KR20040087002A - Polymer cement mortar composition for maintenance materials or finishing materials of building - Google Patents

Polymer cement mortar composition for maintenance materials or finishing materials of building Download PDF

Info

Publication number
KR20040087002A
KR20040087002A KR1020030021223A KR20030021223A KR20040087002A KR 20040087002 A KR20040087002 A KR 20040087002A KR 1020030021223 A KR1020030021223 A KR 1020030021223A KR 20030021223 A KR20030021223 A KR 20030021223A KR 20040087002 A KR20040087002 A KR 20040087002A
Authority
KR
South Korea
Prior art keywords
parts
weight
polymer
cement mortar
materials
Prior art date
Application number
KR1020030021223A
Other languages
Korean (ko)
Other versions
KR100519838B1 (en
Inventor
정성철
권승범
송명신
이용민
조선욱
Original Assignee
(주)대우건설
대영도장 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)대우건설, 대영도장 주식회사 filed Critical (주)대우건설
Priority to KR10-2003-0021223A priority Critical patent/KR100519838B1/en
Publication of KR20040087002A publication Critical patent/KR20040087002A/en
Application granted granted Critical
Publication of KR100519838B1 publication Critical patent/KR100519838B1/en

Abstract

PURPOSE: A polymer cement mortar composition for a repairing or finishing material of construction is provided, to improve adhesive strength, durability and easiness in construction by using a redispersible resin or polymer emulsion and a cement mortar. CONSTITUTION: The polymer cement mortar composition comprises 30-60 parts by weight of white cement; 30-50 parts by weight of silica; 10-20 parts by weight of calcium carbonate; 2-6 parts by weight of an ethylene vinyl acetate-vinyl versatate copolymer-based redispersible polymer, a polyacryl-based redispersible polymer, or their mixture; 0.2-0.6 parts by weight of a silicon-based antifoaming agent; 0.01-0.2 parts by weight of a cellulose salt; and 0.5-1.0 parts by weight of a superplasticizer comprising a naphthalene-formaldehyde sulfate condensate as a main component.

Description

건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물{Polymer cement mortar composition for maintenance materials or finishing materials of building}Polymer cement mortar composition for maintenance materials or finishing materials of building}

본 발명은 내구성능이 저하된 바닥마감의 성능복원을 위해 열화된 콘크리트의 보수, 타일표면의 마감, 낡고 더러워진 바닥재의 보수 등 건축물의 리-모델링 뿐만 아니라, 신축건물의 주차장 등의 바닥마감재 공법에 적합한 재료인 폴리머 시멘트 모르터 조성물에 관한 것으로서, 재유화형 분산 수지 또는 폴리머 에멀젼과 시멘트 모르터의 특성을 복합적으로 이용함으로써, 부착강도 및 내구성이 우수하고 시공이 용이한, 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물에 관한 것이다.The present invention is suitable for the construction of floors such as repair of deteriorated concrete, finishing of tile surfaces, repair of old and dirty flooring materials, as well as floor finishing materials for new parking lots, etc. The present invention relates to a polymer cement mortar composition, which is a material, and is a polymer cement mortar composition for a repair or finishing material of a building that has excellent adhesion strength, durability, and ease of construction by using a combination of properties of a reemulsifying dispersion resin or polymer emulsion and a cement mortar. It is about.

폴리머 모르터 복합체와 관련하여, 한국 공개특허 특2000-0000485에서는, 폴리머 모르터를 제조함에 있어 불포화 폴리에스테르 모르터 수지를 결합재로 하여 금형몰드에 넣고 20℃에서 양생하여 제조하는 것을 개시하였다. 그러나, 이 발명은 결합재로 오르토프탈산염계 불포화 폴리에스테르, 충전재, 골재, 폴리스티렌수지(PS), 발포폴리스티렌(EPS)/폴리스티렌수지(PS), 메틸에틸케톤 퍼옥사이드 등을 사용함으로 인하여 양생이 곤란하고, 일반 건축물에서 다양한 형태로의 적용이 불편하여 활용범위가 성형품에만 국한되는 단점이 있다.Regarding the polymer mortar composite, Korean Patent Laid-Open Publication No. 2000-0000485 discloses preparing a polymer mortar by using an unsaturated polyester morter resin as a binder and curing it at 20 ° C. However, the present invention is difficult to cure due to the use of orthophthalate unsaturated polyester, filler, aggregate, polystyrene resin (PS), expanded polystyrene (EPS) / polystyrene resin (PS), methyl ethyl ketone peroxide, etc. as a binder. However, it is inconvenient to apply to various forms in general buildings, and its range of application is limited to molded products.

