KR200350444Y1 - Non-exposure complex construction structure of insulating partial block type using embossing polyvinyl sheet porous ceramic-thermoplastic resin-asphalt membrane waterproofing material - Google Patents

Non-exposure complex construction structure of insulating partial block type using embossing polyvinyl sheet porous ceramic-thermoplastic resin-asphalt membrane waterproofing material Download PDF

Info

Publication number
KR200350444Y1
KR200350444Y1 KR20-2003-0038437U KR20030038437U KR200350444Y1 KR 200350444 Y1 KR200350444 Y1 KR 200350444Y1 KR 20030038437 U KR20030038437 U KR 20030038437U KR 200350444 Y1 KR200350444 Y1 KR 200350444Y1
Authority
KR
South Korea
Prior art keywords
layer
thermoplastic resin
porous ceramic
asphalt
sheet
Prior art date
Application number
KR20-2003-0038437U
Other languages
Korean (ko)
Inventor
유중근
Original Assignee
중앙방수기업주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 중앙방수기업주식회사 filed Critical 중앙방수기업주식회사
Priority to KR20-2003-0038437U priority Critical patent/KR200350444Y1/en
Application granted granted Critical
Publication of KR200350444Y1 publication Critical patent/KR200350444Y1/en

Abstract

본 고안은 엠보싱 폴리비닐시트와 다공성 세라믹 열가소성 수지계 아스팔트 도막방수재를 이용한 부분절연 블록형 비노출 복합방수층 구조에 관한 것으로, 그 목적은 방수층의 내구성을 혁신적으로 증가시킬 수 있도록 방수층을 단속적으로 부분 절연 시공할 수 있는 엠보싱 폴리비닐시트와 다공성 세라믹 열가소성 수지계 아스팔트 도막방수재를 이용한 부분절연 블록형 비노출 복합방수층 구조를 제공하는 것이다.The present invention relates to a partially insulated block-type unexposed composite waterproof layer structure using an embossed polyvinyl sheet and a porous ceramic thermoplastic resin-based asphalt waterproofing material. The object of the present invention is to intermittently perform partial insulation construction of the waterproof layer to innovatively increase durability of the waterproof layer. It is to provide a partially insulating block-type unexposed composite waterproof layer structure using an embossed polyvinyl sheet and a porous ceramic thermoplastic resin-based asphalt waterproofing material.

이와 같은 목적을 달성하기 위하여 본 고안은 콘크리트 스래브 위에 도포되는 접착증강용 아스팔트 프라이머층; 상기 프라이머층 상부에 연속 배열되고 일측이 겹치게 설치되는 엠보싱 폴리비닐 절연 시트층; 상기 아스팔트 프라이머층 일부구간부터 상기 겹치게 설치된 양 폴리비닐 절연 시트간의 구간에 연속 도포된 다공성 세라믹 열가소성 수지계 아스팔트로 이루어진 줄접착 조인트층; 상기 폴리비닐 절연 시트층 상부에 전면 도포되는 도막방수층인 제 1다공성 세라믹 열가소성 수지계 아스팔트층; 상기 제 1 다공성 세라믹 열가소성 수지계 아스팔트층에 부착된 부직포로 이루어진 보강재층; 상기 보강재층 상부에 도포되어 형성된 도막방수층인 제 2 다공성 세라믹 열가소성 수지계 아스팔트층; 상기 제 2 다공성 세라믹 열가소성 수지계 아스팔트층 상부에 부착된 절연용 폴리비닐필름층으로 적층되어 구성되는 부분절연 블록형 비노출 복합방수층 구조를 제공함에 있다.In order to achieve the above object, the present invention is an asphalt primer layer for adhesion enhancement applied on a concrete slab; An embossed polyvinyl insulating sheet layer which is continuously arranged on the primer layer and has one side overlapped; A string adhesive joint layer made of a porous ceramic thermoplastic resin-based asphalt continuously applied from a portion of the asphalt primer layer to a portion of the overlapping polyvinyl insulating sheets; A first porous ceramic thermoplastic resin asphalt layer which is a coating waterproof layer coated on the polyvinyl insulating sheet layer on the front; A reinforcement layer made of a nonwoven fabric attached to the first porous ceramic thermoplastic resin asphalt layer; A second porous ceramic thermoplastic resin-based asphalt layer which is a coating waterproof layer formed on the reinforcing material layer; It is to provide a partially insulating block-type unexposed composite waterproof layer structure that is laminated with the insulating polyvinyl film layer attached to the second porous ceramic thermoplastic resin-based asphalt layer.

