KR20010057526A - Cosmetic composition containing silica coated color - Google Patents
Cosmetic composition containing silica coated color Download PDFInfo
- Publication number
- KR20010057526A KR20010057526A KR1019990061177A KR19990061177A KR20010057526A KR 20010057526 A KR20010057526 A KR 20010057526A KR 1019990061177 A KR1019990061177 A KR 1019990061177A KR 19990061177 A KR19990061177 A KR 19990061177A KR 20010057526 A KR20010057526 A KR 20010057526A
- Authority
- KR
- South Korea
- Prior art keywords
- silica
- coated
- pigment
- powder
- weight
- Prior art date
Abstract
Description
본 발명은 실리카로 코팅된 안료를 함유하는 분백류 색조화장료에 관한 것이다. 더욱 상세하게는, 본 발명은 안료와 색소를 혼합하고 오일을 결합제로 하여 제조하는 얼굴화장용 화장료에 나노미터 단위인 실리카로 코팅된 안료를 사용하므로서 빛의 정반사와 분비된 피지에 의해 분체가 젖었을 때 나타나는 번들거림 현상을 감소시키는 것을 특징으로 하는 분백류 색조화장료에 관한 것이다.The present invention relates to powdery color cosmetics containing pigments coated with silica. More specifically, the present invention is wetted by the specular reflection of the light and sebum secreted by using a pigment coated with a nanometer silica in the cosmetics for facial makeup prepared by mixing the pigment and the pigment and using the oil as a binder. It relates to powder powder color powder, characterized in that to reduce the appearance of shine when.
종래의 분백류 색조화장료는 분체-오일 성분의 구성비나 제형 및 사용목적에 따라 페이스파우더, 콤팩트, 볼연지, 아이섀도, 투웨이케익, 파우더 파운데이션 등으로 구분될 수 있으며, 피부에 도포되어 대략 4시간 내지 8시간 동안 부착되어 있다. 일반적으로 분백류 제품에 사용되는 분체들은 빛에 대해 정반사도가 높은 판상안료가 주로 이용되고 있으며 이 때문에 나타나는 번들거림 현상은 화장을 부자연스럽게 하는등 화장효과를 저하시킨다. 또한, 도포시간동안에 피부에서 분비되는 피지에 의해 피부에 도포된 분체가 젖었을 때 나타나는 번들거림 현상은 분백류 색조화장료를 사용하는 여성들의 가장 큰 불만 사항이다.Conventional powder powder cosmetics can be divided into face powder, compact, cheek oil, eye shadow, two-way cake, powder foundation, etc., depending on the composition ratio and formulation of the powder-oil component, and applied to the skin for about 4 hours. For 8 hours. In general, powders used in powder products are mainly used as plate pigments having high specular reflectance against light, and the resulting bleeding causes cosmetic effects such as unnatural makeup. In addition, the greasy phenomenon that occurs when the powder applied to the skin by the sebum secreted from the skin during application time is the biggest complaint of women using powdery color cosmetics.
이를 해결하기 위하여, 종래(JP 특개평 10-212211)에는 나노미터 단위인 박편상 산화티탄 집합물인 산화티탄 다공체를 사용해 빛을 산란시켜 번들거림을 줄이려는 노력이 있었으나 산화티탄 자체의 백색도에 의한 부자연스러움 및 성형성 때문에 적용에 많은 어려움이 있다. 또한, JP 특공평 7-119168에서는 실리콘이나 불소계 표면처리제로 코팅된 분체를 사용해 불소특유의 발유성으로 분체가 피지에 젖지 않게하여 과잉으로 분비된 피지에 의한 번들거림 현상을 줄이려 하였으나, 이 또한 사용감이나 제형상의 문제점 즉, 강한발유특성으로 분체는 젖지않으나 화장막자체가 들떠 뭉치는 현상때문에 적용에 많은 어려움이 있었다. 이외에도 흡유성이 우수한 분체를 배합해 분비되는 과잉의 피지를 흡유하게 하는등의 노력이 있었으나 이또한 얼굴에 도포되는 분체량과 분비되는 피지의 양을 고려할때 피지를 완전히 흡유해 번들거림을 없애는 것은 현재로서는 불가능한 일이다.In order to solve this problem, in the prior art (JP JP 10-212211), efforts have been made to reduce shine by scattering light using a titanium oxide porous body that is a flake titanium oxide aggregate in nanometer units, but unnaturalness due to the whiteness of titanium oxide itself. And there are many difficulties in application because of the formability. In addition, in JP 7-119168, powders coated with silicone or fluorine-based surface treatment agents were used to reduce the grease caused by excessive secretion of sebum by preventing the powder from getting wet with sebum due to fluorine-specific oil repellency. The problem with the formulation, that is, the powder does not get wet due to the strong oil repellent property, but there was a lot of difficulties in the application due to the lumping of the makeup itself. In addition, efforts have been made to absorb excess sebum secreted by blending powders with excellent oil absorption properties, but in addition, considering the amount of powder applied to the face and the amount of sebum secreted, it is currently necessary to completely absorb the sebum to eliminate grease. It is impossible for me.