또한, 한국공개특허 특2001-0046911에서는 폴리머 모르터와 시멘트 모르터 복합체를 제조함에 있어 중앙에 제거 가능한 격막을 설치한 후 모르터가 경화되기 전에 격막을 제거하여 모르터를 혼합시키는 방법을 제시하고 있다. 이 발명은 폴리머 성분으로 불포화 폴리에스테르 수지를 사용하고 있으며, 별도로 시멘트 모르터를 제조하여 혼합하는 공정을 거친다. 그러나, 이 발명도 다양한 형태로의 적용이 필요한 건설 시공현장에서 사용이 불가능한 문제점이 있다.In addition, Korean Patent Laid-Open No. 2001-0046911 proposes a method of mixing a mortar by removing a diaphragm before the mortar is cured after installing a removable diaphragm in the center of manufacturing a polymer mortar and a cement mortar composite. This invention uses an unsaturated polyester resin as a polymer component, and goes through the process of manufacturing and mixing a cement mortar separately. However, this invention also has a problem that can not be used in the construction site that needs to be applied in various forms.

상기의 특허에 의해 개시된 성분 이외에도 일반적으로 사용되는 재료로서 에폭시 수지, 우레탄 수지 등이 있다. 그러나, 이러한 수지들은 반드시 주제와 경화제, 기타 첨가제를 사용하여야 하는데, 이들 주제 및 경화제는 휘발성 재료로서 사용시 환경적인 문제를 유발한다. 또한, 이들 에폭시 및 우레탄 수지는 물이 있는 곳에서는 사용이 곤란하며, 사용 후에도 물 또는 습기에 의해 많은 하자가 발생하는 실정이다.In addition to the components disclosed by the above patents, generally used materials include epoxy resins and urethane resins. However, these resins must use a base material, a hardener, and other additives, which cause environmental problems when used as a volatile material. In addition, these epoxy and urethane resins are difficult to use where there is water, and even after use, many defects are generated by water or moisture.

불포화 폴리에스테르계 폴리머 시멘트 모르터재는 주제인 불포화 폴리에스테르 수지와 경화제 및 촉진제 등으로 이루어진다. 여기에 충전재나 기타 재료를 첨가하여 조합한 것을 폴리에스테르수지 폴리머 시멘트 모르터라 하는데, 이것은 주제에 경화제 및 촉진제를 각각 소량첨가 혼합할 경우 주제중의 불포화 폴리에스테르 단량체가 상온에서 공중합 반응하고 겔상태를 거쳐 불용, 불융의 열경화성 중합체가 되는 성질을 이용한 것이다. 따라서, 이들은 열경화성 수지계 재료라 할 수있으며, 본 발명에서 이루고자 하는 상온에서 물을 이용한 고강도, 고부착 성능을 발휘하는 폴리머 시멘트 모르터 재료와는 매우 상이하다.The unsaturated polyester polymer cement mortar material is composed of unsaturated polyester resin, a curing agent, accelerator, and the like. The combination of fillers and other materials added to this is called polyester resin polymer cement mortar, which means that when a small amount of curing agent and accelerator are added to the main body, the unsaturated polyester monomer in the main body is copolymerized at room temperature and gels. It uses the property to become an insoluble and insoluble thermosetting polymer through it. Therefore, they may be referred to as thermosetting resin materials, and are very different from polymer cement mortar materials exhibiting high strength and high adhesion performance using water at room temperature to be achieved in the present invention.

따라서, 본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위해 안출된 것으로서, 기존의 폴리머 보수재 및 마감재가 별도의 경화제를 사용해야 하고, 휘발성 재료를 사용하여 시공해야 하는 문제점을 개선하기 위하여 시멘트를 주재료로 하여 수경화성을 도입하고, 시멘트 재료의 취약점인 취성파괴 및 낮은 부착력의 개선을 위하여 재분산성 폴리머를 사용하며, 기타 시멘트 분산제 등의 재료를 사용함으로써, 시공장비나 시공장소에 구애받지 않고 시공가능하고, 기존에 시공된 재료의 제거없이 적용가능한, 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물을 제공하는 것을 목적으로 한다.Therefore, the present invention has been made to solve the problems of the prior art as described above, the existing polymer repair materials and finishes must use a separate hardener, and to improve the problem that the construction must be made using a volatile material cement main material It is possible to construct irrespective of construction equipment or factory by introducing hydrocurability, using redispersible polymer to improve brittle fracture and low adhesion, which are weaknesses of cement materials, and other materials such as cement dispersant. In addition, an object of the present invention is to provide a polymer cement mortar composition for repair or finishing materials of buildings, which can be applied without the removal of existing construction materials.

