KR20030054956A - Fluorescent material of plasma display panel and method of fabricating the same - Google Patents

Fluorescent material of plasma display panel and method of fabricating the same Download PDF

Info

Publication number
KR20030054956A
KR20030054956A KR1020010085390A KR20010085390A KR20030054956A KR 20030054956 A KR20030054956 A KR 20030054956A KR 1020010085390 A KR1020010085390 A KR 1020010085390A KR 20010085390 A KR20010085390 A KR 20010085390A KR 20030054956 A KR20030054956 A KR 20030054956A
Authority
KR
South Korea
Prior art keywords
ybo
phosphor
zso
layer
display panel
Prior art date
Application number
KR1020010085390A
Other languages
Korean (ko)
Other versions
KR100433223B1 (en
Inventor
정재상
Original Assignee
엘지전자 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지전자 주식회사 filed Critical 엘지전자 주식회사
Priority to KR10-2001-0085390A priority Critical patent/KR100433223B1/en
Publication of KR20030054956A publication Critical patent/KR20030054956A/en
Application granted granted Critical
Publication of KR100433223B1 publication Critical patent/KR100433223B1/en

Abstract

PURPOSE: A phosphor of a plasma display panel and a fabricating method thereof are provided to protect green phosphors from the sputtering and lengthen a lifetime of the plasma display panel by stacking a mixed layer having an anti-sputtering characteristic on the first green phosphor layer. CONSTITUTION: A phosphor of a plasma display panel includes a phosphor layer and a protective layer(40). The phosphor layer is formed with light emitting materials(36G1,36G2). The protective layer is formed on the phosphor layer and contains an anti-sputtering characteristic more than the anti-sputtering characteristic of the phosphor layer. The phosphor layer is formed with the light emitting material such as Zn2SiO4:Mn2+. The protective layer is formed by mixing one of YBO3:Tb3+, YBO:ZSO of 3:1, YBO:ZSO of 1:1, YBO:ZSO of 1:3 with Zn2SiO4:Mn2+. The protective layer faces a discharge space.

Description

플라즈마 디스플레이 패널의 형광체 및 그 제조방법{FLUORESCENT MATERIAL OF PLASMA DISPLAY PANEL AND METHOD OF FABRICATING THE SAME}Phosphor of plasma display panel and manufacturing method thereof {FLUORESCENT MATERIAL OF PLASMA DISPLAY PANEL AND METHOD OF FABRICATING THE SAME}

본 발명은 플라즈마 디스플레이 패널의 구동방법에 관한 것으로, 특히 플라즈마 디스플레이 패널의 수명을 연장시키도록 한 플라즈마 디스플레이 패널의 형광체에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of driving a plasma display panel, and more particularly, to a phosphor of a plasma display panel for extending the life of the plasma display panel.

플라즈마 디스플레이 패널(Plasma Display Panel : 이하 "PDP"라 한다)은 He+Xe, Ne+Xe, He+Xe+Ne 등의 불활성 혼합가스가 방전할 때 발생하는 147nm의 진공자외선이 형광체를 발광시킴으로써 화상을 표시하게 된다. 이러한 PDP는 박막화와 대형화가 용이할 뿐만 아니라 최근의 기술 개발에 힘입어 화질이 향상되고 있다.Plasma Display Panel (hereinafter referred to as "PDP") is an image of 147 nm vacuum ultraviolet rays generated when an inert mixed gas such as He + Xe, Ne + Xe, He + Xe + Ne discharges to emit phosphors. Will be displayed. Such PDPs are not only thin and large in size, but also have improved in image quality due to recent technology development.

도 1을 참조하면, 3전극 교류 면방전형 PDP의 방전셀은 상부기판(16) 상에 형성되어진 서스테인전극쌍(4)과, 하부기판(14) 상에 형성되어진 어드레스전극(2)을 구비한다.Referring to FIG. 1, a discharge cell of a three-electrode AC surface discharge type PDP includes a sustain electrode pair 4 formed on the upper substrate 16 and an address electrode 2 formed on the lower substrate 14. .