본 발명은 상기와 같은 사실에 의거하여 안출한 것으로, 본 발명자들은 이러한 분백류 색조 화장료의 빛 및 피지에 의한 화장상태 변화(번들거림등)를 개선하고자 노력하던 중, 번들거림의 근본원인인 빛에 의한 정반사를 줄이면 화장초기 및 피지가 분비되더라도 시각적으로 나타나는 번들거림 현상은 줄어들 수 있다는 점에 착안하여, 나노미터 단위의 실리카로 코팅된 안료를 사용하게 되었다. 즉, 판상의 안료 표면에 나노미터 단위의 실리카를 코팅하여 형성된 미세한 요철이 입사된 빛을 산란시키고, 시간에 따라 분비되는 피지에 의해 분체가 젖게 되더라도 최종적으로 나타나는 번들거림 현상을 현격히 감소시키는 효과가 있음을 확인하여 본 발명을 완성하게 되었다. 따라서, 본 발명의 목적은 나노미터 단위의 실리카로 코팅된 안료를 함유하여 빛의 정반사와 분비된 피지에 의한 번들거림 현상을 감소시키는데 유용한 분백류 색조화장료를 제공하는 것이다.The present invention has been devised based on the above facts, and the present inventors have tried to improve the light state of such powdery tint cosmetics and the change of makeup state due to sebum, such as bleeding, due to light, which is the root cause of shine. Reducing the specular reflection can reduce the visual shine even if secretion and sebum is secreted. Therefore, the pigment coated with nanometer silica was used. That is, there is an effect of scattering the light incident by fine unevenness formed by coating the nanometer-sized silica on the plate-shaped pigment surface, and even when the powder is wet by sebum secreted over time, the final bleeding phenomenon is remarkably reduced. It was confirmed to complete the present invention. Accordingly, it is an object of the present invention to provide powdery tinctures which are useful for reducing the light reflecting phenomenon caused by sebum and specular reflection of light by containing pigments coated with nanometer silica.
이하, 본 발명을 좀더 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail.
실리카로 코팅된 판상의 안료와 이산화티탄, 색소를 섞어 균일하게 혼합시킨뒤 이들 입자들에 결합제로 사용된 오일을 혼합하여 분쇄, 성형하여 얼굴화장용 화장료를 제조한다.The plate-like pigment coated with silica, titanium dioxide, and pigment are mixed and uniformly mixed, and then the oil used as a binder is mixed with these particles to be pulverized and molded to prepare a cosmetic for facial makeup.
본 발명은 10-100 나노미터 단위의 실리카로 코팅된 안료를 사용해 빛 및 과잉으로 분비된 피지에 의한 빛의 정반사를 감소시켜 번들거림 현상을 줄이고 결과적으로 화장지속력을 증가시키는 우수한 화장료를 제공한다.The present invention uses pigments coated with silica in units of 10-100 nanometers to reduce the specular reflection of light by light and excessively secreted sebum to provide excellent cosmetics to reduce the phenomenon of shine and consequently increase the makeup lasting.
본 발명에 사용된 안료의 실리카 박막 제조는 기존의 박막 증착법과는 달리 박막을 비교적 저온에서 합성할 수 있고, 화학양론적 조절이 용이하며, 원료의 정제가 쉬운 졸-겔 공정을 선택하였다.Silica thin film production of the pigment used in the present invention, unlike the conventional thin film deposition method was selected sol-gel process that can synthesize the thin film at a relatively low temperature, easy stoichiometric control, easy purification of the raw material.
