KR19990073097A - The manufacture method of upper plate for easy fioor - Google Patents
The manufacture method of upper plate for easy fioor Download PDFInfo
- Publication number
- KR19990073097A KR19990073097A KR1019990016107A KR19990016107A KR19990073097A KR 19990073097 A KR19990073097 A KR 19990073097A KR 1019990016107 A KR1019990016107 A KR 1019990016107A KR 19990016107 A KR19990016107 A KR 19990016107A KR 19990073097 A KR19990073097 A KR 19990073097A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- ondol
- press
- top plate
- less
- Prior art date
Abstract
본 발명은 조립식 온돌분야에서 온돌 마감재로 사용되는 조립식 온돌용 상판 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a prefabricated ondol top plate used as an ondol finishing material in the field of prefabricated ondol.
함수율 0.2% 이내의 무기질 규사 또는 무기질 종류의 석재 ø1.5내지2를 21내지22중량%, ø0.5내지1를 53내지54중량 %, 충진제로 탄산칼슘 20㎛이하의 규격 및 타 무기질 재료 중 20㎛이하의 규격으로 대체 사용할 수 있으며, 15내지16중량%을 배합비율로 하고 잘 혼합되게 배합한다.Inorganic silica sand or mineral stone with a water content of 0.2% or less ø1.5 to 2 to 21 to 22% by weight, ø0.5 to 1 to 53 to 54% by weight, and among the standards of calcium carbonate as filler and other inorganic materials It can be used as the standard of 20㎛ or less, and mix it with 15 to 16% by weight as mixing ratio and mix well.
한편 불포화 폴리에스터 수지 1O내지11중량% 이하, 촉진제 (cobalt octoate)는 수지대비 3중량%, 고온 경화제 (methyl ethyl ketone peroxide) 3중량%를 잘 썩이도록 혼합하여 먼저 배합된 조성물과 같이 혼합하고, 한편 가로, 세로의 사각형틀에 이형제(실리콘 또는 스테인산)등을 0.5mm정도 도포 한 후 한지 또는 창호지를 사각의 형틀에 삽입한다.On the other hand, the unsaturated polyester resin 10 to 11% by weight or less, the cobalt octoate 3% by weight compared to the resin, 3% by weight of high temperature curing agent (methyl ethyl ketone peroxide) to mix well so as to mix with the composition blended first, On the other hand, apply a release agent (silicone or stearic acid) about 0.5mm on the horizontal and vertical rectangular frame and insert the paper or window paper into the rectangular frame.
이후 화이바 글라스를 위에 삽입한 다음 배합된 모재를 수평하게 1.2내지1.4cm 의 두께 수평이 되도록 도포한 후 그 위로 화이바 글라스 및 한지를 덮고 가열된 프레스 내부로 삽입한다.After inserting the fiber glass on the top, then the blended base material is applied horizontally to a thickness of 1.2 to 1.4 cm horizontally, and then inserted into the heated press covering the glass glass and Hanji.
프레스의 가열온도는 상부130℃ 하부 150℃를 유지하도록 조정하고, 프레스로 가압 한다. 이때 가열시간은 최소 3분30초 이상 가압하며, 가압은 40㎠/kg이상으로 성형하는 것이다.The heating temperature of the press is adjusted to maintain the upper 130 ℃ lower 150 ℃, pressurized by the press. At this time, the heating time is at least 3 minutes and 30 seconds or more, the pressurization is to be molded to 40 cm2 / kg or more.
Description
본 고안은 조립식 온돌분야에서 온돌 마감재로 사용되는 조립식 온돌용 상판 제조방법에 관한 것이다.The present invention relates to a method for producing a prefabricated ondol plate used as an ondol finishing material in the field of prefabricated ondol.