서스테인전극쌍(4) 각각은 인듐틴옥사이드(Indium-Tin-Oxide : ITO) 등의 투명전극과, 투명전극의 선폭보다 작은 선폭을 가지며, 투명전극의 일측 가장자리에 형성되는 금속버스전극을 포함한다. 금속버스전극은 Cr/Cu/Cr을 증착법으로 적층한 후에 에칭공정을 거쳐 형성된다. 서스테인전극쌍(4)이 스크린인쇄나 진공증착법으로 형성된 상부기판(16)에는 상부 유전체층(12)과 보호막(10)이 적층된다. 상부 유전체층(12)에는 플라즈마 방전시 발생된 벽전하가 축적된다. 보호막(10)은 대략 5000 Å 정도의 두께로 상부 유전체층(12) 상에 형성되어 플라즈마 방전시 발생된 스퍼터링으로 인한 상부 유전체층(12)과 서스테인전극쌍(4)의 손상을 방지함과 아울러 2차 전자의 방출 효율을 높이게 된다. 보호막(10)으로는 통상 산화마그네슘(MgO)이 이용된다.Each of the sustain electrode pairs 4 includes a transparent electrode such as indium tin oxide (ITO), a metal bus electrode having a line width smaller than that of the transparent electrode, and formed at one edge of the transparent electrode. . The metal bus electrode is formed by laminating Cr / Cu / Cr by vapor deposition and then etching. The upper dielectric layer 12 and the protective film 10 are stacked on the upper substrate 16 on which the sustain electrode pairs 4 are formed by screen printing or vacuum deposition. Wall charges generated during plasma discharge are accumulated in the upper dielectric layer 12. The passivation layer 10 is formed on the upper dielectric layer 12 to a thickness of approximately 5000 Å to prevent damage to the upper dielectric layer 12 and the sustain electrode pair 4 due to sputtering generated during plasma discharge, The electron emission efficiency is improved. As the protective film 10, magnesium oxide (MgO) is usually used.

어드레스전극(2)이 형성된 하부기판(14) 상에는 하부 유전체층(18), 격벽(8)이 형성되며, 하부 유전체층(18)과 격벽(8)의 표면에는 스크린 프린팅공정으로 형광체(6)가 형성된다. 어드레스전극(2)은 서스테인전극쌍(4)과 직교된다. 격벽(8)은 스크린 프린팅공정이나 금형법 등으로 형성되어 방전에 의해 생성된 자외선 및 가시광이 인접한 방전셀에 누설되는 것을 방지한다. 형광체(6)는 플라즈마 방전시 발생된 진공 자외선(VUV)에 의해 여기되어 적색, 녹색 또는 청색 중 어느 하나의 가시광선을 발생하게 된다.The lower dielectric layer 18 and the partition wall 8 are formed on the lower substrate 14 on which the address electrode 2 is formed, and the phosphor 6 is formed on the surfaces of the lower dielectric layer 18 and the partition wall 8 by a screen printing process. do. The address electrode 2 is orthogonal to the sustain electrode pair 4. The partition wall 8 is formed by a screen printing process, a mold method, or the like to prevent ultraviolet rays and visible light generated by the discharge from leaking into adjacent discharge cells. The phosphor 6 is excited by vacuum ultraviolet (VUV) generated during plasma discharge to generate visible light of any one of red, green, and blue.

상/하부기판(16,14)과 격벽(8) 사이에 마련된 방전셀의 방전공간에는 방전을 위한 He+Xe, Ne+Xe, He+Xe+Ne 등의 불활성 혼합가스가 주입된다.An inert mixed gas such as He + Xe, Ne + Xe, He + Xe + Ne for discharging is injected into the discharge space of the discharge cells provided between the upper and lower substrates 16 and 14 and the partition wall 8.

형광체(6)는 진공자외선(VUV)에 의해 여기 발광되며, 발광되는 빛의 파장에 따라 적색 형광체, 녹색 형광체 및 청색 형광체로 나뉘어진다.The phosphor 6 is excited by vacuum ultraviolet (VUV) light and is divided into a red phosphor, a green phosphor and a blue phosphor according to the wavelength of light emitted.

