KR200190750Y1 - A panel for the korean under-foor heating system using jade and charcoal - Google Patents
A panel for the korean under-foor heating system using jade and charcoal Download PDFInfo
- Publication number
- KR200190750Y1 KR200190750Y1 KR2020000005287U KR20000005287U KR200190750Y1 KR 200190750 Y1 KR200190750 Y1 KR 200190750Y1 KR 2020000005287 U KR2020000005287 U KR 2020000005287U KR 20000005287 U KR20000005287 U KR 20000005287U KR 200190750 Y1 KR200190750 Y1 KR 200190750Y1
- Authority
- KR
- South Korea
- Prior art keywords
- charcoal
- jade
- mesh
- wollastonite
- kaolin
- Prior art date
Abstract
본 고안은 철망의 메쉬 사이에 옥과 숯을 일정하게 배열하고, 이들 사이에 분말형태의 황토, 고령토, 규회석, 비석을 몰탈 상태에서 채운 후 소결 성형한 상판과, 이에 대응되도록 분말형태의 황토, 숯, 고령토, 규회석, 비석을 사용해 소결 성형한 하판을 이용하여 온돌용 패널을 제작 및 시공함으로서, 수맥파차단. 전자파판단, 습기차단, 벌레차단, 원적외선방출, 공기정화의 효과를 가질수 있게 함과 동시에 상판과 하판에 각각 온수관 및 전열관을 안착하는 홈을 일체로 성형하여 시공의 간편성과 시간단축을 할 수 있도록 이루어진 옥과 숯을 이용한 온돌용 패널 및 그 제조방법에 관한 것으로, 이는 온수관 안착홈과 전열관 안착홈이 상면에 형성되고, 결합돌기가 네모서리에 형성된 하판과, 온수관 안착홈과 전열관 안착홈이 하면에 형성되고, 상기 결합돌기에 대응하는 결합홈이 네모서리에 형성되며, 내부에 위치된 철망의 메쉬내에 옥 및 숯을 각각 배열하여 이루어진 상판과, 상기 결합홈과 결합돌기을 결합하여 형성된 상ㆍ하판의 공간에 분말상태의 황토, 고령토, 규회석 및 비석을 몰탈 상태에서 채워 건조시키는 것을 특징으로 하는 옥과 숯을 이용한 온돌용 패널 특징으로 하는 것이다. 또한, 하판은 100메쉬의 황토 25∼40%와 숯 25∼40%, 180∼200메쉬의 고령토 10∼20%, 규회석 10∼20%, 비석 10∼20% 비율로 혼합하고, 이를 700℃∼800℃로 소결 성형하여 이루어 지도록 하는 것을 특징으로 하는 것이다. 또한, 상기 상판은 내부에 위치하는 철망의 메쉬 사이에 옥 및 숯을 모자이크 형태로 배열하고, 상기 옥 및 숯사이에 200메쉬의 고령토, 규회석 및 비석을 혼합하며, 이를 700℃∼800℃로 소성하여 이루어 지도록 하는 것을 특징으로 하는 것이다. 또한, 상기 옥(15)과 숯(16)의 직경이 3 ∼ 5㎝, 길이 5㎝ 또는 한변이 3 ∼ 5㎝, 길이 5㎝이도록 하는 것을 특징으로 하는 것이다.The present invention arranges jade and charcoal uniformly between meshes of wire meshes, and fills powdered ocher, kaolin, wollastonite and zeolite in mortar state between them, and then sinters and forms the powdered ocher and charcoal accordingly. Water-blocking by manufacturing and constructing panels for ondol using lower plates sintered and molded using kaolin, wollastonite and zeolite. It has the effects of electromagnetic wave determination, moisture blocking, insect blocking, far infrared ray emission, and air purification, and at the same time, the grooves for seating hot water pipes and heat pipes on the upper and lower plates are integrally molded so that the convenience and time can be shortened. It relates to an ondol panel made of jade and charcoal, and a method of manufacturing the same, which includes a hot water pipe seating groove and a heat pipe seating groove formed on an upper surface thereof, and a lower plate having a coupling protrusion formed on a corner, and a hot water pipe seating groove and a heat pipe fitting groove. The upper surface is formed on the lower surface, the coupling groove corresponding to the coupling protrusion is formed in the four corners, the