KR200354391Y1 - A panel for environment-friendly interior - Google Patents

A panel for environment-friendly interior Download PDF

Info

Publication number
KR200354391Y1
KR200354391Y1 KR20-2004-0009308U KR20040009308U KR200354391Y1 KR 200354391 Y1 KR200354391 Y1 KR 200354391Y1 KR 20040009308 U KR20040009308 U KR 20040009308U KR 200354391 Y1 KR200354391 Y1 KR 200354391Y1
Authority
KR
South Korea
Prior art keywords
panel
molten film
film layer
interior
interior panel
Prior art date
Application number
KR20-2004-0009308U
Other languages
Korean (ko)
Inventor
김상설
Original Assignee
김상설
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김상설 filed Critical 김상설
Priority to KR20-2004-0009308U priority Critical patent/KR200354391Y1/en
Application granted granted Critical
Publication of KR200354391Y1 publication Critical patent/KR200354391Y1/en

Abstract

본 고안은 환경친화적인 실내인테리어용 판넬에 관한 것으로, 구체적으로 실내 인테리어용 판넬을 이루는 기재의 한면 위에 용융필름층을 형성하고, 상기 용융필름층 위에 무늬를 포함한 무늬층을 형성한 것을 특징으로 하는 실내 인테리어용 판넬에 관한 것이다.The present invention relates to an environmentally friendly panel for indoor interior, and specifically, a molten film layer is formed on one surface of a substrate constituting the indoor interior panel, and a pattern layer including a pattern is formed on the molten film layer. It relates to an interior interior panel.

본 고안의 판넬은 용융필름층을 형성함으로써, 메라민 수지 또는 요소 수지 접착제의 사용으로 인한 포름알데히드 발암물질의 발생을 해결할 수 있었으며, 소각시 다이옥신 배출이 없어 후처리에도 우수한 장점을 가지고 있다. 또한, 제조비용이나 작업방법이 매우 간단하여 별도의 접착제 도포 설비 없이 적층과정에 용융필름을 간단히 삽입시켜 작업할 수 있다. 특히, 금속 박막에도 쉽게 적용할 수 있어 다양한 인테리어 소재를 제조할 수 있다.The panel of the present invention was able to solve the generation of formaldehyde carcinogens caused by the use of the melamine resin or the urea resin adhesive by forming the molten film layer, and has no advantages in post-treatment since there is no dioxin emission during incineration. In addition, the manufacturing cost or the work method is very simple, it is possible to work by simply inserting the molten film in the lamination process without a separate adhesive coating equipment. In particular, it can be easily applied to a metal thin film can be produced a variety of interior materials.

Description

환경친화적인 실내인테리어용 판넬{A PANEL FOR ENVIRONMENT-FRIENDLY INTERIOR}Environmentally Friendly Interior Interior Panels {A PANEL FOR ENVIRONMENT-FRIENDLY INTERIOR}

본 고안은 실내 인테리어용 판넬에 관한 것이다.The present invention relates to an indoor interior panel.

일반적인 가구 또는 실내 인테리어용 판넬은 합판, MDF(Medium Density Fiberboard)나 파티클 보드(Particle Board) 등과 같은 집성목이나 원목 등으로 만들어지는데, 원목은 상당히 고가이기 때문에 흔히 집대성목을 사용하여 가구 또는 인테리어용 판넬을 제작한다. 그리고 집성목의 한쪽 면 또는 양면에는 판넬의 외관을 미려하게 하며, 추가로 판넬이 습기 등에 노출되어 변형되는 것을 방지하기 위하여 마감시트를 부착할 수 있다.Typical furniture or interior panels are made of aggregate or solid wood, such as plywood, medium density fiberboard (MDF) or particle board, which are often very expensive. To produce. And on one side or both sides of the aggregate wood beautiful appearance of the panel, in addition to the panel may be attached to the finish sheet to prevent the deformation is exposed to moisture.