Description

엠보싱 폴리비닐시트와 다공성 세라믹 열가소성 수지계 아스팔트 도막방수재를 이용한 부분절연 블록형 비노출 복합방수층 구조{Non-exposure complex construction structure of insulating partial block type using embossing polyvinyl sheet porous ceramic-thermoplastic resin-asphalt membrane waterproofing material}Non-exposure complex construction structure of insulating partial block type using embossing polyvinyl sheet porous ceramic-thermoplastic resin-asphalt membrane waterproofing material}

본 고안은 엠보싱 폴리비닐시트와 다공성 세라믹 열가소성 수지계 아스팔트 도막방수재를 이용한 부분절연 블록형 비노출 복합방수층 구조에 관한 것으로, 다수개의 엠보싱을 구비하는 폴리비닐시트를 절연 접착형으로 바탕 콘크리트와 시트 상호간의 조인트를 블록형으로 고정시킴으로써, 시트 하부와 단속적인 방수성을 유지하도록 한 엠보싱 폴리비닐시트와 다공성 세라믹 열가소성 수지계 아스팔트 도막방수재를 이용한 부분절연 블록형 비노출 복합방수층 구조에 관한 것이다.The present invention relates to a partially insulated block-type unexposed composite waterproof layer structure using an embossed polyvinyl sheet and a porous ceramic thermoplastic resin-based asphalt film waterproofing material. The present invention relates to a partially insulated block-type unexposed composite waterproof layer structure using an embossed polyvinyl sheet and a porous ceramic thermoplastic resin-based asphalt coating waterproofing material to maintain the intermittent waterproofness with the sheet bottom by fixing the block shape.

일반적으로 콘크리트 구조물 옥상이나 지하 방수에는 시트 방수공법이 널리 사용되고 있으며, 이러한 시트 방수 공법은 고무와 아스팔트등을 혼합한 롤 (방수시트)을 시공하여 인장성과 내후성을 요구하는 공법으로, 방수층 형성후 방수층 보호 누름 콘크리트층을 두는 비노출방수공법과, 바닥콘크리트 층 위에 노출방수층을 형성하는 노출방수공법이 있으며, 이중, 비노출방수공법이 주로 이용되고 있다. 상기 비노출방수공법은 합성고무나 합성수지를 주 원료로 해서 적층 성형한 합성 고분자 시트를 같은 계의 접착제를 사용하여 붙여서 방수층을 형성시키는 아스팔트 방수와 같은 멘부렌 방수의 일종이다. 이와 같은 시트방수공법은 공정횟수가 적어 시공이 간단하고 균일한 품질을 얻을 수 있어 넓은 면적 시공시 가장 광범위하게 사용되고 있다.Generally, the sheet waterproofing method is widely used on the roof or underground waterproofing of concrete structures. The sheet waterproofing method is a method that requires tensile and weather resistance by constructing a roll (waterproof sheet) mixed with rubber and asphalt. There is a non-exposed waterproofing method for placing a protective pressed concrete layer, and an exposed waterproofing method for forming an exposed waterproofing layer on a floor concrete layer, and a double and non-exposed waterproofing method is mainly used. The non-exposure waterproofing method is a kind of Menblen waterproofing such as asphalt waterproofing which forms a waterproof layer by pasting synthetic rubber or synthetic resin sheet laminated and molded using synthetic resin as a main raw material using an adhesive of the same system. Such a sheet waterproofing method has a small number of processes, so that construction is simple and uniform quality can be obtained.

그러나, 상기 시트 방수공법은 조인트 부분에 대한 시공의 어려움이 있어 이음부와 끝단부에 박리사고가 많고, 방수시트 폭만큼 접착제를 도포하도록 되어 있어, 바탕콘크리트의 균열 또는 거동으로 인한 방수층의 파단으로 이어져 누수 되거나 수명단축의 요인이 되고 있으며, 이로인해 구조물의 장기 내구성이 감소되고, 유지보수 비용이 증가되어 경제적 부담을 가중시키는 문제점이 있었다.However, the sheet waterproofing method is difficult to construct the joint part, so there are many peeling accidents at the joints and ends, and the adhesive is applied as much as the width of the waterproof sheet, resulting in the breakage of the waterproof layer due to cracking or behavior of the base concrete. As a result, there is a problem of leakage or shortening of lifespan, thereby reducing the long-term durability of the structure and increasing the maintenance cost, thereby increasing the economic burden.

본 고안은 상기와 같은 문제점을 해소하기 위한 것으로, 그 목적은 방수층의 내구성을 혁신적으로 증가시킬 수 있도록 방수층을 단속적으로 부분 절연 시공할 수 있는 엠보싱 폴리비닐시트와 다공성 세라믹 열가소성 수지계 아스팔트 도막방수재를 이용한 부분절연 블록형 비노출 복합방수층 구조를 제공하는 것이다.The present invention is to solve the above problems, the purpose is to use an embossed polyvinyl sheet and porous ceramic thermoplastic resin-based asphalt coating waterproofing material that can intermittently partially insulating the waterproof layer to innovatively increase the durability of the waterproof layer It is to provide a partially insulating block type unexposed composite waterproof layer structure.