upper plate formed by arranging jade and char in the mesh of the wire mesh located therein, and the upper and the coupling groove and the coupling protrusion formed Powdered ocher, kaolin, wollastonite and zeolite in the space of the lower plate is filled with mortar to dry and ondol using jade and charcoal It is characterized by the panel. In addition, the lower plate is mixed in a ratio of 25 to 40% loess of 100 mesh and 25 to 40% of charcoal, 10 to 20% of kaolin 10 to 20%, wollastonite 10 to 20% and zeolite 10 to 20%. It is to be made by sintering molding at 800 ℃. In addition, the top plate is arranged in a mosaic of jade and charcoal between the mesh of the wire mesh located inside, and 200 mesh of kaolin, wollastonite and zeolite between the jade and charcoal, and calcined at 700 ℃ to 800 ℃ It is characterized by that to be done. In addition, the jade 15 and the charcoal 16 is characterized by having a diameter of 3 to 5 cm, a length of 5 cm or one side of 3 to 5 cm, a length of 5 cm.
Description
본 고안은 옥과 숯을 이용한 온돌용 패널에 관한 것으로, 더욱 상세하게는 철망의 메쉬 사이에 옥과 숯을 일정하게 배열하고, 이들 사이에 분말형태의 황토, 고령토, 규회석, 비석를 몰탈 상태에서 채운 후 소결 성형한 상판과, 이에 대응되도록 분말형태의 황토, 숯, 고령토, 규회석, 비석을 사용해 소결 성형한 하판을 이용하여 온돌용 패널을 제작 및 시공함으로서, 수맥파차단. 전자파판단, 습기차단, 벌레차단, 원적외선방출, 공기정화의 효과를 가질수 있게 함과 동시에 상판과 하판에 각각 온수관 및 전열관을 안착하는 홈을 일체로 성형하여 시공의 간편성과 시간단축을 할 수 있도록 이루어진 옥과 숯을 이용한 온돌용 패널에 관한 것이다.The present invention relates to an ondol panel using jade and charcoal, and more particularly, jade and charcoal are uniformly arranged between meshes of a wire mesh, and powdered ocher, kaolin, wollastonite, and zeolite are filled between them in a mortar state and sintered. By forming and constructing an ondol panel using a molded upper plate and a lower plate sintered using powdered ocher, charcoal, kaolin, wollastonite, and zeolite so as to correspond to it, blocking water veins. It has the effects of electromagnetic wave determination, moisture blocking, insect blocking, far infrared ray emission, and air purification, and at the same time, the grooves for seating hot water pipes and heat pipes on the upper and lower plates are integrally molded so that the convenience and time can be shortened. It relates to an ondol panel made of jade and char.
일반적으로 단독 주택이나 아파트의 침실, 거실, 주방 등의 바닥 시공시 콘크리트 바닥 또는 콘크리트 슬리브에 온돌 파이프를 배관한 후 그 상면에 시멘트와 모래를 혼합한 몰탈을 물로 반죽하여 바닥 미장 공사를 하고 있으며, 또한, 이를 단위패널로 제작하여 간편히 시공하는 온돌용 패널이 널리 사용되고 있다.In general, when laying the floor of a bedroom, living room, kitchen, etc. in a single house or apartment, the underfloor pipe is piped to the concrete floor or concrete sleeve, and then mortar mixed with cement and sand is kneaded with water on the top surface, In addition, the panel for the ondol which is easily constructed by manufacturing it as a unit panel is widely used.
