KR19990056855A - Bottom plate of iron - Google Patents

Bottom plate of iron Download PDF

Info

Publication number
KR19990056855A
KR19990056855A KR1019970076874A KR19970076874A KR19990056855A KR 19990056855 A KR19990056855 A KR 19990056855A KR 1019970076874 A KR1019970076874 A KR 1019970076874A KR 19970076874 A KR19970076874 A KR 19970076874A KR 19990056855 A KR19990056855 A KR 19990056855A
Authority
KR
South Korea
Prior art keywords
bottom plate
iron
aluminum oxide
oxide film
teflon
Prior art date
Application number
KR1019970076874A
Other languages
Korean (ko)
Other versions
KR100233423B1 (en
Inventor
서상욱
Original Assignee
정담
주식회사 노비타
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정담, 주식회사 노비타 filed Critical 정담
Priority to KR1019970076874A priority Critical patent/KR100233423B1/en
Publication of KR19990056855A publication Critical patent/KR19990056855A/en
Application granted granted Critical
Publication of KR100233423B1 publication Critical patent/KR100233423B1/en

Abstract

본 발명은 전기 다리미에 관한 것으로, 더욱 상세하게는 미끄럼성이 향상된 다리미 바닥판의 표면 구조에 관한 것이다.The present invention relates to an electric iron, and more particularly, to the surface structure of the iron bottom plate with improved sliding properties.

본 발명에 따른 다리미는 바닥판의 표면에 1차로 양극산화처리를 통해 산화알루미늄 피막을 형성한 후, 2차로 상기 산화알루미늄 피막에 마찰저항이 적은 테프론을 코팅하였다. 따라서, 다리미 바닥판의 내식성, 내마멸성, 경도가 개선될 뿐만 아니라, 고온에 안정되며 마찰저항이 적은 테프론이 코팅됨에 따라 바닥판의 미끄럼성이 크게 향상되는 이점이 있다.The iron according to the present invention first formed an aluminum oxide film through anodizing on the surface of the bottom plate, and secondly coated Teflon with low frictional resistance on the aluminum oxide film. Therefore, the corrosion resistance, abrasion resistance, and hardness of the iron sole plate are not only improved, but there is an advantage that the sliding property of the sole plate is greatly improved as Teflon is coated at a high temperature and has low frictional resistance.

Description

다리미의 바닥판Bottom plate of iron

본 발명은 다리미에 관한 것으로, 더욱 상세하게는 미끄럼성이 향상된 다리미 바닥판의 표면 구조에 관한 것이다.The present invention relates to an iron, and more particularly to the surface structure of the iron bottom plate with improved slipperiness.

전기 다리미는 전기적인 발열수단으로 바닥판을 가열하여, 이 바닥판으로 옷감의 구김이나 주름을 펴는 전기기구이다.An electric iron is an electric appliance that heats a bottom plate by an electric heating means and spreads wrinkles or wrinkles on the cloth by the bottom plate.

이러한 전기 다리미는 본체의 하측에 열전도성이 높은 금속재질의 열판이 마련되어 있고, 이 열판에는 전원을 인가 받아 발열하는 열선이 설치되어 있다. 그리고 상기 열판의 하측에는 상기 열판의 열을 전달받을 수 있도록 열판과 인접되게 설치되며, 바닥면이 평면으로 구성된 바닥판이 마련되어 있다.The electric iron is provided with a high thermal conductive metal hot plate at the lower side of the main body, and a hot wire is provided on the hot plate to generate heat by applying power. In addition, the bottom plate of the hot plate is installed adjacent to the hot plate to receive the heat of the hot plate, the bottom surface is provided with a bottom plate consisting of a flat.

또한, 상기 본체의 외측에는 다리미의 온도와 기능을 조절하는 조절기와, 다리미에 외부의 전원이 인가하는 전원코드 등이 마련되어 있다.In addition, the outside of the main body is provided with a regulator for adjusting the temperature and function of the iron, and a power cord for applying external power to the iron.

