KR20040043407A - Cement moltal product and the manufacture method that glaze layer is formed - Google Patents

Cement moltal product and the manufacture method that glaze layer is formed Download PDF

Info

Publication number
KR20040043407A
KR20040043407A KR1020020071654A KR20020071654A KR20040043407A KR 20040043407 A KR20040043407 A KR 20040043407A KR 1020020071654 A KR1020020071654 A KR 1020020071654A KR 20020071654 A KR20020071654 A KR 20020071654A KR 20040043407 A KR20040043407 A KR 20040043407A
Authority
KR
South Korea
Prior art keywords
cement mortar
article
mortar product
product
glaze
Prior art date
Application number
KR1020020071654A
Other languages
Korean (ko)
Inventor
최풍시
Original Assignee
광일산업 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 광일산업 주식회사 filed Critical 광일산업 주식회사
Priority to KR1020020071654A priority Critical patent/KR20040043407A/en
Publication of KR20040043407A publication Critical patent/KR20040043407A/en

Abstract

PURPOSE: A manufacturing method for a cement mortar article provided with a glazed layer is provided to make mass production possible, to use cement mortar articles for various purposes and to increase strength. CONSTITUTION: The manufacturing method for the cement mortar article provided with the glazed layer comprises the steps of: preparing materials and frit glaze for shaping the cement mortar article(11); shaping the cement mortar article of various shapes using the prepared materials(12); curing the shaped cement mortar article(13); pre-heating the cured cement mortar article(21); applying frit glaze to the pre-heated cement mortar article(22); drying up the glazed cement mortar article in the shade, then in a drier(23); plasticizing the dried cement mortar article in an oven(24); cooling down the plasticized cement mortar article(25); soaking the cement mortar article in water, then taking out(26); steam-curing the cement mortar article to recover strength(27); and piling up the cement mortar articles in the open(31), then shipping(32).

Description

유약층이 형성된 시멘트 몰탈 제품 및 그 제조방법{Cement moltal product and the manufacture method that glaze layer is formed}Cement mortal product and the manufacture method that glaze layer is formed}

본 발명은 건축용 내,외장재로 사용되는 시멘트 몰탈 제품의 표면에 유약을 발라 소성시킨 유약층이 형성된 시멘트 몰탈 제품 및 그 제조 방법에 관한 것으로, 수명이 오래가고 저렴하며 대량 생산이 가능한 시멘트 몰탈 제품을 제공하게 되는것이다.The present invention relates to a cement mortar product having a glaze layer formed by glazing on a surface of a cement mortar product used as an interior and exterior material for construction, and a method of manufacturing the same. Will be provided.

건축용 내,외장재로 사용되는 시멘트 몰탈 제품은 타일, 벽면에 부착되는 판재 형태의 마감재, 지붕 장식구 등 다양한 소재가 개발되어 있으나, 모래와 시멘트 및 물을 재료로 하여 형성되는 기존의 시멘트 몰탈 제품은 저렴하게 대량 생산할 수 있는 이점은 있으나 일반 모래와 시멘트를 사용하게 되어 수분에 대하여 취약할 수밖에 없고, 강도가 낮아 수명이 짧은 단점이 있는 것이었다.Cement mortar products used as interior and exterior materials for building have been developed with various materials such as tiles, plate-like finishes attached to the walls, roof ornaments, etc. However, existing cement mortar products made of sand, cement, and water are used. There is an advantage that can be mass-produced inexpensively, but the use of ordinary sand and cement is bound to be vulnerable to moisture, and has a disadvantage of short life due to low strength.

이러한 문제점을 해결하기 위하여 점토 100%를 이용하여 타일 및 내, 외장용 마감재를 제작하여 수명이 짧고 수분에 취약한 기존 시멘트 몰탈 제품에 대한 문제점을 해결하고 있으나, 점토를 이용하여 제작하는 점토 제품은 점토를 수집하여 제품의 모양을 형성하는 과정이 쉽지 않고, 또한 가격이 비싼 단점이 있는 것이었다.In order to solve this problem, 100% of clay is used to produce tiles and interior and exterior finishes, which solves the problems of existing cement mortar products that are short in life and vulnerable to moisture, but clay products manufactured using clay The process of collecting and shaping the shape of the product was not easy, and the price was expensive.