상기와 같은 온돌용 패널의 일례에 대한 종래의 예로서는, 특허 공개번호 1999-0064713의 숯을 이용한 패널 제조방법 및 그 패널에서 찾아 볼 수 있다.As a conventional example of an example of the ondol panel as described above, it can be found in the panel production method using the charcoal of Patent Publication No. 1999-0064713 and the panel.
이건 고안에서는 콘크리트(1) 위에 단열층(2), 보온층(3), 온돌판(4)을 차례로 적층시켜 패널을 구성하는 것에 있어서, 단열층(2)은 황토와 접착용제를, 보온층(3)은 숯(백탄)과 코르크 및 접착용제를, 온돌판(4)은 숯(백탄)과 금강약돌 및 접착용제를 적절한 비율로 혼합한 후 성형하여서 이들을 서로 결합하여 패널을 구성하고 있다.In this invention, in order to form a panel by laminating the heat insulating layer 2, the heat insulating layer 3, and the warm plate 4 on the concrete 1 in order, the heat insulating layer 2 is made of the ocher and the adhesive solvent, and the heat insulating layer 3 ) Is charcoal (coal charcoal) and cork and adhesive solvent, and the ondol plate (4) is charcoal (coal charcoal), diamond powder and adhesive solvent in a suitable ratio and then molded together to form a panel by combining them.
그러나, 상기 고안에서는 온수관(5)을 설치하고 보온층(3)을 시공함으로서, 시공시간이 많이 소요되는 문제점이 있었다.However, in the above design, by installing the hot water pipe 5 and constructing the thermal insulation layer 3, there was a problem in that the construction time is long.
또한, 종래의 온돌용 패널의 또 다른 실시예를 보면, 특허 공개번호 1998-020912의 온돌바닥면 시공방법에서 찾아 볼 수 있다.In addition, when looking at another embodiment of the conventional ondol panel, it can be found in the method for constructing the ondol floor of Patent Publication No. 1998-020912.
이건 고안에서는 단열부재(6)와 난방파이프 안착홈(9)이 구비된 몰탈제품의 지지판재(7)가 일체적으로 적층결합된 단위패널(8)을 준비하고, 상기 준비된 단위패널(8)을 기초층 상면에 배열고정한 다음 지지판(7)의 안착홈(9)내로 난방파이프 (5)를 삽입하면서 몰탈로써 마감하여 시공하는 것을 특징으로 하는 온돌바닥면 시공방법에 관한 고안인것이다.In this invention, the unit panel 8 in which the support plate member 7 of the mortar product having the heat insulating member 6 and the heating pipe seating groove 9 is integrally laminated and prepared is prepared, and the prepared unit panel 8 is prepared. After the arrangement is fixed to the upper surface of the base layer and the heating pipe (5) into the seating groove (9) of the heating floor (5) is to devise a construction method for the underfloor surface, characterized in that the finishing by mortar construction.
그러나, 상기 고안에서는 시공의 간편함과 시간을 단축할 수 는 있을지라도 단위패널의 제조되는 원료가 자연친화적이지 않고 인체에 유익하지 않은 문제점이 있었다.However, in the above design, although the simplicity and time of construction can be shortened, there is a problem in that the raw material manufactured in the unit panel is not natural friendly and is not beneficial to the human body.
즉, 옥이나 숯과 같은 인체에 유익한 효과를 발생시키는 재료를 사용하지 않아 수맥파차단, 전자파판단, 습기차단, 벌레차단, 원적외선방출, 공기정화의 효과를 가질 수 없는 문제점이 있었다.That is, there is a problem that can not have the effect of water wave blocking, electromagnetic wave blocking, moisture blocking, insect blocking, far-infrared emission, air purification because it does not use materials that produce a beneficial effect on the human body, such as jade or charcoal.