구체적으로, 종래 가구 또는 실내 인테리어에 사용되는 판넬은 첨부된 도 1에서 보는 바와 같이, 합판, MDF나 파티클 보드(11) 등의 집성목의 한쪽 면 위에 접착제 층(1)이 형성되고, 상기 접착제 층(1) 위에 판넬의 외관을 미려하게 하기위한 무늬목(12)이 형성되어 있다.Specifically, the panel used in the conventional furniture or interior, as shown in the accompanying Figure 1, the adhesive layer (1) is formed on one side of the laminated wood, such as plywood, MDF or particle board 11, the adhesive layer On (1), the veneer 12 is formed to make the exterior of the panel beautiful.

상기 합판, MDF나 파티클 보드는 가구 또는 인테리어용 판넬의 기재를 이루며 형태 및 강도를 유지하는 것으로, 그 두께를 다양하게 조절하여 그 용도에 따라 사용한다.The plywood, MDF or particle board to form the base of the panel for furniture or interior to maintain the shape and strength, the thickness of the various controls to use according to the purpose.

또한, 상기 무늬목은 나무 질감을 판넬에 나타내기 위해 사용되는 것으로, 현재 소비자에게 가장 많이 선호되는 나무 질감을 얻기에 바람직하다. 그 두께는 그 용도 및 경제성에 따라 다양하게 조절할 수 있다.In addition, the veneer is used to display the wood texture on the panel, it is desirable to obtain the wood texture that is currently most preferred to the consumer. The thickness can be variously adjusted according to the use and economics.

특히, 상기 판넬에서 접착제층은 합판, MDF나 파티클 보드와 무늬목을 접착하기 위한 층으로, 종래에 메라민 수지 또는 요소수지를 사용한다.In particular, the adhesive layer in the panel is a layer for adhering plywood, MDF or particle board and veneer, conventionally used a melamine resin or urea resin.

상기한 구성을 갖는 가구 또는 실내 인테리어용 판넬은 합판, MDF나 파티클 보드와 무늬목을 접착제를 사용하여 접착시킨 후 열압처리하여 얻어진다. 구체적으로, 얇게 슬라시한 무늬목과, 합판, MDF나 파티클 보드를 접착함에 있어 합판, MDF나 파티클 보드의 한쪽 면에 접착제를 도포한 후 무늬목을 그 위에 올려놓고 열압프레스로 열경화시킨다. 이때, 상기 열압은 단위압력 5∼15 ㎏/㎠, 플레스온도 110∼130℃에서 유지시간 60∼240초 동안 수행한다. 상기 열경화 후 UV 피막도장처리를 수행하여 각종 용도로 사용한다.Furniture or interior panel having the above configuration is obtained by bonding the plywood, MDF or particle board and veneer using an adhesive and then hot pressing. Specifically, in bonding thinly sliced veneer and plywood, MDF or particle board, the adhesive is applied to one side of the plywood, MDF or particle board, and then the veneer is placed thereon and thermoset by heat press. At this time, the thermal pressure is performed for a holding time of 60 to 240 seconds at a unit pressure of 5 ~ 15 kg / ㎠, a place temperature 110 ~ 130 ℃. After the heat curing is carried out UV coating coating to be used for various purposes.

상술한 바와 같이, 상기 가구 또는 실내 인테리어용 판넬은 접착제층을 형성하여야 하며, 이때 사용하는 종래 접착제로는 메라민 수지 또는 요소 수지이다.이러한 수지는 가격이 저렴하고 상기와 같은 열경화 과정을 통하여 간단히 판넬을 제작하는데 유용하나, 인체에 치명적인 포름알데히드 발암물질을 방출하여 환경적 또는 건강에 치명적인 문제가 발생한다. 이러한 이유로 인해 종래 접착제층에 비해 친환경적이고 친인체적인 접착제층을 구비한 판넬의 개발이 필요한 실정이다.As described above, the panel for furniture or indoor interior should form an adhesive layer, and the conventional adhesive used here is a melamine resin or urea resin. Such resins are inexpensive and simply through the thermal curing process as described above. It is useful for making panels, but it releases formaldehyde carcinogens, which are fatal to humans, causing environmental and health problems. For this reason, it is necessary to develop a panel having an environment-friendly and human-friendly adhesive layer compared to the conventional adhesive layer.

