KR19990084102A - Method for restoring construction of polymer cement mortar section with spray manner - Google Patents
Method for restoring construction of polymer cement mortar section with spray manner Download PDFInfo
- Publication number
- KR19990084102A KR19990084102A KR1019990039326A KR19990039326A KR19990084102A KR 19990084102 A KR19990084102 A KR 19990084102A KR 1019990039326 A KR1019990039326 A KR 1019990039326A KR 19990039326 A KR19990039326 A KR 19990039326A KR 19990084102 A KR19990084102 A KR 19990084102A
- Authority
- KR
- South Korea
- Prior art keywords
- mortar
- repair
- polymer
- spraying
- cross
- Prior art date
Abstract
본원 발명은 여러 환경적, 기상적 작용에 의해 성능이 저하된 콘크리트 구조물을 보수함에 있어 고압스프레이를 이용한 폴리머시멘트 모르터 단면수복 보수공법에 관한 것으로, 보다 구체적으로는 폴리머시멘트 모르터의 일종인 폴리모르터 1, 폴리모르터 2, 슈퍼폴리모르터, 접착모르터, 방청제 및 코팅제로 구성된 그룹으로부터 선택되는 하나 이상의 조성물을 콘크리트가 탈락된 구조물의 수복단면에 스프레이 시공하여 보수하는 것이다.The present invention relates to a polymer cement mortar cross-sectional repair repair method using a high pressure spray in repairing concrete structures degraded by various environmental and meteorological effects, and more specifically, polymorter 1, which is a kind of polymer cement mortar. At least one composition selected from the group consisting of polymorter 2, superpolymorter, adhesive mortar, anti-corrosive agent and coating agent is spray-repaired on the repaired section of the concrete-deleted structure.
상기 본원 발명에 따른 스프레이공법을 이용한 폴리머시멘트 모르터 단면수복 보수공법은 방청제를 철근표면에 도포하는 단계; 접착모르터를 스프레이 하는 단계; 슈퍼폴리모르터를 스프레이 하여 단면을 수복하는 단계; 폴리모르터 1 또는 폴리모르터 2를 스프레이 하여 수복된 표면을 정리하는 단계; 및 코팅제를 사용하여 표면을 코팅하는 단계를 전부 또는 일부 포함한다.The polymer cement mortar cross-sectional repair repair method using the spray method according to the present invention comprises the steps of applying a rust inhibitor to the surface of the reinforcing bar; Spraying the adhesive mortar; Spraying the superpolymorter to repair the cross section; Spraying polymorter 1 or polymorter 2 to clean up the repaired surface; And coating all or part of the surface with the coating agent.
Description
본원 발명은 여러 환경적, 기상적 작용에 의해 성능이 저하된 콘크리트 구조물을 보수함에 있어, 스프레이공법을 이용한 폴리머시멘트 모르터 단면수복 보수공법에 관한 것으로, 화재발생 후 복구된 터널, 지하차도 등의 마감작업, 철도교량의 교각 콘크리트 보강작업, 새로 건축된 교량의 마감작업, 건물 외장벽의 콘크리트 보수작업, 고층건물의 발코니 표면작업에 사용될 수 있다.The present invention relates to a polymer cement mortar cross-sectional repair and repair method using a spray method in repairing a concrete structure deteriorated due to various environmental and meteorological effects. It can be used for work, concrete reinforcement of bridge bridges of railway bridges, finishing of newly constructed bridges, concrete repairs of building exterior walls, and balcony surface work of high-rise buildings.
특히 본원 발명에 따른 단면수복 보수공법은 콘크리트의 중성화 및 염해에 의해 철근이 부식되어 콘크리트가 탈락된 콘크리트로 된 교량, 지하차도, 복개구조물 및 터널 화재로 인하여 탄화된 콘크리트 구조물의 복구 마감 등의 콘크리트 단면을 복원하기 위하여 접착성과 부착성이 뛰어난 폴리머시멘트 모르터를 고압으로 스프레이 하여 시공함으로써, 시공이 편리하고 모르터의 탈락이 줄어들게 되므로 경제적이고 완벽한 보수시공이 되도록 하는 고압스프레이를 이용한 폴리머시멘트 모르터 단면수복 보수공법에 관한 것이다.In particular, the cross-sectional restoration repair method according to the present invention is a concrete, such as the recovery finish of carbonized concrete structures due to bridges, underground roads, covered structures and tunnel fires made of concrete from which concrete is dropped due to corrosion of reinforcing steel by neutralization and salt damage of concrete. Polymer cement mortar with high adhesion and adhesion to restore the cross section is sprayed at high pressure, making it easy to install and reducing mortar loss, so it is economical and perfect for repair. It is about public law.