본 발명은 상기된 문제를 해결하기 위하여 안출 된 것으로, 건축용 및 마감용으로 사용되는 시멘트 몰탈 제품의 표면에 유약을 도포한 후 이를 소성 시켜 강도가 높고 수명이 긴 시멘트 몰탈제품을 생산 하므로써 값싸고 견고한 시멘트 몰탈 제품의 대량생산이 가능하도록 한 것이다.The present invention has been made in order to solve the above problems, by applying a glaze on the surface of the cement mortar products used for construction and finishing and then firing it by producing a high strength and long-life cement mortar product cheap and robust It is to enable mass production of cement mortar products.

이러한 본 발명은 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와 포틀랜드 시멘트 및 물로 시멘트 몰탈 제품을 성형하고, 시멘트 몰탈 제품을 예열하여 저온에서 녹을 수 있는 프리트 유약을 도포하고 건조시킨 후 소성하고 공냉시킨 다음 물 담그기를 하고 스팀양생을 하여 강도회복을 시킴으로서 이루어지는 것으로, 시멘트 몰탈 제품의 표면에 유약을 발라 소성 시킨 견고하고 값싸며 대량생산이 용이한 시멘트 몰탈 제품을 제공할 수 있는 것이다.The present invention forms a cement mortar product with sand and portland cement and water made of non-metallic materials such as andesite, basalt, and silica sand, and preheats the cement mortar product to apply frit glaze that can be melted at low temperatures, and then calcined and air-cooled. It is made by immersing water and steaming to recover strength, and it is possible to provide cement mortar products that are hard, cheap and easy to mass-produce by applying glaze on the surface of cement mortar products.

도 1 은 본 발명의 유약층이 형성된 시멘트 몰탈 제품인 타일의 일 실시예 사시도1 is a perspective view of an embodiment of a tile which is a cement mortar product in which the glaze layer of the present invention is formed

도 2 는 도 1 에 도시된 제품의 확대 단면도2 is an enlarged cross-sectional view of the product shown in FIG.

도 3 은 본 발명의 유약층이 형성된 시멘트 몰탈 제품의 제조 공정도Figure 3 is a manufacturing process of the cement mortar product formed glaze layer of the present invention

[도면의 주요부분에 대한 부호의 설명][Explanation of symbols on the main parts of the drawings]

1 : 시멘트 몰탈제품2 : 유약층1: cement mortar product 2: glaze layer

12 : 성형공정22 : 유약도포 공정12: molding process 22: glaze coating process

24 : 소성공정25 : 냉각공정24 firing process 25 cooling process

27 : 스팀양생 공정27: steam curing process

본 발명은 시멘트 몰탈 제품(1)을 성형하여 양생하고, 양생된 시멘트 몰탈 제품(1)을 예열하여 프리트 유약을 도포하고 건조시킨 후 이를 소성 시키고 냉각시켜 스팀 양생시킴으로서 유약층(2)이 형성된 시멘트 몰탈 제품(1)을 제공하는 한편 시멘트 몰탈 제품(1)을 제조하는 방법을 제공하는 것으로, 수분에 강하고 수명이 길며 저렴하고 대량생산이 가능한 것이다.According to the present invention, the cement mortar product 1 is cured and cured. The cement mortar product 1 is preheated to apply frit glaze, dried, fired, cooled and steam cured, thereby forming a glaze layer 2. By providing a mortar product (1) while providing a method for producing a cement mortar product (1), it is resistant to moisture, long life, inexpensive and mass production is possible.