도 1 은 본 고안에 따른 방수층 구성을 보인 개념도1 is a conceptual view showing a waterproof layer configuration according to the present invention

도 2 는 본 고안에 따른 엠보싱 폴리비닐 시트의 구성을 보인 예시도2 is an exemplary view showing a configuration of an embossed polyvinyl sheet according to the present invention

도 3 은 본 고안에 따른 엠보싱 폴리비닐 시트의 시공을 보인 개념도3 is a conceptual view showing the construction of the embossed polyvinyl sheet according to the present invention

도 4 는 본 고안에 따른 엠보싱 폴리비닐 시트의 시공상태를 보인 평면예시도Figure 4 is a plan view showing a construction state of the embossed polyvinyl sheet according to the present invention

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

(1) : 아스팔트 프라이머층 (2) : 엠보싱 폴리비닐시트층(1): asphalt primer layer (2): embossed polyvinyl sheet layer

(3) : 줄접착 조인트층 (31) : 중앙부 줄접착층(3): file adhesive layer 31: center file adhesive layer

(4) : 제 1 다공성 세라믹 열가소성 수지계 아스팔트층(4): first porous ceramic thermoplastic resin asphalt layer

(5) : 보강재층(5): reinforcement layer

(6) : 제 2 다공성 세라믹 열가소성 수지계 아스팔트층(6): second porous ceramic thermoplastic resin asphalt layer

(7) : 절연용 폴리비닐필름층 (100): 콘크리트 슬래브 바탕면(7): polyvinyl film layer for insulation (100): concrete slab base surface

(200): 단열재 (300): 누름 콘크리트(200): insulation (300): pressed concrete

(400): 오버랩 처리부 (500): 블록형 씰처리공법400: overlap processing unit 500: block seal processing method

상기와 같은 목적을 달성하기 위하여 본 고안은 콘크리트 슬래브 상부면에 아스팔트 프라이머를 깔고 부직포로 보강한 엠보싱 폴리비닐 시트를 절연 접착하고, 바탕 콘크리트와 시트 상호간의 조인트를 블록형으로 고정시킴으로써 시트 하부의 단속적인 방수성을 유지하며, 시트 상부면에는 다공성 세라믹 열가소성 수지계 아스팔트 도막 방수재를 폴리에스테르 부직포로 2회 도포하여 보강한 후, 상부에 절연용 PE 필름을 설치하도록 되어 있다.In order to achieve the above object, the present invention lays down an asphalt primer on an upper surface of a concrete slab and insulates an embossed polyvinyl sheet reinforced with a nonwoven fabric, and fixes the joint between the base concrete and the sheets in a block shape to control the bottom of the sheet. Maintaining the water-resistant, the sheet upper surface is reinforced with a porous ceramic thermoplastic resin-based asphalt coating waterproofing coating twice with a polyester non-woven fabric, and then to install an insulating PE film on the top.

이하 본 고안을 첨부된 도면에 의거하여 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도 1 은 본 고안에 따른 방수층 구성을 보인 개념도를, 도 2 는 본 고안에 따른 엠보싱 폴리비닐 시트의 구성을 보인 예시도를, 도 3 은 본 고안에 따른 엠보싱 폴리비닐 시트의 시공을 보인 개념도를, 도 4 는 본 고안에 따른 엠보싱 폴리비닐 시트의 시공상태를 보인 평면예시도를 도시한 것으로, 본 고안은 콘크리트 스래브 위에 도포되는 접착증강용 아스팔트 프라이머층(1), 상기 프라이머층 상부에 연속 배열되고 일측이 겹치게 설치되는 엠보싱 폴리비닐 절연 시트층(2), 상기 아스팔트 프라이머층 일부구간부터 상기 겹치게 설치된 양 폴리비닐 절연 시트간의 구간에 연속 도포된 다공성 세라믹 열가소성 수지계 아스팔트로 이루어진 줄접착 조인트층(3), 상기 폴리비닐 절연 시트층 상부에 전면 도포되는 도막방수층인 제 1다공성 세라믹 열가소성 수지계 아스팔트층(4), 상기 제 1 다공성 세라믹 열가소성 수지계 아스팔트층에 부착된 부직포로 이루어진 보강재층(5), 상기 보강재층 상부에 도포되어 형성된 도막방수층인 제 2 다공성 세라믹 열가소성 수지계 아스팔트층(6), 상기 제 2 다공성 세라믹 열가소성 수지계 아스팔트층 상부에 부착된 절연용 폴리비닐필름층(7)으로 적층되는 복합방수층 구조를 구비한다.1 is a conceptual view showing a waterproof layer configuration according to the present invention, Figure 2 is an exemplary view showing the configuration of an embossed polyvinyl sheet according to the present invention, Figure 3 is a conceptual view showing the construction of an embossed polyvinyl sheet according to the present invention 4 is a planar view showing a construction state of the embossed polyvinyl sheet according to the present invention, the present invention is an asphalt primer layer for adhesion enhancement (1) applied on the concrete slab, continuous on the primer layer An embossed polyvinyl insulating sheet layer (2) arranged on one side and overlapping with each other, a string adhesive joint layer made of a porous ceramic thermoplastic resin-based asphalt continuously applied from a section of the asphalt primer layer to a section between the overlapping polyvinyl insulating sheets ( 3), a first porous ceramic thermoplastic resin which is a coating film waterproofing layer applied to the entire surface of the polyvinyl insulating sheet layer Asphalt layer 4, a reinforcement layer 5 made of a nonwoven fabric attached to the first porous ceramic thermoplastic resin-based asphalt layer, and a second porous ceramic thermoplastic resin-based asphalt layer 6 which is a coating waterproof layer formed on the reinforcement layer. And a composite waterproof layer structure laminated with the insulating polyvinyl film layer 7 attached to the second porous ceramic thermoplastic resin-based asphalt layer.