종래의 일반적인 단면수복 보수공법은 여러 가지 보수재료를 교량, 지하차도, 복개구조물 등의 슬래브 하면(下面)의 단면수복 보수 시 흙손이나 헤라 등을 이용하여 작업 시 고개를 쳐들고 수(手)작업에 의해 단면을 패칭 시공해야하기 때문에 작업이 힘들고, 작업능률이 저하될 뿐만 아니라 보수부위의 품질이 저하되어 완벽한 단면수복 보수를 하기가 어려웠다.Conventional cross-sectional repair repair method uses a trowel or hera to repair various repair materials such as bridges, underground roads, and covered structures, using a trowel or hera to repair the cross section. Due to the need to patch the cross section, the work was difficult, not only the work efficiency was lowered, but also the quality of the repaired part was degraded, making it difficult to perform perfect cross-sectional repair.
또한 , 이와 같은 종래의 단면수복 보수공법은 슬래브 하면에서 윗 방향으로 모르터를 단면수복해야 하기 때문에 단면수복층이 큰 경우에는 모르터가 굳기 전에 탈락하는 양이 많아 모르터의 손실이 많을 뿐만 아니라 모르터가 잘 접착되지 않아 오래가지 못하고 재탈락이 발생하거나 모르터의 공극이 많아 구조물의 내구성 증진을 이루지 못하는 문제점이 있었다.In addition, in the conventional cross-sectional repair repair method, the mortar needs to be repaired upward from the lower surface of the slab. Therefore, when the cross-sectional repair layer is large, the amount of falling off before the mortar hardens not only causes the loss of the mortar but also the mortar. There was a problem that can not achieve the durability of the structure because the adhesion does not last long due to re-dropout or mortar voids.
따라서, 본원 발명의 목적은 이와 같은 종래의 시멘트 모르터 단면수복 보수공법이 갖는 문제점을 해결하기 위한 것으로 접착성과 부착성이 뛰어나고 경화성이 우수한 폴리머시멘트 모르터를 스프레이공법으로 시공함으로써 교량, 지하차도, 복개구조물 등의 슬래브 하면(下面)을 쉽게 시공을 할 수 있을 뿐만 아니라 스프레이 장비에 의해 기존 구조물에 접착시킴으로서 모르터의 단면수복 층이 잘 접착되어 재 탈락이 발생하지 않고 오래도록 내구성을 유지할 수 있도록 기존 구조물과의 접착성을 증대시키는 단면수복 보수공법을 제공하는 것이다.Accordingly, an object of the present invention is to solve the problems of the conventional cement mortar repair repair method, such as bridges, underground roadway, covering structure by constructing a polymer cement mortar with excellent adhesion and adhesion and excellent hardenability by spraying It is not only easy to construct the lower surface of the slab, etc., but also by adhering to the existing structure by spray equipment, so that the cross-sectional restoration layer of the mortar is adhered well so that it can maintain durability for a long time without re-dropping. It is to provide a cross-sectional repair repair method to increase the adhesion.
또한 본원 발명은 전공정을 기계화 시공함으로써 작업이 힘들지 않고, 작업능률을 향상시켜 품질이 우수한 완벽한 보수를 할 수 있는 단면수복 보수공법을 제공하는 것이다.In addition, the present invention is to provide a cross-sectional repair repair method that can be a perfect repair with excellent quality by improving the work efficiency by hard work by mechanizing the entire process.