이와 같은 구조로 이루어진 다리미는 전원코드를 통해 전원이 인가되면, 상기 열선에 의해 열판이 가열되게 되고, 열판의 열은 다시 다리미의 바닥판으로 전달되게 된다. 이때 사용자는 가열된 다리미의 바닥판을 옷감의 주름부분이나 구김부에 문질러 줌으로써 주름이나 구김을 펼수 있게 된다.When the iron having such a structure is applied with power through a power cord, the hot plate is heated by the hot wire, and the heat of the hot plate is transferred to the bottom plate of the iron again. At this time, the user can spread the wrinkles or wrinkles by rubbing the bottom plate of the heated iron on the wrinkles or wrinkles of the cloth.

그런데 이러한 다리미는 상기 바닥판의 재질이 알루미늄으로 마련됨에 따라, 이 알루미늄 바닥판이 다림질을 하는 과정에서 옷감에 마찰되어 마모되거나, 또는 사용자의 부주의에 의해 거친부분에 접촉되어 흠집이 발생되는 것을 고려하여, 바닥판이 소정의 강도를 가지도록 하여왔다.By the way, the iron is made of aluminum as the bottom plate is made of aluminum, in consideration of the fact that the aluminum bottom plate is rubbed by the cloth in the process of ironing, wear, or contact with the rough part by the carelessness of the user to generate scratches The bottom plate has been made to have a predetermined strength.

이러한 방법으로는 주로 양극산화법(Anodizing)을 이용되었는데, 이 양극산화법은 전해액 속에 담긴 알루미늄 물품을 양극으로 하여 통전시키게 되면, 알루미늄 면이 산화되어 산화알루미늄(Al₂O₃)의 피막이 생성되게 된다. 이 산화알루미늄 피막은 경도가 우수하고 내식성이 우수한 장점이 있다.Anodizing is mainly used for this method. When anodizing is conducted by using an aluminum article contained in an electrolyte as an anode, an aluminum surface is oxidized to form a film of aluminum oxide (Al₂O₃). This aluminum oxide film has the advantages of excellent hardness and excellent corrosion resistance.

그러나 이러한 표면처리 방법은 경도와 내식성이 우수한 장점이 있지만 옷감의 다림질을 용이하게 하는 미끄럼성을 개선시키는데에는 한계가 있었다.However, the surface treatment method has an advantage in that hardness and corrosion resistance are excellent, but there is a limit in improving slipperiness that facilitates ironing of the cloth.

본 발명은 이상과 같은 점을 고려하여 안출된 것으로, 본 발명의 목적은 다리미 바닥판의 표면처리 방법을 개선하여, 경도와 내식성 뿐만아니라, 미끄럼성이 향상되어 다림질을 용이하게 하는 다리미의 바닥판을 제공하는 것이다.The present invention has been made in view of the above, the object of the present invention is to improve the surface treatment method of the iron bottom plate, as well as hardness and corrosion resistance, slippery improved iron plate to facilitate ironing To provide.

도 1은 본 발명에 따른 다리미의 전체적인 외형을 보인 사시도이다.1 is a perspective view showing the overall appearance of the iron according to the present invention.

도 2는 본 발명에 따른 다리미 바닥판에 형성된 산화알루미늄 피막의 구조를 보인 도면이다.2 is a view showing the structure of the aluminum oxide film formed on the iron bottom plate according to the present invention.

도 3은 본 발명에 따른 다리미 바닥판에 형성된 산화알루미늄 피막에 테프론이 함침된 상태를 보인 도면이다.3 is a view showing a state in which Teflon is impregnated in the aluminum oxide film formed on the iron bottom plate according to the present invention.

* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10: 본체, 11: 손잡이,10: body, 11: handle,

12: 열판, 13: 열선,12: hotplate, 13: heating wire,

14: 바닥판, 15: 조절기,14: bottom plate, 15: adjuster,

16: 전원코드, 20: 산화알루미늄 피막,16: power cord, 20: aluminum oxide film,

21: 활성층, 22: 유공층,21: active layer, 22: porous layer,

23: 핀홀, 24: 테프론.23: pinhole, 24: teflon.

상기의 목적을 달성하기 위한 본 발명은, 그 표면이 양극산화처리 된 바닥판을 구비하는 다리미에 있어서,The present invention for achieving the above object, in the iron provided with a bottom plate whose surface is anodized,

상기 바닥판의 미끄럼성이 향상되도록, 상기 양극산화처리를 통해 형성된 산화알루미늄 피막의 핀홀에 테프론이 함침된 것을 특징으로 한다.Teflon is impregnated into the pinhole of the aluminum oxide film formed through the anodization treatment so as to improve the sliding property of the bottom plate.

