KR20040038953A - Artificial woods from vegetational grinding materials and clay

Info

Publication number: KR20040038953A
Application number: KR1020040025931A
Authority: KR
Inventors: 심만구
Original assignee: 심만구
Priority date: 2004-04-14
Filing date: 2004-04-14
Publication date: 2004-05-08

Abstract

PURPOSE: Provided are artificial woods formed of crushed vegetation materials and minerals, which are produced at a low cost, and have a light weight, and excellent flame resistance, insect resistance, moisture-proofing property and heat insulating property. CONSTITUTION: The artificial woods comprise a reinforcing layer having a certain width, and a layer(20) to be reinforced, which is obtained by applying a mixture comprising crushed vegetation materials, minerals and an adhesive on one surface of the reinforcing layer(10) at a predetermined thickness, wherein the layer(20) and the reinforcing layer(10) are wound many times and then compressed so that a cavity(50) having a certain inner diameter, into which a signal wire such as an electric wire is inserted, is formed.

Description

ARTIFICIAL WOODS FROM VEGETATIONAL GRINDING MATERIALS AND CLAY}

본 발명은 초목분쇄물과 광물질로 제작된 인조목에 관한 것으로, 보다 상세하게는 일정 넓이를 갖는 지류나 직물류의 일측면에 목재, 광물질, 식물섬유질등을 절삭하거나 파쇄한 분쇄물에 접착제를 혼합하여 피보강층을 형성하고, 내측에 중공이 형성되도록 말아서 성형된 초목분쇄물과 광물질로 제작된 인조목에 관한 것이다.The present invention relates to vegetated wood and artificial wood made of minerals, and more specifically, to one side of the paper or textiles having a predetermined width, the adhesive is mixed with the pulverized cutting or crushed wood, minerals, plant fiber, etc. By forming a reinforcement layer, the hollow is formed so as to form a vegetation crushed and artificial wood made of a mineral material.

건축자재로 이용되는 각목은 원목을 일정 두께로 켜서 제작된 것으로 가옥이나 빌딩을 포함한 각종 건축물등을 시공할 때 사용되고 있다.Each piece of wood used as a building material is made of solid wood with a certain thickness, and is used to construct various buildings including houses and buildings.

또한 마감재는 다양한 형태로 제작되는데, 일정한 형태로 성형한 후 외부 표면을 합성수지재나 무늬목등으로 접착하여 제작하여 건물의 내부 또는 외면의 겉면을 마감하는 데 쓰는 재료로써, 내·외부의 여러 가지 영향으로부터 건물을 보호하고 건물의 외양을 아름답게 한다.In addition, the finishing materials are produced in various forms, and after molding to a certain shape, the outer surface is bonded by synthetic resin or veneer, and used to finish the inside or outside of the building. Protect the building and beautify the look of the building.

그러나, 상기와 같은 일반적인 각목이나 마감재는 원목등을 사용하여 제작되기 때문에 방화, 방충, 방습, 보온등이 약하고, 사용 후에는 폐자재로 인해 환경을 오염시키는 문제가 있다. 다시 말해, 상기 각목이나 마감재로 만들어진 가구를 사용한후 폐기시에, 건물의 철거나 수리시에 다량의 산업쓰레기로 배출되어서 매립장으로 운반하여 매립함으로서 막대한 비용이 들어가며 상기 각목이나 마감재가 합성수지재등 화학성분이 혼합되어 제작된 제품은 폐기시에 토양과 수질을 오염시키고, 화재시에는 유독가스를 발생시켜 재산과 인명에 막대한 피해를 주고 있다.However, the general wood or finishing materials as described above are produced using solid wood, so that fire, insect repellent, moisture proof, and warmth are weak, and after use, there is a problem of polluting the environment due to waste materials. In other words, after using the furniture made of the wood or finishing materials, when discarded, during the ironing or repair of the building, a large amount of industrial waste is discharged and transported to a landfill site, which entails enormous costs, and the wood or finishing materials are chemicals such as synthetic resin materials. Products made of mixed ingredients pollute soil and water at the time of disposal, and in the event of fire, toxic gases are generated, causing enormous damage to property and life.