또한, 본 발명은 콘크리트와의 친화성이 우수한 재분산성 폴리머 및 시멘트를 주재료로 사용함으로써, 신축건물의 콘크리트 표면에 마감재로 시공할 수 있고, 기존에 사용되어진 타일, 에폭시 수지 마감재, 우레탄 수지 마감재, 기타 레진 모르터 등의 표면 위에 안정하게 시공될 수 있는, 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물을 제공하는 것을 목적으로 한다.In addition, the present invention can be used as a finishing material on the concrete surface of the new building by using a redispersible polymer and cement having excellent affinity with concrete as a main material, and the tiles, epoxy resin finish, urethane resin finish, It is an object of the present invention to provide a polymer cement mortar composition for repair or finishing materials of buildings, which can be stably constructed on surfaces of other resin mortars and the like.

상기한 바와 같은 목적을 달성하기 위하여, 본 발명에 의한 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물은, 백시멘트 30 내지 60 중량부, 규사 30 내지 50 중량부, 탄산칼슘 10 내지 20 중량부, 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머, 폴리아크릴계 재분산성 폴리머, 또는 이들의 혼합물 2 내지 6 중량부, 실리콘계 소포제 0.2 내지 0.6 중량부, 셀루로오스 염 0.01 내지 0.2 중량부, 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제 0.5 내지 1.0 중량부가 혼합된 것을 특징으로 한다.In order to achieve the above object, the polymer cement mortar composition for repair or finishing materials for buildings according to the present invention, 30 to 60 parts by weight of cement, 30 to 50 parts by weight of silica sand, 10 to 20 parts by weight of calcium carbonate, ethylene 2 to 6 parts by weight of a redispersible polymer of a vinyl acetate-vinyl vasate copolymer series, a polyacrylic redispersible polymer, or a mixture thereof, 0.2 to 0.6 parts by weight of a silicone antifoaming agent, 0.01 to 0.2 parts by weight of cellulose salt, naphthalene- It characterized in that 0.5 to 1.0 parts by weight of a fluidizing agent based on formaldehyde sulfate condensate is mixed.

본 발명에 의한 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물에 있어서, 상기 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머 및 폴리아크릴계 재분산성 폴리머는, 폴리머 시멘트 모르터의 부착강도를 향상시키고, 시멘트 모르터 내부에 점착성 필름을 형성시키기 위한 재료로 사용되는 것을 특징으로 한다.In the polymer cement mortar composition for repair or finishing materials for buildings according to the present invention, the ethylene vinyl acetate-vinyl vasate copolymer-based redispersible polymer and polyacrylic redispersible polymer improve the adhesion strength of the polymer cement mortar, It is used as a material for forming an adhesive film inside the cement mortar.

본 발명에 의한 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물에 있어서, 상기 셀루로오스 염 및 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제는, 폴리머 시멘트 모르터의 분무 시공성 및 작업성을 확보하기 위해 사용되는 것을 특징으로 한다.In the polymer cement mortar composition for repair or finishing materials for buildings according to the present invention, the fluidizing agent mainly composed of the cellulose salt and the naphthalene-formaldehyde sulfate condensate ensures sprayability and workability of the polymer cement mortar. It is characterized by being used to.

본 발명에 의한 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물은, 기본재료로 백시멘트, 입도 크기가 제어된 인조규사, 콘크리트 및 타일 등에 대한 부착력을 증대시키기 위한 폴리머 에멀젼, 및 통기성을 발현해 주는 실리콘계 폴리머를 사용한다.The polymer cement mortar composition for repairing or finishing materials of buildings according to the present invention is a silicone-based resin that expresses breathability as a base material, a polymer emulsion for increasing adhesion to a back cement, a grain size controlled artificial silica, concrete and tiles, and the like. Use a polymer.

재유화형 분말수지는, 합성수지 에멀젼을 건조 분무시킨 것으로서 물을 가했을때 재유화(Redispersion)되는 아크릴계, 초산비닐계, 염화비닐계 등의 합성수지이며, 시멘트계 경화체의 압축강도, 휨강도, 접착강도, 내구성, 내마모성, 방수성능 등을 향상시키는 특성을 갖는다.Re-emulsified powder resin is a synthetic resin emulsion that is dried and sprayed, and is a synthetic resin such as acryl, vinyl acetate, and vinyl chloride which is re-emulsified when water is added.The cemented hardened material has a compressive strength, bending strength, adhesive strength, durability, It has properties to improve wear resistance, waterproof performance, and the like.