상기 엠보싱 폴리비닐 시트층(2)은 내구성이 우수한 다수개의 폴리비닐시트(21)가 연속 배열 설치된 것으로, 0.6∼0.8㎜의 두께를 구비하며, 상부는 아스팔트와의 접착력을 높이기 위해 폴리에스테르 부직포가 접착되고, 하부는 도 2 에 도시된 바와 같이 φ15㎜ 엠보싱(22)이 5㎜ 간격을 유지하고 다수개가 연속배열되어 있어 바탕에서의 습기가 공기가 분산되도록 되어 있다.The embossed polyvinyl sheet layer 2 is provided with a plurality of polyvinyl sheets 21 having excellent durability in a continuous arrangement. The embossed polyvinyl sheet layer 2 has a thickness of 0.6 to 0.8 mm, and a polyester nonwoven fabric is formed on the upper portion to increase adhesion to asphalt. As shown in Fig. 2, the φ15 mm embossing 22 maintains a 5 mm interval and a plurality of continuous arrays are arranged so that air in the ground is dispersed.

상기 줄접착층(3)은 일측 엠보싱 폴리비닐 시트와 이에 이웃하는 또다른 엠보싱 폴리비닐 시트를 연결하고, 엠보싱 폴리비닐시트를 바탕면에 연결하는 것으로, 엠보싱 폴리비닐시트의 겹쳐지는 부분과, 이에 연결되는 바탕면에 다공성 세라믹 열가소성 수지계 아스팔트를 연속도포하여 형성한다.The string adhesive layer 3 connects one side of the embossed polyvinyl sheet and another embossed polyvinyl sheet adjacent thereto, and connects the embossed polyvinyl sheet to the base surface, and the overlapping portion of the embossed polyvinyl sheet and connected thereto. It is formed by continuous coating a porous ceramic thermoplastic resin asphalt on the base surface.

또한, 상기 엠보싱 폴리비닐 시트층은 엠보싱 폴리비닐 시트의 중앙부와 바탕면 사이에 다공성 세라믹 열가소성 수지계 아스팔트를 도포하여 중앙부 줄접착층(31)을 형성하고, 상기 중앙부 줄접착층에 의해 엠보싱 폴리비닐 시트의 중앙부를 접착시킬 수 있다.In addition, the embossed polyvinyl sheet layer is coated with a porous ceramic thermoplastic resin asphalt between the central portion and the base surface of the embossed polyvinyl sheet to form a central string adhesive layer 31, the central portion of the embossed polyvinyl sheet by the central string adhesive layer Can be bonded.

상기 다공성 세라믹 열가소성 수지계 아스팔트는 열가소성수지인 스타이렌 부타디엔 스타이렌 수지(SBS)와 다공성 세라믹과 스트레이트 아스팔트를 주성분으로 하며 여기에 고무가소제, 쿠마론인덴수지, 노화방지제 및 산화방지제 등이 첨가되어 있다.The porous ceramic thermoplastic resin-based asphalt is composed of styrene butadiene styrene resin (SBS), a thermoplastic resin, a porous ceramic and straight asphalt, and a rubber plasticizer, coumarone indene resin, an antioxidant, an antioxidant, and the like are added thereto.

상기 스타이렌 부타디엔 스타이렌 수지는 부타디엔과 스타이렌의 공중합에 의한 합성고무로, 천연고무에 비하여 내약품성, 내노화성, 내후성, 내마모성 및 내열성이 우수한 장점을 구비한다.The styrene butadiene styrene resin is a synthetic rubber obtained by copolymerizing butadiene and styrene, and has excellent chemical resistance, aging resistance, weather resistance, abrasion resistance, and heat resistance as compared with natural rubber.

상기 다공성 세라믹은 단열 효과를 증진시키는 것으로, 비중은 0.6 - 0.8로서 우수한 흐름성과 저흡유가, 우수한 전기적 특성, 높은 녹는점(1200 - 1600℃)을 구비한다.The porous ceramic enhances the thermal insulation effect, and has a specific gravity of 0.6-0.8, and has excellent flowability and low oil absorption, excellent electrical properties, and high melting point (1200-1600 ° C).

