KR19990039262A - Ocher wallpaper and its manufacturing method - Google Patents
Ocher wallpaper and its manufacturing method Download PDFInfo
- Publication number
- KR19990039262A KR19990039262A KR1019970059293A KR19970059293A KR19990039262A KR 19990039262 A KR19990039262 A KR 19990039262A KR 1019970059293 A KR1019970059293 A KR 1019970059293A KR 19970059293 A KR19970059293 A KR 19970059293A KR 19990039262 A KR19990039262 A KR 19990039262A
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- wallpaper
- coated
- paper
- loess
- Prior art date
Abstract
본 발명은 황토벽지 및 그 제조방법에 관한 것으로서, 여러 가지의 화학약품이 혼합된 수지를 벽지의 원지 표면에 코팅시키고, 이 표면에 인쇄를 하여 실크(Silk)벽지를 구성함에 따라 화학약품의 수지에 포르말레이드의 유해성분이 많이 포함되어 인체에 해를 끼치고, 수지재에 의해 습도조절기능을 갖지 못하여 벽지의 손상 발생과 발포재에 의해 발생되는 냄새로 쾌적한 환경을 유지시키지 못하였으며, 벽지의 품질을 저하시키는 문제점이 있었다.The present invention relates to a loess wallpaper and a method of manufacturing the same, wherein a resin mixed with various chemicals is coated on a wallpaper surface and a silk wallpaper is formed by printing on the wallpaper, The harmful component of formaldehyde is contained a lot and harmful to the human body, the humidity control function is not provided by the resin material, the wallpaper is damaged and the smell generated by the foam material does not maintain a pleasant environment, .
본 발명은 벽지의 원지 표면에 코팅되는 수지에 황토를 배합시켜 코팅시킴에 따라 황토성분에 의해 습도조절이 용이하고, 탈취기능에 따른 냄새의 제거가 용이하며, 바이오 및 원적외선의 발생으로 인체의 활력을 증대시키며, 벽지의 원가절감 및 품질의 고급화와 신뢰도를 높일 수 있는 효과가 있다.According to the present invention, it is possible to easily control the humidity by the loess component and to remove the odor due to the deodorizing function as the loess is mixed with the resin coated on the wallpaper surface of the paper, and the bio- And it has the effect of reducing the cost of wallpaper and enhancing the quality and reliability of the quality.
Description
본 발명은 황토벽지 및 그 제조방법에 관한 것으로서, 특히 여러 가지의 화학약품이 혼합된 수지에 황토를 배합시켜 벽지의 원지에 코팅되도록 함에 따라 습도조절과 냄새제거와 바이오 및 원적외선의 발생으로 인체의 활력을 증대와 벽지의 품질고급화를 높일 수 있는 벽지를 제조하는 황토벽지 및 그 제조방법에 관한 것이다.More particularly, the present invention relates to a method for producing a green clay wallpaper and a method for producing the clay wallpaper. The green clay wall is coated with a resin mixed with various chemicals to coat the wallpaper with wallpaper, thereby controlling moisture, deodorizing, The present invention relates to a loess wallpaper for manufacturing a wallpaper capable of enhancing the vitality and enhancing the quality of wallpaper, and a manufacturing method thereof.
일반적으로 벽지에는 미적인 효과를 높이고, 품질의 고급화를 꾀하기 위해 여러 가지의 화학약품이 배합된 합성수지재료(이하 수지(樹脂)라고 한다)를 벽지의 원지(종이)의 표면에 도포시킨 후 이 표면에 여러 가지의 도형이나 그림을 인쇄하여 벽지를 제조한다.In general, in order to enhance the aesthetic effect of the wallpaper and to enhance the quality, a synthetic resin material (hereinafter referred to as "resin") containing various chemicals is applied to the surface of wallpaper paper (paper) The wallpaper is produced by printing various figures or pictures.