도 2를 참조하면, PDP에서 일반적으로 사용되는 적색 형광체의 조성은(YGdBO3: Eu3+)이며, 녹색 형광체의 조성은 Zn2SiO4: Mn2+이다. 그리고 청색 형광체의 조성은 BaMgAl10O17: Eu2+이다. 이 중 녹색 형광체는 전체 휘도에서 차지하는 비율이 가장 크다. 그런데 녹색 형광체는 - 대전특성을 가지므로 방전시 발생되는 양이온의 스퍼터링 즉, 양이온으로 인한 충격에 의해 결정파괴가 쉽게 일어나며, 그로 인하여 시간이 경과함에 따라 녹색광의 휘도가 급격히 떨어지는 경향이 있다. 특히, 방전시 발생된 양이온은 음이온에 비하여 질량이 크므로 녹색 형광체에 가해지는 충격 에너지는 매우 크게 된다. 전술한 바와 같이 녹색 형광체의 휘도 비율이 전체 휘도를 좌우하므로 녹색 형광체의 휘도 저하는 PDP의 수명저하를 초래하게 된다. 결과적으로, PDP의 수명을 연장하기 위해서는 녹색 형광체의 안티-스퍼터링(Anti-sputtering) 또는 내충격성을 강화하는 것이 선결과제로 지적되고 있다.Referring to FIG. 2, the composition of a red phosphor generally used in PDP is (YGdBO 3 : Eu 3+ ), and the composition of the green phosphor is Zn 2 SiO 4 : Mn 2+ . The composition of the blue phosphor is BaMgAl 10 O 17 : Eu 2+ . Among these, the green phosphor has the largest proportion in the overall luminance. However, since the green phosphor has a negative charge characteristic, crystal destruction easily occurs due to sputtering of a cation generated during discharge, that is, an impact caused by a cation, and as a result, the luminance of green light tends to drop rapidly as time passes. In particular, since the cations generated during discharge have a larger mass than the anions, the impact energy applied to the green phosphor is very large. As described above, since the luminance ratio of the green phosphor dictates the overall luminance, the decrease in the luminance of the green phosphor causes the lifetime of the PDP. As a result, in order to extend the life of the PDP, it is pointed out as a priority to enhance the anti-sputtering or impact resistance of the green phosphor.

따라서, 본 발명의 목적은 PDP의 수명을 연장시키도록 한 PDP의 형광체를 제공함에 있다.Accordingly, it is an object of the present invention to provide a phosphor of a PDP that is intended to extend the life of the PDP.

도 1은 종래의 3전극 교류 면방전형 플라즈마 디스플레이 패널의 방전셀 구조를 나타내는 사시도이다.1 is a perspective view showing a discharge cell structure of a conventional three-electrode AC surface discharge type plasma display panel.

도 2는 도 1에 도시된 플라즈마 디스플레이 패널을 부분 절개하여 나타내는 단면도이다.FIG. 2 is a cross-sectional view of a portion of the plasma display panel shown in FIG. 1.

도 3은 본 발명의 실시예에 따른 플라즈마 디스플레이 패널을 나타내는 단면도이다.3 is a cross-sectional view illustrating a plasma display panel according to an exemplary embodiment of the present invention.

도 4는 본 발명의 실시예에 따른 플라즈마 디스플레이 패널의 다층 녹색 형광체에 포함되는 물질의 안티-스퍼터링 특성을 나타내는 그래프이다.4 is a graph showing anti-sputtering characteristics of a material included in a multilayer green phosphor of a plasma display panel according to an exemplary embodiment of the present invention.

도 5는 본 발명의 실시예에 따른 플라즈마 디스플레이 패널과 종래의 플라즈마 디스플레이 패널을 대비하여 시간 경과에 따른 휘도 특성을 나타내는 그래프이다.5 is a graph showing luminance characteristics over time in comparison with a plasma display panel according to an exemplary embodiment of the present invention.

< 도면의 주요 부분에 대한 부호의 설명 ><Description of Symbols for Main Parts of Drawings>

2,32 : 어드레스전극 4,34 : 서스테인전극쌍2,32: address electrode 4,34: sustain electrode pair

6,36G1,36G2 : 형광체 8,38 : 격벽6,36G1,36G2: Phosphor 8,38: Bulkhead

10,40 : 보호막 12,18,42,48 : 유전층10,40: protective film 12,18,42,48: dielectric layer

14,44 : 하부기판 16,46 : 상부기판14,44: Lower board 16,46: Upper board

상기 목적을 달성하기 위하여, 본 발명의 실시예에 따른 PDP의 형광체는 발광물질로 이루어진 형광층과, 형광층보다 안티-스퍼터링 특성이 큰 물질을 함유하여 형광층 상에 형성되는 보호층을 구비한다.In order to achieve the above object, the phosphor of the PDP according to the embodiment of the present invention includes a fluorescent layer made of a light emitting material and a protective layer formed on the fluorescent layer by containing a material having a greater anti-sputtering property than the fluorescent layer. .