본 고안은 이러한 종래의 문제점을 해결하기 위하여 이루어진 것으로, 그목적은 온돌용 패널을 시공함에 있어 시간을 단축할 수 있도록 상ㆍ하판에 온수관 및 전열관을 안착하는 안착홈을 형성한 온돌용 패널을 제공함에 있다.The present invention has been made to solve such a conventional problem, the purpose of the ondol panel formed a seating groove for seating the hot water pipes and heat transfer pipes on the upper and lower panels to reduce the time in the construction of the ondol panel In providing.
또한 상.하판을 인체에 유익한 옥, 숯을 주재료로 하고 고령토, 황토, 규회석, 비석, 흑운모 등의 부원료로 제조함으로서, 인체에 유익한 온돌용 패널을 제공함에 있다.In addition, the upper and lower panels are made of jade and charcoal, which are beneficial to the human body, and are made of subsidiary materials such as kaolin, loess, wollastonite, tombstone, biotite, and the like to provide a panel for ondol beneficial to the human body.
도 1은 종래의 온돌용 패널의 일실시예를 나타낸 단면도.1 is a cross-sectional view showing an embodiment of a conventional ondol panel.
도 2는 종래의 온돌용 패널의 또 다른 실시예를 나타낸 단면도.Figure 2 is a cross-sectional view showing another embodiment of a conventional ondol panel.
도 3은 본 고안의 온돌용 패널이 설치된 상태를 나타낸 도면.Figure 3 is a view showing a state in which the ondol panel is installed of the present invention.
도 4는 본 고안에 따른 온돌용 패널을 상ㆍ하판으로 분리한 분리사시도.Figure 4 is an exploded perspective view of separating the ondol panel according to the present invention into the upper and lower plates.
도 5는 본 고안 도 4의 단면도.5 is a cross-sectional view of the present invention Figure 4;
도 6은 본 고안의 온돌용 패널이 적용된 상태의 단면도.Figure 6 is a cross-sectional view of the state applied to the panel for ondol of the present invention.
(도면중 주요 부분에 대한 부호의 설명)(Explanation of symbols for the main parts of the drawing)
100: 바닥면 10: 상판100: bottom 10: top plate
11: 온수관 안착홈 12: 전열관 안착홈11: hot water pipe seat groove 12: heat pipe seat groove
13: 결합홈 14: 철망13: coupling groove 14: wire mesh
15: 옥 16: 숯15: Jade 16: Charcoal
20; 하판 21: 온수관 안착홈20; Bottom 21: Hot water pipe seat home
22: 전열관 안착홈 23: 결합돌기22: heating tube seating groove 23: coupling projection
P: 패널P: panel
이러한 목적을 해결하기 위한 본 고안은 온수관 안착홈과 전열관 안착홈이 상면에 형성되고, 결합돌기가 네모서리에 형성된 하판과, 온수관 안착홈과 전열관 안착홈이 하면에 형성되고, 상기 결합돌기에 대응하는 결합홈이 네모서리에 형성되며, 내부에 위치된 철망의 메쉬내에 옥 및 숯을 각각 배열하여 이루어진 상판과, 상기 결합홈과 결합돌기을 결합하여 형성된 상ㆍ하판의 공간에 분말상태의 황토, 고령토, 규회석 및 비석을 몰탈 상태에서 채워 건조시키는 것을 특징으로 하는 옥과 숯을 이용한 온돌용 패널 특징으로 하는 것이다.The present invention for solving the above object is a hot water pipe seating groove and the heat transfer pipe seating groove is formed on the upper surface, the bottom plate formed in the four corners, the hot water pipe seating groove and the heat pipe mounting groove is formed on the lower surface, the coupling protrusion Coupling grooves corresponding to each other are formed at the corners, and powder loess is formed in the space of the upper and lower plates formed by arranging jade and char in the mesh of the wire mesh located therein, and the coupling groove and the coupling protrusion. It is characterized by the ondol panel using jade and charcoal, characterized in that kaolin, wollastonite and zeolite are filled and dried in a mortar state.