주지하는 바와 같이 조립식 온돌용 상판은 습식 온돌구조에서 마감미장 대용으로 조립식 온돌에서 지지틀 상면에 설치되어 사용되고 있는바 상기한 상판들은 통상적으로 철판, 목재, PVC판, 천연석재 및 인조석판 등을 이용하여 일정규격의 정사각형 또는 직사각형의 형태로 단위 판재로 제작 및 절단되어 이들을 가로 및 세로로 연결 조립하여 온돌 하부에 설치되어 있는 지지틀 상면에 일정면적을 부설하고 있다.As is well known, the prefabricated ondol top plate is installed and used on the upper surface of the support frame in the prefabricated ondol as a substitute for the finishing plaster in the wet ondol structure. Therefore, it is manufactured and cut into unit boards in the form of square or rectangle of a certain standard, and these are connected and assembled horizontally and vertically, and a certain area is laid on the upper surface of the supporting frame installed under the ondol.
본 발명자는 조립식 온돌에서 배관 지지틀로 사용하는 일체형 난방배관 지지틀을 실용신안 등록출원 제 99-5145283-08호로 제안한바 있으며, 상기한 선 출원 이외에 다른 형태의 지지틀도 사용되고 있으나 이들 또한 상판을 사용하는 것은 공통된 형태이다.The present inventors proposed an integrated heating pipe support frame for use as a pipe support frame in a prefabricated ondol as Utility Model Registration No. 99-5145283-08. In addition to the above-mentioned application, other types of support frames are also used, but these also use a top plate. It is a common form to use.
종래의 온돌용 상판으로 사용하고 있는 자재로는 철판, 합판, 인조석재, 등의 문제점으로 먼저 철판의 경우 두께 0.8내지1.2mm정도를 보편적으로 사용하고 있으며, 열전도율은 매우 좋으나, 온돌상부로 열이 가해질 경우 재료의 수축팽창 및 열변형이 심하고, 쉽게 가열되고 쉽게 식는 문제가 있으며, 집중하중의 경우 220kgf 이상이 되어야 피아노 및 가구의 집중 하중을 견딜 수 있으나 이의 강도에 미치지 못해 함몰되며, 연결부위 연결이 매끄럽지 못하여 연결부위에 단턱이 지는 현상이 심하다.As a material used as a top plate for conventional ondol, there are problems such as iron plate, plywood, artificial stone, etc. First of all, in case of iron plate, the thickness is generally used in the range of 0.8 to 1.2 mm, and the thermal conductivity is very good, When applied, severe shrinkage and thermal deformation of the material, easy heating and easy cooling, and concentrated load of more than 220kgf to withstand the concentrated load of the piano and furniture, but it does not reach the strength of it, sinks, This is not smooth, so the stepped on the connection is severe.
합판 및 목재의 경우에도 열에 의한 수축팽창이 심하고, 열전도가 낯아 단열재의 역할을 하고 있으며, 수분에 의한 변형 때문에 조립식 온돌용 상판으로는 부적합하다. 또한 강도가 약해 이를 보강하기 위해 판재의 두게를 높일 경우 조립식 온돌의 전체 높이가 상승되어 제품 상부표면의 온도는 단열효과로 인해 떨어지게 되는 심각한 문제점을 안고 있다.In case of plywood and wood, the thermal expansion and contraction is severe, and the heat conduction is not good as a heat insulating material, and due to the deformation by moisture is not suitable for the prefabricated ondol top plate. In addition, if the strength of the plate to increase the thickness of the plate in order to reinforce it, there is a serious problem that the overall height of the prefabricated ondol rises and the temperature of the upper surface of the product falls due to the insulation effect.
천연석재를 사용할 경우 석재의 강도를 유지하기 위해 최소한의 두께가 2㎝이상 되어야 하고 축열 및 압축강도는 어느 정도 해결할 수 있으나 충격강도에 약하고 석재와의 연결이 시멘트 및 접착제로 시공되었을 경우 이음매 처리가 깨끗하지 못하고, 연결부위가공이 어려우며, 가격이 고가이며, 자재의 하중이 무거워 시공성이 떨어지게 된다.In case of using natural stone, the minimum thickness should be more than 2cm to maintain the strength of the stone, and the heat storage and compressive strength can be solved to some extent, but it is weak in impact strength and the joint treatment is performed when the connection with stone is made of cement and adhesive. It is not clean, difficult to process the joints, expensive, and heavy load of the material, the workability is poor.