본 발명은 상기한 문제점을 해결하기 위한 것으로, 본 발명의 목적은 생산비가 저렴할 뿐만 아니라 제작이 용이하고, 방화, 방충, 방습, 보온의 효과가 탁월하고, 특히 무게가 가벼운 새로운 형태의 초목분쇄물과 광물질로 제작된 인조목를 제공하는 것이다. 다시 말해, 목재, 광물질, 식물섬유질등의 재료를 절삭하거나 파쇄한 분쇄물에 천연접착제를 혼합하고, 상기 혼합물의 일측면에 지류나 직물류로 형성된 보강층을 도포한 후 이를 목재등의 코어층을 중심으로 복수회 말아서 일정 두께가 형성되도록 감은 후에 일정한 압력으로 다양한 형상으로 형성되도록 제작된 인조목을 제공하는 것이다.The present invention is to solve the above problems, the object of the present invention is not only low production cost, but also easy to manufacture, excellent effect of fire, insect repellent, moisture proof, warm insulation, especially light weight new type of vegetation To provide artificial wood made of and minerals. In other words, the natural adhesive is mixed with a pulverized product that is cut or crushed materials such as wood, minerals, and plant fibers, and a reinforcing layer formed of paper or textiles is applied to one side of the mixture, and then the core is made of a core layer such as wood. After winding a plurality of times to form a predetermined thickness to provide a synthetic wood made to be formed in a variety of shapes at a constant pressure.

본 발명은 일정 넓이를 갖는 보강층(10)과, 상기 보강층(10)의 일측면에 초목분쇄물과 광물질 및 접착제로 혼합된 혼합물을 일정 두께로 형성한 피보강층(20)과, 상기 피보강층(20)과 보강층(10)이 복수회 말아지고 내부에 전선등의 신호선이 삽입될 수 있도록 일정 내경을 갖는 중공부(50)가 형성되도록 압착되어 제작된다.The present invention provides a reinforcing layer 10 having a predetermined width, a reinforcing layer 20 formed on a side of the reinforcing layer 10, a mixture of a mixture of vegetation powder, minerals and adhesive to a predetermined thickness, and the reinforcing layer ( 20) and the reinforcing layer 10 are rolled a plurality of times and pressed to form a hollow portion 50 having a predetermined inner diameter so that a signal line such as an electric wire can be inserted therein.

상기 초목분쇄물은, 볏짚, 보릿짚, 밀짚, 은행나무, 오동나무, 소나무, 닥나무로 이루어진 군에서 선택되어 지고, 상기 광물질은, 점토, 맥반석, 황토, 게르마늄석, 진흙, 규조토, 석회석으로 이루어진 군에서 선택되어지며, 상기 접착제는 송진이거나, 아교일 수 있다.The vegetation grind is selected from the group consisting of rice straw, barley straw, straw, ginkgo biloba, paulownia, pine, and mulberry, and the mineral is a group consisting of clay, ganban stone, loess, germanium stone, mud, diatomaceous earth, and limestone. The adhesive may be rosin or glue.

한편, 상기 보강층(10)은 지류 또는 직물류이다.On the other hand, the reinforcing layer 10 is a paper or textiles.

또한 상기 접착제는, 미역, 다시마, 파래등의 해조류를 사용하여 제조된 해조류 접착제이고, 온기를 발산하는 쌀풀이 더 첨가되거나, 냉기를 발산하는 보릿가루풀이나 밀가루풀이 더 첨가되어 제조될 수 있다.In addition, the adhesive is an algae adhesive prepared using seaweed such as seaweed, kelp, seaweed, etc., may be prepared by the addition of rice grass to radiate warmth, or the addition of barley flour or wheat flour to radiate cold air.

또한 본 발명의 초목분쇄물과 광물질로 제작된 인조목은 상기 피보강층(20)에 강도를 높이기 위한 보강재(40)가 더 삽입되어 구성되고, 상기 중공부(50)에 코어층(60)이 삽입되는 것이 바람직하다.In addition, the artificial wood produced by the vegetation crushed material and the mineral of the present invention is configured to further insert a reinforcing material 40 to increase the strength in the reinforcement layer 20, the core layer 60 in the hollow portion 50 It is preferred to be inserted.

상기 코어층(60)은 목재 또는 금속재 또는 합성수지재인 것을 특징으로 한다.The core layer 60 is characterized in that the wood or metal or synthetic resin.