본 고안의 목적은 상기한 종래 판넬의 문제점을 해결하기 위한 것으로, 구체적으로 유해 물질이 발생되지 않는 환경 친화적인 실내 인테리어용 판넬을 제공하는 것이다.An object of the present invention is to solve the above problems of the conventional panel, and in particular, to provide an environment-friendly indoor interior panel that does not generate harmful substances.

도 1은 종래 무늬목을 포함한 실내 인테리어용 판넬의 단면도이며,1 is a cross-sectional view of a panel for a room interior including a conventional veneer,

도 2는 본 고안에서 제 1 실시예의 실내 인테리어용 판넬의 단면도이며,2 is a cross-sectional view of the panel for the interior of the first embodiment of the present invention,

도 3은 본 고안에서 제 2 실시예의 실내 인테리어용 판넬의 단면도이며,3 is a cross-sectional view of the panel for the interior of the second embodiment in the present invention,

도 4는 본 고안에서 제 3 실시예의 실내 인테리어용 판넬의 단면도이며,4 is a cross-sectional view of the panel for the interior of the third embodiment of the present invention,

도 5는 본 고안에서 제 4 실시예의 실내 인테리어용 판넬의 단면도이며,5 is a cross-sectional view of the panel for the interior of the fourth embodiment in the present invention,

도 6은 본 고안에서 제 5 실시예의 실내 인테리어용 판넬의 단면도이며,6 is a cross-sectional view of the panel for the interior of the fifth embodiment in the present invention,

도 7은 본 고안에서 제 6 실시예의 실내 인테리어용 판넬의 단면도이며,7 is a cross-sectional view of the panel for the interior of the sixth embodiment in the present invention,

도 8은 본 고안에서 제 7 실시예의 실내 인테리어용 판넬의 단면도이며,8 is a cross-sectional view of the panel for the interior of the seventh embodiment in the present invention,

도 9는 본 고안에서 제 8 실시예의 실내 인테리어용 판넬의 단면도이며,9 is a cross-sectional view of the panel for the interior of the eighth embodiment in the present invention,

도 10은 본 고안에서 제 9 실시예의 실내 인테리어용 판넬의 단면도이며,10 is a cross-sectional view of the panel for the interior of the ninth embodiment of the present invention,

* 도면의 주요 부분에 대한 부호의 설명** Explanation of symbols for main parts of the drawing

1 : 접착제층1: adhesive layer

10 : 목재 기재의 판넬, 11 : 합판, MDF, 파티클 보드10: panel of wood substrate, 11: plywood, MDF, particle board

12 : 무늬목, 13 : 표면강화지12: veneer, 13: reinforcement paper

14 : 직물, 15 : 인쇄필름14 fabric, 15 printing film

20 : 페놀수지 함침기재 판넬, 21 : 페놀수지 함침기재20: phenolic resin impregnated base material panel, 21: phenolic resin impregnated base material

22 : 금속 박막,22: metal thin film,

30 : 알루미늄판 기재 판넬, 31 : 알루미늄판30: aluminum plate base panel, 31: aluminum plate

100 : 용융필름층.100: molten film layer.

상기한 목적을 달성하기 위하여, 본 고안은 실내 인테리어용 판넬을 이루는 기재의 한면 위에 용융필름층을 형성하고, 상기 용융필름층 위에 무늬를 포함한 무늬층을 형성한 것을 특징으로 하는 실내 인테리어용 판넬을 제공하는 것이다.In order to achieve the above object, the present invention forms a molten film layer on one surface of the base constituting the panel for the indoor interior, and a panel for the indoor interior, characterized in that formed a pattern layer including a pattern on the molten film layer. To provide.

이하, 본 고안을 상세히 설명한다.Hereinafter, the present invention will be described in detail.