상기 절연용 폴리비닐필름(PE)은 누름 콘크리트층의 온도 차이에 의한 거동이나 집중 응력에 의한 균열 발생 및 차량 이동에 의한 동적부가 하중이 방수층에 직접 간접적으로 전달될 경우에 응력의 분산 및 완화시킴으로써 도막 방수층의 피로성을 경감시키고, 내구수명을 연장시키는 역할을 하는 것으로, 약 0.1 ㎜ 의 두께를 구비하며, 2차 시공된 다공성 세라믹 열가소성 수지계 아스팔트 상부에 설치되어 누름 콘크리트와 절연시키도록 되어 있다.The insulation polyvinyl film (PE) is the stress caused by the temperature difference of the pressed concrete layer or the cracking caused by the concentrated stress and the dynamic part by the movement of the vehicle by dispersing and mitigating stress when the load is directly or indirectly transferred to the waterproof layer It serves to reduce the fatigue of the water-proof coating layer and to extend the service life, and has a thickness of about 0.1 mm, and is installed on the secondary porous ceramic thermoplastic resin-based asphalt to insulate the pressed concrete.

즉, 본 고안은 옥상 또는 지하의 콘크리트 슬래브 바탕면에 시공하고자 할 경우, 먼저 콘크리트 슬래브 바탕면의 이물질을 제거하고, 아스팔트 프라이머를 방수 바탕면에 도포하여 아스팔트 프라이머 층을 형성하며, 상기 형성된 아스팔트 프라이머 층 상부에 위치하도록 조인트용 다공성 세라믹 열가소성 수지계 아스팔트에 의해 다수개의 엠보싱 폴리비닐시트를 설치하여 엠보싱 폴리비닐시트층 형성하고, 상기 형성된 엠보싱 폴리비닐시트층에 세라믹 열가소성 수지계 아스팔트를 전면 도포하여 제 1 다공성 세라믹 열가소성 수지계 아스팔트층을 형성한다. 상기와 같이 형성된 제 1 다공성 세라믹 열가소성 수지계 아스팔트층 상부에 부직포를 설치하여 보강재층을 형성하고, 형성된 보강재층 상부에 다시 다공성 세라믹 열가소성 수지계 아스팔트층을 도포하여 제 2 다공성 세라믹 열가소성 수지계 아스팔트층을 형성한 후, 형성된 제 2 다공성 세라믹 열가소성 수지계 아스팔트층 상부에 절연용 폴리비닐(PE)필름을 설치하도록 되어 있다.That is, when the present invention is to be installed on the concrete slab base surface of the rooftop or underground, first remove the foreign matter on the concrete slab base surface, and apply the asphalt primer to the waterproof base surface to form an asphalt primer layer, the formed asphalt primer Embossed polyvinyl sheet layers are formed by installing a plurality of embossed polyvinyl sheets by the porous ceramic thermoplastic resin asphalt for jointing so as to be positioned above the layer, and the first porous by applying the ceramic thermoplastic resin asphalt to the formed embossed polyvinyl sheet layer in front. A ceramic thermoplastic resin asphalt layer is formed. The non-woven fabric is formed on the first porous ceramic thermoplastic resin-based asphalt layer formed as described above to form a reinforcement layer, and the second porous ceramic thermoplastic resin-based asphalt layer is formed by applying the porous ceramic thermoplastic resin-based asphalt layer on the formed reinforcement layer again. After that, the insulating polyvinyl (PE) film is formed on the second porous ceramic thermoplastic resin-based asphalt layer formed thereon.

상기 다수개의 엠보싱 폴리비닐시트는 도 3 및 도 4 에 도시된 바와 같이, 일측 엠보싱 폴리비닐시트와 이에 이웃하는 또다른 엠보싱 폴리비닐시트가 약 5∼10 ㎝의 일정한 폭을 유지하며 서로 일측이 겹쳐지게 설치된다. 즉, 상기 엠보싱 폴리비닐시트층은 다수개의 엠보싱 폴리비닐시트가 5∼10 ㎝ 폭으로 겹쳐져 설치되어 있다. 상기 절연용 엠보싱 폴리비닐시트의 상부면에는 부직포가 열융착에 의해 부착되어 있다.As shown in FIGS. 3 and 4, the plurality of embossed polyvinyl sheets have one side of the embossed polyvinyl sheet and another embossed polyvinyl sheet adjacent thereto while maintaining a constant width of about 5 to 10 cm and one side of each other overlapping each other. To be installed. That is, the embossed polyvinyl sheet layer is provided with a plurality of embossed polyvinyl sheets overlapping with a width of 5 to 10 cm. A nonwoven fabric is attached to the upper surface of the insulating embossed polyvinyl sheet by thermal fusion.