상기 형광층의 물질은 Zn2SiO4: Mn2+인 것을 특징으로 한다.The material of the fluorescent layer is characterized in that Zn 2 SiO 4 : Mn 2+ .

상기 보호층의 물질은 Zn2SiO4: Mn2+에 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중의 어느 하나가 혼합된 것을 특징으로 한다.The material of the protective layer is Zn 2 SiO 4 : Mn 2 + YBO 3 : Tb 3 + , YBO: ZSO 3: 1, YBO: ZSO 1: 1, YBO: ZSO 1: 3 characterized in that any one is mixed It is done.

상기 보호층은 방전공간과 면하는 것을 특징으로 한다.The protective layer is characterized by facing the discharge space.

상기 보호층에는 Zn2SiO4: Mn2+대비 10∼90%의 혼합비로 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중 적어도 어느 하나가 Zn2SiO4: Mn2+과 혼합되는 것을 특징으로 한다.At least any one of YBO 3 : Tb 3+ , YBO: ZSO 3: 1, YBO: ZSO 1: 1, and YBO: ZSO 1: 3 may be included in the protective layer in a mixing ratio of 10 to 90% of Zn 2 SiO 4 : Mn 2+ . It is characterized in that one is mixed with Zn 2 SiO 4 : Mn 2+ .

본 발명의 실시예에 따른 PDP의 형광체의 제조방법은 기판 상에 발광물질로 이루어진 형광층을 형성하는 단계와, 형광층보다 안티-스퍼터링 특성이 큰 물질이 함유된 보호층을 형광층 상에 형성하는 단계를 포함한다.In the method of manufacturing a phosphor of a PDP according to an embodiment of the present invention, forming a phosphor layer of a light emitting material on a substrate, and forming a protective layer containing a material having a greater anti-sputtering property than the phosphor layer on the phosphor layer It includes a step.

이하, 도 3 내지 도 5를 참조하여 본 발명의 바람직한 실시예에 대하여 설명하기로 한다.Hereinafter, exemplary embodiments of the present invention will be described with reference to FIGS. 3 to 5.

도 3을 참조하면, 본 발명의 실시예에 따른 PDP의 녹색 형광체는 녹색 형과물질로 이루어진 제1 형광체(36G1)과, 높은 안티-스퍼터링 특성을 가지는 물질이 혼합된 제2 형광체(36G2)가 적층된다.Referring to FIG. 3, a green phosphor of a PDP according to an embodiment of the present invention may include a first phosphor 36G1 made of a green mold and a second phosphor 36G2 mixed with a material having high anti-sputtering characteristics. Are stacked.