본 고안에서, 실내 인테리어용 판넬을 이루는 기재는 통상적으로 사용할 수 있는 판넬을 모두 사용할 수 있으며, 구체적으로 본 고안의 용용필름에 의해 접착이 가능하며 제품으로 사용가능한 접착효과를 나타내는 판넬을 사용할 수 있다. 바람직하게는 합판, MDF(Middle Density Fiberboard), 파티클 보드(ParticleBoard), 페놀수지 함침 기재 또는 알루미늄 판을 사용할 수 있다. 이때, 두께는 판넬의 용도에 따라 다양하게 조절할 수 있으며, 바람직하게는 약 15 ㎜가 되도록 조절한다.In the present invention, the substrate constituting the panel for the indoor interior can be used all the panels that can be used in general, specifically can be used by the molten film of the present invention can be used a panel showing the adhesive effect usable as a product. . Preferably, plywood, MDF (Middle Density Fiberboard), Particleboard (ParticleBoard), phenolic resin impregnated substrate or aluminum plate can be used. At this time, the thickness can be variously adjusted according to the use of the panel, preferably adjusted to about 15 mm.

상기 용융필름은 접착제의 역할을 수행하는 것으로, 일정한 열에 의해 용융된 후 냉각되면서 접착력을 나타낸 것으로, 일반적으로 필름형태로 된 것을 사용하는 것이 바람직하다. 이러한 용융필름은 하기에 기술된 무늬를 나타내는 무늬층과 판넬을 이루는 기재가 금속인 경우 더욱 그 우수한 접착 효과를 나타낸다. 종래 에폭시 수지 또는 우레탄 수지를 금속과 열에 의해 접착할 경우, 서로 상이한 팽창성에 의해 뒤틀림 현상이 발생되게 된다. 구체적으로 열에 의해 금속층은 팽창하게 되고, 이와 반대로 상기 수지층은 수축하게 되는 문제점이 발생하게 된다. 그러나, 본 고안의 용융필름은 금속층과의 수축력의 상이함이 적어 뒤틀림 현상이 발생되지 않는 장점이 있다. 또한, 종래 수지의 가장 큰 문제점이 오염 물질을 방출하지 않아 환경친화적이고, 인체친화적인 판넬을 구성할 수 있다.The molten film is to perform the role of the adhesive, it is melted by a constant heat and then cooled while showing the adhesive force, it is generally preferred to use a film form. Such a molten film exhibits an excellent adhesive effect even when the substrate constituting the pattern layer and the panel showing the pattern described below is a metal. When a conventional epoxy resin or urethane resin is bonded to a metal by heat, a warpage phenomenon is caused by different expandability. Specifically, heat causes the metal layer to expand, and conversely, the resin layer contracts. However, the molten film of the present invention has an advantage that the warpage phenomenon does not occur because the difference in shrinkage force with the metal layer is small. In addition, the biggest problem of the conventional resin is that it does not emit pollutants can be configured environmentally friendly, human-friendly panel.

상기 용융필름은 통상적으로 사용되는 모든 공업용 열융용 필름을 사용할 수 있으며, 바람직하게는 에틸렌-초산비닐 공중합체 수지, 폴리에틸렌 수지, 에틸렌-아크릴산 에틸 공중합체 수지, 초산비닐 수지, 폴리비닐 부티랄 수지로 이루어진 그룹 중 선택된 하나 또는 그 이상의 혼합물을 사용할 수 있다.The molten film may be any commercially available industrial heat melting film, preferably ethylene-vinyl acetate copolymer resin, polyethylene resin, ethylene-ethyl acrylate copolymer resin, vinyl acetate resin, polyvinyl butyral resin One or more mixtures selected from the group consisting of can be used.