또한, 상기 5∼10 ㎝ 폭으로 겹쳐져 설치된 엠보싱 폴리비닐시트층은 열가소성 수지계 아스팔트에 의해 서로 줄접착되도록 되어 있으며, 엠보싱 폴리비닐 시트층과 아스팔트 플라이머층간의 접착력을 향상시키기 위하여 아스팔트 프라이머층에 약 5∼10 ㎝의 폭으로 열가소성 수지계 아스팔트를 도포하고 이를 통해 엠보싱 폴리비닐 시트층을 접착하도록 되어 있다. 즉, 상기 엠보싱 폴리비닐시트는 줄접착 조인트층의 연결부에 의해 이웃하는 폴리비닐시트 및 바탕면에 연결/설치되어 있으며, 상기 줄접착 조인트층의 연결부는 일측 폴리비닐시트와 이에 이웃하는 폴리비닐시트와의 겹쳐지는 부분(약 5∼10 ㎝)에 도포되는 열가소성 수지계 아스팔트와, 이에 연결되는 아스팔트 프라이머층에 약 5∼10 ㎝ 폭으로 도포되는 열가소성 수지계 아스팔트로 이루어져 있으며, 줄접착 조인트층 연결부의 전체 폭(일측 엠보싱 폴리비닐시트의 겹쳐지는 부분과 이에 연결되는 아스팔트 프라이머 층에 도포되는 부분의 합)은 14∼16 ㎝을 구비하는 것이 바람직하다.In addition, the embossed polyvinyl sheet layers provided to overlap each other with the width of 5 to 10 cm are bonded to each other by thermoplastic resin-based asphalt. The embossed polyvinyl sheet layers are roughly applied to the asphalt primer layer to improve the adhesive force between the embossed polyvinyl sheet layer and the asphalt primer layer. The thermoplastic resin-based asphalt is applied to a width of 5 to 10 cm to thereby bond the embossed polyvinyl sheet layer. That is, the embossed polyvinyl sheet is connected / installed to the neighboring polyvinyl sheet and the base surface by the connection portion of the string adhesive joint layer, and the connection portion of the string adhesive joint layer is one polyvinyl sheet and the neighboring polyvinyl sheet. It consists of a thermoplastic resin asphalt applied to the overlapped portion (about 5 to 10 cm) and a thermoplastic resin asphalt applied to the asphalt primer layer connected to about 5 to 10 cm in width, It is preferable that the width (sum of the overlapping portion of one side of the embossed polyvinyl sheet and the portion applied to the asphalt primer layer connected thereto) is 14 to 16 cm.

또한, 상기 제 1,2 차 다공성 세라믹 열가소성 수지계 아스팔트층은 각각 약 1∼2㎜ 의 두께를 유지하는 것이 바람직하다.In addition, it is preferable that the first and second porous ceramic thermoplastic resin asphalt layers each have a thickness of about 1 to 2 mm.

이하 본 고안의 복합방수층구조를 시공하는 바람직한 실시예 복합방수공법을 각 단계별로 설명하면 다음과 같다.Hereinafter, a preferred embodiment of the composite waterproof method for constructing a composite waterproof layer structure according to the present invention will be described as follows.

상기와 같이 구성된 본 고안을 이용하여 건물옥상 또는 지하에 방수층을 형성하고자 할 경우,If you want to form a waterproof layer on the building roof or basement using the present invention configured as described above,

먼저, 콘크리트 슬래브 바탕면 상태를 확인하고 이물질 등을 청소하고 바탕면을 정리하는 제 1 단계;First, the first step of checking the concrete slab base surface condition, cleaning foreign matters, etc. to clean up the base surface;

접착증강용 아스팔트 프라이머를 붓이나 롤러를 사용하여(0.3ℓ/㎡) 방수 바탕면에 도포하는 제 2 단계;A second step of applying an adhesion-enhancing asphalt primer to a waterproof base surface using a brush or a roller (0.3 L / m 2);

접착증강용 아스팔트 프라이머의 용제가 휘발되면 조인트용 다공성 세라믹 열가소성수지 수지계 아스팔트를 아스팔트 프라이머층 일부 구간에 1∼3㎜로 도포하는 제 3 단계;A third step of applying a porous ceramic thermoplastic resin-based asphalt for joints at a portion of 1 to 3 mm in a portion of the asphalt primer layer when the solvent of the adhesion-enhancing asphalt primer is volatilized;

0.7㎜의 두께를 구비하는 하부 절연용 엠보싱 폴리비닐시트를 재단하여 상부쪽에 부직포면이 보인 상태에서 바탕면 및 일부구간에 도포된 다공성 세라믹 열가소성 수지계 아스팔트면에 설치하는 제 4 단계;A fourth step of cutting the lower insulating embossed polyvinyl sheet having a thickness of 0.7 mm and installing it on the porous ceramic thermoplastic resin-based asphalt surface applied to the base surface and a part section in a state where the nonwoven fabric surface is visible on the upper side;

상기 설치된 엠보싱 폴리비닐시트의 끝부분에서 양쪽으로 7㎝의 폭을 유지하도록 다공성 세라믹 열가소성 수지계 아스팔트를 펴 바르고, 이 위에 이웃하는 또다른 엠보싱 폴리비닐시트를 다공성 세라믹 열가소성 수지계 아스팔트가 도포된 폭만큼 겹쳐 설치하는 제 5 단계;The porous ceramic thermoplastic resin asphalt is spread on the both ends of the installed embossed polyvinyl sheet to maintain a width of 7 cm on both sides, and another neighboring embossed polyvinyl sheet is overlapped by the width coated with the porous ceramic thermoplastic resin asphalt. A fifth step of installing;