이와같은 종래의 벽지(10)를 제조하기 위한 과정을 설명하면 도 3에서 보는바와 같이 두루마리상태로 공급된 코팅단계에서 원지(20)의 표면에 액체상태의 수지(30)를 도포함으로서 수지코팅된 벽지를 얻게 되는데, 먼저 혼합단계에서 원료수지(LP090과 PB1120) 180㎏을 기준으로 가소재(DOP: Dioctyl Phthalate) 135∼140㎏과, 점도저하제 (VS-2025: Viscosity) 4㎏과, 2차가소재(DOP: Di Odorless Pliasticizer) 20㎏과, 안정제(BZ-806P: Barium- Zinc) 6㎏과, 지당(Titanium Dioxide) 30㎏과, 경탄(돌가루) 90㎏과, 발포제를 3.6㎏과, 산화아연(ZnO) 7.2㎏을 배합시켜 각 재료가 죽(Sol)상태가 되도록 고르게 혼합된 액상수지를 얻는다.3, a liquid resin 30 is coated on the surface of the paper 20 in a coating step supplied in a roll state to form a resin-coated (DOP: Dioctyl Phthalate), 4 kg of a viscosity reducing agent (VS-2025: Viscosity), and 2 kg of a viscosity reducing agent (Viscosity) were weighed based on 180 kg of the raw resin (LP090 and PB1120) 20 kg of a material (DOP: Di Odorless Pliasticizer), 6 kg of stabilizer (BZ-806P: Barium-Zinc), 30 kg of titanium dioxide, 90 kg of astringent (stone powder), 3.6 kg of foaming agent, And 7.2 kg of zinc oxide (ZnO) were mixed to obtain a liquid resin uniformly mixed so that each material was in a sol state.
혼합단꼐에서 배합이 완료된 액상수지를 믹싱단계에서 소정시간동안 믹싱작업으로 각 재료의 입자를 고르게 유지시킨다.In the mixing step, the liquid resin having been compounded in the mixing step is uniformly kept in the respective materials by a mixing operation for a predetermined time.
이렇게 믹싱된 액상수지를 코팅단계에서 별도 공듭된 원지(20)의 표면에 0.02㎜의 두께로 코팅층이 형성되도록 도포시킨다.The liquid resin thus mixed is applied to the surface of the raw paper 20, which is separately prepared in the coating step, so as to form a coating layer with a thickness of 0.02 mm.
도포가 완료되면 건조 및 인쇄단계에서 220℃의 열이 발생되는 건조기를 이용하여 1분당 40m의 속도로 이송되는 원지(20)의 표면에 코팅된 액상수지를 건조시켜 응고되게 한다.When the application is completed, the liquid resin coated on the surface of the raw paper 20, which is fed at a speed of 40 m per minute, is dried by using a drier which generates heat at 220 ° C in the drying and printing steps to coagulate.
건조기에 의해 응고된 수지(30)는 쿨링기에서 강제로 냉각건조되게 하여 경화시킨다.The resin 30 solidified by the dryer is forced to cool and dry in a cooling machine to be cured.
수지(30)가 경화된 원지(20)는 인쇄기로 공급되어 여러 가지의 도형과 그림이 수지(30)의 표면에 인쇄되도록 한다.The raw paper 20 on which the resin 30 is cured is supplied to a printing machine so that various figures and figures are printed on the surface of the resin 30. [
이렇게 건조 및 인쇄단계가 완료되면 가열단계에서 220℃의 온도로 열을 가하여 코팅된 수지(30)가 1∼2㎜정도의 두께를 갖도록 발포시킨다.When the drying and printing steps are completed, heat is applied at a temperature of 220 DEG C in the heating step, and the coated resin 30 is foamed to have a thickness of about 1 to 2 mm.
가열단계를 거친 원지(20)는 형압공정으로 공급되어 수지(30)를 가압시키는 가압롤러의 의해 여러가지형태로 엠보싱이 형성되도록 한다.The raw paper 20 that has undergone the heating step is supplied to a stamping process so that the embossing can be formed in various forms by the pressure roller which presses the resin 30.
수지(30)에 엠보싱의 형성이 완료된 원지(20)는 절단공정에서 1차절단기에 의해 양단을 절단시킨 후 2차절단기에 의해 두루마리로 권취되는 벽지(10)를 적정한 길이로 절단시킨 후 포장단계를 거쳐 출하될 수 있게 한 것이다.After the embossing is completed in the resin 30, both sides of the embossed paper 20 are cut by a primary cutter in the cutting step, the wallpaper 10 wound in a roll by the secondary cutter is cut to an appropriate length, To be shipped through.
