5)로 100 ℃ 이상의 온도로 가열시켜 원단에 용액이 잘 배이도록 한다.While impregnating the fabric in the first mixer 4 containing the mixed solution for 6 hours or more, the bottom surface is heated with a heater 5 to a temperature of 100 ° C. or more so that the solution is well circulated in the fabric.
제 7 공정7th process
상기의 원단을 탈수기(6)에서 탈수시킨 후 제2 건조기(7)에서 100℃ 정도로 온도로 가열하면서 충분히 건조시킨다.The fabric is dehydrated in the dehydrator 6 and then sufficiently dried while heated to a temperature of about 100 ° C. in the second dryer 7.
제 8 공정8th process
아로마 서로피(aroma therapy)의 향기치료제와 제오라이트 가루 및 숯가루를 1:2;3 정도의 비율로 제2 혼합기(8)에 혼합하여 혼합물을 생성한다.The aroma therapy agent of aroma therapy (aroma therapy), zeolite powder and charcoal powder is mixed in the second mixer 8 in a ratio of about 1: 2; 3 to produce a mixture.
제 9 공정9th process
상기 혼합물이 담긴 제2 혼합기(8)에 물을 부으면서 30% 수용액을 만든 다음 상기의 원단을 6시간 이상 함침시켜 충분히 배이도록 한다.Water is poured into the second mixer 8 containing the mixture to make a 30% aqueous solution, and then the fabric is impregnated for 6 hours or more to be sufficiently doubled.
제 10 공정10th process
상기의 원단을 냉각 건조기(9)로 옮겨 -10℃ 이하의 온도에서 냉각 건조시켜 원단에 배인 향과 탈취성분이 장기간 지속되도록 한다.The fabric is transferred to a cooling dryer (9) and cooled and dried at a temperature of -10 ° C. or lower so that the fragrance and deodorizing ingredients contained in the fabric last for a long time.
이상 기술한 바와 같이 본 발명의 원적외선을 방출하는 운동복용 원단의 제조방법에 의하여서는 해송(海松)잎, 삼백초(三白草), 황금(黃芩), 백리향(白里香)을 동일한 분량으로 혼합하여 그늘에서 건조하여 물에 끓인 액체와, 맥반석이나 맥섬석과 같이 원적외선을 발생하는 세라믹 원석을 미분화한 원석 가루를 50% 혼합한 수용액을, 1:1로 혼합한 용액에 원단을 6시간 이상 함침시켰다가 가열하여 탈수, 건조시키고, 상기의 원단을 다시 아로마 서로피(aroma therapy)의 향기치료제와 제오라이트 가루 및 숯가루를 1:2;3 정도의 비율로 혼합한 혼합물의 30% 수용액에 6시간 이상 함침시켰다가 냉각 건조시키도록 함으로써 원적외선을 장기간 발생함은 물론, 아로마 서로피에 의한 향기와 제오라이트 및 숯에 의한 탈취작용이 동시에 이루어져 격렬한 운동에도 땀으로 인한 악취를 방지하는 동시에 원단에서 은은한 향기를 발생하도록 하는 효과가 있는 것이다.As described above, according to the manufacturing method of the sportswear fabric which emits far-infrared ray of the present invention, it is mixed with the same amount of Haesong leaf, three hundred seconds, three kinds of gold, and thyme. The fabric was impregnated with a solution mixed with a 1: 1 mixture of a liquid boiled in water in a shade and a 50% mixture of undifferentiated raw gemstones such as elvan and maltite, which produced far infrared rays. After heating, dehydration and drying, the fabric was impregnated with 30% aqueous solution of a mixture of aroma therapy aroma therapy, zeolite powder and charcoal in a ratio of about 1: 2; 3 for 6 hours or more. In addition to long-term generation of far-infrared rays as well as cooling and drying, the fragrance by aroma each other and the deodorization effect by zeolite and charcoal are performed simultaneously, so that even sweat At the same time to prevent the odor caused by the fabric that will be effective to generate a faint fragrance.
Claims (1)