도1a, 1b는 본 발명의 일실시예에 의한 초목분쇄물과 광물질로 제작된 인조목,Figure 1a, 1b is an artificial tree made of vegetation grinds and minerals according to an embodiment of the present invention,

도2a, 2b는 본 발명의 다른 실시예에 의한 초목분쇄물과 광물질로 제작된 인조목,Figure 2a, 2b is an artificial tree made of vegetation powder and mineral according to another embodiment of the present invention,

도3a, 3b은 본 발명의 또 다른 실시예에 의한 초목분쇄물과 광물질로 제작된 인조목,Figure 3a, 3b is an artificial tree made of vegetation powder and minerals according to another embodiment of the present invention,

도4a, 4b 및 도5는 본 발명에 의한 인조목을 제작하기 위한 설명도.Figures 4a, 4b and 5 are explanatory views for producing artificial wood according to the present invention.

< 도면의 주요 부분에 대한 부호의 설명 ><Description of Symbols for Main Parts of Drawings>

10: 보강층20: 피보강층10: reinforcement layer 20: reinforcement layer

30: 표면층40: 보강재30: surface layer 40: reinforcing material

50: 중공부60: 코어층50: hollow part 60: core layer

이하, 첨부된 도면을 참조하여 본 발명의 초목분쇄물과 광물질로 제작된 인조목을 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail the artificial wood produced from the vegetation pulverization and mineral of the present invention.

도1a, 1b은 본 발명의 일실시예에 의한 초목분쇄물과 광물질로 제작된 인조목이고, 도2a, 2b는 본 발명의 다른 실시예에 의한 초목분쇄물과 광물질로 제작된 인조목이며, 도3a, 3b은 본 발명의 또 다른 실시예에 의한 초목분쇄물과 광물질로 제작된 인조목이고, 도4a, 4b 및 도5는 본 발명에 의한 인조목을 제작하기 위한 설명도이다.Figure 1a, 1b is an artificial tree made of vegetation ground and mineral according to an embodiment of the present invention, Figures 2a, 2b is an artificial tree made of vegetation ground and mineral according to another embodiment of the present invention, Figures 3a, 3b is an artificial tree made of vegetation pulverization and minerals according to another embodiment of the present invention, Figures 4a, 4b and 5 is an explanatory diagram for producing the artificial tree according to the present invention.

본 발명의 바람직한 실시예에 의한 초목분쇄물과 광물질로 제작된 인조목은 상기 도1a 내지 도5에 도시된 바와 같이, 일정 넓이를 갖는 지류 또는 직물류로 형성된 보강층(10)과, 상기 보강층(10)의 일측면에 각종 초목분쇄물과 광물질 및 접착제로 혼합된 혼합물을 일정 두께로 형성한 피보강층(20)과, 상기 피보강층(20)과 보강층(10)이 복수회 감겨진 중심에 위치되는 코어층(60)으로 형성된다. 즉 상기 코어층(60)을 기준으로 일정한 두께가 되도록 복수회 말고, 일정한 형태를 갖도록 압착시킨 후 상기 코어층(60)을 제거하여 중공부(50)가 형성되도록 제작한다. 상기와 같이 제작된 인조목은 건축자재로 사용되는 경우에는 상기 코어층(60)을 제거하여 형성되는 중공된 중공부(50)에 전선 또는 각종 신호선을 삽입하여 시공이 더욱 편리하며, 따로이 전선매설관을 설치하지 않아도 되므로 비용이 감소되고 작업이 편리하게 된다. 또한, 전기적인 쇼트가 발생한 경우에는 상기 피보강층(20)이 방화벽 역할을 수행하기 때문에 화재의 발생을 효과적으로 방지하게 된다.Artificial tree made of vegetation powder and mineral according to a preferred embodiment of the present invention, as shown in Figures 1a to 5, the reinforcement layer 10 and the reinforcement layer 10 formed of a paper or a cloth having a certain width The reinforcement layer 20 formed with a predetermined thickness of a mixture of various vegetation powders and minerals and adhesives on one side of the) and the reinforcement layer 20 and the reinforcement layer 10 are located at the center of the plurality of times wound It is formed of the core layer 60. That is, rather than a plurality of times to have a predetermined thickness based on the core layer 60, after pressing to have a predetermined form to remove the core layer 60 is manufactured to form a hollow portion (50). When the artificial wood produced as described above is used as a building material, the construction is more convenient by inserting an electric wire or various signal lines into the hollow hollow part 50 formed by removing the core layer 60, and laying the wire separately. Eliminating the need to install pipes reduces costs and facilitates work. In addition, when an electrical short occurs, the reinforcement layer 20 serves as a firewall, thereby effectively preventing a fire.