또한, 하판은 100메쉬의 황토 25∼40%와 숯 25∼40%, 180∼200메쉬의 고령토 10∼20%, 규회석 10∼20%, 비석 10∼20% 비율로 혼합하고, 이를 700℃∼800℃로 소결 성형하여 이루어 지도록 하는 것을 특징으로 하는 것이다.In addition, the lower plate is mixed in a ratio of 25 to 40% loess of 100 mesh and 25 to 40% of charcoal, 10 to 20% of kaolin 10 to 20%, wollastonite 10 to 20% and zeolite 10 to 20%. It is to be made by sintering molding at 800 ℃.
또한, 상기 상판은 내부에 위치하는 철망의 메쉬 사이에 옥 및 숯을 모자이크 형태로 배열하고, 상기 옥 및 숯사이에 200메쉬의 고령토, 규회석 및 비석을 혼합하며, 이를 700℃∼800℃로 소성하여 이루어 지도록 하는 것을 특징으로 하는 것이다.In addition, the top plate is arranged in a mosaic of jade and charcoal between the mesh of the wire mesh located inside, and 200 mesh of kaolin, wollastonite and zeolite between the jade and charcoal, and calcined at 700 ℃ to 800 ℃ It is characterized by that to be done.
또한, 상기 옥(15)과 숯(16)의 직경이 3 ∼ 5㎝, 길이 5㎝ 또는 한변이 3 ∼ 5㎝, 길이 5㎝이도록 하는 것을 특징으로 하는 것이다.In addition, the jade 15 and the charcoal 16 is characterized by having a diameter of 3 to 5 cm, a length of 5 cm or one side of 3 to 5 cm, a length of 5 cm.
이하 첨부된 도면의 도 3에서는 본 고안의 온돌용 패널이 적용된 바닥면의 전체적인 구성을 상세히 나타내고 있으며, 이의 도면에서 부호 100은 본 고안에 따른 온돌용 패널이 적용된 바닥면을 나타내고 있다.3 of the accompanying drawings shows the overall configuration of the floor surface is applied to the ondol panel of the present invention in detail, the reference numeral 100 in the drawing shows a floor surface to which the panel for ondol according to the present invention is applied.
바닥면(100)은 다수개의 온돌용 패널(P)이 일정하게 배열되어 있고, 이의 내측에는 온수관(30) 및 전열관(40)이 설치되어 있다.In the bottom surface 100, a plurality of ondol panels P are constantly arranged, and inside the hot water pipe 30 and the heat transfer pipe 40 are installed.
온돌용 패널(P)은 상판(10)과 하판(20)으로 크게 구성되어 있다.The ondol panel P is largely comprised of the upper board 10 and the lower board 20.
상판(10)은 온수관 안착홈(11)과 전열관 안착홈(12)이 하면에 형성되고, 결합홈(13)이 네모서리에 형성되며, 내부에는 철망(14)이 위치하여, 상기 철망(14)의 메쉬내에 옥(15) 및 숯(16)을 각각 배열하여 이루어져 있다.The upper plate 10 has a hot water pipe seating groove 11 and the heat pipe seating groove 12 is formed on the lower surface, the coupling groove 13 is formed in four corners, the wire mesh 14 is located inside, the wire mesh ( The jade 15 and the charcoal 16 are arranged in the mesh of 14, respectively.
이때 옥과 숯을 직경이 3 ∼ 5㎝, 길이 5㎝의 원형 또는 한변이 3 ∼ 5㎝, 길이 5㎝이도록 하는 것이 바람직하다.At this time, it is preferable that jade and charcoal have a diameter of 3 to 5 cm, a circle of 5 cm in length or one side of 3 to 5 cm and a length of 5 cm.
또한, 철망(14)은 지름이 3.2㎜이도록 하는 것이 바람직하다.In addition, the wire mesh 14 is preferably such that the diameter is 3.2mm.