이하에서는 본 발명의 바람직한 실시 예를 첨부도면을 참조하여 설명한다.Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings.

본 발명에 따른 다리미는 도 1에 도시된 바와 같이, 사용자가 다리미를 움직일 수 있도록 손잡이(11)가 일체로 형성되고 선단부가 유선형으로 마련된 본체(10)가 구비되고, 상기 본체(10)의 하측에는 열전도성이 높은 금속재질의 열판(12)이 마련되는데, 이 열판(12)에는 전원을 인가 받아 발열하는 열선(13)이 설치된다. 그리고 상기 열판(12)의 하측에는 상기 열판(12)의 열을 전달받을 수 있도록 열판(12)과 인접되게 설치되며, 옷감의 주름을 펼 수 있도록 바닥면이 평면으로 구성된 바닥판(14)이 마련된다. 이때 상기 바닥판(14)은 상기 본체(10)와 마찬가지로 바닥면의 형상이 유선형으로 형성된다.As shown in FIG. 1, the iron according to the present invention includes a main body 10 having a handle 11 integrally formed and a streamlined end portion provided to allow a user to move the iron, and a lower side of the main body 10. The metal plate is provided with a high thermal conductivity metal plate 12, the heat plate 12 is provided with a heating wire 13 for generating heat by applying power. The bottom plate 14 is installed below the hot plate 12 so as to be adjacent to the hot plate 12 so as to receive heat from the hot plate 12, and the bottom plate 14 has a flat bottom surface to spread wrinkles of the cloth. Prepared. At this time, the bottom plate 14 is formed in a streamlined shape like the main body 10.

또한, 상기 본체(10)의 외측에는 다리미의 온도와 기능을 조절하는 조절기(15)와, 다리미에 외부의 전원이 인가하는 전원코드(16) 등이 마련된다.In addition, the outer side of the main body 10 is provided with a regulator 15 for adjusting the temperature and function of the iron, and a power cord 16 for applying external power to the iron.

이와 같은 구조로 이루어진 다리미는 전원코드(16)를 통해 전원이 인가되면, 상기 열선(13)에 의해 열판(12)이 가열되게 되고, 열판(12)의 열은 다시 다리미의 바닥판(14)으로 전달되게 된다. 이때 사용자는 가열된 다리미의 바닥판(14)을 옷감의 주름부분이나 구김부에 문질러 줌으로써 주름이나 구김을 펼수 있게 된다.When the iron having such a structure is applied with power through the power cord 16, the hot plate 12 is heated by the heating wire 13, and the heat of the hot plate 12 is again the bottom plate 14 of the iron. To be delivered. At this time, the user can spread the wrinkles or wrinkles by rubbing the bottom plate 14 of the heated iron on the wrinkles or wrinkles of the cloth.

한편, 본 발명에 따른 다리미의 바닥판(14)은 재질이 가볍고 열전도율이 우수한 알루미늄으로 마련된다. 그런데 이 알루미늄 바닥판(14)은 재질의 특성이 연질로 구비됨에 따라 다림질을 하는 과정에서 옷감에 마찰되어 마모되거나, 또는 사용자의 부주의에 의해 거친부분에 접촉되어 흠집이 발생될 우려가 있다.On the other hand, the bottom plate 14 of the iron according to the present invention is made of aluminum, which is light in material and excellent in thermal conductivity. However, as the aluminum bottom plate 14 is provided with soft material properties, the aluminum bottom plate 14 may be worn by friction with the cloth during ironing, or may be damaged by contact with rough parts due to carelessness of the user.

이러한 문제를 고려하여 본 발명에 따른 다리미는 상기 바닥판(14)의 표면 경도와 내식성을 높이기 위해 바닥판(14)의 표면에 양극산화법(Anodizing)을 이용한 표면처리를 하게 된다. 그리고, 본 발명에 특징적인 요소로 상기 바닥판(14)의 미끄럼성을 향상시키기 위해 양극산화처리된 표면에 테프론(불소수지)이 코팅되게 된다.In consideration of these problems, the iron according to the present invention is subjected to surface treatment using anodizing on the surface of the bottom plate 14 to increase the surface hardness and corrosion resistance of the bottom plate 14. In addition, Teflon (fluorine resin) is coated on the anodized surface to improve the sliding property of the bottom plate 14 as a characteristic element of the present invention.