또한, 상기 피보강층(20)에 목재, 금속재, 합성수지재등으로 형성된 보강재(40)를 더 삽입시켜 강도를 향상시킬 수 있으며, 상기 코어층(60)을 제거하지 않은 상태에서 건조하여 제작할 수 있다.In addition, the reinforcement layer 40 formed of wood, metal, synthetic resin, or the like may be further inserted into the reinforcement layer 20 to improve strength, and may be manufactured by drying the core layer 60 without removing the core layer 60. .

한편, 상기 제작된 인조목의 표면층(30)에는 지류, 직물류, 합성수재로 만들어진 무늬재를 더 부착시켜 마감재로도 사용할 수 있다. 이 때 상기 중공부(50)에 삽입되는 코어층(60)은 목재, 금속재, 합성수지재등을 사용한다. 여기서, 상기 도1a, 도2a, 도3a, 도4a는 피보강층(20) 위에 보강층(10)을 형성한 것이고, 상기 도1b, 도2b, 도3b, 도4b는 보강층(10) 위에 피보강층(20)을 형성한 것이다.On the other hand, the surface layer 30 of the artificial wood produced can be used as a finishing material by further attaching a pattern made of paper, fabrics, synthetic materials. In this case, the core layer 60 inserted into the hollow part 50 uses wood, metal, synthetic resin, or the like. 1A, 2A, 3A, and 4A form a reinforcement layer 10 on the reinforcement layer 20, and FIGS. 1B, 2B, 3B, and 4B show the reinforcement layer on the reinforcement layer 10. (20) was formed.

상기 피보강층(20)은 초목분쇄물, 광물질, 접착제를 40∼65 : 10∼40 : 10∼20 : 5∼10의 중량부 비율로 혼합 조성하는 것이 바람직하다. 다시 말해 상기 조성물을 혼합하여 일정한 두께와 넓이로 피보강층(20)을 형상한 후 상기 보강층(10)인 지류 또는 직물류를 상기 피보강층(20)의 상부면 또는 하부면에 안치한 후 상기 피보강층(20)을 중간 건조시킨다. 그 후 상기 코어층(60)을 안착시킨 후 일정한 두께가 되도록 코어층(60)을 중심축으로 하여 복수회 말고 다양한 형상으로 형성되도록 압착한 후 완전 건조시켜 제작한다. 이 때 상기 코어층(60)은 도1에 도시된 바와 같이 내부에 중공부(50)가 형성되도록 제거할 수도 있고, 도2에 도시된 바와 같이 상기 중공부(50) 내부에 삽입되도록 형성할 수 있다. 다시 말해, 상기 코어층(60)이 제거되는 경우에는 제작된 인조목의 무게가 감소하게 되고 상기 중공부(50)에 전선등 신호선이 수용되어 따로이 전선매설관을 설치할 필요가 없게 되며, 상기 코어층(60)을 삽입시켜 제작하는 경우에는 강도가 향상된다.The reinforcement layer 20 is preferably a mixed composition of vegetation powder, minerals, and adhesives at a weight part ratio of 40 to 65: 10 to 40: 10 to 20: 5 to 10. In other words, after the composition is mixed to form the reinforcement layer 20 in a constant thickness and width, the paper or fabric, which is the reinforcement layer 10, is placed on the upper or lower surface of the reinforcement layer 20, and then the reinforcement layer ( 20) is intermediately dried. Thereafter, the core layer 60 is seated, and then pressed to form a variety of shapes rather than a plurality of times with the core layer 60 as a central axis so as to have a constant thickness, and then completely dried. At this time, the core layer 60 may be removed so that the hollow portion 50 is formed therein as shown in FIG. 1, or may be formed to be inserted into the hollow portion 50 as shown in FIG. 2. Can be. In other words, when the core layer 60 is removed, the weight of the manufactured artificial wood is reduced, and signal lines such as wires are accommodated in the hollow part 50 so that the wire buried pipes do not need to be installed separately. When the layer 60 is produced by inserting, the strength is improved.