본 발명에서는 재유화형 분말수지로서 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머를 사용는데, 이 재분산성 폴리머는 다른 시멘트 혼화용 폴리머에 비하여 취급이 편리할 뿐만 아니라, 내수성, 내알카리성, 및 내후성이 우수한 필름을 형성한다.In the present invention, a redispersible powder resin uses a redispersible polymer of the ethylene vinyl acetate-vinyl vasate copolymer series, which is more convenient to handle than other cement admixture polymers, and has excellent water resistance, alkali resistance, And a film having excellent weather resistance.

또한, 본 발명에서 사용되는 실리콘계 소포제는 유화상태가 우수하며 취급이 용이하고, 소량으로도 뛰어난 억포 및 소포력을 나타낸다.In addition, the silicone antifoaming agent used in the present invention is excellent in emulsification state, easy to handle, and exhibits excellent suppression and defoaming force even in a small amount.

본 발명에서는 유동화제로서 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제를 사용하는데, 이 유동화제는 초기강도를 증진시키고, 강도의 손실없이 높은 작업성 및 유동성을 부여한다.In the present invention, a fluidizing agent based on naphthalene-formaldehyde sulfate condensate is used as a fluidizing agent, which enhances initial strength and gives high workability and fluidity without loss of strength.

이하, 실시예를 들어 본 발명의 구성 및 발명 효과를 보다 상세하게 설명한다. 아래의 실시예는 본 발명의 내용을 설명하나, 본 발명의 내용이 여기에 한정되지는 않는다.Hereinafter, the configuration and the effects of the present invention will be described in more detail with reference to Examples. The following examples illustrate the content of the invention, but the content of the invention is not limited thereto.

<실시예 1><Example 1>

실시예 1에서는 백시멘트 800g, 정선된 백규사 1000g, 정선된 탄산칼슘 200g, 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머 50g, 실리콘계 소포제 4g, 셀루로오스 염 0.3g, 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제 15g을 건식으로 완전하게 혼합한 후, 물을 430g 첨가한 후 1분당 회전수 20으로 서서히 5분간 교반하였다. 혼합물을 압력 5기압 이상에서 시멘트 모르터 콘으로 분무 시공하였다.In Example 1, 800 g of white cement, 1000 g of selected white sand sand, 200 g of selected calcium carbonate, 50 g of redispersible polymer based on ethylene vinyl acetate-vinyl vasate copolymer, 4 g of silicone-based antifoam, 0.3 g of cellulose salt, naphthalene-form 15 g of a fluidizing agent mainly composed of an aldehyde sulfate condensate was completely mixed in a dry manner, and then 430 g of water was added thereto, followed by stirring for 5 minutes at 20 revolutions per minute. The mixture was sprayed into a cement mortar cone at a pressure of at least 5 atmospheres.

<실시예 2><Example 2>

실시예 2에서는 백시멘트 1000g, 정선된 백규사 1000g, 정선된 탄산칼슘 200g, 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머 25g, 폴리아크릴계 재분산성 폴리머 25g, 실리콘계 소포제 4g, 셀루로오스 염 0.5g, 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제 20g을 건식으로 완전하게 혼합한 후, 물을 430g 첨가한 후 1분당 회전수 20으로 서서히 5분간 교반하였다. 혼합물을 압력 5기압 이상에서 시멘트 모르터 콘으로 분무 시공하였다.In Example 2, 1000 g of white cement, 1000 g of selected white sand, 200 g of selected calcium carbonate, 25 g of redispersible polymer based on ethylene vinyl acetate-vinyl vasate copolymer, 25 g of polyacrylic redispersible polymer, 4 g of silicone defoamer, cellulose Dry mixing of 0.5 g of salt and 20 g of a fluidizing agent mainly composed of naphthalene-formaldehyde sulfate condensate was carried out, and after adding 430 g of water, the mixture was stirred slowly at 20 revolutions per minute for 5 minutes. The mixture was sprayed into a cement mortar cone at a pressure of at least 5 atmospheres.

