KR20020041855A - PVC Carpet Tile Using Carbon Black and the Method of Manufacturing thereof - Google Patents

PVC Carpet Tile Using Carbon Black and the Method of Manufacturing thereof Download PDF

Info

Publication number
KR20020041855A
KR20020041855A KR1020000071469A KR20000071469A KR20020041855A KR 20020041855 A KR20020041855 A KR 20020041855A KR 1020000071469 A KR1020000071469 A KR 1020000071469A KR 20000071469 A KR20000071469 A KR 20000071469A KR 20020041855 A KR20020041855 A KR 20020041855A
Authority
KR
South Korea
Prior art keywords
layer
chloride resin
vinyl chloride
carbon black
containing carbon
Prior art date
Application number
KR1020000071469A
Other languages
Korean (ko)
Other versions
KR100427554B1 (en
Inventor
박호전
장하수
김규열
Original Assignee
성재갑
주식회사 엘지씨아이
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 성재갑, 주식회사 엘지씨아이 filed Critical 성재갑
Priority to KR10-2000-0071469A priority Critical patent/KR100427554B1/en
Publication of KR20020041855A publication Critical patent/KR20020041855A/en
Application granted granted Critical
Publication of KR100427554B1 publication Critical patent/KR100427554B1/en

Abstract

PURPOSE: A polyvinyl chloride carpet tile using carbon black and a manufacturing method thereof are provided to improve the feeling of walking and an acoustic adsorption function by endowing a product with conductivity, and to prevent the operation failure of electronic equipment in the scene of labor. CONSTITUTION: The polyvinyl chloride carpet tile, that conductivity is applied to the whole portion of a product, is comprised of a polyvinyl chloride resin sol layer(1) containing carbon black, a glass fiber layer(3), the polyvinyl chloride resin sol layer containing carbon black, a non-woven fabric layer(4), and a fiber layer(5) formed by weaving raw thread containing carbon fiber, which are laminated successively from the bottom.

Description

카본 블랙을 사용한 염화비닐수지 카펫타일 및 그 제조방법{PVC Carpet Tile Using Carbon Black and the Method of Manufacturing thereof}PVC Carpet Tile Using Carbon Black and the Method of Manufacturing

본 발명은 전도성 물질인 카본 블랙을 함유하는 염화비닐수지층과 카본 섬유가 함유된 원사를 제직한 섬유층을 부착함으로써 제품 전체에 전도성 기능을 부여한 염화비닐수지 카펫 타일 및 그 제조방법에 관한 것이다.The present invention relates to a vinyl chloride resin carpet tile having a conductive function applied to an entire product by attaching a vinyl chloride resin layer containing a carbon black, which is a conductive material, and a fiber layer woven from a yarn containing carbon fibers, and a method of manufacturing the same.

일반적으로 전도성을 가지는 제품의 기능은 전기저항치로 표현될 수 있는데, 미국화재방지협회 99 규정에 의해 표면, 체적 저항이 100,000-10,000,000옴(Ohm)일때에 전도성을 가지는 것으로 규정되고 있으며, 또한 반도체 조립공장등 정전기 장애에 의해서 문제가 발생될 수 있는 장소에서는 상기의 요구품질이 만족되어야만 사용할 수 있는 것으로 규정화되어 있다.In general, the function of a product having conductivity can be expressed as an electrical resistance value. According to the American Fire Protection Association 99, it is defined as having conductivity when the surface and volume resistance is 100,000-10,000,000 Ohm. In a place where a problem may occur due to an electrostatic disturbance such as a factory, it is prescribed that it can be used only when the above required quality is satisfied.

상기의 요구 품질을 만족시키는 종래의 전도성 기능을 가지는 제품을 살펴보면, 각 층에 전도성 물질인 카본 블랙을 일정량 첨가하여 라미네이팅(Laminating)한 제품이 있고, 일정한 형태의 칩에 전도성 물질인 카본 블랙을 코팅하여 압착 후 표면을 갈아낸 제품이 있는데, 이들 제품은 모두 전층이 염화비닐수지로만 이루어진 염화비닐수지 바닥재였다.Looking at a product having a conventional conductive function that satisfies the above required quality, there is a product laminated by adding a certain amount of conductive material carbon black to each layer, coating a carbon black of a conductive material on a certain type of chip After pressing, there was a product whose surface was ground, and all of these products were vinyl chloride resin flooring materials whose entire layer consisted only of vinyl chloride resin.