상기 엠보싱 폴리비닐시트 사이에 위치하는 조인트용 다공성 세라믹 열가소성 수지계 아스팔트가 경화되기 전에 압착용 롤러를 사용하여 조인트을 눌러주는제 6 단계;A sixth step of pressing the joint using a pressing roller before the porous ceramic thermoplastic resin-based asphalt for joints located between the embossed polyvinyl sheets is cured;

상기 상부에 위치하는 엠보싱 폴리비닐시트를 길이방향으로 젖히고 도포된 7㎝의 조인트용 다공성 세라믹 열가소성 수지계 아스팔트와 연결되도록 또한, 총 도포 폭이 15㎝ 가 되게 바탕면에 다공성 세라믹 열가소성 수지계 아스팔트를 도포한 후 젖혀놓은 시트를 원위치하고 이를 압착용 롤러로 눌러 주는 제 7 단계;The embossed polyvinyl sheet positioned at the upper side was rolled in the longitudinal direction and connected to the porous ceramic thermoplastic resin-based asphalt for joints of 7 cm, and the porous ceramic thermoplastic resin-based asphalt was applied to the base surface such that the total coating width was 15 cm. A seventh step of returning the folded sheet to its original position and pressing it with a pressing roller;

상기 제 5 단계와 6 단계를 반복하여 연속적으로 행하여 엠보싱 폴리비닐시트층을 형성하는 제 8 단계;An eighth step of forming the embossed polyvinyl sheet layer by repeating the fifth and sixth steps successively;

상기 형성된 엠보싱 폴리비닐 시트층의 가장자리부터 다공성 세라믹 열가소성 수지계 아스팔트를 전면 도포하여 두께 1∼2㎜ 의 제 1 다공성 세라믹 열가소성 수지계 아스팔트층을 형성하는 제 9 단계;A ninth step of forming a first porous ceramic thermoplastic resin asphalt layer having a thickness of 1 to 2 mm by completely applying the porous ceramic thermoplastic resin asphalt from an edge of the formed embossed polyvinyl sheet layer;

상기 형성된 1차 다공성 세라믹 열가소성 수지계 아스팔트층 상부에 부직포로 이루어진 보강재층을 설치하는 제 10 단계;A tenth step of installing a reinforcement layer made of a nonwoven fabric on the formed first porous ceramic thermoplastic resin-based asphalt layer;

상기 설치된 보강재층 상부에 다공성 세라믹 열가소성 수지계 아스팔트를 다시 전면 도포하여 두께 1∼2㎜ 의 2차 다공성 세라믹 열가소성 수지계 아스팔트층을 형성하는 제 11 단계;An eleventh step of forming a second porous ceramic thermoplastic resin-based asphalt layer having a thickness of 1 to 2 mm by completely applying the porous ceramic thermoplastic resin-based asphalt again on the installed reinforcement layer;

상기 형성된 2차 다공성 세라믹 열가소성 수지계 아스팔트층의 상부에 절연용 PE필름을 설치하여 누름 콘크리트와 절연시키는 제 12 단계를 통해 복합방수층 구조를 이루도록되어 있다.By installing an insulating PE film on top of the formed secondary porous ceramic thermoplastic resin-based asphalt layer, the composite waterproof layer structure is formed through a twelfth step of insulating the pressed concrete.

이와 같이 본 고안은 내구성과 내열성이 우수한 보강 복합형의 엠보싱 문양이 설계된 폴리비닐시트를 다공성 세라믹 열가소성 수지계 아스팔트에 의해 부분적으로 접착 되도록 되어 있어, 도막방수재의 두께 확보, 물리적 강도 보강과 현장풀질관리가 용이하고, 바탕층의 영향 완화, 바탕의 거동에 대한 거동 대응성 증가로 방수층의 파괴를 방지할 수 있다.As such, the present invention is designed to partially bond the polyvinyl sheet designed with the reinforced embossed pattern having excellent durability and heat resistance by porous ceramic thermoplastic resin asphalt, thereby securing the thickness of the coating waterproofing material, reinforcing physical strength, and controlling the field quality. It is easy to prevent the destruction of the waterproof layer by mitigating the influence of the base layer, and increasing the response to the behavior of the base layer.

또한, 보강재(부직포)가 설치되어 있어, 인장 인열강도 및 균열 추종성을 향상시켰으며, 시트방수의 문제점인 조인트 파괴 문제를 효과적으로 보완하였다.In addition, a reinforcing material (non-woven fabric) is installed to improve tensile tear strength and crack followability, and effectively compensate for the joint fracture problem, which is a problem of sheet waterproofing.