상기와 같이 온돌의 기능 및 사용 용도의 적정한 기준 없이 기존의 판재를 그대로 사용하고 있어 실제의 바닥재로 필요한 상판의 요구조건 성능에 크게 미치지 못하여 조립식온돌의 심각한 표면 하자발생 요인이 되고 있다.As mentioned above, the existing plate is used as it is without a proper standard of the function and use of the ondol, which is a factor of serious surface defects of the prefabricated ondol because it does not greatly meet the performance requirements of the top plate required as the actual flooring material.
상기한 문제를 해결하기 위해 본 발명자는 기존 온돌상면에서 가져야하는 판재의 요구조건 성능을 정립하고 이의 조건을 조립식온돌용 상판에 만족시키기 위해 많은 연구와 실험한 끝에 본 발명을 완성하였다.In order to solve the above problems, the present inventors have completed the present invention after many studies and experiments to establish the performance requirements of the plate that must have on the existing ondol top surface and to satisfy the conditions on the prefabricated ondol top plate.
상기한 상판의 요구조건 성능을 보면, 조립식 온돌용 상판은 온수 방열관에서 열을 온돌용 상판을 통하여 실내로 전달해주는 역할을 하므로, 마감재로서 필요한 성능외에도 방열 효율을 높이기 위한 성능 및 축열성이 동시에 요구된다.In view of the performance requirements of the top plate, the prefabricated ondol top plate serves to transfer heat from the hot water radiating pipe to the room through the ondol top plate, and in addition to the performance required as a finishing material, the performance and heat storage property at the same time to increase the heat radiation efficiency Required.
이들 자세하게 나열하면 다음과 같다.The details are as follows.
일정 수준 이상의 압축강도 220kgf 이 필요하며, 특히 피아노, 가구 등의 최대 집중하중으로 작용되는 부위에서 함몰이나 균열이 발생되지 않아야 하며, 바닥 평활도가 우수하고 균열이 발생되지 않아야 하며, 온도변화 및 팽창. 수축에 대한 내구성이 요구되며 이의 적용수치는 시멘트 온돌과 유사한 1.0 x 10-5/℃ 이하가 되어야 하며, 최종 마감재인 비닐장판이나 한지장판 등의 부착이 용이 해야한다.Compressive strength of 220kgf or more is required, especially in the area where the maximum concentrated load of piano, furniture, etc., should not occur, no cracking, good floor smoothness, no cracking, temperature change and expansion. Shrinkage durability is required and its applied value should be 1.0 x 10 -5 / ℃ or less, similar to cement ondol, and should be easily attached to the final sheet, such as vinyl sheet or hanji sheet.
또한 빠르고 고른 열 방출을 위해 열전도율이 높은 재료가 바람직하고, 이의 적용수치는 종래의 시멘트 온돌 1.3㎉/mh℃에 근접한 수치이어야 한다.In addition, a material having high thermal conductivity is preferable for fast and even heat dissipation, and its application value should be close to 1.3 m 3 / mh ° C. of conventional cement ondol.
이외의 사항으로 조립설치가 간단하고, 규격화, 표준화된 자재를 사용하여야 한다.Otherwise, assembly and installation should be simple and standardized and standardized materials should be used.
상기한 요구조건 성능은 조립식온돌 시공완료 후 요구조건 성능을 만족시키지 못함으로 해서 조립식 온돌의 심각한 하자발생 요인이 되고 있기 때문으로 기존의 판재로는 조립식 온돌용으로 대체시공이 불가능하기 때문이다.This is because the above described requirements performance is not a satisfactory cause of the prefabricated ondol after completion of the prefabricated ondol construction, which is why it is impossible to replace the existing plate for the prefabricated ondol.
본 발명은 종래의 상판을 보완하여 상판으로서 가져야할 요구조건 성능을 만족시키고, 시공시 간편하게 조립할 수 있도록 하는데 주안점을 둔 것이다.The present invention is to supplement the conventional top plate to satisfy the requirements performance to have as a top plate, and to make it easy to assemble during construction.
본 발명은 조립식 온돌분야에서 온돌 마감재로 사용되는 조립식 온돌용 상판 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a prefabricated ondol top plate used as an ondol finishing material in the field of prefabricated ondol.