또한 본 발명과 유사하게 염화비닐수지층과 섬유층으로 이루어진 염화비닐수지 카펫 타일의 경우 전도성 기능을 가지는 제품은 제품 전체에 전도성 기능이 부여된 형태가 아니었고, 제품의 일부분에만 전도성 기능이 부여된 것이었다.In addition, similar to the present invention, in the case of the vinyl chloride resin carpet tile made of a vinyl chloride resin layer and a fibrous layer, the product having a conductive function was not provided with a conductive function to the whole product, and only a part of the product had a conductive function. .

이에 본 발명에서는 전도성 물질인 카본 블랙을 함유하는 염화비닐수지층과 카본 섬유가 함유된 원사를 제직한 섬유층을 부착함으로써 제품 전체에 전도성 기능을 부여한 염화비닐수지 카펫 타일 및 그 제조방법을 제공하고자 한다.Accordingly, the present invention is to provide a vinyl chloride resin carpet tile and a method of manufacturing the same by attaching a vinyl chloride resin layer containing a carbon black as a conductive material and a fiber layer woven from a yarn containing carbon fibers. .

도 1은 본 발명에 따른 염화비닐수지 카펫 타일의 단면도.1 is a cross-sectional view of a vinyl chloride resin carpet tile according to the present invention.

도 2는 본 발명에 따른 다른 염화비닐수지 카펫 타일의 단면도.2 is a cross-sectional view of another vinyl chloride resin carpet tile according to the present invention.

(도면의 주요부분에 대한 부호의 설명)(Explanation of symbols for the main parts of the drawing)

1 : 카본 블랙이 함유된 염화비닐수지 졸층1: vinyl chloride resin sol layer containing carbon black

2 : 카본 블랙이 함유된 염화비닐수지 시트층2: vinyl chloride resin sheet layer containing carbon black

3 : 유리섬유층3: glass fiber layer

4 : 부직포층4: nonwoven fabric layer

5 : 카본 섬유가 함유된 원사를 제직한 섬유층5: fiber layer woven from yarn containing carbon fiber

이하 첨부도면에 의거하며 본 발명을 설명하면 다음과 같다.Hereinafter, the present invention will be described with reference to the accompanying drawings.

도 1은 본 발명에 따른 염화비닐수지 카펫 타일의 단면도로서, 아래로부터 차례대로 카본 블랙이 함유된 염화비닐수지 졸층(1), 유리섬유층(3), 카본 블랙이 함유된 염화비닐수지 졸층(1), 부직포층(4) 및 카본 섬유가 함유된 원사를 제직한 섬유층(5)이 적층된 구조의 염화비닐수지 카펫 타일을 보여준다.1 is a cross-sectional view of a vinyl chloride resin carpet tile according to the present invention, a vinyl chloride resin sol layer 1 containing carbon black, a glass fiber layer 3, and a carbon chloride resin layer containing carbon black 1 ), A vinyl chloride resin carpet tile having a structure in which a nonwoven fabric layer 4 and a fiber layer 5 woven from a yarn containing carbon fibers are laminated.

이러한 도 1의 염화비닐수지 카펫 타일의 제조방법은 다음과 같다.The manufacturing method of the vinyl chloride resin carpet tile of Figure 1 is as follows.

먼저, 이형 캐리어 상부에 전도성 물질인 카본 블랙이 함유된 액상의 염화비닐수지졸을 일정 두께로 코팅하여 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시킨다.First, the vinyl chloride resin sol layer 1 containing carbon black is formed by coating a liquid vinyl chloride sol containing a conductive material carbon black on a release carrier to a predetermined thickness.

이때 카본 블랙이 함유된 염화비닐수지 졸층(1)의 염화비닐수지 졸의 조성은 중합도가 1300 또는 1700인 염화비닐수지 100중량부에 가소제인 디옥틸프탈레이트 90중량부, 부틸벤질프탈레이트 10중량부, TXIB 10중량부 및 DDB 20중량부, 안정제인 바륨-아연계 화합물 7중량부, 충전제인 중탄산칼슘 100중량부 및 전도성 물질인 카본 블랙 33중량부가 배합된 것이다.At this time, the composition of the vinyl chloride resin sol of the vinyl chloride resin sol layer 1 containing carbon black is 100 parts by weight of vinyl chloride resin having a polymerization degree of 1300 or 1700, 90 parts by weight of dioctylphthalate, 10 parts by weight of butylbenzylphthalate, 10 parts by weight of TXIB and 20 parts by weight of DDB, 7 parts by weight of a barium-zinc compound as a stabilizer, 100 parts by weight of calcium bicarbonate as a filler, and 33 parts by weight of carbon black as a conductive material.