여기서 시멘트 몰탈 제품(1)은 건축물의 내,장재로 사용되는 타일, 벽면에 부착되는 판재 형태의 마감재로 사용되는 것으로, 점토를 이용하여 소성 건조시키지 않고 시멘트로 제작하여 수분에 강하고 강도가 높으며 대량생산이 가능하도록 하는 것이다.The cement mortar product (1) is used as a finishing material in the form of tiles attached to the walls and walls, used as interior and decoration of the building, and made of cement without plastic drying using clay, which is strong in moisture, high in strength, and bulky. To make it possible.

이러한 본 발명의 시멘트 몰탈 제품(1)은 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와 포틀랜드 시멘트 및 물을 이용하여 성형한 시멘트 몰탈제품(1)의 표면에 저온에서 녹는 프리트 유약을 발라 유약층(2)을 형성하므로서 구성된다.The cement mortar product (1) of the present invention is glazed by applying a frit glaze that melts at a low temperature on the surface of the cement mortar product (1) formed by using sand and portland cement and water made of nonmetal materials such as andesite, basalt, and silica sand. It is configured by forming the layer 2.

또한 본 발명의 시멘트 몰탈 제품의 제조방법은 시멘트 몰탈 제품(1)을 성형하기 위한 재료와 프리트 유약을 준비하는 재료준비공정(11)과, 준비된 재료를 이용하여 원하는 형상의 시멘트 몰탈 제품(1)을 성형하는 성형공정(12)과, 성형된 시멘트 몰탈 제품(1)을 양생하는 양생공정(13)과, 충분히 양생된 시멘트 몰탈 제품(1)을 예열 시키는 예열공정(21)과, 예열된 시멘트 몰탈 제품(1)에 프리트 유약을 도포하는 유약 도포공정(22)과, 유약이 도포된 시멘트 몰탈 제품(1)을 그늘에서 건조시키는 한편 건조로에서 건조시키는 건조공정(23)과, 건조된 시멘트 몰탈 제품(1)을 소성로에서 소성 시키는 소성공정(24)과, 소성된 시멘트 몰탈 제품(1)을 공냉 시키는 냉각공정(25)과, 공냉된 시멘트 몰탈 제품(1)을 물에 담갔다 꺼내는 물 담그기 공정(26)과, 물 담그기가 끝난 시멘트 몰탈 제품(1)을 스팀 양생시켜 강도를 회복시키는 스팀 양생공정(27)을 수행하므로서 이루어지는 것으로, 스팀 양생이 완료된 시멘트 몰탈 제품(1)은 야적공정(31)을 거친 후 출하공정(32)을 거치도록 하여 소비자에게 인도되도록 한다.In addition, the method for producing a cement mortar product of the present invention includes a material preparation step 11 for preparing a material for forming the cement mortar product 1 and frit glaze, and a cement mortar product 1 having a desired shape using the prepared material. Molding step 12 for forming a mold, curing step 13 for curing the molded cement mortar product 1, preheating step 21 for preheating the sufficiently cured cement mortar product 1, and preheated cement. Glaze application process 22 for applying frit glaze to mortar product 1, drying process 23 for drying glaze-coated cement mortar product 1 while drying in a drying furnace, and dried cement mortar A firing step 24 for firing the product 1 in a kiln, a cooling step 25 for air-cooling the fired cement mortar product 1, and a water dipping step for immersing and removing the air-cooled cement mortar product 1 in water. 26, and when water is finished It is made by performing the steam curing process (27) to restore the strength by steam curing the mortar product (1), the cement mortar product (1) after the steam curing is completed, the shipping process (32) To be delivered to consumers.

이하 본 발명의 각 제조 공정별로 상세히 살펴본다.Hereinafter, each manufacturing process of the present invention will be described in detail.

재료준비 공정(11)Material Preparation Process (11)

시멘트 몰탈 제품(1)을 제조하기 위하여 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와, 포틀랜드 시멘트, 물, 섬유 첨가제, 프리트 유약을 준비한다.In order to manufacture the cement mortar product 1, sand made of nonmetallic materials such as andesite, basalt, and silica sand, and portland cement, water, fiber additives, and frit glaze are prepared.

