KR200387237Y1 - Portable Product Having Name Indicating Part - Google Patents

Abstract

The present invention relates to a product formed with a statement base portion that can easily identify the user or owner of the article, the portable article formed with a statement base portion of the present invention 40 to 60 parts by weight of inorganic pigments on the outside of the body or a handle portion A coating composition comprising 25 to 35 parts by weight of polymer resin, 12 to 18 parts by weight of solvent, and 3 to 7 parts by weight of an additive including a quencher and an antifoaming agent is applied to form a statement base part. The article formed with a statement base portion of the paint composition of the present invention is a simple article description method and can be used in toothbrushes and cups that frequently come into contact with water because the letters do not spread even when contacted with water. Since it is easy to distinguish from others and is not confused with one's own, it has an effect of facilitating management.

Description

Portable Product Having Name Indicating Part

The present invention relates to a product formed with a statement base portion that can easily identify the user or owner of the article, and more specifically, oil-based ballpoint pen, etc. in plastic or wood items such as daily necessities or office supplies that are mainly injection molded into plastic material The present invention relates to a product in which a name base portion is formed that can easily display the name of a user or owner.

The necessities and office supplies, usually made of plastic, ceramics or wood, which are a kind of synthetic resins due to mass production, are encountered a lot in our surroundings.

However, life necessities or office supplies made of portable plastic materials can be identified to some extent because the types, shapes, and colors of the corresponding plastic bodies may vary, but sometimes a separate user mark is displayed on plastic articles of similar colors. It is very difficult to easily determine who the user is because there is no.

In particular, the toothbrushes used in individual homes and offices are used whenever an individual needs them. Toothbrush holders or toothbrush holders are used to distinguish their own.However, similar types, colors, and shapes of similar plastic articles can be distinguished or identified. There is a limit.

Small office items such as rulers, ballpoint pens, or glues, such as glue, may be used to write a name on the tow paper, but the tow paper may fall off over time. The appearance is not so good.

In today's offices, many individual cups made of plastic are used. In this case, display means for identifying the user or owner are required. In addition, in the case of managing a lot of paintings by others in the work, it is good to have a statement base on the outside of the painting. This is because the etching part of the painting is often hard to identify until it is written in Chinese or imprinted with ink pads.

Toothbrushes provided with marking means in handle bags of toothbrushes have been disclosed in Korean Utility Model Nos. 0198380 and 0195354. However, the signs disclosed above are covered with a transparent cover plate while being detachably inserted and mounted. In order to manufacture detachably or to manufacture a separate cover plate, the manufacturing process is very complicated and there is a limit to use in a ballpoint pen, a portable cup, and the like. In addition, the cover plate does not consider the sign to be completely separated from the moisture, and is likely to be exposed to moisture upon detachment.

In addition, Patent No. 0250398 discloses a name plate structure in which an opaque paper and a transparent paper are bonded to each other and a chemical treatment of a carbon film capable of printing a name on the adhesive side of the opaque paper. This is also a complicated manufacturing process, which costs a lot of money and manpower.

Therefore, there has been a demand for a plastic or wood daily necessity in which a statement base portion having a simple structure and manufacturing process is formed.

The present invention has been made in order to solve the above problems is to provide a plastic or wood household goods having a statement base that can easily identify the user or owner.

The present inventors have tried various methods to solve the problems of the prior art as a result of additives including 40 to 60 parts by weight of inorganic pigments, 25 to 35 parts by weight of polymer resin, 12 to 18 parts by weight of solvent and a matting agent and antifoaming agent. The coating composition consisting of 7 parts by weight to 7 parts by weight is applied to the outside of the main body of the portable article or the handle by a coating method such as a silk screen, and dried to form a name base portion, and the name is written on an oil ink such as a conventional oil ballpoint pen thereon. The present invention was completed by finding that not only the substrate is easy but also that the ink based on the statement does not bleed or erase even when exposed to moisture.

The material of the portable article is preferably plastic, porcelain or wood and most preferably a plastic material.

Portable article formed with a statement base portion of the present invention for achieving the above object is 40 to 60 parts by weight of inorganic pigment, 25 to 35 parts by weight of polymer resin, 12 to 18 parts by weight of solvent and matting agent on the outer side of the body or a part of the handle portion and A coating composition including 3 to 7 parts by weight of an additive including an antifoam is applied to form a statement base part.