다음, 염화비닐수지 졸층(1)의 상부에 치수안정성이 있는 유리섬유층(3)을 적층한 후, 유리섬유층(3)의 상부에 상기의 염화비닐수지 졸의 조성과 같은 염화비닐수지 졸을 코팅하여 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시킨 다음, 다시 치수안정성이 있는 부직포층(4)을 적층한다.Next, after laminating the dimensional stability glass fiber layer (3) on top of the vinyl chloride resin sol layer (1), and coated with a vinyl chloride resin sol such as the composition of the above-mentioned vinyl chloride resin sol on the glass fiber layer (3) Then, the vinyl chloride resin sol layer 1 containing carbon black was formed, and then the nonwoven fabric layer 4 having dimensional stability was laminated.

마지막으로, 부직포층(4) 상부에 전도성 카본 섬유가 함유된 원사를 제직한섬유층(5)을 적층한 후, 130 - 150℃의 열풍에 3 - 5분간 건조하여 염화비닐수지 카펫 타일을 완성한다.Finally, after laminating the fibrous layer 5 woven from the yarn containing conductive carbon fibers on the nonwoven fabric layer 4, it is dried for 3 to 5 minutes in hot air at 130 to 150 ° C. to complete the vinyl chloride resin carpet tile. .

이때 카본 섬유가 함유된 원사를 제직한 섬유층(5)은 일반섬유 100중량부에 카본섬유 20중량부가 배합된 것이다.At this time, the fiber layer 5 woven from the yarn containing the carbon fiber is a blend of 20 parts by weight of carbon fiber to 100 parts by weight of normal fiber.

즉, 상기의 염화비닐수지 카펫 타일은 카본 블랙이 함유된 액상의 염화비닐수지 졸이 다공질 물질인 유리섬유층(3)과 부직포층(4)에 스며들게 되어 제품 전체에 전도성을 부여할 수 있는 것이다.That is, in the vinyl chloride resin carpet tile, the liquid vinyl chloride sol containing carbon black is impregnated into the glass fiber layer 3 and the nonwoven fabric layer 4, which are porous materials, to impart conductivity to the entire product.

도 2는 본 발명에 따른 다른 염화비닐수지 카펫 타일의 단면도로서, 아래로부터 차례대로 카본 블랙이 함유된 염화비닐수지 시트층(2), 카본 블랙이 함유된 염화비닐수지 졸층(1), 유리섬유층(3), 카본 블랙이 함유된 염화비닐수지 졸층(1), 부직포층(4) 및 카본 섬유가 함유된 원사를 제직한 섬유층(5)이 적층된 구조의 염화비닐수지 카펫 타일을 보여준다.Figure 2 is a cross-sectional view of another vinyl chloride resin carpet tile according to the present invention, the vinyl chloride resin sheet layer (2) containing carbon black in order from the bottom, the vinyl chloride resin sol layer (1), glass fiber layer containing carbon black (3) A vinyl chloride resin carpet tile in which a vinyl chloride resin sol layer 1 containing carbon black, a nonwoven fabric layer 4, and a fiber layer 5 woven from a yarn containing carbon fibers are laminated.

이러한 도 2의 염화비닐수지 카펫 타일의 제조방법은 다음과 같다.The method for producing the vinyl chloride resin carpet tile of Figure 2 is as follows.

먼저, 칼렌더링 공법으로 전도성 물질인 카본 블랙이 함유된 염화비닐수지 시트층(2)을 제조한다.First, a vinyl chloride resin sheet layer 2 containing carbon black, which is a conductive material, is manufactured by a calendering method.

이때 카본 블랙이 함유된 염화비닐수지 시트층(2)의 염화비닐수지의 조성은 중합도가 100 또는 800인 염화비닐수지 100중량부에 가소제인 디옥틸프탈레이트 40중량부, 안정제인 바륨-아연계 화합물 4중량부, 충전제인 중탄산칼슘 100중량부 및 전도성 물질인 카본 블랙 25.5중량부를 배합한 것이다.At this time, the composition of the vinyl chloride resin of the vinyl chloride resin sheet layer 2 containing carbon black is 40 parts by weight of dioctylphthalate as a plasticizer and a barium-zinc compound as a stabilizer in 100 parts by weight of a vinyl chloride resin having a polymerization degree of 100 or 800. 4 parts by weight, 100 parts by weight of calcium bicarbonate as a filler and 25.5 parts by weight of carbon black as a conductive material are blended.