도 1은 본원 발명에 따른 폴리머시멘트 모르터 단면수복 보수단면도1 is a polymer cement mortar cross-sectional repair repair cross-sectional view according to the present invention
도 2는 본원 발명에 따른 스프레이공법을 이용한 폴리머시멘트 모르터 단면수복 보수 시공 공정도Figure 2 is a polymer cement mortar cross-sectional repair repair construction process using the spray method according to the present invention
이러한 본원 발명의 목적은 폴리머시멘트 모르터의 일종인 폴리모르터 1, 폴리모르터 2, 충진모르터, 접착모르터, 방청제 및 코팅제로 구성된 그룹으로부터 선택된 하나 이상의 조성물을 콘크리트가 탈락된 구조물의 수복 단면에 스프레이 시공하여 콘크리트단면을 보수하는 공법에 의해 달성된다.An object of the present invention is to spray-install one or more compositions selected from the group consisting of poly mortar 1, poly mortar 2, filling mortar, adhesive mortar, anti-corrosive agent and coating agent, which is a kind of polymer cement mortar, to the repair section of the concrete-deleted structure. Achieved by the method of repairing the concrete section.
본원 발명에 따른 스프레이공법을 이용한 폴리머시멘트 모르터 단면수복 보수공법은 방청제를 철근표면에 도포하는 단계; 접착모르터를 스프레이 하는 단계; 충진모르터를 스프레이 하여 단면을 수복하는 단계; 폴리모르터 1 또는 폴리모르터 2를 스프레이 하여 수복된 표면을 정리하는 단계; 및 코팅제를 사용하여 표면을 코팅하는 단계를 전부 또는 일부 포함한다.Polymer cement mortar cross-sectional repair repair method using the spray method according to the present invention comprises the steps of applying a rust inhibitor to the surface of the reinforcement; Spraying the adhesive mortar; Repairing the cross section by spraying a filling mortar; Spraying polymorter 1 or polymorter 2 to clean up the repaired surface; And coating all or part of the surface with the coating agent.
상기 단면수복 보수공법에서, 방청제를 철근표면에 도포하는 단계는 철근의 부식을 방지하기 위한 것이고, 접착모르터를 스프레이 하는 단계는 기존 콘크리트와 단면수복 모르터와의 접착을 증진시키기 위하여 접착모르터를 3∼5bar정도의 고압으로 스프레이하여 이루어지고, 충진모르터로 단면을 수복하는 단계는 충진모르터를 6∼20bar 정도의 고압으로 스프레이하여 이루어지며, 폴리모르터 1 또는 폴리모르터 2로 표면을 정리하는 단계는 상기 폴리모르터 1 또는 2를 6∼10bar 정도의 고압으로 스프레이 하여 이루어지고, 코팅제로 표면을 코팅하는 것은 수복된 구조물의 완벽한 보호를 위해 화학이온의 침투 등 콘크리트를 침식시키는 물질의 침투를 억제하기 위한 것이다.In the cross-sectional repair repair method, the step of applying the anti-rust agent to the surface of the reinforcing bar is to prevent the corrosion of the reinforcing bar, spraying the adhesive mortar to the adhesive mortar to improve the adhesion of the existing concrete and the cross-sectional restoration mortar 3 ~ Spraying at a high pressure of about 5bar, the step of restoring the cross section with the filling motor is made by spraying the filling motor at a high pressure of about 6 ~ 20bar, the step of cleaning the surface with polymorter 1 or polymorter 2 is the poly Spraying mortar 1 or 2 to a high pressure of about 6 ~ 10bar, and coating the surface with a coating agent is to suppress the penetration of substances that erode concrete, such as the penetration of chemical ions for the complete protection of the repaired structure.
또한, 본 발명에 따른 단면수복 보수공법에서 콘크리트의 성능저하 정도나 구조물의 위치에 따라 상술한 5단계 공정을 모두 시공하는 것이 아니라 제 4단계 공정 또는 제 3단계 공정만으로도 시공할 수 있다. 즉 철근이 부식하지 않은 경우에는 상기 방청제를 도포하는 단계를 생략하고, 콘크리트의 탈락이 없는 경우에는 상기 방청제를 도포하는 단계 및 충진모르터로 단면을 수복하는 단계를 생략하며, 표면코팅이 필요하지 않은 경우에는 상기 코팅제로 표면을 코팅하는 단계를 생략하고 본 발명에 따른 단면 수복 보수공법을 시공할 수 있다.In addition, according to the present invention, the above-described five-step process may be performed only by the fourth step or the third step, depending on the degree of deterioration of the concrete or the location of the structure. That is, if the reinforcing bar is not corroded, the step of applying the rust preventive agent is omitted, and if there is no dropout of the concrete, the step of applying the rust preventive agent and the step of restoring the cross section with the filling mortar, do not require surface coating In this case, it is possible to omit the step of coating the surface with the coating agent and construct a cross-sectional repair repair method according to the present invention.