이러한 제조과정을 거쳐 완성된 벽지(10)는 도 4에 도시하였으며, 이 벽지(10)의 구성은 원지(20)의 표면에 엠보싱이 형성된 수지(30)가 코팅되어 있고, 이 수지(30)의 표면에는 여러 가지의 도형과 그림이 인쇄되어 있다.4 shows the wallpaper 10. The wallpaper 10 is coated with a resin 30 having an embossed surface formed on the surface of the base paper 20, There are various figures and figures printed on the surface of.
그러나 상기한 벽지(10)는 여러 가지의 화학약품이 혼합된 수지(30)를 원지(20)의 표면에 코팅시키고, 이 수지(30)의 표면에 인쇄를 하여 일반적으로 알고 있는 실크(Silk)벽지를 구성하고 있음에 따라 외관과 기능성을 갖춘 벽지(10)의 고급화를 요구하는 소비자의 욕구 충족을 실현시키기 어려웠다.However, in the wallpaper 10, the resin 30 mixed with various chemicals is coated on the surface of the paper 20, and printing is performed on the surface of the resin 30 to form a generally known silk. It has been difficult to realize the desire of the consumer to demand the upgrading of the wallpaper 10 having the appearance and the function according to the constitution of the wallpaper.
또한 여러 가지의 화학약품으로 배합된 수지(30)에는 포르말레이드의 유해성분이 포함되어 있고, 이 성분을 KS규격에서는 2㎎/㎡이하로 유지되도록 규제하고 있다.Resins (30) formulated with various chemicals also contain harmful components of formaldehyde, which are regulated to be 2 mg / m2 or less in the KS standard.
그러나 상기 포르말레이드성분은 수지벽지에서 2㎎/㎡이상을 포함하고 있는 확률이 크므로 유해성분의 저감을 실현시키기에는 많은 어려움이 있었다.However, since the formaldehyde component has a high probability of containing 2 mg / m < 2 > or more in resin wallpaper, it has been difficult to realize the reduction of harmful components.
또한 수지(30)재에 의해 코팅된 벽지(10)는 통기성과 습도조절기능을 갖지 못하여 벽지(10)에 습기가 발생되고, 이로 인해 곰팡이와 불순물의 발생으로 벽지의 손상을 발생시켰다.In addition, the wallpaper 10 coated with the resin 30 does not have a breathability and a humidity control function, and moisture is generated in the wallpaper 10, thereby causing damage to the wallpaper due to the generation of mold and impurities.
그리고 수지(30)에 포함되어 있는 발포재에 의해 화학약품의 냄새 발생으로 쾌적한 환경을 유지시키지 못하였고, 수지(30)가 비중이 높고 가격이 비싼 화학약품으로 구성되어 있어 벽지(10)의 무게중량의 증대로 운송 및 사용취급성이 용이하지 못하는 동시에 원가절감을 기할 수 없는 문제점이 있었다.And the resin 30 contained in the resin 30 can not maintain a comfortable environment due to the smell of the chemical agent. The resin 30 is composed of a chemical having a high specific gravity and a high price, There is a problem that transportation and use handling are not easy due to an increase in weight and cost can not be reduced.
본 발명은 상기와 같은 종래의 문제점을 해결하기 위하여 발명한 것으로서, 벽지의 원지 표면에 코팅되는 수지에 황토를 배합시켜 코팅시킴에 따라 벽지의 고급화와 품질을 높일 수 있게 한 것을 목적으로 한다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made to solve the above-mentioned problems occurring in the prior art, and it is an object of the present invention to improve the quality and quality of wallpaper by blending yellow loess with a resin coated on a wallpaper surface.
도 1은 본 발명의 벽지를 제조하기 위한 공정도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a process diagram for producing wallpaper of the present invention. FIG.
도 2는 본 발명에 의해 제조된 벽지의 단면도.2 is a sectional view of a wallpaper produced by the present invention.
도 3는 종래의 벽지를 제조하기 위한 공정도.3 is a process diagram for manufacturing a conventional wallpaper.
도 4는 종래의 벽지 단면도.4 is a sectional view of a conventional wallpaper.