As the inorganic pigments, white pigments (zinc oxide, titanium oxide, 등 白, etc.) known to be used in paints, red pigments (Bengala, vermilion, cadmium red, etc.), yellow pigments (黄 鉛, ocher, cadmium yellow, etc.) , Green pigments (emerald 綠, chromium oxide, etc.), blue pigments (Prussian blue, cobalt blue, etc.), purple pigments (manganese, mars, etc.), black pigments (carbon black, black, etc.), transparent white pigments (Silica bag, alumina bag, white gel, calcium carbonate, etc.), and titanium dioxide, which is a white pigment, is most preferred.

As the polymer resin, synthetic resin such as natural resin or phenol resin, melamine resin, urethane resin, epoxy resin, alkyd resin, vinyl acetate resin, acrylic emulsion resin, ABS resin, PVC resin, etc. ABS resin has the best adhesion.

The solvent may be alcohols or ketones, but it is preferable to use a mixture of Cyclohexanone, Butyl Cellosolve, Isophorone and Xylen, particularly preferably 50 to 70 parts by weight of Cyclohexanone and 3 to 7 parts by weight of Butyl Cellosolve based on 100 parts by weight of the solvent. It is preferred to use a mixture of 15 to 25 parts by weight of Isophorone and 12 to 18 parts by weight of Xylen.

The additive preferably further includes a pigment dispersant and a thickener in addition to the quencher and the antifoaming agent. Matting agents reduce the gloss of the coating and include silica, aluminum stearate, and polyethylene wax. Defoamers prevent foaming of paints, and examples thereof include silicones, surfactants, and higher alcohols. Pigment dispersants enhance the dispersibility of pigments and thickeners (thickers) are added to paints to increase viscosity, prevent flowability, and prevent sedimentation of pigments. Examples of thickeners include methyl cellulose, hydroxy ethyl cellulose, polyvinyl alcohol, and the like.

The coating of the ink is particularly preferably performed by a silk screen method.

The color of the paint composition is preferably light blue or pink of white or paston series, but any color that can recognize the name when a name is written with an oil ballpoint pen is possible. When preparing a paint composition that is not white, it may further include a colorant.

If the pigment content of 100 parts by weight of the total paint composition is less than 40 parts by weight, the user name of the statement base is low in clarity, and if it exceeds 60 parts by weight, the resin content is lowered. . On the other hand, if the content of the polymer resin is more than 35 parts by weight, the adhesion of the paint is enhanced, but the coating film is well contaminated can be easily messed up, if less than 25 parts by weight of the statement is easily spread.

In addition, if the solvent is 12 parts by weight or less, it is difficult to evenly mix each component, and if the additives such as the antifoaming agent and the quencher is 3 parts by weight or less, the workability is much lowered due to the deterioration of the properties of the mixed liquid.

Hereinafter, preferred embodiments of the present invention will be described in detail based on the following examples and exemplary drawings. However, the technical idea of the present invention is not limited to the following examples.

Example 1 Preparation of Paint Composition

A coating composition was prepared by mixing 50 parts by weight of titanium dioxide (KA100 per trioxide), 30 parts by weight of an ABS resin, 15 parts by weight of a solvent, and 5 parts by weight of an additive. The solvent used was a mixture of 60 parts by weight of Cyclohexanone, 5 parts by weight of Butyl Cellosolve, 20 parts by weight of Isophorone, and 15 parts by weight of Xylen based on 100 parts by weight of the solvent. The additive is 15 parts by weight of the matting agent based on 100 parts by weight of the antifoaming agent. A weight part, 40 weight part of pigment dispersants, and 25 weight part of thickeners were used.

Example 2: Preparation of Paint Composition

A coating composition was prepared by mixing 60 parts by weight of titanium dioxide (KA100 per trioxide), 20 parts by weight of an ABS resin, 15 parts by weight of a solvent, and 5 parts by weight of an additive. The composition of the solvent and the additive was the same as in Example 1.

Example 3: Preparation of Paint Composition

A coating composition was prepared by mixing 40 parts by weight of titanium dioxide (KA100 per trioxide), 40 parts by weight of an ABS resin, 15 parts by weight of a solvent, and 5 parts by weight of an additive. The composition of the solvent and the additive was the same as in Example 1.