한편 본원 발명에서 사용하는 폴리머시멘트 모르터는 시멘트, 물, 잔골재 및 다른 혼화재료를 혼합비빔하여 만든 통상적인 모르터에 폴리비닐 아세테이트, 스티렌-부타디엔 공중합체, 아크릴 수지, 스티렌-아크릴 공중합체 등으로 구성된 그룹으로부터 선택되는 하나 이상의 폴리머를 더 포함한 것을 의미한다.Meanwhile, the polymer cement mortar used in the present invention is a group composed of polyvinyl acetate, styrene-butadiene copolymer, acrylic resin, styrene-acryl copolymer, etc. in a conventional mortar made by mixing and mixing cement, water, fine aggregate and other miscible materials. It means further comprising one or more polymers selected from.
또한 본원 발명에서 사용되는 폴리모르터 1, 폴리모르터 2, 충진모르터, 접착모르터는 상기 폴리머시멘트 모르터의 일종으로, 폴리모르터 1은 10-15%의 폴리머, 30-40%의 시멘트, 35-45%의 규사, 12-20%의 물 및 1-3% 의 혼화제가 배합된 조성물로서 미세하기 때문에 표면을 매끄럽게 구성하고 이산화탄소 및 염분의 침투를 억제할 수 있어 내구성을 증진하는 특성을 가진다.In addition, polymorter 1, polymorter 2, filling mortar, adhesive mortar used in the present invention is one of the polymer cement mortar, polymorter 1 is 10-15% polymer, 30-40% cement, 35-45% Because of the fine composition of the silica sand, 12-20% water and 1-3% admixture, the surface can be made smooth and the penetration of carbon dioxide and salt can be suppressed and has the property of enhancing durability.
상기 폴리모르터 2는 15-20%의 폴리머, 30-40%의 시멘트, 35-45%의 규사, 12-20%의 물 및 1-3% 의 혼화제가 배합된 조성물로서 내화학 저항성이 우수한 특성을 가지며, 특히 황산염에 저항이 더 큰 재료이다.The polymorter 2 is composed of 15-20% polymer, 30-40% cement, 35-45% silica sand, 12-20% water, and 1-3% admixture. It is a material that has a higher resistance to sulphate.
상기 충진모르터는 8-15%의 폴리머, 25-30%의 시멘트, 40-55%의 규사, 8-18%의 물 및 1-3% 의 혼화제가 배합된 조성물로서 리바운드되지 않고 접착력이 강하며 강도를 회복할 수 있는 특징을 가진다.The filling mortar is composed of 8-15% polymer, 25-30% cement, 40-55% silica sand, 8-18% water and 1-3% admixture. Has the characteristic of recovering strength.
상기 접착모르터는 12-20%의 폴리머, 35-50%의 시멘트, 30-35%의 규사, 10-20%의 물 및 1-3% 의 혼화제가 배합된 조성물이다.The adhesive mortar is a composition comprising 12-20% polymer, 35-50% cement, 30-35% silica sand, 10-20% water and 1-3% admixture.
여기서 상기 폴리머시멘트 모르터에 사용될 수 있는 혼화제로는 AE제, 감수제, AE감수제, 유동화제, 고성능감수제, 지연제, 경화촉진제, 철근방청제, 발포제, 방수제 등이 있다.Here, the admixtures that may be used in the polymer cement mortar include an AE agent, a water reducing agent, an AE water reducing agent, a fluidizing agent, a high performance water reducing agent, a retardant, a curing accelerator, a reinforcing bar rusting agent, a foaming agent, a waterproofing agent, and the like.