또한, 다수개의 폴리비닐시트는 조인트 씰 봉합 처리 및 바탕과의 줄접착되어 있어, 누수 사고시 부분적인 보수가 가능하며, 이로인해 단속적인 방수성을 유지할 수 있는 등 많은 효과가 있다.In addition, a plurality of polyvinyl sheet is a joint seal sealing process and the line adhesion with the base, it is possible to partially repair in case of water leakage accident, thereby maintaining intermittent waterproofness, there are many effects.

Claims (7)

콘크리트 스래브 위에 도포되는 접착증강용 아스팔트 프라이머층;Adhesion primer asphalt primer layer applied on the concrete slab; 상기 프라이머층 상부에 연속 배열되고 일측이 겹치게 설치되는 엠보싱 폴리비닐 절연 시트층;An embossed polyvinyl insulating sheet layer which is continuously arranged on the primer layer and has one side overlapped; 상기 아스팔트 프라이머층 일부구간부터 상기 겹치게 설치된 양 폴리비닐 절연 시트간의 구간에 연속 도포된 다공성 세라믹 열가소성 수지계 아스팔트로 이루어진 줄접착 조인트층;A string adhesive joint layer made of a porous ceramic thermoplastic resin-based asphalt continuously applied from a portion of the asphalt primer layer to a portion of the overlapping polyvinyl insulating sheets; 상기 폴리비닐 절연 시트층 상부에 전면 도포되는 도막방수층인 제 1다공성 세라믹 열가소성 수지계 아스팔트층;A first porous ceramic thermoplastic resin asphalt layer which is a coating waterproof layer coated on the polyvinyl insulating sheet layer on the front; 상기 제 1 다공성 세라믹 열가소성 수지계 아스팔트층에 부착된 부직포로 이루어진 보강재층;A reinforcement layer made of a nonwoven fabric attached to the first porous ceramic thermoplastic resin asphalt layer; 상기 보강재층 상부에 도포되어 형성된 도막방수층인 제 2 다공성 세라믹 열가소성 수지계 아스팔트층;A second porous ceramic thermoplastic resin-based asphalt layer which is a coating waterproof layer formed on the reinforcing material layer; 상기 제 2 다공성 세라믹 열가소성 수지계 아스팔트층 상부에 부착된 절연용 폴리비닐필름층으로 적층되어 구성된 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.Partially insulating block-type unexposed composite waterproof layer structure, characterized in that the stack is formed of an insulating polyvinyl film layer attached on the second porous ceramic thermoplastic resin-based asphalt layer. 제 1 항에 있어서;The method of claim 1; 상기 엠보싱 폴리비닐 시트는 하부에 φ12∼18㎜ 엠보싱이 3∼8㎜ 간격을 유지하고 다수개가 연속 배열되어 있는 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.The partially embossed polyvinyl sheet is a partially insulated block-type unexposed composite waterproof layer structure, wherein a plurality of φ 12-18 mm embossings are spaced 3-8 mm apart and arranged in series. 제 1 항에 있어서;The method of claim 1; 상기 엠보싱 폴리비닐 시트는 0.6∼0.8㎜의 두께를 구비하는 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.The partially embossed polyvinyl sheet has a thickness of 0.6 to 0.8 mm. 제 1 항 내지 제 3 항 중 어느 한 항에 있어서;The method of any one of claims 1 to 3; 상기 엠보싱 폴리비닐 시트 상부에는 폴리에스테르 부직포가 열융착되어 있는 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.Partially insulating block-type unexposed composite waterproof layer structure, characterized in that the polyester non-woven fabric is heat-sealed on the embossed polyvinyl sheet. 제 1 항에 있어서;The method of claim 1; 상기 엠보싱 폴리비닐 시트층은 일측 엠보싱 폴리비닐 시트와 이웃하는 또다른 엠보싱 폴리비닐 시트가 5∼10 ㎝ 폭으로 겹쳐져 설치된 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.The embossed polyvinyl sheet layer is partially insulating block-type unexposed composite waterproof layer structure, characterized in that one side embossed polyvinyl sheet and another neighboring embossed polyvinyl sheet is installed overlapping 5 to 10 cm in width. 제 1 항에 있어서;The method of claim 1; 상기 줄접착층은 14∼16 ㎝ 폭을 유지하는 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.The partially bonded block-type unexposed composite waterproofing layer structure, wherein the string adhesive layer maintains a width of 14 to 16 cm. 제 1 항에 있어서;The method of claim 1; 상기 제 1, 2 다공성 세라믹 열가소성 수지계 아스팔트층은 각각 두께 1∼2㎜ 를 유지하는 것을 특징으로 하는 부분절연 블록형 비노출 복합방수층 구조.The first and second porous ceramic thermoplastic resin-based asphalt layers each have a thickness of 1 to 2 mm, wherein the partially insulating block type unexposed composite waterproof layer structure.
KR20-2003-0038437U 2003-12-10 2003-12-10 Non-exposure complex construction structure of insulating partial block type using embossing polyvinyl sheet porous ceramic-thermoplastic resin-asphalt membrane waterproofing material KR200350444Y1 (en)