다음, 염화비닐수지 시트층(2)의 상부에 전도성 물질인 카본 블랙이 함유된액상의 염화비닐수지 졸을 코팅하여 염화비닐수지 졸층(1)을 형성시킨 다음, 치수안정성이 있는 유리섬유층(3)을 적층한다.Next, a vinyl chloride resin sol layer 1 is formed by coating a liquid vinyl chloride sol containing carbon black, which is a conductive material, on the upper part of the vinyl chloride resin sheet layer 2, and then the dimensional stability glass fiber layer 3 )).

이때 카본 블랙이 함유된 염화비닐수지 졸층(1)의 염화비닐수지 졸의 조성은 중합도가 1300 또는 1700인 염화비닐수지 100중량부에 가소제인 디옥틸프탈레이트 90중량부, 부틸벤질프탈레이트 10중량부, TXIB 10중량부 및 DDB 20중량부, 안정제인 바륨-아연계 화합물 7중량부, 충전제인 중탄산칼슘 100중량부 및 전도성 물질인 카본 블랙 33중량부가 배합된 것이다.At this time, the composition of the vinyl chloride resin sol of the vinyl chloride resin sol layer 1 containing carbon black is 100 parts by weight of vinyl chloride resin having a polymerization degree of 1300 or 1700, 90 parts by weight of dioctylphthalate, 10 parts by weight of butylbenzylphthalate, 10 parts by weight of TXIB and 20 parts by weight of DDB, 7 parts by weight of a barium-zinc compound as a stabilizer, 100 parts by weight of calcium bicarbonate as a filler, and 33 parts by weight of carbon black as a conductive material.

다음, 유리섬유층(3)의 상부에 상기의 염화비닐수지 졸의 조성과 같은 염화비닐수지 졸을 코팅하여 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시킨 다음, 다시 치수안정성이 있는 부직포층(4)을 적층한다.Next, a vinyl chloride resin sol such as the composition of the vinyl chloride resin sol is coated on the glass fiber layer 3 to form a vinyl chloride resin sol layer 1 containing carbon black, and then the nonwoven fabric having dimensional stability again. Layer 4 is laminated.

마지막으로, 부직포층(4) 상부에 전도성 카본 섬유가 함유된 원사를 제직한 섬유층(5)을 적층한 후, 130 - 150℃의 열풍에 3 - 5분간 건조하여 염화비닐수지 카펫 타일을 완성한다.Finally, after laminating the fibrous layer 5 woven from the yarn containing the conductive carbon fibers on the nonwoven fabric layer 4, it is dried for 3 to 5 minutes in a hot air of 130-150 ℃ to complete the vinyl chloride resin carpet tile. .

이때 카본 섬유가 함유된 원사를 제직한 섬유층(5)은 일반섬유 100중량부에 카본섬유 20중량부가 배합된 것이다.At this time, the fiber layer 5 woven from the yarn containing the carbon fiber is a blend of 20 parts by weight of carbon fiber to 100 parts by weight of normal fiber.

즉, 상기의 염화비닐수지 카펫 타일은 카본 블랙이 함유된 액상의 염화비닐수지 졸이 다공질 물질인 유리섬유층(3)과 부직포층(4)에 스며들게 되어 제품 전체에 전도성을 부여할 수 있는 것이다.That is, in the vinyl chloride resin carpet tile, the liquid vinyl chloride sol containing carbon black is impregnated into the glass fiber layer 3 and the nonwoven fabric layer 4, which are porous materials, to impart conductivity to the entire product.

이러한 본 발명의 염화비닐수지 카펫 타일은 전도성 물질인 카본 블랙을 함유한 염화비닐수지층에 전도성 카본 섬유를 부착하여 제품 전체에 전도성 기능을 부여함으로써 보행감이 좋고 흡음성이 있으며 산업현장, 사무공간등에서 정전기 장애에 의해 발생될 수 있는 고가의 전자장비의 오작동, 화재, 인체의 불쾌감등을 해소할 수 있게 되었다.The vinyl chloride resin carpet tile according to the present invention attaches the conductive carbon fiber to the vinyl chloride resin layer containing the carbon black, which is a conductive material, and gives a conductive function to the entire product. It is possible to solve the malfunction of expensive electronic equipment, fire, and the discomfort of human body, which can be caused by static electricity disturbance.