상기 무늬층은 판넬의 미려한 외관 및 기타 난연 등의 기능을 나타내기 위한것으로, 바람직하게는 무늬목, 직물, 인쇄필름, 알루미늄 박막 또는 동박과 같은 금속 박막 등을 사용할 수 있다. 이 중 무늬목은 그 자체로 층을 형성할 수 있을 뿐만 아니라, 표면의 흠집 등의 문제를 해결하기 위하여, 메라민 수지가 함침된 표면 강화지를 그 위에 적층하여 사용할 수 있다. 이때, 메라민 수지는 본 고안의 목적인 환경친화적이 판넬을 위해 소량만 사용하며, 바람직하게는 표면 강화지에 대해 0.01∼5 중량%로 제한한다. 또한, 상기 표면 강화지에 난연기능을 부가하기 위해 인산염, 붕소, 할로겐, 안티몬, 질소 등의 첨가제를 함침시켜 사용할 수 있다.The pattern layer is intended to exhibit a beautiful appearance of the panel and other functions such as flame retardant, and preferably may be a metal thin film such as veneer, fabric, printing film, aluminum thin film or copper foil. Among them, the veneer may not only form a layer by itself, but also in order to solve problems such as surface scratches, surface reinforcing paper impregnated with a melamine resin may be laminated and used thereon. At this time, the melamine resin is used only a small amount for the environmentally friendly panel for the purpose of the present invention, preferably limited to 0.01 to 5% by weight relative to the surface reinforcement paper. In addition, it can be used by impregnating additives such as phosphate, boron, halogen, antimony, nitrogen in order to add a flame retardant function to the surface reinforcement paper.

본 고안의 실내 인테리어용 판넬 각 층을 적층한 후 열압프레스를 사용하여 제조한다. 이때, 열압조건은 단위압력 15∼60 ㎏/㎠, 프레스 온도 120∼150℃, 유지시간 20초∼25분간이 바람직하며, 열압 후 냉각 또는 열간 해체 시킨다.Each layer of the interior panel of the present invention is laminated and then manufactured using a hot press. At this time, the hot pressure condition is preferably 15 to 60 kg / cm 2, press temperature 120 to 150 ° C., holding time 20 seconds to 25 minutes, and cooling or hot disassembly after hot pressure.

이하, 첨부된 도면을 참조하여 본 고안의 실내 인테리어용 판넬의 실시예를 상세시 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail an embodiment of a panel for an interior interior of the present invention.

도 2는 본 고안의 실내 인테리어용 판넬의 제 1 실시예를 보인 단면도이다. 도 2에서 보는 바와 같이, 상기 판넬은 합판, MDF 또는 파티클 보드(11)층의 한면 위에 용융필름층(100)이 형성되고, 상기 용융필름층(100) 위에 무늬목(12)이 형성된다.2 is a cross-sectional view showing a first embodiment of an interior panel of the present invention. As shown in Figure 2, the panel is a molten film layer 100 is formed on one surface of the plywood, MDF or particle board 11 layer, the veneer 12 is formed on the molten film layer 100.

도 3은 본 고안의 실내 인테리어용 판넬의 제 2 실시예를 보인 단면도이다.도 3에서 보는 바와 같이, 상기 판넬은 상기 도 2의 적층 구조를 갖는 판넬의 무늬목 위에 메라민 수지가 함침된 표면강화지(13)가 형성된다.Figure 3 is a cross-sectional view showing a second embodiment of the interior panel of the present invention. As shown in Figure 3, the panel is a surface-reinforced paper impregnated with a melamine resin on the veneer of the panel having the laminated structure of Figure 2 (13) is formed.

도 4는 본 고안의 실내 인테리어용 판넬의 제 3 실시예를 보인 단면도이다. 도 4에서 보는 바와 같이, 상기 판넬은 합판, MDF 또는 파티클 보드(11)층의 한면 위에 용융필름층(100)이 형성되고, 상기 용융필름층(100) 위에 직물(14)이 형성된다.Figure 4 is a cross-sectional view showing a third embodiment of the panel for an interior interior of the present invention. As shown in FIG. 4, the panel has a molten film layer 100 formed on one surface of a plywood, MDF or particle board 11 layer, and a fabric 14 formed on the molten film layer 100.

도 5는 본 고안의 실내 인테리어용 판넬의 제 4 실시예를 보인 단면도이다. 도 5에서 보는 바와 같이, 상기 판넬은 합판, MDF 또는 파티클 보드(11)층의 한면 위에 용융필름층(100)이 형성되고, 상기 용융필름층(100) 위에 인쇄필름(15)이 형성된다.5 is a cross-sectional view showing a fourth embodiment of an interior panel of the present invention. As shown in FIG. 5, the panel has a molten film layer 100 formed on one surface of a plywood, MDF or particle board 11 layer, and a print film 15 formed on the molten film layer 100.