본 발명의 특성을 확인하기 위하여, 상기에서 제조된 폴리머 시멘트 모르터의 물성을 측정하였으며, 그 결과는 하기 표 1에 나타내었다.In order to confirm the characteristics of the present invention, the physical properties of the polymer cement mortar prepared above were measured, and the results are shown in Table 1 below.

항 목Item 단위unit 측정결과Measurement result 측정방법How to measure 1. 타일과의 부착강도1. Strength of adhesion with tiles kgf/cm2 kgf / cm 2 8.58.5 KS F 4715-97KS F 4715-97 2. 모르터와의 부착강도2. Bonding strength with mortar kgf/cm2 kgf / cm 2 2121 KS F 4715-97KS F 4715-97 3. 내충격성3. Impact resistance 육안관찰Visual observation 이상 없음clear KS F 4715-97KS F 4715-97 4. 난연성4. Flame retardant 난연1급Flame retardant class 1 KS F 2271-98KS F 2271-98

1. 강도 및 부착강도1. Strength and adhesion

주택의 천정이나 벽체에 사용되는 마감재는 굳이 강도가 클 필요는 없다. 그러나, 바닥 마감재는 일정이상의 강도가 요구된다. 특히, 부착강도는 제품 자체의 특성을 좌우한다고 보아야 할 것이다.The finishing materials used for ceilings and walls of houses do not have to be strong. However, floor finishes require a certain level of strength. In particular, it should be seen that the adhesion strength influences the characteristics of the product itself.

또한, 리-모델링을 위해서는 기존에 사용한 재료를 제거하여야 하나, 기존에사용되어진 재료가 완전하게 제거되지 않을 수 있다는 점을 감안한다면, 기존에 사용되어진 재료의 표면 위에 덧씌우는 작업이 필요하다. 이때, 기존 재료와의 부착성능이 무엇보다도 중요하다.In addition, the re-modeling to remove the previously used material, but considering that the previously used material may not be completely removed, it is necessary to overwrite the surface of the previously used material. At this time, the adhesion performance with the existing material is important above all.

본 발명의 폴리머 시멘트 모르터는 모르터와의 부착강도가 21kgf/㎠ 정도로 나타나는데, 이는 시멘트와 재유화형 분말수지와의 이상적인 조화로 인하여 재유화형 폴리머와 혼용된 시멘트가 콘크리트 피착면(천장, 벽, 바닥)에 침투되어 콘크리트층과 일체화를 이루기 때문이다.In the polymer cement mortar of the present invention, the adhesive strength of the mortar is about 21 kgf / cm 2, which is due to the ideal balance between the cement and the reemulsified powder resin. This is because it penetrates into and integrates with the concrete layer.

또한, 본 발명은 시멘트 페이스트내 개기공 상태의 불안정한 구조를 혼련과정에서 폐기공 상태의 매우 안정적인 구조(폐기공 내부를 재유화형 폴리머로 코팅)로 형성시킴으로써, 2차적으로 물이 혼입되어도 수축이나 벽, 바닥의 갈라짐이 전혀 없다.In addition, the present invention is to form an unstable structure of the open pore state in the cement paste as a very stable structure of the closed pore state (coating the inside of the pores with a re-emulsified polymer) during the kneading process, so that even if water is mixed secondly, There is no crack at the bottom.

2. 연 소 성2. Combustibility

일반적인 에폭시나 우레탄 마감재는 난연재료의 첨가로 자기소화성은 있지만, 화재시 연소하는 가연성 물질이다. 따라서, 시공이나 보관시에 화기와 접촉하지 않도록 충분한 주의가 필요하며, 내부 마감재로의 시공도 피하여야 한다. 이를 보완하기 위하여 본 발명의 폴리머 시멘트 모르터는 원재료 자체가 불연재로 구성되어 있어 불에 타지 않고, 화재시 연기도 발생되지 않으므로 건축물 내부의 마감재로 적합한 재료라고 할 수 있다.Typical epoxy or urethane finishes are self-extinguishing with the addition of flame retardant materials, but are combustible materials that burn in the event of fire. Therefore, sufficient care must be taken to avoid contact with fire during construction and storage, and construction with internal finishing materials should also be avoided. In order to compensate for this, the polymer cement mortar of the present invention is composed of a non-combustible material, so it does not burn and does not generate smoke in a fire.