이러한 다리미 바닥판(14)의 표면처리 방법을 도 2와 도 3을 참조하여 순서적으로 설명한다.The surface treatment method of the iron bottom plate 14 will be described in order with reference to FIGS. 2 and 3.

양극산화법은 알루미늄으로 성형된 상기 바닥판(14)을 전해액속에 담근 상태에서, 상기 바닥판(14)을 양극으로 하고, 통전시키게 되면 바닥판(14)의 표면에 얇은 산화알루미늄 활성층(21)이 형성되게 된다. 이 때 전압이 충분히 크면 전해액에 의한 침식 작용과 더불어 이 얇은 활성층(21)이 파괴되면서 상당한 양의 열이 발생되고, 이 열은 전해액에 의한 침식 작용을 더욱 증대시켜 주어 활성층(21)의 표면은 다공성의 피막으로 구성된 유공층(22)이 형성되게 된다. 즉, 유공층(22)에는 정육각형 격자의 중심부에 별모양의 핀홀(23)이 형성되게 된다.In the anodizing method, when the bottom plate 14 formed of aluminum is immersed in an electrolyte, the bottom plate 14 is used as an anode, and when the current is energized, a thin aluminum oxide active layer 21 is formed on the surface of the bottom plate 14. Will be formed. At this time, if the voltage is large enough, a considerable amount of heat is generated as the thin active layer 21 is destroyed along with the erosion effect by the electrolyte solution, and this heat further increases the erosion effect by the electrolyte solution. The porous layer 22 composed of a porous film is formed. That is, in the hole layer 22, a star-shaped pinhole 23 is formed in the center of the regular hexagonal lattice.

또한, 이 때 발생된 산소는 유공층(22) 내측의 알루미늄을 산화시켜 새로운 활성층(21)을 생성시키게 되고, 이와 같은 과정이 반복되어 산화알루미늄 피막(20)은 내측으로 성장되게 된다. 즉, 산화알루미늄 피막(20)은 표면부분에 핀홀(23)이 형성된 유공층(22)이 형성되고, 유공층의 하측이 활성층(21)으로 구성되게 된다.In addition, the oxygen generated at this time oxidizes the aluminum inside the pore layer 22 to generate a new active layer 21, and this process is repeated, so that the aluminum oxide film 20 is grown inward. That is, the aluminum oxide film 20 is formed with a hole layer 22 having a pinhole 23 formed on its surface portion, and the lower side of the hole layer is composed of the active layer 21.

이러한 과정을 통하여 형성된 산화알루미늄 피막(20)은 다리미 바닥판(14)의 내식성, 내마멸성, 표면경도를 향상시킬 뿐만 아니라 미려한 외관을 제공하게 된다.The aluminum oxide film 20 formed through this process not only improves the corrosion resistance, abrasion resistance, and surface hardness of the iron bottom plate 14, but also provides a beautiful appearance.

또한, 본 발명에 따른 다리미의 바닥판(14)은 상기 양극산화처리가 완료되면 상기 유공층(22)의 핀홀(23)분분에 액상의 테프론(24)을 함침시키게 된다.In addition, the bottom plate 14 of the iron according to the present invention impregnates the liquid teflon 24 in the pinhole 23 portion of the pore layer 22 when the anodizing treatment is completed.

이 테프론(24)은 화학약품에 대한 내구력 및 전기적성질이 뛰어날 뿐만 아니라 325℃ 내외의 고온에서도 안정되고, 마찰계수가 대단히 적은 특징이 있다. 본 발명에서는 이러한 테프론(24)의 고온 안정성과 마찰계수가 적은 특징이 다리미의 바닥판(14) 표면처리에 이용된 것이다.The Teflon 24 is not only excellent in durability and electrical properties for chemicals, but also stable at high temperatures around 325 ° C, and has a very low coefficient of friction. In the present invention, the high temperature stability and the low coefficient of friction of the Teflon 24 are used to treat the bottom plate 14 of the iron.