도 6은 본 고안의 실내 인테리어용 판넬의 제 5 실시예를 보인 단면도이다. 도 6에서 보는 바와 같이, 상기 판넬은 페놀수지 함침 기재(21)층의 한면 위에 용융필름층(100)이 형성되고, 상기 용융필름층(100) 위에 무늬목(12)이 형성된다.6 is a cross-sectional view showing a fifth embodiment of an interior panel of the present invention. As shown in Figure 6, the panel is a molten film layer 100 is formed on one surface of the phenolic resin impregnated substrate 21 layer, the veneer 12 is formed on the molten film layer 100.

도 7는 본 고안의 실내 인테리어용 판넬의 제 6 실시예를 보인 단면도이다. 도 7에서 보는 바와 같이, 상기 판넬은 상기 도 6의 적층 구조를 갖는 판넬의 무늬목 위에 메라닌 수지가 함침된 표면강화지(13)가 형성된다.7 is a cross-sectional view showing a sixth embodiment of an interior panel of the present invention. As shown in FIG. 7, the panel is formed with a surface-reinforced paper 13 impregnated with a melanin resin on the veneer of the panel having the laminated structure of FIG.

도 8은 본 고안의 실내 인테리어용 판넬의 제 7 실시예를 보인 단면도이다. 도 8에서 보는 바와 같이, 상기 판넬은 페놀수지 함침 기재(21)층의 한면 위에 용융필름층(100)이 형성되고, 상기 용융필름층(100) 위에 알루미늄 박막 또는 동 박막과 같은 금속 박막(22)이 형성된다.8 is a cross-sectional view showing a seventh embodiment of an interior panel of the present invention. As shown in FIG. 8, the panel has a molten film layer 100 formed on one surface of the phenolic resin impregnated substrate 21 layer, and a metal thin film 22 such as an aluminum thin film or a copper thin film on the molten film layer 100. ) Is formed.

도 9는 본 고안의 실내 인테리어용 판넬의 제 8 실시예를 보인 단면도이다. 도 9에서 보는 바와 같이, 상기 판넬은 알루미늄 판(31)층의 한면 위에 용융필름층(100)이 형성되고, 상기 용융필름층(100) 위에 무늬목(12)이 형성된다.9 is a cross-sectional view showing an eighth embodiment of an interior panel of the present invention. As shown in Figure 9, the panel is a molten film layer 100 is formed on one side of the aluminum plate 31 layer, the veneer 12 is formed on the molten film layer 100.

도 10은 본 고안의 실내 인테리어용 판넬의 제 9 실시예를 보인 단면도이다. 도 107에서 보는 바와 같이, 상기 판넬은 상기 도 96의 적층 구조를 갖는 판넬의 무늬목 위에 메라민 수지가 함침된 표면강화지(13)가 형성된다.10 is a cross-sectional view showing a ninth embodiment of an interior panel of the present invention. As shown in FIG. 107, the panel is formed with a surface-reinforced paper 13 impregnated with a melamine resin on the veneer of the panel having the laminated structure of FIG.

상술한 바와 같이, 본 고안의 판넬은 메라민 수지 또는 요소 수지 접착제의 사용으로 인한 유해성 문제인 포름알데히드 발암물질의 발생을 해결할 수 있었으며, 제조비용이나 작업방법이 매우 간단하여 별도의 접착제 도포 설비 없이 적층과정에 용융필름을 간단히 삽입시켜 작업할 수 있다. 특히, 금속 박막에도 쉽게 적용할 수 있어 다양한 인테리어 소재를 제조할 수 있다. 또한 본 고안의 판넬은 친환경적인 제품으로, 소각시 다이옥신 배출이 없어 후처리에도 우수한 장점을 가지고 있다.As described above, the panel of the present invention was able to solve the generation of formaldehyde carcinogens, which is a hazard problem due to the use of the melamine resin or the urea resin adhesive, and the manufacturing cost or working method is very simple, so that the lamination process without a separate adhesive coating equipment This can be done by simply inserting the molten film into it. In particular, it can be easily applied to a metal thin film can be produced a variety of interior materials. In addition, the panel of the present invention is an environmentally friendly product, there is no dioxin emissions during incineration and has excellent advantages in post-treatment.