또한, 옥(15)과 숯(16)사이에 200메쉬의 황토, 고령토, 규회석 및 비석을 혼합하고, 이를 700℃∼800℃로 소성하여 이루어 지도록 하는 것이다.In addition, 200 mesh loess, kaolin, wollastonite and zeolite are mixed between the jade 15 and the charcoal 16 and calcined to 700 to 800 ° C.
즉, 인체에 유해한 시멘트를 사용하지 않고 접착성이 좋은 분말형태의 황토, 고령토, 규회석 및 비석을 물과 혼합하여 몰탈상태에서 옥(15)과 숯(16)사이에 채운 후 700℃∼800℃로 소성하여 사각형태의 패널(P)을 만듬으로서, 옥(15)과 숯(16)을 고정시키고, 패널(P)의 균열을 방지하는 것이다.That is, without using cement that is harmful to human body, it is filled with jade, kaolin, wollastonite and zeolite in powder form with good adhesion and filled with water between jade (15) and charcoal (16) in mortar state. By firing in a rectangular panel P, the jade 15 and the charcoal 16 are fixed to prevent the panel P from being cracked.
하판(20)은 상판(10)과 대응되도록 온수관 안착홈(21)과 전열관 안착홈(22)이 상면에 형성되고, 상판에 형성된 결합홈(13)에 삽입되는 결합돌기(23)가 네모서리에 형성되어져 있다.The lower plate 20 has a hot water pipe seating groove 21 and a heat pipe seating groove 22 formed on an upper surface thereof so as to correspond to the top plate 10, and a coupling protrusion 23 inserted into the coupling groove 13 formed on the top plate is four. It is formed at the corner.
또한, 하판(20)은 100메쉬의 황토 25∼40%와 숯 25∼40%, 180∼200메쉬의 고령토 10∼20%, 규회석 10∼20%, 비석 10∼20% 비율로 혼합하고, 이를 700℃∼800℃로 소성하여 사각형태의 패널(P)을 만드는 것이다.In addition, the lower plate 20 is mixed in the ratio of 25 to 40% loess of 100 mesh and 25 to 40% of charcoal, 10 to 20% of kaolin 10 to 20%, wollastonite 10 to 20%, zeolite 10 to 20% It bakes at 700 degreeC-800 degreeC, and forms the panel P of square shape.
즉, 결합되는 상판(10)과 하판(20)사이에 온수관(30) 및 전열관(40)을 위치할 수 있도록 안착홈(11)(12)(21)(22)을 반원형으로 각각 형성하고, 이들 사이에 200메쉬의 황토, 고령토, 규회석, 비석을 몰탈상태에서 상ㆍ하판(10)(20)사이에 채워 건조하여 이루어 지도록 하는 것이다.That is, the mounting grooves 11, 12, 21, 22 are formed in a semi-circular shape so that the hot water pipe 30 and the heat transfer pipe 40 can be positioned between the upper plate 10 and the lower plate 20 to be coupled thereto. Between them, 200 mesh loess, kaolin, wollastonite, and zeolite are filled by drying between the upper and lower plates 10 and 20 in a mortar state.
한편, 온수관(30) 및 전열관(40)을 설치하도록 안착홈(11)(12)(21)(22)을 형성하는 것은 여름철 장마시에 방안에 습기가 차는데 온수관(30)을 사용할 수도 있지만, 필요한 방만을 빠르게 전열관(40)으로 난방하기 위한 것이고, 겨울철에는 초저녁은 온수난방 취침후에는 전기난방을 하여 저녁내내 일정온도 유지 및 한방중에 보일러 가동에 따른 소음을 제거 할 수 있는 것이다.On the other hand, forming the seating grooves 11, 12, 21, 22 to install the hot water pipe 30 and the heat transfer pipe 40 may use the hot water pipe 30 to dampen the room during the rainy season in summer. However, only the necessary room is to heat the heat pipe 40 quickly, in the early winter in the evening, after the hot water heating bedtime to the electric heating to maintain a constant temperature throughout the evening and to remove the noise due to the operation of the boiler in one shot.