이 PDP의 상판은 상부기판(46) 상에 형성되어진 서스테인전극쌍(34), 서스테인전극쌍(34)이 형성된 상부기판(46) 상에 적층되는 상부 유전체층(42) 및 보호막(40)을 포함한다. 서스테인전극쌍(34) 각각은 인듐틴옥사이드(Indium-Tin-Oxide : ITO) 등의 투명전극과, 투명전극의 선폭보다 작은 선폭을 가지며 투명전극의 일측 가장자리에 형성되는 금속버스전극을 포함한다. 이 서스테인전극쌍(34) 중 어느 하나는 셀을 선택하기 위한 어드레스 기간에 부극성의 스캔펄스가 공급되어 주사라인을 선택하는 스캔전극 역할을 겸하게 된다. 또한, 서스테인전극쌍(34)은 서스테인기간에 교번적으로 서스테인펄스가 공급되어 어드레스방전에 의해 선택된 셀에 대하여 유지방전을 일으키게 된다. 상부 유전체층(42)에는 플라즈마 방전시 발생된 벽전하가 축적된다. 보호막(40)은 MgO 등의 재료로 형성되어 플라즈마 방전시 발생된 스퍼터링으로 인한 상부 유전체층(42)과 서스테인전극쌍(34)의 손상을 방지함과 아울러 2차 전자의 방출 효율을 높이게 된다.The top plate of the PDP includes a sustain electrode pair 34 formed on the upper substrate 46, an upper dielectric layer 42 and a protective film 40 stacked on the upper substrate 46 on which the sustain electrode pair 34 is formed. do. Each of the sustain electrode pairs 34 includes a transparent electrode such as indium tin oxide (ITO), and a metal bus electrode having a line width smaller than that of the transparent electrode and formed at one edge of the transparent electrode. One of the sustain electrode pairs 34 serves as a scan electrode for selecting a scan line by supplying a negative scan pulse in an address period for selecting a cell. In the sustain electrode pair 34, sustain pulses are alternately supplied during the sustain period to cause sustain discharge for the cells selected by the address discharge. In the upper dielectric layer 42, wall charges generated during plasma discharge are accumulated. The passivation layer 40 is formed of a material such as MgO, thereby preventing damage to the upper dielectric layer 42 and the sustain electrode pair 34 due to sputtering generated during plasma discharge, and increasing emission efficiency of secondary electrons.

이 PDP의 하판은 하부기판(44) 상에 형성되어진 어드레스전극(32)과, 어드레스전극(32)을 덮도록 하부기판(44) 상에 전면 증착되는 하부 유전체층(48), 하부 유전체층(48)으로부터 수직으로 형성되는 격벽(38) 및, 하부 유전체층(48)과 격벽(38)의 표면에 형성된 형광체(36R,36G,36B)를 포함한다. 어드레스전극(32)은 서스테인전극쌍(34)과 직교되어 서스테인전극쌍(34) 중 어느 하나에 공급되는 스캔펄스에 동기되는 정극성의 데이터펄스가 공급된다. 이 어드레스전극(32)과 서스테인전극쌍(34) 중 어느 하나 사이에 대향방전 형태로 일어나는 어드레스방전에 의해 셀이 선택된다. 격벽(38)은 어드레스전극(32)과 나란하게 형성되어 방전에 의해생성된 자외선 및 가시광이 인접한 방전셀에 누설되는 것을 방지한다. 형광체에 있어서, 적색 형광체는 GdBO3: Eu3+이며, 청색 형광체는 BaMgAl10O17: Eu2+이다. 그리고 녹색 형광체의 제1 형광층(36G1)은 격벽(38)과 기판(44) 상에 형성되며, 제2 형광층(36G2)은 제1 형광층(36G2) 상에 형성된다.The lower plate of the PDP includes an address electrode 32 formed on the lower substrate 44, a lower dielectric layer 48 and a lower dielectric layer 48 deposited on the lower substrate 44 so as to cover the address electrode 32. And a partition wall 38 formed vertically from the lower dielectric layer 48 and phosphors 36R, 36G, and 36B formed on the surface of the partition wall 38. The address electrode 32 is orthogonal to the sustain electrode pair 34 and supplied with a positive data pulse synchronized with the scan pulse supplied to any one of the sustain electrode pair 34. The cell is selected by the address discharge occurring in the form of counter discharge between any one of the address electrode 32 and the sustain electrode pair 34. The partition wall 38 is formed in parallel with the address electrode 32 to prevent the ultraviolet rays and the visible light generated by the discharge from leaking to the adjacent discharge cells. In the phosphor, the red phosphor is GdBO 3 : Eu 3+ and the blue phosphor is BaMgAl 10 O 17 : Eu 2+ . The first fluorescent layer 36G1 of the green phosphor is formed on the partition 38 and the substrate 44, and the second fluorescent layer 36G2 is formed on the first fluorescent layer 36G2.

녹색 형광체의 제1 및 제2 형광층(36G1,36G2)은 모두 스크린 프린팅으로 형성되며, 그 물질과 그 안티-스퍼터링 특성은 다음의 표 1과 같이 정리 될 수 있다.The first and second fluorescent layers 36G1 and 36G2 of the green phosphor are both formed by screen printing, and the material and its anti-sputtering characteristics may be summarized as shown in Table 1 below.