본 발명은 상기한 목적을 달성하기 위해 조립식 온돌용 판재의 조성물 구성을 무기질의 천연석재 및 인공골재를 주원료로 하며, 이를 구성함에 있어 무기질 규사 또는 무기질 종류의 석재 ø1.5내지2를 21내지22중량 %, ø0.5내지1를 53내지54중량 %, 충진제로 탄산칼슘 20㎛이하의 규격 및 타 무기질 재료 중 20㎛이하의 규격으로 대체 사용할 수 있으며, 15내지16중량%을 배합비율로 하고, 잘 혼합되게 배합한다.In order to achieve the above object, the composition of the prefabricated ondol plate is composed of inorganic natural stone and artificial aggregate as the main raw materials, and the composition of the inorganic silica sand or inorganic type ø1.5 to 2 to 21 to 22 Weight%, ø0.5 to 1 to 53 to 54% by weight, the filler can be used as the standard of calcium carbonate less than 20㎛ and other inorganic materials less than 20㎛, 15 to 16% by weight as the compounding ratio , Mix well.
이때 각 조성물은 함수율 0.2% 이내의 것을 사용하며, 상온을 유지하고 있어야 한다.At this time, each composition is used within the water content of 0.2%, and should be maintained at room temperature.
한편 불포화 폴리에스터 수지 1O내지11중량% 이하, 촉진제 (cobalt octoate)는 수지대비 3중량%, 고온 경화제 (methyl ethyl ketone peroxide) 3중량%를 잘 썩이도록 혼합하여 먼저 배합된 조성물과 같이 혼합하여 조성하고, 한편 가로, 세로의 사각형틀에 이형제(실리콘 또는 스테인산)등을 0.5mm정도 도포 한 후 한지 또는 창호지를 사각의 형틀에 삽입한다.On the other hand, the unsaturated polyester resin 10 to 11% by weight or less, the cobalt octoate is 3% by weight compared to the resin, 3% by weight of the high temperature curing agent (methyl ethyl ketone peroxide) to mix well to mix and mix like a composition blended first On the other hand, a mold release agent (silicone or stearic acid), etc., is applied to the horizontal and vertical rectangular frame about 0.5mm, and then the Korean paper or window paper is inserted into the rectangular frame.
이후 화이바 글라스를 위에 삽입한 다음 배합된 모재를 수평하게 1.2내지1.4cm 의 두께 수평이 되도록 도포한 후 그 위로 화이바 글라스 및 한지 또는 창호지를 차례로 삽입하고 가열된 프레스 내부로 삽입한다.After inserting the fiber glass on the top, then the blended base material is applied horizontally to a thickness of 1.2 to 1.4 cm horizontally, and then the fiber glass and Hanji or window paper are inserted in turn, and then into the heated press.
이때 화이바 글라스는 사각의 형틀에서 움직이지 않도록 수지코팅을 한 것으로 면사의 굵기는 0.13에서0.16mm이내로 사용한다.At this time, the fiberglass is coated with resin so that it does not move in a square mold. The thickness of cotton yarn is used within 0.13 to 0.16mm.
가열된 프레스의 가열온도는 상부130℃ 하부 150℃를 유지하도록 조정하고, 프레스로 가압 한다. 이때 가열시간은 최소 3분30초 이상 가압하며, 가압은 40㎠/kg이상으로 한다.The heating temperature of the heated press is adjusted to maintain the upper 130 ° C lower 150 ° C, and pressurized by the press. At this time, the heating time is pressurized for at least 3 minutes and 30 seconds, and pressurized to 40 cm 2 / kg or more.
상기와 같이 프레스에서 가압이 이루어지게 되면 배합된 모재는 수평 압력 하에서 1cm의 두께로 일정한 틀을 유지하게 되고, 사각의 금형 내부에 있는 모재는 경화제가 혼합되어 있는 상태에서 105℃ 도달시점에서 경화제가 분해되어 기체로 상승하게 되고 모재는 급속하게 경화되어 불포화 폴리에스터 수지의 냄새를 탈취하면서 판재가 금형의 형상에 따라 성형되는 것이다.When pressurization is performed in the press as described above, the blended base material maintains a constant mold with a thickness of 1 cm under horizontal pressure, and the base material in the square mold has a curing agent at 105 ° C. in a state where the curing agent is mixed. It decomposes and rises to the gas, and the base material is rapidly cured to deodorize the smell of the unsaturated polyester resin, and the plate is molded according to the shape of the mold.