여기서 기존의 시멘트 몰탈 제품(1)은 모래와 시멘트 및 물을 이용하여 제품의 형상대로 프레싱하여 성형시키게 되나 이러한 재료로 제작된 제품은 소성과정에서 500oC 이상 소성시킬 경우 강도가 약해져 강도 회복이 되지 않으므로 기존 재료를 이용할 수 없으며, 고온에서도 팽창과 수축이 적고 강도회복이 이루어질 수 있는 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래를 사용하여야 한다.Here, the existing cement mortar product (1) is molded by pressing in the shape of the product by using sand, cement and water, but the product made of such a material is weak in strength when fired at 500 o C or higher during the firing process, thereby recovering strength. Because it is not used, existing materials cannot be used, and sand made of nonmetallic materials such as andesite, basalt, and silica sand, which have low expansion and contraction and can recover strength even at high temperatures, should be used.

성형공정(12)Molding Process (12)

재료준비 공정(11)에서 준비된 재료를 이용하여 통상의 방법대로 시멘트 몰탈 제품(1)을 성형하게 되는 것으로, 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와 포틀랜드 시멘트 및 물을 사용하여 원하는 형태의 시멘트 몰탈 제품(1)을 프레싱하여 제작한다.The cement mortar product 1 is molded according to a conventional method using the material prepared in the material preparation process 11, and the desired shape is made using sand, portland cement and water made of nonmetallic materials such as andesite, basalt, and silica sand. It is produced by pressing the cement mortar product (1).

여기서 보강용 섬유 첨가제를 첨가하여 시멘트 몰탈 제품(1)을 성형할 수 있으며, 상기 섬유첨가제는 소성중에 가스를 발생시키고 강도의 향상을 전환시키기 위하여 사용하는 것으로, 상기 섬유 첨가제는 필요에 따라 첨가를 선택할 수 있다.Wherein the cement mortar product (1) can be molded by adding a reinforcing fiber additive, and the fiber additive is used to generate gas during firing and to change the improvement of strength, and the fiber additive may be added as necessary. You can choose.

양생공정(13)Curing Process (13)

상기된 성형 공정(12)에서 성형된 시멘트 몰탈 제품(1)은 기존의 방법대로 충분한 양생이 이루어지게 한다.The cement mortar product 1 molded in the forming process 12 described above allows sufficient curing to occur in the conventional manner.

예열공정(21)Preheating Process (21)

양생공정(13)을 거쳐 충분히 양생된 시멘트 몰탈 제품(1)을 터널형 노(爐)를 통과시켜 예열을 하도록 하고, 시멘트 몰탈 제품(1)이 150oC를 유지하도록 한다.Cement mortar product (1) sufficiently cured through the curing process (13) to pass through the tunnel-type furnace to preheat, and the cement mortar product (1) to maintain 150 ° C.

유약도포 공정(22)Glaze Coating Process (22)

예열이 이루어진 시멘트 몰탈 제품(1)의 표면에 프리트 유약을 도포한다.A frit glaze is applied to the surface of the pre-heated cement mortar product 1.

여기서 프리트 유약은 기존 유약을 구성하는 성분인 SiO2, Al2O3, PbO, CaO, B2O3중에서 PbO와 B2O3의 함량을 높여 고온에서 저온으로 전환하여 녹을 수 있도록 약 800oC 에서 녹을 수 있게 하는 한편 녹는 온도를 조절하여 소성 가능한 성질을갖게 된다.Here, frit glaze is about 800 o to be dissolved in high temperature to low temperature by increasing the content of PbO and B 2 O 3 among SiO 2 , Al 2 O 3 , PbO, CaO, and B 2 O 3 that make up the existing glaze. It can be melted at C while controlling its melting temperature to be calcinable.

