KR19990037218U - Subsidiary materials for yellow soil use - Google Patents

Abstract

The present invention relates to a furniture member using loess.

To this end, the present invention is characterized in that the ocher powder is coated with a thickness of 0.01 ~ 0.03mm on all six surfaces of the furniture member of wood, the transparent urethane solution is coated thereon and the transparent urethane solution is coated on top of it. It is done.

Description

SUBSIDIARY MATERIALS FOR YELLOW SOIL USE}

The present invention relates to a furniture member using loess.

It is best to be used as a member for furniture, but since it is expensive, it is attached to the surface of the laminated wood or MDF board with a very thin wooden sheet or similar to the pattern of the wood on the surface of the laminated wood, MDF board, plywood, etc. The use of a synthetic resin sheet printed with a pattern is widely used.

However, they have the disadvantages such as low price but low quality as furniture and low durability, and the use of solid wood is increasing.

However, because the wood itself is so widely used, a new sense of aesthetics is required due to the somewhat dry feeling and the uniformity of appearance, and furthermore, the development of the furniture member that emphasizes the functionality is required.

Therefore, the present invention provides a furniture member using ocher that makes the texture of the wood and the appearance more beautiful.

In addition, the present invention provides a furniture member using loess which is excellent in insect repellent function, far infrared ray function, flame retardant function, moisture proof function and the like.

To this end, the present invention is characterized in that the ocher powder is coated with a thickness of 0.01 ~ 0.03mm on all six surfaces of the furniture member of wood, the transparent urethane solution is coated thereon and the transparent urethane solution is coated on top of it. It is done.

1 is a cross-sectional view showing the configuration of the present invention.

<Code Description of Main Parts of Drawing>

10: Furniture member 11: loess powder coating layer

12: Transparent urethane liquid undercoat layer 13: Transparent urethane liquid top coat layer

Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, the manufacturing method of the present invention is presented for reference.

After taking the first step of collecting the loess and finely pulverizing the particles into particles of 1,000 to 2,000 mesh, the second step of mixing the loess powder and water in a ratio of 6: 4 and stirring it through a stirrer is performed. Next, a third step of filling the ocher powder prepared by the second step above is carried out into the container of the upper and lower sets of roller apparatuses in which the lower roller is inserted halfway into the container, and the lower roller becomes the ocher powder. Enough in liquid.

Next, a fourth step of passing the wooden board between the upper and lower rollers of the roller apparatus to coat the ocher powder solution in a thickness of 0.01 ~ 0.03mm above and below the wooden board. At this time, the roller is a rubber coated roller or a rubber roller, it is preferable to use a sponge roller, by adjusting the upper roller up and down to adjust the coating thickness of the ocher powder. Here, the coating thickness of the ocher powder may exceed 0.03mm, but in this case, the pattern of the wood may not be exposed, so the thickness of the ocher powder need not be more than 0.03mm unless it is a special case.

Next, after the fifth step of drying the wooden board subjected to the fourth process in a hot air fan for 5 to 8 hours, the upper and lower surfaces of the wooden board subjected to the fifth process are polished 10-15 times with # 220 sandpaper. 6 The process is performed. At this time, it is preferable to use an automatic polishing machine (automatic sand paper machine) for polishing, but in some cases, manual work is also possible. An eighth step of applying the transparent urethane liquid to the upper and lower surfaces of the wooden board after the sixth step with a lower coat and then drying the transparent urethane coated surface 10 to 15 times with # 220 to 300 sandpaper once dried. The process is performed.

Next, after performing the ninth step after the eighth process and applying a transparent urethane as a top coat to dry the hot air, the ninth step of cutting the wood plate subjected to the ninth process to the necessary dimensions to use as a furniture member Complete it first.

Since the upper and lower surfaces of the furniture members produced through the tenth step have already been primarily completed, the eleventh process is performed to coat the ocher powder with a thickness of 0.01 to 0.03 mm on the four vertical surfaces except for these. Next, a twelfth step of drying the members having undergone the eleventh process in a hot air blower for 5 to 8 hours, and a thirteenth step of polishing the longitudinal surface of four surfaces of the members having undergone the twelfth process with # 220 sandpaper 10 to 15 times. Process, the 14th step of applying a transparent urethane liquid on the longitudinal surface of the members having undergone the 13th process, as a coat and a transparent urethane coating surface subjected to the 14th process again 10-15 times with # 220-300 sandpaper After the fifteenth step and the fifteenth step, the sixteenth step of drying the hot air by applying transparent urethane as a top coat is the same as described above.

As described above, the furniture member of the present invention has an ocher powder coating layer 11 formed on the entire surface of the furniture member 10 as shown in FIG. 1, and a transparent urethane liquid undercoat layer 11 is formed thereon. Is formed.

The present invention, since the ocher powder is coated while dense to the surface of the member was found that in addition to the texture of the wood and the natural color of the loess is well combined, the appearance is very beautiful. And the flame retardant, insect repellent, moisture proof, corrosion resistance, etc. of the ocher powder are grafted to the member, and this is a transparent urethane liquid, which is perfectly preserved through the top coat and the top treatment, so that the flame retardant, insect repellent, moisture proof, and corrosion resistance are excellent. It can be seen that the odor is not added to the member is also added.

In addition, it is natural that loess has a function of emitting far infrared rays in itself and has a beneficial effect on the human body.

The present invention can be applied to any wood plate, such as laminated wood, plywood, MDF board, as well as solid wood, so that the high value added, as well as applying ocher powder to this other furniture member as well as the present invention It is natural to be bound by the technical category.

The present invention as described above, by grafting the ocher to the furniture member such as solid wood, to provide a new type of furniture member that is imparted to the various functions as described above and beneficial to health while solving the problem of somewhat dry and monotonous There are a number of features, such as the ability to create high added value, increase economic competitiveness, and obtain foreign currency through exports.

Claims (1)

Ocher powder is coated with a thickness of 0.01 ~ 0.03mm on all six surfaces of the wooden furniture member, the transparent urethane liquid is coated on top of it, and the transparent urethane liquid is coated on top of it. absence.