녹색 형광체Green phosphor 두께(μm)Thickness (μm) 물질matter 안티-스퍼터링특성Anti-sputtering characteristics 제1 형광층(36G1)First fluorescent layer 36G1 ∼수십μmTo several tens of μm Zn2SiO4: Mn2+ Zn 2 SiO 4 : Mn 2+ 보통(normal)Normal 제2 형광층(36G2)Second fluorescent layer 36G2 수∼수십μmSeveral to several ten μm Zn2SiO4: Mn2++ YBO3: Tb3+외 안티-스퍼터링특성이 우수한 물질Zn 2 SiO 4 : Mn 2+ + YBO 3 : Tb 3+ and other materials with excellent anti-sputtering properties 아수(good)Good

제2 형광층(36G2)은 셀의 방전공간과 접하여 이온이 직접 충돌하게 되지만 도 4에서 알 수 있는 바 녹색 형광물질 Zn2SiO4: Mn2+과 혼합되는 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 등의 물질이 안티-스퍼터링 특성이 Zn2SiO4: Mn2+에 비하여 50% 이상 우수하므로 물리적인 손상이 작음은 물론 도 5와 같이 장시간 경과하여도 종래의 녹색 형광체에 비하여 휘도가 높은 수준을 유지하게 되므로 그 만큼 PDP의 수명을 연장시킬 수 있게 된다. 여기서, 형광층(36G2)의 혼합비는 Zn2SiO4: Mn2+대비 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중 적어도 어느 하나가 10∼90% 혼합된다.The second fluorescent layer 36G2 directly contacts the discharge space of the cell and directly collides with ions, but it can be seen from FIG. 4 that YBO 3 : Tb 3+ , YBO: mixed with the green phosphor Zn 2 SiO 4 : Mn 2+. Since ZSO 3: 1, YBO: ZSO 1: 1, YBO: ZSO 1: 3, etc., the anti-sputtering property is superior to Zn 2 SiO 4 : Mn 2+ by 50% or more, so that physical damage is small as well. Even after a long time as shown in Fig. 5, since the luminance is maintained higher than that of the conventional green phosphor, the lifetime of the PDP can be extended. Here, the mixing ratio of the fluorescent layer 36G2 is at least one of YBO 3 : Tb 3+ , YBO: ZSO 3: 1, YBO: ZSO 1: 1, and YBO: ZSO 1: 3 relative to Zn 2 SiO 4 : Mn 2+ . Is mixed 10-90%.

한편, 본 발명에 따른 PDP의 형광체는 다층 구조의 형광체를 녹색 형광체를 중심으로 설명하였지만 녹색 형광체뿐 아니라 적색 형광체 및 청색 형광체를 다층 구조로 하고 그 다층 구조에서 방전공간과 면하는 층에 안티-스퍼터링 특성이 우수한 물질을 혼합할 수도 있다.On the other hand, the phosphor of the PDP according to the present invention has been described with the phosphor of a multi-layer structure mainly on the green phosphor, but not only the green phosphor, but also the red phosphor and blue phosphor as a multi-layer structure and anti-sputtering on the layer facing the discharge space in the multilayer structure It is also possible to mix materials having excellent properties.

상술한 바와 같이, 본 발명에 따른 PDP의 형광체는 기판과 격벽 상에 면하는 제1 층의 녹색 형광물질 상에 안티-스퍼터링 특성이 우수한 물질이 혼합된 층을 적층함으로써 녹색 형광체를 스퍼터링으로부터 보호하여 PDP의 수명을 연장시키게 된다.As described above, the phosphor of the PDP according to the present invention protects the green phosphor from sputtering by laminating a layer of a material having excellent anti-sputtering property on the green phosphor of the first layer facing the substrate and the partition wall. It will extend the life of PDP.

이상 설명한 내용을 통해 당업자라면 본 발명의 기술사상을 일탈하지 아니하는 범위에서 다양한 변경 및 수정이 가능함을 알 수 있을 것이다. 따라서, 본 발명의 기술적 범위는 명세서의 상세한 설명에 기재된 내용으로 한정되는 것이 아니라 특허 청구의 범위에 의해 정하여 져야만 할 것이다.Those skilled in the art will appreciate that various changes and modifications can be made without departing from the technical spirit of the present invention. Therefore, the technical scope of the present invention should not be limited to the contents described in the detailed description of the specification but should be defined by the claims.