상기 초목분쇄물은 분말 또는 다양한 모양의 박피 또는 칩과, 100∼200메시 상태의 광물질과 물을 50 : 50의 중량비율로 혼합하여 제조하거나, 분말이나 다양한 모양의 박피와 칩으로 된 초목분쇄물과, 100∼200메시(mesh) 상태의 광물질과 물을 60 : 40 의 중량비율로 혼합하여 제조된 것을 사용하며, 여기에 해조류와 물을 40 : 60 의 중량비율로 하여 4∼8시간을 끓여서 제조된 해조류 접착제를 혼합하여 조성한다. 또한 여기에는 상기 혼합물의 5∼10 중량%의 보강재료를 더 포함시켜 조성할 수도 있다.The vegetation powder is prepared by mixing powder or various types of peeling or chips, and minerals and water in a 100 to 200 mesh state at a weight ratio of 50:50, or the vegetation powders of powder or various shapes of peeling and chips. And, it is prepared by mixing the minerals and water in the 100-200 mesh state in a weight ratio of 60: 40, and the seaweeds and water in a weight ratio of 40: 60 to boil 4 to 8 hours The prepared algae adhesive is mixed. The composition may further comprise 5 to 10% by weight of the reinforcing material of the mixture.

여기서 상기 초목분쇄물은 건조된 볏짚, 보릿짚, 밀짚, 은행나무, 오동나무, 소나무, 닥나무 등에서 적어도 하나 이상이 선택되어지고, 상기 광물질은 황토, 규조토, 맥반석, 석회석 중에서 적어도 하나 이상이 선택되어지고, 상기 해조류(미역, 다시마, 파래 등)는 4∼8 시간을 끓인 후 찌꺼기는 제거하고 60∼80℃를 유지시켜 해조류 접착제를 제작한다.Wherein the vegetation crushed is at least one or more selected from dried rice straw, barley straw, straw, ginkgo, paulownia, pine, mulberry, etc., and the mineral material is selected from at least one of ocher, diatomaceous earth, elvan, limestone , The seaweed (seaweed, kelp, seaweed, etc.) after boiling for 4 to 8 hours to remove the residue and to maintain the temperature of 60 to 80 ℃ to prepare the seaweed adhesive.

또한 상기 해조류 접착제에 온기를 발산하는 기능이 있는 보강재료로써 볏짚 분쇄물과 쌀풀을 혼합하여 제조한다. 또한 한기를 발산하는 기능이 있는 보강재료로써 보릿대짚 분쇄물이나 밀대짚 분쇄물등을 한기를 발산하는 기능이 있는 보릿가루풀이나 밀가루풀을 혼합하여 제조한 것을 사용한다.In addition, as a reinforcing material having a function of dissipating warmth to the algae adhesive is prepared by mixing rice straw milling and rice grass. In addition, as a reinforcing material having a function of releasing chill, a mixture of barley flour or flour paste having a function of releasing chilly barley straw crushed product or wheat straw crushed product is used.

본 발명에서는 상기 온기를 발산하거나, 냉기를 발산하는 기능에 따라 냉방용과 난방용 마감재로 각각 제조할 수 있다.In the present invention, depending on the function of dissipating the warmth or cold air, it can be prepared as a cooling and heating finish respectively.

한편, 상기 혼합조성물의 강도를 높이기 위한 보강재료로는 목화솜을 5∼50 ㎜ 상태로 세절하거나 또는 대마, 마닐라삼의 껍질, 펄프, 닥나무를 5∼50 ㎜ 상태로 세절한 것을 선택하여 더 혼합할 수 있다. 상기 목화솜은 흡습성, 보온성이 뛰어나고 탄력성이 우수하여 복원력이 풍부하며, 물과 함유되면 뭉치고 단단해지는 특성이 있고, 상기 대마는 마직물로서 물의 흡수나 발산이 빠르고 습윤시에는 강도가 더 좋아지는 특징을 가지고 있으며, 상기 습식조건에서 뿐만 아니라 건식조건에서도 재료의 강도를 증가시키는 재료로 알려져 있다.On the other hand, as a reinforcing material to increase the strength of the mixed composition, the cotton wool is finely cut into 5 to 50 mm or hemp, manila hemp bark, pulp, and mulberry to be cut into 5 to 50 mm. can do. The cotton wool is excellent in hygroscopicity, warmth and elasticity is rich in the restoring power, it is characterized by agglomeration and hardening when contained with water, the hemp is a hemp fabric, the absorption and divergence of water is fast and when wet, the strength is better It is known to be a material that increases the strength of the material not only in the wet condition but also in the dry condition.