특히, 중앙 보일러 시설인 아파트인 경우에는 여름철 장미시 또는 개인이 난방이 필요한 경우 마음대로 난방할 수 없는 단점을 보강하여 전기로 마음대로 난방할 수 있게 하는 것이다.In particular, in the case of an apartment which is a central boiler facility, it is possible to heat the electricity freely by reinforcing the disadvantage of not being able to heat freely when summer roses or individuals need heating.
계속해서 본 고안에 따른 패널의 제조방법 및 시공방법을 상세히 설명하면 다음과 같다.Next, the manufacturing method and construction method of the panel according to the present invention will be described in detail.
제 1공정(상판제조공정)First process (top plate manufacturing process)
본 고안에 따른는 제 1공정은 상판제조공정으로서, 원적외선이 방출되어 인체에 유익한 물질이 방출되는 옥(15)과 숯(16)을 철망(14)의 메쉬 사이에 일정하게 배열하고, 200메쉬의 황토, 고령토, 규회석 및 비석 분말을 몰탈상태에서 상기 옥(15) 및 숯(16)의 사이에 채워 700∼800도의 온도에서 소결 성형하여 상판(10)을 제조한다.According to the present invention, the first process is a top plate manufacturing process, in which jade 15 and char 16 are constantly arranged between the meshes of the wire mesh 14, where far-infrared rays are emitted to release substances beneficial to the human body. Ocher, kaolin, wollastonite and zeolite powder are sandwiched between the jade (15) and charcoal (16) in a mortar state to prepare a top plate 10 by sintering at a temperature of 700 ~ 800 degrees.
이때 상판(10)은 온수관(30) 및 전열관(40)이 안착되는 안착홈(11)(12)이 형성되고, 네모서리에는 체결홈(13)을 일체로 형성하여 성형하는 것이다.At this time, the top plate 10 is formed with a seating groove (11, 12) on which the hot water pipe (30) and the heat transfer pipe (40) is seated, and is formed by forming the fastening groove (13) integrally in the four corners.
또한, 상판을 소결 성형 후 상면과 하면을 깍아 내어 수평이 되도록 절삭한다.In addition, after the top plate is sintered and molded, the top and bottom surfaces are scraped off and cut to be horizontal.
이는 옥과 숯이 상판의 표면에 노출되게 하여 육안으로 볼 때 심리적 효과를 기대할 수 있으며, 또한, 옥과 숯이 갖지고 있는 인체의 유효한 성질의 기능을 극대화 할 수 있는 것이다.This is to expose the surface of the jade and charcoal can be expected psychological effect with the naked eye, and also to maximize the function of the effective properties of the human body having jade and charcoal.
제 2공정(하판제조공정)2nd process (lower plate manufacturing process)
제 2공정은 상판(10)에 대응하는 하판(20)을 제조하는 공정으로서, 이는 100메쉬의 황토 25∼40%와 숯 25∼40%, 180∼200메쉬의 고령토 10∼20%, 규회석 10∼20%, 비석 10∼20% 비율로 혼합하고, 이를 700℃∼800℃로 소결 성형하여 하판(20)을 제조한다.The second step is to manufacture the lower plate 20 corresponding to the upper plate 10, which is 25 to 40% of 100 mesh ocher, 25 to 40% char, 10 to 20% kaolin 10 to 20 mesh, wollastonite 10 The lower plate 20 is manufactured by mixing at a ratio of 20% to 20% and 10 to 20% of the zeolite, followed by sintering at 700 ° C to 800 ° C.
이때 하판(20)은 상판(10)에 대응되도록 온수관(30) 및 전열관(40)이 안착되는 안착홈(21)(22)이 형성되고, 네 모서리에도 상판(10)에 형성된 체결홈(13)에 대응되는 체결돌기(23)를 일체로 성형하는 것이다.At this time, the lower plate 20 is a mounting groove 21, 22 is formed in which the hot water pipe 30 and the heat transfer pipe 40 is seated so as to correspond to the upper plate 10, the fastening groove formed in the upper plate 10 at four corners ( The fastening protrusion 23 corresponding to 13) is integrally molded.