Claims (9)

발광물질로 이루어진 형광층과,A fluorescent layer made of a light emitting material, 상기 형광층보다 안티-스퍼터링 특성이 큰 물질을 함유하여 상기 형광층 상에 형성되는 보호층을 구비하는 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체.And a protective layer formed on the fluorescent layer by containing a material having a greater anti-sputtering property than the fluorescent layer. 제 1 항에 있어서,The method of claim 1, 상기 형광층의 물질은 Zn2SiO4: Mn2+인 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체.Material of the fluorescent layer is Zn 2 SiO 4: phosphor for a plasma display panel characterized in that the Mn 2+. 제 1 항에 있어서,The method of claim 1, 상기 보호층의 물질은 Zn2SiO4: Mn2+에 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중의 어느 하나가 혼합된 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체.The material of the protective layer is Zn 2 SiO 4 : Mn 2 + YBO 3 : Tb 3 + , YBO: ZSO 3: 1, YBO: ZSO 1: 1, YBO: ZSO 1: 3 characterized in that any one is mixed Phosphor of a plasma display panel. 제 1 항에 있어서,The method of claim 1, 상기 보호층은 방전공간과 면하는 것을 특징으로 하는 플라즈마 디스플레이패널의 형광체.The protective layer is a phosphor of the plasma display panel, characterized in that facing the discharge space. 제 1 항에 있어서,The method of claim 1, 상기 보호층에는 Zn2SiO4: Mn2+대비 10∼90%의 혼합비로 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중 적어도 어느 하나가 Zn2SiO4: Mn2+과 혼합되는 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체.At least any one of YBO 3 : Tb 3+ , YBO: ZSO 3: 1, YBO: ZSO 1: 1, and YBO: ZSO 1: 3 may be included in the protective layer in a mixing ratio of 10 to 90% of Zn 2 SiO 4 : Mn 2+ . One phosphor is mixed with Zn 2 SiO 4 : Mn 2+ . 기판 상에 발광물질로 이루어진 형광층을 형성하는 단계와,Forming a fluorescent layer made of a light emitting material on the substrate; 상기 형광층보다 안티-스퍼터링 특성이 큰 물질이 함유된 보호층을 상기 형광층 상에 형성하는 단계를 포함하는 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체의 제조방법.And forming a protective layer on the fluorescent layer, the protective layer containing a material having a greater anti-sputtering property than the fluorescent layer. 제 6 항에 있어서,The method of claim 6, 상기 형광층의 물질은 Zn2SiO4: Mn2+인 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체의 제조방법.The material of the phosphor layer is Zn 2 SiO 4 : Mn 2 + The method of manufacturing a phosphor of the plasma display panel, characterized in that. 제 6 항에 있어서,The method of claim 6, 상기 보호층의 물질은 Zn2SiO4: Mn2+에 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중의 어느 하나가 혼합된 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체.The material of the protective layer is Zn 2 SiO 4 : Mn 2 + YBO 3 : Tb 3 + , YBO: ZSO 3: 1, YBO: ZSO 1: 1, YBO: ZSO 1: 3 characterized in that any one is mixed Phosphor of a plasma display panel. 제 6 항에 있어서,The method of claim 6, 상기 보호층에는 Zn2SiO4: Mn2+대비 10∼90%의 혼합비로 YBO3: Tb3+, YBO : ZSO 3:1, YBO : ZSO 1:1, YBO : ZSO 1:3 중 적어도 어느 하나가 Zn2SiO4: Mn2+과 혼합되는 것을 특징으로 하는 플라즈마 디스플레이 패널의 형광체의 제조방법.At least any one of YBO 3 : Tb 3+ , YBO: ZSO 3: 1, YBO: ZSO 1: 1, and YBO: ZSO 1: 3 may be included in the protective layer in a mixing ratio of 10 to 90% of Zn 2 SiO 4 : Mn 2+ . A process for producing a phosphor of a plasma display panel, wherein one is mixed with Zn 2 SiO 4 : Mn 2+ .
KR10-2001-0085390A 2001-12-26 2001-12-26 Fluorescent material of plasma display panel and method of fabricating the same KR100433223B1 (en)