상기한 방법은 서로 다른 크기의 무기질 석재가 가장 큰 알갱이를 중심으로 하여 좀 더 작은 알갱이가 주변에 붙여 있게 되고 그 알갱이들은 수지가 알갱이 외부로 고르게 도포 되어 있으며, 알갱이 사이의 공간을 좀더 작은 무기질 충진재가 채워주고 프레스 되는 압력에 의해서 완전히 밀착되어 공간을 채워 주므로서 조직이 형성되는 것이다. 또한 상판의 아래. 위 부분에 압착되어 있는 한지 또는 창호지 와 화이바 글라스는 프레스의 압력에 의해 배합된 주재료와 완전밀착 하게되고, 한지는 형틀과의 이형효과 및 최종마감재의 부착이 용이하도록 설정하였으며, 화이바 글라스는 휨 강도를330kg/㎡을 유지하도록 한 것이다.In the above method, smaller sized grains are attached around the largest grains of inorganic stones of different sizes, and the grains are coated with resin evenly to the outside of the grains. The tissue is formed by completely filling the space by the pressure of filling and pressing. Also down the top. Hanji or window paper and fiberglass glass pressed on the upper part are completely in contact with the main material blended by the pressure of the press.Hanji paper is set to facilitate the release effect and the attachment of the final finisher to the mold. Maintain 330kg / ㎡.
완성된 조립식 온돌용 상판은 상온에서 서서히 식히면서 수평이 유지된 상태에서 보관한다.The finished prefabricated ondol top plate is stored in a horizontal state while slowly cooling at room temperature.
본 발명은 사각의 형틀 내부로 주원료로 무기질 규사 및 세라믹 분사를 불포화 폴리에스터 수지와 혼합 열 경화 시켜서 된 것으로 제품의 크기는 시공편의를 위하여 이동과 설치가 간편하고 설치 시 연결부분을 금형의 형태에 따라 쉽게 성형할 수 있다.The present invention is made by mixing and thermally curing inorganic silica sand and ceramic spraying with unsaturated polyester resin as the main raw materials into a square mold, the size of the product is easy to move and install for convenience of construction, and the connection part in the form of a mold It can be easily molded accordingly.
상기와 같이 본 발명은 조립식 온돌상판을 인공골재 및 무기질로 일체로 성형하여 그 강도가 크고, 무기질 및 난연 유기질의 불연재료의 사용으로 화재에도 연소되지 않으며, 축열성이 50℃에서 15℃ 까지 온도하강 시간이 130분으로 나타나 양호하고 상기한 상판을 사용하게 되면 상판의 두께를 1cm이하로 줄일 수 있어 무게가 가벼워 시공이 원활하고, 성형하면서 연결부위 가공이 가능하여 쫄대를 이용해 수평으로 연속 연결 작업이 가능하여 시공이 간편하게 되고, 온돌 상부에서의 집중 하중을 요구성능 치수 이상인 235kgf 로 나타나 기존의 시멘트 온돌바닥과 같이 단단하고, 열팽창 계수가 0.92x 10-5/℃ 이하로 종래의 시멘트 온돌 보다 낯아 수축팽창에 의한 변형이 작고, 열전도율이 1.24㎉/mh℃로 시멘트 온돌과 유사하게 나타나 쾌적한 온열감 으로 주거생활을 누릴 수 있는 효과가 있는 것이다,As described above, the present invention is integrally molded prefabricated ondol plate with artificial aggregate and inorganic material, and its strength is high. The fall time is 130 minutes, which is good. When the top plate is used, the thickness of the top plate can be reduced to 1 cm or less, so the weight is light, and the construction is smooth. this is possible by a simple construction, and shows a concentrated load at the top to floor heating than required performance dimensions 235kgf hard as conventional cement floor under-floor heating, and a thermal expansion coefficient than that of a conventional cement floor heating natah below 0.92x 10 -5 / ℃ Small deformation due to shrinkage expansion and thermal conductivity is 1.24㎉ / mh ℃, which is similar to cement ondol. It is effective to have a huge life,
Claims (2)