이하에서는 본원 발명에 따른 스프레이공법을 이용한 폴리머시멘트 모르터 단면수복 보수공법을 첨부도면에 도시한 실시예에 의해 설명한다.Hereinafter, the polymer cement mortar cross-sectional repair repair method using the spray method according to the present invention will be described by the embodiment shown in the accompanying drawings.
도 1은 본원 발명에 따른 스프레이 공법을 이용한 폴리머시멘트 모르터 단면수복 보수공법의 단면도에 관한 것으로, 이를 참조하면 제 1단계는 철근의 부식을 방지하기 위하여 방청제 TK(중앙크리텍사 제품)를 철근표면에 바르는 단계이다. 제 2단계는 기존 콘크리트와의 단면수복 모르터와의 접착을 증진시키기 위하여 접착모르터 TH200(중앙크리텍사 제품)를 고압스프레이장비인 베리오제트(Werner Mader GMBH 제품)를 사용하여 3∼5bar정도의 고압으로 스프레이한다. 제 3단계는 콘크리트가 많이 탈락되고 단면의 손상이 심한 단면을 폴리머모르터를 깊게 충진하여 수복하기 위해, 리바운드되지 않고 접착력이 강하며 강도를 회복할 수 있는 특징을 가진 충진모르터 TF200(중앙크리텍사 제품)을 10-20bar 정도의 고압으로 스프레이하여 단면을 수복한다. 제 4단계는 제 3단계에서 시공된 충진모르터 TF200(중앙크리텍사 제품)의 표면이 거칠어 표면을 매끄럽게 하고 내구성을 유지할 목적으로 시공하는 것으로, 미세하기 때문에 표면을 매끄럽게 구성하고 이산화탄소 및 염분의 침투를 억제할 수 있어 내구성을 증진하는 특성이 있는 폴리모르터 1 TS200(중앙 크리텍사 제품) 또는 내화학저항성이 우수한 특성을 가진 폴리모르터 2 TS250(중앙 크리텍사 제품)을 6∼10bar 정도의 고압으로 스프레이하여 표면정리를 한다. 최종적으로 제 5단계는 콘크리트의 내구성이 특별히 요구되는 구조물의 경우 완벽한 보호를 위해 화학이온의 침투 등 콘크리트를 침식시키는 물질의 침투를 완벽히 억제하는 특성을 가진 코팅제 V100(중앙 크리텍사 제품)을 사용하여 표면을 코팅하는 것이다.1 is a cross-sectional view of the polymer cement mortar cross-sectional repair repair method using a spray method according to the present invention, the first step is to prevent the corrosion of the reinforcing bar TK (manufactured by Central Crytec Co.) to the surface of the rebar It is a step of application. In the second step, the adhesive mortar TH200 (manufactured by Jung-Crytec) was used at a high pressure of about 3 to 5 bar using Veri-Jate (Werner Mader GMBH), a high-pressure spraying machine, to promote the adhesion of the cross-sectional restoration mortar with the existing concrete. Spray. In the third step, the filling motor TF200 (Central Crytec's product), which is characterized by strong rebound, adhesive strength and recovery of strength, is used to deeply fill the polymer mortar and recover the section where the concrete is dropped off and the section is severely damaged. ) To the cross section by spraying it at a high pressure of 10-20 bar. In the fourth step, the surface of the filling motor TF200 (manufactured by Jung-Crytec Co., Ltd.), constructed in the third step, is rough and smooth, and it is installed for the purpose of maintaining durability.The fourth step is to make the surface smooth and to prevent infiltration of carbon dioxide and salt. Spray it at a high pressure of about 6 to 10 bar with Polymorter 1 TS200 (manufactured by Central Critech) or Polymorror 2 TS250 (manufactured by Central Critec) with excellent chemical resistance. Clean up the surface. Finally, the fifth step uses the coating material V100 (manufactured by Central Critech Co., Ltd.), which has the property of completely suppressing the penetration of materials that erode concrete, such as the penetration of chemical ions, for the complete protection of structures that require the durability of concrete. Coating the surface.