3. 유 해 성3. Harmful

무기질 섬유상의 내외장인 암면, 유리면 등은 시공시 피부와 접촉하면 자극을 유발하는 문제가 있고, 반면 유기계 개보수재는 연소시 연소가스로부터 유독성 물질이 배출되는 위험이 있다. 특히, 요소 수지를 적용하여 만든 마감재는 사용중 인체에 해로운 포름알데히드가 방출되어 캐나다 및 미국 일부 지역에서는 사용을 금지하고 있다.Rock wool, glass wool, etc., which are internal and external on inorganic fibers, cause irritation when they come into contact with the skin during construction, while organic remodeling materials have a risk of toxic substances being emitted from combustion gases during combustion. In particular, finishes made with urea resin are banned in some parts of Canada and the United States because formaldehyde is released during use.

이러한 유해성을 배제하기 위해서 본 발명의 폴리머 시멘트 모르터는 섬유상 물질인 암면, 유리면 등을 사용하지 않고, 일반적인 실리카를 시멘트와 함께 혼용하여 제조함으로써 피부와 접촉시 자극이 없고, 화재시 연소되지 않으며, 유독가스 또한 배출되지 않는다.In order to exclude such harmfulness, the polymer cement mortar of the present invention does not use fibrous rock wool or glass wool, and is prepared by mixing general silica with cement so that it is not irritated upon contact with the skin and does not burn in a fire. No gas is also emitted.

본 발명에 따른 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물은, 시멘트 모르터의 장점과 폴리머의 장점이 결합된 복합재료로서, 콘크리트, 타일, 금속 등에의 부착력이 우수하여 노후화 및 열화된 건축물의 개·보수용뿐만 아니라, 신축 건축물의 내·외장 마감용으로 사용될 수 있다.The polymer cement mortar composition for repair or finishing materials for buildings according to the present invention is a composite material combining the advantages of cement mortar with the advantages of polymer, and has excellent adhesion to concrete, tiles, metals, etc. In addition to repair, it can be used for interior and exterior finishing of new buildings.

Claims (3)

백시멘트 30 내지 60 중량부, 규사 30 내지 50 중량부, 탄산칼슘 10 내지 20 중량부, 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머, 폴리아크릴계 재분산성 폴리머, 또는 이들의 혼합물 2 내지 6 중량부, 실리콘계 소포제 0.2 내지 0.6 중량부, 셀루로오스 염 0.01 내지 0.2 중량부, 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제 0.5 내지 1.0 중량부가 혼합된 것을 특징으로 하는 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물.30 to 60 parts by weight of back cement, 30 to 50 parts by weight of silica sand, 10 to 20 parts by weight of calcium carbonate, redispersible polymer of ethylene vinyl acetate-vinyl vasate copolymer series, polyacrylic redispersible polymer, or mixtures thereof 2 to 6 parts by weight, silicone antifoaming agent 0.2 to 0.6 parts by weight, cellulose salt of 0.01 to 0.2 parts by weight, building materials, characterized in that the mixing agent 0.5 to 1.0 parts by weight of a naphthalene-formaldehyde sulfate condensate as a main component Or a polymer cement mortar composition for the finish. 제 1 항에 있어서,The method of claim 1, 상기 에틸렌 비닐 아세테이트-비닐 바사테이트 공중합물 계열의 재분산성 폴리머 및 폴리아크릴계 재분산성 폴리머는, 폴리머 시멘트 모르터의 부착강도를 향상시키고, 시멘트 모르터 내부에 점착성 필름을 형성시키기 위한 재료로 사용되는 것을 특징으로 하는 건축물의 보수재 또는 마감재용 폴리머 시멘트 모르터 조성물.The redispersible polymer and the polyacrylic redispersible polymer of the ethylene vinyl acetate-vinyl vasate copolymer series are used as a material for improving the adhesion strength of the polymer cement mortar and forming an adhesive film inside the cement mortar. Polymer cement mortar composition for repair or finishing materials of buildings. 제 1 항에 있어서,The method of claim 1, 상기 셀루로오스 염 및 나프탈렌-포름알데히트 설페이트 축합물을 주성분으로 하는 유동화제는, 폴리머 시멘트 모르터의 분무 시공성 및 작업성을 확보하기 위해 사용되는 것을 특징으로 하는 건축물의 보수재 또는 마감재용 폴리머 시멘트모르터 조성물.The fluidizing agent mainly composed of the cellulose salt and the naphthalene-formaldehyde sulfate condensate is used to secure spray workability and workability of the polymer cement mortar, and the polymer cement mortar for repair or finishing materials of buildings. Composition.
KR10-2003-0021223A 2003-04-04 2003-04-04 Polymer cement mortar composition for maintenance materials or finishing materials of building KR100519838B1 (en)