이러한 테프론(24) 코팅은 상술한 바와 같이 액상의 테프론에 상기 바닥판(14)을 함침시킴으로써 산화알루미늄 피막의 핀홀(23)에 테프론(24)이 유입되어 고착되게 하는 방법과, 스프레이 등을 이용하여 산화알루미늄 피막(20)에 테프론을 코팅하는 등 다양한 방법이 적용될 수 있다.As described above, the Teflon 24 coating is a method in which the Teflon 24 is introduced into the pinhole 23 of the aluminum oxide film and fixed by impregnating the bottom plate 14 in the liquid Teflon as described above. Thus, various methods such as coating Teflon on the aluminum oxide film 20 may be applied.

이처럼 본 발명에 따른 다리미의 바닥판(14)은 1차로 양극산화처리를 통해 산화알루미늄 피막(20)을 형성한 후, 2차로 상기 산화알루미늄 피막(20)에 마찰저항이 적은 테프론(24)을 코팅함으로써, 바닥판(14)의 표면이 내식성, 내마멸성, 경도가 개선될 뿐만 아니라, 미끄럼성이 향상되게 된다.As described above, the bottom plate 14 of the iron according to the present invention first forms an aluminum oxide film 20 through anodizing, and secondly, a teflon 24 having low frictional resistance is applied to the aluminum oxide film 20. By coating, the surface of the bottom plate 14 is not only improved in corrosion resistance, abrasion resistance, and hardness, but also in slipperiness.

즉, 다리미의 바닥판(14)은 산화아루미늄 피막(20)에 형성된 핀홀(23)에 테프론(24)이 함침되어 고착됨으로써, 미끄럼성이 크게 향상되게 되고, 이러한 테프론(24)은 고온에서도 안정된 상태를 유지하므로 장기간 사용을 하더라고 그 특성이 오래 유지되게 된다.That is, the bottom plate 14 of the iron is impregnated with the Teflon 24 in the pinhole 23 formed in the aluminum oxide film 20, so that the sliding property is greatly improved, and the Teflon 24 is improved even at a high temperature. Since it maintains a stable state, its characteristics are maintained for a long time even after long-term use.

이상에서 상세히 설명한 바와 같이, 본 발명에 따른 다리미는 바닥판의 표면에 1차로 양극산화처리를 통해 산화알루미늄 피막을 형성한 후, 2차로 상기 산화알루미늄 피막에 마찰저항이 적은 테프론을 코팅하였다. 따라서, 다리미 바닥판의 내식성, 내마멸성, 경도가 개선될 뿐만 아니라, 고온에 안정되며 마찰저항이 적은 테프론이 코팅됨에 따라 바닥판의 미끄럼성이 크게 향상되는 이점이 있다.As described above in detail, the iron according to the present invention first formed an aluminum oxide film on the surface of the bottom plate through anodizing, and then coated teflon with a low friction resistance on the aluminum oxide film. Therefore, the corrosion resistance, abrasion resistance, and hardness of the iron sole plate are not only improved, but there is an advantage that the sliding property of the sole plate is greatly improved as Teflon is coated at a high temperature and has low frictional resistance.

Claims (2)

그 표면이 양극산화처리 된 바닥판을 구비하는 다리미에 있어서,In the iron having a bottom plate whose surface is anodized, 상기 바닥판의 미끄럼성이 향상되도록, 상기 양극산화처리를 통해 형성된 산화알루미늄 피막의 핀홀에 테프론이 함침된 것을 특징으로 하는 다리미의 바닥판.Teflon is impregnated into the pinhole of the aluminum oxide film formed through the anodization treatment, so that the slipperiness of the bottom plate is improved. 다리미 바닥판의 표면에 양극산화처리를 하여 산화알루미늄 피막을 형성시키는 단계와,Anodizing the surface of the iron sole plate to form an aluminum oxide film, 상기 산화알루미늄 피막이 형성된 상기 바닥판을 액상의 테프론에 함침시켜 상기 산화알루미늄 피막에 형성된 핀홀에 상기 테프론을 유입시키는 단계를 포함하는 다리미의 바닥판 표면처리 방법.And impregnating the bottom plate having the aluminum oxide film with a liquid teflon to introduce the teflon into a pinhole formed in the aluminum oxide film.
KR1019970076874A 1997-12-29 1997-12-29 Bottom plate of iron KR100233423B1 (en)