제 3공정은(상ㆍ하판 결합공정)The third process is (upper and lower plate joining process)
상기 제 1공정과 제 2공정에서 소결 성형된 상ㆍ하판(10)(20)을 결합하는 공정으로서, 이 공정에서는 콘크리트 슬라브 또는 콘크리트 바닥면(100) 위에 단열재(50)를 깔고, 이 위에 하판(20)을 일정하게 설치한다.Bonding the upper and lower plates 10 and 20 sintered and molded in the first step and the second step, in which the insulating material 50 is laid on the concrete slab or the concrete floor 100, and the lower plate is placed thereon. (20) is installed regularly.
그리고, 하판(20)의 상면에 형성된 안착홈(21)(22)에 각각 온수관(30) 및 전열관(40)을 설치하고, 이 위에 상판(10)을 덮는다.Then, the hot water pipe 30 and the heat transfer pipe 40 are respectively installed in the seating grooves 21 and 22 formed on the upper surface of the lower plate 20, and the upper plate 10 is covered thereon.
이때 상ㆍ하판(10)(20)을 체결홈(13)과 체결돌기(23)에 의해 고정하고 공극과 수평을 맞추기 위하여 이들 사이에는 200메쉬의 황토, 고령토, 규회석, 비석을 몰탈상태에서 자연건조하게 되는 것이며, 이에 따라 상기 재료들의 특성에 의해 접착성이 좋고 건조가 빨리 이루어지며, 또한 갈라짐 등을 방지하여 공사 기간을 단축할 수 있는 것이다.At this time, in order to fix the upper and lower plates 10 and 20 by the fastening groove 13 and the fastening protrusion 23 and to level the pores, 200 mesh of loess, kaolin, wollastonite and tombstones are naturally in the mortar state. As a result, the adhesive properties are good and the drying is quick by the characteristics of the materials, and the construction period can be shortened by preventing cracking and the like.
그리고, 상ㆍ하판(10)(20)이 건조되어 일체로 굳어지면 이의 위에 장판(60)을 깔게 되는데 본 고안에서는 비닐장판을 사용하지 않고 종이장판, 특히, 통기성이 좋은 한지를 사용하는게 보다 바람직하다.In addition, when the upper and lower plates 10 and 20 are dried and hardened integrally, the sheet 60 is laid on the sheet. In the present invention, it is more preferable to use a sheet of paper, especially a paper sheet with good ventilation, without using a vinyl sheet. Do.
이상에서는 온돌 패널이 바닥면에 적용되는 것을 일예를 들어 설명하였지만, 본 고안의 온돌 패널은 침대에 설치하여 온돌 침대로도 사용할 수 있는 것이다.The above has been described as an example that the ondol panel is applied to the floor, the ondol panel of the present invention can be used as an ondol bed by installing on the bed.
이상 상세히 설명한 바와 같은 본 고안은 원적외선이 방출되는 옥과 숯을 주재료하여 온돌용 패널을 상ㆍ하로 소결 성형함으로서, 수맥파차단, 전자판차단, 습기차단, 벌레차단, 원적외선방출, 공기정화 등을 할 수 있는 효과가 있는 것이다.The present invention as described in detail above, by sintering the up and down panels for the main floor with jade and charcoal emitting far-infrared radiation, water blocking, electronic board blocking, moisture blocking, insect blocking, far infrared emission, air purification, etc. It is effective.
또한, 온수관 및 전열관을 안착홈을 상ㆍ하판에 형성함으로서 시공이 간편하고 시간을 단축시킬 수 있는 효과가 있는 것이다.In addition, the hot water pipe and the heat transfer pipe are formed in the upper and lower plate mounting grooves, the construction is easy and has the effect of reducing the time.
Claims (5)