도 2는 본원 발명의 고압스프레이에 의한 단면수복 보수공법의 공정도를 나타낸 것으로, 상기 도 2에 따라 본원 발명의 단면수복 보수공법을 보다 구체적으로 살펴보면, 먼저 기존콘크리트의 열화부위를 슈미트햄머(Werner Mader GMBH 제품)나 초음파측정기(Werner Mader GMBH 제품)로 측정하고 철거두께를 결정한 후 그 부위를 최고압력 500∼1000bar의 고압스프레이로 철거하고 청소된 하지면을 최고압력 100∼300bar의 고압스프레이 세척을 한 후 자연건조 시킨다.Figure 2 shows a process diagram of the cross-sectional repair repair method by the high-pressure spray of the present invention, in more detail look at the cross-sectional repair repair method of the present invention according to Figure 2, first the deterioration of the existing concrete Schmidhammer (Werner Mader GMBH) or ultrasonic measuring instrument (Werner Mader GMBH), and after demolition thickness was removed, the area was removed with a high pressure spray of 500 ~ 1000 bar and the cleaned floor was cleaned with high pressure spray of 100 ~ 300 bar. After drying naturally.
콘크리트가 열화되어 탈락하고 철근이 노출되어 부식된 경우 철근의 부식방지를 위해 방청제 TK(중앙크리텍사 제품)를 브러쉬로 철근표면에 바른다. 철근이 부식되지 않고 노출되지도 않은 경우에는 방청제 TK(중앙크리텍사 제품)를 바를 필요가 없다. 철근부식방지제인 상기 방청제 TK를 바른 후 강한 직사광선이나 바람의 영향이 있을 경우 시트나 매트를 사용하여 보호한다.If the concrete is deteriorated due to deterioration and the rebar is exposed and corroded, the anti-rust agent TK (manufactured by Central Crytec) is applied to the surface of the rebar with a brush to prevent corrosion of the rebar. If the bar is not corroded or exposed, it is not necessary to apply the rust preventive TK (manufactured by Central Crytec). After applying the anti-corrosive agent TK, which is a reinforcing corrosion inhibitor, protect it using a sheet or a mat in case of strong direct sunlight or wind effect.
콘크리트가 탈락된 부위의 단면수복 전에 하지면의 흡수력을 감소시키기 위해 스프레이를 이용하여 물로 적신 다음 충진 모르터의 접착력강화를 위해 접착모르터 TH 200(중앙크리텍사 제품)을 압력 3∼5bar 정도의 고압으로 건조시 1.0 mm의 시공 최소두께가 되도록 스프레이한다.To reduce the absorbency of the lower surface before the cross-sectional restoration of the concrete drop-out area, use a spray-soaked water with water, and then apply the adhesive mortar TH 200 (manufactured by Central Critec) at a high pressure of 3 to 5 bar to increase the adhesion of the filling mortar. When drying, spray to a minimum thickness of 1.0 mm.
콘크리트의 탈락부위에 충진모르터 TF 200(중앙크리텍사 제품)를 압력 6∼20bar 정도의 고압으로 스프레이하여 충진한다. 이때 30 mm 이상의 보수는 여러 번 시공하며, 충진된 면은 부드럽게 두들기고 거칠게 만든다.Filling the sprayed mortar TF 200 (manufactured by Jung-Crytec Co., Ltd.) at a high pressure of about 6 ~ 20 bar to the dropping part of concrete. At this time, more than 30 mm of repair should be done several times, and the filled surface is softly beaten and roughened.
시공된 면을 평탄하게 하고 내구성을 증진하기 위하여 폴리모르터 1 TS 200(중앙 크리텍사 제품) 또는 폴리모르터 2 TS 250(중앙 크리텍사 제품)을 압력 6∼10bar 정도로 스프레이하여 시공 최소두께가 2.0mm 이상이 되도록 스프레이 한다. 시공된 면은 빠른 건조로 인한 균열을 막기 위해 양생제나 양생포로 보호하며, 시공된 면이 완전 경화 하기전 하중이 가해지지 않도록 한다.In order to make the surface flat and to increase durability, spray the polymorter 1 TS 200 (manufactured by Center Critec) or polymorter 2 TS 250 (manufactured by Center Critec) at a pressure of 6 to 10 bar and the minimum construction thickness is 2.0 mm or more. Spray to get The constructed surface is protected with a curing agent or curing agent to prevent cracking due to rapid drying, and the load is not applied before the surface is completely hardened.