Example 4: Preparation of Paint Composition

A paint composition was prepared by mixing 52 parts by weight of titanium dioxide (KA100 per trioxide), 32 parts by weight of an ABS resin, 12 parts by weight of a solvent, and 4 parts by weight of an additive. The composition of the solvent and the additive was the same as in Example 1.

Example 5

Ink was applied to the handle portion of the toothbrush made of a plastic body (1) by a silkscreen method to prepare a toothbrush having a statement base (2). It is shown in FIG. 1 that the statement is written with an oil ballpoint pen or the like on the statement base part formed in the toothbrush.

Example 6

The ink was applied to the handle portion of the coating 1 made of plastic or wood by the silk screen method to prepare a coating on which the statement base portion 2 was formed. It is shown in FIG. 2 that the statement is written with an oil ballpoint pen or the like on the statement base part formed in the toothbrush.

Example 7

Ink was applied to the outer portion of the cup made of a plastic body (1) by the silkscreen method to prepare a cup on which the statement base portion (2) was formed. It is shown in FIG. 3 that the statement is written with an oil ballpoint pen or the like on the statement base part formed in the cup. The statement base part was formed in the main body outer side (a) and the handle part (b).

 Example 8

Ink was applied to a part of the outer side of the pen made of a plastic body 1 by a silk screen method to prepare a pen on which a statement base portion 2 was formed. It is shown in FIG. 4 that the statement is written with an oil ballpoint pen or the like on the statement base part formed in the cup.

Experimental Example 1

As a coating composition prepared in Examples 1 to 4, a statement base was formed on the toothbrush handle of a plastic material of PET material, the statement was written with a general oil ballpoint pen, and the shape thereof was observed and the results are shown in Table 1 below.

Table 1

Example 1 Example 2 Example 3 Example 4 Sharpness of writing Great Great usually Great Ink adhesion Great usually Great Great Smear Great usually Great Great Mixed Great Great Great usually

From the above results, the higher the amount of inorganic pigment, the better the clarity of the writing, but it is easy to bleed. If the amount of the inorganic pigment is small, the sharpness of the writing is lowered. It can be seen that the mixing is poor.

Experimental Example 2

30 seconds, 1 minute, 2 minutes, 5 minutes after forming the statement base portion on the toothbrush handle of the plastic material of PET material with a paint composition prepared in Examples 1 to 4 and the statement with a general oil ball-point pen Was rubbed with a finger and smeared to form ink. The results are shown in Table 2.

Example 1 Example 2 Example 3 Example 4 30 seconds elapsed △ △ △ △ 1 minute elapsed ○ △ ○ ○ 2 minutes ○ ○ ○ ○ 5 minutes ○ ○ ○ ○ ○: When the ink does not bleed at all △: When there is no problem to read the smudges and text slightly ×: When the text is blurred and unreadable

As described above, the article formed with the statement base part according to the present invention can easily describe the statement, and there is no fear of swelling or tearing like a traction paper even when exposed to moisture.

As described above, the article formed with the statement base portion of the paint composition of the present invention can be used in toothbrushes and cups that have a simple statement method and are often in contact with water because the letters do not spread even when contacted with water. In addition, the article formed with the statement base portion of the present invention is easy to distinguish from others, not to be confused with their own and can be returned even if lost. In addition, in the case of managing a plurality of things of another person, there is an effect that makes the management easier.

1 is a toothbrush formed with a statement base portion in the handle portion according to an embodiment of the present invention.

Figure 2 is a seal formed with a statement base portion in the handle portion according to an embodiment of the present invention.

Figure 3 is a cup formed with a statement base portion in the handle portion (a) and the body outer side (b) according to an embodiment of the present invention.

Figure 4 is a writing instrument formed a statement base portion in the handle portion according to an embodiment of the present invention.

* Explanation of symbols for the main parts of the drawings

1: portable goods

2: statement base

Claims (6)

A base material; 40 to 60 parts by weight of an inorganic pigment, 25 to 35 parts by weight of a polymer resin, 12 to 18 parts by weight of a solvent, and 3 to 7 parts by weight of an additive including a quencher and an antifoaming agent. Portable article comprising a statement base portion formed in the coating layer of the composition. The portable article of claim 1, wherein the substrate is made of plastic, wood, or porcelain material. A portable article according to claim 1 or 2, which is a toothbrush. The portable article of claim 1 or 2, which is a cup. The portable article according to claim 1 or 2, which is a paint. The portable article according to claim 1 or 2, which is a writing instrument.