(도면의 주요 부분에 대한 부호설명)(Reference Numerals for Main Parts of the Drawings)
10 ; 벽지 20 ; 원지10; Wallpaper 20; Origin
30 ; 수지 40 ; 황토30; Resin 40; ocher
이하 본 발명의 구성을 상세히 설명하면 다음과 같다.Hereinafter, the configuration of the present invention will be described in detail.
원지(20)의 공급에 따른 표면에 액상수지를 코팅시키는 코팅단계와:A coating step of coating a liquid resin on a surface of the base paper 20 according to the supply of the base paper 20;
상기 코팅단계에서 액상수지를 코팅하기 위해 여러 가지의 화학약품중 원료수지 180㎏을 기준으로 수분이 80%이상 탈취된 황토분말을 18∼22%정도 혼합시키고 혼합된 액상수지의 입자를 균일하게 유지시키는 혼합단계와;In order to coat the liquid resin in the coating step, 18% to 22% of the loess powder, which is deodorized by 80% or more of water, is mixed with 180 kg of the raw resin among various chemicals and the particles of the mixed liquid resin are uniformly maintained ;
상기 코팅단계이후에 원지(20)에 코팅된 액상수지를 건조시켜 응고된 수지(30)의 표면에 인쇄하는 건조 및 인쇄단계와;A drying and printing step of drying the liquid resin coated on the paper stock (20) after the coating step and printing on the surface of the solidified resin (30);
상기 건조 및 인쇄단계를 거친 원지(20)에 코팅된 액상수지를 발포시킬 수 있도록 240∼270℃정도의 온도로 가열시키는 가열단계와;A heating step of heating the coated paper 20 to a temperature of about 240 to 270 DEG C so that the liquid resin coated on the paper 20 after the drying and printing step can be foamed;
상기 가열단계를 거친 원지(20)의 수지(30)에 엠보싱을 형성하기 위한 형압단계와;A pressing step of forming an embossing on the resin (30) of the paper (20) through the heating step;
형압단계를 거친 원지(20)의 양단과 길이방향을 절단에 의해 벽지(10)가 완성되도록 하는 절단단계와:A cutting step of cutting the both ends of the raw paper 20 having been subjected to the pressing step and the longitudinal direction thereof to complete the wallpaper 10;
를 포함하는 것이다..
이와같이 된 본 발명의 일 실시예를 첨부도면에 의하여 상세히 설명하면 다음과 같다.BRIEF DESCRIPTION OF THE DRAWINGS The above and other objects, features and advantages of the present invention will be more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which: FIG.
도 1에서 보는바와 같이 벽지(10)를 제조하기 위해 코팅단계로 공급되는 두루마리상태의 원지(20)의 표면에 액상수지를 도포한다.As shown in Fig. 1, a liquid resin is applied to the surface of the rolled paper 20 fed to the coating step for producing the wallpaper 10. Fig.
상기한 액상수지는 원지(20)의 표면에 코팅하는 코팅단계전에 혼합단계에서 원료수지(LP090과 PB1120) 180㎏을 기준으로 18%∼22%정도의 황토분말을 36±3㎏정도 혼합시켜 216±3㎏정도 되도록 한다.킨다.The liquid resin may be prepared by mixing about 36 ~ 3 kg of loess powder of about 18% to 22% with respect to 180 kg of the raw resin (LP090 and PB1120) in the mixing step before coating step of coating on the surface of the raw paper 20 Let it be about 3 kg.
상기한 황토분말은 황토를 채취하여 120∼130(mash)의 그물망으로 순수황토만을 선별하여 수분이 80% 이상 탈수되도록 하고, 3단밀(Mill)을 이용하여 황토입자를 고르게 분쇄시킨다.The above-mentioned loess powder is sampled from 120 to 130 (mash) net of pure yellow ocher, so that water is dehydrated by 80% or more, and the loess particles are evenly pulverized using a 3-mill.