Claims (4)

아래로부터 차례대로 카본 블랙이 함유된 염화비닐수지 졸층(1), 유리섬유층 (3), 카본 블랙이 함유된 염화비닐수지 졸층(1), 부직포층(4) 및 카본 섬유가 함유된 원사를 제직한 섬유층(5)이 적층된 구조의, 제품 전체에 전도성이 부여된 염화비닐수지 카펫 타일.From below, weaving the vinyl chloride resin sol layer 1 containing carbon black, the glass fiber layer 3, the vinyl chloride resin sol layer 1 containing the carbon black, the nonwoven fabric layer 4 and the yarn containing the carbon fiber A vinyl chloride resin carpet tile in which conductivity is imparted to the entire product, in which one fiber layer 5 is laminated. 아래로부터 차례대로 카본 블랙이 함유된 염화비닐수지 시트층(2), 카본 블랙이 함유된 염화비닐수지 졸층(1), 유리섬유층(3), 카본 블랙이 함유된 염화비닐수지 졸층(1), 부직포층(4) 및 카본 섬유가 함유된 원사를 제직한 섬유층(5)이 적층된 구조의, 제품 전체에 전도성이 부여된 염화비닐수지 카펫 타일.Vinyl chloride resin sheet layer 2 containing carbon black from the bottom, vinyl chloride resin sol layer 1 containing carbon black, glass fiber layer 3, vinyl chloride resin sol layer 1 containing carbon black, A vinyl chloride resin carpet tile in which conductivity is imparted to an entire product of a structure in which a nonwoven fabric layer 4 and a fiber layer 5 woven from a yarn containing carbon fibers are laminated. 카본 블랙이 함유된 액상의 염화비닐수지 졸을 코팅하여 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시키고, 염화비닐수지 졸층(1)의 상부에 유리섬유층 (3)을 적층한 후, 유리섬유층(3)의 상부에 다시 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시킨 다음, 부직포층(4)을 적층하고, 부직포층(4) 상부에 카본 섬유가 함유된 원사를 제직한 섬유층(5)을 적층하여 130 - 150℃의 열풍에 3 - 5분간 건조시킴으로써, 제품 전체에 전도성이 부여된 염화비닐수지 카펫 타일을 제조하는 방법.After coating the liquid vinyl chloride sol containing carbon black to form a vinyl chloride resin sol layer 1 containing carbon black, and laminating the glass fiber layer 3 on top of the vinyl chloride resin sol layer 1, After forming a vinyl chloride resin sol layer 1 containing carbon black again on top of the glass fiber layer 3, the nonwoven fabric layer 4 is laminated, and weaving the yarn containing carbon fiber on the nonwoven fabric layer 4 upper portion. A method of producing a vinyl chloride resin carpet tile in which conductivity is imparted to an entire product by laminating one fibrous layer (5) and drying it for 3 to 5 minutes in a hot air of 130 to 150 ° C. 칼렌더링 공법으로 전도성 물질인 카본 블랙이 함유된 염화비닐수지 시트층 (2)을 제조하고, 염화비닐수지 시트층(2)의 상부에 카본 블랙이 함유된 액상의 염화비닐수지 졸을 코팅하여 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시키고, 염화비닐수지 졸층(1)의 상부에 유리섬유층(3)을 적층한 후, 유리섬유층(3)의 상부에 다시 카본 블랙이 함유된 염화비닐수지 졸층(1)을 형성시킨 다음, 부직포층 (4)을 적층하고, 부직포층(4) 상부에 카본 섬유가 함유된 원사를 제직한 섬유층(5)을 적층하여 130 - 150℃의 열풍에 3 - 5분간 건조시킴으로써, 제품 전체에 전도성이 부여된 염화비닐수지 카펫 타일을 제조하는 방법.A vinyl chloride resin sheet layer (2) containing carbon black as a conductive material was prepared by a calendering method, and a liquid carbon chloride resin sol containing carbon black was coated on top of the vinyl chloride resin sheet layer (2) to form carbon. The black chloride-containing vinyl chloride resin layer 1 is formed, and the glass fiber layer 3 is laminated on the vinyl chloride resin sol layer 1, and the carbon black-containing chloride is further formed on the glass fiber layer 3 again. After forming the vinyl resin sol layer (1), the nonwoven fabric layer (4) is laminated, and the fiber layer (5) woven from a yarn containing carbon fibers is laminated on the nonwoven fabric layer (4) to hot air at 130-150 ° C. A method of producing a vinyl chloride resin carpet tile imparting conductivity to an entire product by drying for 3-5 minutes.
KR10-2000-0071469A 2000-11-29 2000-11-29 PVC Carpet Tile Using Carbon Black and the Method of Manufacturing thereof KR100427554B1 (en)