본 발명에 사용되는 유약은 800oC에서 녹게 되므로 시멘트 몰탈 제품(1)의 강도 회복에 문제가 없으나, 기존의 유약을 사용하면 1200oC에서 녹게 되어 소성후 강도 회복이 이루어지지 않기 때문에 사용할 수 없으며, 기존 유약은 점토로 이루어진 제품에만 사용이 가능한 것이다.Since the glaze used in the present invention melts at 800 o C, there is no problem in the strength recovery of the cement mortar product (1). However, when the existing glaze is used, the glaze melts at 1200 o C and thus cannot be used for strength recovery after firing. No existing glazes can be used only for products made of clay.

즉 본 발명은 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와 포틀랜드 시멘트 및 물을 사용하여 제조된 시멘트 몰탈 제품(1)에 사용되어 비교적 저온인 800oC 에서 녹게 되어 강도 회복을 시킬 수 있게 된다.That is, the present invention is used in cement mortar products (1) manufactured using sand and portland cement and water made of nonmetallic materials such as andesite, basalt, and silica sand, so that they can be melted at a relatively low temperature of 800 ° C. to recover strength. do.

건조공정(23)Drying Process (23)

프리트 유약이 도포된 시멘트 몰탈 제품(1)은 음지에서 하루정도 자연건조 시키고, 터널형 건조로를 통과시켜 건조시키도록 하되 상기 터널형 건조로는 200-500oC의 온도를 갖도록 하고, 시멘트 몰탈 제품(1)은 약 30분 정도 상기 터널형 건조로를 이동시켜 수증기를 완전히 증발시키도록 한다.The cement mortar product (1) coated with frit glaze is naturally dried in the shade for about a day and dried by passing through a tunnel-type drying furnace, but the tunnel-type drying furnace has a temperature of 200-500 o C, and a cement mortar product ( 1) moves the tunnel-type drying furnace for about 30 minutes to completely evaporate the water vapor.

소성공정(24)Firing Process (24)

건조 공정(23)에서 충분히 수증기가 제거된 시멘트 몰탈 제품(1)은 소성로로 이동시켜 650-900oC의 온도로 약 60분 정도를 지내게 하여 충분한 소성이 이루어지도록 한다.Cement mortar product (1) sufficiently steamed in the drying step 23 is moved to the firing furnace to spend about 60 minutes at a temperature of 650-900 ° C to ensure sufficient firing.

이때 프리트 유약은 충분히 녹아 소성되게 되며, 시멘트 몰탈 제품(1)의 강도도 손상되지 않고 소성이 종료되면 강도 회복이 이루어지게 된다.At this time, the frit glaze is sufficiently melted and fired, and the strength recovery of the cement mortar product 1 is completed without firing.

냉각공정(25)Cooling Process (25)

소성공정(24)을 거친 시멘트 몰탈 제품(1)은 바람을 이용하여 100oC의 온도를 가질 때까지 냉각시켜 주도록 한다.Cement mortar product (1) after the calcination process (24) is cooled to a temperature of 100 ° C by using wind.

물 담그기 공정(26)Water Dipping Process (26)

냉각공정(25)을 거친 시멘트 몰탈 제품(1)은 물에 15분 정도를 담가주어 수화반응이 빠르게 진행되도록 한다.Cement mortar product (1) after the cooling process (25) is soaked in water for about 15 minutes to allow the hydration reaction to proceed quickly.

스팀 양생 공정(27)Steam Curing Process (27)

물 담그기 공정(26)이 끝난 시멘트 몰탈 제품(1)은 70oC의 온도로 6-7시간 정도 스팀 양생이 이루어지도록 하여 충분한 강도회복이 이루어지도록 한다.Cement mortar product (1) after the water soaking process (26) is steam curing for 6-7 hours at a temperature of 70 ° C to ensure sufficient strength recovery.

야적공정(31)Field Processing (31)

스팀 양생 공정(27)까지 마친 시멘트 몰탈 제품(1)은 야적하여 둔다.The cement mortar product 1 which completed the steam curing process 27 is stored in a yard.

출하 공정(32)Shipping Process (32)

야적된 시멘트 몰탈 제품(1)을 수요자에게 출하한다.The unloaded cement mortar product (1) is shipped to the consumer.