상기 황토분말이 혼합된 재료에는 가소재(DOP: Dioctyl Phthalate)를 135∼140㎏과, 점도저하제 (VS-2025:Viscosity) 4㎏과, 2차가소재(DOP: Di Odorless Pliasticizer) 20㎏과, 안정제(BZ-806P: Barium- Zinc) 6㎏과, 지당(Titanium Dioxide) 30㎏과, 경탄(돌가루) 90㎏과, 발포제 3.6㎏과, 산화아연(ZnO) 7.2㎏을 배합시켜 각 재료가 죽(Sol)상태가 되도록 대기압상태의 상온에서 고르게 혼합시킨다.The material in which the loess powder is mixed includes 135 to 140 kg of DOP (Dioctyl Phthalate), 4 kg of a viscosity reducing agent (VS-2025; Viscosity), 20 kg of a DOP (Di Odorless Pliasticizer) 6 kg of stabilizer (BZ-806P: Barium-Zinc), 30 kg of titanium dioxide, 90 kg of astringent (stone powder), 3.6 kg of foaming agent and 7.2 kg of zinc oxide And mixed evenly at room temperature under atmospheric pressure so as to be in a sol state.
상기 황토의 수분은 80%이상을 탈취시켜 화학약품과의 혼합이 용이하게 이루어지게 한다.The water content of the loess is deodorized by 80% or more so that mixing with the chemical is easy.
황토분말이 혼합되어 배합이 완료된 액상수지는 혼합단계의 믹싱기에 구비된 마찰롤러에 의해 소정시간동안 믹싱작업으로 각 재료의 입자를 고르게 유지시킨다.The liquid resin in which the loess powder is mixed and the mixture is completed, the particles of each material are uniformly maintained by the mixing operation for a predetermined time by the friction roller provided in the mixing device of the mixing step.
이렇게 믹싱된 액상수지는 코팅단계에서 원지(20)의 표면에 0.02㎜의 두께로 코팅층이 형성되도록 도포시킨다.The liquid resin thus mixed is applied to the surface of the base paper 20 in a coating step so as to form a coating layer with a thickness of 0.02 mm.
액상수지의 도포가 완료되면 건조 및 인쇄단계에서 220℃의 열이 발생되는 건조기를 이용하여 1분당 40m의 속도로 이송되는 원지(20)의 표면에 코팅된 액상수지의 건조에 따라 응고되어 코팅층이 형성되는 수지(30)를 형성한다.When the application of the liquid resin is completed, the liquid resin coated on the surface of the raw paper 20, which is conveyed at a speed of 40 m per minute, is coagulated by using a drier which generates heat at 220 ° C. in the drying and printing steps, Thereby forming the resin 30 to be formed.
건조 및 인쇄단계가 완료되면 쿨링기에서 응고된 원지(20)의 수지(30)를 냉각시켜 경화시킨다.When the drying and printing steps are completed, the resin 30 of the raw paper 20 solidified in the cooling machine is cooled and cured.
경화된 원지(20)는 인쇄기로 공급되어 여러 가지의 도형과 그림이 코팅된 수지(30)의 표면에 인쇄되도록 한다.The cured raw paper 20 is supplied to a printing machine so as to be printed on the surface of the resin 30 coated with various figures and figures.
건조 및 인쇄단계를 완료한 원지(20)는 가열단계에서 기존보다 20∼30% 증대된 240∼270℃의 온도로 황토(40)를 함유하고 있는 코딩된 수지(30)에 열을 가하여 원지(20)의 표면에서 1∼2㎜정도의 두께를 갖도록 발포시킨다.The raw paper 20 having completed the drying and printing steps is heated in the heating step by heating the coded resin 30 containing the loess 40 at a temperature of 240 to 270 DEG C which is increased by 20 to 30% 20 so as to have a thickness of about 1 to 2 mm.
가열단계를 거친 원지(20)는 형압공정으로 공급되어 수지(30)를 가압시키는 가압롤러의 의해 여러가지형태로 엠보싱이 형성되도록 한다.The raw paper 20 that has undergone the heating step is supplied to a stamping process so that the embossing can be formed in various forms by the pressure roller which presses the resin 30.
수지(30)에 엠보싱의 형성이 완료된 원지(20)는 절단단계에서 1차절단기를 통과시켜 양단을 절단시킨 후 2차절단기를 통과시켜 두루마리로 권취되는 벽지(10)의 길이를 적정하게 절단되게 하므로서 황토벽지(10)의 제조를 완성시킨다.After the embossing is completed in the resin 30, the embossed paper 20 is passed through a primary cutter to cut both ends, and then passed through a secondary cutter so that the length of the wallpaper 10 wound in a roll is properly cut Thereby completing the manufacture of the loess wallpaper 10.