Claims (8)

실내 인테리어용 판넬을 이루는 기재의 한면 위에 용융필름층을 형성하고, 상기 용융필름층 위에 무늬를 포함한 무늬층을 형성한 것을 특징으로 하는 실내 인테리어용 판넬.An indoor interior panel, comprising: forming a molten film layer on one surface of a substrate forming an indoor interior panel, and forming a pattern layer including a pattern on the molten film layer. 제 1항에 있어서, 상기 실내 인테리어용 판넬이 합판, MDF 또는 파티클 보드층의 한면 위에 용융필름층이 형성되고, 상기 용융필름층 위에 무늬목이 형성된 것을 특징으로 하는 실내 인테리어용 판넬.The indoor interior panel of claim 1, wherein the indoor interior panel has a molten film layer formed on one surface of a plywood, MDF or particle board layer, and a veneer is formed on the molten film layer. 제 1항에 있어서, 상기 실내 인테리어용 판넬이 합판, MDF 또는 파티클 보드층의 한면 위에 용융필름층이 형성되고, 상기 용융필름층 위에 직물층이 형성된 것을 특징으로 하는 실내 인테리어용 판넬.The indoor interior panel of claim 1, wherein the indoor interior panel has a molten film layer formed on one surface of a plywood, MDF or particle board layer, and a fabric layer formed on the molten film layer. 제 1항에 있어서, 상기 실내 인테리어용 판넬이 합판, MDF 또는 파티클 보드층의 한면 위에 용융필름층이 형성되고, 상기 용융필름층 위에 인쇄필름이 형성된 것을 특징으로 하는 실내 인테리어용 판넬.The indoor interior panel of claim 1, wherein the indoor interior panel has a molten film layer formed on one surface of a plywood, MDF, or particle board layer, and a printing film is formed on the molten film layer. 제 1항에 있어서, 상기 실내 인테리어용 판넬이 페놀수지 함침 기재 위에 용융필름층이 형성되고, 상기 용융필름층 위에 무늬목 층이 형성된 것을 특징으로 하는 실내 인테리어용 판넬.The indoor interior panel of claim 1, wherein the indoor interior panel has a molten film layer formed on a phenolic resin-impregnated substrate, and a veneer layer is formed on the molten film layer. 제 1항에 있어서, 상기 실내 인테리어용 판넬이 페놀수지 함침 기재 위에 용융필름층이 형성되고, 상기 용융필름층 위에 알루미늄박막 또는 동박으로 이루어진 금속박막층이 형성된 것을 특징으로 하는 실내 인테리어용 판넬.The indoor interior panel according to claim 1, wherein the indoor interior panel has a molten film layer formed on a phenolic resin impregnated substrate, and a metal thin film layer made of aluminum thin film or copper foil is formed on the molten film layer. 제 1항에 있어서, 상기 실내 인테리어용 판넬이 알루미늄 판 위에 용융필름층이 형성되고, 상기 용융필름층 위에 무늬목이 형성된 것을 특징으로 하는 실내 인테리어용 판넬.The indoor interior panel of claim 1, wherein the indoor interior panel has a molten film layer formed on an aluminum plate, and a veneer is formed on the molten film layer. 제 2, 5 또는 7항에 있어서, 추가로 무늬목 위에 메라민수지 또는 난연처리 메라민 수지가 함침된 표면강화지가 형성된 것을 특징으로 하는 실내 인테리어용 판넬.8. The panel for indoor interior according to claim 2, 5 or 7, further comprising a surface-reinforced paper impregnated with a melamine resin or a flame-retardant melamine resin on the veneer.
KR20-2004-0009308U 2004-04-03 2004-04-03 A panel for environment-friendly interior KR200354391Y1 (en)