즉, 상기 재료들을 상기 초목분쇄물, 광물질, 접착제와 혼합하게 되면, 수분에 의해 뭉치고 엉키는 특성에 의해 재료들의 결합력을 향상시키게 되어 외력에 의해 쉽게 파손되거나 구부러지는 현상을 최소화시킬 수 있게 된다.That is, when the materials are mixed with the vegetation grinds, minerals, and adhesives, the bonding strength of the materials is improved by the agglomeration and entanglement caused by moisture, thereby minimizing the easily broken or bent by external force.

한편, 상기 보강재료에는 방향성분을 추가로 혼합하여 사용할 수 있다. 즉, 송화가루나 허브를 추가로 혼합하여 제조할 수 있다.On the other hand, the reinforcing material may be used by further mixing the aromatic components. That is, it can be manufactured by further mixing calendula and herbs.

또한, 상기 해조류 접착제와는 별도로 송진 또는 아교를 접착제로 사용할 수 있다. 상기 송진 또는 아교는 자연과 친화적인 접착제로써 환경오염을 방지할 수 있게 된다.In addition, rosin or glue can be used as the adhesive separately from the seaweed adhesive. The rosin or glue is able to prevent environmental pollution as a natural and friendly adhesive.

상기 보강층(10)은 지류나 직물류를 사용하며, 특히 한지를 사용하는 것이 바람직하다.The reinforcement layer 10 uses paper or textiles, and in particular, it is preferable to use Hanji.

한편, 마감재로 사용할 경우에는 일정한 형상으로 압축 성형한 후에는 무늬목이나 합성수지재로 외부로 표출되는 부분을 접착하여 사용할 수 있지만, 상기 합성수지재는 환경오염을 유발할 수 있다.On the other hand, when used as a finishing material, after compression molding to a certain shape can be used by bonding the parts exposed to the outside with veneer or synthetic resin material, the synthetic resin material may cause environmental pollution.

상기와 같이 본 발명에 의한 인조목은 사용 후 폐기 시에는 천연소재로 제조되어 토양에서 분해가 용이하고 분해 시에는 퇴비의 기능을 갖게 된다.As described above, the artificial tree according to the present invention is prepared from natural materials at the time of disposal after use, so that it is easy to decompose in the soil and has a function of composting when decomposed.

앞에서 설명되고, 도면에 도시된 본 발명의 일실시예는 본 발명의 기술적사상을 한정하는 것으로 해석되어서는 안 된다. 본 발명의 보호범위는 청구범위에 기재된 사항에 의하여만 제한되고, 본 발명의 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상을 다양한 형태로 개량 변경하는 것이 가능하다. 따라서 이러한 개량 및 변경은 통상의 지식을 가진 자에게 자명한 것인 한 본 발명의 보호범위에 속하게 될 것이다.An embodiment of the present invention described above and illustrated in the drawings should not be construed as limiting the technical spirit of the present invention. The protection scope of the present invention is limited only by the matters described in the claims, and those skilled in the art can change and change the technical idea of the present invention in various forms. Therefore, such improvements and modifications will fall within the protection scope of the present invention, as will be apparent to those skilled in the art.

상기와 같이 본 발명에 의하면, 환경친화적이고 자연순환적인 초목분쇄물과 광물질로 혼합되고 말아져서 성형되기 때문에 인체에 유익하고, 재료를 자연에서 손쉽게 얻을 수 있기 때문에 경제적이며 생산비용이 저렴하고, 내부에 형성된 중공부를 통해 전선등의 신호선을 삽입할 수 있기 때문에 전선매설관을 사용하여 설치하는 비용이 절감될 수 있을 뿐만 아니라 천연자원을 효율적으로 사용할 수 있게 된다.As described above, according to the present invention, it is beneficial to the human body because it is mixed and rolled with environmentally friendly and natural cyclic vegetation powder and minerals, and because the material can be easily obtained from nature, it is economical and low in production cost. Signal lines, such as electric wires, can be inserted through the hollows formed in the wire, so that the cost of installing the wire buried pipe can be reduced and natural resources can be efficiently used.