이렇게 벽지(10)의 제조가 완료되면 포장단계를 거쳐 출하될 수 있게 한 것이다.When the wallpaper 10 is completely manufactured, it can be shipped through the packaging step.
이러한 제조과정을 거쳐 완성된 벽지(10)는 도 2에 도시하였다.The wallpaper 10 completed through this manufacturing process is shown in Fig.
이 벽지(10)는 원지(20)의 표면에 황토(40)가 함유된 수지(30)가 엠보싱을 가진 상태로 코팅되어 있고, 이 수지(30)의 표면에는 여러 가지의 도형과 그림이 인쇄되어 있다.The wallpaper 10 is coated with the resin 30 containing the yellow clay 40 on the surface of the green sheet 20 with embossing and various shapes and pictures are printed on the surface of the resin 30. [ .
따라서 여러 가지의 화학약품에 황토가 상호 점착결합 구성되어 있어 외관과 특정한 기능성을 갖춘 벽지(10)의 고급화를 요구하는 소비자의 욕구를 충족시킬 수 있게 한 것이다.Accordingly, the yellow clay is adhesively bonded to various chemicals, thereby satisfying the consumer's desire for upgrading the wallpaper 10 having the appearance and the specific functionality.
또한 황토의 성분이 수지(30)에 18∼22%정도 함유되어 있어 여러 가지의 화학약품에서 발생되는 유해성분인 포르말레이드를 KS규격에서 규제하고 있는 2㎎/㎡이하로 유지될 수 있게 하여 인체에 해를 끼치지 않는 벽지(10)의 제조가 가능한 것이다.Also, since the content of loess is contained in resin (30) in the range of 18 to 22%, formaldehyde, which is a harmful component generated from various chemicals, can be maintained at 2 mg / m 2 or less It is possible to manufacture the wallpaper 10 which does not harm the human body.
또한 황토를 포함하고 있는 수지(30)에 의해 코팅된 벽지(10)가 습도조절기능을 가짐에 따라 벽지에 습기가 차는 것을 방지하여 벽지(10)의 손상을 방지할 수 있다.In addition, since the wallpaper 10 coated with the resin 30 containing the loess has the humidity control function, it is possible to prevent moisture from getting on the wallpaper, thereby preventing the wallpaper 10 from being damaged.
특히 황토성분에서 발생되는 바이오(Bio) 및 원적외선에 의해 자연친화적인 느낌을 가질 수 있어 상쾌한 실내분위기의 환경을 도모하고, 인체의 생체리듬 증대로 건강에 유익한 효과를 줄수 있게 한다.In particular, it is possible to have a feeling of nature-friendly by the bio and far-infrared rays generated from the loess component, thereby providing an environment of refreshing indoor atmosphere and providing a beneficial effect to health by increasing the body rhythm of the human body.
또한 황토에는 탈취재의 기능을 가지고 있어 발포재에 의해 발생되는 냄새를 제거하여 쾌적한 환경을 유지시키고, 비교적 가격이 싸고 비중이 가벼운 황토에 의해 벽지(10)의 원가를 절감시키는 동시에 무게중량의 저하로 운송 및 사용취급성을 용이하게 할 수 있는 것이다.In addition, the loess has a function of deodorizing material to remove the odor generated by the foamed material, thereby maintaining a pleasant environment, and the cost of the wallpaper 10 can be reduced by the relatively low-cost and light-weight loess, Thereby facilitating transportation and handling.
이상에서와 같이 벽지의 원지 표면에 코팅되는 수지에 황토를 배합시켜 코팅시킴에 따라 황토성분에 의해 습도조절이 용이하고, 탈취기능에 따른 냄새의 제거가 용이하며, 바이오 및 원적외선의 발생으로 인체의 활력을 증대시키며, 벽지의 원가절감 및 품질의 고급화와 신뢰도를 높일 수 있는 효과가 있다.As described above, it is possible to easily adjust the humidity by the yellow clay component and to remove the odor by the deodorizing function by coating the resin coated on the surface of the paper wallpaper with the yellow soil, and it is easy to remove the odor. Increase the vitality, reduce the cost of wallpaper, and enhance the quality and reliability.
Claims (2)