박막제작에 있어서, 첫 단계인 실리카 졸 제작을 위해 출발물질로 TEOS(Si(OC2H5)4)를 사용하였으며, 용매로는 에탄올, 증류수를 사용하였고, 맑고 투명한 졸 제작을 위해 촉매로 염산을 사용하였다. 상기 방법으로 제조된 실리카 졸을 분백류 색조화장품에서 주로 사용되고 있는 탈크, 마이카, 세리사이트등 판상안료와 색소등의 미분체 표면위에 축합반응을 통한 졸-겔 코팅법으로 나노미터 단위의 실리카 박막을 10-30 중량부(wt%) 코팅하여 사용하게 된다.In thin film manufacturing, TEOS (Si (OC 2 H 5 ) 4 ) was used as a starting material for the production of silica sol, which is the first step, ethanol and distilled water were used as solvent, and hydrochloric acid as a catalyst for preparing a clear and transparent sol. Was used. The silica sol prepared by the above method was subjected to a sol-gel coating method through a condensation reaction on the surface of fine pigments such as talc, mica and sericite, which are mainly used in powdery color cosmetics, and fine pigments such as dyes. 10-30 parts by weight (wt%) is used to coat.
본 발명에 사용되는 실리카로 코팅된 안료의 종류 및 함량은 특별히 제한되는 것은 아니나 일반적으로 분백류 색조화장품에 많이 사용되며 또한 입자형태가 판상이기 때문에 빛에 대한 정반사율이 높은 탈크와 마이카, 세리사이트를 5-90 중량부 사용하였으며, 바람직하게는 30-70 중량부를 사용할 경우 우수한 빛의 정반사 감소효과를 나타낸다. 실리카로 코팅된 안료가 5 중량부 이하일때는 원하는 정도의 번들거림 개선효과가 나타나지 않으며 90 중량부 이상에서는 사용감과 제형상의 문제점이 발생한다.The type and content of the silica-coated pigment used in the present invention are not particularly limited, but are generally used in powdery tint cosmetics, and since the particle shape is plate-like, talc, mica, and sericite having high specular reflectance to light are used. 5-90 parts by weight was used, and preferably 30-70 parts by weight of the excellent light reflecting effect is reduced. When the silica-coated pigment is 5 parts by weight or less, the desired degree of lubrication improvement does not appear, and at 90 parts by weight or more, there is a problem in feeling of use and formulation.
이하, 본 발명의 구체적인 구성과 작용을 실시예 및 비교예에 의거하여 더욱 상세히 설명한다. 그러나, 본 발명은 하기의 예에만 국한되지는 않는다.Hereinafter, the specific configuration and operation of the present invention will be described in more detail based on Examples and Comparative Examples. However, the present invention is not limited to the following examples.
실시예 1Example 1
하기 표 1의 조성비에 따라 원료 1내지 7을 혼합, 분쇄하고 원료 11(향)을 분무하고, 원료 8내지 10을 가열 용해시켜 분무한 후 혼합 분쇄하여 투웨이케익을 제조하였다.According to the composition ratio of Table 1, the raw materials 1 to 7 were mixed and pulverized, the raw material 11 (flavor) was sprayed, and the raw materials 8 to 10 were dissolved by spraying, followed by mixing and grinding to prepare a two-way cake.
실시예 2Example 2
실리카로 코팅된 세리사이트와 탈크를 사용한 것을 제외하고는 상기 실시예 1과 동일하게 수행하여 투웨이케익을 제조하였다.A two-way cake was prepared in the same manner as in Example 1, except that sericite and talc coated with silica were used.
비교예 1Comparative Example 1
실리카로 코팅된 안료를 사용하지 않은 것을 제외하고는 상기 실시예 1과 동일하게 수행하여 투웨이케익을 제조하였다.A two-way cake was prepared in the same manner as in Example 1 except that the pigment coated with silica was not used.
정반사율 측정Specular reflectance measurement
실시예 1, 2 및 비교예 1에서 제조한 제품에 대하여 빛에 의한 정반사율을 측정하여 그 결과를 하기 표 2에 나타냈다. 빛에 의한 정반사율 측정은 Gloss meter(Nippon Denshoku Kogyo Co. Ltd)로 실시했으며 정반사율은 -10도 입사광을 +10도 각도에서 측정하였다.Specular reflectance by light was measured for the products prepared in Examples 1 and 2 and Comparative Example 1, and the results are shown in Table 2 below. The specular reflectance by light was measured with a Gloss meter (Nippon Denshoku Kogyo Co. Ltd.) and specular reflectance was measured at -10 degrees and at +10 degrees.