마지막 단계로 중성화, 동결융해로 인한 손상을 방지하기 위해 코팅제 V 100(중앙크리텍사 제품)을 압력 3∼5bar로 스프레이 하여 코팅하고 작업장 주위를 깨끗이 정리한다.As a final step, to prevent damage due to neutralization and freeze-thawing, coating V 100 (manufactured by Central Crytec Co., Ltd.) at a pressure of 3 to 5 bar is applied and the work area is cleaned up.
한편, 본원 발명에 따른 스프레이공법에 의한 단면수복 보수공법의 우수성을 살펴보기 위해, 본원 발명에 따른 단면수복 보수공법과 종래의 단면수복 보수공법을 표 1 및 표 2에서 비교하였다.Meanwhile, in order to examine the superiority of the cross-sectional repair repair method by the spray method according to the present invention, the cross-sectional repair repair method according to the present invention and the conventional cross-sectional repair repair method was compared in Table 1 and Table 2.
표 1 및 표 2에서 살펴본 바와 같이 본원 발명에 따른 스프레이공법을 이용한 단면수복 보수공법은 종래 기술의 단면수복 보수공법에 비해, 시공시간 및 시공비용 면에서 대단히 우수할 뿐만 아니라 보수된 단면의 압축강도 및 중성화, 염분의 침투력 등의 품질에 있어서도 우수한 것을 확인할 수 있다.As shown in Table 1 and Table 2, the cross-sectional repair repair method using the spray method according to the present invention is not only excellent in construction time and construction cost, but also compressive strength of the repaired cross-section compared to the conventional cross-sectional repair repair method And it can confirm that it is excellent also in quality, such as neutralization and salt penetration.
이와 같이 본원 발명의 스프레이공법을 이용한 단면수복 보수공법을 통하여 콘크리트가 탈락되고 철근이 부식되어 성능이 저하된 교량, 지하차도, 터널, 고가차도, 하수박스 및 복개구조물의 단면수복 보수에 있어서 종래의 수작업에 의한 패칭공법의 단점을 완전히 보완할 수 있을 뿐만 아니라 기계화 시공에 따라 시공시간을 단축하고 완벽한 보수시공이 가능하다.As described above, in the section repair repair of bridges, underground roadways, tunnels, elevated roadways, sewer boxes, and covered structures, where concrete is dropped and the steel is corroded through the cross-section repair repair method using the spray method of the present invention. Not only can completely compensate for the shortcomings of the patching method by manual work, but also shorten the construction time and perfect repair work according to mechanized construction.
또한, 본원 발명에 따른 단면수복 보수공법은 고압에 의해 미세한 폴리머시멘트 모르터를 스프레이공법에 의해 고압을 이용하여 스프레이 시공함으로써, 기존 콘크리트와의 부착성을 증대시키고 모르터의 공극을 치밀하게 하여 보수부위의 내구성의 증진 및 콘크리트구조물의 내구성을 저하시키는 요인이 구조물에 침투하지 못하도록 할뿐만 아니라 화재 등으로 인하여 탄화된 콘크리트를 다시 알칼리화 하는 탁월한 효과가 있다.In addition, the cross-sectional repair repair method according to the present invention by spraying the fine polymer cement mortar by high pressure by the spray method using a high pressure, thereby increasing the adhesion to the existing concrete and densifying the pores of the mortar to close the repair site Not only do not prevent the penetration of the structure to increase the durability and deterioration of the durability of the concrete structure, but also has an excellent effect of alkalizing the carbonized concrete due to fire.
아울러 본원 발명에 따른 단면수복공법 시공시 모르터의 탈락율을 5%이하로 줄일 수 있어 단면수복의 품질을 확보하고 모르터의 손실을 줄여 경제적이다.In addition, when the construction of the cross-sectional restoration method according to the present invention can reduce the dropout rate of the mortar to less than 5% to ensure the quality of the cross-sectional restoration and economical by reducing the loss of the mortar.
Claims (11)