이상의 공정에 의해 제조된 시멘트 몰탈 제품(1)은 도 1 및 도 2 와 같이 표면에 유약층(2)이 형성되는 것으로, 시멘트 몰탈 제품(1)의 구체적인 형상은 도시하지 않았으며, 그 형상이 다르다 하여 본 발명의 권리 범주를 벗어날 수는 없다.Cement mortar product (1) manufactured by the above process is that the glaze layer (2) is formed on the surface as shown in Figs. 1 and 2, the specific shape of the cement mortar product (1) is not shown, the shape is It does not differ from the scope of the present invention by different.

이상과 같이 본 발명은 시멘트 몰탈 제품의 표면에 유약층을 형성시킴으로서강도가 보강되고 수분에 취약한 문제점을 해결하는 한편 대량생산이 가능하도록 한 것으로, 시멘트 몰탈 제품을 다양한 용도로 사용할 수 있는 것이다.As described above, the present invention is to solve the problem of strengthening strength and vulnerable to moisture by forming a glaze layer on the surface of the cement mortar product, and to enable mass production, and the cement mortar product can be used for various purposes.

Claims (2)

안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와 포틀랜드 시멘트 및 물을 이용하여 성형한 시멘트 몰탈제품의 표면에 800oC 정도에서 녹는 프리트 유약을 바른 후 이를 소성시켜 유약층을 형성시킨 것을 특징으로 하는 유약층이 형성된 시멘트 몰탈 제품.A glaze layer was formed by applying a frit glaze that melted at about 800 o C on the surface of cement mortar products formed using non-metal sands such as andesite, basalt, and silica sand, and portland cement and water. Cement mortar product formed with a glaze layer. 안산암, 현무암, 규사 등의 비금속 재질로 이루어진 모래와 포틀랜드 시멘트 및 물을 이용하여 원하는 형상의 시멘트 몰탈 제품을 성형하고 이를 양생시키는 단계,Molding and curing the cement mortar product having a desired shape using sand and portland cement and water made of nonmetallic materials such as andesite, basalt, and silica sand, 충분히 양생된 시멘트 몰탈 제품을 150oC로 예열시키는 예열공정과,A preheating process to preheat the fully cured cement mortar product to 150 o C, 예열된 시멘트 몰탈 제품에 800oC에서 녹는 프리트 유약을 도포하는 유약 도포공정과,Glaze application process for applying frit glaze that melts at 800 o C to preheated cement mortar products, 유약이 도포된 시멘트 몰탈 제품을 그늘과 200-500oC의 온도로 건조로에서 건조시키는 건조공정과,A drying process of drying the glaze-coated cement mortar product in a shade and drying oven at a temperature of 200-500 o C, 건조된 시멘트 몰탈 제품을 650-900oC의 온도로 소성로에서 60분간 소성시키는 소성공정과,A firing process of firing the dried cement mortar product at a temperature of 650-900 o C for 60 minutes in a kiln, 소성된 시멘트 몰탈 제품을 100oC로 공냉시키는 냉각공정과,A cooling process of air-cooling the calcined cement mortar product to 100 o C, 공냉된 시멘트 몰탈 제품을 15분간 물에 담갔다 꺼내는 물담그기 공정과,Water soaking process of soaking air-cooled cement mortar product in water for 15 minutes, 물담그기가 끝난 시멘트 몰탈 제품을 70oC의 온도로 6-7시간 스팀 양생시키는 스팀 양생공정을 수행하여 제조되는 것을 특징으로 하는 유약층이 형성된 시멘트 몰탈 제품 제조 방법.A method of producing a cement mortar product with a glaze layer, characterized in that it is manufactured by performing a steam curing process for steam curing the soaked cement mortar product at a temperature of 70 o C for 6-7 hours.
KR1020020071654A 2002-11-18 2002-11-18 Cement moltal product and the manufacture method that glaze layer is formed KR20040043407A (en)