상기 표 2에서 보는 바와 같이, 실리카로 코팅된 안료를 사용한 경우 안료 표면에 코팅된 실리카에 의한 빛의 산란으로 정반사율이 현격히 감소함을 알 수 있었다. 이는 안료 표면에 코팅된 나노미터 단위의 실리카가 요철과 같은 작용으로 빛을 난반사시킴에 기인한 것이다. 이는 기존의 연구들과 비교할 때 제형 및 사용감의 변화없이 번들거림 현상을 획기적으로 개선한 것이라 할 수 있다.As shown in Table 2, when the silica-coated pigment is used, it can be seen that the specular reflectance is significantly reduced due to scattering of light by the silica coated on the pigment surface. This is because nanometer silica coated on the surface of the pigment diffusely reflects light in an uneven manner. This is a dramatic improvement of the lubrication phenomenon without a change in formulation and feel compared to previous studies.
관능평가Sensory evaluation
실리카로 코팅된 안료를 사용한 경우 실제 피부도포시의 번들거림의 차이를 알아보기 위해, 실시예 1, 2 및 비교예 1에서 제조한 제품에 대해서 20세 내지 50세의 여성 30명을 시험대상으로 브라인드 테스트를 실시하고 화장시의 느낌 및 상태를 관능평가하여 그 결과를 하기 표 3에 나타냈다.In order to determine the difference in the shine when applying the pigment coated with silica, 30 women aged 20 to 50 years were blinded on the products prepared in Examples 1, 2 and Comparative Example 1 The test was carried out and the sensory evaluation of feeling and condition during make-up was shown in Table 3 below.
표 3의 평가기준은 다음과 같으며 각각의 값은 통계처리하여 나타냈다. (5:아주 우수하다, 4:우수하다, 3:보통이다, 2:나쁘다, 1:아주 나쁘다)The evaluation criteria of Table 3 are as follows and each value is shown by the statistical process. (5: very good, 4: excellent, 3: normal, 2: bad, 1: very bad)
실시예 3 및 비교예 2Example 3 and Comparative Example 2
하기 표 4의 조성비에 따라 1에서 7의 원료를 혼합 분쇄하고, 11의 향을 분무하고, 8에서 10의 원료를 가열 용해시켜 분무한 후, 혼합 분쇄하여 콤팩트를 제조하였다.The raw materials of 1 to 7 were mixed and pulverized according to the composition ratio of Table 4 below, the fragrance of 11 was sprayed, the raw materials of 8 to 10 were melted and sprayed, and then mixed and ground to prepare a compact.
브라인드 테스트Blind test
상기 실시예 3 및 비교예 2에서 제조한 제품에 대하여 20세 내지 50세의 여성 30명을 대상으로 브라인드 테스트를 실시하고, 그 결과를 하기 표 5에 나타내었다.The blind test was conducted on 30 women aged 20 to 50 years with respect to the products prepared in Example 3 and Comparative Example 2, and the results are shown in Table 5 below.
상기 표 2, 3 및 5에서 보는 바와 같이 실리카로 코팅된 안료를 함유하는 분백류 색조화장료는 종래의 분백류 색조화장료에 비해 제품사용감 및 화장효과가 유지된 상태로 특히 번들거림 개선효과가 우수하였다.As shown in Tables 2, 3, and 5, powdered whitening cosmetics containing pigments coated with silica were particularly excellent in lubrication improvement effect in a state in which the product usability and make-up effect were maintained compared to conventional powdered whitening cosmetics.
이상 설명하고 실시예와 비교예를 통하여 알 수 있는 바와 같이 본 발명은 빛 및 과잉으로 분비된 피지에 의한 빛의 정반사를 감소시켜 번들거림 현상을 줄이고 화장지속력을 증가시키는 분백료 색조화장료를 제공할 수 있어 화장품 산업상 매우 유용한 발명이다.As described above and as can be seen through the Examples and Comparative Examples, the present invention can provide a powder coloring tincture that reduces the specular reflection of light by light and excess secreted sebum to reduce the bleeding phenomenon and increase the makeup persistence. It is a very useful invention in the cosmetic industry.
Claims (3)