또한, 접착제의 종류에 따라 냉방용과 난방용으로 각각 제조할 수 있어 사용 용도에 따라 냉방효과와 보온효과를 한층 더 향상시킬 수 있으며, 특히 보강재료인 섬유질의 목화솜, 대마, 마닐라삼, 펄프, 닥나무 중에 선택하여 혼합함으로써 재료의 결합강도를 향상시킬 수 있는 장점이 있다.In addition, depending on the type of adhesive can be produced for cooling and heating, respectively, it can further improve the cooling effect and the warming effect, depending on the intended use, especially fiber cotton cotton, hemp, manila hemp, pulp, mulberry There is an advantage of improving the bonding strength of the material by selecting and mixing in the.

한편, 본 발명은 환경 오염이 없고, 화재의 위험으로부터 안전한 난연성 인조목을 얻을 수 있을 뿐만아니라 주택과 생활공간의 공기를 맑고 깨끗하게 유지시켜서 쾌적한 생활환경을 인간에게 제공하여 건강한 신체를 유지하는데 도움이 되고 산과 들판에서 자라는 풀(잎)과 나무(잎)등으로 만들어진 초목분쇄물과 바다에서 자라는 해초와 자연에서 얻어지는 광물질등 친환경적인 소재를 활용함으로서 사용후 폐기시에 버리는 그 쓰레기를 작물을 재배하는 논과 밭에 양질의 퇴비로 사용할 수 있고, 자연친화적으로 순환이 되기 때문에 건축폐기물로 인한 토양오염을 획기적으로 예방할 수 있다.On the other hand, the present invention is not only environmental pollution, can obtain a flame-retardant artificial wood safe from the danger of fire, but also helps to maintain a healthy body by providing a pleasant living environment to humans by keeping the air of houses and living spaces clean and clean. By using eco-friendly materials such as vegetation grinds made of grass and leaves growing in mountains and fields, and seaweeds growing in the sea and minerals obtained from nature, the waste that is thrown away at the time of disposal after use is grown. It can be used as a good compost for rice fields and fields, and because it is circulated in nature, it can dramatically prevent soil pollution caused by building waste.

Claims

The reinforcement layer 10 having a predetermined width, the reinforcement layer 20 formed on a side of the reinforcement layer 10, a mixture of vegetation powder, minerals and adhesives to a predetermined thickness, and the reinforcement layer 20 and Artificial wood made of pulverized material and mineral material, characterized in that the reinforcing layer 10 is rolled a plurality of times and pressed to form a hollow portion 50 having a predetermined inner diameter so that a signal line such as an electric wire can be inserted therein .

The method of claim 1,

The vegetation grind is selected from the group consisting of rice straw, barley straw, straw, ginkgo biloba, paulownia, pine, and white

The mineral material, artificial wood made of pulverized plants and minerals, characterized in that selected from the group consisting of clay, elvan, loess, germanium stone, mud, diatomaceous earth, limestone.

The method of claim 1,

Artificial wood, which is made of vegetation crushed material and minerals, characterized in that the surface agent formed by at least one of paper, textiles, wood, synthetic resins are further bonded to the outer surface of the artificial wood.

The method of claim 1,

The adhesive is artificial wood made of vegetation powder and minerals, characterized in that the rosin.

The method of claim 1,

The adhesive is artificial wood made of vegetation powder and minerals, characterized in that the glue.

The method of claim 1,

The reinforcing layer 10 is artificial wood made of vegetation grinds and minerals, characterized in that the paper or paper.

The method of claim 1,

The adhesive is artificial wood made of crushed wood and minerals, characterized in that the seaweed adhesive prepared using seaweed such as seaweed, kelp, green sea.

The method of claim 7, wherein

The adhesive is artificial wood made of pulverized plants and minerals, characterized in that the rice paste is further added to the warmth produced.

The method of claim 7, wherein

The adhesive is artificial wood made of pulverized plants and minerals, characterized in that the barley flour or flour paste for emitting cold air is further added.

The method according to any one of claims 1 to 7,

Artificial wood made of pulverized wood and minerals, characterized in that the reinforcement 40 is further inserted into the reinforced layer 20 to increase the strength.

The method according to any one of claims 1 to 7,

Artificial wood made of vegetation powder and minerals, characterized in that the core layer 60 is inserted into the hollow portion 50.

The method of claim 11,

The core layer 60 is artificial wood made of pulverized wood and minerals, characterized in that the wood or metal material or synthetic resin material.